CH684181A5 - Delaminatable composites. - Google Patents
Delaminatable composites. Download PDFInfo
- Publication number
- CH684181A5 CH684181A5 CH2692/92A CH269292A CH684181A5 CH 684181 A5 CH684181 A5 CH 684181A5 CH 2692/92 A CH2692/92 A CH 2692/92A CH 269292 A CH269292 A CH 269292A CH 684181 A5 CH684181 A5 CH 684181A5
- Authority
- CH
- Switzerland
- Prior art keywords
- layers
- layer
- composites
- polymer
- soluble
- Prior art date
Description
1 1
CH 684 181 A5 CH 684 181 A5
2 2nd
Beschreibung description
Vorliegende Erfindung betrifft delaminierbare Verbünde enthaltend Schichten aus Kunststoffen, Me-tallfolien und/oder celiulosischen Materialien. The present invention relates to delaminable composites containing layers of plastics, metal foils and / or celiulosic materials.
Verbünde aus verschiedenen thermoplastischen Kunststoffen, z.B. aus Folien und Folienverbunden, wie Coextrudaten oder Schichtstoffen, Verbünde aus thermoplastischen Kunststoffen enthaltend als Aussen- oder Zwischenschicht eine Metallfolie, wie z.B. eine Aluminiumfolie, insbesondere als Sperrschicht gegen Gase, Dämpfe, Feuchtigkeit und dergleichen oder Verbünde enthaltend thermoplastische Kunststoffe und cellulosische Materialien wie Papier, Pappe etc. und gegebenenfalls eine Metallfolie, sind bekannt. Composites made of various thermoplastics, e.g. of foils and foil composites, such as coextrudates or laminates, composites of thermoplastic materials containing a metal foil as outer or intermediate layer, e.g. An aluminum foil, in particular as a barrier layer against gases, vapors, moisture and the like, or composites containing thermoplastic plastics and cellulosic materials such as paper, cardboard etc. and optionally a metal foil are known.
Es ist nicht einfach, solche Verbünde aus verschiedenen Werkstoffen nach erfolgtem Gebrauch, z.B. nach dem Gebrauch als Verpackungsmaterial zu rezykiieren. Ein Deponieren oder Verbrennen solcher Verbünde ist beim heutigen Umweltbe-wusstsein oft nicht mehr opportun. Ein Rezykiieren, das heisst auftrennen und separates Aufarbeiten jedes Werkstoffes von miteinander trennfest verbundenen Stoffen, wie Kunststoffolien, fallweise von mehreren Kunststoffolien unterschiedlicher Polymerisate unter sich oder zusammen mit Metallfolien und/oder Papieren gestaltet sich aufwendig. It is not easy to make such composites from different materials after use, e.g. to recycle after use as packaging material. Landfilling or incinerating such groups is often no longer appropriate with today's environmental awareness. Recycling, that is to say separating and separately processing each material from materials which are bonded to one another in a separable manner, such as plastic films, in some cases from several plastic films of different polymers among themselves or together with metal foils and / or papers, is complex.
Wünschenswert sind deshalb Verbünde, die vorerst trennfest miteinander verbunden sind und nach Gebrauch sich auf einfache Weise in ihre einzelnen Werkstoffe separieren lassen. For this reason, it is desirable to have composites that are initially connected to one another so that they can be easily separated into their individual materials after use.
Aufgabe vorliegender Erfindung ist es, solche delaminierbaren Verbünde zu schaffen. The object of the present invention is to create such delaminable composites.
Erfindungsgemäss wird dies dadurch erreicht, dass der Verbund wenigstens drei Schichten enthält, wobei wenigstens eine Schicht eines in nichtneutralem wässrigem Medium löslichen Polymerisates zwischen zwei Schichten aus Kunststoffen, Metallen und/oder celiulosischen Materialien angebracht ist. This is achieved according to the invention in that the composite contains at least three layers, at least one layer of a polymer which is soluble in a non-neutral aqueous medium being applied between two layers of plastics, metals and / or celiulosic materials.
Beispielsweise kann demnach ein erfindungsge-mässer Verbund nacheinander eine Schicht eines Kunststoffes, eines Metalles oder eines celiulosischen Materials, eine Schicht eines in nichtneutralem wässrigem Medium löslichen Polymerisates und eine Schicht eines Kunststoffes aufweisen. For example, a composite according to the invention can have a layer of a plastic, a metal or a celiulosic material, a layer of a polymer that is soluble in a non-neutral aqueous medium and a layer of a plastic.
Ein Verbund kann zweckmässig eine Schicht eines Metalles und dabei insbesondere eine Metallfolie und eine Schicht eines Kunststoffes und dabei insbesondere eine Kunststoffolie, enthalten, wobei zwischen den beiden Schichten resp. Folien eine Schicht z.B. in Folienform, eines in nichtneutralem wässrigem Medium löslichen Polymerisates befindet. A composite can expediently contain a layer of a metal and in particular a metal foil and a layer of a plastic and in this case in particular a plastic film, with between the two layers respectively. Foils one layer e.g. is in film form, a polymer which is soluble in non-neutral aqueous medium.
Ein erfindungsgemässer Verbund kann beispielsweise auch zwei Schichten verschiedener Kunststoffe aufweisen, wobei sich zwischen den zwei Schichten eine Schicht eines in nichtneutralem wässrigem Medium löslichen Polymerisates befindet. A composite according to the invention can, for example, also have two layers of different plastics, a layer of a polymer which is soluble in a non-neutral aqueous medium being located between the two layers.
Sinngemäss können auch Verbünde vorgesehen werden, die mehr als die drei genannten Schichten aufweisen. Correspondingly, networks can be provided that have more than the three layers mentioned.
Beispielsweise können zwei gleiche oder ver- For example, two identical or different
eçhiedene Kunststoffechichten und dazwischen eine Metallfolie in einem Verbund enthalten sein, wobei ein- oder beidseitig auf der Metallfolie eine Schicht eines in nichtneutralem wässrigem Medium löslichen Polymerisates angeordnet ist. Various plastic layers and between them a metal foil can be contained in a composite, a layer of a polymer which is soluble in non-neutral aqueous medium being arranged on one or both sides of the metal foil.
Andere Beispiele, in nicht abschliessender Aufzählung, sind Verbünde enthaltend wenigstens zwei Schichten aus Kunststoffolien und zwischen den Kunststoffolien wenigstens eine Schicht eines in nichtneutralem wässrigem Medium löslichen Polymerisates und eine oder mehrere Sperrschichten, insbesondere keramische Schichten. Other examples, in a non-exhaustive list, are composites containing at least two layers of plastic films and between the plastic films at least one layer of a polymer that is soluble in non-neutral aqueous medium and one or more barrier layers, in particular ceramic layers.
