CA2786317C

CA2786317C - Process for the production of lithium carbonate

Info

Publication number: CA2786317C
Application number: CA2786317A
Authority: CA
Inventors: Ignatius Kim Seng Tan
Original assignee: Tianqi Lithium Corp
Current assignee: Tianqi Lithium Corp
Priority date: 2010-01-07
Filing date: 2010-11-19
Publication date: 2020-07-07
Anticipated expiration: 2030-11-19
Also published as: CA2786317A1; CN102892708B; AU2010341402B2; AU2010341402A1; CN102892708A; WO2011082444A1

Abstract

A process for the production of lithium carbonate is provided, including the steps of calcining alpha-spodumene to produce beta-spodumene, sulphating the beta-spodumene and passing it to a leach step in which lithium sulphate is leached in water to produce a pregnant leach slurry, removing impurities from the pregnant leach slurry and precipitating calcium carbonate therefrom, passing the pregnant leach slurry to an ion exchange step to remove residual calcium, magnesium, iron and aluminum, and then adding sodium carbonate to the pregnant leach slurry to produce lithium carbonate slurry and a sodium sulphate mother liquor. The lithium carbonate slurry can then be digested with carbon dioxide and subsequently decomposed and crystallised to produce lithium carbonate.

Description

"Process for the Production of Lithium Carbonate"
Field of the Invention The present invention relates to a process for the production of lithium carbonate.
More particularly, the process of the present invention is intended to provide a high purity or battery grade lithium carbonate product. The process of the present invention may also provide a sodium sulphate product.
Background Art Known processes for the production of lithium carbonate from lithium containing ores or concentrates typically utilise the thermal treatment of an alpha-spodumene ore or concentrate. This thermal treatment can be referred as decrepitation and transforms the alpha-spodumene to beta-spodumene which is in turn able to be solubilised by acid. The step in which the beta-spodumene is sulphated in acid takes place in a kiln and produces water soluble lithium sulphate. The lithium sulphate is passed to one or more leaching tanks in which the lithium sulphate is leached with water. Limestone, lime and sodium carbonate are subsequently added to the product of the leach so as to adjust the pH of the slurry, whereby certain impurities, including iron, aluminium, magnesium and calcium are precipitated. The residue is then separated which leaves a concentrated solution of lithium sulphate. The lithium sulphate solution is then treated with a concentrated sodium carbonate solution so as to precipitate lithium carbonateõ

Such a process is described in Canadian Patent 1297265.
=
However, the above described process of the prior art is relatively inefficient in the removal of impurities that remain in the pregnant leach solution, which results in a relatively impure lithium carbonate product. This is particularly problematic when attempting to produce a high quality or battery grade lithium carbonate product.
Further, the lithium carbonate precipitation step of the prior art results in a sodium sulphate solution in addition to the pr,ecipitated lithium carbonate. The sodium sulphate solution has traditionally been treated to crystallise sodium sulphate decahydrate for drying and disposal or sale, with some liquor recirculated to the

- 2 -water leach of the lithium sulphate. Such a process does not effectively utilize the sodium sulphate solution to produce a sodium sulphate product, the sodium decahydrate requiring drying/or heating before disposal. Similarly, the impurities removed from the pregnant leach solution, including iron, alumina and silicates have simply passed to waste and have remained unutilized.
Attempts have been made previously to increase the purity of lithium carbonate product, particularly that obtained from brines or bitterns. Such efforts include the use of carbon dioxide to produce a lithium bicarbonate solution, at elevated pressure (up to 20 atm), with the subsequent precipitation of lithium carbonate.
An additional further purification step is then necessary, such as a further ion exchange or separation step, to produce the target purity of lithium carbonate.
Such a process is described in US Patent 6048507 to Amouzegar et al. The need in such processes for elevated pressure and additional impurity removal steps impacts adversely on the economy of the process.
The process of the present invention has as one object thereof to overcome substantially one or more of the above mentioned problems associated with prior art processes, or to at least provide a useful alternative thereto.
Reference to cited material or information contained in the text should not be understood as a concession that the material or information was part of the common general knowledge or was known in Australia or any other country.
Throughout this specification, unless the context requires otherwise, the word "comprise", or variations such as "comprises" or "comprising", will be understood to imply the inclusion of a stated integer or group of integers but not the exclusion of any other integer or group of integers.
27293818_1INATDOCS

