CA2132222C - Liquid crystal device - Google Patents
Liquid crystal deviceInfo
- Publication number
- CA2132222C CA2132222C CA002132222A CA2132222A CA2132222C CA 2132222 C CA2132222 C CA 2132222C CA 002132222 A CA002132222 A CA 002132222A CA 2132222 A CA2132222 A CA 2132222A CA 2132222 C CA2132222 C CA 2132222C
- Authority
- CA
- Canada
- Prior art keywords
- group
- anhydride
- film
- liquid crystal
- bis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention provides a liquid crystal material disposed between said pair of substrates, wherein at least one of said substrates is provided with a film comprising a polyimide compound having in its polyimide main-chain structural unit at least one alkyl side chain containing an alkyl chain moiety having a length of 2 to 10 carbon atoms.
Description
21.~ 2 Liquid Crystal Device This application is a divisional of our copending Application Serial No. 2024445-3 filed on August 31, 1990 .
BACKGROUND OF THE INVENTION
Field of the Invention The present invention relates to a liquid crystal device, in particular, a ferroelectric liquid crystal device, used in a liquid crystal display device or a liquid crystal optical shutter. More particularly, the present invention is concerned with a liquid crystal device having achieved an improvement of display characteristics because of an improvement of the state of liquid crystal molecular alignment.
Related Background Art Clark and Lagerwall have proposed a display device of the type in which the refractive index anisotropy of ferroelectric liquid crystal molecules is utilized and transmitted light rays are controlled by its combination with a polarizer (see Japanese Patent Laid-Open Gazette No. 56-107216 and U.S. Patent No. 4,367,924). This ferroelectric liquid crystal commonly has a chiral smectic C phase (Sm*C) or H phase (Sm*H) of non-spiral structure in a specific temperature range, and, under such a state, has the properties of assuming either a first optically stable state or a second optically stable state in response to an electric field applied and 21.~
BACKGROUND OF THE INVENTION
Field of the Invention The present invention relates to a liquid crystal device, in particular, a ferroelectric liquid crystal device, used in a liquid crystal display device or a liquid crystal optical shutter. More particularly, the present invention is concerned with a liquid crystal device having achieved an improvement of display characteristics because of an improvement of the state of liquid crystal molecular alignment.
Related Background Art Clark and Lagerwall have proposed a display device of the type in which the refractive index anisotropy of ferroelectric liquid crystal molecules is utilized and transmitted light rays are controlled by its combination with a polarizer (see Japanese Patent Laid-Open Gazette No. 56-107216 and U.S. Patent No. 4,367,924). This ferroelectric liquid crystal commonly has a chiral smectic C phase (Sm*C) or H phase (Sm*H) of non-spiral structure in a specific temperature range, and, under such a state, has the properties of assuming either a first optically stable state or a second optically stable state in response to an electric field applied and 21.~
1 also maintaining that state when no electric field is applied, in other words, the bistable state (or two stable states). This ferroelectric liquid crystal also has a quick response to changes in electric fields, and is expected to be widely utilized as a display device of a high-speed and memory type. In particular, in view of its function, it is expected to be applicable as a display device with a large screen and high detail.
In order for an optical modulation device applying such a bistable liquid crystal to exhibit desired drive characteristics, a liquid crystal disposed between a pair of parallel substrates is required to be in the state of molecular orientation that the conversion between the above two stable states may effectively take place, independently of an applied state of electric field.
In the case of a liquid crystal device in which the double refraction of a liquid crystal is utilized, the transmittance under crossed nicols is expressed by:
I/Io = sin2 4~ sin2 ,~nd wherein Io incident light intensity, I: transmitted light intensity, 21.~ 2 1 ~: tilt angle ~n: refractive index anisotropy d: film thickness of a liquid crystal layer, A: wavelength of incident light.
Thus, the tilt angle ~ in the above non-spiral structure is present as an angle in the direction of an average molecular axis of a liquid crystal molecule twistingly oriented in the first and second states of alignment. According to the above expression, the transmittance reaches a maximum when the tilt angle is an angle of 22.5, and hence a tilt angle ~ in the non-spiral structure realizes the bistable state is required to be as near as possible to 22.5.
Incidentally, as a method of aligning ferroelectric liquid crystal, it is desirable to use a method by which a molecular layer formed of a plurality of molecules that form a smectic liquid crystal can be monoaxially aligned along its normal and yet the manufacturing process can be carried out by a simple aligning treatment.
The method as disclosed, for example, in U.S.
Patent No. 4,561,726 is known as a method of aligning a ferroelectric liquid crystal, in particular, a chiral smectic liquid crystal of non-spiral structure.
However, in instances in which alignment -methods hitherto used, in particular, alignment 21.~ 22 methods using a polyimide film having been subjected to rubbing are applied to the above bistable ferroelectric liquid crystal of non-spiral structure as reported by Clark and Lagerwall, there are the following problems.
Experiments made by the present inventors revealed that a tilt angle in a ferroelectric liquid crystal of non-spiral structure obtained by making alignment using the conventional polyimide film having been subjected to rubbing becomes smaller than a tilt angle in a ferroelectric liquid crystal of spiral structure. In particular, the tilt angle e in a ferroelectric liquid crystal of non-spiral structure obtained by making alignment using the conventional polyimide film having been subjected to rubbing was approximately 3 to 8 in general, and the transmittance at that time was approximately 3 to 5% at best.
Thus, according to Clark and Lagerwall, the tilt angle in a ferroelectric liquid crystal of non-spiral structure that realizes the bistable state should be the same angle as the tilt angle in a ferroelectric liquid crystal of spiral structure. In practice, however, the tilt angle e in the non-spiral -- 21.~
1 structure is smaller than the tilt angle e in the spiral structure. It was also revealed that the reason why the tilt angle ~ in the non-spiral structure is smaller than the tilt angle e in the spiral structure is ascribable to the twisted orientation of liquid crystal molecules in the non-spiral structure. More specifically, in the ferroelectric liquid crystal of non-spiral structure, liquid crystal molecules are twistingly oriented in a continuous form at a twist angle ~, which is twisted from an axis of a liquid crystal molecule adjacent to an upper substrate toward an axis of a liquid crystal molecule adjacent to a lower substrate (i.e., in the direction of twisted orientation), with respect to the lS normal of each substrate. This is the reason why the tilt angle ~ in the non-spiral structure becomes smaller than the tilt angle ~ in the spiral structure.
In the instance where a chiral smectic liquid crystal is aligned using a conventional polyimide O alignment film having been subjected to rubbing, the polyimide alignment film is present as an insulating layer between an electrode and a liquid crystal layer.