Zweckmässig weisen die Verbünde jeweils zwischen Schichten verschiedener Werkstoffe oder verschiedener Kunststoffe eine Schicht des in nichtneutralem wässrigem Medium löslichen Polymerisates auf. Der jeweilige Schichtaufbau richtet sich nach den Erfordernissen der Praxis. The composites expediently each have a layer of the polymer which is soluble in a non-neutral aqueous medium, between layers of different materials or different plastics. The respective layer structure is based on practical requirements.
Als Schichten eines in nichtneutralem wässrigem Medium löslichen Polymerisates können verschiedene Polymerisate verwendet werden. Various polymers can be used as layers of a polymer which is soluble in a non-neutral aqueous medium.
Beispiele sind Aminogruppen enthaltende Polymerisate aus mindestens einem Acryiat und einem Aminoacrylat, sowie gegebenenfalls neutralen Vinyl-monomeren, die von den Acrylaten verschieden sind. Examples are polymers containing amino groups from at least one acrylate and an aminoacrylate, and optionally neutral vinyl monomers which are different from the acrylates.
Solche Polymerisate sind in neutralem bis basischem Medium unlöslich, sind jedoch in saurem, wässrigem Medium löslich. Such polymers are insoluble in neutral to basic medium, but are soluble in acidic, aqueous medium.
Die genannten Polymerisate sind an sich bekannt und weiterführende Angaben lassen sich z.B. der EP 0 320 757 entnehmen. The polymers mentioned are known per se and further information can be obtained e.g. see EP 0 320 757.
Ein anderes Beispiel eines Polymerisates, das in alkalischem, wässrigem Medium löslich ist, besteht im wesentlichen aus einem Copolymerisat aus Ethylacrylat und Methacrylsäure mit einem Molverhältnis im Bereich von 2:1 bis 4:1. Das Molekulargewicht der Copolymerisate kann im Bereich von 50 000 bis 100 000 und insbesondere bei 60 000 bis 80 000 liegen. Another example of a polymer which is soluble in an alkaline, aqueous medium consists essentially of a copolymer of ethyl acrylate and methacrylic acid with a molar ratio in the range from 2: 1 to 4: 1. The molecular weight of the copolymers can be in the range from 50,000 to 100,000 and in particular from 60,000 to 80,000.
Die Polymerisate an sich sind aus der EP 0 316 676 bekannt. Weiterführende Angaben lassen sich der Patentschrift entnehmen. The polymers themselves are known from EP 0 316 676. Further information can be found in the patent specification.
Polymerisate, die in saurem und alkalischem wässrigem Medium löslich sind, bestehen vorzugsweise aus einem Copolymerisat von Acryl- und/oder Methacrylsäure und Acryiat und/oder Methacrylat. Polymers that are soluble in acidic and alkaline aqueous medium preferably consist of a copolymer of acrylic and / or methacrylic acid and acrylate and / or methacrylate.
Dabei ist das Acryiat und/oder Methacrylat vorzugsweise ein Ester von Acrlysäure und/oder Methacrylsäure mit einem Alkohol, der 1 bis 18 C-Atome, besitzt. Der Kunststoff besitzt vorteilhaft ein Molgewicht von 50 000 bis 200 000. Weiterführende Angaben zu diesem an sich bekannten Polymerisat sind in der EP 0 330 997 enthalten. Ein Beispiel für ein erfindungsgemäss zu verwendendes Copolymerisat findet sich beispielsweise in der DE-OS 3 435 468. The acrylate and / or methacrylate is preferably an ester of acrylic acid and / or methacrylic acid with an alcohol which has 1 to 18 carbon atoms. The plastic advantageously has a molecular weight of 50,000 to 200,000. Further information on this polymer, which is known per se, is contained in EP 0 330 997. An example of a copolymer to be used according to the invention can be found, for example, in DE-OS 3 435 468.
Die in nichtneutralem wässrigem Medium löslichen Polymerisate können in Form einer Folie, beispielsweise einer Dicke von 8 (im bis 150 um, vorzugsweise 30 (im bis 100 (im verwendet werden. Die Folien können durch eine Breitschlitzdüse geformt oder als Blasfolie hergestellt werden. The polymers which are soluble in non-neutral aqueous medium can be used in the form of a film, for example a thickness of 8 μm to 150 μm, preferably 30 μm to 100 μm. The films can be shaped by a slot die or produced as a blown film.
Copolymerisate können mit Vorteil in einem Extruder durch radikalische Polymerisation der entsprechenden Monomere hergestellt werden. Copolymers can advantageously be prepared in an extruder by radical polymerization of the corresponding monomers.
5 5
10 10th
15 15
20 20th
25 25th
30 30th
35 35
40 40
45 45
50 50
55 55
60 60
65 65
2 2nd
3 3rd
CH 684 181 A5 CH 684 181 A5
4 4th
Zweckmässig sind Verbünde deren Schicht oder Schichten eines in nichtneutralem wässrigem Medium löslichen Polymerisates in alkalischem Medium mit einem pH von 8 und höher und/oder in saurem Medium mit einem pH von 6 und tiefer löslich ist. Composites whose layers or layers of a polymer which is soluble in non-neutral aqueous medium are expedient in alkaline medium with a pH of 8 and higher and / or in acidic medium with a pH of 6 and lower.
Als Kunststoffe können nicht thermoplastische und thermoplastische Kunststoffe verwendet werden. Thermoplastic and thermoplastic plastics cannot be used as plastics.
Die Kunststoffe können als Folien, Folienverbunde, Extrudate, Coextrudate oder als Formmassen, wie Spritzgussformmassen etc. verwendet werden. The plastics can be used as films, film composites, extrudates, coextrudates or as molding compounds, such as injection molding compounds, etc.
Besonders bevorzugt sind axial oder insbesondere biaxial orientierte Folien oder Folienverbunde aus thermoplastischen Kunststoffen. Axially or in particular biaxially oriented films or film composites made of thermoplastic materials are particularly preferred.
Als thermoplastische Kunststoffe, z.B. zur Bildung einer Folie und als Kunststoffolien zur Bildung oder als Bestandteil von Folienverbunden oder Trägerfolien, können, in beispielhafter Aufzählung, die Thermoplaste auf Acetal-, Acryl-, Amid-, Arylenoxid-, Arylensulfid-, Arylensulfon-, Carbonat-, Cellulose-, Ester-, Imid-, Olefin-, Styrol- und Vinyl-Basis genannt werden. As thermoplastics, e.g. to form a film and as plastic films to form or as a component of film composites or carrier films, the thermoplastics can be exemplified on acetal, acrylic, amide, arylene oxide, arylene sulfide, arylene sulfone, carbonate, cellulose, Ester, imide, olefin, styrene and vinyl base can be mentioned.
