CA2342928A1 - Carbon black, method for producing carbon black and use of the same - Google Patents
Carbon black, method for producing carbon black and use of the same Download PDFInfo
- Publication number
- CA2342928A1 CA2342928A1 CA002342928A CA2342928A CA2342928A1 CA 2342928 A1 CA2342928 A1 CA 2342928A1 CA 002342928 A CA002342928 A CA 002342928A CA 2342928 A CA2342928 A CA 2342928A CA 2342928 A1 CA2342928 A1 CA 2342928A1
- Authority
- CA
- Canada
- Prior art keywords
- carbon black
- same
- tan
- delta
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Carbon black characterized by a STSA surface of between 20 and 180 m2 /g, a 24M4-DBP absorption of between 40 and 140 ml/100 g, a specific BET surface of between 20 and 250 m2 /g, a content of 0.01 to 20 wt. % of silicon, referred to its overall weight, and a tan .delta.0 /tan .delta.60 ratio greater than 3.37-0.0068 STSA is produced by mixing silicon-containing compounds with the carbon black raw materials in the oxidative pyrolysis of the carbon black raw materials and optionally using carbon black oil as fuel. The carbon black can be used as a filler in rubber mixtures, preferably for tires.
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE19840663.0 | 1998-09-05 | ||
DE19840663A DE19840663A1 (en) | 1998-09-05 | 1998-09-05 | soot |
PCT/EP1999/006365 WO2000014162A1 (en) | 1998-09-05 | 1999-08-28 | Carbon black, method for producing carbon black and use of the same |
Publications (2)
Publication Number | Publication Date |
---|---|
CA2342928A1 true CA2342928A1 (en) | 2000-03-16 |
CA2342928C CA2342928C (en) | 2008-05-06 |
Family
ID=7880005
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CA002342928A Expired - Fee Related CA2342928C (en) | 1998-09-05 | 1999-08-28 | Carbon black, method for producing carbon black and use of the same |
Country Status (20)
Country | Link |
---|---|
EP (1) | EP1109866B1 (en) |
JP (1) | JP4452407B2 (en) |
KR (1) | KR100583551B1 (en) |
CN (1) | CN1210352C (en) |
AT (1) | ATE225832T1 (en) |
AU (1) | AU5742799A (en) |
BR (1) | BR9914483B1 (en) |
CA (1) | CA2342928C (en) |
CZ (1) | CZ301448B6 (en) |
DE (2) | DE19840663A1 (en) |
EG (1) | EG22239A (en) |
ES (1) | ES2185398T3 (en) |
HU (1) | HUP0103961A3 (en) |
ID (1) | ID29878A (en) |
PL (1) | PL198902B1 (en) |
PT (1) | PT1109866E (en) |
SK (1) | SK2522001A3 (en) |
TR (1) | TR200100599T2 (en) |
WO (1) | WO2000014162A1 (en) |
ZA (1) | ZA200100808B (en) |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
RU2512349C2 (en) * | 2008-10-01 | 2014-04-10 | Бриджстоун Корпорейшн | Rubber mix and air tire made therewith |
US8871173B2 (en) | 2010-02-19 | 2014-10-28 | Cabot Corporation | Method for carbon black production using preheated feedstock and apparatus for same |
US10907049B2 (en) | 2014-08-29 | 2021-02-02 | Orion Engineered Carbons Gmbh | Process for controlling the porosity of carbon blacks |
US11639444B2 (en) | 2015-11-21 | 2023-05-02 | Suncoal Industries Gmbh | Hydrothermal treatment of renewable raw material |
Families Citing this family (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2002069237A (en) * | 2000-09-01 | 2002-03-08 | Bridgestone Corp | Rubber composition |
US20040071626A1 (en) * | 2002-10-09 | 2004-04-15 | Smith Thomas Dale | Reactor and method to produce a wide range of carbon blacks |
JP4602654B2 (en) * | 2003-08-29 | 2010-12-22 | 株式会社フルヤ金属 | Thin film layer forming elastomer molding |
JP4780941B2 (en) * | 2004-08-03 | 2011-09-28 | 富士化学株式会社 | Method for producing silica-treated carbon black, carbon black obtained by the method, and rubber composition containing the same |
JP4909517B2 (en) * | 2005-02-03 | 2012-04-04 | 株式会社ブリヂストン | Rubber composition for tire |
