Background technology
Existing aluminum pot roughly divides two kinds of stretching aluminum pot and die casting aluminum pots.The stretching aluminum pot has the following disadvantages: 1, the bottom of a pan of stretching aluminum pot, pot wall and pot oral area thickness basically identical, it is yielding that the blocked up then waste material of thickness of pot body, thickness are crossed thin then pot body.2, general fixing between handle and pot body by riveted joint or welding.By the aluminum pot of riveted and fixed, the inboard junction of the pot body not easy cleaning of dirt that easily bonds; By welding fixing aluminum pot, its complex process, bonding strength is not high between handle and pot body.3, the compound iron plate of pot bottom needs again through one combination process, and its combined strength bination is not enough, makes inconvenient.
The die casting aluminum pot has the following disadvantages: aluminum pot adopts the method manufacturing of die casting, easily produces pore in the pot body, can not be in the bottom compound other metallic plate, and aluminum material hardness is lower, scratches easily.
Summary of the invention
The objective of the invention is to: a kind of rational in infrastructure, easily manufactured aluminum pot is provided.
Another object of the present invention is to: a kind of method of making aforementioned aluminum pot is provided.
The present invention decides on a verdict by following technology side and realizes:
A kind of aluminum pot, pot body include the bottom of a pan, pot wall, pot oral area and handle; It is characterized in that: the described the bottom of a pan, pot wall, pot oral area and handle are the integral pieces that is formed through the forcing press forging and pressing by aluminium block, and the bottom of a pan and pot oral area thickness are greater than the pot wall thickness.Because the bottom of a pan of pot body and pot oral area thickness greater than the pot wall thickness, are guaranteeing to save material again when the pot body has sufficient intensity.Because handle is an one with the pot wall, makes handle can be directly fixed on the handle, pot body inboard does not have fixedly vestige, is beneficial to cleaning.Because the bottom of a pan thickness is thicker, during use, the bottom of a pan is heated evenly, and food is difficult for sticking with paste at the end.
In the present invention, the described the bottom of a pan is compounded with metallic plate, and the metallic plate and the bottom of a pan link into an integrated entity by forging and pressing.In manufacture process, aluminium block is placed metallic plate top, can be with pot body formed and clad metal sheet process at one time, make make more convenient.Make pot body be difficult for scratching.
In the present invention, described metallic plate is a kind of of stainless iron plate, corrosion resistant plate or copper coin.Adopt stainless iron plate, aluminum pot can use on electromagnetic oven.
In the present invention, described handle is provided with the handle fixing hole.Be convenient to fixed handle.Certainly, handle also can be located at a pot oral area, and handle is directly made handle and used.
A kind of manufacture method of aluminum pot; It is characterized in that: insert a pot mould in forcing press, the high temperature aluminium block is put in the pot mould of forcing press, the operating pressure machine is with the disposable aluminum pot that forges into of aluminium block.Employing forges the method for extruding and makes aluminum pot, and its pot body has imperforate advantage.
Described pot mould adopts the bottom of a pan and the setting of pot oral area thickness greater than the pot wall thickness.It can guarantee to save material when the pot body has sufficient intensity.
When the high temperature aluminium block is placed pot mould, above or below aluminium block, put into metallic plate, operating pressure machine then is with the disposable aluminum pot that becomes to have the compound end that forges of aluminium block and metallic plate.It is more convenient that feasible manufacturing has the aluminum pot at the compound end, saved one combination process producing aluminum pot with composite bottom in the prior art.Simultaneously, combining that the bottom of a pan and composite bottom close is more reliable, break-off of the compound end can not occur.Certainly metallic plate can cover the external side of whole cooker.
Be provided with handle in the described pot mould, handle forges formation simultaneously with the pot body.Employing forges the aluminum pot of the method production of extruding, and the external side of pot can form handle, is convenient to fixed handle.
The specific embodiment
As shown in Figure 1: the pot body of present embodiment includes the bottom of a pan 1, pot wall 2, pot oral area 3 and handle 4.The bottom of a pan, pot wall, pot oral area and handle are the integral pieces that is formed through the forcing press forging and pressing by aluminium block.The thickness of the bottom of a pan 1 of pot body and pot oral area 3 is greater than pot wall 2 thickness, and handle 4 is located on pot wall.The bottom of a pan is compounded with magnetic conductive metal sheet 5, and magnetic conductive metal sheet is stainless iron plate, and magnetic conductive metal sheet 5 links into an integrated entity by forging and pressing with 1 in the bottom of a pan.Handle 4 is provided with the screw 6 that is used for fixing handle.
The manufacture method of present embodiment is as follows:
Insert a pot mould in forcing press, the pot mould adopts the bottom of a pan and pot oral area thickness greater than the setting of pot wall thickness, is provided with handle simultaneously in the pot mould.High temperature aluminium block and magnetic conductive metal sheet are put in the pot mould of forcing press together, and the operating pressure machine is with the disposable aluminum pot with composite bottom that forges into of aluminium block and magnetic conductive metal sheet.
The present embodiment the bottom of a pan and pot oral area thickness are greater than the pot wall thickness, and it is guaranteeing to save material again when the pot body has sufficient intensity.Handle forms with the pot body disposable, and handle can be directly fixed on the handle, and is beneficial to cleaning.Pot body adult and compounded magnetic conductive metallic plate process at one time, and make that manufacturing is more convenient.