CN100462464C - 铝钙硅铁合金 - Google Patents
铝钙硅铁合金 Download PDFInfo
- Publication number
- CN100462464C CN100462464C CNB200610040963XA CN200610040963A CN100462464C CN 100462464 C CN100462464 C CN 100462464C CN B200610040963X A CNB200610040963X A CN B200610040963XA CN 200610040963 A CN200610040963 A CN 200610040963A CN 100462464 C CN100462464 C CN 100462464C
- Authority
- CN
- China
- Prior art keywords
- calcium
- aluminium
- silicon
- steel
- ferro
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种主要用于精炼钢脱氧脱硫处理的铝钙硅铁合金,含有铝、钙、硅、铁,以其各组分重量百分含量铝28~35%,钙17~25%,硅14~17%,铁为余量为主要特征,本发明与公知技术相比,具有脱氧脱硫能力更强,脱氧脱硫速度更快,能够达到深度脱氧脱硫,能够适用于低硅钢种钢液的精炼处理等特点。
Description
技术领域
本发明涉及一种主要用于精炼钢脱氧脱硫处理的铝钙硅铁合金。
背景技术
石灰石形态钙,是钢铁冶炼过程中配入的一种碱性炉料。而用钙来处理钢液则是钢液脱氧的一种重要手段,更为重要的是用钙脱硫也可以取得显著的效果。现在,钙已成为控制钢液中的氧化物和硫化物夹杂形态、大小和分布状态的常用添加剂。经过钙处理的钢液,不但流动性好,而且有效减少了连铸中可能出现的诸如水口不畅甚至阻塞的问题,提高了最终产品的洁净度、机械加工性、延展性和耐冲击强度。
钙的脱氧能力很强,但在炼钢温度下的钙蒸气压非常高,而且钙在钢液中的溶解度很小。因此,用单一的钙脱氧损耗太大。为了提高钙的脱氧能力,通常钙是以比较稳定的硅钙、铝钙、硅钙锰、硅钙钡和硅钙铝等二元或多元合金形式加到钢液中去的。常用的是硅钙、铝钙和铝钙硅合金。
由于铝钙硅合金可以部分克服钙硅合金脱氧所产生的脱氧速度慢,所得的夹杂物是细小球状夹杂物不易从钢液中排除等不足,而在精炼钢脱氧处理中较多地被采用。
公知的铝钙硅铁合金的各组分重量百分含量,在文献中记载的有两种,一种是在合金手册中记载的,其各组分重量百分含量是硅25%,钙18~22%,铝18~22%,铁为余量;另一种是中国专利公开号CN1676623A公布的,其各组分重量百分含量是,硅30~42%,钙6~12%,铝10~28%,铁为余量。上述两种铝钙硅铁合金,由于三元素复合存在,而进一步提高了脱氧能力,加快了脱氧速度,CaO-Al2O3系夹杂物容易聚集长大上浮而排除,因而对改善钢液流动性,降低损耗,提高产品质量都有显著效果。
但是,由于上述公知的铝钙硅铁合金所存的铝、钙含量相对较低,而硅的含量则相对较高的共同特征,因而公知技术均存在着脱氧能力相对较差,脱氧速度相对较慢,深度脱氧不够,尤其是由于其硅含量高,而影响氧化夹杂物排除速度,且不适宜于低硅钢种钢液的精炼脱氧处理。
发明内容
本发明所要解决的技术问题是,提供一种脱氧脱硫能力相对较强,脱氧脱硫速度相对较快,能够达到深度脱氧脱硫,能够满足低硅钢种钢液精炼处理的铝钙硅铁合金,以克服公知技术的不足。
本发明解决其所要解决技术问题的技术方案是:
一种主要用于精炼钢脱氧脱硫处理的铝钙硅铁合金,含有铝、钙、硅、铁,其发明点在于,各组分的重量百分含量是:
铝 28~35%;
钙 17~25%;
硅 14~17%;
铁 余 量。
本发明优选的各组分重量百分含量是:
铝 32~35%;
钙 20~25%;
硅 15~17%;
铁 余 量。
本发明更优选的各组分重量百分含量是:
铝 32%;
钙 20%;
硅 15%;
铁 余量。
本发明由于适当增加了铝、钙含量,从而相对提高了脱氧脱硫能力,能够达到深度脱氧脱硫;加快了脱氧脱硫速度,缩短了钢水脱氧脱硫处理时间,提高了生产效率,且可明显避免由于炉前处理时间长,而降低钢水温度影响连铸过程正常进行问题的发生。同时由于减少了硅含量,可以适用于低硅钢种的精炼处理。
具体实施方式
本发明制备方法的简要描述是,可按照常规的重熔法生产,即根据所要制备本发明的各组分重量百分含量,经过计算后称取各原料,然后分批分时段投加入中频电炉中重熔、铸块即得。
具体实施方式之一,
以每1000Kg炉料计,称取含硅60%含钙30%的硅钙合金258Kg,A00铝锭263Kg,含钙74%铝24.6%的铝钙合金152Kg,废钢327Kg,分批分时段投入中频电炉中重熔即得本发明,所制备的本发明各组分的重量百分含量是:铝28%,钙17%,硅14%,铁为余量。
具体实施方式之二,
以每1000Kg炉料计,称取含硅60%含钙30%的硅钙合金317Kg,A00铝锭313Kg,含钙74%铝24.6%的铝钙合金236Kg,废钢134Kg,分批分时段投入中频电炉中重熔即得本发明,所制备的本发明各组分的重量百分含量是:铝35%,钙25%,硅17%,铁为余量。
具体实施方式之三,
以每1000Kg炉料计,称取含硅60%含钙30%的硅钙合金283Kg,A00铝锭296Kg,含钙74%铝24.6%的铝钙合金183Kg,废钢238Kg,分批分时段投入中频电炉中重熔即得本发明,所制备的本发明各组分的重量百分含量是:铝32%,钙20%,硅15%,铁为余量。
本发明由于含铝量较高,为了避免可能产生的粉化,应当采取防粉化措施。
本发明初样在感应炉炼钢作盛钢桶钢液精炼脱氧脱硫处理,经过9炉次的试验,本发明与采用公知技术相比较,其脱氧脱硫能力平均提高12%,脱氧脱硫处理时间平均缩短10秒钟。经处理后钢的洁净度,机械加工性能,延展性和耐冲击强度,都有明显的提高,试验结果显示,本发明尤其适宜于具有优良延展性的低硅钢种钢液的精炼处理,特别适宜于轿车钢板钢液的精炼处理。
Claims (3)
1.一种主要用于精炼钢脱氧脱硫处理的铝钙硅铁合金,含有铝、钙、硅、铁,其特征在于:各组分的重量百分含量是:
铝 28~35%;
钙 17~25%;
硅 14~17%;
铁 余量。
2.根据权利要求1所述的铝钙硅铁合金,其特征在于:各组分的重量百分含量是:
铝 32~35%;
钙 20~25%;
硅 15~17%;
铁 余量。
3.根据权利要求2所述的铝钙硅铁合金,其特征在于:各组分的重量百分含量是:
铝 32%;
钙 20%;
硅 15%;
铁 余量。