CN100358984C - Composite calcium sulphonate lubricating grease - Google Patents
Composite calcium sulphonate lubricating grease Download PDFInfo
- Publication number
- CN100358984C CN100358984C CNB2005100470008A CN200510047000A CN100358984C CN 100358984 C CN100358984 C CN 100358984C CN B2005100470008 A CNB2005100470008 A CN B2005100470008A CN 200510047000 A CN200510047000 A CN 200510047000A CN 100358984 C CN100358984 C CN 100358984C
- Authority
- CN
- China
- Prior art keywords
- lubricating grease
- extreme pressure
- acid
- property
- calcium sulfonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to lubricating grease which uses high-viscosity mineral oil as base oil and uses calcium alkylbenzenesulfonate with a high base number, fatty acid, orthoboric acid glacial acetic acid and calcium hydroxide as thickeners, particularly composite calcium sulfonate lubricating grease. The production process of the composite calcium sulfonate lubricating grease comprises: the base oil, the calcium alkylbenzenesulfonate with a high base number, the glacial acetic acid, the orthoboric acid and the calcium hydroxide are added according to the proportion of the specified part by weight to be converted and saponified at the temperature of 100DEGC; then, the fatty acid is added to be compounded, high-temperature compound refining is carried out when the maximum temperature is raised to more than 180DEGC, and an antioxidant, an extreme pressure agent and an oiliness agent are added when the temperature is reduced to 110 DEGC; finally, a homogenizer is used for post-treatment, filtration and packaging. The composite calcium sulfonate lubricating grease has the advantages of outstanding high-temperature property, high shear stability, excellent water resisting property, high extreme pressure property, good adhesion property and good integrative water-proof property. When containing 20% of water, the composite calcium sulfonate lubricating grease has an outstanding anti-rust property and an excellent extreme pressure property to bearings, and the composite calcium sulfonate lubricating grease is suitable for the working condition of rolling mill bearings.
Description
Technical field
The present invention relates to a kind of is base oil with the high viscosity mineral oil, is the lubricating grease of viscosifying agent with high base number calcium alkylbenzenesulfonate, lipid acid, boric acid, glacial acetic acid and calcium hydroxide, composite calcium sulfonate grease lubricant.
Background technology
Fast development along with metallurgical industry, the equipment work condition of Steel Mill is more and more harsher, the equipment bearing of medium-sized factory, bar factory, medium plate mill, hot rolled strip factory mostly at high temperature, at a high speed, move under the environment of heavy loading, Duo Shui, many dirt, this has just proposed higher requirement to the used PERFORMANCE OF GREASES of steel rolling equipment bearing.
The lubricating grease that is used for the steel rolling equipment bearing is many at present based on extreme pressure lithium base fat or extreme pressure compound lithium, but because this lipoid soap structure is limit, fat in use often occurring is washed away by water and runs off or thinning phenomenon, so just brought inconvenience to the user, short as life cycle, stuffing is safeguarded frequent, and bearing causes wearing and tearing because of lacking enough lubricating grease easily, or get rusty because of big entering of water gaging, therefore easily have lubricated accident.So just influenced normal production, the financial loss that causes because of break down maintenance is surprising in Steel Mill.
Summary of the invention
The purpose of this invention is to provide a kind of viscosifying agent is based on the high base number calcium alkylbenzenesulfonate; and with the calcium soap compound lubricating grease composite calcium sulfonate grease lubricant of lipid acid, glacial acetic acid, boric acid; through the evidence of how tame Steel Mill; successfully solved the difficult problem of Steel Mill with fat; it is not thinning that this fat is met water; do not run off; duration of service and maintenance time have been prolonged; to the antirust excellent protection that provides of bearing; wearing and tearing never take place in bearing and influence is produced, to bearing high loading, high temperature, at a high speed, the operating mode of many water is very suitable.
Composite calcium sulfonate grease lubricant, it is characterized in that with the high viscosity Dormant oils be base oil, form compound soap with the high low molecular acid viscosifying agent of high base number calcium alkylbenzenesulfonate and other, add oxidation inhibitor, extreme pressure agent, oiliness improver and make, wherein the weight part proportioning of each composition is as follows:
High viscosity Dormant oils: 42-70
High base number calcium alkylbenzenesulfonate: 10-20
Lipid acid: 10-16
Glacial acetic acid: 3-6
Boric acid: 2-5
Calcium hydroxide: 4.7-9.5
Oxidation inhibitor: 0.5-1
Extreme pressure agent: 3-6
Oiliness improver: 2-4
Described high viscosity Dormant oils is meant the mixing oil of 150BS and 400SN, and its kinematic viscosity of 100 ℃ is 13-20mm
2/ s; Described extreme pressure agent is meant phosphoric acid ester or phosphite ester compound.
Described high base number calcium alkylbenzenesulfonate is meant that code name is the high base number calcium alkylbenzenesulfonate of T106, and market is on sale.
Described lipid acid is meant 12 oxystearic acids, and market is on sale.
Described glacial acetic acid is meant industrial goods, and market is on sale.
Described boric acid is meant industrial goods, and market is on sale.
Described calcium hydroxide is meant industrial goods, and market is on sale.
Described oxidation inhibitor is meant pentanoic.
Described oiliness improver is meant 124 Triazole fatty amine salt compounds.