Hence, when a voltage with one polarity is applied so that the first optical stable state (for example, a state of the display in white) is switched to the-second optical stable state (for example, a state of 21.~ 2 the display in black), a reverse electric field V~v with the other polarity is produced in a ferroelectric liquid crystal layer after removal of the application of this voltage with one polarity, and this reverse electric field V~ has often caused an after-image at the time of display. The above phenomenon of producing a reverse electric field is elucidated in Yoshida Akio, "Switching Characteristics of SSFLC", A Collection of Drafts for Liquid Crystal Forum, p.142-143, October, 1987.
SUMMARY OF THE INVENTION
Accordingly, an object of the present invention is to provide a liquid crystal device that has solved the above problems, in particular, to provide a ferroelectric liquid crystal device that can produce a large tilt angle e in the non-spiral structure of a chiral smectic liquid crystal, enables display of an image with a high contrast, and can achieve display causing no after-image.
21.7~ %
_ 7 Accordingly, the present invention is characterized by a liquid crystal device comprising a pair of substrates and a liquid crystal material disposed between said pair of substrates, wherein at least one of said substrates is provided with a laminated film comprised of a film comprising a polyimide containing a structural unit represented by the following Formula (I) and a film comprising a polyimide containing a structural unit represented by the following Formula (II).
O
C C
/\ /\
-N R I N-R z - (I) C C
Il 11 O O
20 and - O O
Il 11 \ / \ / ¦ ( II ) Il 11 O O
In the above Formulas (I) and (II), R
21.~
_ - 8 -1 represents a benzene group, a diphenyl group, a naphthalene group, a diphenylmethane group, a diphenyl sulfide group, a diphenyl ether group, or a derivative group thereof on which at least one methyl group or ethyl group is substituted; R2 represents a benzene group, a diphenyl group, a naphthalene group, a benzene sulfide group, a diphenyl sulfone group, a diphenyl ether group, a phenoxyphenyl group, or a derivative group thereof on which at least one methyl group or ethyl group is substituted; R3 represents the same as defined for Rl, a derivative group thereof on which at least one trifluoromethane group is substituted, or a 2,2-bisphenylhexafluoropropane group or a derivative group thereof on which at least one trifluoromethane group is substituted; R4 and R5 may be the same or different, and each represent the same as defined for R2 or a derivative group thereof on which at least one trifluoromethane group is substituted, and 2,2-bisphenylhexafluoropropane group or a derivative thereof on which at least one trifluoromethane group is substituted.
BRIEF DESCRIPTION OF THE DRAWINGS
Fig. l is a cross-sectional illustration of a liquid crystal device according to the present invention.
2~ 2~2 _ g 1 Fig. 2 is a perspective illustration of a state of alignment of a chiral smectic liquid crystal of spiral structure, and Fig. 3 is perspective illustration of a state of alignment of a chiral smectic liquid crystal of non-spiral structure.
Fig. 4A is a cross-sectional illustration of a state of alignment of a chiral smectic liquid crystal aligned according to an aligning method of the present invention, Fig. 4B illustrates C-directors of its two stable states of uniform alignment, and Fig. 4C
illustrates C-directors of two stabel states of spray alignment.
Fig. SA is a plan to illustrate a tilt angle in the state of uniform alignment, and Fig. SB is a lS plan to illustrate a tilt angle ~ in the state of spray alignment.
Figs. 6A, 6B and 6C are cross-sectional illustrations of the distribution of electric charges in a ferroelectric liquid crystal, the direction of spontaneous polarization Ps, and the direction of a reverse electric field Vrev, respectively.
Fig. ~ is a plan to illustrate changes of the tilt angle ~ at the time of application of an electric field and after that time.
Fig. 8 illustrates optical response characteristics in an example of the prior art, and 21.~
1 Fig. 9 illustrates optical response characteristics in an example of the present invention.
Fig. 10 illustrates wave forms of a drive voltage used in Examples of the present invention.
5Fig. 11 illustrates a method of forming an aligning film of the present invention by the LB
process.
Figs. 12A and 12B each illustrates the constitution of a polyimide liquid crystal alignment film of the present invention.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
Fig. 1 diagramatically illustrates a ferroelectric liquid crystal cell according to the present invention.
The numerals lla and llb denote substrates (glass plates) covered with transparent electrodes 12a and 12b made of In2O3 or ITO (indium-tin oxide), respectively. Insulating films 13a and 13b (SiO2 films, TiO2 films, Ta2O5 films or the like) and alignment control films 14a and 14b formed using the polyimide of the present invention are laminated thereon, respectively. A liquid crystal 15 is disposed between the substrates lla and llb. The distance between the substrates lla and llb is set to be a distance (for example, O.1 ~m to 3 ~m) small 21.~ 2 -1 enough to control the formation of a spiral structure in the case when the liquid crystal 15 is a ferroelectric smectic liquid crystal. In that case, the alignment of the liquid crystal 15 has a bistability. The above distance small enough is retained using a beads spacer 16 (e.g., silica beads, alumina beads) disposed between the substrates lla and llb.
The first embodiment of the present invention will be described below.
Polyimide films used in the present invention as the above alignment control films 14a and 14b can be obtained by forming a polyamide acid, synthesized by condensation reaction of a carboxylic anhydride with a diamine, into films by coating or the LB
process, followed by imidation.
An alkyl-substituted carboxylic anhydride and a diamine which are used in the present invention include, for example, the following:
~ Diamines -( 1 ) t~m (R~n H 2 N ~ X ~ NH 2X=O, S, CH 2 (2) (R)m (R)n (R)n (R)m H 2 N ~ O ~ Y ~ ~ NH 2 Y=C (CF 3) 2. CH 2 - 12 - 2~
l - Carboxylic anhydrides -(1) ' O O
Il 11 O~C/O
Il 11 (~)m (2) (R)m (R)n O O
Il 11 O/~C\O
O O
In order for an optical modulation device applying such a bistable liquid crystal to exhibit desired drive characteristics, a liquid crystal disposed between a pair of parallel substrates is required to be in the state of molecular orientation that the conversion between the above two stable states may effectively take place, independently of an applied state of electric field.
In the case of a liquid crystal device in which the double refraction of a liquid crystal is utilized, the transmittance under crossed nicols is expressed by:
I/Io = sin2 4~ sin2 ,~nd wherein Io incident light intensity, I: transmitted light intensity, 21.~ 2 1 ~: tilt angle ~n: refractive index anisotropy d: film thickness of a liquid crystal layer, A: wavelength of incident light.
Thus, the tilt angle ~ in the above non-spiral structure is present as an angle in the direction of an average molecular axis of a liquid crystal molecule twistingly oriented in the first and second states of alignment. According to the above expression, the transmittance reaches a maximum when the tilt angle is an angle of 22.5, and hence a tilt angle ~ in the non-spiral structure realizes the bistable state is required to be as near as possible to 22.5.
