CN100360624C - 水性金属漆及其制备方法 - Google Patents
水性金属漆及其制备方法 Download PDFInfo
- Publication number
- CN100360624C CN100360624C CNB2006100072113A CN200610007211A CN100360624C CN 100360624 C CN100360624 C CN 100360624C CN B2006100072113 A CNB2006100072113 A CN B2006100072113A CN 200610007211 A CN200610007211 A CN 200610007211A CN 100360624 C CN100360624 C CN 100360624C
- Authority
- CN
- China
- Prior art keywords
- water
- paint
- silicon
- based metal
- metallic paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种水性金属漆及其制备方法,属于环保型漆领域。本发明的水性金属漆由以下原料组成,聚羧酸钠、甲氨基丙醇、防腐杀菌剂、防霉剂、矿物油硅、珠光颜料,硅丙烯酸聚合物、十二碳酯醇、丙烯酸酯、非离子聚氨酯、水;本发明的水性金属漆是经过预分散、中速分散聚合和增稠调漆三阶段制备而成。本发明的水性金属漆耐候性能、耐水性能、耐擦洗性能优越,施工适宜的温度范围宽,其色彩鲜亮且丰富,环保无污染、便于翻新维修,减少施工成本。适用于建筑外墙、混凝土梁柱构件、石板、石柱等砖、混凝土、水泥、石头、石棉等基面保护及装饰用。
Description
技术领域:
本发明涉及一种水性金属漆及其制备方法,属于环保型漆领域。
背景技术:
常规水性建筑涂料是靠添加色浆来改变其色泽,添加的色浆越多对涂料的成本和品质都会有很大的影响,保色性和室外耐候性一般在三年就会出现退色粉化等问题,这种涂料不具有金属闪光效果,只适用于内外墙的普通装饰效果。现有技术中也有水性金属漆,解决了上述的部分问题,但是大多采用钛白粉(TiO)会对水性金属漆的金属光泽有很大的影响,使金属光泽降低,另外在分散时需要高速分散。
发明内容:
本发明的目的是提供一种水性金属漆,这种金属漆不但耐候性、耐沾污、耐水性、耐擦洗性能优越,金属光泽好。
本发明的另一个目的是提供这种水性金属漆的制备方法。
为达到上述的目的,本发明的技术方案如下:本发明的水性金属漆由以下重量百分含量的原料组成,聚羧酸钠0.1%-0.5%、甲氨基丙醇0.1%-0.2%、防腐杀菌剂0.1%-0.2%、防霉剂0.2%-0.6%、矿物油硅0.1%-0.4%、珠光颜料10.5%-14.5%,硅丙烯酸聚合物44.7%-48.7%、十二碳酯醇1.0%-1.4%、丙烯酸酯0.6%-1.3%、非离子聚氨酯0.1%-0.4%、水33.36%-41.36%。
本发明水性金属漆的原料优选的重量百分含量为:聚羧酸钠0.3%、甲氨基丙醇0.12%、防腐杀菌剂0.12%、防霉剂0.4%、矿物油硅0.2%、珠光颜料12.5%,硅丙烯酸聚合物46.7%、十二碳酯醇1.2%、丙烯酸酯0.9%、非离子聚氨酯0.2%、水37.36%。
本发明水性金属漆的制备方法依次包括如下步骤:
(1)预分散
将所述配比的防腐杀菌剂、甲氨基丙醇和所述水的总量的91%混合进行低速分散3分钟,转速为150转/分,除去水中的细菌,得到预分散产物,PH=8-9;
(2)中速分散聚合
将所述配比的聚羧酸钠、矿物油硅、防霉剂、珠光颜料和硅丙烯酸聚合物加入到上述预分散产物中,进行中速分散聚合,转速为400转/分、分散时间10分钟、操作温度为30℃-40℃,得到中速分散聚合产物;
(3)增稠调漆
在上述中速分散聚合产物中加入所述配比的十二碳酯醇、丙烯酸酯和所述剩余的9%的水,将转速提高到500转/分,加入所述配比的非离子聚氨酯,将粘度调节为96KU,分散10分钟,即得水性金属漆成品。
本发明的水性金属漆适用于建筑外墙、混凝土梁柱构件、石板、石柱等砖、混凝土、水泥、石头、石棉等基面保护及装饰用。
综合起来可以得出,本发明具有以下特点:
1、本发明采用低速分散、有机聚合的原理来生产,减去了常用的砂磨高速分散环节,降低了生产成本,只是乳胶漆生产时间和工序的一半。
2、本发明产品是通过珠光颜料来体现的,不同于原来使用的矿物原料或色浆,既能达到闪光的效果又不褪色。