- 3 -Disclosure of the Invention In accordance with the present invention there is provided a process for the production of lithium carbonate, the process characterised by the steps of:
(i) Calcining an alpha-spodumene ore or concentrate to produce beta-spodumene;
(ii) Sulphating the beta-spodumene at elevated temperature;
(iii) Passing the sulphated beta-spodumene to a leach step in which lithium sulphate is leached in water;
(iv) Passing the pregnant leach solution from the leach step to a series of impurity removal steps in which iron, alumina, silicates and magnesium are, in large part, precipitated and removed;
(v) Adding sodium carbonate to the product of step (iv) by which calcium is precipitated;
(vi) The product of step (v) is then passed to an ion exchange step in which residual calcium, magnesium and other remaining multivalent cations are substantially removed; and (vii) Passing the purified' product of step (vi) to a lithium carbonate precipitation step in which sodium carbonate is added to produce precipitated lithium carbonate and a sodium sulphate mother liquor.
Preferably, the mother liquor from step (vii) is passed to an anhydrous sodium sulphate recovery process from which a solid sodium sulphate product is obtained. A portion of the sodium sulphate mother liquor is preferably recirculated to the leach of step (iii).
The lithium carbonate precipitation step (vii) is preferably conducted in at least one draft tube baffled crystalliser with a residence time of about 90 minutes.

4 PCT/AU2010/001557 Preferably, the lithium carbonate. precipitation step (vii) is conducted sequentially in two crystallisers.
In one form of the invention the precipitated lithium carbonate of step (vii) is thickened prior to passing to a filter step. The filter step is preferably followed by a repulp washing stage and a centrifuge step. Both the filter step and centrifuge step preferably incorporate a hot wash to reduce impurities. The resulting product = is preferably then milled to minus 6 pm.
In another form of the present invention the precipitated lithium carbonate of step == (vii) is thickened. prior to passing to a bicarbonate circuit, the bicarbonate circuit comprising digestion with carbon dioxide to produce a bicarbonate intermediate, and subsequent crystallisation to produce a lithium carbonate product of increased purity.
=
Preferably, the sodium sulphate recovery process is fed from the thickening step after the lithium carbonate precipitation step (vii). The sodium sulphate recovery process preferably comprises creating a supersaturated solution and passing this solution to a crystallisation step. The crystallisation step is preferably conducted at a temperature of about 80 C to 90 C and a pressure of about 45 kPa(a). The residence time is preferably about 60 minutes.
Still preferably, water evaporated from the solution in the creation of the supersaturated solution is recompressed, combined with make-up steam and utilised in the anhydrous sodium sulphate crystallisation step. This crystallisation step preferably utilises a vacuum evaporative crystalliser. =
The crystallisation step produces a crystal slurry that is preferably discharged to a centrifuge step. This centrifuge step preferably further comprises a wash with water, the liquid product of which is recycled back to the leach step (iii).
The solid product of the centrifuge step and wash is then preferably dried.
Preferably, the impurity removal steps of step (iv) comprise, in turn, the addition of lime/hydrated lime, hydrogen peroxide and sodium hydroxide. After the addition of the hydrogen peroxide the slurry is preferably thickened, the underflow of the

