CN100357517C - 棉杆蒸煮预处理液 - Google Patents
棉杆蒸煮预处理液 Download PDFInfo
- Publication number
- CN100357517C CN100357517C CNB2005101042924A CN200510104292A CN100357517C CN 100357517 C CN100357517 C CN 100357517C CN B2005101042924 A CNB2005101042924 A CN B2005101042924A CN 200510104292 A CN200510104292 A CN 200510104292A CN 100357517 C CN100357517 C CN 100357517C
- Authority
- CN
- China
- Prior art keywords
- boiling
- present
- cotton stalk
- pretreatment liquid
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种棉杆造纸蒸煮预处理液。本发明的棉杆蒸煮预处理液,其特别之处在于:含有1-5%重量的氢氧化钠,0.01-0.5%重量的硼氢化钠。采用本发明的棉秆蒸煮预处理液对棉秆进行预处理后,与常规蒸煮得到的纸浆相比:细浆得率提高1-6%,白度可以提高8-15%ISO,卡伯值降低了6-10。
Description
(一)所属技术领域
本发明涉及一种造纸蒸煮预处理液,特别涉及一种棉杆造纸蒸煮预处理液。
(二)背景技术
生产漂白棉秆纸浆,用传统蒸煮方法效果不好,难以漂白。采用微生物预处理技术,周期长,成本高。
(三)发明内容
本发明为了克服以上技术的不足,提供了一种棉杆蒸煮预处理液,具有成本低、生产工艺简单、漂白效果好、纸浆得率高的特点。
本发明是通过以下措施来实现的:
本发明涉及一种棉杆蒸煮预处理液,其特别之处在于:含有1-5%重量的氢氧化钠,0.01-0.5%重量的硼氢化钠。
本发明的棉杆蒸煮预处理液,更优选的技术方案为,氢氧化钠含量为1-3%,硼氢化钠含量为0.02-0.2%。
具体使用方法为:蒸煮前将棉秆备料后加入本发明的预处理药液中,在90℃温度下处理30min,然后挤压出预处理药液,再加入常规蒸煮药液(烧碱-蒽醌法和硫酸盐法蒸煮方法均可),进行正常蒸煮。
采用本发明的棉秆蒸煮预处理液对棉秆进行预处理后,与常规蒸煮得到的纸浆相比:细浆得率提高1-6%,白度可以提高8-15%ISO,卡伯值降低了6-10。
(四)具体实施方式
实施例1:
棉杆备料后,加入含有3%重量的氢氧化钠、0.05%重量的硼氢化钠的预处理液中,在90℃温度下处理30min,然后挤压出预处理药液,再加入烧碱-蒽醌蒸煮液中进行蒸煮,再按常规方法制浆。
经测试:细浆得率提高6%,白度可以提高8.2%ISO,卡伯值降低了5.8。(与常规烧碱-蒽醌法蒸煮得到棉秆浆质量相比较,细浆得率35.5%,未漂浆白度19.5%ISO,卡伯值为20.66。下同)。
实施例2:
棉杆备料后,加入含有1%重量的氢氧化钠、0.01%重量的硼氢化钠的预处理液中,在90℃温度下处理30min,然后挤压出预处理药液,再加入烧碱-蒽醌蒸煮液中进行蒸煮,再按常规方法制浆。
经测试:细浆得率提高4%,白度可以提高7.2%ISO,卡伯值降低了7.8。
实施例3:
棉杆备料后,加入含有4%重量的氢氧化钠、0.4%重量的硼氢化钠的预处理液中,在90℃温度下处理30min,然后挤压出预处理药液,再加入烧碱-蒽醌蒸煮液中进行蒸煮,再按常规方法制浆。
经测试:细浆得率提高1%,白度可以提高13.2%ISO,卡伯值降低了9.8。
实施例4:
棉杆备料后,加入含有2%重量的氢氧化钠、0.05%重量的硼氢化钠的预处理液中,在90℃温度下处理30min,然后挤压出预处理药液,再加入硫酸盐法蒸煮液中进行蒸煮,再按常规方法制浆。细浆得率40.2%,未漂浆白度35.7%ISO,卡伯值12.15。(常规硫酸盐法蒸煮得到棉秆浆质量:细浆得率38.5%,未漂浆白度20.2%ISO,卡伯值15.65。)
Claims (2)
1.一种棉杆蒸煮预处理液,其特征在于:是由1-5%重量的氢氧化钠和0.01-0.5%重量的硼氢化钠制成的预处理液。
2.根据权利要求1所述的棉杆蒸煮预处理液,其特征在于:氢氧化钠含量为1-3%,硼氢化钠含量为0.02-0.2%。