Incidentally, as a method of aligning ferroelectric liquid crystal, it is desirable to use a method by which a molecular layer formed of a plurality of molecules that form a smectic liquid crystal can be monoaxially aligned along its normal and yet the manufacturing process can be carried out by a simple aligning treatment.
The method as disclosed, for example, in U.S.
Patent No. 4,561,726 is known as a method of aligning a ferroelectric liquid crystal, in particular, a chiral smectic liquid crystal of non-spiral structure.
However, in instances in which alignment -methods hitherto used, in particular, alignment 21.~ 22 methods using a polyimide film having been subjected to rubbing are applied to the above bistable ferroelectric liquid crystal of non-spiral structure as reported by Clark and Lagerwall, there are the following problems.
Experiments made by the present inventors revealed that a tilt angle in a ferroelectric liquid crystal of non-spiral structure obtained by making alignment using the conventional polyimide film having been subjected to rubbing becomes smaller than a tilt angle in a ferroelectric liquid crystal of spiral structure. In particular, the tilt angle e in a ferroelectric liquid crystal of non-spiral structure obtained by making alignment using the conventional polyimide film having been subjected to rubbing was approximately 3 to 8 in general, and the transmittance at that time was approximately 3 to 5% at best.
Thus, according to Clark and Lagerwall, the tilt angle in a ferroelectric liquid crystal of non-spiral structure that realizes the bistable state should be the same angle as the tilt angle in a ferroelectric liquid crystal of spiral structure. In practice, however, the tilt angle e in the non-spiral -- 21.~
1 structure is smaller than the tilt angle e in the spiral structure. It was also revealed that the reason why the tilt angle ~ in the non-spiral structure is smaller than the tilt angle e in the spiral structure is ascribable to the twisted orientation of liquid crystal molecules in the non-spiral structure. More specifically, in the ferroelectric liquid crystal of non-spiral structure, liquid crystal molecules are twistingly oriented in a continuous form at a twist angle ~, which is twisted from an axis of a liquid crystal molecule adjacent to an upper substrate toward an axis of a liquid crystal molecule adjacent to a lower substrate (i.e., in the direction of twisted orientation), with respect to the lS normal of each substrate. This is the reason why the tilt angle ~ in the non-spiral structure becomes smaller than the tilt angle ~ in the spiral structure.
In the instance where a chiral smectic liquid crystal is aligned using a conventional polyimide O alignment film having been subjected to rubbing, the polyimide alignment film is present as an insulating layer between an electrode and a liquid crystal layer.
Hence, when a voltage with one polarity is applied so that the first optical stable state (for example, a state of the display in white) is switched to the-second optical stable state (for example, a state of 21.~ 2 the display in black), a reverse electric field V~v with the other polarity is produced in a ferroelectric liquid crystal layer after removal of the application of this voltage with one polarity, and this reverse electric field V~ has often caused an after-image at the time of display. The above phenomenon of producing a reverse electric field is elucidated in Yoshida Akio, "Switching Characteristics of SSFLC", A Collection of Drafts for Liquid Crystal Forum, p.142-143, October, 1987.
SUMMARY OF THE INVENTION
Accordingly, an object of the present invention is to provide a liquid crystal device that has solved the above problems, in particular, to provide a ferroelectric liquid crystal device that can produce a large tilt angle e in the non-spiral structure of a chiral smectic liquid crystal, enables display of an image with a high contrast, and can achieve display causing no after-image.
21.7~ %
_ 7 Accordingly, the present invention is characterized by a liquid crystal device comprising a pair of substrates and a liquid crystal material disposed between said pair of substrates, wherein at least one of said substrates is provided with a laminated film comprised of a film comprising a polyimide containing a structural unit represented by the following Formula (I) and a film comprising a polyimide containing a structural unit represented by the following Formula (II).
O
C C
/\ /\
-N R I N-R z - (I) C C
Il 11 O O
20 and - O O
Il 11 \ / \ / ¦ ( II ) Il 11 O O
In the above Formulas (I) and (II), R
21.~
_ - 8 -1 represents a benzene group, a diphenyl group, a naphthalene group, a diphenylmethane group, a diphenyl sulfide group, a diphenyl ether group, or a derivative group thereof on which at least one methyl group or ethyl group is substituted; R2 represents a benzene group, a diphenyl group, a naphthalene group, a benzene sulfide group, a diphenyl sulfone group, a diphenyl ether group, a phenoxyphenyl group, or a derivative group thereof on which at least one methyl group or ethyl group is substituted; R3 represents the same as defined for Rl, a derivative group thereof on which at least one trifluoromethane group is substituted, or a 2,2-bisphenylhexafluoropropane group or a derivative group thereof on which at least one trifluoromethane group is substituted; R4 and R5 may be the same or different, and each represent the same as defined for R2 or a derivative group thereof on which at least one trifluoromethane group is substituted, and 2,2-bisphenylhexafluoropropane group or a derivative thereof on which at least one trifluoromethane group is substituted.
BRIEF DESCRIPTION OF THE DRAWINGS
Fig. l is a cross-sectional illustration of a liquid crystal device according to the present invention.
2~ 2~2 _ g 1 Fig. 2 is a perspective illustration of a state of alignment of a chiral smectic liquid crystal of spiral structure, and Fig. 3 is perspective illustration of a state of alignment of a chiral smectic liquid crystal of non-spiral structure.
Fig. 4A is a cross-sectional illustration of a state of alignment of a chiral smectic liquid crystal aligned according to an aligning method of the present invention, Fig. 4B illustrates C-directors of its two stable states of uniform alignment, and Fig. 4C
illustrates C-directors of two stabel states of spray alignment.
Fig. SA is a plan to illustrate a tilt angle in the state of uniform alignment, and Fig. SB is a lS plan to illustrate a tilt angle ~ in the state of spray alignment.
Figs. 6A, 6B and 6C are cross-sectional illustrations of the distribution of electric charges in a ferroelectric liquid crystal, the direction of spontaneous polarization Ps, and the direction of a reverse electric field Vrev, respectively.
Fig. ~ is a plan to illustrate changes of the tilt angle ~ at the time of application of an electric field and after that time.
Fig. 8 illustrates optical response characteristics in an example of the prior art, and 21.~
1 Fig. 9 illustrates optical response characteristics in an example of the present invention.
Fig. 10 illustrates wave forms of a drive voltage used in Examples of the present invention.
5Fig. 11 illustrates a method of forming an aligning film of the present invention by the LB
process.