- 5 --thickening step then being filtered and dried to provide an alumina silicate product.
Still preferably, the beta-spodumene of step (i) is cooled and milled prior to the = sulphating step (ii). The beta-spodurnene is preferably milled to less than about 300 pm.
Still further preferably, the sulphating step (ii) is conducted in a sulphating kiln at = about 250 C over a residence time of about 45 minutes.
Still further preferably, the sulphated spodumene is cooled prior to feeding into the leach Step (iii).
The bicarbonate circuit preferably further comprises a centrifuge/wash step and a .
= repulp step prior to the digestion step. The digestion step is preferably conducted at atmospheric pressure and at .a temperature of less than about 20 C to 40 C.
Preferably, the crystallisation step comprises the addition of steam to a lithium bicarbonate product of the digestion step, thereby producing both carbon dioxide and lithium carbonate products. The crystallisation step is preferably conducted at about 95 C.
Still preferably, the lithium carbonate product of the crystallisation step is passed to a thickening step, the overflow from which is passed, at least in part, to the repulp step prior to the digestion step. The overflow is preferably subjected to cooling prior to passing to the repulp step.
In a preferred form of the present invention a lithium carbonate product of the = thickening step provided after the crystallisation step is passed, or recirculated, to a point in the bicarbonate circuit prior to the digestion step so as to increase the purity of the ultimate lithium carbonate product. Preferably, the recirculated lithium carbonate is added to the centrifuge step prior to the repulp step.
In accordance with the present invention there is further provided a process for the production of lithium carbonate, the process characterised by the steps of:

- 6 -=
(i) Calcining an alpha-spodumene or ore concentrate to produce beta-spodumene;
(ii) Sulphating the beta-spodumene at elevated temperature;
(iii) Passing the sulphated beta-spodurnene to a leach step in which lithium sulphate is leached in water;
(iv) Passing the pregnant leach solution from the leach step to a series of impurity removal steps in which iron, alumina, silicates and magnesium are, in large part, precipitated and removed;
(v) Adding sodium carbonate to the product of step (iv) by which calcium is precipitated; =
(vi) The product of step (v) is then passed to an ion exchange step in which residual calcium, magnesium and other remaining multivalent = cations are substantially removed;
= (vii) Passing the purified product of step (vi) to a lithium carbonate precipitation step in which sodium carbonate is added to produce precipitated lithium carbonate and a sodium sulphate mother liquor;
and = (viii) Passing the precipitated lithium carbonate of step (vii) to a bicarbonate circuit, the bicarbonate circuit comprising digestion with carbon dioxide to produce a bicarbonate intermediate, and subsequent crystallisation to produce a lithium carbonate product of = increased purity.
Brief Description of the Drawings The process of the present invention will now be described, by way Of example only, with reference to two embodiments thereof and the accompanying drawings, in which:-

- 7 -Figure 1 is a schematic flow-sheet depicting a process for the production of lithium carbonate in accordance with a first embodiment of the present invention; and =
Figure 2 is a schematic flow-sheet depicting a bicarbonate circuit that is provided as a substitute for a portion of the process of Figure 1, in accordance with a second embodiment of the present invention.
Best Mode(s) for Carrying Out the Invention In Figure 1 there is shown a process 10 for the production of lithium carbonate, in accordance with a first embodiment of the present invention. , All of the unit operations embodied in the process 10 are designed to operate continuously with full process instrumentation and control being provided for.
A concentrate stockpile and reclaim area 12 encompasses a 12 week capacity = stockpile (30,0001) of alpha-spodumene concentrate 14. Front end loaders and belt conveyors 18 transport the alpha-spodumene concentrate to a calcining step, conducted in a direct fired rotary kiln calciner 20.
The alpha-spodumene concentrate is calcined at about 1080 C to convert the alpha-spodumene to the leachable beta-spodumene. Off-gases from the calciner are directed through a cyclone and an electrostatic precipitator specified to comply with known environmental emissions limits. The hot calcine is indirectly 20 cooled in a cooling step 22 and then dry-milled to less than 300 pm in a ball mill 24.
After storage in a surge bin, the beta-spodumene is mixed with a 40% excess of concentrated (98% wlw acid) sulphuric acid 26, and roasted at 250 C for about to 45 minutes in an indirectly heated sulphating kiln 28. Off-gases from the sulphating kiln 28 are cleaned in a wet scrubber. The sulphated beta-spodumene is then cooled to 95 C in a bin that feeds a leach circuit 30. An excess of at least 20% acid (based on the lithium content of the ore), preferably at least 40%
acid, is used to maximise the lithium extraction while minimising reagent use and any need for sulphate addition to the leach circuit 30.

