CA2817174C - Copolymers comprising carboxylic acid groups, sulfo groups and polyalkylene oxide groups as a scale-inhibiting additive to washing and cleaning products - Google Patents
Copolymers comprising carboxylic acid groups, sulfo groups and polyalkylene oxide groups as a scale-inhibiting additive to washing and cleaning products Download PDFInfo
- Publication number
- CA2817174C CA2817174C CA2817174A CA2817174A CA2817174C CA 2817174 C CA2817174 C CA 2817174C CA 2817174 A CA2817174 A CA 2817174A CA 2817174 A CA2817174 A CA 2817174A CA 2817174 C CA2817174 C CA 2817174C
- Authority
- CA
- Canada
- Prior art keywords
- weight
- acid
- formula
- monomers
- monomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to copolymers containing, incorporated by polymerization, a1) 30 to 90 wt % of at least one monoethylenically unsaturated C3-C8-carboxylic acid, an anhydride or a salt thereof; a2) 3 to 60 wt % of at least one monomer containing sulfonic acid groups; a3) 3 to 60 wt % of at least one non-ionic monomer of the formula I H2C=C (R1) (CH2)xO [R2-O]o-R3 (I), in which R1 is hydrogen or methyl, R2 is identical or different, linear or branched C2-C6-alkylene residues, which can be arranged in blocks or statistically, and R3 is hydrogen or a linear-chain or branched C1-C4-alkyl residue, x is 0, 1 or 2, and o is a natural number from 3 to 50; a4) 0 to 30 wt % of one or more additional ethylenically unsaturated monomers, which can be polymerized with a1), a2), and a3), wherein the sum of a1), a2), a3) and a4) equals 100 wt %.
Description
=
= .
As originally filed Copolymers comprising carboxylic acid groups, sulfo groups and polyalkylene oxide groups as a scale-inhibiting additive to washing and cleaning products Description The invention relates to copolymers comprising carboxylic acid groups, sulfo groups and polyalkylene oxide groups, and to the use thereof as a scale-inhibiting additive to washing and cleaning products, especially to phosphate-containing and phosphate-free detergent formulations for machine dishwashing.
Machine dishwashing should deliver the washed dishes in a residue-free cleaned condition with a faultlessly shiny surface, for which a detergent, a rinse aid and regenerating salt for water softening typically have to be used. "3 in 1"
dishwasher detergents were introduced to the market in 2001 and combine the functions of detergent, rinse aid and regenerating salt in one product. In addition to detergent components for removal of the soiling on the ware, they comprise integrated rinse aid surfactants which ensure that water runs off the whole area of the ware during the rinsing and drying cycle, thus preventing scale and water spots. In addition, they comprise components for binding of the hardness-forming calcium and magnesium ions. As a result, there is no need for the consumer to replenish rinse aid and salt in the machine dishwasher. The incorporation of further functions (for example protection from glass corrosion and protection from the tarnishing of silver) led to the development of x in 1 (where, for example, x = 6 or 9) or "all in one" products.
Copolymers composed of carboxyl-containing and sulfo-containing monomers have been an important part of phosphate-containing and phosphate-free machine dishwashing detergents for many years. However, the contribution that they make to the detergent and rinsing performance and in particular the contribution that they make to the prevention of scale on the ware is still in need of improvement.
EP-A 0 778 340 describes the use of copolymers of allyl alcohol ethoxylates and acrylic acid in phosphate-free dishwasher detergent compositions.
WO 05/08527 discloses sulfo-containing copolymers, the preparation of the copolymers and the use thereof as an additive to washing, cleaning and rinse aid products. The copolymers comprise (a) 70 to 100 mol% of at least two different monoethylenically unsaturated carboxylic acid monomers and (b) 0 to 30 mol /0 of one
= .
As originally filed Copolymers comprising carboxylic acid groups, sulfo groups and polyalkylene oxide groups as a scale-inhibiting additive to washing and cleaning products Description The invention relates to copolymers comprising carboxylic acid groups, sulfo groups and polyalkylene oxide groups, and to the use thereof as a scale-inhibiting additive to washing and cleaning products, especially to phosphate-containing and phosphate-free detergent formulations for machine dishwashing.
Machine dishwashing should deliver the washed dishes in a residue-free cleaned condition with a faultlessly shiny surface, for which a detergent, a rinse aid and regenerating salt for water softening typically have to be used. "3 in 1"
dishwasher detergents were introduced to the market in 2001 and combine the functions of detergent, rinse aid and regenerating salt in one product. In addition to detergent components for removal of the soiling on the ware, they comprise integrated rinse aid surfactants which ensure that water runs off the whole area of the ware during the rinsing and drying cycle, thus preventing scale and water spots. In addition, they comprise components for binding of the hardness-forming calcium and magnesium ions. As a result, there is no need for the consumer to replenish rinse aid and salt in the machine dishwasher. The incorporation of further functions (for example protection from glass corrosion and protection from the tarnishing of silver) led to the development of x in 1 (where, for example, x = 6 or 9) or "all in one" products.
Copolymers composed of carboxyl-containing and sulfo-containing monomers have been an important part of phosphate-containing and phosphate-free machine dishwashing detergents for many years. However, the contribution that they make to the detergent and rinsing performance and in particular the contribution that they make to the prevention of scale on the ware is still in need of improvement.
EP-A 0 778 340 describes the use of copolymers of allyl alcohol ethoxylates and acrylic acid in phosphate-free dishwasher detergent compositions.
WO 05/08527 discloses sulfo-containing copolymers, the preparation of the copolymers and the use thereof as an additive to washing, cleaning and rinse aid products. The copolymers comprise (a) 70 to 100 mol% of at least two different monoethylenically unsaturated carboxylic acid monomers and (b) 0 to 30 mol /0 of one
2 or more nonionic monomers. The sulfo groups are introduced by amidation with an amino-C1-02-alkanesulfonic acid.
WO 2005/042684 describes the use of specific copolymers of acrylic acid, methacrylic acid and acrylic acid alkoxylates as scale-inhibiting additives in machine dishwashing.
DE 102 25 794 describes the use of sulfo-containing copolymers formed from 30 to 95 mol% of a monoethylenically unsaturated carboxylic acid, 3 to 35 mol% of at least one sulfa-containing monomer and 2 to 35 mol% of a (meth)acrylic acid alkoxylate as a scale-inhibiting additive to washing and cleaning products. In the examples, copolymers formed from (meth)acrylic acid, methoxy polyethylene glycol methacrylate and sulfoethylmethacrylic acid sodilim salt are used. In a further example, a binary copolymer formed from acrylic acid and 2-acrylamido-2-methylpropanesulfonic acid is =
used.
WO 2008/132131 describes the use of sulfo-containing copolymers formed from 30 to 95 mol% of acrylic acid and/or methacrylic acid, 3 to 35 mol% of a sulfa-containing monomer and 2 to 35 mol% of a nonionic monomer of the formula H2C=C(R2)-COO-R3-[-R4-0-]8,-R5 as a scale-inhibiting additive to machine dishwasher detergents for prevention of the formation of calcium phosphate deposits.
WO 2010/024468 describes the use of copolymers formed from a carboxylate-containing monomer, a sulfonate-containing polymer and an allyl ether or allyl alcohol ethoxylate with 1 to 5 ethylene oxide groups as an additive to washing and cleaning products. A preferred sulfonate-containing monomer is 2-hydroxy-
WO 2005/042684 describes the use of specific copolymers of acrylic acid, methacrylic acid and acrylic acid alkoxylates as scale-inhibiting additives in machine dishwashing.
DE 102 25 794 describes the use of sulfo-containing copolymers formed from 30 to 95 mol% of a monoethylenically unsaturated carboxylic acid, 3 to 35 mol% of at least one sulfa-containing monomer and 2 to 35 mol% of a (meth)acrylic acid alkoxylate as a scale-inhibiting additive to washing and cleaning products. In the examples, copolymers formed from (meth)acrylic acid, methoxy polyethylene glycol methacrylate and sulfoethylmethacrylic acid sodilim salt are used. In a further example, a binary copolymer formed from acrylic acid and 2-acrylamido-2-methylpropanesulfonic acid is =
used.
WO 2008/132131 describes the use of sulfo-containing copolymers formed from 30 to 95 mol% of acrylic acid and/or methacrylic acid, 3 to 35 mol% of a sulfa-containing monomer and 2 to 35 mol% of a nonionic monomer of the formula H2C=C(R2)-COO-R3-[-R4-0-]8,-R5 as a scale-inhibiting additive to machine dishwasher detergents for prevention of the formation of calcium phosphate deposits.
WO 2010/024468 describes the use of copolymers formed from a carboxylate-containing monomer, a sulfonate-containing polymer and an allyl ether or allyl alcohol ethoxylate with 1 to 5 ethylene oxide groups as an additive to washing and cleaning products. A preferred sulfonate-containing monomer is 2-hydroxy-
3-allyloxypropanesulfonic acid.
It is an object of the invention to provide copolymers which are notable for advantageous use properties, especially for their scale-inhibiting action and wide usability in the machine dishwashing sector, in phosphate-containing and phosphate-free dishwasher detergents.
It is a further object of the invention to provide improved phosphate-containing and phosphate-free detergent formulations for machine dishwashing, which give rise to an improved washing outcome. It is a particular object of the invention to provide such formulations, which give rise to streak-, deposit- and drip-free dishware without use of additional rinse aid.
=
. =
The object is achieved by copolymers which comprise, in copolymerized form, al) 30 to 90% by weight of at least one monoethylenically unsaturated C3-C8,-carboxylic acid or of an anhydride or salt thereof, a2) 3 to 60% by weight of at least one monomer comprising sulfo groups, a3) 3 to 60% by weight of at least one nonionic monomer of the formula (I) H2C=C(R1)(CH2)x0[R2-0]0-R3 (I) in which R1 is hydrogen or methyl, R2 are identical or different, linear or branched C2-C6-alkylene radicals which may be arranged in blocks or randomly, and R3 is hydrogen or a straight-chain or branched C1-C4-alkyl radical, x is 0, 1 or 2 and o is a number from 3 to 50, a4) 0 to 30% by weight of one or more further ethylenically unsaturated monomers which are polymerizable with al), a2) and a3), where the sum of al), a2), a3) and a4) adds up to 100% by weight.
The object is also achieved by the use of the copolymers as a scale-inhibiting additive to washing and cleaning products, especially to phosphate-free or phosphate-containing detergent formulations for machine dishwashing.
It has been found that, by adding the inventive copolymers which comprise carboxylic acid groups, sulfo groups and polyalkylene oxide groups to phosphate-containing and phosphate-free machine dishwasher detergents, outstanding cleaning and rinse aid performance and excellent scale inhibition both with respect to inorganic and organic deposits can be achieved.
The object is additionally achieved by a detergent formulation for machine dishwashing, comprising, as components:
a) 1 to 20% by weight of at least one copolymer which comprises, in copolymerized form, al) 30 to 90% by weight of at least one monoethylenically unsaturated C3-C8-carboxylic acid or of an anhydride or salt thereof, a2) 3 to 60% by weight of a monomer comprising sulfo groups, a3) 3 to 60% by weight of at least one nonionic monomer of the formula (I) H2C=C(R1)(CH2)x0[R2-0]0-R3 (I) . .
It is an object of the invention to provide copolymers which are notable for advantageous use properties, especially for their scale-inhibiting action and wide usability in the machine dishwashing sector, in phosphate-containing and phosphate-free dishwasher detergents.
It is a further object of the invention to provide improved phosphate-containing and phosphate-free detergent formulations for machine dishwashing, which give rise to an improved washing outcome. It is a particular object of the invention to provide such formulations, which give rise to streak-, deposit- and drip-free dishware without use of additional rinse aid.
=
. =
The object is achieved by copolymers which comprise, in copolymerized form, al) 30 to 90% by weight of at least one monoethylenically unsaturated C3-C8,-carboxylic acid or of an anhydride or salt thereof, a2) 3 to 60% by weight of at least one monomer comprising sulfo groups, a3) 3 to 60% by weight of at least one nonionic monomer of the formula (I) H2C=C(R1)(CH2)x0[R2-0]0-R3 (I) in which R1 is hydrogen or methyl, R2 are identical or different, linear or branched C2-C6-alkylene radicals which may be arranged in blocks or randomly, and R3 is hydrogen or a straight-chain or branched C1-C4-alkyl radical, x is 0, 1 or 2 and o is a number from 3 to 50, a4) 0 to 30% by weight of one or more further ethylenically unsaturated monomers which are polymerizable with al), a2) and a3), where the sum of al), a2), a3) and a4) adds up to 100% by weight.
The object is also achieved by the use of the copolymers as a scale-inhibiting additive to washing and cleaning products, especially to phosphate-free or phosphate-containing detergent formulations for machine dishwashing.
It has been found that, by adding the inventive copolymers which comprise carboxylic acid groups, sulfo groups and polyalkylene oxide groups to phosphate-containing and phosphate-free machine dishwasher detergents, outstanding cleaning and rinse aid performance and excellent scale inhibition both with respect to inorganic and organic deposits can be achieved.
The object is additionally achieved by a detergent formulation for machine dishwashing, comprising, as components:
a) 1 to 20% by weight of at least one copolymer which comprises, in copolymerized form, al) 30 to 90% by weight of at least one monoethylenically unsaturated C3-C8-carboxylic acid or of an anhydride or salt thereof, a2) 3 to 60% by weight of a monomer comprising sulfo groups, a3) 3 to 60% by weight of at least one nonionic monomer of the formula (I) H2C=C(R1)(CH2)x0[R2-0]0-R3 (I) . .
4 in which R1 is hydrogen or methyl, R2 are identical or different, linear or branched C2-C6-alkylene radicals which may be arranged in blocks or randomly, and R.' is hydrogen or a straight-chain or branched Cl-C4-alkyl radical, x is 0, 1 or 2 and o is a number from 3 to 50, a4) 0 to 30% by weight of one or more ethylenically unsaturated monomers which are polymerizable with al), a2) and a3), where the sum of al), a2), a3) and a4) adds up to 100% by weight, b) 0 to 20% by weight of polycarboxylates other than component a), c) 0 to 50% by weight of complexing agents, d) 0 to 70% by weight of phosphates, e) 0 to 60% by weight of further builders and cobuilders, 0 0.1 to 20% by weight of nonionic surfactants, 9) 0 to 30% by weight of bleaches and optionally bleach activators and bleach catalysts, h) 0 to 8% by weight of enzymes, i) 0 to 50% by weight of one or more further additives such as anionic or zwitterionic surfactants, alkali carriers, corrosion inhibitors, defoamers, dyes, fragrances, fillers, organic solvents, tabletting aids, disintegrants, thickeners, solubilizers and water, wherein the sum of components a) to i) adds up to 100% by weight.