The production technique of composite calcium sulfonate grease lubricant is: weight part proportioning in accordance with regulations adds base oil, high base number calcium alkylbenzenesulfonate, glacial acetic acid, boric acid and calcium hydroxide and transforms and saponification reaction at 100 ℃, add the compound reaction of lipid acid again, the highest being warmed up to carried out the compound refining of high temperature more than 180 ℃, cool to 110 degree and add oxidation inhibitor, extreme pressure agent, oiliness improver, carry out aftertreatment with clarifixator then, filter packing.Composite calcium sulfonate grease lubricant of the present invention has following advantage;
1) high-temperature behavior is outstanding, and dropping point does not trickle during high temperature up to more than 300 ℃;
2) shear stability is good, 60 ℃ of tumbler tests, and the cone penetration difference is at 5 below the unit, and is not thinning after the work;
3) water repelling property excellence, 79 ℃ of water drench number of dropouts and have only 2%, and it is few to guarantee to run off when big water gaging washes away;
4) extreme pressure property height, four-ball tester PB value can reach more than the 882N, and the PD value can reach more than 4900, is fit to the heavy loading operating mode;
5) adhesion property is good, at moisture 20% o'clock, also has stronger viscosity, makes the grease lubrication function well;
6) comprehensive waterproof is good, and is outstanding to the rustless property of bearing at moisture 20% o'clock, extreme pressure property excellence, the working condition of suitable Steel Mill bearing.
Embodiment
Embodiment 1:
Composite calcium sulfonate grease lubricant is a base oil with the high viscosity Dormant oils, forms compound soap with the high low molecular acid viscosifying agent of high base number calcium alkylbenzenesulfonate and other, adds oxidation inhibitor, extreme pressure agent, oiliness improver and makes, and wherein the weight part proportioning of each composition is as follows:
150BS:34
400SN:36
High base number calcium alkylbenzenesulfonate: 10
12 oxystearic acids: 10
Glacial acetic acid: 3
Boric acid: 4
Calcium hydroxide: 6
Pentanoic: 1
Phosphite ester compound: 3
124 Triazole fatty amine salt compounds: 2
The production technique of composite calcium sulfonate grease lubricant is: weight part proportioning in accordance with regulations adds base oil, high base number calcium alkylbenzenesulfonate, glacial acetic acid, boric acid and calcium hydroxide and transforms and saponification reaction at 100 ℃, add the compound reaction of lipid acid again, the highest being warmed up to carried out the compound refining of high temperature more than 180 ℃, cool to 110 degree and add oxidation inhibitor, extreme pressure agent, oiliness improver, carry out aftertreatment with clarifixator then, filter packing.
Embodiment 2:
Composite calcium sulfonate grease lubricant is a base oil with the high viscosity Dormant oils, forms compound soap with the high low molecular acid viscosifying agent of high base number calcium alkylbenzenesulfonate and other, adds oxidation inhibitor, extreme pressure agent, oiliness improver and makes, and wherein the weight part proportioning of each composition is as follows:
150BS:36
400SN:20
High base number calcium alkylbenzenesulfonate: 15
12 oxystearic acids: 12
Glacial acetic acid: 4
Boric acid: 4
Calcium hydroxide: 7.0
Pentanoic: 0.5
Phosphite ester compound: 4
124 Triazole fatty amine salt compounds: 3
The production technique of composite calcium sulfonate grease lubricant is with embodiment 1.
Embodiment 3:
Composite calcium sulfonate grease lubricant is a base oil with the high viscosity Dormant oils, forms compound soap with the high low molecular acid viscosifying agent of high base number calcium alkylbenzenesulfonate and other, adds oxidation inhibitor, extreme pressure agent, oiliness improver and makes, and wherein the weight part proportioning of each composition is as follows:
150BS:20
400SN:27
High base number calcium alkylbenzenesulfonate: 20
12 oxystearic acids: 16
Glacial acetic acid: 5
Boric acid: 3
Calcium hydroxide: 7.5
Pentanoic: 0.8
Phosphite ester compound: 6
124 Triazole fatty amine salt compounds: 4
The production technique of composite calcium sulfonate grease lubricant is with embodiment 1.
Claims (4)
1, composite calcium sulfonate grease lubricant, it is characterized in that with the high viscosity Dormant oils be base oil, form compound soap with the high low molecular acid viscosifying agent of high base number calcium alkylbenzenesulfonate and other, add oxidation inhibitor, extreme pressure agent, oiliness improver and make, wherein the weight part proportioning of each composition is as follows:
High viscosity Dormant oils: 42-70
High base number calcium alkylbenzenesulfonate: 10-20
Lipid acid: 10-16
Glacial acetic acid: 3-6
Boric acid: 2-5
Calcium hydroxide: 4.7-9.5
Oxidation inhibitor: 0.5-1
Extreme pressure agent: 3-6
Oiliness improver: 2-4
Described high viscosity Dormant oils is meant the mixing oil of 150BS and 400SN, and its kinematic viscosity of 100 ℃ is 13-20mm
2/ s; Described extreme pressure agent is meant phosphoric acid ester or phosphite ester compound.
2, composite calcium sulfonate grease lubricant according to claim 1 is characterized in that described oxidation inhibitor is meant pentanoic.
3, composite calcium sulfonate grease lubricant according to claim 1 is characterized in that described oiliness improver is meant 124 Triazole fatty amine salt compounds.
4, the production technique of the described composite calcium sulfonate grease lubricant of a kind of claim 1, it is characterized in that this technological process is: weight part proportioning in accordance with regulations adds base oil, high base number calcium alkylbenzenesulfonate, glacial acetic acid, boric acid and calcium hydroxide and transforms and saponification reaction at 100 ℃, add the compound reaction of lipid acid again, the highest being warmed up to carried out the compound refining of high temperature more than 180 ℃, cool to 110 degree and add oxidation inhibitor, extreme pressure agent, oiliness improver, carry out aftertreatment with clarifixator then, filter, packing.