CN100337956C - 一种能自行生成竖状网纹、鱼鳞纹或横向网纹的面釉 - Google Patents
一种能自行生成竖状网纹、鱼鳞纹或横向网纹的面釉 Download PDFInfo
- Publication number
- CN100337956C CN100337956C CNB2005100312409A CN200510031240A CN100337956C CN 100337956 C CN100337956 C CN 100337956C CN B2005100312409 A CNB2005100312409 A CN B2005100312409A CN 200510031240 A CN200510031240 A CN 200510031240A CN 100337956 C CN100337956 C CN 100337956C
- Authority
- CN
- China
- Prior art keywords
- reticulate pattern
- coat enamel
- cover
- oxide
- horizontal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种能自行生成竖状网纹、鱼鳞纹或横向网纹的面釉,其特征在于:它的组成物原料如下:石英8~13%、方解石25~35%、氧化铝2~4%、氧化铁8%、碳酸钡3~6%、氧化钴1%、粘土30~40%、熔块6~13%。所述的该面釉,在光滑瓷坯体上施用时形成不规则竖纹网花;所述的该面釉,在凹凸状成型瓷坯上则形成不规则的鱼鳞纹或横向网纹。根据以上技术方案提出的这种面釉,在将其施于已上底釉的坯体上,经烧制后的成品上能显现不规则的竖状网纹、鱼鳞状凹凸纹或横向网纹,使瓷体上的花纹更自然、更具美感。
Description
技术领域
本发明涉及一种能自动生成竖状网纹、鱼鳞纹或横向网纹的面釉,属陶瓷釉料配方类,尤其是指用于二次上釉用的面釉。
背景技术
各种日用陶瓷器具上的色彩与图案有多种方法制成,一般它们都是在成型后的瓷坯上通过施加不同釉色颜料烧制而成,也有用手工绘画方法用色釉在坯体或已烧制成的器具上作画,而后再烧制成功。上述多种施加面釉的方式工序繁多;而且其成形图案一般均比较呆板,缺乏艺术想象力和感染力。
发明内容
本发明的目的:在于提供一种能自行生成竖状网纹、鱼鳞纹或横向网纹的面釉;使烧成后的制品更具艺术想象力和感染力。
这种能自行生成竖状网纹、鱼鳞纹或横向网纹的面釉,其特征在于:所述面釉的原料如下(以重量百分比计):石英8~13%、方解石25~35%、氧化铝2~4%、氧化铁8%、碳酸钡3~6%、氧化钻1%、熔块6~13%、粘土30~37%。
所述各种原料中其粒径小于200目的颗粒物料占原料总量98%以上。
所述面釉,其烧成温度在1200~1260℃。
所述面釉在光滑瓷坯体上施用时形成不规则竖状网纹。
所述面釉在凹凸状瓷坯上形成不规则的鱼鳞纹。
所述面釉在横向局部环状台阶形瓷器坯体上形成环状花纹与竖状网纹相结合的横向网纹。
根据以上技术方案提出的这种面釉,在将其施于已上底釉的成型坯体上,经烧制后的成品上能显现不规则的竖状网纹、凹凸状鱼鳞纹或横向网纹,使体上的花纹更自然、更具美感。
附图说明
附图1为使用该面釉所形成的竖状网纹的效果图;
附图2为使用该面釉所形成的凹凸状鱼磷纹的效果图;
附图3为使用该面釉所形成的横向网纹的效果图。
图中:1、竖状网纹 2、鱼磷纹 3、横向网纹
具体实施方式(以重量百分比计)
实例1 | 实例2 | 实例3 | |
石英方解石氧化铝氧化铁碳酸钡氧化钴熔块粘土 | 8352831637 | 10.530384.519.533.5 | 132548611330 |
作为上述面釉的实际使用,有以下几个特点:
第一,面釉的烧成温度应控制在1200℃-1260℃;
第二,在光滑瓷坯的不同颜色的底釉上施加该面釉以后,就会形成不同颜色的不规则的竖状网纹式花纹;
第三,在凹凸状瓷坯的不同颜色的底釉上施加该面釉以后,形成不规则鱼鳞纹,或者横向网状花纹。
根据本发明人对上述面釉烧成机理的探讨,认识到:涂于瓷器成型坯体(既指光滑坯体,也包括凹凸型坯体)上的该面釉,在窑炉升温过程中逐渐凝聚、并且在瓷泥做成的成型坯体上形成不规则的竖纹网纹、鱼鳞纹,或者横向网纹。这三种形式花纹的形成,实际上与陶瓷成型坯体的表面平整度紧密相关:其一,当陶瓷成型坯体表面为平整光滑面时,该种面釉即形成如附图1所示的竖状网纹1;同时在这种花纹的形成过程中,由于面釉的凝聚是逐渐完成的,在重力作用下形成向下滴淌的效果,因此使瓷器表面形成的这种竖状网纹1具有上部色彩略浅、纹线略细,而到下部渐渐变深、***的自然美现象。
其二,当所采用的瓷器坯体,做成凹凸不平的鱼磷坑状时,所述的该面釉在窑炉升温过程中逐渐凝聚、并且在瓷泥做成的成型坯体上形成鳞次栉比的如附图2所示的鱼鳞纹2;
其三,当所采用的瓷器坯体,做成横向局部环状台阶时,所述的该面釉在窑炉升温过程中逐渐凝聚、并且在瓷泥做成的成型坯体上形成如附图3所示的横向环状花纹与竖状网纹相结合的横向网纹3。
本发明方案中采用的熔块是本行业通用的一种材料,来自于专业生产厂家,这种熔快的组成原料如下:二氧化硅58.3%,三氧化二铝10.17%,三氧化二铁0.08%,氧化钙10.44%,氧化镁0.12%,氧化钾6.96%,氧化钠4.36%,氧化锂0.29%,氧化硼9.27%。
Claims (6)
1、一种能自行生成竖状网纹、鱼鳞纹或横向网纹的面釉,其特征在于:所述面釉的原料如下(以重量百分比计):石英8~13%、方解石25~35%、氧化铝2~4%、氧化铁8%、碳酸钡3~6%、氧化钴1%、熔块6~13%、粘土30~37%;其中熔块的组成原料为:二氧化硅58.3%、三氧化二铝10.17%、三氧化二铁0.08%、氧化钙10.44%、氧化镁0.12%、氧化钾6.96%、氧化钠4.36%、氧化锂0.29%、氧化硼9.27%。
2、如权利要求1所述的一种能自行生成竖状网纹、鱼鳞纹或横向网纹的面釉,其特征在于:所述面釉的各种原料中,粒径小于200目的颗粒物料占原料总重量的98%以上。
3、如权利要求1所述的一种能自行生成竖状网纹、鱼鳞纹或横向网纹的面釉,其特征在于:所述面釉的烧成温度在1200~1260℃。
4、如权利要求1所述的一种能自行生成竖状网纹、鱼鳞纹或横向网纹的面釉,其特征在于:所述面釉,在光滑瓷坯体上施用时形成不规则竖状网纹(1)。
5、如权利要求1所述的一种能自行生成竖状网纹、鱼鳞纹或横向网纹的面釉,其特征在于:所述面釉在凹凸状成型瓷坯上则形成不规则的鱼鳞纹(2)。
6、如权利要求1所述的一种能自行生成竖状网纹、鱼鳞纹或横向网纹的面釉,其特征在于:所述面釉在横向局部环状台阶形瓷器坯体上形成环状花纹与竖状网纹相结合的横向网纹(3)。