The invention also provides a detergent formulation for machine dishwashing, comprising, as components a) 1 to 20% by weight of at least one copolymer which comprises, in copolymerized form, al) 30 to 90% by weight of at least one monomer selected from the group consisting of acrylic acid, methacrylic acid and salts thereof, a2) 3 to 60% by weight of at least one monomer comprising sulfo groups selected from allylsulfonic acid and 2-acrylamido-2-methylpropanesulfonic acid, a3) 3 to 60% by weight of at least one nonionic monomer of the formula I
H2C=C(R1)(CH2),0[R2-0]0-R3 (I) 4a in which R1 is hydrogen or methyl, R2 are identical or different, linear or branched C2-C6-alkylene radicals which may be arranged in blocks or randomly, and R3 is hydrogen or a straight-chain or branched Ci-C4-alkyl radical, x is 0, 1 or 2 and o is a natural number from >5 to 50, a4) 0 to 30% by weight of one or more further ethylenically unsaturated monomers which are polymerizable with al), a2) and a3), where the sum of al), a2), a3) and a4) adds up to 100% by weight, b) 0 to 20% by weight of polycarboxylates other than component a) c) 0.1 to 50% by weight of complexing agents, d) 0 to 70% by weight of phosphates, e) 0.1 to 60% by weight of further builders and cobuilders, f) 0.1 to 20% by weight of nonionic surfactants, g) 0 to 30% by weight of bleaches and optionally bleach activators and bleach catalysts, h) 0.1 to 8% by weight of enzymes, i) 0.1 to 50% by weight of one or more further additives selected from the group consisting of anionic or zwitterionic surfactants, alkali carriers, corrosion inhibitors, defoamers, dyes, fragrances, fillers, organic solvents, tabletting aids, disintegrants, thickeners, solubilizers and water, wherein the sum of components a) to i) adds up to 100% by weight.
The invention also provides a copolymer which comprises, in copolymerized form, al) 30 to 90% by weight of at least one monomer selected from the group consisting of acrylic acid, methacrylic acid and salts thereof, a2) 3 to 60% by weight of at least one monomer comprising sulfo groups selected from allylsulfonic acid and 2-acrylamido-2-methylpropanesulfonic acid, a3) 3 to 60% by weight of at least one nonionic monomer of the formula I
H2C=C(R1)(CH2),0[R2-0]0-R3 (I) in which R1 is hydrogen or methyl, R2 are identical or different, linear or branched C2-C6-alkylene radicals which may be arranged in blocks or randomly, 4b and R3 is hydrogen or a straight-chain or branched Ci-C4-alkyl radical, x is 2 and o is a natural number from >5 to 50, a4) 0 to 30% by weight of one or more further ethylenically unsaturated monomers which are polymerizable with al), a2) and a3), where the sum of al), a2), a3) and a4) adds up to 100% by weight.
The invention also provides a use of the copolymer of the invention as a scale-inhibiting additive in phosphate-free or phosphate-containing detergent formulations for machine dishwashing.
As component al), the copolymer comprises 30 to 90% by weight of at least one monoethylenically unsaturated C3-C8-carboxylic acid, or of an anhydride or a salt thereof.
Suitable unsaturated C3-C8-carboxylic acids are especially acrylic acid, methacrylic acid, ethacrylic acid, vinylacetic acid, allylacetic acid, crotonic acid, maleic acid, fumaric acid, mesaconic acid and itaconic acid, and the water-soluble salts thereof. When the unsaturated C3-C8-carboxylic acids mentioned can form anhydrides, the latter are also suitable as monomers al), for example maleic anhydride, itaconic anhydride and methacrylic anhydride.
Preferred monoethylenically unsaturated C3-C8-carboxylic acids are acrylic acid and methacrylic acid, and the water-soluble salts thereof. Water-soluble salts are especially the sodium and potassium salts of the acids.
As component a2), the copolymer comprises 3 to 60% by weight of at least one monomer comprising sulfo groups.
The sulfo-containing monomers are preferably those of the formulae (Ha) and (11b) H2C=CH-X-S03H - (11a)
The invention also provides a detergent formulation for machine dishwashing, comprising, as components a) 1 to 20% by weight of at least one copolymer which comprises, in copolymerized form, al) 30 to 90% by weight of at least one monomer selected from the group consisting of acrylic acid, methacrylic acid and salts thereof, a2) 3 to 60% by weight of at least one monomer comprising sulfo groups selected from allylsulfonic acid and 2-acrylamido-2-methylpropanesulfonic acid, a3) 3 to 60% by weight of at least one nonionic monomer of the formula I
H2C=C(R1)(CH2),0[R2-0]0-R3 (I) 4a in which R1 is hydrogen or methyl, R2 are identical or different, linear or branched C2-C6-alkylene radicals which may be arranged in blocks or randomly, and R3 is hydrogen or a straight-chain or branched Ci-C4-alkyl radical, x is 0, 1 or 2 and o is a natural number from >5 to 50, a4) 0 to 30% by weight of one or more further ethylenically unsaturated monomers which are polymerizable with al), a2) and a3), where the sum of al), a2), a3) and a4) adds up to 100% by weight, b) 0 to 20% by weight of polycarboxylates other than component a) c) 0.1 to 50% by weight of complexing agents, d) 0 to 70% by weight of phosphates, e) 0.1 to 60% by weight of further builders and cobuilders, f) 0.1 to 20% by weight of nonionic surfactants, g) 0 to 30% by weight of bleaches and optionally bleach activators and bleach catalysts, h) 0.1 to 8% by weight of enzymes, i) 0.1 to 50% by weight of one or more further additives selected from the group consisting of anionic or zwitterionic surfactants, alkali carriers, corrosion inhibitors, defoamers, dyes, fragrances, fillers, organic solvents, tabletting aids, disintegrants, thickeners, solubilizers and water, wherein the sum of components a) to i) adds up to 100% by weight.
The invention also provides a copolymer which comprises, in copolymerized form, al) 30 to 90% by weight of at least one monomer selected from the group consisting of acrylic acid, methacrylic acid and salts thereof, a2) 3 to 60% by weight of at least one monomer comprising sulfo groups selected from allylsulfonic acid and 2-acrylamido-2-methylpropanesulfonic acid, a3) 3 to 60% by weight of at least one nonionic monomer of the formula I
H2C=C(R1)(CH2),0[R2-0]0-R3 (I) in which R1 is hydrogen or methyl, R2 are identical or different, linear or branched C2-C6-alkylene radicals which may be arranged in blocks or randomly, 4b and R3 is hydrogen or a straight-chain or branched Ci-C4-alkyl radical, x is 2 and o is a natural number from >5 to 50, a4) 0 to 30% by weight of one or more further ethylenically unsaturated monomers which are polymerizable with al), a2) and a3), where the sum of al), a2), a3) and a4) adds up to 100% by weight.
The invention also provides a use of the copolymer of the invention as a scale-inhibiting additive in phosphate-free or phosphate-containing detergent formulations for machine dishwashing.
As component al), the copolymer comprises 30 to 90% by weight of at least one monoethylenically unsaturated C3-C8-carboxylic acid, or of an anhydride or a salt thereof.
Suitable unsaturated C3-C8-carboxylic acids are especially acrylic acid, methacrylic acid, ethacrylic acid, vinylacetic acid, allylacetic acid, crotonic acid, maleic acid, fumaric acid, mesaconic acid and itaconic acid, and the water-soluble salts thereof. When the unsaturated C3-C8-carboxylic acids mentioned can form anhydrides, the latter are also suitable as monomers al), for example maleic anhydride, itaconic anhydride and methacrylic anhydride.
Preferred monoethylenically unsaturated C3-C8-carboxylic acids are acrylic acid and methacrylic acid, and the water-soluble salts thereof. Water-soluble salts are especially the sodium and potassium salts of the acids.
As component a2), the copolymer comprises 3 to 60% by weight of at least one monomer comprising sulfo groups.
The sulfo-containing monomers are preferably those of the formulae (Ha) and (11b) H2C=CH-X-S03H - (11a)
5 H2C=C(CH3)-X-S03H (11b) in which X is an optionally present spacer group which may be selected from -(CH2)-where n = 0 to 4, -06H4-, -CH2-0-C6H4-, -C(0)-NH-C(CH3)2-, -C(0)-NH-CH(CH2C113)-, -C(0)NH-CH(CH3)CH2-, -C(0)NH-C(CH3)20H2-, -C(0)NH-CH2CH(OH)CH2-, -C(0)NH-CH2-, -C(0)NH-CH2CH2- and -C(0)NH-CH2CH2CH2-.
Particularly preferred sulfo-containing monomers are 1-acrylamido-1-propanesulfonic acid (X = -C(0)NH-CH(CH2CH3)- in formula 11a), 2-acrylamido-2-propanesulfonic acid (X = -C(0)NH-CH(CH3)CH2- in formula 11a), 2-acrylamido-2-methylpropanesulfonic acid (AMPS, X = -C(0)NH-C(CH3)2CH2- in formula 11a), 2-methacrylamido-2-methyl-propanesulfonic acid (X = -C(0)NH-C(CH3)20H2- in formula 11b), 3-methacrylamido-2-hydroxypropanesulfonic acid (X = -C(0)NH-CH2CH(OH)CH2- in formula 11b), allylsulfonic acid (X = CH2 in formula 11a), methallylsulfonic acid (X = CH2 in formula 11b), allyloxybenzenesulfonic acid (X = -CH2-0-C6H4- in formula 11a), methallyloxybenzenesulfonic acid (X = -CH2-0-C61-14- in formula 11b), 2-hydroxy-3-(2-propenyloxy)propanesulfonic acid, 2-methyl-2-propene-1-sulfonic acid (X =
CH2 in formula 11b), styrenesulfonic acid (X = C6H4 in formula 11a), vinylsulfonic acid (X absent in formula Ha), 3-sulfopropyl acrylate (X = -C(0)0-CH2CH2CH2- in formula 11a), 2-sulfoethyl methacrylate (X = -C(0)0-CH2CH2- in formula 11b), 3-sulfopropyl methacrylate (X = -C(0)0-CH2CH2CH2- in formula 11b), sulfomethacrylamide (X =
-C(0)NH- in formula 11b), sulfomethylmethacrylamide (X = -C(0)NH-0H2- in formula fib) and salts of the acids mentioned. Suitable salts are generally water-soluble salts, preferably the sodium, potassium and ammonium salts of the acids mentioned.
Especially preferred are 1-acrylamidopropanesulfonic acid, 2-acrylamido-2-propanesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid (AMPS), 2-meth-acrylamido-2-methylpropanesulfonic acid, 3-methacrylamido-2-hydroxypropanesulfonic acid, 2-hydroxy-3-(2-propenyloxy)propanesulfonic acid, 2-sulfoethyl methacrylate, styrenesulfonic acid, vinylsulfonic acid, allylsulfonic acid (ALS) and methallylsulfonic acid, and salts of the acids mentioned.
Very particularly preferred sulfo-containing monomers are 2-acrylamido-2-methylpropanesulfonic acid (AMPS) and allylsulfonic acid, and the water-soluble salts thereof, especially the sodium, potassium and ammonium salts thereof.
Particularly preferred sulfo-containing monomers are 1-acrylamido-1-propanesulfonic acid (X = -C(0)NH-CH(CH2CH3)- in formula 11a), 2-acrylamido-2-propanesulfonic acid (X = -C(0)NH-CH(CH3)CH2- in formula 11a), 2-acrylamido-2-methylpropanesulfonic acid (AMPS, X = -C(0)NH-C(CH3)2CH2- in formula 11a), 2-methacrylamido-2-methyl-propanesulfonic acid (X = -C(0)NH-C(CH3)20H2- in formula 11b), 3-methacrylamido-2-hydroxypropanesulfonic acid (X = -C(0)NH-CH2CH(OH)CH2- in formula 11b), allylsulfonic acid (X = CH2 in formula 11a), methallylsulfonic acid (X = CH2 in formula 11b), allyloxybenzenesulfonic acid (X = -CH2-0-C6H4- in formula 11a), methallyloxybenzenesulfonic acid (X = -CH2-0-C61-14- in formula 11b), 2-hydroxy-3-(2-propenyloxy)propanesulfonic acid, 2-methyl-2-propene-1-sulfonic acid (X =
CH2 in formula 11b), styrenesulfonic acid (X = C6H4 in formula 11a), vinylsulfonic acid (X absent in formula Ha), 3-sulfopropyl acrylate (X = -C(0)0-CH2CH2CH2- in formula 11a), 2-sulfoethyl methacrylate (X = -C(0)0-CH2CH2- in formula 11b), 3-sulfopropyl methacrylate (X = -C(0)0-CH2CH2CH2- in formula 11b), sulfomethacrylamide (X =
-C(0)NH- in formula 11b), sulfomethylmethacrylamide (X = -C(0)NH-0H2- in formula fib) and salts of the acids mentioned. Suitable salts are generally water-soluble salts, preferably the sodium, potassium and ammonium salts of the acids mentioned.
Especially preferred are 1-acrylamidopropanesulfonic acid, 2-acrylamido-2-propanesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid (AMPS), 2-meth-acrylamido-2-methylpropanesulfonic acid, 3-methacrylamido-2-hydroxypropanesulfonic acid, 2-hydroxy-3-(2-propenyloxy)propanesulfonic acid, 2-sulfoethyl methacrylate, styrenesulfonic acid, vinylsulfonic acid, allylsulfonic acid (ALS) and methallylsulfonic acid, and salts of the acids mentioned.
Very particularly preferred sulfo-containing monomers are 2-acrylamido-2-methylpropanesulfonic acid (AMPS) and allylsulfonic acid, and the water-soluble salts thereof, especially the sodium, potassium and ammonium salts thereof.
6 As component a3), the copolymer comprises 3 to 60% by weight of at least one nonionic monomer of the formula (I) H2C=C(R1)(CH2)x0[R2-0]0-R3 (I) in which R1 is hydrogen or methyl, R2 is identical or different C2-06-alkylene radicals which may be linear or branched and arranged in blocks or randomly, and R3 is hydrogen or a straight-chain or branched C1-C4-alkyl radical, x is 0, 1, 2 and o is from 3 to 50.
The alkylene radicals may also be arranged in blocks and randomly, i.e. in one or more blocks of identical alkylene oxide radicals and additionally randomly in one or more blocks of two or more different alkylene oxide radicals. This is also included by the wording "arranged in blocks or randomly".
Preferred nonionic monomers a3) are those based on ally! alcohol (R1 = H; x =
1) and isoprenol (R1 = methyl; x = 2).
