CN100457941C - Production method of 5754 aluminum alloy blank using cast rolling machine - Google Patents
Production method of 5754 aluminum alloy blank using cast rolling machine Download PDFInfo
- Publication number
- CN100457941C CN100457941C CNB2006101638797A CN200610163879A CN100457941C CN 100457941 C CN100457941 C CN 100457941C CN B2006101638797 A CNB2006101638797 A CN B2006101638797A CN 200610163879 A CN200610163879 A CN 200610163879A CN 100457941 C CN100457941 C CN 100457941C
- Authority
- CN
- China
- Prior art keywords
- refining
- aluminium
- casting
- rolling machine
- aluminium liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a manufacturing method of 5754 aluminium alloy blank through casting machine, which comprises the following steps: fusing alloy aluminium liquid; refining; filtering; casting; obtaining the cast coil or board.
Description
Technical field
The present invention relates to the aluminium processing technique field, specifically utilize casting and rolling machine to produce the production method of 5754 aluminum alloy blanks.
Background technology
At present; ingot casting hot rolling and two kinds of production methods of Hezlet are generally adopted in the production of 5754 aluminum alloy blanks; these two kinds of method facility investments are huge; technical requirements and production cost are higher; especially ingot casting hot rolling method is all very high aspect energy consumption and production cost; and the handiness of producing is relatively poor, relatively is fit to large-scale production in batches.Original ingot casting hot rolling production technique is: melting → refining → ingot casting → homogenizing sawing → mill face → heating → hot rolling → batch → detect → finished product.
Summary of the invention
The purpose of this invention is to provide a kind ofly can reduce production costs, the energy that economizes on resources, shorten the production cycle, the convenient casting and rolling machine of producing that utilizes produces the production method of 5754 aluminum alloy blanks.
Technical scheme of the present invention is to utilize casting and rolling machine to produce 5754 aluminum alloy blanks, and its production technique is as follows: alloy aluminum liquid through melting, concise, grain refining, filtration after, enter the casting and rolling machine casting and produce casting volume or plate.
Operational path:
Melting → refining → casting → batch → detect → finished product
Concrete production method is:
Electrolytic aluminium liquid, aluminium ingot or processing waste (aluminium waste) and high pure magnesium ingot, wherein about 70~80%, aluminium ingot of electrolytic aluminium liquid or processing waste 20~30%, high pure magnesium ingot 3.2%, after adding the smelting furnace fusing, detect chemical ingredients, Mg content is controlled in 2.8~3.2% scopes in the chemical ingredients, after chemical ingredients is qualified, carry out furnace refining, feed high-purity N
2(purity 99.999%) and refining agent (addition be aluminium liquid total amount 1~2%) carry out refining, and refining temperature enters then and leaves standstill stove below 750 ℃, add grain-refining agent aluminium titanium boron wire (addition is 1.5~2%), carry out grain refining, online N
2(purity 99.999%) degasification, filtration, casting and rolling machine are rolling, 670~685 ℃ of preceding oven temperature, degree, and roll speed is 0.7~0.8m/min, batches then, checks, and can become the work in-process of finished product or next procedure.
The mechanical property of product of the present invention:
State | Tensile strength (MPa) | Unit elongation (%) |
O | 190~205 | ≥12 |
H24 | 240~285 | ≥6 |
H18 | ≥320 | ≤3 |
The positively effect that the present invention brought is: reduce by 600~800 yuan/ton than existing ingot casting hot-rolling method production cost; Product performance are near hot-rolled product, and its Production Flow Chart is short, and energy consumption is low, and cost is low, yield rate is high, and production method is easy.
Embodiment
Embodiment 1:
In furnace, add electrolytic aluminium liquid 80%, aluminium ingot 20% (or aluminium waste) and high pure magnesium ingot (addition 3.2%), in melting below 750 ℃, chemical ingredients detects then, and Mg content is controlled in 2.8~3.2% scopes, after reaching the requirement of 5754 alloying constituents, feed high-purity N
2(purity 99.999%, press the ordinary method operation on the technical manual) and the refining agent (trade(brand)name of aluminium liquid total amount 2%, the Institute for Applied Technology provides by Wuhua, Kunming, its major ingredient be sodium-chlor salt such as Repone K) carry out refining, enter (12 tons) and leave standstill stove, add grain-refining agent aluminium titanium boron wire (aluminium liquid total amount 2%), carry out refinement, online N
2Degasification, filtration are used
Casting and rolling machine rolls and is rolled, and preceding oven temperature, degree is 670~685 ℃, and roll speed is 0.76m/min, in mill roll-gap through the successive condensation and rolling after produce casting volume or plate, through check finished product.
Embodiment 2:
In furnace, add electrolytic aluminium liquid 70%, aluminium ingot 30% (or aluminium waste) and high pure magnesium ingot (addition 3.0%), in melting below 750 ℃, chemical ingredients detects then, and Mg content is controlled in 2.8~3.0% scopes, after reaching the requirement of 5754 alloying constituents, feed high-purity N
2Refining agent (the trade(brand)name of (purity 99.999%) and aluminium liquid total amount 1%, the Institute for Applied Technology provides by Wuhua, Kunming, its major ingredient be sodium-chlor salt such as Repone K) carry out refining, enter (12 tons) and leave standstill stove, add grain-refining agent aluminium titanium boron wire (aluminium liquid total amount) 1.5%, carry out refinement, online N
2Degasification, filtration are used
Casting and rolling machine rolls and is rolled, and preceding oven temperature, degree is 670~685 ℃, and roll speed is 0.76m/min, in mill roll-gap through the successive condensation and rolling after produce casting volume or plate, through check finished product.
Claims (1)
1. production method of utilizing casting and rolling machine to produce 5754 aluminum alloy blanks, it is characterized in that technological process is: after electrolytic aluminium liquid 70~80%, aluminium ingot or processing waste 20~30% and the 3.2% adding smelting furnace fusing of high pure magnesium ingot, detect chemical ingredients, Mg content is controlled in 2.8~3.2% scopes in the chemical ingredients, carry out furnace refining then, feed high-purity N
2With addition be that 1~2% refining agent of aluminium liquid total amount carries out refining, refining temperature is below 750 ℃; Enter then and leave standstill stove, add the grain-refining agent aluminium titanium boron wire, its addition is 1.5~2% of an aluminium liquid total amount, carries out grain refining, online N
2Degasification, filtration, casting and rolling machine are rolling, 670~685 ℃ of preceding oven temperature, degree, and roll speed is 0.7~0.8m/min, batches then, checks, and can become the work in-process of finished product or next procedure.