Figs. 12A and 12B each illustrates the constitution of a polyimide liquid crystal alignment film of the present invention.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
Fig. 1 diagramatically illustrates a ferroelectric liquid crystal cell according to the present invention.
The numerals lla and llb denote substrates (glass plates) covered with transparent electrodes 12a and 12b made of In2O3 or ITO (indium-tin oxide), respectively. Insulating films 13a and 13b (SiO2 films, TiO2 films, Ta2O5 films or the like) and alignment control films 14a and 14b formed using the polyimide of the present invention are laminated thereon, respectively. A liquid crystal 15 is disposed between the substrates lla and llb. The distance between the substrates lla and llb is set to be a distance (for example, O.1 ~m to 3 ~m) small 21.~ 2 -1 enough to control the formation of a spiral structure in the case when the liquid crystal 15 is a ferroelectric smectic liquid crystal. In that case, the alignment of the liquid crystal 15 has a bistability. The above distance small enough is retained using a beads spacer 16 (e.g., silica beads, alumina beads) disposed between the substrates lla and llb.
The first embodiment of the present invention will be described below.
Polyimide films used in the present invention as the above alignment control films 14a and 14b can be obtained by forming a polyamide acid, synthesized by condensation reaction of a carboxylic anhydride with a diamine, into films by coating or the LB
process, followed by imidation.
An alkyl-substituted carboxylic anhydride and a diamine which are used in the present invention include, for example, the following:
~ Diamines -( 1 ) t~m (R~n H 2 N ~ X ~ NH 2X=O, S, CH 2 (2) (R)m (R)n (R)n (R)m H 2 N ~ O ~ Y ~ ~ NH 2 Y=C (CF 3) 2. CH 2 - 12 - 2~
l - Carboxylic anhydrides -(1) ' O O
Il 11 O~C/O
Il 11 (~)m (2) (R)m (R)n O O
Il 11 O/~C\O
O O
(3) O O
Il 11 ~C/O
(R)m In the foregoing, m and n each represent an integer of 0 to 3; R is selected from the group consisting of:
normal-CQH2Q+1-, Q = an integer of 2 to 10;
normal-CQH2Q+1CO-, Q = an integer of 2 to 10;
nrmal-CQH2Q+1-~ Q = an integer of 2 to 10;
normal CF3(C~2)k(CH2)Q ' Q+k = an integer of 2 to 10 and k =
2, 3 or 5;
normal CF3(~F2)k(CH2)Q
Q+k = an integer of 2 to 10 and k =
2, 3 or 5;
2~.~?22;~
l (CF3)2CF(CH2)Q-, Q = an integer of 0, 1 to 8; or (CF3)2CF(CH2)QCO-, Q = an integer of 0, 1 to 8. And R can be combined with different two or more kinds of the group above.
In the present invention, it is possible to use two or more kinds of the above R-substituted diamine and/or two or more kinds of the carboxylic acid anhydride. Alternatively, it is also possible to use a polyamide acid synthesised by condensation reaction of the above R-substituted diamine or carboxylic anhydride with a conventionally known carboxylic anhydride or unsubstituted diamine. These can be used in the form of a copolymer comprised of various combinations.
The polyimide film used in the present invention can be provide on a substrate in the following method: First, the polyamide acid, which is a precursor of a polyimide, and a long-chain alkylamine are mixed in a solvent such as dimehtylformamide, dimethylacetamide, dimethyl sulfoxide or N-methylpyrrolidone, in a molar ratio of 1:2 to form a 0.1 to 1.0 mM solution (monomer units).
The resulting solution is spread on an interface between air and water, and a film is built up on the substrate by a conventionally known LB process.
Zl.~
1 Thereafter, the built-up film is heated to a temperature of from 100 to 350C, and preferably from 200 to 300C, to effect dehydration, cyclization and removal of amines. A polyimide film can be thus formed. This LB polyimide film can obtain uniform monoaxial aligning properties without rubbing treatment, and thus the LB process is suitable as a method of forming an alignment film.
For the purpose of achieving the object of the present invention, the film formation method is by no means limited to the above LB process. A film formed by conventionally known spin coating, spray coating or roll coating, which is then subjected to rubbing treatment using a cloth or the like, can also exhibit a superior performance as an alignment film. The rubbing may preferably be carried out in the direction A as shown in Fig. 1 so as to be in the same directions for the upper and lower substrates.
The polyimide film used in the first embodiment of the present invention may be formed to have a film thickness of from about 10 A to about 1 ~um, preferably from 30 A to 2,000 A, and more preferably from 30 A to 300 A.
Use of the insulating films 13a and 13b shown in Fig. 1 may be omitted. In the present invention, in the case when the polyimide films are provided on 21.~?,2 _ - 15 -l the insulating films 13a and 13b (each preferably having a film thickness of from 200 A to 1,000 A), such polyimide aligning films may be formed to each have a film thickness of not more than 200 A, and preferably not more than 100 A.
As the second embodiment of the present invention, the above alignment control films 14a and 14b may each be formed of a laminated film comprised of films comprising a polyimide containing a structural unit represented by the above Formula (I) and a polyimide containing a structural unit represented by the above Formula (II), respectively.
These polyimide films can be obtained by subjecting a polyamide acid synthesized by condensation reaction of a carboxylic anhydride with a diamine, to imidation.
In the case of the polyimide containing the structure of Formula (I), the carboxylic acid anhydride used in the present invention includes, for example, pyromellitic anhydride, 2,3,6,7-naphthalenetetracarboxylic anhydride, 3,3',4,4'-diphenyltetracarboxylic anhydride, 1,2,5,6-naphthalenetetracarboxylic anhydride, 2,2',3,3'-diphenyltetracarboxylic anhydride, thiophene-2,3,4,5-tetracarboxylic anhydride, 3,3',4,4'-diphenyl propanetetracarboxylic anhydride, 3,3',4,4'- -diphenylsulfonetetracarboxylic anhydride, 3,3',4,4'-i~ Z1.'2;;l,`2;~2 1 diphenylethertetracarboxylic anhydride, 3,3~,4,4'-diphenylsulfidetetracarboxylic anhydride,(hereinafter called "Group A"), and also includes derivatives of any of the compounds of Group A on which at least one methyl group or ethyl group is substituted .(hereinafter called "Group B"). In the case of the polyimide containing the structure of Formula (II), the carboxylic anhydride includes, in addition to those shown as Group A and Group B, 1,1,1,3,3,3-hexafluoro-2,2-bis(3,4-phenyldicarboxylic anhydride)propane, and derivatives of any of the compounds of Groups A and B or the above 1,1,1,3,3,3-hexafluoro-2,2-bis(3,4-phenyldicarboxylic anhydride)propane, on which at least one trifluoromethyl group is substituted.