The nonionic monomer a3) comprises preferably an average of 8 to 40, more preferably 10 to 30, especially 10 to 25, alkylene oxide units. The index o in formula (I) is based on the mean number of alkylene oxide units.
Preferred alkylene oxide units R2-0 are ethylene oxide, 1,2-propylene oxide and 1,2-.. butylene oxide, particular preference being given to ethylene oxide and 1,2-propylene oxide.
In a specific embodiment, the nonionic monomers a3) comprise only ethylene oxide units. In a further specific embodiment, the nonionic monomers a3) comprise ethylene oxide and 1,2-propylene oxide units, which may be arranged in blocks or randomly.
R3 is preferably hydrogen or methyl.
As component a4), the copolymer may comprise 0 to 30% by weight of one or more further ethylenically unsaturated monomers polymerizable with al), a2) and a3).
Useful further ethylenically unsaturated monomers a4) include, for example, acrylamide, t-butylacrylamide, vinyl acetate, vinyl methyl ether, hydroxybutyl vinyl ether, 1-vinylpyrrolidone, 1-vinylcaprolactam, 1-vinylimidazole, 2-vinylpyridine,
The alkylene radicals may also be arranged in blocks and randomly, i.e. in one or more blocks of identical alkylene oxide radicals and additionally randomly in one or more blocks of two or more different alkylene oxide radicals. This is also included by the wording "arranged in blocks or randomly".
Preferred nonionic monomers a3) are those based on ally! alcohol (R1 = H; x =
1) and isoprenol (R1 = methyl; x = 2).
The nonionic monomer a3) comprises preferably an average of 8 to 40, more preferably 10 to 30, especially 10 to 25, alkylene oxide units. The index o in formula (I) is based on the mean number of alkylene oxide units.
Preferred alkylene oxide units R2-0 are ethylene oxide, 1,2-propylene oxide and 1,2-.. butylene oxide, particular preference being given to ethylene oxide and 1,2-propylene oxide.
In a specific embodiment, the nonionic monomers a3) comprise only ethylene oxide units. In a further specific embodiment, the nonionic monomers a3) comprise ethylene oxide and 1,2-propylene oxide units, which may be arranged in blocks or randomly.
R3 is preferably hydrogen or methyl.
As component a4), the copolymer may comprise 0 to 30% by weight of one or more further ethylenically unsaturated monomers polymerizable with al), a2) and a3).
Useful further ethylenically unsaturated monomers a4) include, for example, acrylamide, t-butylacrylamide, vinyl acetate, vinyl methyl ether, hydroxybutyl vinyl ether, 1-vinylpyrrolidone, 1-vinylcaprolactam, 1-vinylimidazole, 2-vinylpyridine,
7 4-vinylpyridine, methyl methacrylate, ethyl acrylate, isobutene, diisobutene, isoprenol, 1-alkenes such as 1-octene, N,N-dimethylacrylamide and styrene.
The proportion of copolymerized monomers al), especially of copolymerized acrylic acid, methacrylic acid or of a water-soluble salt of these acids, is preferably 40 to 90%
by weight, more preferably 45 to 85% by weight and especially preferably 50 to 85% by weight. The proportion of copolymerized monomers a2), especially of copolymerized 2-acrylamido-2-methylpropanesulfonic acid, is preferably 4 to 40% by weight, more preferably 6 to 35% by weight and especially preferably 8 to 32% by weight.
The proportion a3) of monomer units of the formula (I) is preferably 4 to 40% by weight, more preferably 6 to 35% by weight and especially 8 to 32% by weight.
If monomers a4) are present in the inventive copolymers, the proportion thereof is preferably up to 20% by weight, more preferably up to 15% by weight and especially up to 10% by weight.
The inventive copolymers a) generally have a mean molecular weight M, of 2000 to 200 000 g/mol, preferably of 3000 to 100 000 g/mol, more preferably of 10 000 to 50 000 g/mol, determined by gel permeation chromatography at room temperature with .. water as an eluent against polyacrylate standards.
The K values thereof are 15 to 100, preferably 20 to 80, more preferably 30 to 50, measured at pH 7 in 1% by weight aqueous solution at 25 C according to H. Fikentscher, Cellulose-Chemie volume 13, pages 58-64 and 71-74 (1932).
The inventive copolymers can be prepared by free-radical polymerization of the monomers. It is possible to work by any known free-radical polymerization process. In addition to polymerization in bulk, mention should be made especially of the processes of solution polymerization and emulsion polymerization, preference being given to solution polymerization.
The polymerization is preferably performed in water as a solvent. However, it can also be undertaken in alcoholic solvents, especially C1-04-alcohols, such as methanol, ethanol and isopropanol, or mixtures of these solvents with water.
Suitable polymerization initiators are compounds which decompose thermally, by a redox mechanism or photochemically (photoinitiators) to form free radicals.
Among the thermally activable polymerization initiators, preference is given to initiators having a decomposition temperature in the range from 20 to 180 C, especially from 50
The proportion of copolymerized monomers al), especially of copolymerized acrylic acid, methacrylic acid or of a water-soluble salt of these acids, is preferably 40 to 90%
by weight, more preferably 45 to 85% by weight and especially preferably 50 to 85% by weight. The proportion of copolymerized monomers a2), especially of copolymerized 2-acrylamido-2-methylpropanesulfonic acid, is preferably 4 to 40% by weight, more preferably 6 to 35% by weight and especially preferably 8 to 32% by weight.
The proportion a3) of monomer units of the formula (I) is preferably 4 to 40% by weight, more preferably 6 to 35% by weight and especially 8 to 32% by weight.
If monomers a4) are present in the inventive copolymers, the proportion thereof is preferably up to 20% by weight, more preferably up to 15% by weight and especially up to 10% by weight.
The inventive copolymers a) generally have a mean molecular weight M, of 2000 to 200 000 g/mol, preferably of 3000 to 100 000 g/mol, more preferably of 10 000 to 50 000 g/mol, determined by gel permeation chromatography at room temperature with .. water as an eluent against polyacrylate standards.
The K values thereof are 15 to 100, preferably 20 to 80, more preferably 30 to 50, measured at pH 7 in 1% by weight aqueous solution at 25 C according to H. Fikentscher, Cellulose-Chemie volume 13, pages 58-64 and 71-74 (1932).
The inventive copolymers can be prepared by free-radical polymerization of the monomers. It is possible to work by any known free-radical polymerization process. In addition to polymerization in bulk, mention should be made especially of the processes of solution polymerization and emulsion polymerization, preference being given to solution polymerization.
The polymerization is preferably performed in water as a solvent. However, it can also be undertaken in alcoholic solvents, especially C1-04-alcohols, such as methanol, ethanol and isopropanol, or mixtures of these solvents with water.
Suitable polymerization initiators are compounds which decompose thermally, by a redox mechanism or photochemically (photoinitiators) to form free radicals.
Among the thermally activable polymerization initiators, preference is given to initiators having a decomposition temperature in the range from 20 to 180 C, especially from 50
8 to 90 C. Examples of suitable thermal initiators are inorganic peroxo compounds such as peroxodisulfates (ammonium peroxodisulfate and preferably sodium peroxodisulfate), peroxosulfates, percarbonates and hydrogen peroxide; organic peroxo compounds such as diacetyl peroxide, di-tert-butyl peroxide, diamyl peroxide, dioctanoyl peroxide, didecanoyl peroxide, dilauroyl peroxide, dibenzoyl peroxide, bis(o-toly1) peroxide, succinyl peroxide, tert-butyl perneodecanoate, tert-butyl perbenzoate, tert-butyl perisobutyrate, tert-butyl perpivalate, tert-butyl peroctoate, tert-butyl perneodecanoate, tert-butyl perbenzoate, tert-butyl peroxide, tert-butyl hydroperoxide, cumene hydroperoxide, tert-butyl peroxy-2-ethylhexanoate and diisopropyl peroxydicarbamate; azo compounds such as 2,2'-azobisisobutyronitrile, 2,2'-azobis(2-methylbutyronitrile) and azobis(2-amidopropane) dihydrochloride.
These initiators can be used in combination with reducing compounds as initiator/regulator systems. Examples of such reducing compounds include phosphorus compounds such as phosphorous acid, hypophosphites and phosphinates, sulfur compounds such as sodium hydrogensulfite, sodium sulfite and sodium formaldehyde-sulfoxylate, and hydrazine.
Also frequently used are redox initiator systems which consist of a peroxo compound, a metal salt and a reducing agent. Examples of suitable peroxo compounds are hydrogen peroxide, peroxodisulfate (as the ammonium, sodium or potassium salt), peroxosulfates, and organic peroxo compounds such as tert-butyl hydroperoxide, cumene hydroperoxide or dibenzoyl peroxide. Suitable metal salts are in particular iron(II) salts such as iron(II) sulfate heptahydrate. Suitable reducing agents are sodium sulfite, the disodium salt of 2-hydroxy-2-sulfinatoacetic acid, the disodium salt of 2-hydroxy-2-sulfonatoacetic acid, sodium hydroxymethanesulfinate, ascorbic acid, isoascorbic acid or mixtures thereof.
Examples of suitable photoinitiators are benzophenone, acetophenone, benzyl dialkyl ketones and derivatives thereof.
Preference is given to using thermal initiators, preference being given to inorganic peroxo compounds, especially sodium peroxodisulfate. The peroxo compounds are particularly advantageously used in combination with sulfur-containing reducing agents, especially sodium hydrogensulfite, as the redox initiator system. In the case of use of this initiator/regulator system, copolymers comprising ¨S03-Na+ and/or ¨SO4-1\la+ as end groups are obtained, which are notable for exceptional cleaning power and scale-inhibiting action.
These initiators can be used in combination with reducing compounds as initiator/regulator systems. Examples of such reducing compounds include phosphorus compounds such as phosphorous acid, hypophosphites and phosphinates, sulfur compounds such as sodium hydrogensulfite, sodium sulfite and sodium formaldehyde-sulfoxylate, and hydrazine.
Also frequently used are redox initiator systems which consist of a peroxo compound, a metal salt and a reducing agent. Examples of suitable peroxo compounds are hydrogen peroxide, peroxodisulfate (as the ammonium, sodium or potassium salt), peroxosulfates, and organic peroxo compounds such as tert-butyl hydroperoxide, cumene hydroperoxide or dibenzoyl peroxide. Suitable metal salts are in particular iron(II) salts such as iron(II) sulfate heptahydrate. Suitable reducing agents are sodium sulfite, the disodium salt of 2-hydroxy-2-sulfinatoacetic acid, the disodium salt of 2-hydroxy-2-sulfonatoacetic acid, sodium hydroxymethanesulfinate, ascorbic acid, isoascorbic acid or mixtures thereof.
Examples of suitable photoinitiators are benzophenone, acetophenone, benzyl dialkyl ketones and derivatives thereof.
Preference is given to using thermal initiators, preference being given to inorganic peroxo compounds, especially sodium peroxodisulfate. The peroxo compounds are particularly advantageously used in combination with sulfur-containing reducing agents, especially sodium hydrogensulfite, as the redox initiator system. In the case of use of this initiator/regulator system, copolymers comprising ¨S03-Na+ and/or ¨SO4-1\la+ as end groups are obtained, which are notable for exceptional cleaning power and scale-inhibiting action.
9 Alternatively, it is also possible to use phosphorus-containing initiator/regulator systems, for example hypophosphites/phosphinates.
The amounts of -photoinitiator and initiator/regulator system should be matched to the substances used in each case. If, for example, the preferred peroxodisulfate/hydrogensulfite system is used, typically 2 to 6% by weight, preferably 3 to 5% by weight, of peroxodisulfate and generally 5 to 30% by weight, preferably 5 to
The amounts of -photoinitiator and initiator/regulator system should be matched to the substances used in each case. If, for example, the preferred peroxodisulfate/hydrogensulfite system is used, typically 2 to 6% by weight, preferably 3 to 5% by weight, of peroxodisulfate and generally 5 to 30% by weight, preferably 5 to
10% by weight, of hydrogensulfite are used, based in each case on the monomers al), a2), a3) and optionally a4).
If desired, it is also possible to use polymerization regulators. Suitable examples are sulfur compounds such as mercaptoethanol, 2-ethylhexyl thioglycolate, thioglycolic acid and dodecyl mercaptan. When polymerization regulators are used, the amount thereof used is generally 0.1 to 15% by weight, preferably 0.1 to 5% by weight and more preferably 0.1 to 2.5% by weight, based on monomers al), a2), a3) and optionally a4).
The polymerization temperature is generally 20 to 200 C, preferably 20 to 150 C and more preferably 20 to 120 C.
The polymerization can be performed under atmospheric pressure, but is preferably undertaken in a closed system under the autogenous pressure which evolves.
The copolymers can be obtained in the acidic state, but they can also, if desired for the application, be neutralized or partly neutralized by addition of bases, especially of sodium hydroxide solution, as early as during the polymerization or after the polymerization has ended. The preferred pH of the aqueous copolymer solutions is in the range from 3 to 8.5.
The copolymers used in accordance with the invention can be used directly in the form of the aqueous solutions obtained in the course of preparation by means of solvent polymerization in water, or in dried form (obtained, for example, by spray drying, spray granulation, fluidized spray drying, roller drying or freeze drying).
In addition to component a), the inventive detergent formulations may comprise, as component b), 0 to 20% by weight of polycarboxylates other than component a).
These may be hydrophilically or hydrophobically modified.
If polycarboxylates other than component a) are present, they are generally present in amounts of 0.1 to 20% by weight.
Suitable examples are alkali metal salts of homo- and copolymers of acrylic acid or of methacrylic acid. Suitable for copolymerization are monoethylenically unsaturated dicarboxylic acids such as maleic acid, fumaric acid, maleic anhydride, itaconic acid and citraconic acid. A suitable polymer is especially polyacrylic acid, which preferably 5 has a molar mass of 2000 to 40 000 g/mol. Due to its superior solubility, among this group, preference may be given to short-chain polyacrylic acid which has molar masses of 2000 to 10 000 g/mol, especially 3000 to 8000 g/mol. Additionally suitable are copolymeric polycarboxylates, especially those of acrylic acid with methacrylic acid and of acrylic acid or methacrylic acid with maleic acid and/or fumaric acid.
It is also possible to use copolymers of at least one monomer from the group consisting of monoethylenically unsaturated 03-010-mono- or dicarboxylic acids or anhydrides thereof, such as maleic acid, maleic anhydride, acrylic acid, methacrylic acid, fumaric acid, itaconic acid and citraconic acid with at least one hydrophilically or hydrophobically modified monomer, as enumerated hereinafter.