- 8 -, The spodumene is leached in the leach circuit 30 in a recycled sodium sulphate solution 32. The leach circuit 30 comprises a few leaching tanks operating at about 60 C to 80 C. About 95% of the lithium is leached from the betaspodumene.
Soluble iron, aluminium and magnesium are removed in large part from the leach liquor through a series of impurity removal steps, including pH modification (raising) through the addition of hydrated lime 34, the addition of hydrogen peroxide 36 (to ensure iron is present in the ferric form), and precipitation of magnesium through the addition of hydrated lime 38 at a pH of about 10 to not more than 11. Calcium is then removed in a calcium precipitation step 40 with the addition of sodium carbonate 42. The impurity precipitation occurs with the leached solids present in the slurry.
A thickening step 44 is provided prior to the addition of the hydrated lime 38. The overflow from the thickening step 44 is passed to a filter step, for example a polishing sand filter 46. The underf low from both the thickening step 44 and the filter 46 are passed to a filter step to be described hereinafter.
The product of the calcium precipitation step 40 is passed to a filtration step comprising a polishing filter 47. A resulting filtrate 48 is passed through a polishing sand filter 47 and an ion exchange step 50, comprising an IX column 50 to remove residual calcium, magnesium and other multivalent cations.
The solution passing from the ion exchange step 50 is heated 52 and then reacted with a hot sodium carbonate solution 54 in a lithium carbonate crystalliser 56 operating at 85 C. The crystalliser 56 is a draft tube baffled crystalliser and the solution flashed therein is highly supersaturated. A secondary crystalliser 56 is also provided, to which the supersaturated solution is passed after the first crystalliser 56 so as to remove the super-saturation. The result is small, inclusion free crystals of lithium carbonate readily amenable to milling.
The small crystals from the crystalliser 56 are thickened in a thickening step before passing to a filter step, incorporating for example a belt filter 60.
The filter step 60 is followed by a repulp washing stage 62 (at 40% w/w solids) before the crystals are sent to a continuous centrifuge 66. To reduce impurities, for example residual entrained sodium sulphate, the filter-step 60 and the centrifuge 66 use a

- 9 -hot wash 68, achieving an overall wash efficiency of 99%.
Solid crystals resulting from the centrifuge 66 are dried in an indirect-fired kiln 70 at 120 C. Resulting dry coarse lithium carbonate is air milled to less than 6 pm in a micronizer 72 and then pneumatically conveyed to storage bins, cooled to 50 C
in a jacketed screw conveyor and then bagged 74.
The majority of the overflow from the thickening step 58 passes to a sodium sulphate precipitation step 76. The remainder of the flow is recycled to the leach ' circuit 30. The sodium sulphate in solution, about 293 gpl, is precipitated or crystallised in, for example, a vacuum evaporative crystalliser operating at a temperature of about 80 C to 90 C and pressure of about 45 kPa(a). This allows the use of lower cost materials of construction for the crystalliser. The residence time is about 60 minutes so as to achieve a coarse crystal product. Super-saturation is achieved in the precipitation step 76 by evaporating approximately half the water from the overflow of the thickening step 58 in the evaporative crystallisation stage. The resulting water vapour is recompressed, combined with make-up steam 78 and used as the evaporative medium for the crystalliser.
A crystal slurry 80 is discharged to a single continuous centrifuge 82, where crystals are washed by cold water 84 achieving a wash efficiency of 99%. The resulting solution 32 is recycled back to the leach circuit 30. Solids from the centrifuge 82 are fed to an indirect-fired kiln 86, operating at about 120 C, which dries the crystals. The crystal product is pneumatically conveyed to product bins 88, and cooled to less than 80 C in a jacketed screw conveyer as it is conveyed from the bins to bagging stations.
Condensate throughout the process 10 is used as make-up water for hot process water, cold process water and cooling water. As the process 10 does not return condensate there is an overall positive water balance and about 1 t/h of process water is discharged to a waste (not shown).
It is to be understood that the thickening step 58 may be bypassed with certain draft tube baffled crystalliser designs.

