CN100495772C - 一种镍氢或镍镉电池正极板的制作工艺 - Google Patents

一种镍氢或镍镉电池正极板的制作工艺 Download PDF

Info

Publication number
CN100495772C
CN100495772C CNB2007100280619A CN200710028061A CN100495772C CN 100495772 C CN100495772 C CN 100495772C CN B2007100280619 A CNB2007100280619 A CN B2007100280619A CN 200710028061 A CN200710028061 A CN 200710028061A CN 100495772 C CN100495772 C CN 100495772C
Authority
CN
China
Prior art keywords
nickel
positive plate
slurry
manufacture craft
hour
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2007100280619A
Other languages
English (en)
Other versions
CN101071856A (zh
Inventor
郭楚义
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2007100280619A priority Critical patent/CN100495772C/zh
Publication of CN101071856A publication Critical patent/CN101071856A/zh
Application granted granted Critical
Publication of CN100495772C publication Critical patent/CN100495772C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种镍氢或镍镉电池正极板的制作工艺，其工艺步骤如下：1.将基于浆料总量的质量百分比分别为：40～50%的氢氧化亚镍，2～5%的氧化亚钴，10～20%的石墨均匀搅拌在一起，然后加入15～20%的粘合剂以及8～15%的纯净水在常温下均匀搅拌为正极板浆料；2.使用拉浆炉将浆料涂覆在镀镍钢网上，拉浆炉的烘干温度为100～140℃，拉浆速度为80～100m/小时；3.采用压滚机将烘干后的极板进行碾压，碾压间隙为：0.4～0.7mm，牵引速度为80～100m/小时；4.采用裁片机，裁出固定尺寸的正极板；5.在正极板上焊接正极极耳；本发明采用钢网作导电骨架，进行流水线生产，生产效率高、工艺简单。

Description

一种镍氢或镍镉电池正极板的制作工艺
技术领域
本发明涉及一种电池正极板的制作工艺，特别是一种镍氢或镍镉电池正极板的制作工艺
背景技术
目前碱性镍氢或镍镉二次电池充放电过程中，通常使用泡沫镍板作为电池正极板的骨架材料，泡沫镍板是塑料泡沫经过镀镍处理形成的镍纤维状泡沫体，它具有均匀、密实且相互关连的空间和通道，是填充镍活性物质的理想载体，可是由于泡沫镍的状态为纤维状的泡沫体，所以极耳的焊接较困难；另外，金属镍的价格较高，从而导致电池成本提高。
发明内容
为了克服现有技术的不足，本发明提供一种制造成本低，强度高，工艺简单的镍氢或镍镉电池正极板的制作工艺。
本发明解决上述技术问题所采用的技术方案是：
一种镍氢或镍镉电池正极板的制作工艺，其工艺步骤如下：
(1)将基于浆料总量的质量百分比分别为：40～50％的氢氧化亚镍，2～5％的氧化亚钴，10～20％的石墨均匀搅拌在一起，然后加入15～20％的粘合剂以及8～15％纯净水在常温下均匀搅拌为正极板浆料；
(2)使用拉浆炉将浆料涂覆在厚度为：0.2～1.0mm的镀镍钢网上，拉浆炉的烘干温度为100～140℃，拉浆速度为80～100m/小时；
(3)采用压滚机将烘干后的极板进行碾压，碾压间隙为：0.4～0.7mm，牵引速度为80～100m/小时；
(4)采用裁片机，裁出固定尺寸的正极板；
(5)在正极板上焊接正极极耳。
本发明的有益效果是：本发明采用镀镍钢带或钢网作导电骨架，进行流水线生产，提高了生产效率，提高了镍的利用率，降低了成本，生产效率高，且工艺简单，从而可以广泛应用于镍氢或镍镉电池的正极板制作上。
具体实施方式
一种镍氢或镍镉电池正极板的制作工艺，其工艺步骤如下：
1)将基于浆料总量的质量百分比分别为：40～50％的氢氧化亚镍，2～5％的氧化亚钴，10～20％的石墨均匀搅拌在一起，然后加入15～20％的粘合剂以及8～15％纯净水在常温下均匀搅拌为正极板浆料；
2)使用拉浆炉将浆料涂覆在厚度为：0.2～1.0mm的镀镍钢网上，拉浆炉的烘干温度为100～140℃，最佳的烘干温度为120℃；拉浆速度为80～100m/小时，最佳的拉浆速度为90m/小时；
3)采用压滚机将烘干后的极板进行碾压，碾压间隙为：0.4～0.7mm；实际碾压间隙按照实际产品要求为准；
4)采用裁片机，裁出固定尺寸的正极板；
5)在正极板上焊接正极极耳。
实施例1：
一种使用镀镍钢带制作镍氢或镍镉电池正极板的制作工艺，其工艺步骤如下：
1、将基于浆料总量的质量百分比分别为：48％的氢氧化亚镍，5％的氧化亚钴，18％的石墨均匀搅拌在一起，然后加入18％的粘合剂以及11％纯净水在常温下均匀搅拌为正极板浆料；
2、使用拉浆炉将浆料涂覆在厚度为：0.2～1.0mm的镀镍钢网上，钢网厚度按照客户要求而定，拉浆炉的烘干温度为120℃，拉浆速度为90m/小时；
3、采用压滚机将烘干后的极板进行碾压，碾压间隙为：0.4～0.7mm；实际碾压间隙按照实际产品要求为准；
4、采用裁片机，裁出固定尺寸的正极板；
5、在正极板上焊接正极极耳。
实施例2：
一种使用镀镍钢网制作镍氢或镍镉电池正极板的制作工艺，其工艺步骤如下：
1、将基于浆料总量的质量百分比分别为：50％的氢氧化亚镍，5％的氧化亚钴，19％的石墨均匀搅拌在一起，然后加入17％的粘合剂以及9％纯净水在常温下均匀搅拌为正极板浆料；
2、使用拉浆炉将浆料涂覆在厚度为：0.2～1.0mm的镀镍钢网上，钢网厚度按照客户要求而定，拉浆炉的烘干温度为120℃，拉浆速度为90m/小时；
3、采用压滚机将烘干后的极板进行碾压，碾压间隙为：0.4～0.7mm；实际碾压间隙按照实际产品要求为准；
4、采用裁片机，裁出固定尺寸的正极板；
5、在正极板上焊接正极极耳。
本发明采用钢网作导电骨架，进行流水线生产，提高了生产效率，提高了镍的利用率，降低了成本，生产效率高，且工艺简单，从而可以广泛应用于镍氢或镍镉电池的正极板制作上。