Beispiele von Thermoplasten auf Acetal-Basis sind Polyvinylbutyral, Polyformaldehyd, Polyacetal-dehyd, Mischpolymere und Terpolymere derselben. Examples of acetal-based thermoplastics are polyvinyl butyral, polyformaldehyde, polyacetal dehyde, copolymers and terpolymers thereof.
Beispiele für Thermoplaste auf Acryl-Basis sind Polyalkylmethacrylate, z.B. Polymethylmethacryla-te, Polytert-butylacrylat, Mischpolymere und Terpolymere derselben, Vinyl-, Styrol-, Acrylatester- und Methacrylatestermischpolymere und -terpolymere von Acrylnitril und Methacrylnitril. Examples of acrylic-based thermoplastics are polyalkyl methacrylates, e.g. Polymethyl methacrylate, poly-butyl acrylate, copolymers and terpolymers thereof, vinyl, styrene, acrylate ester and methacrylate ester copolymers and terpolymers of acrylonitrile and methacrylonitrile.
Zu den Thermoplasten auf Amid-Basis gehören beispielsweise Polyamid 6, ein Homopolymerisat aus e-Caprolactam (Polycaprolactam); Polyamid 11, ein Polykondensat aus 11-Aminoundecan-säure (Poly-11-aminoundecanamid); Polyamid 12, ein Homopolymerisat aus ü)-Laurinlactam (Polylaurin-lactam); Polyamid 6,6, ein Homopolykondensat aus Hexamethylen-diamin und Adipinsäure (Polyhex-amethylenadipamid); Polyamid 6,10, ein Homopolykondensat aus Hexamethylendiamin und Sebacin-säure (Polyhexamethylensebacamid); Polyamid 6, 12, ein Homopolykondensat aus Hexamethylendiamin und Dodecandisäure (Polyhexamethylendode-canamid) oder Polyamid 6-3-T, ein Homopolykondensat aus Trimethylhexamethylendiamin und Tere-phthalsäure (Polytrimethylhexamethylenterephthal-amid), sowie Gemische davon. The amide-based thermoplastics include, for example, polyamide 6, a homopolymer of e-caprolactam (polycaprolactam); Polyamide 11, a polycondensate of 11-aminoundecanoic acid (poly-11-aminoundecanamide); Polyamide 12, a homopolymer of ü) -laurin lactam (polylaurin-lactam); Polyamide 6,6, a homopolycondensate of hexamethylene diamine and adipic acid (polyhexamethylene adipamide); Polyamide 6.10, a homopolycondensate of hexamethylene diamine and sebacic acid (polyhexamethylene sebacamide); Polyamide 6, 12, a homopolycondensate of hexamethylene diamine and dodecanedioic acid (polyhexamethylene dodecanamide) or polyamide 6-3-T, a homopolycondensate of trimethylhexamethylene diamine and terephthalic acid (polytrimethylhexamethylene terephthalamide), and mixtures thereof.
Beispiele für Thermoplaste auf Carbonat-Basis sind Polycarbonate auf Basis von 2,2-(4,4-Dihy-droxy-diphenol)-propan oder anderer Dihydroxy-diarylalkanen oder Mischungen von Dihydroxy-diarylalkanen mit anderen aromatischen oder aliphatischen Dihydroxyverbindungen, wie 2,2-(4,4'-Dihydroxy-3,3',5,5'-tetrabromdiphenyl)-propan und 2,2-(4,4'-Dihydroxy 3,3', 5,5'-tetramethyldiphenyl)-propan oder beruhen auf 1,1-(4,4'-Dihydroxy-3,3',5,5'-tetrachlordiphenyl)-propan oder 2,2-(4,4'-Dihydroxy-3,3',5,5'-tetramethyldiphenyl)-propan, jeweils umgesetzt beispielsweise mit Phosgen oder Diphenylcarbonat. Mitumfasst sind auch modifizierte Polycarbonate, auf ein Vinylpolymerisat aufgepfropfte Polycarbonate oder mit beispielsweise ABS-Poly-merisaten abgemischte Polycarbonate. Examples of thermoplastics based on carbonate are polycarbonates based on 2,2- (4,4-dihydroxy-diphenol) propane or other dihydroxy-diarylalkanes or mixtures of dihydroxy-diarylalkanes with other aromatic or aliphatic dihydroxy compounds, such as 2. 2- (4,4'-dihydroxy-3,3 ', 5,5'-tetrabromodiphenyl) propane and 2,2- (4,4'-dihydroxy 3,3', 5,5'-tetramethyldiphenyl) propane or are based on 1,1- (4,4'-dihydroxy-3,3 ', 5,5'-tetrachlorodiphenyl) propane or 2,2- (4,4'-dihydroxy-3,3', 5,5 '-tetramethyldiphenyl) propane, each implemented, for example, with phosgene or diphenyl carbonate. Also included are modified polycarbonates, polycarbonates grafted onto a vinyl polymer or polycarbonates blended with, for example, ABS polymers.
Thermoplaste auf Ester-Basis sind beispielsweise For example, thermoplastics based on esters
Polyalkylenterephthalate oder Polyalkylenisophthala-te, mit Alkylengruppen oder -resten mit 2 bis etwa 10 Kohlenstoffatomen, wobei die Alkylengruppen oder -reste auch mit weinigstens einem -O- unterbrochen sein können, wie z.B. Polyethylentereph-thalat, Polybutylenterephthalat (Polytetramethylente-rephthalat), Polydecamethylenterephthalat, Poly-1,4-cyclohexyldimethylolterephthalat, Mischpolymere und Terpolymere davon. Polyalkylene terephthalates or polyalkylene isophthalates, with alkylene groups or radicals having 2 to about 10 carbon atoms, wherein the alkylene groups or radicals can also be interrupted with at least one -O-, e.g. Polyethylene terephthalate, polybutylene terephthalate (polytetramethylene terephthalate), polydecamethylene terephthalate, poly-1,4-cyclohexyldimethylol terephthalate, copolymers and terpolymers thereof.
Beispiele für Thermoplaste auf Arylenoxid-, Arylensulfon- und Arylensulfid-Basis sind Poly-phenylenoxid, Polyphenylensulfid, Polyethersulfon, Poiyarylether, Polyarylsulfon oder Polysulfon. Examples of thermoplastics based on arylene oxide, arylene sulfone and arylene sulfide are polyphenylene oxide, polyphenylene sulfide, polyether sulfone, polyaryl ether, polyaryl sulfone or polysulfone.
