CH715999A2 - Piece of jewelry in composite elastomer material. - Google Patents
Piece of jewelry in composite elastomer material. Download PDFInfo
- Publication number
- CH715999A2 CH715999A2 CH00390/19A CH3902019A CH715999A2 CH 715999 A2 CH715999 A2 CH 715999A2 CH 00390/19 A CH00390/19 A CH 00390/19A CH 3902019 A CH3902019 A CH 3902019A CH 715999 A2 CH715999 A2 CH 715999A2
- Authority
- CH
- Switzerland
- Prior art keywords
- mass
- sep
- piece
- composition
- elastomeric
- Prior art date
Abstract
L'invention se rapporte à une pièce de bijouterie réalisée en matière composite élastomère. Selon l'invention, la matière composite élastomère comprend une matrice en élastomère dans laquelle est dispersé entre 0.5% et 4% en masse de fibres cellulosiques, entre 0 et 2% en masse d'un additif antibactérien, entre 0 et 5 % en masse de charges conductrices thermiquement, entre 0 et 1% en masse d'agents anti-odeurs, et entre 0 et 1% en masse de silice.The invention relates to a piece of jewelry made of elastomeric composite material. According to the invention, the elastomeric composite material comprises an elastomeric matrix in which is dispersed between 0.5% and 4% by mass of cellulosic fibers, between 0 and 2% by mass of an antibacterial additive, between 0 and 5% by mass thermally conductive fillers, between 0 and 1% by mass of anti-odor agents, and between 0 and 1% by mass of silica.
Description
Domaine de l'inventionField of the invention
[0001] La présente invention concerne le domaine technique des matériaux à base d'élastomères. Plus précisément, l'invention concerne une pièce de bijouterie réalisée à partir d'une matière composite élastomère pour la, un procédé de fabrication de pièces, ainsi que les pièces obtenues. The present invention relates to the technical field of materials based on elastomers. More specifically, the invention relates to a piece of jewelry made from an elastomeric composite material for the, a method of manufacturing parts, as well as the parts obtained.
[0002] Dans la présente invention, pièce de bijouterie désigne tout objet de parure, mais également des composants utilisés dans l'horlogerie ou dans la joaillerie. Plus particulièrement, l'invention concerne des bracelets, tels que des bracelets de montre. [0002] In the present invention, piece of jewelry designates any object of adornment, but also components used in watchmaking or in jewelry. More particularly, the invention relates to bracelets, such as watch bracelets.
Arrière-plan de l'inventionBackground of the invention
[0003] De nombreux matériaux élastomères existent sur le marché et sont connus pour leur utilisation en tant que bracelet par exemple pour leur qualité de confort, de touché souple et leur résistance. [0003] Many elastomeric materials exist on the market and are known for their use as a bracelet, for example for their quality of comfort, of flexible touch and their resistance.
[0004] Ainsi, il est connu du document JP 2000204265 de réaliser une matière élastomère thermoplastique comportant des propriétés antibactériennes et présentant une bonne résistance au vieillissement. [0004] Thus, it is known from document JP 2000204265 to produce a thermoplastic elastomer material having antibacterial properties and having good resistance to aging.
[0005] On connaît également du brevet EP 2 468 127 une pièce de bijouterie, au moins partiellement réalisée en un matériau composite comprenant une matrice élastomère dans laquelle sont dispersées des charges de renfort choisies parmi le groupe comprenant des microfibres, des nanoparticules de polytétrafluoroéthylène, et leurs mélanges, ledit matériau composite étant obtenu à partir d'une composition comprenant entre 60% et 95% en poids d'au moins un élastomère, entre 0% et 5% en poids de microfibres et entre 0% et 40% en poids de nanoparticules de polytétrafluoroéthylène, par rapport au poids total de la composition, au moins l'une desdites charges de renfort étant présente. [0005] Also known from patent EP 2 468 127 is a piece of jewelry, at least partially made of a composite material comprising an elastomeric matrix in which are dispersed reinforcing fillers chosen from the group comprising microfibers, polytetrafluoroethylene nanoparticles, and mixtures thereof, said composite material being obtained from a composition comprising between 60% and 95% by weight of at least one elastomer, between 0% and 5% by weight of microfibers and between 0% and 40% by weight of polytetrafluoroethylene nanoparticles, relative to the total weight of the composition, at least one of said reinforcing fillers being present.
[0006] Cependant, ces matières élastomères utilisées pour les bracelets ou les composants d'horlogerie en contact avec la peau ne permettent pas d'obtenir une bonne évacuation de la transpiration, les propriétés antibactériennes permettant seulement de neutraliser les mauvaises odeurs, et les fibres présentes dans la matière ne permettent que de renforcer mécaniquement cette dernière. De plus, les bracelets sont souvent soumis à des frottements ou de l'abrasion ce qui tend à enlever une certaine quantité de l'agent antibactérien et donc à diminuer l'efficacité de ce dernier. [0006] However, these elastomeric materials used for bracelets or watch components in contact with the skin do not make it possible to obtain good evacuation of perspiration, the antibacterial properties only making it possible to neutralize bad odors, and the fibers present in the material only mechanically reinforce the latter. In addition, the bracelets are often subjected to friction or abrasion which tends to remove a certain amount of the antibacterial agent and therefore to reduce the effectiveness of the latter.
