CN100374239C - 修复管模用的烧结焊剂及其制造方法 - Google Patents
修复管模用的烧结焊剂及其制造方法 Download PDFInfo
- Publication number
- CN100374239C CN100374239C CNB2005100475618A CN200510047561A CN100374239C CN 100374239 C CN100374239 C CN 100374239C CN B2005100475618 A CNB2005100475618 A CN B2005100475618A CN 200510047561 A CN200510047561 A CN 200510047561A CN 100374239 C CN100374239 C CN 100374239C
- Authority
- CN
- China
- Prior art keywords
- ferro
- molybdenum
- sintered flux
- titanium
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明属于焊接材料领域,特别是一种修复管模用的烧结焊剂及其制造方法,烧结焊剂由下述重量百分比的组分所组成:三氧化二铝15-18,氧化镁25,氧化钙7-8,二氧化硅12-13,氟化钙22-25,锰铁合金4-4.5,铬或铬铁合金5-6,钼铁合金1.0-1.2,镍0.2-0.3,钛铁合金3.8-4,其制造方法步骤包括原料质量检验,按重量百分比配料,干混,加20-30%水湿混,造粒后在600-750℃烘干,10-60目筛分得到灰黄色成品烧结焊剂。利用本发明的烧结焊剂对铸铁管模进行整体堆焊所得的堆焊金属成分为:碳≤0.12%,锰为0.4-0.8%,硅为0.40-0.80%,铬为2.0-3.0%,钼为0.30-0.60%,镍约0.10%,铜约0.10%,钛约0.10%,硫、磷≤0.03,其抗烈、耐磨、抗氧化性能优良,线膨胀系数小。
Description
技术领域
本发明属于焊接材料领域,特别是一种修复管模用的烧结焊剂及其制造方法,用于整体堆焊修复管模。
背景技术
管模是离心浇铸机生产大型铸管的主要工具。在离心浇铸机生产大型铸管的过程中,管模反复在高温条件下工作。在如此恶劣条件下工作的管模为在其内壁形成大量热裂纹(龟裂)而造成破坏,因此是一种易损料,其消耗量非常大(每只新管模价值40-50万元)。为了降低生产成本,提高经济效益,要采用整体堆焊技术对其进行修复,以供反复使用。用堆焊方法对管模进行整体修复,除了要有合适的工具外,主要是要用适当的焊剂,使堆焊层能满足管模的工作要求,也就是要有专用的烧结焊剂。
发明内容
本发明的目的是提供一种修复管模用的烧结焊剂及其制造方法。
本发明的目的是通过下述技术方案来实现的。
按照本发明的修复管模用的烧结焊剂,其特征在于由下列重量百分比的组分所组成:
三氧化二铝 15-18
氧化镁 25
氧化钙 7-8
二氧化硅 12-13
氟化钙 22-25
锰铁合金 4-4.5
铬或铬铁合金 5-6
钼铁合金 1.0-1.2
镍 0.2-0.3
钛铁合金 3.8-4。
所述的锰铁合金为含锰75-85%的中碳锰铁合金,所述的铬铁合金为含铬量为68-75%的铬铁合金,所述的钼铁合金为含钼量为55-65%的钼铁合金,所述的钛铁合金为含钛量为25-35%的钛铁合金。
本发明的修复管模用的烧结焊剂的制造方法,其特征在于包括下列步骤:
1)对所述的各种组分原料进行质量检验,
2)按照所述的组分重量比进行配料,
3)进行混料,先进行干混,在加入原料重量比为20-30%的水进行湿混,
4)在造粒机上造粒,制造出粒度为2.0-0.28mm的圆形颗粒,
5)在600-750℃温度下进行烘干,
6)用10-60目筛进行筛分后获得灰黄色成品烧结焊剂。
用本发明的修复管模的烧结焊剂修复的管模,经反复实践试验应用,结果显示其有如下的特点:
1、抗热裂性能良好;
2、具有良好的耐磨性能和抗氧化性能;
3、线膨胀系数小;
4、开裂和变形倾向小。
因此是一种很有推广价值的修复管模用的烧结焊剂。
检验结果证明,用本发明的烧结焊剂堆焊所得到的堆焊金属成分为:碳≤0.12%,锰为0.4-0.8%,硅为0.40-0.80%,铬为2.0-3.0%,钼为0.30-0.60%,镍约0.10%,铜约0.10%,钛约0.10%,硫≤0.03,磷≤0.03,余量为铁。其中的硫、铜、磷来自各种铁合金中的微量残留。
具体实施方式
下面用实施例来说明本发明的具体实施方式。
实施例1
修复管模用的烧结焊剂,由下列重量百分比的组分所组成:
三氧化二铝 15
氧化镁 25
氧化钙 8
二氧化硅 12
氟化钙 25
含锰量80%的锰铁合金 4.5
铬 5.0
含钼量60%的钼铁合金 1.2
镍 0.3
含钛量30%的钛铁合金 4。
将上述组分的材料干混后加入20-30%的水混合均匀后造粒,在600-750℃温度下烘干,用10-60目筛子进行筛分,经检验获得合格的成品。
实施例2
修复管模用的烧结焊剂,由下列重量百分比的组分所组成:
三氧化二铝 18
氧化镁 25
氧化钙 7
二氧化硅 13
氟化钙 22
含锰量80%的中碳锰铁 4.0
含铬72%的铬铁合金 6.0
含钼量60%的钼铁合金 1.0
镍 0.2
含钛量30%的钛铁合金 3.8。
制作方法同实施例1。
Claims (5)
1.一种修复管模用的烧结焊剂,其特征在于由下列重量百分比的组分所组成:
三氧化二铝 15-18
氧化镁 25
氧化钙 7-8
二氧化硅 12-13
氟化钙 22-25
锰铁合金 4-4.5
铬或铬铁合金 5-6
钼铁合金 1.0-1.2
镍 0.2-0.3
钛铁合金 3.8-4。
2.根据权利要求1所述的修复管模用的烧结焊剂,其特征在于所述的锰铁合金为含锰75-85%的中碳锰铁合金,所述的铬铁合金为含铬量为68-75%的铬铁合金,所述的钼铁合金为含钼量为55-65%的钼铁合金,所述的钛铁合金为含钛量为25-35%的钛铁合金。
3.根据权利要求1所述的修复管模用的烧结焊剂,其特征在于由下列重量百分比的组分所组成:
三氧化二铝 15
氧化镁 25
氧化钙 8
二氧化硅 12
氟化钙 25
含锰量80%的锰铁合金 4.5
铬 5.0
含钼量60%的钼铁合金 1.2
镍 0.3
含钛量30%的钛铁合金 4
4.根据权利要求1所述的修复管模用的烧结焊剂,其特征在于由下列重量百分比的组分所组成:
三氧化二铝 18
氧化镁 25
氧化钙 7
二氧化硅 13
氟化钙 22
含锰量80%的中碳锰铁 4.0
含铬72%的铬铁合金 6.0
含钼量60%的钼铁合金 1.0
镍 0.2
含钛量30%的钛铁合金 3.8。
5.根据权利要求1、3、4所述的修复管模用的烧结焊剂的制造方法,其特征在于包括下列步骤:
1)对所述的各种组分原料进行质量检验,
2)按照所述的组分重量比进行配料,
3)进行混料,先进行干混,在加入原料重量比为20-30%的水进行湿混,
4)在造粒机上造粒,制造出粒度为2.0-0.28mm的圆形颗粒,
5)在600-750℃温度下进行烘干,
6)用10-60目筛进行筛分后获得灰黄色成品烧结焊剂。