As for the diamine also used in the present invention, it includes, for example, in the case of the polyimide containing the structure of Formula (I), m-phenylene diamine, p-phenylene diamine, m-xylene diamine, p-xylene diamine, 4,4'-diaminodiphenyl ether, 4,4'-diaminodiphenyl methane, 2,2'-bis(4-aminophenyl)propane, 4,4'-methylenedianiline, 4,4'-diaminodiphenyl sulfide, 4,4'-diaminodiphenylsulfonic acid, 1,5-diaminonaphthalene, and 3,3'-dimethylbenzidine (hereinafter called "Group C"), andalso includes derivatives of any of the compounds of 21.'~?,;'`;~;~
' 1 Group C on which at least one methyl group or ethyl group is substituted. In the case of the polyimide containing the structure of Formula (II), the diamine includes, for example, 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(3-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(2-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis(4-aminophenyl)hexafluoropropane, 2,2-bis[4-(4-aminophenyl sulfide)phenyl]hexafluoropropane, 2,2-bis[4-(4-aminobenzyl)phenyl]hexafluoropropane, 2,2-bis[4-(4-aminophenylsulfonic acid)phenyl]
hexafluoropropane, and 2,2-bis(5-aminonaphthyl) hexafluoropropane (hereinafter called "Group D"), and also includes derivatives of any of the compounds of Group D on which at least one methyl group, ethyl group and/or trifluoromethyl group is or are substituted. Since the polyimide used in the present invention may only partially contain the above structural unit in its polymer main chain, it is also possible to utilize a copolymer polyimide comprised of two or more kinds of carboxylic anhydrides and/or two or more kinds of diamines.
A method of building up on a substrate the polyimide alignment layer used in the second embodiment of the present invention will be described below. The polyimide alignment layer of the present 21.~ 2 1 invention can be formed by laminating the polyimide film contaihing the structure represented by Formula (I) (hereinafter called"polyimide film A") and the polyimide film containing the structure represented by Formula (II) (hereinafter called "polyimide film B") as previously described. Fig. 12 illustrates its constitution. Such alignment layer constitution can be roughly grouped into an instance in which a polyimide film B 101 is provided on a polyimide film A
(Fig. 12A) and an instance in which these are alternately laminated (Fig. 12B). In the alignment film of the present invention, at least an outermost polyimide layer is required to be formed by the Langmuir-Brodgett process (herein after called "LB
process"). In respect of a lower polyimide layer than the outermost layer, it may be formed either by coating methods hitherto widely used or by the LB
process. More specifically, in the case when an alignment film having the constitution as shown in Fig. 12A is prepared, the following instances are possible: (i) an instance in which the polyimide film A is formed by coating and the polyimide film B is formed by the LB process, (ii) an instance in which the polyimide film A and part of the polyimide film B
(on the side contiguous to the polyimide film A) are formed by coating, and only its upper, outermost 21.~2;~
1 polyimide film B is formed by the LB process, and (iii) all polyimide films are formed by the LB
process. In the case when aligning films are formed to have the constitution as shown in Fig. 12B, it is preferred to form all the polyimide layers by the LB
process. The LB process is a process of making a monomolecular film or a built-up film thereof by utilizing the mechanism that when the hydrophilic part and hydrophobic part are appropriately balanced (i,e, amphiphatic balance) in a structure having the both parts in the molecule, the molecule forms a monomolecular layer on a water surface with its hydrophilic group downward, where the monomolecular layer thus formed is transferred to a substrate.
lS Hence, using such an LB process, an organic ultra-thin film having a film thickness controlled in a molecule length order can be provided in a uniform, homogeneous and stable state over a large area.
In order to form the polyimide alignment film of the present invention by the use of the above LB
process, a precursor polyamide acid is spread over a water surface. At this time, the hydrophobic part and hydrophilic part must be introduced into the molecule as described above. This can be achieved by mixing a long-chain alkylamine to form an amine salt on a -carboxyl group of the polyamide acid. More 21.~22;~2 1 specifically, quaternizing the nitrogen of a long-chain alkylamine brings about the introduction of the hydrophilic part, and a long-chain alkyl moiety is attributable to the introduction of the hydrophobic part. The long-chain alkyl amine that can be used includes primary amines such as n-hexadecylamine, n-octadecylamine and n-docosylamine, secondary amines such as di-n-decylamine, di-n-dodecylamine and di-n-tetradecylamine, and tertiary amines such as N,N-dimethyl-n-hexadecylamine, N,N-dimethyl-n-octadecylamine, N-methyl-di-n-decylamine, N-methyl-di-n-dodecylamine, N-methyl-di-n-tetradecylamine, tri-n-nonylamine, tri-n-decylamine and tri-n-dodecylamine.
These may be mixed in such a ratio that may form all lS carboxyl groups of the polyamide acid into amine salts. More specifically, there are usually two carboxyl groups per repeating unit of a polyamide acid, and in such an instance the molar ratio of repeating units of the polyamide acid to an amine may preferably be 1:2 to 1:3, and more preferably from 1:2 to 1:2.5. As a solvent used here, N,N-dimethylacetamide is preferred, but any solvents may be used so long as they can well dissolve the polyamide acid and make the resulting solution to be readily spread over a water surface. There are no particular limitations on the concentration of the ~ 21 - 21.~22~,2 l polyamide acid. From the viewpoint of spreadability, it may preferably be in a concentration ranging from 1 x 10 to 1 x 10 M for the repeating unit of a polyimide acid. A polyamide acid amine salt solution prepared in this way is gently spread over an aqueous phase. Here, pure water of 5 to 20C is commonly used as the aqueous phase. Its pH may be adjusted by adding every sort of metal ions or adding an alkali.
Next, the polyamide acid amine salt thus spread over the water surface is compressed to form a monomolecular film of the polyamide acid amine salt.
The surface pressure for this compression depends on the types of the polyamide or acid amine salt used.
It may be approximately in the range of from 5 to 35 mN/m. To the monomolecular film on the water surface, thus prepared, the liquid crystal cell substrate previously described may be immersed and then drawn up in the direction crossing the monomolecular film on the water surface while the surface pressure is kept constant, so that two layers of monomolecular films can be built up on the substrate. The rate at which the substrate is immersed and drawn up here depends on the types of the polyamide acid amine salt. It may be approximately from 3 to 50 mm/min. Such an operation may be repeated, whereby a built-up film of monomolecular films comprising the polyamide acid - 22 - 2~ ?~
1 amine salt can be obtained in the desired layers. In order to obtain the alternately laminated film as shown in Fig. 12B, the monomolecular film on the water surface is removed for each step of immersing and drawing-up when the formation of a film on the substrate is completed, and another monomolecular film may be formed afresh so that film formation can be further carried out. This operation may be repeated.