Résumé de l'inventionSummary of the invention
[0007] L'invention a notamment pour objectif de pallier aux différents inconvénients de ces techniques connues. The object of the invention is in particular to overcome the various drawbacks of these known techniques.
[0008] Plus précisément, un objectif de l'invention est de fournir une pièce de bijouterie en une matière élastomère destinées à être en contact prolongé avec la peau (direct ou indirect), et obtenir un élastomère avec des propriétés permettant d'améliorer l'évacuation de la transpiration, tout en conservant une bonne colorabilité et une bonne résistance au vieillissement (UV, transpiration, esthétique, déchirement). More specifically, an objective of the invention is to provide a piece of jewelry made of an elastomeric material intended to be in prolonged contact with the skin (direct or indirect), and to obtain an elastomer with properties making it possible to improve the evacuation of perspiration, while maintaining good colorability and good resistance to aging (UV, perspiration, aesthetics, tearing).
[0009] Ces objectifs, ainsi que d'autres qui apparaîtront plus clairement par la suite, sont atteints selon l'invention à l'aide d'une pièce de bijouterie réalisée en matière composite élastomère, ladite matière composite élastomère comprenant une matrice élastomère dans laquelle est dispersé entre 0 et 4% en masse de fibres cellulosiques, entre 0 et 2% en masse d'un additif antibactérien, entre 0 et 5 % en masse de charges conductrices thermiquement, entre 0 et 1% en masse d'agents anti-odeurs, et entre 0 et 1% en masse de silice. These objectives, as well as others which will emerge more clearly below, are achieved according to the invention using a piece of jewelry made of elastomeric composite material, said elastomeric composite material comprising an elastomeric matrix in which is dispersed between 0 and 4% by mass of cellulosic fibers, between 0 and 2% by mass of an antibacterial additive, between 0 and 5% by mass of thermally conductive fillers, between 0 and 1% by mass of anti-bacterial agents -odors, and between 0 and 1% by mass of silica.
[0010] Conformément à d'autres variantes avantageuses de l'invention : <tb><SEP>- La matrice élastomère est un fluoroélastomère de type caoutchouc fluorocarbone ; <tb><SEP>- la matière élastomère comprend des fibres cellulosiques courtes et des fibres cellulosiques longues, la longueur des fibres cellulosiques étant comprises entre 0.5mm et 1.5mm ; <tb><SEP>- la matière composite comprend entre 1.5% et 3.5% en masse de microfibres, et de préférence 2% en masse de microfibres courtes et 1.5% en masse de microfibres longues par rapport au poids total de la composition ; <tb><SEP>- la matière élastomère comprend au moins entre 0 et 30% en masse d'un additif colorant ; <tb><SEP>- la matière élastomère comprend moins entre 0 et 1% en masse d'agents antiodeurs ; <tb><SEP>- la matière élastomère comprend au moins un agent de démoulage ; <tb><SEP>- la matière élastomère comprend entre 0 et 1% en masse d'un agent azurant.According to other advantageous variants of the invention: <tb> <SEP> - The elastomeric matrix is a fluoroelastomer of the fluorocarbon rubber type; <tb> <SEP> - the elastomeric material comprises short cellulosic fibers and long cellulosic fibers, the length of the cellulosic fibers being between 0.5mm and 1.5mm; <tb> <SEP> - the composite material comprises between 1.5% and 3.5% by mass of microfibers, and preferably 2% by mass of short microfibers and 1.5% by mass of long microfibers relative to the total weight of the composition; <tb> <SEP> - the elastomeric material comprises at least between 0 and 30% by mass of a coloring additive; <tb> <SEP> - the elastomeric material comprises less between 0 and 1% by mass of anti-odor agents; <tb> <SEP> - the elastomeric material comprises at least one mold release agent; <tb> <SEP> - the elastomeric material comprises between 0 and 1% by weight of a brightening agent.
[0011] L'invention concerne aussi et notamment toute pièce d'horlogerie réalisée en matière élastomère conformément à l'invention. The invention also and in particular relates to any timepiece made of elastomeric material according to the invention.