Suitable hydrophobic monomers are, for example, isobutene, diisobutene, butene, pentene, hexene and styrene, olefins having 10 or more carbon atoms or mixtures thereof, for example 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-octadecene, 1-eicosene, 1-docosene, 1-tetracosene and 1-hexacosene, C22-alpha-olefin, a mixture of 020-C24-alpha-olefins and polyisobutene having an average of 12 to 100 carbon atoms.
Suitable hydrophilic monomers are monomers with sulfonate or phosphonate groups, and nonionic monomers with a hydroxyl function or alkylene oxide groups.
Examples include: ally' alcohol, isoprenol, methoxy polyethylene glycol (meth)acrylate, methoxy polypropylene glycol (meth)acrylate, methoxy polybutylene glycol (meth)acrylate, methoxy poly(propylene oxide-co-ethylene oxide) (meth)acrylate, ethoxy polyethylene glycol (meth)acrylate, ethoxy polypropylene glycol (meth)acrylate, ethoxy polybutylene glycol (meth)acrylate and ethoxy poly(propylene oxide-co-ethylene oxide) (meth)-acrylate. The polyalkylene glycols comprise 3 to 50, especially 5 to 40 and in particular 10 to 30 alkylene oxide units.
Particularly preferred sulfo-containing monomers are 1-acrylamido-1-propanesulfonic acid, 2-acrylamido-2-propanesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, 2-methacrylamido-2-methylpropanesulfonic acid, 3-methacrylamido-2-hydroxypropane-sulfonic acid, allylsulfonic acid, methallylsulfonic acid, allyloxybenzenesulfonic acid, methallyloxybenzenesulfonic acid, 2-hydroxy-3-(2-propenyloxy)propanesulfonic acid, 2-methyl-2-propene-1-sulfonic acid, styrenesulfonic acid, vinylsulfonic acid, 3-sulfopropyl acrylate, 2-sulfoethyl methacrylate, 3-sulfopropyl methacrylate, =
If desired, it is also possible to use polymerization regulators. Suitable examples are sulfur compounds such as mercaptoethanol, 2-ethylhexyl thioglycolate, thioglycolic acid and dodecyl mercaptan. When polymerization regulators are used, the amount thereof used is generally 0.1 to 15% by weight, preferably 0.1 to 5% by weight and more preferably 0.1 to 2.5% by weight, based on monomers al), a2), a3) and optionally a4).
The polymerization temperature is generally 20 to 200 C, preferably 20 to 150 C and more preferably 20 to 120 C.
The polymerization can be performed under atmospheric pressure, but is preferably undertaken in a closed system under the autogenous pressure which evolves.
The copolymers can be obtained in the acidic state, but they can also, if desired for the application, be neutralized or partly neutralized by addition of bases, especially of sodium hydroxide solution, as early as during the polymerization or after the polymerization has ended. The preferred pH of the aqueous copolymer solutions is in the range from 3 to 8.5.
The copolymers used in accordance with the invention can be used directly in the form of the aqueous solutions obtained in the course of preparation by means of solvent polymerization in water, or in dried form (obtained, for example, by spray drying, spray granulation, fluidized spray drying, roller drying or freeze drying).
In addition to component a), the inventive detergent formulations may comprise, as component b), 0 to 20% by weight of polycarboxylates other than component a).
These may be hydrophilically or hydrophobically modified.
If polycarboxylates other than component a) are present, they are generally present in amounts of 0.1 to 20% by weight.
Suitable examples are alkali metal salts of homo- and copolymers of acrylic acid or of methacrylic acid. Suitable for copolymerization are monoethylenically unsaturated dicarboxylic acids such as maleic acid, fumaric acid, maleic anhydride, itaconic acid and citraconic acid. A suitable polymer is especially polyacrylic acid, which preferably 5 has a molar mass of 2000 to 40 000 g/mol. Due to its superior solubility, among this group, preference may be given to short-chain polyacrylic acid which has molar masses of 2000 to 10 000 g/mol, especially 3000 to 8000 g/mol. Additionally suitable are copolymeric polycarboxylates, especially those of acrylic acid with methacrylic acid and of acrylic acid or methacrylic acid with maleic acid and/or fumaric acid.
It is also possible to use copolymers of at least one monomer from the group consisting of monoethylenically unsaturated 03-010-mono- or dicarboxylic acids or anhydrides thereof, such as maleic acid, maleic anhydride, acrylic acid, methacrylic acid, fumaric acid, itaconic acid and citraconic acid with at least one hydrophilically or hydrophobically modified monomer, as enumerated hereinafter.
Suitable hydrophobic monomers are, for example, isobutene, diisobutene, butene, pentene, hexene and styrene, olefins having 10 or more carbon atoms or mixtures thereof, for example 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-octadecene, 1-eicosene, 1-docosene, 1-tetracosene and 1-hexacosene, C22-alpha-olefin, a mixture of 020-C24-alpha-olefins and polyisobutene having an average of 12 to 100 carbon atoms.
Suitable hydrophilic monomers are monomers with sulfonate or phosphonate groups, and nonionic monomers with a hydroxyl function or alkylene oxide groups.
Examples include: ally' alcohol, isoprenol, methoxy polyethylene glycol (meth)acrylate, methoxy polypropylene glycol (meth)acrylate, methoxy polybutylene glycol (meth)acrylate, methoxy poly(propylene oxide-co-ethylene oxide) (meth)acrylate, ethoxy polyethylene glycol (meth)acrylate, ethoxy polypropylene glycol (meth)acrylate, ethoxy polybutylene glycol (meth)acrylate and ethoxy poly(propylene oxide-co-ethylene oxide) (meth)-acrylate. The polyalkylene glycols comprise 3 to 50, especially 5 to 40 and in particular 10 to 30 alkylene oxide units.
Particularly preferred sulfo-containing monomers are 1-acrylamido-1-propanesulfonic acid, 2-acrylamido-2-propanesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, 2-methacrylamido-2-methylpropanesulfonic acid, 3-methacrylamido-2-hydroxypropane-sulfonic acid, allylsulfonic acid, methallylsulfonic acid, allyloxybenzenesulfonic acid, methallyloxybenzenesulfonic acid, 2-hydroxy-3-(2-propenyloxy)propanesulfonic acid, 2-methyl-2-propene-1-sulfonic acid, styrenesulfonic acid, vinylsulfonic acid, 3-sulfopropyl acrylate, 2-sulfoethyl methacrylate, 3-sulfopropyl methacrylate, =
11 sulfomethacrylamide, sulfomethylmethacrylamide, and salts of the acids mentioned, such as the sodium, potassium or ammonium salts thereof.
Particularly preferred monomers containing phosphonate groups are vinylphosphonic acid and salts thereof.
Furthermore, it is also possible to additionally use amphoteric and cationic polymers.
As component c), the inventive detergent formulations may comprise 0 to 50% by weight of one or more complexing agents. If complexing agents are present, they are present in amounts of 0.1 to 50% by weight, preferably 1 to 45% by weight and more preferably 1 to 40% by weight. Preferred complexing agents are selected from the group consisting of nitrilotriacetic acid, ethylenediaminetetraacetic acid, diethylenetriaminepentaacetic acid, hydroxyethylethylenediaminetriacetic acid and methylglycinediacetic acid, glutamic acid-diacetic acid, iminodisuccinic acid, hydroxyiminodisuccinic acid, ethylenediaminedisuccinic acid, aspartic acid-diacetic acid, and salts thereof. Particularly preferred complexing agents c) are methylglycinediacetic acid and salts thereof.
As component d), the inventive detergent may comprise 0 to 70% by weight of phosphates. When the detergent comprises phosphates, it comprises them generally in amounts of 1 to 70% by weight, preferably of 5 to 60% by weight, more preferably of 20 to 55% by weight.
Among the multitude of commercially available phosphates, the alkali metal phosphates, with particular preference for pentasodium triphosphate or pentapotassium triphosphate (sodium tripolyphosphate or potassium tripolyphosphate), are of the greatest significance in the washing and cleaning products industry.
Suitable phosphates for dishwashing compositions are especially alkali metal phosphates and polymeric alkali metal phosphates, which may be present in the form of their alkaline, neutral or acidic sodium or potassium salts. Examples of such phosphates are trisodium phosphate, tetrasodium diphosphate, disodium dihydrogendiphosphate, pentasodium tripolyphosphate, what is called sodium hexametaphosphate, oligomeric trisodium phosphate with a degree of oligomerization of 5 to 1000, preferably 5 to 50, and the corresponding potassium salts, or mixtures of sodium hexametaphosphate and the corresponding potassium salts, or mixtures of the sodium and potassium salts. Especially preferred are tripolyphosphate salts.
Particularly preferred monomers containing phosphonate groups are vinylphosphonic acid and salts thereof.
Furthermore, it is also possible to additionally use amphoteric and cationic polymers.
As component c), the inventive detergent formulations may comprise 0 to 50% by weight of one or more complexing agents. If complexing agents are present, they are present in amounts of 0.1 to 50% by weight, preferably 1 to 45% by weight and more preferably 1 to 40% by weight. Preferred complexing agents are selected from the group consisting of nitrilotriacetic acid, ethylenediaminetetraacetic acid, diethylenetriaminepentaacetic acid, hydroxyethylethylenediaminetriacetic acid and methylglycinediacetic acid, glutamic acid-diacetic acid, iminodisuccinic acid, hydroxyiminodisuccinic acid, ethylenediaminedisuccinic acid, aspartic acid-diacetic acid, and salts thereof. Particularly preferred complexing agents c) are methylglycinediacetic acid and salts thereof.
As component d), the inventive detergent may comprise 0 to 70% by weight of phosphates. When the detergent comprises phosphates, it comprises them generally in amounts of 1 to 70% by weight, preferably of 5 to 60% by weight, more preferably of 20 to 55% by weight.
Among the multitude of commercially available phosphates, the alkali metal phosphates, with particular preference for pentasodium triphosphate or pentapotassium triphosphate (sodium tripolyphosphate or potassium tripolyphosphate), are of the greatest significance in the washing and cleaning products industry.
Suitable phosphates for dishwashing compositions are especially alkali metal phosphates and polymeric alkali metal phosphates, which may be present in the form of their alkaline, neutral or acidic sodium or potassium salts. Examples of such phosphates are trisodium phosphate, tetrasodium diphosphate, disodium dihydrogendiphosphate, pentasodium tripolyphosphate, what is called sodium hexametaphosphate, oligomeric trisodium phosphate with a degree of oligomerization of 5 to 1000, preferably 5 to 50, and the corresponding potassium salts, or mixtures of sodium hexametaphosphate and the corresponding potassium salts, or mixtures of the sodium and potassium salts. Especially preferred are tripolyphosphate salts.
12 As component e), the inventive detergent may comprise 0 to 60% by weight of builders and cobuilders. When the detergent comprises builders and cobuilders, it comprises them generally in amounts of 0.1 to 60% by weight. Builders and cobuilders are water-soluble or water-insoluble substances, the main task of which consists in the binding of calcium and magnesium ions.
These may be low molecular weight carboxylic acids and salts thereof, such as alkali metal citrates, especially anhydrous trisodium citrate or trisodium citrate dihydrate, alkali metal succinates, alkali metal malonates, fatty acid sulfonates, oxidisuccinate, alkyl or alkenyl disuccinates, gluconic acids, oxadiacetates, carboxymethyloxysuccinates, tartrate monosuccinate, tartrate disuccinate, tartrate monoacetate, tartrate diacetate and a-hydroxypropionic acid.
A further substance class with cobuilder properties which may be present in the inventive detergents is that of the phosphonates. These are especially hydroxyalkane-or aminoalkanephosphonates. Among the hydroxyalkanephosphonates, 1-hydroxyethane-1,1-diphosphonate (HEDP) is of particular significance as a cobuilder.
It is preferably used in the form of the sodium salt, the disodium salt being neutral and the tetrasodium salt alkaline (pH 9). Useful aminoalkanephosphonates preferably include ethylenediaminetetramethylenephosphonate (EDTMP), diethylenetriamine-pentamethylenephosphonate (DTPMP) or the higher homologs thereof. They are preferably used in the form of the neutral sodium salts, for example as the hexasodium salt of EDTMP or as the hepta- and octasodium salt of DTPMP. The builder used from the class of the phosphonates is preferably HEDP. The aminoalkanephosphonates additionally have marked heavy metal binding capacity. Accordingly, especially when the compositions also comprise bleaches, it may be preferable to use aminoalkanephosphonates, especially DTPMP, or to use mixtures of the phosphonates mentioned.
A further substance class in the builder system is that of the silicates.
Crystalline sheet-type silicates with the general formula NaMSi,(02x+1 yH20 may be present, where M is sodium or hydrogen, x is from 1.9 to 22, preferably from 1.9 to 4, particularly preferred values for x being 2, 3 or 4, and y is from 0 to 33, preferably 0 to 20. In addition, amorphous sodium silicates with an Si02:Na20 ratio of 1 to 3.5, preferably of 1.6 to 3 and especially of 2 to 2.8 can be used.
In addition, carbonates and hydrogencarbonates are used, among which the alkali metal salts, especially sodium salts, are preferred.
These may be low molecular weight carboxylic acids and salts thereof, such as alkali metal citrates, especially anhydrous trisodium citrate or trisodium citrate dihydrate, alkali metal succinates, alkali metal malonates, fatty acid sulfonates, oxidisuccinate, alkyl or alkenyl disuccinates, gluconic acids, oxadiacetates, carboxymethyloxysuccinates, tartrate monosuccinate, tartrate disuccinate, tartrate monoacetate, tartrate diacetate and a-hydroxypropionic acid.
A further substance class with cobuilder properties which may be present in the inventive detergents is that of the phosphonates. These are especially hydroxyalkane-or aminoalkanephosphonates. Among the hydroxyalkanephosphonates, 1-hydroxyethane-1,1-diphosphonate (HEDP) is of particular significance as a cobuilder.
It is preferably used in the form of the sodium salt, the disodium salt being neutral and the tetrasodium salt alkaline (pH 9). Useful aminoalkanephosphonates preferably include ethylenediaminetetramethylenephosphonate (EDTMP), diethylenetriamine-pentamethylenephosphonate (DTPMP) or the higher homologs thereof. They are preferably used in the form of the neutral sodium salts, for example as the hexasodium salt of EDTMP or as the hepta- and octasodium salt of DTPMP. The builder used from the class of the phosphonates is preferably HEDP. The aminoalkanephosphonates additionally have marked heavy metal binding capacity. Accordingly, especially when the compositions also comprise bleaches, it may be preferable to use aminoalkanephosphonates, especially DTPMP, or to use mixtures of the phosphonates mentioned.