In order to obtain a single layer film, two methods can be used. One of them is a method in which a substrate is previously kept immersed in an aqueous phase, thereafter a monomolecular film is formed on a water surface, and this monomolecular film is transferred to the substrate through a drawing-up step. The other of them is a method in which a monomolecular film is formed on the water surface, then a substrate is immersed in it so that the monomolecular film is transferred to the substrate, thereafter the monomolecular film on the water surface is removed, and the substrate on which a single layer film has been formed is drawn up. From the viewpoint of the stability of the film transferred to the substrate, it is desirable to use the former method.
The monomolecular film or a built-up film of monomolecular films comprising the polyamide acid-amine salt, formed on the substrate in this way, may _ - 23 -1 be heated to carry out a dehydration and cyclization (imidization) reaction and an deamination reaction.
The desired polyimide film can be thus obtained.
Baking, carried out here, should preferably be carried out at 150C to 300C 10 to 60 minutes in approximation, and in a nitrogen atmosphere or under reduced pressure. In either constitution of Figs. 12A
and 12B, the polyamide film formed by the LB process may preferably be formed in a layer number within the range of from 1 to 10, and in a film thickness of from 8 to 400 A in total (each layer has a film thickness of approximately from 4 to 80 A, though depending on the type of the polyimide). In regard to the direction in which the substrate is drawn up, the films should preferably be so formed as to be in the same direction (for example, the direction A shown in Fig. 1) between the upper and lower substrates when a cell has been made up.
As previously described, in the lower layer of the polyimide monomolecular film or the built-up film of polyimide monomolecular films, coating methods hitherto widely used may be used to form a polyimide film. In order to provide such a polyimide film on the substrate, a polyamide acid, which is a precursor of the polyimide, may be dissolved in a solvent such as N,N-dimethylformamide, N,N-dimethylacetamide, - 24 - Zl-~,2~2 1 N,N-dimethyl sulfoxide or N-methylpyrrolidone to form a 0.01 to 40 wt.% solution, and the resulting solution may be coated on a substrate by spin coating, spray coating or roll coating, followed by heating at a temperature of from 100 to 350C, and preferably from 200 to 300C, to carry out dehydration and cyclization(imidation). The desired polyimide film can be thus formed. The polyi`mide film formed by such coating methods may preferably have a film thickness of from about 30 A to about 2,000 A, and more preferably from 200 A to 1,000 A . Use of the insulating layers 13a and 13b as shown in Fig. 1 can be omitted.
Liquid crystal materials used in the present invention may preferably be liquid crystals that produce a chiral smectic phase through an isotropic phase, a cholesteric phase, and a smectic A phase in the temperature-decreasing process. Particularly preferred is a liquid crystal with a pitch of not less than 0.8 ,um when it is in a cholesteric phase (the pitch in a cholesteric phase is measured at the middle in the temperature range of the cholesteric phase).
Preferably usable as a specific liquid crystal is a liquid crystal composition containing the following liquid crystal materials "LC-1", "80B" and "80SI*" in the following percentage.
- 25 - 21~ 2 o CH 3 C8 H 17~C--(~)CH 2 CHC 2 H 5 C 2 H 5 CHCH 2~C--O~){)c 8 H
80SI *
C 8 H 17 ~C--O~H 2 CHC 2 H 5 Liquid crystal Composition ( 1 ) ( C ) go/ ( ) 10 (2) (LC-l)80/(8B)20 (3) (LC-1)70/(80B)30 (4) (LC-1)60/(80B)40 (5) 80SI*
(In the table, the subscript numerals are each expressed in weight ratio.) Fig. 2 is a diagramatical drawing of an example of a cell, to illustrate the operation of a ferroelectric liquid crystal. The numerals 21a and 2lb each denotes a substrate (a glass plate) covered 21.~ 2~, 1 with a transparent electrode comprised of a thin film made of In2O2, SnO2, ITO or the like. Between the substrates, a liquid crystal of an SmC* (chiral smectic C) phase or an SmH* (chiral smectic H) phase is sealed, which is so aligned that its liquid crystal molecular layer 22 may be perpendicular to the glass surfaces. A line 23 shown by a thick line indicates a liquid crystal molecule. This liquid crystal molecule 23 has a dipole moment (Pl) 24 in the direction falling at right angles with its molecule. When a voltage higher than a given threshold value is applied between the electrodes provided on the substrates 21a and 21b, the spiral structure of the liquid crystal molecule 23 comes loose, and thus the liquid crystal molecule 23 can change its direction of alignment so that all of dipole moments (Pl) 24 face toward the direction of the electric field. The liquid crystal molecule 23 has a slender shape, and shows refractive index anisotropy between its direction of the longitudinal axis and direction of the lateral axis.
Hence, it can be easily understood that if, for example, polarizers which are in crossed nicols each other are placed on both sides of a glass surface, there can be provided a liquid crystal optical modulation device capable of changing optical characteristics depending on the polarity of the Z~ 222 1 applied voltage.
A surface stabilized ferroelectric liquid crystal cell in the state of bistable alignment, which is used in the liquid crystal device of the present invention, can be made to have a sufficiently small thickness, for example, of from 0.1 ~m to 3 ~m. As the thickness of a liquid crystal layer becomes smaller in this way, the spiral structure of a liquid crystal molecule comes loose even in the state where no electric field is applied, and turns to have a non-spiral structure, so that its dipole moment P or P' results in either an upward state (34a) or a downward state (34b), as shown in Fig. 3. When as shown in Fig. 3 an electric field Ea or Eb of a voltage higher than a given threshold value and having a different polarity is applied to such a cell through means of applying a voltage (31a) and (31b), the dipole moment changes its direction to an upward direction 34a or a downward direction 34b corresponding to the electric field vector of the electric field Ea or Eb, and, corresponding therewith, the liquid crystal molecule is aligned in the direction of either a first stable state 33a or a second stable state 33b.
The effects obtainable from this ferroelectric liquid crystal cell are firstly that the response speed is very high, and secondly that the alignment of '~ - 28 - Zl.~22~, l the liquid crystal molecule is bistable. The second effect will-be further described with reference to, for example, Fig. 3. When the electric field Ea is applied, the liquid crystal molecule is aligned in the first stable state 33a and this state is stable even when the electric field has been removed. On the other hand, when the electric field Eb of a reverse direction is applied, the liquid crystal molecule is aligned in the second stable state 33b to change their direction, and still remain in this state even when the electric field has been removed. The respective states of alignment are also maintained so long as the electric field Ea to be applied does not exceed a given threshold value.
