CN101041739B - 由pc(聚碳酸酯)次料改性的pc/abs合金(一) - Google Patents
由pc(聚碳酸酯)次料改性的pc/abs合金(一) Download PDFInfo
- Publication number
- CN101041739B CN101041739B CN2006100342964A CN200610034296A CN101041739B CN 101041739 B CN101041739 B CN 101041739B CN 2006100342964 A CN2006100342964 A CN 2006100342964A CN 200610034296 A CN200610034296 A CN 200610034296A CN 101041739 B CN101041739 B CN 101041739B
- Authority
- CN
- China
- Prior art keywords
- parts
- butadiene
- polycarbonate
- acrylonitrile
- oxidation inhibitor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种由PC次料改性的PC/ABS合金的配方,由按质量份数计算的下列组分组成:PC回收料:45~60份、ABS:20~35份、接枝共聚物:1~5份、抗冲改性剂:3~10份、环氧树脂:0.1~1份、抗氧剂:0.1~0.5份、溴系阻燃剂:6~12份、锑系阻燃剂:1~2份、无机阻燃剂:1~2份、聚四氟乙烯:0.2~0.8份。本发明提供的由PC次料改性的PC/ABS合金,采用高效的合金相容剂对PC回收料与ABS进行共混改性,制成PC/ABS合金料,一方面可降低PC的熔体黏度,改善其加工性能,另一方面对PC进行经济的回收利用,不会对环境造成额外的负担。
Description
技术领域
本发明涉及高分子材料技术中热塑性树脂组合物领域,具体涉及一种PC(Polycarbonate,聚碳酸酯)次料改性成为阻燃PC/ABS合金的配方。
背景技术
PC是一种综合性能优越的工程塑料,具有优异的冲击韧性、尺寸稳定性、电气绝缘性、耐蠕变性、耐候性、透明性和无毒性等优点,广泛用于机械设备、建筑工程、交通运输、仪表及电子电气照明等领域。
PC也有一些明显的缺陷,如:加工流动性差、易应力开裂、对缺口敏感、容易磨损、耐化学药品性差、价格偏高等。PC的消耗量较大,同时制品生产过程中产生的次料、水口料和回收料的量也多,因此对PC回收料进行改性使其能重复使用,具有重要意义。而ABS具有较好的耐化学腐蚀性,良好的加工性以及较高的性价比。将PC回收料与ABS进行共混改性制成PC/ABS合金料,一方面可降低PC的熔体黏度,改善其加工性能,同时能改善PC的缺口敏感性和耐化学药品性,另一方面又可对PC进行回收重复利用。
发明内容
本发明的目的在于提供一种PC回收料改性为阻燃PC/ABS合金的配方,对PC次料进行回收改性。
为达到上述目的,本发明提供的PC回收料改性为阻燃PC/ABS合金的配方是在PC回收料中添加ABS、相容剂、环氧树脂及抗氧剂、阻燃剂等进行改性,从而提高其机械性能,实现了PC的回收利用。值得指出的是,PC/ABS合金燃烧时存在严重的滴落现象,而经阻燃化改性后,材料的冲击性能会明显下降。对此,为改善材料的韧性和阻燃性能,本发明采用了兼具防止燃烧滴落作用的抗冲改性剂CPE或PVC。
本发明提供的一种由PC次料改性的PC/ABS合金,由按质量份数计算的下列组分组成:
(a)PC回收料 45~60份
(b)ABS 20~35份
(c)接枝共聚物 1~5份
(d)抗冲改性剂 3~10份
(e)环氧树脂 0.1~1份
(f)抗氧剂 0.1~0.5份
(g)溴系阻燃剂 6~12份
(h)锑系阻燃剂 1~2份
(i)无机阻燃剂 1~2份
(j)聚四氟乙烯 0.2~0.8份