Thermoplaste auf Acetal-, Acryl-, Ester- und Arylenbasis können z.B. auch als Block-copolymere oder als Pfropfpolymere angewendet werden. Thermoplastics based on acetal, acrylic, ester and arylene can e.g. also be used as block copolymers or as graft polymers.
Thermoplaste auf Cellulose-Basis sind z.B. Cellu-loseester, wie Celluloseacetat, Cellulosepropionat, Celluiosebutyrat und Celluloseacetatbutyrat oder polymermodifiziertes Celluloseacetatbutyrat. Thermoplastics based on cellulose are e.g. Cellulose esters, such as cellulose acetate, cellulose propionate, cellulose butyrate and cellulose acetate butyrate or polymer-modified cellulose acetate butyrate.
Beispiele für Thermoplaste auf Imid-Basis sind Poly-N-alkylenmaleimide, wie Poly-N-methylma-leimid, Mischpolymere, Terpolymere oder Blockmischpolymer- und gepfropfte Kautschukmodifikationen derselben, ferner Poly-imde und Copoly-(imid/Amide) von Pyromellithdianhydrid und m-Phenylendiamin oder ähnliche Polyarylenimide und Copoly-(Arylenimid/Amide). Examples of imide-based thermoplastics are poly-N-alkylene maleimides, such as poly-N-methylma-glue, copolymers, terpolymers or block copolymers and grafted rubber modifications thereof, furthermore poly-imde and copoly- (imide / amides) of pyromellitic dianhydride and m -Phenylenediamine or similar polyaryleneimides and copoly- (aryleneimide / amides).
Beispiele für Thermoplaste auf Olefin-Basis sind Polyolefine, wie Polyethylen, z.B. Polyethylen hoher Dichte (HDPE, Dichte grösser als 0,944g/cm3), Polyethylen mittlerer Dichte (MDPE, Dichte 0,926-0,940 g/cm3), lineares Polyethylen mittlerer Dichte (LMDPE, Dichte 0,926-0,940 g/cm3), Polyethylen niedriger Dichte (LDPE, Dichte 0,910-0,925 g/cm3) und lineares Polyethylen niedriger Dichte (LLDPE, Dichte 0,916-0,925 g/cm3), Polypropylen, ataktisches oder isotaktisches Polypropylen, kristallenes und amorphes Polyproylen oder Gemische davon, Poly-1-buten, Poly-3-methylbuten, Poly-4-methyl-penten und Copolymere davon, wie z.B. von Polyethylen mit Vinylacetat, Vinylacetat und Acryl-estern, Vinylalkohol, Acrylsäure, z.B. lonomerharze, wie Copolymerisate von Ethylen mit etwa 11% Acrylsäure, Methacrylsäure, Acrylestern, Methacryl-estern, Tetrafluorethylen oder Polypropylen, sowie statistische Copolymere, Block-Copolymere oder Olefinpolymer-Elastomer-Mischungen. Examples of olefin-based thermoplastics are polyolefins such as polyethylene, e.g. High density polyethylene (HDPE, density greater than 0.944g / cm3), medium density polyethylene (MDPE, density 0.926-0.940 g / cm3), linear medium density polyethylene (LMDPE, density 0.926-0.940 g / cm3), low density polyethylene ( LDPE, density 0.910-0.925 g / cm3) and linear low density polyethylene (LLDPE, density 0.916-0.925 g / cm3), polypropylene, atactic or isotactic polypropylene, crystalline and amorphous polypropylene or mixtures thereof, poly-1-butene, poly 3-methylbutene, poly-4-methylpentene and copolymers thereof, such as of polyethylene with vinyl acetate, vinyl acetate and acrylic esters, vinyl alcohol, acrylic acid, e.g. ionomer resins, such as copolymers of ethylene with about 11% acrylic acid, methacrylic acid, acrylic esters, methacrylic esters, tetrafluoroethylene or polypropylene, and also random copolymers, block copolymers or olefin polymer-elastomer mixtures.
Beispiele für Thermoplaste auf Styrol-Basis sind Polystyrol, Co- und Ter-Polymerisate davon, Copolymerisate mit Acrylnitril (SAN), Copolymerisate mit Butadien (SB) und Terpolymerisate, die Synthesekautschuke und Acrylnitril enthalten (ABS). Examples of thermoplastics based on styrene are polystyrene, copolymers and terpolymers thereof, copolymers with acrylonitrile (SAN), copolymers with butadiene (SB) and terpolymers which contain synthetic rubbers and acrylonitrile (ABS).
Als Thermoplaste auf Vinyl-Basis, die angewendet werden können, sind zu nennen die Polymere des Vinylchlorids und Vinylkunststoffe, enthaltend Vinylchlorideinheiten in deren Struktur, wie Polyvinylchlorid, Copolymere und Pfropfpolymere davon, beispielsweise Vinylchlorid-Ethylen-Polymer, Vinylchlorid-Ethylen-Methacrylat-Polymer, Vinylchlo-rid-Ethylen-Vinylacetat-Polymer, Vinylchlorid-Methyl-methacrylat-Polymer, Vinylchlorid-Octylacrylat-Poly-mer, Vinylchlorid-Vinylidenchiorid-Polymer, Vinylchlo-rid-Vinylacetat-Maleinsäure-Polymer, oder Vinylchlo-rid-Vinylidenchlorid-Acrylnitril-PoIymer, sowie ge5 The vinyl-based thermoplastics which can be used are the polymers of vinyl chloride and vinyl plastics containing vinyl chloride units in their structure, such as polyvinyl chloride, copolymers and graft polymers thereof, for example vinyl chloride-ethylene polymer, vinyl chloride-ethylene-methacrylate polymer , Vinyl chloride-ethylene-vinyl acetate polymer, vinyl chloride-methyl methacrylate polymer, vinyl chloride-octyl acrylate polymer, vinyl chloride-vinylidene chloride polymer, vinyl chloride-vinyl acetate-maleic acid polymer, or vinyl chloride-vinylidene chloride polymer, or Acrylonitrile polymer, and ge5
10 10th
15 15
20 20th
25 25th
30 30th
35 35
40 40
45 45
50 50
55 55
60 60
65 65
3 3rd
5 5
CH 684 181 A5 CH 684 181 A5
6 6
pfropfte Modifikationen. Die Thermoplaste auf Vinyl-Basis können auch auf an sich bekannte Weise mit Primär- oder Sekundärweichmacher weichgemacht sein. grafted modifications. The vinyl-based thermoplastics can also be plasticized in a manner known per se with primary or secondary plasticizers.
Als cellulosische Materialien können beispielsweise Papiere, Pappe, Karton, Halbkarton, Vliese, Filze usw. genannt werden. As cellulosic materials, for example, papers, cardboard, cardboard, half-cardboard, nonwovens, felts, etc. can be mentioned.