A further substance class in the builder system is that of the silicates.
Crystalline sheet-type silicates with the general formula NaMSi,(02x+1 yH20 may be present, where M is sodium or hydrogen, x is from 1.9 to 22, preferably from 1.9 to 4, particularly preferred values for x being 2, 3 or 4, and y is from 0 to 33, preferably 0 to 20. In addition, amorphous sodium silicates with an Si02:Na20 ratio of 1 to 3.5, preferably of 1.6 to 3 and especially of 2 to 2.8 can be used.
In addition, carbonates and hydrogencarbonates are used, among which the alkali metal salts, especially sodium salts, are preferred.
13 As component f), the inventive detergent formulations comprise 0.1 to 20% by weight of nonionic surfactants, typically weakly foaming or low-foaming nonionic surfactants.
These are present preferably in proportions of 0.1 to 15% by weight, more preferably of 0.25 to 10% by weight.
Suitable nonionic surfactants comprise the surfactants of the general formula (III) R19-0-(CH2CH20)p-(CHR17CH20)m-R19 (III) in which R19 is a linear or branched alkyl radical having 8 to 22 carbon atoms, R17 and R19 are each independently hydrogen or a linear or branched alkyl radical having 1-10 carbon atoms or H, where R17 is preferably methyl, p and m are each independently 0 to 300. Preferably, p = 1 - 100 and m = 0 - 30.
The surfactants of the formula (III) may be either random copolymers or block copolymers, preferably block copolymers.
In addition, it is possible to use di- and multiblock copolymers formed from ethylene oxide and propylene oxide, which are commercially available, for example, under the Pluronic (BASF SE) or Tetronic (BASF Corporation) name. In addition, it is possible to use reaction products formed from sorbitan esters with ethylene oxide and/or propylene oxide. Likewise suitable are amine oxides or alkyl glycosides. An overview of suitable nonionic surfactants is given by EP-A 851 023 and DE-A 198 19 187.
It is also possible for mixtures of several different nonionic surfactants to be present.
As component g), the inventive detergent formulations may comprise 0 to 30% by weight of bleaches, optionally bleach activators and optionally bleach catalysts. If the detergent formulations comprise bleaches, bleach activators or bleach catalysts, they comprise the latter in amounts totaling 0.1 to 30% by weight, preferably 1 to 30% by weight and more preferably 5 to 30% by weight.
Bleaches are divided into oxygen bleaches and chlorine bleaches. Oxygen bleaches used include alkali metal perborates and the hydrates thereof, and alkali metal percarbonates. Preferred bleaches in this context are sodium perborate in the form of the mono- or tetrahydrate, sodium percarbonate or the hydrates of sodium percarbonate.
Likewise usable as oxygen bleaches are persulfates and hydrogen peroxide.
These are present preferably in proportions of 0.1 to 15% by weight, more preferably of 0.25 to 10% by weight.
Suitable nonionic surfactants comprise the surfactants of the general formula (III) R19-0-(CH2CH20)p-(CHR17CH20)m-R19 (III) in which R19 is a linear or branched alkyl radical having 8 to 22 carbon atoms, R17 and R19 are each independently hydrogen or a linear or branched alkyl radical having 1-10 carbon atoms or H, where R17 is preferably methyl, p and m are each independently 0 to 300. Preferably, p = 1 - 100 and m = 0 - 30.
The surfactants of the formula (III) may be either random copolymers or block copolymers, preferably block copolymers.
In addition, it is possible to use di- and multiblock copolymers formed from ethylene oxide and propylene oxide, which are commercially available, for example, under the Pluronic (BASF SE) or Tetronic (BASF Corporation) name. In addition, it is possible to use reaction products formed from sorbitan esters with ethylene oxide and/or propylene oxide. Likewise suitable are amine oxides or alkyl glycosides. An overview of suitable nonionic surfactants is given by EP-A 851 023 and DE-A 198 19 187.
It is also possible for mixtures of several different nonionic surfactants to be present.
As component g), the inventive detergent formulations may comprise 0 to 30% by weight of bleaches, optionally bleach activators and optionally bleach catalysts. If the detergent formulations comprise bleaches, bleach activators or bleach catalysts, they comprise the latter in amounts totaling 0.1 to 30% by weight, preferably 1 to 30% by weight and more preferably 5 to 30% by weight.
Bleaches are divided into oxygen bleaches and chlorine bleaches. Oxygen bleaches used include alkali metal perborates and the hydrates thereof, and alkali metal percarbonates. Preferred bleaches in this context are sodium perborate in the form of the mono- or tetrahydrate, sodium percarbonate or the hydrates of sodium percarbonate.
Likewise usable as oxygen bleaches are persulfates and hydrogen peroxide.
14 Typical oxygen bleaches are also organic peracids, for example perbenzoic acid, peroxy-alpha-naphthoic acid, peroxylauric acid, peroxystearic acid, phthalimidoperoxycaproic acid, 1,12-diperoxydodecanedioic acid, 1,9-diperoxyazelaic acid, diperoxoisophthalic acid or 2-decyldiperoxybutane-1,4-dioic acid.
In addition, the following oxygen bleaches may also find use in the detergent formulation:
Cationic peroxy acids described in patent applications US 5,422,028, US
5,294,362 and US 5,292,447, and sulfonyl peroxy acids described in patent application US 5,039,447.
Chlorine bleaches and the combination of chlorine bleaches with peroxidic bleaches can likewise be used. Known chlorine bleaches are, for example, 1,3-dichloro-5,5-dimethylhydantoin, N-chlorosulfamide, chloramine T, dichloramine T, chloramine B, N,N"-dichlorobenzoylurea, dichloro-p-toluenesulfonamide or trichloroethylamine.
Preferred chlorine bleaches are sodium hypochlorite, calcium hypochlorite, potassium hypochlorite, magnesium hypochlorite, potassium dichloroisocyanurate or sodium dichloroisocyanurate.
Chlorine bleaches are used in amounts of generally 0.1 to 20% by weight, preferably of 0.2 to 10% by weight, more preferably of 0.3 to 8% by weight, based on the overall detergent formulation.
It is additionally possible to add small amounts of bleach stabilizers, for example phosphonates, borates, metaborates, metasilicates or magnesium salts.
Bleach activators are compounds which, under perhydrolysis conditions, give rise to aliphatic peroxocarboxylic acids having preferably 1 to 10 carbon atoms, especially 2 to 4 carbon atoms, and/or substituted perbenzoic acid. Suitable compounds are those which comprise one or more N- or 0-acyl groups and/or optionally substituted benzoyl groups, for example substances from the class of the anhydrides, esters, imides, acylated imidazoles or oximes. Examples are tetraacetylethylenediamine (TAED), tetraacetylmethylenediamine (TAMD), tetraacetylglycoluril (TAG U), tetraacetylhexylenediamine (TAHD), N-acylimides, for example N-nonanoylsuccinimide (NOSI), acylated phenolsulfonates, for example n-nonanoyl- or isononanoyloxybenzenesulfonates (n- or iso-NOBS), pentaacetylglucose (FAG), 1,5-diacety1-2,2-dioxohexahydro-1,3,5-triazine (DADHT) or isatoic anhydride (ISA).
Likewise suitable as bleach activators are nitrile quats, for example N-methyl-= '1 morpholinioacetonitrile salts (M MA salts) or trimethylammonioacetonitrile salts (TMAQ
salts).
Preferentially suitable bleach activators are those from the group consisting of 5 polyacylated alkylenediamines, more preferably TAED, N-acylimides, more preferably NOSI, acylated phenolsulfonates, more preferably n- or iso-NOBS, MMA and TMAQ.
Bleach activators are used in amounts of generally 0.1 to 10% by weight, preferably of 1 to 9% by weight, more preferably of 1.5 to 8% by weight, based on the overall 10 detergent formulation.
In addition to the conventional bleach activators or in their stead, it is also possible for what are called bleach catalysts to be present. These substances are bleach-boosting transition metal salts or transition metal complexes, for example manganese-, iron-,
In addition, the following oxygen bleaches may also find use in the detergent formulation:
Cationic peroxy acids described in patent applications US 5,422,028, US
5,294,362 and US 5,292,447, and sulfonyl peroxy acids described in patent application US 5,039,447.
Chlorine bleaches and the combination of chlorine bleaches with peroxidic bleaches can likewise be used. Known chlorine bleaches are, for example, 1,3-dichloro-5,5-dimethylhydantoin, N-chlorosulfamide, chloramine T, dichloramine T, chloramine B, N,N"-dichlorobenzoylurea, dichloro-p-toluenesulfonamide or trichloroethylamine.
Preferred chlorine bleaches are sodium hypochlorite, calcium hypochlorite, potassium hypochlorite, magnesium hypochlorite, potassium dichloroisocyanurate or sodium dichloroisocyanurate.
Chlorine bleaches are used in amounts of generally 0.1 to 20% by weight, preferably of 0.2 to 10% by weight, more preferably of 0.3 to 8% by weight, based on the overall detergent formulation.
It is additionally possible to add small amounts of bleach stabilizers, for example phosphonates, borates, metaborates, metasilicates or magnesium salts.
Bleach activators are compounds which, under perhydrolysis conditions, give rise to aliphatic peroxocarboxylic acids having preferably 1 to 10 carbon atoms, especially 2 to 4 carbon atoms, and/or substituted perbenzoic acid. Suitable compounds are those which comprise one or more N- or 0-acyl groups and/or optionally substituted benzoyl groups, for example substances from the class of the anhydrides, esters, imides, acylated imidazoles or oximes. Examples are tetraacetylethylenediamine (TAED), tetraacetylmethylenediamine (TAMD), tetraacetylglycoluril (TAG U), tetraacetylhexylenediamine (TAHD), N-acylimides, for example N-nonanoylsuccinimide (NOSI), acylated phenolsulfonates, for example n-nonanoyl- or isononanoyloxybenzenesulfonates (n- or iso-NOBS), pentaacetylglucose (FAG), 1,5-diacety1-2,2-dioxohexahydro-1,3,5-triazine (DADHT) or isatoic anhydride (ISA).
Likewise suitable as bleach activators are nitrile quats, for example N-methyl-= '1 morpholinioacetonitrile salts (M MA salts) or trimethylammonioacetonitrile salts (TMAQ
salts).
Preferentially suitable bleach activators are those from the group consisting of 5 polyacylated alkylenediamines, more preferably TAED, N-acylimides, more preferably NOSI, acylated phenolsulfonates, more preferably n- or iso-NOBS, MMA and TMAQ.
Bleach activators are used in amounts of generally 0.1 to 10% by weight, preferably of 1 to 9% by weight, more preferably of 1.5 to 8% by weight, based on the overall 10 detergent formulation.
In addition to the conventional bleach activators or in their stead, it is also possible for what are called bleach catalysts to be present. These substances are bleach-boosting transition metal salts or transition metal complexes, for example manganese-, iron-,
15 cobalt-, ruthenium- or molybdenum-salen complexes or -carbonyl complexes.
Usable bleach catalysts are also manganese, iron, cobalt, ruthenium, molybdenum, titanium, vanadium and copper complexes with nitrogen-containing tripod ligands, and cobalt-, iron-, copper- and ruthenium-amine complexes.
As component h), the inventive detergent formulations may comprise 0 to 8% by weight of enzymes. If the detergent formulations comprise enzymes, they comprise the latter generally in amounts of 0.1 to 8% by weight. It is possible to add enzymes to the detergent in order to enhance the performance of the detergents or to ensure the same quality of cleaning performance under milder conditions. The most frequently used enzymes include lipases, amylases, cellulases and proteases. In addition, it is possible, for example, also to use esterases, pectinases, lactases and peroxidases.
In addition, the inventive detergents may comprise, as component i), from 0 to 50% by weight of one or more further additives such as anionic or zwitterionic surfactants, alkali carriers, corrosion inhibitors, defoamers, dyes, fragrances, fillers, organic solvents, tabletting aids, disintegrants, thickeners, solubilizers and water. If the detergent formulation comprises further additives, they are generally present in amounts of 0.1 to 50% by weight.
The formulations may comprise anionic or zwitterionic surfactants, preferably in a blend with nonionic surfactants. Suitable anionic and zwitterionic surfactants are specified in EP-A 851 023 and DE-A 198 19 187.
As further constituents of the detergent formulation, alkali carriers may be present. In addition to the ammonium or alkali metal carbonates, ammonium or alkali metal
Usable bleach catalysts are also manganese, iron, cobalt, ruthenium, molybdenum, titanium, vanadium and copper complexes with nitrogen-containing tripod ligands, and cobalt-, iron-, copper- and ruthenium-amine complexes.
As component h), the inventive detergent formulations may comprise 0 to 8% by weight of enzymes. If the detergent formulations comprise enzymes, they comprise the latter generally in amounts of 0.1 to 8% by weight. It is possible to add enzymes to the detergent in order to enhance the performance of the detergents or to ensure the same quality of cleaning performance under milder conditions. The most frequently used enzymes include lipases, amylases, cellulases and proteases. In addition, it is possible, for example, also to use esterases, pectinases, lactases and peroxidases.
In addition, the inventive detergents may comprise, as component i), from 0 to 50% by weight of one or more further additives such as anionic or zwitterionic surfactants, alkali carriers, corrosion inhibitors, defoamers, dyes, fragrances, fillers, organic solvents, tabletting aids, disintegrants, thickeners, solubilizers and water. If the detergent formulation comprises further additives, they are generally present in amounts of 0.1 to 50% by weight.
The formulations may comprise anionic or zwitterionic surfactants, preferably in a blend with nonionic surfactants. Suitable anionic and zwitterionic surfactants are specified in EP-A 851 023 and DE-A 198 19 187.
As further constituents of the detergent formulation, alkali carriers may be present. In addition to the ammonium or alkali metal carbonates, ammonium or alkali metal
16 hydrogencarbonates and ammonium or alkali metal sesquicarbonates already mentioned for the builder substances, the alkali carriers used may also be ammonium or alkali metal hydroxides, ammonium or alkali metal silicates and ammonium or alkali metal metasilicates, and mixtures of the aforementioned substances.
The corrosion inhibitors used may be silver anticorrosives from the group of the triazoles, the benzotriazoles, the bisbenzotriazoles, the aminotriazoles, the alkylaminotriazoles and the transition metal salts or complexes.
To prevent glass corrosion, which is manifested by cloudiness, iridescence, streaks and lines on the glass, glass corrosion inhibitors are used. Preferred glass corrosion inhibitors are from the group of the magnesium, zinc and bismuth salts and complexes.