- 10 -It is further envisaged that tantalite and alumina may also be recovered using the process 10 of the present invention. The filter cake from the thickening step may be discharged to a tantalite recovery plant (not shown). Discharge from the tantalite recovery plant may be fed onto a belt filter to remove water, which is returned to the tantalite recovery plant. The filter does not use washing and has a filtration area of 19 m2. The filer cake from the belt filter is dried in a direct-fired kiln. The dry alumina silicate is cooled to 50 C in a jacketed screw conveyor and then pneumatically conveyed to a storage bin prior to dispatch.
In Figure 2 there is shown a bicarbonate circuit 100 in accordance with a second embodiment of the present invention. The bicarbonate circuit 100 is intended for use in combination with a significant proportion of the process 10 of the first embodiment of the present invention and reference to like numerals denotes like.
parts or steps. However, this should not be understood to limit the generality of use of the bicarbonate circuit 100 as it is envisaged that the bicarbonate circuit .. 100 may have applications beyond that exemplified herein.
In the second embodiment of the present invention the small crystals from the crystalliser 56 that are thickened in the thickening step 58 are, rather than being passed to the belt filter 60 of Figure 1, passed to the bicarbonate circuit 100 of Figure 2.
Underflow.from the thickening step 58 is passed, at a temperature of about 85 C, to a centrifuge 102 in which the lithium carbonate crystals are washed. The lithium carbonate product is about 99.0% purity at this point. The product of the centrifuge 102 has a moisture content of about 14% and is directed to a repulp = step 104 to which a cooled recirculation liquor 108, to be described hereinafter, is added. The temperature of the repulp step 104 is about 45 C.
The product of the repulp step 104 is about 2 to 5% w/w solids which are directed to a digestion step 110 at less than about 50 C, for example 40 C. The digestion step 110 comprises the addition of a carbon dioxide feed stream 112 to the repulped lithium carbonate from the repulp step 104, with the addition of cooling, in a stirred reactor vessel at atmospheric pressure fora time of about 90 minutes, producing a lithium bicarbonate intermediate product 114 at less than about 50 C,

- 11 -for example 40 C.
The lithium bicarbonate intermediate product 114 is passed from the digestion step 110 to a filter step .116. A filter bypass route 118 is available. The lithium bicarbonate intermediate product 114 is in turn passed to a crystallisation step 120 comprising a multi-compartment agitated reactor vessel to which a steam feed 122 added. The crystallisation step 120 is conducted at atmospheric pressure in three overflow stages at about 95 C, and produces lithium carbonate crystals 124 and carbon dioxide 126 products.
The carbon dioxide product 126 from the crystallisation step 120 is compressed 128, .. passed to a drying step 130 using a condenser, and produces a condensate 106 as a product. This condensate 106 is combined with an overflow from a thickener 136, to be described hereinafter. From the drying step 130 the carbon dioxide is passed to further compression 132. At least a' portion of the carbon dioxide from the compression step 132 is utilized as the carbon dioxide 112 for use in the digestion step 110. Any excess carbon dioxide from compression may be stored in tank(s) 134. Alternatively, carbon dioxide may also be drawn from tanks 134 for use in the digestion step 134.
The lithium carbonate product 124 of the crystallisation step 120 is passed, at about 95 C, to a thickening step 136, from which the overflow 138 is recirculated either as .. the recirculation liquor 108 after a cooling Step(s) 142, to the repulp step 104, or as a bleed 144 to the leach circuit 30 shown in Figure 1. The cooling of the recirculation liquor 108 in the cooling step(s) 142, which may incorporate a chiller 146, reduces the temperature from about an initial 94 C to about 35 C prior to addition to the repulp step 104.
.. Lithium carbonate underflow 148 from the thickening step. 136 is passed to a centrifuge 150 in which it is washed, with the subsequent lithium carbonate product then being passed to a dryer 70 as shown in Figure 1, and the subsequent steps as described with reference to that Figure. The lithium carbonate product so produced is about 99.9% purity, or battery grade.
Additional purification may be achieved through a recycle 152 of all, or a portion 27293818_1INATDOCS