其中的接枝共聚物是马来酸酐接枝ABS、SEBS(饱和苯乙烯-丁二烯-苯乙烯嵌段共聚物)或PS共聚物(即ABS-g-MAH、SEBS-g-MAH或PS-g-MAH)。
其中的抗冲改性剂是兼具阻燃、防燃烧滴落作用的CPE(氯化聚乙烯)或PVC(聚氯乙稀)。
其中的抗氧剂是抗氧剂2921或抗氧剂2225等。
其中的溴系阻燃剂是溴化聚碳酸酯、十溴二苯醚、八溴醚、四溴双酚A、四溴双酚A聚碳酸酯齐聚物或六溴环十二烷等。
其中的锑系阻燃剂是三氧化二锑、五氧化二锑或锑酸钠等。
其中的无机阻燃剂是氢氧化铝、氢氧化镁、硼酸锌或微胶囊化红磷等。
优选地,本发明提供的由PC次料改性的PC/ABS合金,由按质量份数计算的下列组分组成:
(a)PC回收料 60份
(b)ABS 24份
(c)ABS-g-MAH 4份
(d)CPE 5份
(e)环氧树脂 0.5份
(f)抗氧剂2921 0.2份
(g)溴化聚碳酸酯 9份
(h)三氧化二锑 1.5份
(i)硼酸锌 1.5份
(j)聚四氟乙烯 0.5份
优选地,本发明提供的由PC次料改性的PC/ABS合金,由按质量份数计算的下列组分组成:
(a)PC回收料 50份
(b)ABS 30份
(c)ABS-g-MAH 4份
(d)CPE 8份
(e)环氧树脂 0.1份
(f)抗氧剂2921 0.3份
(g)溴化聚碳酸酯 6份
(h)三氧化二锑 1份
(i)硼酸锌 1份
(j)聚四氟乙烯 0.3份
优选地,本发明提供的由PC次料改性的PC/ABS合金,由按质量份数计算的下列组分组成:
(a)PC回收料 45份
(b)ABS 32份
(c)ABS-g-MAH 5份
(d)CPE 2份
(e)环氧树脂 0.3份
(f)抗氧剂2921 0.3份
(g)溴化聚碳酸酯 12份
(h)三氧化二锑 2份
(i)硼酸锌 2份
(j)聚四氟乙烯 0.3份
本发明提供的由PC次料改性的PC/ABS合金中采用高效的合金相容剂,对PC回收料与ABS进行共混改性制成PC/ABS合金料,一方面可降低PC的熔体黏度,改善其加工性能,另一方面对PC进行经济的回收利用,不会对环境造成额外的负担。
本发明的由PC次料改性的PC/ABS合金可用本技术领域现有的技术方式制成各种形式的成型品以供利用。
具体实施方式
实施例1
取PC回收料、ABS、抗冲改性剂、环氧树脂、抗氧剂、阻燃剂等成分,按下述组成配方将所有原料进行共混:
(a)PC回收料 60份
(b)ABS 24份
(c)ABS-g-MAH 4份
(d)CPE 5份
(e)环氧树脂 0.5份
(f)抗氧剂2921 0.2份
(g)溴化聚碳酸酯 9份
(h)三氧化二锑 1.5份
(i)硼酸锌 1.5份
(j)聚四氟乙烯 0.5份
再将该共混料通过挤出机中混炼造粒,所得混炼造粒经注射成型制成成品,最后按国家标准GB13525/T-92测试所得成品的机械性能及按美国电工协会UL94标准测试其阻燃性能,结果如表1所示。
表1:实施例1所得PC经ABS改性后的合金性能
项目 | 测定值 |
冲击强度(kJ/M<sup>2</sup>) | 33.29 |
拉伸强度(MPa) | 57.34 |
弯曲强度(MPa) | 89.50 |
阻燃性 | V-0 |
实施例2
取PC回收料、ABS、抗冲改性剂、环氧树脂、抗氧剂、阻燃剂等成分,按下述组成配方将所有原料进行共混:
(a)PC回收料 50份
(b)ABS 30份
(c)ABS-g-MAH 4份
(d)CPE 8份
(e)环氧树脂 0.1份
(f)抗氧剂2921 0.3份
(g)溴化聚碳酸酯 6份
(h)三氧化二锑 1份
(i)硼酸锌 1份
(j)聚四氟乙烯 0.3份
再将该共混料通过挤出机中混炼造粒,所得混炼造粒经注射成型制成成品,最后按国家标准GB13525/T-92测试所得成品的机械性能及按美国电工协会UL94标准测试其阻燃性能,结果如表2所示。
表2:实施例2所得PC经ABS改性后的合金性能
项目 | 测定值 |
冲击强度(kJ/M<sup>2</sup>) | 38.72 |
拉伸强度(MPa) | 56.88 |
弯曲强度(MPa) | 87.65 |