AR068839A1 (en) * | 2007-10-09 | 2009-12-09 | Cbp Carbon Ind Inc | PROCESOPARA CLASSIFY PARTICLES IN PIROLIZED CARBON |
KR20100098381A (en) | 2007-11-07 | 2010-09-06 | 씨비피 카본 인더스트리즈 인코포레이티드 | Asphalt composition using pyrolysed carbonaceous materials |
DE102009027043B4 (en) * | 2009-06-19 | 2019-05-09 | Evonik Carbon Black Gmbh | Process for producing carbon black |
CN102884111B (en) * | 2009-12-03 | 2014-09-24 | 米其林集团总公司 | Filler blending for rubber formulations |
JP2012077133A (en) * | 2010-09-30 | 2012-04-19 | Toyo Tire & Rubber Co Ltd | Rubber composition and pneumatic tire |
FR2995559B1 (en) * | 2012-09-17 | 2014-09-05 | Michelin & Cie | TIRE WITH TREAD COMPRISING A THERMOPLASTIC ELASTOMER AND CARBON BLACK |
CN105073906B (en) | 2013-03-15 | 2019-05-14 | 卡博特公司 | Use the method for producing black pigment of incremental agent fluid |
CN103613959B (en) * | 2013-12-12 | 2015-10-21 | 云南大为制焦有限公司 | Black reactor |
JP6872640B2 (en) | 2017-12-26 | 2021-05-19 | Toyo Tire株式会社 | A method for producing a rubber wet masterbatch and a method for producing a rubber composition. |
WO2020123894A1 (en) * | 2018-12-14 | 2020-06-18 | Chrisman Ray W | Carbon black from biomass |
PL3757172T3 (en) * | 2019-06-25 | 2023-12-04 | Orion Engineered Carbons Gmbh | A process for producing carbon black and related furnace reactor |
CN111690272B (en) * | 2020-06-18 | 2021-08-17 | 浙江工业大学 | Method for improving specific surface area of rubber pyrolysis carbon black by using simulated flue gas |
CN113402905A (en) * | 2021-06-28 | 2021-09-17 | 青岛黑猫新材料研究院有限公司 | High-porosity carbon black, preparation method and preparation device thereof |
Family Cites Families (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0828789B1 (en) * | 1995-05-22 | 2005-09-14 | Cabot Corporation | Elastomeric compounds incorporating silicon-treated carbon blacks |
DE19521565A1 (en) * | 1995-06-19 | 1997-01-16 | Degussa | Improved Furnaceruße and process for their preparation |
DE19613796A1 (en) * | 1996-04-04 | 1997-10-09 | Degussa | Carbon black and process for its preparation |
-
1998
- 1998-09-05 DE DE19840663A patent/DE19840663A1/en not_active Ceased
-
1999
- 1999-08-28 BR BRPI9914483-2A patent/BR9914483B1/en not_active IP Right Cessation
- 1999-08-28 TR TR2001/00599T patent/TR200100599T2/en unknown
- 1999-08-28 AT AT99944554T patent/ATE225832T1/en not_active IP Right Cessation
- 1999-08-28 PL PL346421A patent/PL198902B1/en not_active IP Right Cessation
- 1999-08-28 PT PT99944554T patent/PT1109866E/en unknown
- 1999-08-28 HU HU0103961A patent/HUP0103961A3/en unknown
- 1999-08-28 ID IDW20010764A patent/ID29878A/en unknown
- 1999-08-28 DE DE59903057T patent/DE59903057D1/en not_active Expired - Lifetime
- 1999-08-28 CN CNB998106224A patent/CN1210352C/en not_active Expired - Fee Related
- 1999-08-28 ES ES99944554T patent/ES2185398T3/en not_active Expired - Lifetime
- 1999-08-28 EP EP99944554A patent/EP1109866B1/en not_active Expired - Lifetime
- 1999-08-28 SK SK252-2001A patent/SK2522001A3/en unknown
- 1999-08-28 AU AU57427/99A patent/AU5742799A/en not_active Abandoned
- 1999-08-28 CZ CZ20010642A patent/CZ301448B6/en not_active IP Right Cessation
- 1999-08-28 JP JP2000568914A patent/JP4452407B2/en not_active Expired - Fee Related
- 1999-08-28 WO PCT/EP1999/006365 patent/WO2000014162A1/en active IP Right Grant
- 1999-08-28 CA CA002342928A patent/CA2342928C/en not_active Expired - Fee Related
- 1999-08-28 KR KR1020017002878A patent/KR100583551B1/en not_active IP Right Cessation
- 1999-09-02 EG EG109999A patent/EG22239A/en active
-
2001
- 2001-01-29 ZA ZA200100808A patent/ZA200100808B/en unknown
