CN100573928C - 一种制造太阳能电池的磷扩散方法 - Google Patents
一种制造太阳能电池的磷扩散方法 Download PDFInfo
- Publication number
- CN100573928C CN100573928C CNB2007101328418A CN200710132841A CN100573928C CN 100573928 C CN100573928 C CN 100573928C CN B2007101328418 A CNB2007101328418 A CN B2007101328418A CN 200710132841 A CN200710132841 A CN 200710132841A CN 100573928 C CN100573928 C CN 100573928C
- Authority
- CN
- China
- Prior art keywords
- solar cell
- silicon
- phosphorus diffusion
- minutes
- monocrystalline silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种制造太阳能电池的磷扩散方法,其特征在于,包括如下步骤:(1)将待处理的单晶硅片在900~950℃氮气气氛下进行退火处理20~30分钟;(2)将上述处理后的硅片在850~1050℃氯化氢气氛下进行氧化处理,使其表面生成厚度为10至30纳米的氧化层;(3)再在850~900℃下通磷源扩散,使得表面方块电阻控制在40~50欧姆,结深0.2~1.0微米;(4)最后在700~750℃氮气气氛下退火处理30~60分钟,完成单晶硅片的磷扩散处理。本发明可以采用纯度为4、5N的单晶硅作为制造太阳能电池的材料,因而,可以利用冶金硅等纯度较低的材料,极大地降低了材料成本,有利于单晶硅太阳能电池的普及应用。
Description
技术领域
本发明涉及一种制造太阳能电池的扩散制结工艺,具体涉及一种制造太阳能电池的磷扩散方法。
背景技术
太阳能是人类取之不尽、用之不竭的可再生能源,也是清洁能源,使用太阳能可有效减轻环境污染。大阳能光电利用是近些年来发展最快、最具活力的研究领域之一。太阳能电池主要以半导体材料为基础制作,其工作原理是光电材料吸收光能后发生光电子转换反应而产生电流,目前广泛采用的是硅太阳能电池。硅太阳能电池又分为单晶硅太阳电池、非晶硅太阳电池和多晶硅太阳电池等。其中,单晶硅大阳能电池转换效率最高,技术也最为成熟。
现有技术中,单晶硅大阳能电池的制造主要包括如下步骤:去损伤层-制绒-扩散制结-等离子刻蚀去边-去磷硅玻璃-减反射膜-丝网印刷-烧结。其中,扩散制结(通常是磷扩散制结)是一个关键步骤,制结质量会影响最终的光电转换效率。在工业化生产中,典型的结制备分为两步:第一步用氮气通过液态的POCl3,将所需的杂质用载流气体输运至高温半导体表面,杂质扩散深度约几百个纳米;第二步是高温处理,使预沉积在表面的杂质原子继续向基体深处扩散,这样就形成了一个N+/N层,这样的结构有利于后续电极的制备。这种发射区结构也可以用一步扩散法制得,但是需要增加一个腐蚀过程;快热法也可以用于上述制结步骤,可大大简化上述过程,但这种工艺还只处于初期研究阶段。
然而,上述扩散制结工艺都是建立在高质量单晶硅材料的基础上的,一般都要求硅材料的纯度在6N以上,而纯度越高,其材料成本也就越高,使得单晶硅大阳能电池的价格居高不下,难以实现普及应用。同时,利用原料纯度低的金属硅作为起始原料,经过熔融精炼、单向凝固精制等工序后,可得到纯度为4N~5N的硅材料,如果进一步提纯以得到6N以上的高纯度硅,则会大大增加成本,还会降低硅的利用率。因此,开发一种直接利用4N~5N的低纯度硅材料来制备具有较好的转换效率的单晶硅太阳能电池的磷扩散方法必将具有很大的意义。
发明内容
本发明目的是提供一种制造太阳能电池的磷扩散工艺,以便可以采用较低纯度的硅材料来制备太阳能电池。
为达到上述目的,本发明采用的技术方案是:一种制造太阳能电池的磷扩散方法,包括如下步骤:
(1)将待处理的单晶硅片在900~950℃氮气气氛下进行退火处理20~30分钟;
(2)将上述处理后的硅片在850~1050℃氯化氢气氛下进行氧化处理,使其表面生成厚度为10至30纳米的氧化层;
(3)再在850~900℃下通磷源扩散,使得表面方块电阻控制在40~50欧姆,结深0.2~1.0微米;
(4)最后在700~750℃氮气气氛下退火处理30~60分钟,完成单晶硅片的磷扩散处理。
上述技术方案中,所述步骤(2)的氧化处理时间为20~30分钟。
所述步骤(3)的磷扩散时间为25~60分钟。