阻燃性 | V-0 |
实施例3
取PC回收料、ABS、抗冲改性剂、环氧树脂、抗氧剂、阻燃剂等成分,按下述组成配方将所有原料进行共混:
(a)PC回收料 45份
(b)ABS 32份
(c)ABS-g-MAH 5份
(d)CPE 2份
(e)环氧树脂 0.3份
(f)抗氧剂2921 0.3份
(g)溴化聚碳酸酯 12份
(h)三氧化二锑 2份
(i)硼酸锌 2份
(j)聚四氟乙烯 0.3份
再将该共混料通过挤出机中混炼造粒,所得混炼造粒经注射成型制成成品,最后按国家标准GB13525/T-92测试所得成品的机械性能及按美国电工协会UL94标准测试其阻燃性能,结果如表3所示。
表3:实施例3所得PC经ABS改性后的合金性能
项目 | 测定值 |
冲击强度(kJ/M<sup>2</sup>) | 24.29 |
拉伸强度(MPa) | 55.38 |
弯曲强度(MPa) | 86.91 |
阻燃性 | V-0 |
以上具体实施方式,是对本发明所作的详细说明。注意这些实施方式并非用以限定本发明,对于本领域的熟练技术人员,在不背离本发明精神的情况下所做出的改进和补充,应该视为在本发明的保护范围之内。
Claims (5)
1.一种由PC次料改性的PC/ABS合金,其特征在于,由按质量份数计算的下列组分组成:
(a)聚碳酸酯回收料 45~60份;
(b)丙烯腈-丁二烯-苯乙烯三元共聚物 20~35份;
(c)接枝共聚物 1~5份;
(d)抗冲改性剂 3~10份;
(e)环氧树脂 0.1~1份;
(f)抗氧剂 0.1~0.5份;
(g)溴系阻燃剂 6~12份;
(h)锑系阻燃剂 1~2份;
(i)无机阻燃剂 1~2份;
(j)聚四氟乙烯 0.2~0.8份;
其中,所述接枝共聚物是丙烯腈-丁二烯-苯乙烯三元共聚物-马来酸酐接枝共聚物、饱和苯乙烯-丁二烯-苯乙烯嵌段共聚物-马来酸酐接枝共聚物或聚苯乙烯-马来酸酐接枝共聚物;所述抗冲改性剂是氯化聚乙烯或聚氯乙稀;所述溴系阻燃剂是选自溴化聚碳酸酯、十溴二苯醚、八溴醚、四溴双酚A、四溴双酚A聚碳酸酯齐聚物或六溴环十二烷中的一种;所述锑系阻燃剂是选自三氧化二锑、五氧化二锑或锑酸钠中的一种;所述无机阻燃剂是选自氢氧化铝、氢氧化镁、硼酸锌或微胶囊化红磷中的一种。
2.根据权利要求1所述的由PC次料改性的PC/ABS合金,其特征在于,所述抗氧剂是抗氧剂2921或抗氧剂2225。
3.根据权利要求1-2中任意一项所述的由PC次料改性的PC/ABS合金,其特征在于,由按质量份数计算的下列组分组成:
(a)聚碳酸酯回收料 60份;
(b)丙烯腈-丁二烯-苯乙烯三元共聚物 24份;
(c)丙烯腈-丁二烯-苯乙烯三元共聚物-马来酸酐接枝共聚物 4份;
(d)氯化聚乙烯 5份;
(e)环氧树脂 0.5份;
(f)抗氧剂2921 0.2份;
(g)溴化聚碳酸酯 9份;
(h)三氧化二锑 1.5份;
(i)硼酸锌 1.5份;
(j)聚四氟乙烯 0.5份。
4.根据权利要求1-2中任意一项所述的由PC次料改性的PC/ABS合金,其特征在于,由按质量份数计算的下列组分组成:
(a)聚碳酸酯回收料 50份;
(b)丙烯腈-丁二烯-苯乙烯三元共聚物 30份;
(c)丙烯腈-丁二烯-苯乙烯三元共聚物-马来酸酐接枝共聚物 4份;
(d)氯化聚乙烯 8份;
(e)环氧树脂 0.1份;
(f)抗氧剂2921 0.3份;
(g)溴化聚碳酸酯 6份;
(h)三氧化二锑 1份;
(i)硼酸锌 1份;
(j)聚四氟乙烯 0.3份。
5.根据权利要求1-2中任意一项所述的由PC次料改性的PC/ABS合金,其特征在于,由按质量份数计算的下列组分组成:
(a)聚碳酸酯回收料 45份;
(b)丙烯腈-丁二烯-苯乙烯三元共聚物 32份;
(c)丙烯腈-丁二烯-苯乙烯三元共聚物-马来酸酐接枝共聚物 5份;
(d)氯化聚乙烯 2份;
(e)环氧树脂 0.3份;
(f)抗氧剂2921 0.3份;
(g)溴化聚碳酸酯 12份;
(h)三氧化二锑 2份;
(i)硼酸锌 2份;
(j)聚四氟乙烯 0.3份。