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
RU2512349C2 (en) * | 2008-10-01 | 2014-04-10 | Бриджстоун Корпорейшн | Rubber mix and air tire made therewith |
US8871173B2 (en) | 2010-02-19 | 2014-10-28 | Cabot Corporation | Method for carbon black production using preheated feedstock and apparatus for same |
US9574087B2 (en) | 2010-02-19 | 2017-02-21 | Cabot Corporation | Method for carbon black production using preheated feedstock and apparatus for same |
US10907049B2 (en) | 2014-08-29 | 2021-02-02 | Orion Engineered Carbons Gmbh | Process for controlling the porosity of carbon blacks |
US11639444B2 (en) | 2015-11-21 | 2023-05-02 | Suncoal Industries Gmbh | Hydrothermal treatment of renewable raw material |
Also Published As
Publication number | Publication date |
---|---|
CA2342928C (en) | 2008-05-06 |
BR9914483A (en) | 2001-10-30 |
BR9914483B1 (en) | 2009-05-05 |
CZ301448B6 (en) | 2010-03-03 |
CZ2001642A3 (en) | 2001-06-13 |
KR100583551B1 (en) | 2006-05-26 |
EG22239A (en) | 2002-11-30 |
SK2522001A3 (en) | 2002-03-05 |
ATE225832T1 (en) | 2002-10-15 |
CN1317037A (en) | 2001-10-10 |
HUP0103961A2 (en) | 2002-02-28 |
JP2002524602A (en) | 2002-08-06 |
ID29878A (en) | 2001-10-18 |
AU5742799A (en) | 2000-03-27 |
JP4452407B2 (en) | 2010-04-21 |
ZA200100808B (en) | 2002-05-07 |
PL198902B1 (en) | 2008-07-31 |
PT1109866E (en) | 2003-02-28 |
KR20010079746A (en) | 2001-08-22 |
EP1109866B1 (en) | 2002-10-09 |
HUP0103961A3 (en) | 2003-05-28 |
ES2185398T3 (en) | 2003-04-16 |
WO2000014162A1 (en) | 2000-03-16 |
EP1109866A1 (en) | 2001-06-27 |
TR200100599T2 (en) | 2001-07-23 |
DE19840663A1 (en) | 2000-03-09 |
DE59903057D1 (en) | 2002-11-14 |
CN1210352C (en) | 2005-07-13 |
PL346421A1 (en) | 2002-02-11 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CA2342928A1 (en) | Carbon black, method for producing carbon black and use of the same | |
WO2002092680A3 (en) | Rubber composition for tyre crown ply reinforcement | |
CA2289105A1 (en) | Improved silica product for use in elastomers | |
KR950011329A (en) | Precipitated silica | |
DE69233426D1 (en) | Process for the preparation of conductive polymer compositions | |
RU2003105225A (en) | RUBBER COMPOSITION FOR REINFORCEMENT COMBINATION OF PNEUMATIC TIRE COMB | |
DE60019370D1 (en) | Semiconductive cable screens | |
CA2496922A1 (en) | Silanised, structurally modified, pyrogenically produced silica | |
WO2005113688A3 (en) | Carbonaceous material with broad aggregate size distribution and improved dispersibility | |
KR900001798A (en) | Carbon black to blend in tire tread rubber | |
WO1997035918A3 (en) | Rubber compositions | |
EP1233042B8 (en) | Carbon black, method for producing the same and use thereof | |
EP1616905A4 (en) | Rubber composition and tire using the same | |
ES2160472A1 (en) | Pneumatic tire for heavy duty use | |
ES2134129A1 (en) | Pneumatic tire for heavy load | |
JPS6470539A (en) | Pneumatic tire | |
KR950026935A (en) | Rubber compositions for tire treads for trucks and buses | |
KR910008091A (en) | Cavan black for tire tread rubber | |
EP0831124A4 (en) | Carbon black filled rubber compositions | |
KR950025064A (en) | Tire Tread Rubber Composition with Special Coupling Agent | |
JPS56157605A (en) | Radial tire for small-size truck | |
Hayashi et al. | Pore Size Distribution of Activated Carbons Prepared by Activation with Chemical Agents | |
KR960007030B1 (en) | Car tire | |
JPS644659A (en) | Carbon black having wide agglomerate distribution | |
JP2000000472A (en) | Production of liquid hydrocarbon fuel catalyst |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
EEER | Examination request | ||
MKLA | Lapsed |
Effective date: 20140828 |