[0012] L'invention concerne également un procédé de fabrication d'une pièce de bijouterie conforme à l'invention, le procédé de fabrication comprend les étapes suivantes : <tb><SEP>- réaliser une composition comprenant au moins un élastomère, entre 0.5% et 4% en masse de fibres cellulosiques, entre 0 et 2% en masse d'un additif antibactérien, entre 0 et 5 % en masse de charges conductrices thermiquement, entre 0 et 1% en masse d'agents anti-odeurs, et entre 0 et 1% en masse de silice ; <tb><SEP>- réaliser un moulage de la composition obtenue à l'étape précédente ; <tb><SEP>- réaliser les étapes de finition de la pièce moulée obtenue lors de la deuxième étape.The invention also relates to a method of manufacturing a piece of jewelry according to the invention, the manufacturing method comprises the following steps: <tb> <SEP> - produce a composition comprising at least one elastomer, between 0.5% and 4% by mass of cellulosic fibers, between 0 and 2% by mass of an antibacterial additive, between 0 and 5% by mass of fillers thermally conductive, between 0 and 1% by mass of anti-odor agents, and between 0 and 1% by mass of silica; <tb> <SEP> - performing a molding of the composition obtained in the previous step; <tb> <SEP> - carry out the finishing steps for the molded part obtained during the second step.
[0013] Selon ce procédé, la matrice élastomère est un fluoroélastomère de type caoutchouc fluorocarbone. According to this process, the elastomeric matrix is a fluoroelastomer of fluorocarbon rubber type.
[0014] D'autres caractéristiques et avantages de l'invention apparaîtront plus clairement à la lecture de la description suivante d'un mode de réalisation particulier de l'invention, donné à titre de simple exemple illustratif et non limitatif. Other characteristics and advantages of the invention will emerge more clearly on reading the following description of a particular embodiment of the invention, given by way of simple illustrative and non-limiting example.
Description détaillée des modes de réalisation préférésDetailed description of the preferred embodiments
[0015] L'invention concerne une pièce de bijouterie réalisée en matière composite élastomère, ladite matière composite élastomère comprenant une matrice élastomère dans laquelle est dispersé entre 0 et 4% en masse de fibres cellulosiques, entre 0 et 2% en masse d'un additif antibactérien, entre 0 et 1 % de charges conductrices thermiquement, entre 0 et 1% d'agents antiodeurs, et entre 0 et 1% de silice. The invention relates to a piece of jewelry made of elastomeric composite material, said elastomeric composite material comprising an elastomeric matrix in which is dispersed between 0 and 4% by weight of cellulosic fibers, between 0 and 2% by weight of a antibacterial additive, between 0 and 1% of thermally conductive fillers, between 0 and 1% of anti-odor agents, and between 0 and 1% of silica.
[0016] Selon l'invention, la matière élastomère choisie pour la matrice est choisie parmi les fluoroélastomères. According to the invention, the elastomeric material chosen for the matrix is chosen from fluoroelastomers.
[0017] Le terme „fluoroélastomère“ est utilisé au sens général indépendamment de la teneur en fluor et désigne à la fois les élastomères fluorés dont la chaîne principale est partiellement substituée, c'est-à-dire les fluoroélastomères communément appelés FKM, ainsi que les élastomères fluorés dont la chaine principale est entièrement substituée, c'est-à-dire les perfluoroélastomères communément appelés FFKM. The term "fluoroelastomer" is used in the general sense regardless of the fluorine content and denotes both fluoroelastomers whose main chain is partially substituted, that is to say fluoroelastomers commonly called FKM, as well as fluoroelastomers whose main chain is entirely substituted, that is to say perfluoroelastomers commonly called FFKM.
[0018] De préférence, l'élastomère est un fluoroélastomère, et plus préférentiellement un fluoroélastomère de type FKM. Preferably, the elastomer is a fluoroelastomer, and more preferably a fluoroelastomer of the FKM type.
[0019] La quantité d'élastomère est comprise entre 55% et 95% en poids par rapport au poids total de la composition. The amount of elastomer is between 55% and 95% by weight relative to the total weight of the composition.
[0020] Selon un autre mode de réalisation, la matière élastomère est choisie parmi un ou plusieurs élastomères thermoplastiques tels que le polyuréthane, le polyéther block amide, les copolyesters élastomères, les élastomères acryliques ou les élastomères styréniques. [0020] According to another embodiment, the elastomeric material is chosen from one or more thermoplastic elastomers such as polyurethane, polyether block amide, elastomeric copolyesters, acrylic elastomers or styrenic elastomers.
[0021] Encore selon un autre mode de réalisation de l'invention, la matière est choisie parmi des élastomères vulcanisables à froid tels que les silicones. [0021] Yet another embodiment of the invention, the material is chosen from cold vulcanizable elastomers such as silicones.
[0022] La dureté de la matière élastomère peut être choisie sur une gamme de 20 shore OO à 90 shore D suivant le besoin haptique et fonctionnel. The hardness of the elastomeric material can be chosen over a range of 20 shore OO to 90 shore D depending on the haptic and functional needs.