Fig. 4A is a cross-sectional view to diagramatically explain the state of alignment of liquid crystal molecules as produced in the direction of alignment according to the present invention.
The numerals 61a and 61b shown in Fig. 4A
denote an upper substrate and a lower substrate, respectively. The numeral 60 denotes a molecular layer formed of liquid crystal molecules 62, and the liquid crystal molecules 62 are arranged with changes in their positions along the base 64 (circular) of a cone 63.
Fig. 4B illustrates C-directors in the state Zl.~?;~Z
1 of uniform alignment. U1 in Fig. 4B shows C-directors 81 which are in one state of stable alignment, and U2, C-directors 81 which are the other state of stable alignment. Each C-director 81 is a projection of a molecular longitudinal axis (molecular axis) on an imaginary face perpendicular to the normal of the molecular layer 60 shown in Fig. 4A.
On the other hand, the state of alignment as produced using a conventional rubbed polyamide film is illustrated by the C-directors in Fig. 4C. For the state of alignment as shown in Fig. 4C, the molecular axis is so largely twisted from the upper substrate 61a toward the lower substrate 61b that the tilt angle ~ is small.
Fig. 5A is a plan to show the tilt angle ~
when the C-directors 81 are in the state of Fig. 4B
(herein called "the state of uniform alignment"), and Fig. 5B is a plan to show the tilt angle ~ when the C-directors 81 are in the state of Fig. 4C (herein called "the state of spray alignment"). In Figs. 5A
and 5B, the numeral 50 denotes the axis of rubbing treatment applied to the above-described polyimide film of the present invention, or the direction in which a substrate is drawn up when the above-described polyimide film of the present invention is formed-by the LB process. The numeral 5la denotes an average - 30 - 21.~
1 molecular axis formed in the state of alignment U1;
51b, an average molecular axis formed in the state of alignment U2; 52a, an average molecular axis formed in the state of alignment S1; and 52b, an average molecular axis formed in the state of alignment S2.
The average molecular axes 5la and 5lb can be converted by applying a voltage of reverse polarity which exceeds a threshold voltage each other. The same may also takes place between the average molecular axes 52a and 52b.
Usefulness of the state of uniform alignment to the delay of optical response (after-image) caused by a reverse electric field Vrev will be explained below. When the capacity of an insulating layer lS (alignment control film) of a liquid crystal cell is represented by Ci, the capacity of a liquid crystal layer by CLc, and the spontaneous polarization of a liquid crystal by Ps, the Vrev that causes the after-image is represented by the following expression:
Vrev 2 Ps / (Ci + CLC) Figs. 6A to 6C are cross-sectional views to illustrate the distribution of electric charges in a ferroelectric liquid crystal, the direction of spontaneous polarization Ps, and the direction of a reverse electric field Vrev, respectively. Fig. 6A
shows the state of distribution of plus and minus 21.~
~~ - 31 -electric charges in a memory state before application of a pulse electric field. The spontaneous polarization Ps is in the direction from the plus electric charges to the minus electric charges. In Fig. 6B, immediately after removing the pulse electric field the spontaneous polarization Ps is in a reverse direction to the direction in the state shown in Fig. 6A (hence, the liquid crystal molecules are reversed from the one state of stable alignment to the other state of stable alignment).
Since, however, the state of distribution of plus and minus electric charges is the same as in the state shown in Fig. 6A, a reverse electric field Vrev is produced in the liquid crystal in the direction of the arrow. This reverse electric field Vrev disappears after a while as shown in Fig. 6C, and the state of distribution of plus and minus electric charges is changed.
Fig. 7 illustrates changes of optical response occurring in the state of spray alignment as produced using a conventional polyimide aligning film, which are converted to changes of the tilt angle e. As shown in Fig. 7, when a pulse electric field is applied, the molecular axis is overshot from the average molecular axis S(A) formed in the state of spray alignment to the average molecular axis U2 formed in the state of uniform alignment, which is in the vicinity of the maximum tilt angle e, along the 21.~ Z
1 direction of an arrow X1. Immediately after removal of the pulse electric field, the reverse electric field Vrev as shown in Fig. 6B acts, and the tilt angle ~ is decreased, along the direction of an arrow X2, to the average molecular axis S(B) formed in the state of spray alignment. Then, a state of stable alignment can be obtained in which, because of the action of attenuation of the reverse electric field Vrev as shown in Fig. 6C, the tilt angle ~ has been a little increased, along the direction of an arrow X3, to the average molecular axis S(C) formed in the state of spray alignment. Optical response obtained here is made clear in Fig. 8.
According to the present invention, employment of the aligning film of the present invention does not bring about such a state of alignment of a liquid crystal that the average molecular axes S(A), S(B) and S(C) are formed in the state of spray alignment as shown in Fig. 7, and hence makes it possible to align 0 a liquid crystal to form an average molecular axis that may give a tilt angle ~ approximate to the maximum tilt angle e. Here, in the second embodiment of the present invention, the lower layer polyimide film mainly containing the structure represented by Formula (I) (i.e., the polyimide film A shown in Fig.
12A and the alternately laminated films of the Zl.~?,~2 1 polyimide films A and B other than the outermost layer, shown in Fig. 12B) is formed for the purposes of assuring the monoaxialness concerning initial liquid crystal alignment and also eliminating the influence the irregularities or the like of substrate surfaces (in practice, the insulating layers 13a and 13b) may have on the state of alignment of a liquid crystal. Hence, depending on the state of the lower layer polyimide film, the polyimide film B shown in Fig. 12A can be a single layer monomolecular film.
Fig. 9 shows optical response obtained when the polyimide aligning film of the present invention is used. As is evident from Fig. 9, no delay of optical response caused by the after-image occurs and lS also a high contrast is produced in a memory state.
According to experiments made by the present inventors, employment of the aligning method using the particular polyimide alignment film as will be made clearer in the following Examples has achieved a state O of alignment that gives a high optical contrast between a light state and a dark state, in particular, gives a high contrast to unselected picture elements at the time of the multiplexing drive as disclosed in U.S. Patent No. 4,655,561, etc., and also brings about no delay in optical response at the time of switching (at the time of multiplexing drive), which may cause 21.~?,2;~2 _ - 34 -1 the after-image at the time of display.
The present invention will be described below by giving Examples.
Example l Two sheets of l.l mm thick glass plates each provided with a l,000 A thick IT0 film were prepared.
The respective glass substrates were left to stand in saturated vapor of hexamethyldisilazane (HMDS) to carry out hydrophobic treatment. Thereafter, on each substrate thus treated, a built-up film of polyimide monomolecular films built up in 2, 4, 6, 8, lO, 20, 30 or 40 layers was formed by the LB process to provide an aligning film without rubbing treatment.