Die erfindungsgemässen Verbünde können wenigstens eine Sperrschicht oder Barriereschicht gegen Licht, Gase und Dämpfe wie Sonne, Luft, Sauerstoff und Wasserdampf, enthalten. Ebenfalls wichtig ist eine Sperrwirkung gegen andere chemische, physikalische und auch mikrobielle Einflüsse und gegen Feuchtigkeit, Aromen und Fremdgerüche. Es können beispielsweise Metallfolien, keramische Schichten, metallische Schichten oder Kunststoffolien mit Sperreigenschaften angewendet werden. The composites according to the invention can contain at least one barrier layer or barrier layer against light, gases and vapors such as sun, air, oxygen and water vapor. A barrier effect against other chemical, physical and also microbial influences and against moisture, aromas and foreign smells is also important. For example, metal foils, ceramic layers, metallic layers or plastic foils with barrier properties can be used.
Als Metallfolien können beispielsweise Folien aus Aluminium oder Stahl verwendet werden. For example, foils made of aluminum or steel can be used as metal foils.
Bevorzugt als Metallfolie wird eine Folie aus Aluminium oder Aluminiumlegierungen. A foil made of aluminum or aluminum alloys is preferred as the metal foil.
Die Dicke der Folien aus Aluminium oder Aluminiumlegierungen beträgt z.B. 6 bis 100 um, zweckmässig 7 bis 60 um und bevorzugt 10 bis 50 um. The thickness of the foils made of aluminum or aluminum alloys is e.g. 6 to 100 µm, suitably 7 to 60 µm and preferably 10 to 50 µm.
Als Sperrschicht und dabei insbesondere als keramische Schicht können die Oxide und/oder Nitride von Metallen oder Halbmetallen, z.B. diejenigen des Siliciums, des Aluminiums oder Nickels angewendet werden. Damit umfasst sind auch die Oxinitride der genannten Metalle oder Haibmetalle. Als keramische Schicht werden zweckmässig Oxide der allgemeinen Formel SiOx, wobei x eine Zahl von 1 bis 2 darstellt, oder der allgemeinen Formel AlyOz, wobei y/z eine Zahl von 0,2 bis 1,5 darstellt, angewendet. As oxides and / or nitrides of metals or semimetals, e.g. those of silicon, aluminum or nickel can be used. This also includes the oxynitrides of the metals or halides mentioned. Oxides of the general formula SiOx, where x is a number from 1 to 2, or of the general formula AlyOz, where y / z is a number from 0.2 to 1.5, are expediently used as the ceramic layer.
Als keramische Schichten sind die Siliciumoxide oder Aiuminiumoxide zweckmässig. Die Siliciumoxide können die Formel SiOx, wobei x bevorzugt eine Zahl von 1 bis 2 darstellt, besonders bevorzugt von 1,1 bis 1,9 und insbesondere von 1,2 bis 1,7 darstellt, aufweisen. Die Aluminiumoxide können die Formel AlyOz, wobei y/z z.B. eine Zahl von 0,2 bis 1,5 und bevorzugt von 0,65 bis 0,85 darstellt, aufweisen. The silicon oxides or aluminum oxides are expedient as ceramic layers. The silicon oxides can have the formula SiOx, where x preferably represents a number from 1 to 2, particularly preferably from 1.1 to 1.9 and in particular from 1.2 to 1.7. The aluminum oxides can have the formula AlyOz, where y / z e.g. represents a number from 0.2 to 1.5 and preferably from 0.65 to 0.85.
Die keramische Schicht wird beispielsweise durch eine Vakuumdünnschichttechnik, zweckmässig auf der Basis von Elektronenstrahlverdampfen oder Widerstandsheizen oder induktivem Heizen aus Tiegeln zweckmässig auf eine Trägerfolie aufgebracht. Bevorzugt ist das Elektronenstrahlverdampfen. Die beschriebenen Verfahren können reaktiv und/oder mit Ionenunterstützung gefahren werden. The ceramic layer is, for example, expediently applied to a carrier film by vacuum thin-film technology, advantageously on the basis of electron beam evaporation or resistance heating or inductive heating from crucibles. Electron beam evaporation is preferred. The described methods can be carried out reactively and / or with ion support.
Die Dicke der keramischen Schicht kann von 5 bis 500 nm (Nanometer) betragen, wobei Schichtdicken von 10 bis 200 nm bevorzugt und von 40 bis 150 nm besonders bevorzugt sind. The thickness of the ceramic layer can be from 5 to 500 nm (nanometers), layer thicknesses from 10 to 200 nm being preferred and from 40 to 150 nm being particularly preferred.
Zweckmässig beträgt die Menge an Oxiden und/ oder Nitriden von Metallen und/oder Halbmetallen einer keramischen Schicht 50 bis 400 mg/m2 Verbund, bevorzugt 100 bis 150 mg/m2 Verbund und insbesondere 110 bis 130 mg/m2 Verbund. The amount of oxides and / or nitrides of metals and / or semimetals of a ceramic layer is expediently 50 to 400 mg / m2 composite, preferably 100 to 150 mg / m2 composite and in particular 110 to 130 mg / m2 composite.
Die Sperrschicht kann auch eine metallische Schicht darstellen. Beispiel einer metallischen Schicht ist eine Aluminiumschicht. Metallische Schichten werden in der Regel durch Sputtern, Aufdampfen oder stromlose chemische oder elektrolytische Abscheidung z.B. auf eine Trägerfolie aufgebracht. The barrier layer can also be a metallic layer. An example of a metallic layer is an aluminum layer. Metallic layers are usually created by sputtering, vapor deposition or electroless chemical or electrolytic deposition e.g. applied to a carrier film.
Metallische Schichten sind beispielsweise 5 bis 500 nm, zweckmässig 10 bis 200 nm und vorzugsweise 40 bis 150 nm dick. Metallic layers are, for example, 5 to 500 nm, advantageously 10 to 200 nm and preferably 40 to 150 nm thick.