[0023] Il est possible de réaliser par moulage des éléments durs d'une boîte avec des duretés de 90 shore D par exemple, alors que les matières shore OO et shore A seront plutôt utilisées en revêtement sur un élément dur. Les pièces souples telles que les bracelets seront réalisées à partir d'une dureté shore A. It is possible to produce by molding hard elements of a box with hardnesses of 90 shore D for example, while the Shore OO and Shore A materials will rather be used as a coating on a hard element. Soft parts such as bracelets will be made from Shore A hardness.
[0024] Par exemple, dans le cas d'une boîte de montre, l'élastomère peut être pulvérisé à la surface de la boite et servir de revêtement, ou bien surmoulé pour apporter un toucher doux. [0024] For example, in the case of a watch case, the elastomer can be sprayed onto the surface of the case and serve as a coating, or else overmolded to provide a soft feel.
[0025] Selon l'invention, la matière élastomère comprend des charges conductrices thermiquement présentant une conductivité thermique supérieure à 20W.m-1.K-1, telles du nitrure de bore hexagonal ou du graphène ou des nanotubes de carbone, par exemple. La quantité de ces charges conductrices thermiquement dans la matière élastomère est comprise entre 0.04% et 5% en masse et permettent d'accroître la conductivité thermique de la matière d'un facteur 3, de 0.4 à 1.2W.m-1.K-1 sans pour autant accroître la conductivité électrique de celle-ci. De telles charges conductrices thermiquement ont pour avantage de mieux évacuer la chaleur corporelle et donc de limiter la transpiration. [0025] According to the invention, the elastomeric material comprises thermally conductive fillers having a thermal conductivity greater than 20W.m-1.K-1, such as hexagonal boron nitride or graphene or carbon nanotubes, for example. The quantity of these thermally conductive fillers in the elastomeric material is between 0.04% and 5% by mass and make it possible to increase the thermal conductivity of the material by a factor of 3, from 0.4 to 1.2Wm-1.K-1 without for all that increase the electrical conductivity thereof. Such thermally conductive fillers have the advantage of better evacuating body heat and therefore of limiting perspiration.
[0026] Selon un aspect avantageux de l'invention, la matière élastomère comprend également un additif antibactérien par exemple à base d'argent de manière à limiter, voire d'empêcher, le développement des bactéries, à la surface et à l'intérieur de la matière, dues essentiellement à la transpiration du porteur lorsque le bracelet est au contact de la peau par exemple. According to an advantageous aspect of the invention, the elastomeric material also comprises an antibacterial additive, for example based on silver, so as to limit, or even prevent, the development of bacteria, on the surface and inside material, mainly due to the perspiration of the wearer when the bracelet is in contact with the skin for example.
[0027] De préférence, l'additif antimicrobien utilisé est le Sanitized® BC A 21-41. Cet additif se présente sous la forme d'argent encapsulé dans un matériau en verre céramique, sa résistance aux hautes températures permet de l'ajouter facilement dans le mélange sans altérer les propriétés antibactériennes. Selon les besoins, la quantité d'additif antibactérien est comprise entre 0% à 2% en masse. [0027] Preferably, the antimicrobial additive used is Sanitized® BC A 21-41. This additive is in the form of silver encapsulated in a ceramic glass material, its resistance to high temperatures allows it to be easily added to the mixture without altering the antibacterial properties. Depending on requirements, the amount of antibacterial additive is between 0% to 2% by mass.
[0028] La matière élastomère comprend aussi un agent anti-odeur tel que par exemple de la zéolite (Lithofill MM) de manière à absorber les odeurs, généralement cet agent se présente sous la forme de grain présentant une taille de 0 à 10 µm. Selon les besoins, la quantité d'agent antiodeur est comprise entre 0% à 1% en masse. Selon une variante de l'invention, la zéolite peut servir de support pour diffuser un parfum, cette dernière pourra par exemple recevoir une ou des huiles essentielles ou encore une ou des fragrances. Un tel mode de réalisation est particulièrement intéressant compte tenu du fait que la zéolite permet de diffuser le parfum pendant une très longue durée. [0028] The elastomeric material also comprises an anti-odor agent such as, for example, zeolite (Lithofill MM) so as to absorb odors, generally this agent is in the form of a grain having a size of 0 to 10 μm. Depending on requirements, the amount of anti-odor agent is between 0% to 1% by mass. According to a variant of the invention, the zeolite can serve as a support for diffusing a perfume, the latter could for example receive one or more essential oils or one or more fragrances. Such an embodiment is particularly advantageous given the fact that the zeolite makes it possible to diffuse the perfume for a very long period of time.
[0029] La matière élastomère comprend un agent de renfort tel que de la silice pour améliorer sa durabilité. [0029] The elastomeric material includes a reinforcing agent such as silica to improve its durability.
[0030] Selon l'invention, la matière élastomère comprend des microfibres hydrophiles agencée pour évacuer l'humidité, et notamment la transpiration, au travers de la matière élastomère. Conformément à la présente invention, les microfibres hydrophiles présentent une finesse inférieure à 150 mTex, ce qui est une taille suffisante pour pouvoir transporter les molécules type H2O. [0030] According to the invention, the elastomeric material comprises hydrophilic microfibers designed to evacuate moisture, and in particular perspiration, through the elastomeric material. In accordance with the present invention, the hydrophilic microfibers have a fineness of less than 150 mTex, which is a sufficient size to be able to transport molecules of the H2O type.