3、本发明的水性金属漆,涂于墙壁具有防尘、防污,用水冲洗或雨淋后不易变色,具有优异的防水透气性能涂层具有小于3A的毛细孔,可平衡墙体与外界的环境的湿度、温度及气压所引起的差异,涂层既防水又透气,并且不影响涂层的附着力,涂层不开裂、不起泡、不脱落。
4、本发明产品采用的原料全部为环保型产品。产品的VOC含量远远低于国家标准,是目前唯一可兼具水性环保涂料和溶剂型金属闪光涂料两种功能的新型特殊产品。
以下实施例用于进一步详细说明本发明,但非限定本发明。
具体实施方式
实施例1
原料的重量百分含量为:聚羧酸钠0.3%、甲氨基丙醇0.12%、异噻唑啉酮0.12%、唑啉酮0.4%、矿物油硅0.2%、珠光颜料12.5%,硅丙烯酸聚合物46.7%、十二碳酯醇1.2%、丙烯酸酯0.9%、非离子聚氨酯0.2%、水37.36%。所用原料的来源及规格如表1
表1原料来源及规格型号
阶段 | 原料 | 生产厂家 | 规格型号 |
预分散 | 水 | / | / |
异噻唑啉酮 | 日本诺普科化工公司 | 防腐杀菌剂LXE | |
甲氨基丙醇 | 美国陶氏化工公司 | 多功能助剂AMP-P5 | |
中速分散聚合 | 聚羧酸钠 | 美国罗门哈斯化工公司 | 分散剂SN5040 |
唑啉酮 | 美国罗门哈斯化工公司 | 防霉剂CD | |
矿物油硅 | 日本诺普科化工公司 | 消泡剂8034 | |
珠光颜料 | 浙江坤威颜料化工公司 | / | |
硅丙烯酸聚合物 | 马来西亚利富达化工公司 | 乳液 | |
增稠调漆 | 十二碳酯醇 | 美国罗门哈斯化工公司 | 成膜助剂CS-12 |
丙烯酸酯 | 美国罗门哈斯化工公司 | 增稠剂TTP35 | |
非离子聚氨酯 | 美国罗门哈斯化工公司 | 流平剂M2020 | |
水 | / | / | |
丙烯酸酯 | 美国罗门哈斯化工公司 | 增稠剂TTP35 |
本发明金属漆的制备方法依次包括如下步骤:
(1)预分散
将所述配比的异噻唑啉酮、甲氨基丙醇和所述水的总量的91%混合进行低速分散3分钟,转速为150转/分,除去水中的细菌,得到预分散产物,PH=8-9;
(2)中速分散聚合
将所述配比的聚羧酸钠、矿物油硅、唑啉酮、珠光颜料和硅丙烯酸聚合物加入到上述预分散产物中,进行中速分散聚合,转速为400转/分、分散时间10分钟、操作温度为30℃-40℃,得到中速分散聚合产物;
(3)增稠调漆
在上述中速分散聚合产物中加入所述配比的十二碳酯醇、丙烯酸酯和所述剩余的9%的水,将转速提高到500转/分,加入所述配比的非离子聚氨酯,将粘度调节为96KU,分散10分钟,即得水性金属漆成品。
对上述实施例中制得的水性金属漆根据国家标准进行技术参数测定,测定结果如表2
项目 | 实施例1试样 |
表干耐候性耐水性耐擦洗性施工性环保性能 | 20分钟耐盐雾试验1000小时,相当于室外10年以上180小时无粉化、无变色、无异常8000次以上可在5℃-40℃之间施工不含有害物质 |
由测定结果表明,本发明的水性金属漆耐候性能、耐水性能、耐擦洗性能优越,施工适宜的温度范围宽,其色彩鲜亮且丰富,环保无污染、便于翻新维修,减少施工成本。
Claims (3)
1、一种水性金属漆,其特征在于:它由以下重量百分含量的原料组成,聚羧酸钠0.1%-0.5%、甲氨基丙醇0.1%-0.2%、防腐杀菌剂0.1%-0.2%、防霉剂0.2%-0.6%、矿物油硅0.1%-0.4%、珠光颜料10.5%-14.5%,硅丙烯酸聚合物44.7%-48.7%、十二碳酯醇1.0%-1.4%、丙烯酸酯0.6%-1.3%、非离子聚氨酯0.1%-0.4%、水33.36%-41.36%。
2、如权利要求1所述的水性金属漆,其特征在于:它由以下重量百分含量的原料组成,聚羧酸钠0.3%、甲氨基丙醇0.12%、防腐杀菌剂0.12%、防霉剂0.4%、矿物油硅0.2%、珠光颜料12.5%,硅丙烯酸聚合物46.7%、十二碳酯醇1.2%、丙烯酸酯0.9%、非离子聚氨酯0.2%、水37.36%。
3、如权利要求1或2所述的水性金属漆的制备方法,其特征在于:依次包括如下步骤:
预分散
将所述配比的防腐杀菌剂、甲氨基丙醇和所述水的总量的91%混合进行低速分散3分钟,转速为150转/分,除去水中的细菌,得到预分散产物,PH=8-9;
中速分散聚合
将所述配比的聚羧酸钠、矿物油硅、防霉剂、珠光颜料和硅丙烯酸聚合物加入到上述预分散产物中,进行中速分散聚合,转速为400转/分、分散时间10分钟、操作温度为30℃-40℃,得到中速分散聚合产物;
增稠调漆
在上述中速分散聚合产物中加入所述配比的十二碳酯醇、丙烯酸酯和所述剩余的9%的水,将转速提高到500转/分,加入所述配比的非离子聚氨酯,将粘度调节为96KU,分散10分钟,即得水性金属漆成品。