Es ist auch bevorzugt, eine Kunststoffsperrschicht, insbesondere eine Kunststoffolie mit Sperreigenschaften allein oder im Verbund mit anderen Folien aus den genannten thermoplastischen Kunststoffen anzuwenden. Folien mit Sperreigenschaften sind an sich bekannt und können z.B. aus Ethylen-vinylalkohol-Copolymeren, Polyvinylidenchlorid, Po-lyacrilnitril, z.B. BAREX, Polyacryl-Polyamid-Copoly-mere Sperrschicht-Copolyester, z.B. Mitsui B-010, aromatische und amorphe Polyamide, z.B. N-MXD6 der Mitsubishi Gas Chemical, bestehen oder diese Polymere enthalten und können z.B. 6 (im bis 200 um dick sein. It is also preferred to use a plastic barrier layer, in particular a plastic film with barrier properties, alone or in combination with other films made of the thermoplastic materials mentioned. Films with barrier properties are known per se and can e.g. from ethylene-vinyl alcohol copolymers, polyvinylidene chloride, polyacrylonitrile, e.g. BAREX, polyacrylic-polyamide-copolymer barrier copolyester, e.g. Mitsui B-010, aromatic and amorphous polyamides, e.g. N-MXD6 from Mitsubishi Gas Chemical, or contain these polymers and can e.g. 6 (im up to 200 µm thick.
Nach vorliegender Erfindung sind Verbünde zweckmässig, die wenigstens eine Sperrschicht gegen Gase, Feuchtigkeit und Dämpfe enthalten. According to the present invention, composites are expedient which contain at least one barrier layer against gases, moisture and vapors.
Bevorzugt ist in den Verbunden eine Sperrschicht insbesondere eine Metallfolie oder eine keramische Schicht. A barrier layer, in particular a metal foil or a ceramic layer, is preferred in the composites.
Wird eine keramische oder metallische Schicht vorgesehen, so wird diese zweckmässig auf eine Trägerschicht aufgebracht. Die Trägerschicht kann eine Folie oder ein Folienverbund aus den genannten thermoplastischen Kunststoffen darstellen oder die Trägerschicht kann auch das in nichtneutralem wässrigem Medium lösliche Polymerisat sein. If a ceramic or metallic layer is provided, this is expediently applied to a carrier layer. The carrier layer can be a film or a film composite made from the thermoplastic materials mentioned, or the carrier layer can also be the polymer that is soluble in a non-neutral aqueous medium.
Beispielsweise können eine Trägerschicht und darauf aufgebracht wenigstens eine keramische, resp. metallische Schicht eine der Schichten des erfindungsgemässen Verbundes darstellen. Zweckmässig wird die keramische, respektive metallische Schicht, in einem Verbund derart angeordnet, dass solche Schichten nicht auf die Aussenseiten des fertigen Verbundes zu liegen kommen. For example, a carrier layer and at least one ceramic, or. metallic layer represent one of the layers of the composite according to the invention. The ceramic or metallic layer is expediently arranged in a composite in such a way that such layers do not come to lie on the outer sides of the finished composite.
Die Kunststoffolien aus den genannten Thermoplasten können auf an sich bekannte Weise zu Kunststoffolienverbunden verarbeitet werden. The plastic films from the thermoplastics mentioned can be processed to plastic film composites in a manner known per se.
Die Dicke einer einzelnen Kunststoffolie oder der einzelnen Kunststofffolien in Folienverbunden oder Trägerfolien kann beispielsweise bei 8 bis 1000 (im, bevorzugt bei 10 bis 600 (im und insbesondere bei 12 bis 50 (im liegen. The thickness of an individual plastic film or of the individual plastic films in film composites or carrier films can be, for example, 8 to 1000 (im, preferably 10 to 600 (im and in particular 12 to 50 (im.
Die verschiedenen Schichten, z.B. die Kunststofffolien oder -schichten untereinander, die z.B. keramische Schichten enthaltenden Trägerfolien untereinander, wie auch alle Schichten gegenseitig, können mit Kaschierklebern und/oder Haftvermittlern und gegebenenfalls Vorlack durch Kaschieren oder auch durch Heisskalandrieren, Extrusionsbeschich-ten, Coextrusionsbeschichten zu Laminaten oder Folienverbunden verarbeitet werden. The different layers, e.g. the plastic foils or layers with each other, e.g. Backing films containing ceramic layers with one another, as well as all layers with one another, can be processed with laminating adhesives and / or adhesion promoters and, if appropriate, pre-varnish by lamination or also by hot calendering, extrusion coating, coextrusion coating to form laminates or film composites.
Zur Unterstützung und Verbesserung der Verbundhaftung von Haftvermittler und Kaschierkleber, zwischen den Schichten eines Folienverbundes ist es oft zweckmässig, der Haftvermittlerschicht auf der kleberzugewandten Seite eine ausreichende Oberflächenspannung zu vermitteln. Die Erhöhung der Oberflächenspannung kann z.B. durch eine Flammvorbehandlung oder eine Koronabehandlung erfolgen. To support and improve the bond between the bonding agent and lamination adhesive between the layers of a film composite, it is often advisable to impart sufficient surface tension to the bonding agent layer on the side facing the adhesive. The increase in surface tension can e.g. by flame pretreatment or corona treatment.
5 5
10 10th
15 15
20 20th
25 25th
30 30th
35 35
40 40
45 45
50 50
55 55
60 60
65 65
4 4th
7 7
CH 684 181 A5 CH 684 181 A5
8 8th
Die vorstehend genannten Kunststoffolien, resp. Kunststoffoiienverbunde, sowie Metallfolien und cel-luiosische Materialien, können ihrerseits zu den erfindungsgemässen Verbunden verarbeitet werden. The plastic films mentioned above, respectively. Plastic film composites, as well as metal foils and Celiosian materials, can in turn be processed into the composites according to the invention.
Die Laminierung der einzelnen Schichten der delaminierbaren Verbünde kann beispielsweise durch Heisskalandrieren, Kaschierung, Extrusions-kaschieren oder durch Coextrusionsbeschichtung erfolgen, wobei das Extrusionskaschieren bevorzugt ist. The individual layers of the delaminable composites can be laminated, for example, by hot calendering, lamination, extrusion lamination or by coextrusion coating, with extrusion lamination being preferred.
Bei der Extrusionskaschierung kann insbesondere das in nichtneutralem wässrigem Medium lösliche Polymerisat aus dem Extruder durch eine Breitschlitzdüse zwischen zwei zulaufende Schichten, insbesondere in Folienform, aus Kunststoffen, Metallen und/oder celiulosischen Materialien, geführt werden. Die zulaufenden Schichten können beispielsweise jede über eine Walze zugeführt und im Walzenspalt zu einem Verbund vereinigt werden. In the case of extrusion lamination, in particular the polymer which is soluble in non-neutral aqueous medium can be passed from the extruder through a slot die between two tapered layers, in particular in the form of a film, made of plastics, metals and / or celiulosic materials. The tapered layers can, for example, each be fed via a roller and combined into a composite in the roller nip.