Paraffin oils and silicone oils can optionally be used as defoamers and for protection of plastic and metal surfaces. Defoamers are generally used in proportions of 0.001% by weight to 5% by weight. In addition, it is possible to add dyes, for example patent blue, preservatives, for example Kathon CG, perfumes and other fragrances to the inventive detergent formulation.
An example of a suitable filler is sodium sulfate.
The inventive detergent formulations can be provided in liquid or solid form, in one or more phases, as tablets or in the form of other dosage units, in packaged or unpackaged form.
The invention is illustrated in detail by the examples which follow.
Examples In all cases, the molecular weights were determined by means of gel permeation chromatography (GPC). This was done using 2 columns (Suprema Linear M) and a precolumn (Suprema precolumn), all of the Suprema-Gel brand (HEMA) from Polymer Standard Services (Mainz, Germany) at 35 C with a flow rate of 0.8 ml/min. The eluent was the aqueous solution buffered at pH 7 with TRIS, to which 0.15M NaCI and 0.01M
NaN3 had been added. Calibration was effected with an Na-PAA standard, the integral molecular weight distribution curve of which had been determined by coupled SEC-laser light scattering, by the calibration method of M.J.R. Cantow et al. (J.
Polym. Sci., A-1, 5(1967)1391-1394), but without the concentration correction proposed therein. All samples were adjusted to pH 7 with a 50% sodium hydroxide solution, a portion of this solution was diluted to a solids content of 1.5 mg/ml with demineralized water, and the
The corrosion inhibitors used may be silver anticorrosives from the group of the triazoles, the benzotriazoles, the bisbenzotriazoles, the aminotriazoles, the alkylaminotriazoles and the transition metal salts or complexes.
To prevent glass corrosion, which is manifested by cloudiness, iridescence, streaks and lines on the glass, glass corrosion inhibitors are used. Preferred glass corrosion inhibitors are from the group of the magnesium, zinc and bismuth salts and complexes.
Paraffin oils and silicone oils can optionally be used as defoamers and for protection of plastic and metal surfaces. Defoamers are generally used in proportions of 0.001% by weight to 5% by weight. In addition, it is possible to add dyes, for example patent blue, preservatives, for example Kathon CG, perfumes and other fragrances to the inventive detergent formulation.
An example of a suitable filler is sodium sulfate.
The inventive detergent formulations can be provided in liquid or solid form, in one or more phases, as tablets or in the form of other dosage units, in packaged or unpackaged form.
The invention is illustrated in detail by the examples which follow.
Examples In all cases, the molecular weights were determined by means of gel permeation chromatography (GPC). This was done using 2 columns (Suprema Linear M) and a precolumn (Suprema precolumn), all of the Suprema-Gel brand (HEMA) from Polymer Standard Services (Mainz, Germany) at 35 C with a flow rate of 0.8 ml/min. The eluent was the aqueous solution buffered at pH 7 with TRIS, to which 0.15M NaCI and 0.01M
NaN3 had been added. Calibration was effected with an Na-PAA standard, the integral molecular weight distribution curve of which had been determined by coupled SEC-laser light scattering, by the calibration method of M.J.R. Cantow et al. (J.
Polym. Sci., A-1, 5(1967)1391-1394), but without the concentration correction proposed therein. All samples were adjusted to pH 7 with a 50% sodium hydroxide solution, a portion of this solution was diluted to a solids content of 1.5 mg/ml with demineralized water, and the
17 mixture was stirred for 12 hours. The samples were subsequently filtered. In each case 100 pl were injected by means of a Sartorius Minisart RC 25 (0.2 pm).
Comparative example Cl A reactor was initially charged with 503.9 g of demineralized water together with 2.36 g of a 50% by weight aqueous solution of phosphorous acid. Subsequently, the mixture was heated to internal temperature 100 C under a nitrogen atmosphere. At this temperature, 58.9 g of a 10.0% by weight aqueous sodium peroxodisulfate solution, 39.2 g of a 40% by weight aqueous sodium bisulfite solution and 394.0 g of a mixture consisting of 10.9% by weight of distilled acrylic acid, 11.2% by weight of methoxy polyethylene glycol methacrylate (Mw = 1086 g/mol), 11.9% by weight of distilled methacrylic acid, 4.5% by weight of 2-sulfoethylmethacrylic acid sodium salt and 61.5%
demineralized water were simultaneously metered in separated and in parallel while stirring. The monomer mixture was metered in within 5 hours, sodium peroxodisulfate within 5.25 hours and sodium bisulfite within 5 hours. This was followed by continued polymerization at 100 C for another 2 hours. Thereafter, the mixture was cooled to room temperature and then 90.0 g of a 50% by weight aqueous sodium hydroxide solution were used to establish a pH of 7.4. The pH and K values, molecular weights Mr, and M, and the solids content were determined, and the product mixture was .. assessed visually.
Comparative example C2 A reactor was initially charged with 904.6 g of demineralized water together with 2.36 g of a 50% by weight aqueous solution of phosphorous acid. Subsequently, the mixture was heated to internal temperature 100 C under a nitrogen atmosphere. At this temperature, 117.8 g of a 10.2% by weight aqueous sodium peroxodisulfate solution, 78.4 g of a 40% by weight aqueous sodium bisulfite solution and 752.8 g of a mixture consisting of 11.4% by weight of distilled acrylic acid, 11.8% by weight of methoxy polyethylene glycol methacrylate (Mw = 1086 g/mol), 12.5% by weight of distilled methacrylic acid and 64.3% by weight of demineralized water and 140.8 g of a 25% by weight sodium vinylsulfonate solution were simultaneously metered in separated and in parallel while stirring. The monomer mixture was metered in within 5 hours, sodium peroxodisulfate within 5.25 hours and sodium bisulfite within 5 hours. This was followed by continued polymerization at 100 C for another 2 hours. Thereafter, the mixture was cooled to room temperature and then 1 g of a 50% by weight aqueous sodium hydroxide solution was used to establish a pH of 7.2. The pH and K values, molecular weights Mn and Mw and the solids content were determined, and the product mixture was assessed visually.
Comparative example Cl A reactor was initially charged with 503.9 g of demineralized water together with 2.36 g of a 50% by weight aqueous solution of phosphorous acid. Subsequently, the mixture was heated to internal temperature 100 C under a nitrogen atmosphere. At this temperature, 58.9 g of a 10.0% by weight aqueous sodium peroxodisulfate solution, 39.2 g of a 40% by weight aqueous sodium bisulfite solution and 394.0 g of a mixture consisting of 10.9% by weight of distilled acrylic acid, 11.2% by weight of methoxy polyethylene glycol methacrylate (Mw = 1086 g/mol), 11.9% by weight of distilled methacrylic acid, 4.5% by weight of 2-sulfoethylmethacrylic acid sodium salt and 61.5%
demineralized water were simultaneously metered in separated and in parallel while stirring. The monomer mixture was metered in within 5 hours, sodium peroxodisulfate within 5.25 hours and sodium bisulfite within 5 hours. This was followed by continued polymerization at 100 C for another 2 hours. Thereafter, the mixture was cooled to room temperature and then 90.0 g of a 50% by weight aqueous sodium hydroxide solution were used to establish a pH of 7.4. The pH and K values, molecular weights Mr, and M, and the solids content were determined, and the product mixture was .. assessed visually.
Comparative example C2 A reactor was initially charged with 904.6 g of demineralized water together with 2.36 g of a 50% by weight aqueous solution of phosphorous acid. Subsequently, the mixture was heated to internal temperature 100 C under a nitrogen atmosphere. At this temperature, 117.8 g of a 10.2% by weight aqueous sodium peroxodisulfate solution, 78.4 g of a 40% by weight aqueous sodium bisulfite solution and 752.8 g of a mixture consisting of 11.4% by weight of distilled acrylic acid, 11.8% by weight of methoxy polyethylene glycol methacrylate (Mw = 1086 g/mol), 12.5% by weight of distilled methacrylic acid and 64.3% by weight of demineralized water and 140.8 g of a 25% by weight sodium vinylsulfonate solution were simultaneously metered in separated and in parallel while stirring. The monomer mixture was metered in within 5 hours, sodium peroxodisulfate within 5.25 hours and sodium bisulfite within 5 hours. This was followed by continued polymerization at 100 C for another 2 hours. Thereafter, the mixture was cooled to room temperature and then 1 g of a 50% by weight aqueous sodium hydroxide solution was used to establish a pH of 7.2. The pH and K values, molecular weights Mn and Mw and the solids content were determined, and the product mixture was assessed visually.
18 Example 1 A reactor was initially charged with 225.0 g of demineralized water together with 225.0 g of an ally' alcohol alkoxylate of the formula CH2=CHCH20-(E04.1)(E012.3P05.5)-H.
Subsequently, the mixture was heated to internal temperature 90 C under a nitrogen atmosphere. At this temperature, 107.1 g of a 7% by weight aqueous sodium peroxodisulfate solution, 46.9 g of a 40% by weight aqueous sodium bisulfite solution and 994.8 g of a mixture consisting of 30.1% by weight of distilled acrylic acid, 22.9%
by weight of 2-acrylamido-2-methylpropanesulfonic acid, 0.006% by weight of 4-methoxyphenol solution, 4.4% by weight of sodium hydroxide solution and 42.6% by weight of demineralized water were metered in simultaneously, separately and in parallel while stirring. The monomer mixture was metered in within 3 hours, sodium peroxodisulfate within 4.5 hours and sodium bisulfite within 2.75 hours. After the end of the monomer feed, 110.0 g of a 50% by weight aqueous sodium hydroxide solution were added at internal temperature 90 C within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 hour. Thereafter, 382.7 g. of demineralized water were added, which cooled the polymer solution to room temperature. The pH and K values, molecular weights Mr, and Mw and the solids content were determined, and the product mixture was assessed visually.
Example 2 A reactor was initially charged with 300.0 g of demineralized water together with 120.0 g of allyl alcohol alkoxylate of the formula CH2=CHCH20-(E04.1)(E012.3P05.5)-H.
Subsequently, the mixture was heated to internal temperature 90 C under a nitrogen atmosphere. At this temperature, 85.7 g of a 7% by weight aqueous sodium peroxodisulfate solution, 45.0 g of a 40% by weight aqueous sodium bisulfite solution and 880.5 g of a mixture consisting of 40.9% by weight of distilled acrylic acid, 13.8%
by weight of 2-acrylamido-2-methylpropanesulfonic acid, 0.003% by weight of 4-methoxyphenol solution, 5.3% by weight of sodium hydroxide solution and 40.0% by weight of demineralized water were metered in simultaneously, separately and in parallel while stirring. The monomer mixture was metered in within 3 hours, sodium peroxodisulfate within 4.5 hours and sodium bisulfite within 2.75 hours. After the end of the monomer feed, 148.9 g of a 50% by weight aqueous sodium hydroxide solution were added at internal temperature 90 C within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 hour. Thereafter, 132.7 g of demineralized water were added, which cooled the polymer solution to room temperature. The pH and K values, molecular weights Mn and M, and the solids content were determined, and the product mixture was assessed visually.
Subsequently, the mixture was heated to internal temperature 90 C under a nitrogen atmosphere. At this temperature, 107.1 g of a 7% by weight aqueous sodium peroxodisulfate solution, 46.9 g of a 40% by weight aqueous sodium bisulfite solution and 994.8 g of a mixture consisting of 30.1% by weight of distilled acrylic acid, 22.9%
by weight of 2-acrylamido-2-methylpropanesulfonic acid, 0.006% by weight of 4-methoxyphenol solution, 4.4% by weight of sodium hydroxide solution and 42.6% by weight of demineralized water were metered in simultaneously, separately and in parallel while stirring. The monomer mixture was metered in within 3 hours, sodium peroxodisulfate within 4.5 hours and sodium bisulfite within 2.75 hours. After the end of the monomer feed, 110.0 g of a 50% by weight aqueous sodium hydroxide solution were added at internal temperature 90 C within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 hour. Thereafter, 382.7 g. of demineralized water were added, which cooled the polymer solution to room temperature. The pH and K values, molecular weights Mr, and Mw and the solids content were determined, and the product mixture was assessed visually.
Example 2 A reactor was initially charged with 300.0 g of demineralized water together with 120.0 g of allyl alcohol alkoxylate of the formula CH2=CHCH20-(E04.1)(E012.3P05.5)-H.
Subsequently, the mixture was heated to internal temperature 90 C under a nitrogen atmosphere. At this temperature, 85.7 g of a 7% by weight aqueous sodium peroxodisulfate solution, 45.0 g of a 40% by weight aqueous sodium bisulfite solution and 880.5 g of a mixture consisting of 40.9% by weight of distilled acrylic acid, 13.8%
by weight of 2-acrylamido-2-methylpropanesulfonic acid, 0.003% by weight of 4-methoxyphenol solution, 5.3% by weight of sodium hydroxide solution and 40.0% by weight of demineralized water were metered in simultaneously, separately and in parallel while stirring. The monomer mixture was metered in within 3 hours, sodium peroxodisulfate within 4.5 hours and sodium bisulfite within 2.75 hours. After the end of the monomer feed, 148.9 g of a 50% by weight aqueous sodium hydroxide solution were added at internal temperature 90 C within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 hour. Thereafter, 132.7 g of demineralized water were added, which cooled the polymer solution to room temperature. The pH and K values, molecular weights Mn and M, and the solids content were determined, and the product mixture was assessed visually.
19 Example 3 A reactor was initially charged with 300.0 g of demineralized water together with 60.0 g of allyl alcohol alkoxylate of the formula CH2=CHCH20-(E04.1)(E012.3P05.5)-H.
Subsequently, the mixture was heated to internal temperature 90 C under a nitrogen atmosphere. At this temperature, 85.7 g of a 7% by weight aqueous sodium peroxodisulfate solution, 75.0 g of a 40% by weight aqueous sodium bisulfite solution and 915.3 g of a mixture consisting of 52.4% by weight of distilled acrylic acid, 6.6% by weight of 2-acrylamido-2-methylpropanesulfonic acid, 0.002% by weight of 4-methoxyphenol solution, 2.5% by weight of sodium hydroxide solution and 38.5% by weight of demineralized water were metered in simultaneously, separately and in parallel while stirring. The monomer mixture was metered in within 3 hours, sodium peroxodisulfate within 4.5 hours and sodium bisulfite within 2.75 hours. After the end of the monomer feed, 148.9 g of a 50% by weight aqueous sodium hydroxide solution were added at internal temperature 90 C within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 hour. Thereafter, 132.7 g of demineralized water were added, which cooled the polymer solution to room temperature. The pH and K values, molecular weights Mn and NI, and the solids content were determined, and the product mixture was assessed visually.