Claims (6)

1.一种镍氢或镍镉电池正极板的制作工艺，其特征在于，工艺步骤如下：
(1)将基于浆料总量的质量百分比分别为：40～50％的氢氧化亚镍，2～5％的氧化亚钴，10～20％的石墨均匀搅拌在一起，然后加入15～20％的粘合剂以及8～15％纯净水在常温下均匀搅拌为正极板浆料；
(2)使用拉浆炉将浆料涂覆在厚度为：0.2～1.0mm的镀镍钢网上，拉浆炉的烘干温度为100～140℃，拉浆速度为80～100m/小时；
(3)采用压滚机将烘干后的极板进行碾压，碾压间隙为：0.4～0.7mm，牵引速度为80～100m/小时；
(4)采用裁片机，裁出固定尺寸的正极板；
(5)在正极板上焊接正极极耳。
2.根据权利要求1所述的一种镍氢或镍镉电池正极板的制作工艺，其特征在于：在步骤(1)所述的氢氧化亚镍为47％，氧化亚钴为4％，石墨为17％。
3.根据权利要求1所述的一种镍氢或镍镉电池正极板的制作工艺，其特征在于：在步骤(1)所述的粘合剂为17％，纯净水为15％。
4.根据权利要求1所述的一种镍氢或镍镉电池正极板的制作工艺，其特征在于：在步骤(2)所述的烘干温度为120℃。
5.根据权利要求1所述的一种镍氢或镍镉电池正极板的制作工艺，其特征在于：在步骤(2)所述的拉浆速度为90m/小时。
6.根据权利要求1所述的一种镍氢或镍镉电池正极板的制作工艺，其特征在于：在步骤(3)所述的牵引速度为90m/小时。
CNB2007100280619A 2007-05-18 2007-05-18 一种镍氢或镍镉电池正极板的制作工艺 Expired - Fee Related CN100495772C (zh)