在单晶硅片中,因杂质和杂质、缺陷与杂质之间的相互作用,重金属或微缺陷在一定的温度下会发生迁移和再凝集。因而,通过退火可以使晶片中含杂聚成纳米级的小团,从而降低复合中心密度,提高少子寿命。然而,传统的方案中,退火处理通常需要进行4、5个小时,其扩散温度是从低到高再到低的,当用于处理纯度为4、5N的单晶硅时,难以获得良好的除杂和制结效果。本发明在退火和磷扩散之间加入了氯化氢气氛下的氧化处理,即采用含氯氧化法制作了氧化层,因而,整个过程中,温度变化是从高到低再高再到低呈梯度变化的,实际试验表明,采用上述方法后,获得了良好的效果。
由于上述技术方案运用,本发明与现有技术相比具有下列优点:
本发明在通磷源扩散前后进行退火,使晶片中含杂聚成纳米级的小团,从而降低复合中心密度,提高少子寿命;并且在退火和磷扩散之间加入了氯化氢气氛下的氧化处理步骤。经过上述处理,本发明可以采用纯度为4、5N的单晶硅作为制造太阳能电池的材料,因而,可以利用冶金硅等纯度较低的材料,极大地降低了材料成本,有利于单晶硅太阳能电池的普及应用。
具体实施方式
下面结合实施例和对比例对本发明作进一步描述:
实施例一:
将一组纯度为5N的硅片用如下磷扩散工艺处理:步骤1,在950℃氮气气氛下保持20分钟;步骤2,在850℃氯化氢气氛下保持20分钟;步骤3,在900℃通磷源扩散50分钟;步骤4,在750℃氮气气氛下保持30分钟。然后采用常规工艺方法进一步处理,得到一组太阳能电池片。
随机选取10片,在AM1.5,温度27℃条件下测定其短路电流Isc、开路电压Voc、最大功率Pmax、填充因子FF和光电转换效率EF,结果如下表所示:
序号 Isc(A) Voc(mV) Pmax(W) FF(%) EF(%)
1 4.46644 610.52 1.73559 63.648 11.68116
2 4.54678 613.26 2.17556 77.882 14.61594
3 4.53085 613.22 2.09676 78.303 14.64234
4 4.49747 610.76 1.85691 76.332 14.11197
5 4.38281 607.12 2.07611 69.785 12.49769
6 4.44712 609.22 2.05781 76.629 13.97298
7 4.42516 608.7 2.09916 76.396 13.84986
8 4.43123 608.15 2.09444 77.895 14.12916
9 4.46954 608.6 2.09446 76.994 14.09635
10 4.50129 612.25 2.10562 76.404 14.17161
平均值 4.469869 610.18 2.039242 75.0268 13.77691
实施例二:
将另外一组纯度为5N的硅片用如下磷扩散工艺处理:步骤1,在900℃氮气气氛下保持25分钟;步骤2,在1000氯化氢气氛下保持25分钟;步骤3,在900℃通磷源扩散30分钟;步骤4,在700℃氮气气氛下保持50分钟。然后采用常规工艺方法进一步处理,得到一组太阳能电池片。
随机选取10片,在AM1.5,温度27℃条件下测定其短路电流Isc、开路电压Voc、最大功率Pmax、填充因子FF和光电转换效率EF,结果如下表所示:
序号 Isc(A) Voc(mV) Pmax(W) FF(%) EF(%)
1 4.35766 609.14 2.04992 77.226 13.79673
2 4.4196 610.17 2.09707 77.773 14.11409
3 4.39372 607.99 2.07775 77.78 13.98408
4 4.3689 608.53 2.06782 77.778 13.91723
5 4.37946 608.45 2.05224 77.017 13.81236
6 4.44184 612.49 2.13835 78.599 14.39191
7 4.40191 608.81 1.71494 63.991 11.54202
8 4.45567 612.57 2.10022 76.947 14.13526
9 4.42383 613.46 2.10247 77.472 14.15045
10 4.27499 605.99 1.78353 68.847 12.00382
平均值 4.391758 609.76 2.044531 75.343 13.5848
实施例三:
将另外一组纯度为5N的硅片用如下磷扩散工艺处理:步骤1,在920℃氮气气氛下保持30分钟;步骤2,在950℃氯化氢气氛下保持30分钟;步骤3,在850℃通磷源扩散60分钟;步骤4,在700℃氮气气氛下保持40分钟。然后采用常规工艺方法进一步处理,得到一组太阳能电池片。
随机选取16片,在AM1.5,温度28℃条件下测定其短路电流Isc、开路电压Voc、最大功率Pmax、填充因子FF和光电转换效率EF,结果如下表所示:
序号 Isc(A) Voc(mV) Pmax(W) FF(%) EF(%)
1 4.40454 607.89 2.00977 75.063 13.52651
2 4.43724 609.05 2.04521 75.678 13.76501
3 4.42288 609.12 2.09828 77.885 14.12223
4 4.4701 609.89 2.08441 76.456 14.0289
5 4.46758 609.76 2.08204 76.428 14.0129
6 4.51984 611.04 2.10364 76.169 14.15827
7 4.43159 606.86 2.07638 77.207 13.97485
8 4.54037 609.98 2.12963 76.895 14.3332
9 4.49947 608.79 2.0755 75.769 13.96892
10 4.52432 610.23 2.11063 76.449 14.20537
11 4.4557 609.58 2.02947 74.719 13.65908
12 4.50928 607.72 2.01459 73.515 13.55895
13 4.55504 610.54 2.14621 77.173 14.44481
14 4.51071 610.46 2.08132 75.585 14.00807
15 4.51885 611.89 2.0619 74.571 13.87738
16 4.49353 609.17 2.07788 75.909 13.98492
平均值 4.485065 609.4981 2.076679 75.96694 13.97684
对比例一
将一组纯度为5N的硅片用传统磷扩散工艺处理,得到一组太阳能电池片。
随机选取12片,在AM1.5,温度27℃条件下测定其短路电流Isc、开路电压Voc、最大功率Pmax、填充因子FF和光电转换效率EF,结果如下表所示:
序号 Isc(A) Voc(mV) Pmax(W) FF(%) EF(%)
1 3.92058 0.60462 0.84076 0.35468 5.65863
2 3.98012 0.61667 0.92812 0.37815 6.24662
3 3.97738 0.61748 0.97356 0.39641 6.55244
4 4.04155 0.61912 1.05359 0.42107 7.09106
5 4.23414 0.61565 1.13905 0.43696 7.66626
6 4.24061 0.62082 1.20179 0.45649 8.08848
7 4.38697 0.61601 1.31707 0.48737 8.86438
8 4.57012 0.61332 1.41021 0.50312 9.49122
9 4.62997 0.61498 1.49039 0.52343 10.03087
10 4.64822 0.61207 1.63927 0.57619 11.03289
11 4.59806 0.61483 1.79448 0.63476 12.07754
12 4.70738 0.6133 1.93556 0.67043 13.02708
平均值 4.327925 0.614906 1.310321 0.486588 8.818956
从上述实施例和对比例可以看出,三个实施例中,获得的太阳能电池的性能均匀性好,三批太阳能电池的转换效率平均值分别为13.77691%、13.5848%和13.97684%,而对比例的电池性能上下波动极大,并且其转换效率平均值仅为8.818956%,由于对比例电池的一致性太差,转换效率过低,不能进入商业化应用。
可见,采用本发明的技术方案,可以有效地利用较低纯度的单晶硅片制作太阳能电池,从而大大降低了太阳能电池的制造成本。
Claims (3)
1.一种制造太阳能电池的磷扩散方法,其特征在于,包括如下步骤:
(1)将待处理的单晶硅片在900~950℃氮气气氛下进行退火处理20~30分钟;
(2)将上述处理后的硅片在850~1050℃氯化氢气氛下进行氧化处理,使其表面生成厚度为10至30纳米的氧化层;
(3)再在850~900℃下通磷源扩散,使得表面方块电阻控制在40~50欧姆,结深0.2~1.0微米;
(4)最后在700~750℃氮气气氛下退火处理30~60分钟,完成单晶硅片的磷扩散处理。
2.根据权利要求1所述的制造太阳能电池的磷扩散方法,其特征在于:所述步骤(2)的氧化处理时间为20~30分钟。
3.根据权利要求1所述的制造太阳能电池的磷扩散方法,其特征在于:所述步骤(3)的磷扩散时间为25~60分钟。