Example 4 A reactor was initially charged with 225.0 g of demineralized water together with 225.0 g of allyl alcohol alkoxylate of the formula CH2=CHCH20-(E04.1)(E012.3P05.5)-H.
Subsequently, the mixture was heated to internal temperature 90 C under a nitrogen atmosphere. At this temperature, 112.0 g of a 7% by weight aqueous sodium peroxodisulfate solution, 103.1 g of a 40% by weight aqueous sodium bisulfite solution and 931.4 g of a mixture consisting of 48.3% by weight of distilled acrylic acid, 8.1% by weight of 2-acrylamido-2-methylpropanesulfonic acid, 0.002% by weight of 4-methoxyphenol solution, 3.1% by weight of sodium hydroxide solution and 40.5% by weight of demineralized water were metered in simultaneously, separately and in parallel while stirring. The monomer mixture was metered in within 3 hours, sodium peroxodisulfate within 4.5 hours and sodium bisulfite within 2.75 hours. After the end of the monomer feed, 188.7 g of a 50% by weight aqueous sodium hydroxide solution were added at internal temperature 90 C within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 hour. Thereafter, 350.0 g of demineralized water were added, which cooled the polymer solution to room temperature. The pH and K values, molecular weights N/In and RN and the solids content were determined, and the product mixture was assessed visually.
=
Example 5 A reactor was initially charged with 150.0 g of demineralized water together with 50.0 g of allyl alcohol alkoxylate of the formula CH2=CHCH20-(E016)-H. Subsequently, the mixture was heated to internal temperature 90 C under a nitrogen atmosphere.
At this 5 temperature, 214.0 g of a 7% by weight aqueous sodium peroxodisulfate solution, 50.0 g of a 40% by weight aqueous sodium bisulfite solution and 818.7 g of a mixture consisting of 36.7% by weight of distilled acrylic acid, 18.5% by weight of 2-acrylamido-2-methylpropanesulfonic acid, 0.001% by weight of 4-methoxyphenol solution, 7.5% by weight of sodium hydroxide solution and 37.7% by weight of demineralized water were 10 metered in simultaneously, separately and in parallel while stirring.
The monomer mixture was metered in within 3 hours, sodium peroxodisulfate within 4.5 hours and sodium bisulfite within 2.75 hours. After the end of the monomer feed, 162.2 g of a 50%
by weight aqueous sodium hydroxide solution were added at internal temperature within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 15 hour. Thereafter, the polymer solution was cooled to room temperature.
The pH and K
values, molecular weights Mn and M, and the solids content were determined, and the product mixture was assessed visually.
Example 6
Subsequently, the mixture was heated to internal temperature 90 C under a nitrogen atmosphere. At this temperature, 85.7 g of a 7% by weight aqueous sodium peroxodisulfate solution, 75.0 g of a 40% by weight aqueous sodium bisulfite solution and 915.3 g of a mixture consisting of 52.4% by weight of distilled acrylic acid, 6.6% by weight of 2-acrylamido-2-methylpropanesulfonic acid, 0.002% by weight of 4-methoxyphenol solution, 2.5% by weight of sodium hydroxide solution and 38.5% by weight of demineralized water were metered in simultaneously, separately and in parallel while stirring. The monomer mixture was metered in within 3 hours, sodium peroxodisulfate within 4.5 hours and sodium bisulfite within 2.75 hours. After the end of the monomer feed, 148.9 g of a 50% by weight aqueous sodium hydroxide solution were added at internal temperature 90 C within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 hour. Thereafter, 132.7 g of demineralized water were added, which cooled the polymer solution to room temperature. The pH and K values, molecular weights Mn and NI, and the solids content were determined, and the product mixture was assessed visually.
Example 4 A reactor was initially charged with 225.0 g of demineralized water together with 225.0 g of allyl alcohol alkoxylate of the formula CH2=CHCH20-(E04.1)(E012.3P05.5)-H.
Subsequently, the mixture was heated to internal temperature 90 C under a nitrogen atmosphere. At this temperature, 112.0 g of a 7% by weight aqueous sodium peroxodisulfate solution, 103.1 g of a 40% by weight aqueous sodium bisulfite solution and 931.4 g of a mixture consisting of 48.3% by weight of distilled acrylic acid, 8.1% by weight of 2-acrylamido-2-methylpropanesulfonic acid, 0.002% by weight of 4-methoxyphenol solution, 3.1% by weight of sodium hydroxide solution and 40.5% by weight of demineralized water were metered in simultaneously, separately and in parallel while stirring. The monomer mixture was metered in within 3 hours, sodium peroxodisulfate within 4.5 hours and sodium bisulfite within 2.75 hours. After the end of the monomer feed, 188.7 g of a 50% by weight aqueous sodium hydroxide solution were added at internal temperature 90 C within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 hour. Thereafter, 350.0 g of demineralized water were added, which cooled the polymer solution to room temperature. The pH and K values, molecular weights N/In and RN and the solids content were determined, and the product mixture was assessed visually.
=
Example 5 A reactor was initially charged with 150.0 g of demineralized water together with 50.0 g of allyl alcohol alkoxylate of the formula CH2=CHCH20-(E016)-H. Subsequently, the mixture was heated to internal temperature 90 C under a nitrogen atmosphere.
At this 5 temperature, 214.0 g of a 7% by weight aqueous sodium peroxodisulfate solution, 50.0 g of a 40% by weight aqueous sodium bisulfite solution and 818.7 g of a mixture consisting of 36.7% by weight of distilled acrylic acid, 18.5% by weight of 2-acrylamido-2-methylpropanesulfonic acid, 0.001% by weight of 4-methoxyphenol solution, 7.5% by weight of sodium hydroxide solution and 37.7% by weight of demineralized water were 10 metered in simultaneously, separately and in parallel while stirring.
The monomer mixture was metered in within 3 hours, sodium peroxodisulfate within 4.5 hours and sodium bisulfite within 2.75 hours. After the end of the monomer feed, 162.2 g of a 50%
by weight aqueous sodium hydroxide solution were added at internal temperature within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 15 hour. Thereafter, the polymer solution was cooled to room temperature.
The pH and K
values, molecular weights Mn and M, and the solids content were determined, and the product mixture was assessed visually.
Example 6
20 A reactor was initially charged with 250.0 g of demineralized water together with 50.0 g of allyl alcohol alkoxylate (CH2=CHCH20-(E07.7P03.0)-H. Subsequently, the mixture was heated to internal temperature 90 C under a nitrogen atmosphere. At this temperature, 75.0 g of a 7% by weight aqueous sodium peroxodisulfate solution, 50.0 g of a 30.7% by weight aqueous sodium hypophosphite solution and 760.4 g of a mixture consisting of 39.5% by weight of distilled acrylic acid, 20.0% by weight of 2-acrylamido-2-methylpropanesulfonic acid, 0.002% by weight of 4-methoxyphenol solution, 7.6% by weight of sodium hydroxide solution and 32.9% by weight of demineralized water were metered in simultaneously, separately and in parallel while stirring. The monomer mixture was metered in within 3 hours, sodium peroxodisulfate within 4.5 hours and sodium bisulfite within 2.75 hours. After the end of the monomer feed, 120.0 g of a 50%
by weight aqueous sodium hydroxide solution were added at internal temperature within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 hour. Thereafter, 75.0 g of demineralized water were added to cool the polymer solution to room temperature. The pH and K values, molecular weights Mn and Mw and the solids content were determined, and the product mixture was assessed visually.
Example 7 A reactor was initially charged with 250.0 g of demineralized water together with 50.0 g of allyl alcohol alkoxylate of the formula CH2=CHCH20-(E06)(E05.1P03.6)-H.
Subsequently, the mixture was heated to internal temperature 90 C under a nitrogen =
=
by weight aqueous sodium hydroxide solution were added at internal temperature within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 hour. Thereafter, 75.0 g of demineralized water were added to cool the polymer solution to room temperature. The pH and K values, molecular weights Mn and Mw and the solids content were determined, and the product mixture was assessed visually.
Example 7 A reactor was initially charged with 250.0 g of demineralized water together with 50.0 g of allyl alcohol alkoxylate of the formula CH2=CHCH20-(E06)(E05.1P03.6)-H.
Subsequently, the mixture was heated to internal temperature 90 C under a nitrogen =
=
21 atmosphere. At this temperature, 75.0 g of a 7% by weight aqueous sodium peroxodisulfate solution, 50.0 g of a 40% by weight aqueous sodium bisulfite solution and 760.4 g of a mixture consisting of 39.4% by weight of distilled acrylic acid, 19.9%
by weight of 2-acrylamido-2-methylpropanesulfonic acid, 0.002% by weight of 4-methoxyphenol solution, 7.6% by weight of sodium hydroxide solution and 33.1% by weight of demineralized water were metered in simultaneously, separately and in parallel while stirring. The monomer mixture was metered in within 3 hours, sodium peroxodisulfate within 4.5 hours and sodium bisulfite within 2.75 hours. After the end of the monomer feed, 132.0 g of a 50% by weight aqueous sodium hydroxide solution were added at internal temperature 90 C within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 hour. Thereafter, 50.0 g of demineralized water were added to cool the polymer solution to room temperature. The pH and K values, molecular weights Mn and NI, and the solids content were determined, and the product mixture was assessed visually.
Example 8 A glass reactor equipped with stirrer, thermometer, pH electrode and several feed devices was initially charged with 30 g of deionized water, 59 g of an aqueous sodium allyisulfonate solution (35% by weight of sodium allylsulfonate) and 0.01 g of iron(II) sulfate heptahydrate, which were adjusted to a polymerization initiation temperature of 20 C (initial charge). In a separate feed vessel, 72 g of acrylic acid were mixed homogeneously with 72 g of deionized water (solution A). In a further separate feed vessel, 10.5 g of isoprenol polyethylene glycol of the formula CH2=C(CH3)CH2CH2-(E0113)-H were mixed homogeneously with 10.5 g of deionized water (solution B). After the mixing, 0.75 g of 2-mercaptoethanol was added to solution B. In parallel, a third solution of 5 g of sodium hydroxymethanesulfinate (BrOggolit SFS from Bruggemann GmbH) in 45 g of water was prepared (solution C).
=
After preparing solutions A, B and C, 6 g of hydrogen peroxide (30% by weight in water) were added to the initial charge mixture. At the same time, the addition of solution A, solution B and solution C to the stirred initial charge was commenced.
Solution A was added at a dosage rate of 144 g/h over 60 minutes.
Solution B was added in parallel with a dosage rate of 21.75 g/h over the said period of 60 minutes.
=
by weight of 2-acrylamido-2-methylpropanesulfonic acid, 0.002% by weight of 4-methoxyphenol solution, 7.6% by weight of sodium hydroxide solution and 33.1% by weight of demineralized water were metered in simultaneously, separately and in parallel while stirring. The monomer mixture was metered in within 3 hours, sodium peroxodisulfate within 4.5 hours and sodium bisulfite within 2.75 hours. After the end of the monomer feed, 132.0 g of a 50% by weight aqueous sodium hydroxide solution were added at internal temperature 90 C within 1.5 hours. This was followed by continued polymerization at 90 C for another 1 hour. Thereafter, 50.0 g of demineralized water were added to cool the polymer solution to room temperature. The pH and K values, molecular weights Mn and NI, and the solids content were determined, and the product mixture was assessed visually.
Example 8 A glass reactor equipped with stirrer, thermometer, pH electrode and several feed devices was initially charged with 30 g of deionized water, 59 g of an aqueous sodium allyisulfonate solution (35% by weight of sodium allylsulfonate) and 0.01 g of iron(II) sulfate heptahydrate, which were adjusted to a polymerization initiation temperature of 20 C (initial charge). In a separate feed vessel, 72 g of acrylic acid were mixed homogeneously with 72 g of deionized water (solution A). In a further separate feed vessel, 10.5 g of isoprenol polyethylene glycol of the formula CH2=C(CH3)CH2CH2-(E0113)-H were mixed homogeneously with 10.5 g of deionized water (solution B). After the mixing, 0.75 g of 2-mercaptoethanol was added to solution B. In parallel, a third solution of 5 g of sodium hydroxymethanesulfinate (BrOggolit SFS from Bruggemann GmbH) in 45 g of water was prepared (solution C).
=
After preparing solutions A, B and C, 6 g of hydrogen peroxide (30% by weight in water) were added to the initial charge mixture. At the same time, the addition of solution A, solution B and solution C to the stirred initial charge was commenced.
Solution A was added at a dosage rate of 144 g/h over 60 minutes.
Solution B was added in parallel with a dosage rate of 21.75 g/h over the said period of 60 minutes.
=
22 Solution C was added in parallel with a dosage rate of 10 g/h over the said period of 60 minutes. Subsequently, the dosage rate of solution C was increased to 50 g/h and it was pumped into the initial charge mixture while stirring over a period of 10 minutes.
= After complete addition of solutions A, B and C, no peroxide was found in the reaction vessel.
Subsequently, the resulting polymer solution was adjusted to a pH of 2.6 with about 2.8 g of a 50% by weight sodium hydroxide solution.
The resulting copolymer was obtained in a colorless solution which had a solids content of 37.0%. The mean molecular weight of the copolymer was Mw 18 000 g/mol.
The pH and K values, molecular weights Mr, and M, and the solids content were determined and the product mixture was assessed visually.
The composition of the polymers is reproduced in table 1.
Table 1 Monomer proportions Monomer composition of the [% by wt.]
copolymer Cl AS/MAS/SEMA/MPEGMA(1000) 28.3 : 31.0 : 29.2 : 11.6 C2 AS/MASNS/MPEGMA(1000) 28.3 : 31.0 :29.2 : 11.6 1 AS/AMPS/CH2=CHCH20-(E04.1)(E012.3P05.5)-H 40 : 30 : 30 2 AS/AMPS/CH2=CHCH20-(E04.1)(E012.3P05.5)-H 60 : 20 : 20 3 AS/AMPS/CH2=CHCH20-(E04.1)(E012.3P05.5)-H 80 : 10 :10 4 AS/AMPS/CH2=CHCH20-(E04.1)(E012.3P05.5)-H 60: 10 : 30 5 AS/AMPS/CH2=CHCH20-(E015)-H 60 : 30 : 10 6 AS/AMPS/ CH2=CHCH20-(E07,7P03.0) -H 60 : 30 : 10 7 AS/AMPS/CH2=CHCH20-(E06.0(E05.1P03.6)-H 60 : 30 : 10 8 AS/IPEG500/ALS 60 : 20 : 20 AS .7-- acrylic acid
= After complete addition of solutions A, B and C, no peroxide was found in the reaction vessel.