- 12 -of, the lithium carbonate product from the centrifuge step 150 to the centrifuge step 102. This can be expected to increase the purity, of the. ultimate lithium carbonate produot to a target of above 99.9% purity.
= Any available low grade lithium carbonate 154 may be fed to the repulp step 104 to be repulped, and purified via the bicarbonate circuit 100.
=
It is envisaged that the bicarbonate circuit 100 may be by-passed should = maintenance be required. The lithium carbonate product so produced will be an "off-spec" material, typically of technical grade.
Overall lithium recovery through the process of the present invention is about 82%.
As can be seen from the above, the process of the present invention provides a process by which a high purity or battery grade lithium carbonate product may be obtained from an alpha-spodumene ore or concentrate. The purity of the lithium carbonate product may be improved further through incorporation of a bicarbonate circuit as described. Further, the process of the present invention also allows the production Of a useful sodium sulphate product. The process of the present invention as described herein is typically a simpler and more economic route to the production of a high purity lithium carbonate product when compared with processes that have been described in the prior art.
=
=
Modifications and variations such as would be apparent to the skilled addressee are considered to fall within the scope of the present invention.

Claims

THE EMBODIMENTS OF THE INVENTION IN WHICH AN EXCLUSIVE PROPERTY OR
PRIVILEGE IS CLAIMED ARE DEFINED AS FOLLOWS:

1. A process for producing lithium carbonate, said process comprising the steps of:
(i) calcining an alpha-spodumene ore or concentrate to produce beta-spodumene;
(ii) sulphating the beta-spodumene at elevated temperature to produce sulphated beta-spodumene;
(iii) passing the sulphated beta-spodumene to a leach step in which lithium sulphate is leached from the sulphated beta-spodumene in water to produce a pregnant leach slurry;
(iv) passing the pregnant leach slurry from the leach step to a series of impurity removal steps in which iron, alumina, silicates and magnesium are substantially precipitated and removed;
(v) adjusting the pH of the product of step (iv) to a value of about 10 to not more than 11, and adding sodium carbonate to the product of step (iv) to precipitate calcium carbonate which is removed;
(vi) passing the product of step (v) to an ion exchange step in which residual calcium, magnesium, iron and aluminum are removed, thereby producing a purified product; and (vii) passing the purified product of step (vi) to a lithium carbonate precipitation step in which sodium carbonate is added to produce a lithium carbonate slurry and a sodium sulphate mother liquor.

2. The process according to Claim 1, wherein the sodium sulphate mother liquor is passed to an anhydrous sodium sulphate recovery process from which a solid sodium sulphate product is obtained.

3. The process according to Claim 1 or 2, wherein a portion of the sodium sulphate mother liquor is recirculated to the leach step, wherein the lithium sulphate is leached in a combination of the sodium sulphate mother liquor and the water.

4. The process according to any one of Claims 1-3, wherein the lithium carbonate precipitation step is conducted in a draft tube baffled crystalliser with a residence time of about 90 minutes.

5. The process according to any one of Claims 1-3, wherein the lithium carbonate precipitation step is conducted sequentially in two or more draft tube baffled crystallisers with a total combined residence time of about 90 minutes.

6. The process according to any one of Claims 1-5, wherein the lithium carbonate slurry is thickened by removing water therefrom prior to passing to a filter step.

7. The process according to Claim 6, wherein the filter step is followed by a repulp step and a centrifuge step.

8. The process according to Claim 7, wherein both the filter step and centrifuge step incorporate a hot wash to reduce impurities.

9. The process according to Claim 7 or 8, wherein the solid product of the centrifuge step is subsequently milled to an average particle size of less than 6 in diameter.