[0031] Selon l'invention, les fibres hydrophiles sont réalisées en une matière cellulosique, et on utilisera de préférence des fibres de type Lyocell telles que les Lenzing Tencel FCP. According to the invention, the hydrophilic fibers are made of a cellulosic material, and fibers of the Lyocell type such as Lenzing Tencel FCP will preferably be used.
[0032] De préférence, la composition selon l'invention comprend entre 0,5% et 4%, de préférence entre 1.5% et 3.5%, en poids de microfibres par rapport au poids total de la composition. Les microfibres utilisées présentent une longueur comprise entre 0.5 mm et 1.5mm. Preferably, the composition according to the invention comprises between 0.5% and 4%, preferably between 1.5% and 3.5%, by weight of microfibers relative to the total weight of the composition. The microfibers used have a length of between 0.5 mm and 1.5mm.
[0033] La présence de ces microfibres dans la matière permet de former un réseau de canaux microscopiques, et les nanofibrilles formant les microfibres conduisent l'humidité rapidement et uniformément au travers de la matière. The presence of these microfibers in the material makes it possible to form a network of microscopic channels, and the nanofibrils forming the microfibers conduct moisture rapidly and uniformly through the material.
[0034] De manière à améliorer le transport de l'humidité au travers de la matière, les microfibres incorporées dans la matière sont composées de microfibres cellulosiques courtes et de microfibres cellulosiques longues, la longueur des fibres cellulosiques étant comprises entre 0.5mm et 1.5mm. In order to improve the transport of humidity through the material, the microfibers incorporated into the material are composed of short cellulosic microfibers and long cellulosic microfibers, the length of the cellulosic fibers being between 0.5mm and 1.5mm .
[0035] La composition selon l'invention comprend 2% en poids de microfibres courtes et 1.5% en poids de microfibres longues par rapport au poids total de la composition. The composition according to the invention comprises 2% by weight of short microfibers and 1.5% by weight of long microfibers relative to the total weight of the composition.
[0036] Un tel mélange de microfibres courtes et microfibres longues aux microfibres se touchent et forment des canaux améliorant le pouvoir de diffusion de la matrice formée par la matière élastomère et l'humidité peut être transportée par capillarité à travers la matière et ainsi être évacuée. Such a mixture of short microfibers and long microfibers with microfibers touch each other and form channels improving the diffusing power of the matrix formed by the elastomeric material and moisture can be transported by capillary action through the material and thus be evacuated .
[0037] Selon l'invention, les microfibres ont préférentiellement une section transversale en forme d'hélice pour leur donner une surface spécifique plus importante et donc un pouvoir de diffusion plus rapide. According to the invention, the microfibers preferably have a cross section in the form of a helix to give them a larger specific surface area and therefore a faster diffusing power.
[0038] Plus précisément, la section des fibres hydrophiles est en forme d'hélice à n pales avec n strictement supérieur à deux, de manière à offrir une plus grande surface spécifique et ainsi favoriser l'évacuation de l'humidité. More specifically, the section of the hydrophilic fibers is in the form of a helix with n blades with n strictly greater than two, so as to provide a greater specific surface area and thus promote the evacuation of moisture.
[0039] La composition peut comprendre également des agents de vulcanisation ou de réticulation propres à l'élastomère, et autres additifs traditionnels communément utilisé par l'homme du métier dans le domaine des formulations à base d'élastomère, et plus particulièrement des formulations à base de fluoroélastomère. The composition may also comprise vulcanizing or crosslinking agents specific to the elastomer, and other traditional additives commonly used by those skilled in the art in the field of elastomer-based formulations, and more particularly formulations with fluoroelastomer base.
[0040] Avantageusement, la composition peut comprendre un colorant ou un pigment. Des mélanges de colorants et/ou de pigments peuvent également être utilisés. [0040] Advantageously, the composition can comprise a dye or a pigment. Mixtures of dyes and / or pigments can also be used.
[0041] On utilisera par exemple du dioxyde de titane pour réaliser une composition de couleur blanche, dans ce cas la quantité de colorant utilisée est de 30% en masse. De manière à améliorer le rendu de la couleur blanche un agent azurant est utilisé, ce dernier permet de rééquilibrer le spectre de couleurs et de fournir un blanc plus blanc. La quantité d'agent azurant utilisée est d'environ 1% en masse. For example, titanium dioxide will be used to produce a white composition, in this case the amount of dye used is 30% by weight. In order to improve the rendering of the white color, a brightening agent is used, the latter makes it possible to rebalance the color spectrum and to provide a whiter white. The amount of brightening agent used is about 1% by weight.