Beispielsweise kann eine zulaufende Folie eine Folie aus thermoplastischem Kunststoff, wie Po-lyethylenterephthalat, und die andere zulaufende Folie eine Aluminiumfolie sein und das in nichtneutralem wässrigem Medium lösliche Polymerisat wird aus dem Extruder, durch eine Breitschlitzdüse, in Form einer erstarrenden Folie, in einen Walzenspalt geführt. Im Walzenspalt werden die Schichten zu einem Verbund gefügt. For example, a tapered film can be a film made of thermoplastic, such as polyethylene terephthalate, and the other tapered film can be an aluminum film, and the polymer, which is soluble in a non-neutral aqueous medium, is extruded from the extruder, through a slot die, in the form of a solidifying film, into a nip guided. The layers are joined to form a bond in the nip.
Die Kunststoffolien und -verbünde können glasklar, getrübt, durchgefärbt oder farbbedeckt angewendet werden. Damit ist es möglich, z.B. opaque oder undurchsichtige Verbünde zu gestalten. The plastic films and composites can be used crystal clear, cloudy, colored through or covered with color. This makes it possible, e.g. to create opaque or opaque composites.
Bei allen Ausführungsarten kann auch zumindest aussen, wenigstens eine bedruckte, konterbedruckte oder eingefärbte Schicht eines Materials, wie z.B. eine Kunststoffolie oder Papier vorgesehen sein. In all types of construction, at least one outside, at least one printed, counterprinted or colored layer of a material, such as e.g. a plastic film or paper may be provided.
Auf wenigstens einer Seite eines delaminierbaren Verbundes nach vorliegender Erfindung können Siegelschichten z.B. als Siegellacke oder Siegelfolien angebracht sein. On at least one side of a delaminable composite according to the present invention, sealing layers e.g. as sealing waxes or sealing foils.
Die Siegelschichten sind an sich bekannt, und können beispielsweise LLDPE, LDPE, MDPE, HDPE, Polypropylen und Polylethylenterephthalat enthalten oder daraus bestehen und in Folien- oder Lackform vorliegen und diese können beispielsweise eine Dicke im Bereich von 1 bis 50 um für Lak-ke und 5 bis 100 (im für Folien aufweisen. Entsprechend können auch an sich bekannte Heisssiegel-lacke Verwendung finden. The sealing layers are known per se and can, for example, contain or consist of LLDPE, LDPE, MDPE, HDPE, polypropylene and polyethyleneterephthalate and can be in film or lacquer form and these can have a thickness in the range from 1 to 50 μm for lacquer and 5 to 100 (mm for foils. Correspondingly, heat-seal lacquers known per se can also be used.
Delaminierbare Verbünde können beispielsweise den nachfolgenden Schichtaufbau aufweisen: Delaminable composites can have the following layer structure, for example:
a) Polyolefin, insbesondere Polyethylen oder Polypropylen, a) polyolefin, in particular polyethylene or polypropylene,
b) in nichtneutralem wässrigem Medium lösliches Polymerisat, b) polymer soluble in non-neutral aqueous medium,
c) Metallfolie, insbesondere Aluminiumfolie, c) metal foil, in particular aluminum foil,
oder a) Polyester, insbesondere Polyethylenterephtha-lat, or a) polyester, in particular polyethylene terephthalate,
b) in nichtneutralem wässrigem Medium lösliches Polymerisat, b) polymer soluble in non-neutral aqueous medium,
c) Metallfolie, insbesondere Aluminiumfolie, c) metal foil, in particular aluminum foil,
oder a) Polyolefin, insbesondere Polyethylen oder Polypropylen, or a) polyolefin, in particular polyethylene or polypropylene,
b) in nichtneutralem wässrigem Medium lösliches Polymerisat, b) polymer soluble in non-neutral aqueous medium,
c) Metallfolie, insbesondere Aluminiumfolie, c) metal foil, in particular aluminum foil,
b') in nichtneutralem wässrigem Medium lösliches Polymerisat, b ') polymer soluble in non-neutral aqueous medium,
a') Polyolefin, insbesondere Polyethylen oder Polypropylen. a ') Polyolefin, especially polyethylene or polypropylene.
Die Schichten können durch Extrusionskaschierung, mit einem Haftvermittler oder durch Lackka-schierung, gegeneinander kaschiert werden. Die Schichten a) und b) und a') und b') können auch in einem ersten Schritt durch Coextrusionsbeschichtung, in Abhängigkeit von der Schicht; Extrusionskaschierung oder Heisskalandrierung gegeneinander kaschiert werden, die Schicht c) kann in einem zweiten Schritt gegen den Verbund a), b) aus dem ersten Schritt kaschiert werden und falls vorgesehen, kann die Schicht a'), b') gegen den Verbund a), b), c) kaschiert werden. The layers can be laminated against each other by extrusion lamination, with an adhesion promoter or by lacquer lamination. The layers a) and b) and a ') and b') can also in a first step by coextrusion coating, depending on the layer; Extrusion lamination or hot calendering can be laminated against each other, layer c) can be laminated against composite a), b) from the first step in a second step and, if provided, layer a '), b') against composite a), b), c) are laminated.
Die Dicken der einzelnen Schichten können beispielsweise für Schichten a) und a') 10 bis 200 um, vorzugsweise 50 um, für Schichten b) und b') 10 bis 50 um, vorzugsweise 20 um, und für Schichten c) 7 bis 100 um, vorzugsweise 20 um, betragen. The thicknesses of the individual layers can be, for example, 10 to 200 μm, preferably 50 μm for layers a) and a ′), 10 to 50 μm, preferably 20 μm for layers b) and b ′), and 7 to 100 μm for layers c) , preferably 20 µm.
Zweckmässig sind auch Kunststoff-Verbunde. Bevorzugt in Kunststoff-Verbunden sind Sperrschichten. Besonders bevorzugt als Sperrschichten sind dabei keramische Schichten. Plastic composites are also useful. Barrier layers are preferred in plastic composites. Ceramic layers are particularly preferred as barrier layers.
Keramische Schichten sind deshalb bedeutungsvoll, da deren geringe Mengen, welche eine Sperrschicht ergeben, bei der Rezyklierung der Kunststoffe weder mengenmässig noch durch eine Reaktivität ins Gewicht fallen. Ceramic layers are important because their small amounts, which result in a barrier layer, are neither important in terms of quantity nor due to reactivity when recycling plastics.
Beispielsweise kann ein solcher Verbund die Schichten enthalten: For example, such a composite can contain the layers:
a) eine Polyethylenterephthaiatfolie einer Dicke von 12 bis 50 um, a) a polyethylene terephthalate film with a thickness of 12 to 50 μm,
b) darauf abgeschieden eine keramische Schicht, b) deposited on it a ceramic layer,
c) in nichtneutralem wässrigem Medium lösliches Polymerisat d) eine Polyolefinfolie, wie eine Polyethylen- oder Polypropylenfolie, in einer Dicke von 12 bis 50 um. c) polymer soluble in non-neutral aqueous medium d) a polyolefin film, such as a polyethylene or polypropylene film, in a thickness of 12 to 50 μm.