10. The process according to any one of Claims 1-5, wherein the lithium carbonate slurry is thickened by removing water therefrom prior to passing to a lithium carbonate purification process, the lithium carbonate purification process comprising a digestion step with carbon dioxide to produce a bicarbonate intermediate, and a subsequent decomposition and crystallisation step to produce a lithium carbonate product of increased purity.

11. The process according to Claim 2, wherein the sodium sulphate recovery process comprises creating a supersaturated solution and passing this solution to a crystallisation step.

12. The process according to Claim 11, wherein the crystallisation step is conducted at a temperature of about 80°C to about 90°C and a pressure of about 45 kPa(a).

13. The process according to Claim 11 or 12, wherein the crystallisation step has a residence time of about 60 minutes.

14. The process according to Claim 11, wherein creating the supersaturated solution produces evaporated water that is recompressed, and wherein the crystallisation step further comprises the addition of steam combined with the recompressed evaporated water.

15. The process according to Claim 11, wherein the crystallisation step utilizes a vacuum evaporative crystalliser.

16. The process according to any one of Claims 11 to 15, wherein the crystallisation step produces a crystal slurry that is discharged to a centrifuge step.

17. The process according to Claim 16, wherein the solid product of the centrifuge step is washed with cold water; and the liquid product of the centrifuge step and the washing water are recycled back to the leach step, wherein the lithium sulphate is leached in a combination of the liquid product and the water.

18. The process according to Claim 17, wherein the solid product of the centrifuge step and wash is subsequently dried.

19. The process according to any one of Claims 1-18, wherein the impurity removal steps comprise the addition, in turn, of lime/hydrated lime, hydrogen peroxide and sodium hydroxide.

20. The process according to Claim 19, wherein after the addition of the hydrogen peroxide, the pregnant leach slurry is thickened by a centrifuge step, and the solid product of the centrifuge step is dried to provide an alumina silicate product.

21. The process according to any one of Claims 1-20, wherein the beta-spodumene is cooled to 100°C or less and milled prior to the sulphating step.

22. The process according to Claim 21, wherein the beta-spodumene is milled to an average particle size of less than 300 µm in diameter.

23. The process according to any one of Claims 1-22, wherein the sulphating step is conducted in a sulphating kiln at about 250°C over a residence time of about 45 minutes.

24. The process according to Claim 23, wherein the sulphated beta-spodumene is cooled to 95°C prior to passing to the leach step.

25. The process according to Claim 10, wherein the lithium carbonate purification process further comprises a centrifuge step and a repulp step prior to the digestion step.

26. The process according to Claim 10, wherein the digestion step is conducted at atmospheric pressure and at a temperature of about 20°C to about 40°C.

27. The process according to Claim 10, wherein the decomposition and crystallisation step comprises the addition of steam to the bicarbonate intermediate of the digestion step, thereby producing both carbon dioxide and lithium carbonate products.

28. The process according to Claim 10, wherein the decomposition and crystallisation step is conducted at about 95°C.

29. The process according to Claim 10, wherein the lithium carbonate product of the decomposition and crystallisation step is thickened by a centrifuge step, and the liquid product from the centrifuge step is passed, at least in part, to a repulp step prior to the digestion step.

30. The process according to Claim 29, wherein the liquid product of the centrifuge step is subjected to cooling to 40°C or less prior to passing to the repulp step.

31. The process according to Claim 29 or 30, wherein the solid product of the centrifuge step provided after the decomposition and crystallisation step is passed to a dryer to obtain lithium carbonate product.

32. The process according to Claim 29 or 30, wherein the solid product of the centrifuge step provided after the decomposition and crystallisation step is recirculated to a point in the lithium carbonate purification process prior to the digestion step so as to increase the purity of the lithium carbonate product.

33. The process according to Claim 32, wherein the recirculated solid product of the centrifuge step is added to the centrifuge step prior to the repulp step.

34. The process according to any one of Claims 1-9, further comprising passing the lithium carbonate slurry to a lithium carbonate purification process, the lithium carbonate purification process comprising digestion with carbon dioxide, to produce a bicarbonate intermediate, and a subsequent decomposition and crystallisation step to produce a lithium carbonate product of increased purity.