[0042] Dans le cas d'une composition blanche, on ajoutera un fluoroélastomère de type FKM transparent à hauteur de 10% en masse pour améliorer la résistance à la salissure de la composition et améliorer la souplesse du produit final. In the case of a white composition, a transparent FKM type fluoroelastomer will be added in an amount of 10% by weight to improve the resistance to soiling of the composition and to improve the flexibility of the final product.
[0043] Dans le cas d'une composition de couleur noire, on utilisera directement un fluoroélastomère de type FKM de couleur noire. La couleur noire pouvant être obtenue via du noir de carbone (Grade N-660). In the case of a black-colored composition, a black-colored FKM-type fluoroelastomer will be used directly. The black color can be obtained via carbon black (Grade N-660).
[0044] La matière décrite précédemment peut être directement moulée pour réaliser des brins de bracelets mono-matière en élastomère confortable, ou encore surmoulé pour réaliser des brins de bracelets bi-matières confortables, chaque brin présentant une première partie inférieure en matière confortable en contact avec la peau, et une partie supérieure dans une autre matière avantageuse pour sa fonction. On peut également imaginer que chacune des parties présente une couleur différente dans un but purement esthétique. The material described above can be directly molded to make strands of single-material bracelets in comfortable elastomer, or else overmolded to make strands of comfortable bi-material bracelets, each strand having a first lower part in comfortable material in contact. with the skin, and an upper part in another material advantageous for its function. We can also imagine that each of the parts has a different color for purely aesthetic purposes.
[0045] Ci-après, trois exemples de composition sont décrits, chacun d'entre eux comprend une base qui forme la matrice élastomère dans laquelle sont dispersés les additifs. Ces exemples se basent sur des échantillons réalisés par la demanderesse conformément à l'invention. Hereinafter, three examples of composition are described, each of them comprises a base which forms the elastomeric matrix in which the additives are dispersed. These examples are based on samples produced by the applicant in accordance with the invention.
[0046] Pour un bracelet de couleur noire, la composition suivante est utilisée : For a black colored bracelet, the following composition is used:
Première étape (base noire)First step (black base)
[0047] <tb>FKM<SEP>P-457 (Solvay)<SEP>100 <tb>NC<SEP>Grade N-660 (cabot)<SEP>22 <tb>Huile<SEP>Nafol 1822B (Sasol)<SEP>1.5 <tb>Vulc<SEP>Drimix Kenrich (TAlC)<SEP>3 <tb>Vulc<SEP>Luperox 101XL45<SEP>2.5[0047] <tb> FKM <SEP> P-457 (Solvay) <SEP> 100 <tb> NC <SEP> Grade N-660 (cabot) <SEP> 22 <tb> Oil <SEP> Nafol 1822B (Sasol) <SEP> 1.5 <tb> Vulc <SEP> Drimix Kenrich (TAlC) <SEP> 3 <tb> Vulc <SEP> Luperox 101XL45 <SEP> 2.5
2ème étape (mélange des additifs conforts dans la base)2nd step (mixing comfort additives in the base)
[0048] <tb>black base<SEP>Selon la formule ci-dessous<SEP>100 <tb>short cellulose<SEP>Lenzing Tencel FCP, 0.5mm<SEP>2 <tb>lonq cellulose<SEP>Lenzinq Tencel FCP, 1.5mm<SEP>1.5 <tb>zéolite<SEP>Lithofill MM<SEP>0.5 <tb>Graphene (*)<SEP>8 à 12couches : 3mu<SEP>0.045 <tb>silice (*)<SEP>Aerosil 200<SEP>0.5 <tb>Antibacterial<SEP>Sanitized BCA21-41<SEP>2 <tb>(*)Le graphène est ici la charge choisie afin d'améliorer la conductivité thermique du mélange et donc d'améliorer l'échange thermique entre la peau et le bracelet.[0048] <tb> black base <SEP> According to the formula below <SEP> 100 <tb> cellulose shorts <SEP> Lenzing Tencel FCP, 0.5mm <SEP> 2 <tb> lonq cellulose <SEP> Lenzinq Tencel FCP, 1.5mm <SEP> 1.5 <tb> zeolite <SEP> Lithofill MM <SEP> 0.5 <tb> Graphene (*) <SEP> 8 to 12 layers: 3mu <SEP> 0.045 <tb> silica (*) <SEP> Aerosil 200 <SEP> 0.5 <tb> Antibacterial <SEP> Sanitized BCA21-41 <SEP> 2 <tb> (*) Graphene is here the filler chosen in order to improve the thermal conductivity of the mixture and therefore to improve the heat exchange between the skin and the bracelet.