Subsequently, the resulting polymer solution was adjusted to a pH of 2.6 with about 2.8 g of a 50% by weight sodium hydroxide solution.
The resulting copolymer was obtained in a colorless solution which had a solids content of 37.0%. The mean molecular weight of the copolymer was Mw 18 000 g/mol.
The pH and K values, molecular weights Mr, and M, and the solids content were determined and the product mixture was assessed visually.
The composition of the polymers is reproduced in table 1.
Table 1 Monomer proportions Monomer composition of the [% by wt.]
copolymer Cl AS/MAS/SEMA/MPEGMA(1000) 28.3 : 31.0 : 29.2 : 11.6 C2 AS/MASNS/MPEGMA(1000) 28.3 : 31.0 :29.2 : 11.6 1 AS/AMPS/CH2=CHCH20-(E04.1)(E012.3P05.5)-H 40 : 30 : 30 2 AS/AMPS/CH2=CHCH20-(E04.1)(E012.3P05.5)-H 60 : 20 : 20 3 AS/AMPS/CH2=CHCH20-(E04.1)(E012.3P05.5)-H 80 : 10 :10 4 AS/AMPS/CH2=CHCH20-(E04.1)(E012.3P05.5)-H 60: 10 : 30 5 AS/AMPS/CH2=CHCH20-(E015)-H 60 : 30 : 10 6 AS/AMPS/ CH2=CHCH20-(E07,7P03.0) -H 60 : 30 : 10 7 AS/AMPS/CH2=CHCH20-(E06.0(E05.1P03.6)-H 60 : 30 : 10 8 AS/IPEG500/ALS 60 : 20 : 20 AS .7-- acrylic acid
23 MAS = methacrylic acid AMPS = 2-acrylamido-2-methylpropylsulfonic acid IPEG500 = isoprenol polyethylene glycol with an average of 11.3 ethylene oxide units The analytical data of the polymers are reproduced in table 2.
Table 2: Analytical data for the examples Example Solids K value pH Mwc Visual assessment content (pH 7) (tq) [Na Cl 18.1 31.9 7.2 14 BOO Clear, pale yellowish, viscous solution C2 18.8 22.3 7.2 5 930 Clear, pale yellowish, viscous solution 1 33.2 44.2 4.5 20 400 Clear, colorless, viscous solution 2 40.4 50.9 4.5 30 600 Clear, colorless, viscous solution 3 40.2 49.8 4.5 26 500 Clear, colorless, viscous solution 4 41.1 49.7 4.5 31 200 Clear, colorless, viscous solution 5 41.6 39.5 4.5 29 100 Clear, colorless, viscous solution 6 40.9 35.2 4.5 21 200 Clear, colorless, viscous solution 7 42.6 43.3 4.5 20 200 Slightly cloudy, colorless, viscous solution 8 39.4 26.9 2.5 29 700 Clear, colorless, viscous solution a) ISO 3251, (0.25 g, 150 C, 2h) b) determined by the Fikentscher method with a 1% solution in demineralized water c) determined by gel permeation chromatography The polymers were tested in the following phosphate-free formulations PF1 and PF2, and in the phosphate-based formulation P1. The composition of the test formulations is reproduced in table 3 (figures in % by weight).
Table 3 Protease 1 2 2 Amylase 0.2 0.5 0.5 Surfactant 5 5 4.5 Polymer 10 14 6.5 Sodium percarbonate 10.5 12.5 12.5 a =
Table 2: Analytical data for the examples Example Solids K value pH Mwc Visual assessment content (pH 7) (tq) [Na Cl 18.1 31.9 7.2 14 BOO Clear, pale yellowish, viscous solution C2 18.8 22.3 7.2 5 930 Clear, pale yellowish, viscous solution 1 33.2 44.2 4.5 20 400 Clear, colorless, viscous solution 2 40.4 50.9 4.5 30 600 Clear, colorless, viscous solution 3 40.2 49.8 4.5 26 500 Clear, colorless, viscous solution 4 41.1 49.7 4.5 31 200 Clear, colorless, viscous solution 5 41.6 39.5 4.5 29 100 Clear, colorless, viscous solution 6 40.9 35.2 4.5 21 200 Clear, colorless, viscous solution 7 42.6 43.3 4.5 20 200 Slightly cloudy, colorless, viscous solution 8 39.4 26.9 2.5 29 700 Clear, colorless, viscous solution a) ISO 3251, (0.25 g, 150 C, 2h) b) determined by the Fikentscher method with a 1% solution in demineralized water c) determined by gel permeation chromatography The polymers were tested in the following phosphate-free formulations PF1 and PF2, and in the phosphate-based formulation P1. The composition of the test formulations is reproduced in table 3 (figures in % by weight).
Table 3 Protease 1 2 2 Amylase 0.2 0.5 0.5 Surfactant 5 5 4.5 Polymer 10 14 6.5 Sodium percarbonate 10.5 12.5 12.5 a =
24 Tetraacetylethylenediamine 4 4 4 Sodium disilicate 2 5 4 Sodium tripolyphosphate 40 Heavy soda 18.8 25 25 Sodium citrate dihydrate 33 25 Citric acid 5 Methylglycinediacetic acid 15 0 Hydroxyethane-(1,1-diphosphonic 0.5 2 1 acid) The following test conditions were observed:
Dishwasher: Miele G 1222 SCL
Program: 65 C (with prewash) Ware: 3 knives (WMF Berlin table knives, monobloc) 3 Amsterdam drinking glasses, 0.2 I
3 "OCEAN BLAU" BREAKFAST PLATES (MELAMINE) 3 porcelain plates: FLAT RIMMED PLATES, 19 CM
Arrangement: knives in the cutlery drawer, glasses in the upper basket, plates sorted in the lower basket Dishwasher detergent: 21 g Addition of soil: 50 g of molten ballast soil is metered in with the formulation after the prewash, see below for composition Rinse temperature: 65 C
Water hardness: 21 dH (Ca/Mg):HCO3 (3:1):1.35 Rinse cycles: 15; with pause for 1 h between each (10 min with door open, 50 min with door closed) Evaluation: visual after 15 rinse cycles The ware was assessed after 15 cycles in a darkened chamber under light behind an aperture plate, using a scale of marks from 10 (very good) to 1 (very poor).
Marks of 1 - 10 were awarded both for spotting (very many intense spots = 1 to no spots = 10) and for scale (1 = very high scale, 10 = no scale).
Composition of the ballast soil:
Starch: 0.5% potato starch, 2.5% gravy Fat: 10.2% margarine Protein: 5.1% egg yolk, 5.1% milk Others: 2.5% tomato ketchup, 2.5% mustard, 0.1% benzoic acid, 71.4% water Result:
Especially on glass and knives, the inventive copolymers exhibit an improved effect compared to the comparative examples.
5 The tables which follow list the added marks for scale formation and spotting on knives and drinking glasses.
Phosphate-free formulation PF 1 Polymer Knives (S + B) Glasses (S + B) Total (max 40) Cl 12 12 24 S = spotting B = scale Phosphate-containing formulation P1 Polymer Knives (S + B) Glasses (S + B) Total (max 40) Cl 19 12 31 The inventive polymers were also tested in the formulation PF2. With the formulation PF2 too, the inventive copolymers were better than the comparative polymers.
Dishwasher: Miele G 1222 SCL
Program: 65 C (with prewash) Ware: 3 knives (WMF Berlin table knives, monobloc) 3 Amsterdam drinking glasses, 0.2 I
3 "OCEAN BLAU" BREAKFAST PLATES (MELAMINE) 3 porcelain plates: FLAT RIMMED PLATES, 19 CM
Arrangement: knives in the cutlery drawer, glasses in the upper basket, plates sorted in the lower basket Dishwasher detergent: 21 g Addition of soil: 50 g of molten ballast soil is metered in with the formulation after the prewash, see below for composition Rinse temperature: 65 C
Water hardness: 21 dH (Ca/Mg):HCO3 (3:1):1.35 Rinse cycles: 15; with pause for 1 h between each (10 min with door open, 50 min with door closed) Evaluation: visual after 15 rinse cycles The ware was assessed after 15 cycles in a darkened chamber under light behind an aperture plate, using a scale of marks from 10 (very good) to 1 (very poor).
Marks of 1 - 10 were awarded both for spotting (very many intense spots = 1 to no spots = 10) and for scale (1 = very high scale, 10 = no scale).
Composition of the ballast soil:
Starch: 0.5% potato starch, 2.5% gravy Fat: 10.2% margarine Protein: 5.1% egg yolk, 5.1% milk Others: 2.5% tomato ketchup, 2.5% mustard, 0.1% benzoic acid, 71.4% water Result:
Especially on glass and knives, the inventive copolymers exhibit an improved effect compared to the comparative examples.
5 The tables which follow list the added marks for scale formation and spotting on knives and drinking glasses.
Phosphate-free formulation PF 1 Polymer Knives (S + B) Glasses (S + B) Total (max 40) Cl 12 12 24 S = spotting B = scale Phosphate-containing formulation P1 Polymer Knives (S + B) Glasses (S + B) Total (max 40) Cl 19 12 31 The inventive polymers were also tested in the formulation PF2. With the formulation PF2 too, the inventive copolymers were better than the comparative polymers.
Claims (13)
1. A detergent formulation for machine dishwashing, comprising, as components a) 1 to 20% by weight of at least one copolymer which comprises, in copolymerized form, a1) 30 to 90% by weight of at least one monomer selected from the group consisting of acrylic acid, methacrylic acid and salts thereof, a2) 3 to 60% by weight of at least one monomer comprising sulfo groups selected from allylsulfonic acid and 2-acrylamido-2-methylpropanesulfonic acid, a3) 3 to 60% by weight of at least one nonionic monomer of the formula I
H2C=C(R1)(CH2)xO[R2-O]o-R3 (I) in which R1 is hydrogen or methyl, R2 are identical or different, linear or branched C2-C6-alkylene radicals which may be arranged in blocks or randomly, and R3 is hydrogen or a straight-chain or branched C1-C4-alkyl radical, x is 0, 1 or 2 and o is a natural number from >5 to 50, a4) 0 to 30% by weight of one or more further ethylenically unsaturated monomers which are polymerizable with a1), a2) and a3), where the sum of a1), a2), a3) and a4) adds up to 100% by weight, b) 0 to 20% by weight of polycarboxylates other than component a) c) 0.1 to 50% by weight of complexing agents, d) 0 to 70% by weight of phosphates, e) 0.1 to 60% by weight of further builders and cobuilders, f) 0.1 to 20% by weight of nonionic surfactants, g) 0 to 30% by weight of bleaches and optionally bleach activators and bleach catalysts, h) 0.1 to 8% by weight of enzymes, i) 0.1 to 50% by weight of one or more further additives selected from the group consisting of anionic or zwitterionic surfactants, alkali carriers, corrosion inhibitors, defoamers, dyes, fragrances, fillers, organic solvents, tabletting aids, disintegrants, thickeners, solubilizers and water, wherein the sum of components a) to i) adds up to 100% by weight.
H2C=C(R1)(CH2)xO[R2-O]o-R3 (I) in which R1 is hydrogen or methyl, R2 are identical or different, linear or branched C2-C6-alkylene radicals which may be arranged in blocks or randomly, and R3 is hydrogen or a straight-chain or branched C1-C4-alkyl radical, x is 0, 1 or 2 and o is a natural number from >5 to 50, a4) 0 to 30% by weight of one or more further ethylenically unsaturated monomers which are polymerizable with a1), a2) and a3), where the sum of a1), a2), a3) and a4) adds up to 100% by weight, b) 0 to 20% by weight of polycarboxylates other than component a) c) 0.1 to 50% by weight of complexing agents, d) 0 to 70% by weight of phosphates, e) 0.1 to 60% by weight of further builders and cobuilders, f) 0.1 to 20% by weight of nonionic surfactants, g) 0 to 30% by weight of bleaches and optionally bleach activators and bleach catalysts, h) 0.1 to 8% by weight of enzymes, i) 0.1 to 50% by weight of one or more further additives selected from the group consisting of anionic or zwitterionic surfactants, alkali carriers, corrosion inhibitors, defoamers, dyes, fragrances, fillers, organic solvents, tabletting aids, disintegrants, thickeners, solubilizers and water, wherein the sum of components a) to i) adds up to 100% by weight.
2. The detergent formulation according to claim 1, wherein component g) comprises bleaches, bleach activators and bleach catalysts.
3. The detergent formulation according to claim 1 or 2, wherein x in formula (l) is 1.
4. The detergent formulation according to claim 3, wherein R1 in formula (l) is H.
5. The detergent formulation according to claim 1 or 2, wherein x in formula (l) is 2.
6. The detergent formulation according to claim 5, wherein R1 in formula (l) is methyl.
7. The detergent formulation according to any one of claims 1 to 6, wherein the nonionic monomer of the formula (l) comprises ethylene oxide and/or propylene oxide copolymerized in blocks and/or randomly.
8. The detergent formulation according to any one of claims 1 to 7, wherein the nonionic monomer of the formula (l) comprises an average of 8 to 40 alkylene oxide units in copolymerized form.
9. The detergent formulation according to any one of claims 1 to 8, wherein the copolymer a) comprises 40 to 90% by weight of monomers al), 4 to 40% by weight of monomers a2) and 4 to 40% by weight of monomers a3).
10. The detergent formulation according to claim 9, wherein the copolymer a) comprises 45 to 85% by weight of monomers al), 6 to 35% by weight of monomers a2) and 6 to 35% by weight of monomers a3).
11. A copolymer which comprises, in copolymerized form, a1) 30 to 90% by weight of at least one monomer selected from the group consisting of acrylic acid, methacrylic acid and salts thereof, a2) 3 to 60% by weight of at least one monomer comprising sulfo groups selected from allylsulfonic acid and 2-acrylamido-2-methylpropanesulfonic acid, a3) 3 to 60% by weight of at least one nonionic monomer of the formula l H2C=C(R1)(CH2)xO[R2-O]o-R3 (1) in which R1 is hydrogen or methyl, R2 are identical or different, linear or branched C2-C6-alkylene radicals which may be arranged in blocks or randomly, and R3 is hydrogen or a straight-chain or branched C1-C4-alkyl radical, x is 2 and o is a natural number from >5 to 50, a4) 0 to 30% by weight of one or more further ethylenically unsaturated monomers which are polymerizable with a1), a2) and a3), where the sum of a1), a2), a3) and a4) adds up to 100% by weight.
12. The copolymer according to claim 11, wherein R1 in formula (l) is methyl.
13. Use of the copolymer according to claim 11 or 12 as a scale-inhibiting additive in phosphate-free or phosphate-containing detergent formulations for machine dishwashing.