CN100532702C - Window dressing face fabric processing agent and its usage method - Google Patents
Window dressing face fabric processing agent and its usage method Download PDFInfo
- Publication number
- CN100532702C CN100532702C CNB2007101604649A CN200710160464A CN100532702C CN 100532702 C CN100532702 C CN 100532702C CN B2007101604649 A CNB2007101604649 A CN B2007101604649A CN 200710160464 A CN200710160464 A CN 200710160464A CN 100532702 C CN100532702 C CN 100532702C
- Authority
- CN
- China
- Prior art keywords
- face fabric
- window dressing
- dressing face
- processing agent
- fabric processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a window decoration face material process agent, which adopts the following weight proportion per square meter of the window decoration face material to process the agent: PVC powder 95 to 105g; DOP 60 to 70g; Ba-Zn 2 to 3 g; antimony dioxide 5 to 15g; CaCO<SUB>3</SUB> 15 to 25g; D<SUB>80</SUB> 2.5 to 3.5g. The invention also relates to a usage method of the window decoration face material process agent. The invention is characterized by anti-pulling, sun shielding, air ventilating, water proofing, flame proofing and antibiotic property, and the invention has an effective anti-spy function, the invention product structure and surface style are elegant, bright and special.
Description
Technical field
The present invention relates to a kind of window dressing face fabric processing agent and using method thereof.
Background technology
Window dressing face fabric is the thing of indoor indispensability, the window dressing face fabric of Chu Xianing is various in style in the market, mainly be divided into shade fabric and printing opacity lining two big classes: the shade fabric of the first kind is meant that under the irradiation of sun lights or light light can't penetrate curtain and enters the lining of indoor or outdoors, after this lining is handled through coating, every square metre of window dressing face fabric of finishing agent that used coating is handled adopts following prescription: acrylic acid 60g, water 40g, Ba-Zn 2g, CaCO
315g, D80 2g, viscosity is 65/mpa.s, bake out temperature 160-170 ℃, time 40-60 second.After handling, coating becomes the airproof plane of monoblock lining.Though it can shut out the light, and is airtight, also stopped the circulation of air simultaneously, particularly during the broiling summer, directly influence IAQ.The printing opacity lining of second class is meant that under the irradiation of sunlight or light light can penetrate curtain and enters the lining of indoor or outdoors, promptly do not handle through coating, though its printing opacity but not sunshade anti-ly spy on that effect is bad, antibiotic, anti drawing strongly power not enough, cracky, yielding, not shading.
Summary of the invention
In order to address the above problem, the object of the present invention is to provide a kind of window dressing face fabric processing agent and using method thereof, have tension, sunshade, ventilative, waterproof, fire-retardant, antibiotic; Accomplished simultaneously effective peep-proof visual function again, in an elegant style beautiful, the peculiar characteristics of its product structure and surface.
For reaching above-mentioned purpose, the present invention adopts following technical scheme,
A kind of window dressing face fabric processing agent, every square metre of finishing agent that window dressing face fabric adopts following materials of weight proportions to make:
PVC powder (2-methoxyl group-4-nitroaniline) 95-105g;
DOP (dioctyl phthalate) 60-70g;
Ba-Zn (heat stabilizer) 2-3g;
Antimony trichloride 5-15g;
CaCO
3?15-25g；
D
80(neighbour-hydroxybenzoic acid sodium) 2.5-3.5g.
The present invention adopts PVC powder 95g/m
2-105g/m
2Ratio has used double-layered structure's structure, i.e. the fine latitude of fine latitude of shrink property and gentle water-based.Making hydrone transfer to skin from the internal layer of lining distributes.Adopt DOP60g/m
2-70g/m
2.Ratio, promptly the fine latitude of the strong structure mode of molecule and fabric is combined as a whole, and its feature can be carried out physical sterilization exactly.The ratio of antimony trichloride makes fire resistance reach national standard B1 level, has antistatic effect preferably simultaneously.Ba-Zn can effectively reduce the air-conditioning electric energy up to 60%.
The finishing agent that described every square metre of window dressing face fabric preferably adopts following materials of weight proportions to make:
PVC powder (2-methoxyl group-4-nitroaniline) 100g;
DOP (dioctyl phthalate) 65g;
Ba-Zn (heat stabilizer) 2.5g;
Antimony trichloride 10g;
CaCO
3?20g；
D
80(neighbour-hydroxybenzoic acid sodium) 3g.
The using method of described window dressing face fabric processing agent is: window dressing face fabric is being checked through cloth inspecting machine illumination, after the arrangement, with the finishing agent of preparing according to the above ratio, finishing agent viscosity is: 1000-3000/Mpa.s, the starching coating, it utilizes tension characteristic, strengthens surface tension, makes the globule can't see through the space of lining surface texture.Be applied on the window dressing face fabric, infrared ray is followed the tracks of after the oven dry a period of time of heating at a certain temperature behind the heavy twist, and the door width of cloth is in accordance with regulations put burr, packed products in order then.
Described temperature is controlled at 160-190 ℃.
Described drying time is 2-3 minute.