[0049] Pour un bracelet de couleur blanche, la composition suivante est utilisée : For a bracelet of white color, the following composition is used:
1<ère>étape (base neutre)1st step (neutral basis)
[0050] <tb>FKM<SEP>P-457<SEP>100 <tb>Huile<SEP>Nafol 1822B (Sasol)<SEP>1.5 <tb>Vulc<SEP>Drimix Kenrich (TAlC)<SEP>3 <tb>Vulc<SEP>Luperox 101XL45<SEP>2.5 <tb>silice<SEP>Aerosil 200<SEP>17[0050] <tb> FKM <SEP> P-457 <SEP> 100 <tb> Oil <SEP> Nafol 1822B (Sasol) <SEP> 1.5 <tb> Vulc <SEP> Drimix Kenrich (TAlC) <SEP> 3 <tb> Vulc <SEP> Luperox 101XL45 <SEP> 2.5 <tb> silica <SEP> Aerosil 200 <SEP> 17
2ème étape (mélange des additifs conforts dans la base neutre)2nd step (mixing comfort additives in the neutral base)
[0051] <tb>Base neutre<SEP>according above formula<SEP>100 <tb>short cellulose<SEP>Lenzinq Tencel FCP, 0.5mm<SEP>2 <tb>long cellulose<SEP>Lenzing Tencel FCP, 1.5mm<SEP>1.5 <tb>zéolite<SEP>Lithofill MM<SEP>0.5 <tb>Nitre de bore hBN (*)<SEP>3M™ Boron Nitride Cooling Filler Flakes CFF 500-3 and 200-3<SEP>5 <tb>TiO2<SEP>TI Pure R104, dupont<SEP>30 <tb>silice<SEP>Aerosil 200<SEP>0.5 <tb>Antibacterial<SEP>Sanitized BCA21-41<SEP>2 <tb>Azurant optique<SEP><SEP>1 <tb>Zinc stearate<SEP><SEP>0.5 <tb>FKM transparent(*)<SEP>P-957, Solvay<SEP>10 <tb>(*) Le nitrure de bore hexagonal est la charge choisie afin d'améliorer la conductivité thermique du mélange et donc d'améliorer l'échange thermique entre la peau et le bracelet. <tb>(*)Le FKM transparent est ajouté en fin de mélange a un fort taux de cisaillement afin de créer un mélange polyphasé (dispersion du FKM transparent dans le mélange initialement réalisé) : cette technique permet d'améliorer la résistance à la salissure du mélange blanc et d'améliorer sa souplesse et donc le confort au porter.[0051] <tb> Neutral base <SEP> according above formula <SEP> 100 <tb> cellulose shorts <SEP> Lenzinq Tencel FCP, 0.5mm <SEP> 2 <tb> long cellulose <SEP> Lenzing Tencel FCP, 1.5mm <SEP> 1.5 <tb> zeolite <SEP> Lithofill MM <SEP> 0.5 <tb> Boron Niter hBN (*) <SEP> 3M ™ Boron Nitride Cooling Filler Flakes CFF 500-3 and 200-3 <SEP> 5 <tb> TiO2 <SEP> TI Pure R104, dupont <SEP> 30 <tb> silica <SEP> Aerosil 200 <SEP> 0.5 <tb> Antibacterial <SEP> Sanitized BCA21-41 <SEP> 2 <tb> Optical brightener <SEP> <SEP> 1 <tb> Zinc stearate <SEP> <SEP> 0.5 <tb> FKM transparent (*) <SEP> P-957, Solvay <SEP> 10 <tb> (*) The hexagonal boron nitride is the filler chosen in order to improve the thermal conductivity of the mixture and therefore to improve the heat exchange between the skin and the bracelet. <tb> (*) The transparent FKM is added at the end of the mixture at a high shear rate in order to create a polyphase mixture (dispersion of the transparent FKM in the mixture initially produced): this technique makes it possible to improve the resistance to soiling of the white mixture and to improve its flexibility and therefore the wearing comfort.