Die Verbünde nach vorliegender Erfindung sind deshalb besonders geeignet für Verpackungsmaterialien, Packstoffe und Verpackungen aller Art. The composites according to the present invention are therefore particularly suitable for packaging materials, packaging materials and packaging of all kinds.
Beispielsweise können aus den erfindungsgemässen Verbunden Verpackungsmaterialien oder Packstoffe für flexible oder halbstarre Verpackungen hergestellt werden. For example, packaging materials or packaging materials for flexible or semi-rigid packaging can be produced from the composites according to the invention.
Das Verpackungsmaterial oder der Packstoff kann z.B. auf marktüblichen Verpackungsmaschinen zu flexiblen oder halbstarren Verpackungen, wie beispielsweise Beuteln, Siegelnahtbeuteln, Schlauchbeuteln, Standbeuteln, Sachets, Einwick-lern, Taschen, Schalen, Bedeckelungen, Nahrungsmittelbehälter, Menueschalen, Tuben und durch Zie- The packaging material or packaging material can e.g. on conventional packaging machines for flexible or semi-rigid packaging, such as bags, sealed seam bags, tubular bags, stand-up bags, sachets, wrappers, bags, trays, covers, food containers, dinner trays, tubes and by means of goats
5 5
10 10th
15 15
20 20th
25 25th
30 30th
35 35
40 40
45 45
50 50
55 55
60 60
65 65
5 5
g G
CH 684 181 A5 CH 684 181 A5
10 10th
hen oder Tiefen verformte Packungen, verarbeitet werden. Durch Siegeln mittels Kaltsiegel-, Heisssie-gei-, Induktions- bzw. Ultraschallsiegeltechnik können Nähte gelegt und Verpackungen erzeugt werden und die Verpackungen dicht verschlossen werden. Diese Verarbeitungstechniken sind an sich bekannt. or deeply deformed packs. Sealing using cold sealing, hot sealing, induction or ultrasonic sealing technology enables seams to be placed and packaging to be produced and the packaging to be tightly sealed. These processing techniques are known per se.
Die vorliegende Erfindung betrifft auch die Verwendung von erfindungsgemässen Verpackungen zur Aufnahme von verschiedenen Füllgütern. The present invention also relates to the use of packaging according to the invention for holding various filling goods.
Die Verpackungen eignen sich zur Aufnahme von Füllgütern jeder Art, z.B. der chemischen Industrie, der pharmzeutischen Industrie, der Kosmetikindustrie oder der Nahrungsmittelindustrie. The packaging is suitable for holding any kind of filling, e.g. the chemical industry, the pharmaceutical industry, the cosmetics industry or the food industry.
Nach dem Gebrauch können die Verpackungsmaterialien und Packstoffe auf einfache Weise sortenrein rezykliert werden. Die Verpackungsmaterialien und Packstoffe, wie auch alle anderen aus den erfindungsgemässen Verbundmaterialien hergestellten Gegenstände können z.B. zerkleinert werden. Eine Zerkleinerung ist insbesondere bei grossflächig anfallenden Materialien zweckmässig. After use, the packaging materials and packaging materials can be easily recycled sorted. The packaging materials and packaging materials, like all other objects made from the composite materials according to the invention, can e.g. be crushed. Crushing is particularly useful for large-area materials.
Die Materialien können dann, entsprechend der Natur des in nichtneutralem wässrigem Medium löslichen Polymerisates, in entsprechende Medien gegeben werden. Depending on the nature of the polymer which is soluble in non-neutral aqueous medium, the materials can then be added to appropriate media.
Beispielsweise können die Verbünde in alkalische wässrige Medien, wie Lösungen von Alkalicarbona-ten, Alkalihydrogencarbonaten, Alkaiimetasilicaten, Alkalihydroxiden oder Ammoniaklösungen gegeben werden oder die Verbünde können in einer wässri-gen Säure, beispielsweise einer organischen Säure oder einer Mineralsäure, wie Ameisensäure, Essigsäure, Salzsäure, Schwefelsäure etc. gegeben werden. For example, the compounds can be placed in alkaline aqueous media, such as solutions of alkali metal carbonates, alkali metal bicarbonates, alkali metal silicates, alkali metal hydroxides or ammonia solutions, or the compounds can be placed in an aqueous acid, for example an organic acid or a mineral acid, such as formic acid, acetic acid, hydrochloric acid , Sulfuric acid etc. are given.
Anstelle von wässrigen sauren oder alkalischen Lösungen können auch organische Lösungsmittel verwendet werden. Geeignete organische Lösungsmittel sind z.B. Alkohole wie Methanoi, Ethanol, Propanol, Ketone, wie Aceton, Aromaten, wie Benzol oder Toluol oder Ester, wie Ethylacetat. Instead of aqueous acidic or alkaline solutions, organic solvents can also be used. Suitable organic solvents are e.g. Alcohols such as methanoi, ethanol, propanol, ketones such as acetone, aromatics such as benzene or toluene or esters such as ethyl acetate.
Bei dieser Behandlung zerfallen die Verbünde in ihre Schichten, soweit lösliche Polymerisate zwischen den Schichten angeordnet waren und damit z.B. in verschiedene Kunststoffsorten oder in die Kunststoff- und Metallsorten etc. Die einzelnen Werkstoffe können dann separiert und der Wiederverwertung zugeführt werden. Das wässrige Medium resp. Lösungsmittel kann ebenfalls aufgearbeitet werden und die darin gelösten Polymerisate zurückgewonnen werden. In this treatment, the composites disintegrate into their layers insofar as soluble polymers were arranged between the layers and thus e.g. in different types of plastic or in the types of plastic and metal, etc. The individual materials can then be separated and recycled. The aqueous medium resp. Solvent can also be worked up and the polymers dissolved therein can be recovered.
Es ist auch möglich, bei z.B. einem fünfschichtigen Verbund verschieden lösliche Polymerisate zwischen den drei zu trennenden Schichten vorzusehen. Eine erste Schichtentrennung kann in z.B. alkalischem, eine zweite Schichtentrennung kann in z.B. saurem Medium erfolgen. Damit gelingt es beispielsweise drei Werkstoffe sortenrein zu trennen. It is also possible to use e.g. to provide a five-layer composite of differently soluble polymers between the three layers to be separated. A first layer separation can e.g. alkaline, a second layer separation can e.g. acidic medium. This makes it possible, for example, to separate three materials by type.
Claims (6)