The present invention adopts the finishing agent starching coating of preparation according to the above ratio, be applied on the window dressing face fabric, handle, 160 ℃-190 ℃ of times/2-3 minute through high-temperature shaping behind the heavy twist, make durable, the tension of lining stable significantly, in high-frequency use, can not be out of shape exactly.
The invention has the beneficial effects as follows: prescription that utilization of the present invention is developed voluntarily and using method thereof, product structure and surperficial style are optimized more, overcome the deficiency of existing formula technique simultaneously.Mainly show tension, sunshade, ventilative, waterproof, fire-retardant, antibiotic.Accomplished simultaneously effective peep-proof visual function again, its product structure and surface are in an elegant style beautiful, and be peculiar.
The specific embodiment
Embodiment 1
The window dressing face fabric processing agent that present embodiment adopts, every square metre of finishing agent that window dressing face fabric adopts following materials of weight proportions to make: PVC powder (2-methoxyl group-4-nitroaniline) 95g; DOP (dioctyl phthalate) 60g; Ba-Zn (heat stabilizer) 2g; Antimony trichloride 5g; CaCO
315g; D
80(neighbour-hydroxybenzoic acid sodium) 2.5g.Window dressing face fabric is being checked through cloth inspecting machine illumination, after the arrangement, with the finishing agent of preparing according to the above ratio, finishing agent viscosity is: 1000-3000/Mpa.s, the starching coating is applied on the window dressing face fabric, and temperature is controlled at the oven dry infrared ray tracking after 2-3 minute of heating under 190 ℃ behind the heavy twist, the door width of cloth is in accordance with regulations put burr, packed products in order then.
Embodiment 2
The window dressing face fabric processing agent that present embodiment adopts, every square metre of finishing agent that window dressing face fabric adopts following materials of weight proportions to make: PVC powder (2-methoxyl group-4-nitroaniline) 100g; DOP (dioctyl phthalate) 65g; Ba-Zn (heat stabilizer) 2.5g; Antimony trichloride 10g; CaCO
320g; D
80(neighbour-hydroxybenzoic acid sodium) 3g.Window dressing face fabric is being checked through cloth inspecting machine illumination, after the arrangement, with the finishing agent of preparing according to the above ratio, finishing agent viscosity is: 1000-3000/Mpa.s, the starching coating is applied on the window dressing face fabric, and temperature is controlled at the oven dry infrared ray tracking after 2-3 minute of heating under 175 ℃ behind the heavy twist, the door width of cloth is in accordance with regulations put burr, packed products in order then.
Embodiment 3
The window dressing face fabric processing agent that present embodiment adopts, every square metre of finishing agent that window dressing face fabric adopts following materials of weight proportions to make: PVC powder (2-methoxyl group-4-nitroaniline) 105g; DOP (dioctyl phthalate) 70g; Ba-Zn (heat stabilizer) 3g; Antimony trichloride 15g; CaCO
325g; D
80(neighbour-hydroxybenzoic acid sodium) 3.5g.Window dressing face fabric is being checked through cloth inspecting machine illumination, after the arrangement, with the finishing agent of preparing according to the above ratio, finishing agent viscosity is: 1000-3000/Mpa.s, the starching coating is applied on the window dressing face fabric, and temperature is controlled at the oven dry infrared ray tracking after 2-3 minute of heating under 160 ℃ behind the heavy twist, the door width of cloth is in accordance with regulations put burr, packed products in order then.
Claims (5)
1, a kind of window dressing face fabric processing agent is characterized in that: every square metre of finishing agent that window dressing face fabric adopts following materials of weight proportions to make:
2-methoxyl group-4-nitroaniline PVC powder 95-105g;
DOP?60-70g；
Ba-Zn?2-3g；
Antimony trichloride 5-15g;
CaCO
3?15-25g；
Neighbour-hydroxybenzoic acid sodium D
802.5-3.5g.
2, window dressing face fabric processing agent as claimed in claim 1 is characterized in that: every square metre of finishing agent that window dressing face fabric adopts following materials of weight proportions to make:
2-methoxyl group-4-nitroaniline PVC powder 100g;
DOP?65g；
Ba-Zn?2.5g；
Antimony trichloride 10g;
CaCO
3?20g；
Neighbour-hydroxybenzoic acid sodium D
803g.
3, a kind of using method of window dressing face fabric processing agent as claimed in claim 1, it is characterized in that may further comprise the steps: window dressing face fabric is being checked through cloth inspecting machine illumination, after the arrangement, will be by 2-methoxyl group-4-nitroaniline PVC powder 95-105g, DOP60-70g, Ba-Zn 2-3g, antimony trichloride 5-15g, CaCO
315-25g, neighbour-hydroxybenzoic acid sodium D
802.5-3.5g the finishing agent of ratio preparation, finishing agent viscosity is: 1000-3000/Mpa.s, starching coating, be applied on the window dressing face fabric, the infrared ray of heating at a certain temperature behind the heavy twist after oven dry a period of time is followed the tracks of, door width of cloth arrangement burr in accordance with regulations then, packed products.
4, the using method of window dressing face fabric processing agent as claimed in claim 3 is characterized in that: described temperature is controlled at 160-190 ℃.
5, the using method of window dressing face fabric processing agent as claimed in claim 3 is characterized in that: described drying time is 2-3 minute.