[0052] Pour les bracelets ayant une autre couleur, la composition suivante est utilisée : For the bracelets having another color, the following composition is used:
1ère étape (base neutre)1st step (neutral basis)
[0053] <tb>FKM<SEP>P-457<SEP>100 <tb>Huile<SEP>Nafol 1822B (Sasol)<SEP>1.5 <tb>Vulc<SEP>Drimix Kenrich (TAlC)<SEP>3 <tb>Vulc<SEP>Luperox 101XL45<SEP>2.5 <tb>silice<SEP>Aerosil 200<SEP>17[0053] <tb> FKM <SEP> P-457 <SEP> 100 <tb> Oil <SEP> Nafol 1822B (Sasol) <SEP> 1.5 <tb> Vulc <SEP> Drimix Kenrich (TAlC) <SEP> 3 <tb> Vulc <SEP> Luperox 101XL45 <SEP> 2.5 <tb> silica <SEP> Aerosil 200 <SEP> 17
2ème étape (mélange des additifs dans la base neutre)2nd step (mixing the additives in the neutral base)
[0054] <tb>Base neutre<SEP>according above formula<SEP>100 <tb>short cellulose<SEP>Lenzinq Tencel FCP, 0.5mm<SEP>2 <tb>lonq cellulose<SEP>Lenzing Tencel FCP, 1.5mm<SEP>1.5 <tb>zéolite<SEP>Lithofill MM<SEP>0.5 <tb>Nitre de bore hBN (*)<SEP>3M™ Boron Nitride Cooling Filler Flakes CFF 500-3 and 200-3<SEP>5 <tb>silice<SEP>Aerosil 200<SEP>0.5 <tb>Antibacterial<SEP>Sanitized BCA21-41<SEP>2 <tb>Azurant optique<SEP><SEP>1 <tb>Zinc stearate<SEP><SEP>0.5[0054] <tb> Neutral base <SEP> according above formula <SEP> 100 <tb> cellulose shorts <SEP> Lenzinq Tencel FCP, 0.5mm <SEP> 2 <tb> lonq cellulose <SEP> Lenzing Tencel FCP, 1.5mm <SEP> 1.5 <tb> zeolite <SEP> Lithofill MM <SEP> 0.5 <tb> Boron Niter hBN (*) <SEP> 3M ™ Boron Nitride Cooling Filler Flakes CFF 500-3 and 200-3 <SEP> 5 <tb> silica <SEP> Aerosil 200 <SEP> 0.5 <tb> Antibacterial <SEP> Sanitized BCA21-41 <SEP> 2 <tb> Optical brightener <SEP> <SEP> 1 <tb> Zinc stearate <SEP> <SEP> 0.5
[0055] La pièce de bijouterie en matière composite élastomère selon l'invention est obtenue par un procédé comprenant les étapes suivantes : <tb><SEP>- réaliser une préparation d'une composition telle que décrite ci-dessus ; <tb><SEP>- réaliser un moulage de la composition obtenue lors de la première étape pour obtenir la forme désirée ; <tb><SEP>- réaliser les étapes de finition de la pièce moulée obtenue lors de la deuxième étape.The piece of jewelry made of elastomeric composite material according to the invention is obtained by a process comprising the following steps: <tb> <SEP> - carrying out a preparation of a composition as described above; <tb> <SEP> - molding the composition obtained during the first step to obtain the desired shape; <tb> <SEP> - carry out the finishing steps for the molded part obtained during the second step.
[0056] Selon les besoins de l'homme du métier et des pièces à réaliser, les étapes de finition de la pièce moulée peuvent consister en une couture, l'impression d'un motif, la réalisation de trous dans la matière, etc... According to the needs of those skilled in the art and the parts to be produced, the stages of finishing the molded part can consist of sewing, printing a pattern, making holes in the material, etc. ..
[0057] Le moulage de la composition peut être effectué par tout type de procédé connu de l'homme du métier, tel que le moulage par injection, par extrusion ou par compression. The molding of the composition can be carried out by any type of method known to those skilled in the art, such as injection molding, by extrusion or by compression.
[0058] La vulcanisation est réalisée de manière connue à une température généralement comprise entre 130°C et 200°C, pendant un temps suffisant qui peut varier en fonction de la pièce désirée, par exemple entre 60 et 300 secondes en fonction de la température de vulcanisation, du système de vulcanisation adopté et de la cinétique de vulcanisation de la composition. Vulcanization is carried out in a known manner at a temperature generally between 130 ° C and 200 ° C, for a sufficient time which may vary depending on the desired part, for example between 60 and 300 seconds depending on the temperature vulcanization process, the vulcanization system adopted and the vulcanization kinetics of the composition.
[0059] La pièce de bijouterie peut être par exemple un bracelet, notamment un bracelet de montre. Plus spécifiquement, un bracelet selon l'invention peut présenter des formes et des découpes particulières et répondre malgré tout à un cahier des charges sévère en termes de tenue mécanique, et plus spécifiquement en termes de résistance à la traction, de résistance aux salissures, tout en prodiguant une bonne évacuation de la sueur du porteur. The piece of jewelry may for example be a bracelet, in particular a watch strap. More specifically, a bracelet according to the invention can have particular shapes and cutouts and still meet strict specifications in terms of mechanical strength, and more specifically in terms of tensile strength, resistance to soiling, all by providing good wicking of the wearer's sweat.
[0060] Une telle matière pour améliorer le confort permet de fabriquer des pièces d'horlogerie ou des bijoux comme des bracelets, des boucles de bracelets, des colliers, des boîtes, des fonds de boîte, des poussoirs, des boucles ou encore des lunettes. [0060] Such a material to improve comfort makes it possible to manufacture timepieces or jewelry such as bracelets, bracelet buckles, necklaces, boxes, case backs, pushers, buckles or even glasses. .
[0061] Bien entendu, la présente invention ne se limite pas à l'exemple illustré et est susceptible de diverses variantes et modifications qui apparaîtront à l'homme de l'art. Of course, the present invention is not limited to the example illustrated and is susceptible of various variants and modifications which will appear to those skilled in the art.
Claims (15)