The process of forming the built-up film of polyimide monomolecular films will be detailed below.
The polyamide acid represented by the formula (l) was dissolved in N,N-dimethylacetamide (in concentration of l x lO M in terms of the repeating unit polyamide acid), and thereafter the solution and a 2 x lO 3 M solution separately prepared by dissolving N,N-dimethyloctadecylamine in the same solvent were mixed in equimolar amounts (v/v). A
solution of the polyamide acid octadecylamine salt represented by the formula (2) was thus prepared.
21.~ 2 O O
C C NH ~O~ NH
HOC COH C 6 H g C 6 H g ~- O O
O O
C~C --NH ~O~ NH
O=C C--O C 6 H g C 6 H g 0 I ~3 11 (~3 (2) HN (CH 3 ) 2 HN (CH 3 ) 2 (CH 2 ) 17 CH 3 (CH 2 ) 17 CH 3 The resulting solution was spread over an aqueous phase 111 (Fig. 11) comprised of pure water of 20C in water temperature to form a monomolecular film on the water surface. After removal of the solvent, a float as the partition plate 113 was moved to reduce the spreading area until the surface pressure was raised up to 25 mN/m. While keeping constant the surface pressure, the above ITO glass substrate was gently immersed at a rate of 5 mm/min in the direction crossing the water surface, and thereafter subsequently gently drawn up at a rate of 3 mm/min, thus making a two-layer Y-type monomolecular built-up film. Such operations were repeated to form a Zl.~?,22Z
_ 1 monomolecular built-up film (LB film) having a given number of monomolecular layers and comprising the polyamide acid octadecyl salt. Next, such a substrate was heated in vacuo under conditions of a rate of temperature rise of 20C/min and 300C constant-temperature heating for 10 minutes to carry out imidization. The desired aligning films were thus obtained.
Thereafter, alumina beads with an average particle diameter of 1.5 ~m were sprayed on one of the glass substrates. Then, the two sheets of glass substrates were put together in such a way that the axes of dipping directions (directions on the upper and lower substrates) of the respective aligning films were in parallel and in the same treatment directions each other. A cell was thus fabricated.
Into the resulting cell, a ferroelectric smectic liquid crystal "CS-1014" (trade name; a product of Chisso Corporation) was vacuum-injected in the state of an isotropic phase, and then annealed to 30C at a rate of 0.5C/hr from the state of the isotropic phase. Thus, it was possible to align the liquid crystal. In the cell of the present Example in which this "CS-1014" was used, the phase changes were 25 as follows: --- 21.~?,~;2 l 80.5C 69.1C 50C
Iso ) Ch ) SmA ) SmC*
(Iso: isotropic phase, Ch: cholesteric phase, SmA:
smectic A phase, SmC*: chiral smectic C phase) The liquid crystal cell provided with the aligning films each comprising the 10-layer LB film prepared as described above was inserted between a pair of 90 crossed nicols polarizers. Thereafter, a 30 V pulse for 50 ~sec was applied thereto and then the 90 crossed nicols were set to the position of extinction (a darkest state). Transmittance at this time was measured using a photomultiplier.
Subsequently, a -30 V pulse for 50 ~sec was applied, and transmittance at this time (a bright state) was measured in the same manner. As a result, it was revealed that the tilt angle ~ was 16, the transmittance in the darkest state was 0.9 %, the transmittance in the bright state was 50 %, and hence the ratio of contrast was 55:1.
The delay in optical response that causes an after-image was 0.2 second or less.
Using this liquid crystal cell, display was carried out according to multiplexing drive in which the drive wave forms as shown in Fig. 10 were used.
As a result, a display with a high contrast and high grade was obtained. After an image was displayed by Zl.~ 2 l inputting given characters, the whole screen was turned off to a white state to confirm that no after-image was seen to have occurred. The letter symbols SN, SN+1 and SN+2 in Fig. 10 represent wave forms of the voltages applied to scanning lines. The letter symbol I represents a wave form of the voltage applied to a typical information line. I-SN is a synthetic wave form of the voltage applied to the crossing area of the information line I and the scanning line SN.
In the present Example, experiments were made under conditions of V0 = 5 V to 8 V and ~T = 20 ~sec to 70 ~usec. Results of experiments on dependence to the number of LB film layers are shown in Table 1.
Table 1 Number of Delay in LB film layers Ratio of contrast optical response 2 42:1 0.2 sec or less 4 43:1 0.2 sec or less 6 53:1 0.2 sec or less 8 55:1 0.2 sec or less 55:1 0.2 sec or less 51:1 0.2 sec 51:1 0.3 sec 51:1 0.4 sec 21.~;~;22;~
1 Regardeless of the number of the LB film layers, it was possible to obtain alignment films with superior switching characteristics compared with conventional aligning films.
Example 2 Two sheets of 1.1 mm thick glass plates each provided with a 1,000 A thick IT0 film were prepared in the same manner as in Example 1. The respective glass substrates were coated with a solution of 3.0 %
by weight of the polyamide acid represented by Formula (1) as used in Example 1, dissolved in a 5/1 mixed solvent of N-methylpyrrolidone/n-butyl cellosolve, for 30 minutes using a spin coater of 3,000 rpm. After films were formed, each film was heated and baked at 300C for about 1 hour. The film hereby formed had a thickness of 250 A. The resulting coating film was subjected to rubbing in one direction using a nylon cloth. Thereafter, in the same manner as in Example 1, a cell was fabricated and the ratio of contrast and the delay in optical response were measured to reveal that excellent device characteristics were obtainable like the case when films were prepared by the LB
process.
Ratio of contrast: 50:1 Delay in optical response: 0.4 sec.
Display was also carried out according to ~_ - 40 - Zl.~
1 multiplexing drive in the same manner as in Example 1 to obtain the same results as in Example 1 in respect of contrast and after-image.
Examples 3 to 10 Cells were obtained in the same manner as in Example 1 except that the alignment control films (alignment films) and liquid crystal materials as shown in Table 2 were used. The respective cells were tested in the same manner as in Example 1. Results obtained in respect of the ratio of contrast and the delay in optical response are shown in Table 3.
Display was also carried out according to multiplexing drive in the same manner as in Example 1 to obtain the same results as in Example 1 in respect of contrast and after-image.
-- - 41 - 21~ 2 0 ~
o ~_, C) o 00 .~ ~ -o q~
o a~~ J Q. O
Ji C) I ~D 0 ~ O O
O ~
~r ~, ~ o --o ~ ~ 0 ' I
J
0=1~o=0 0=~ o=o O=I~U=O
=C~ o=O o=C~ Vo~= O=V o=O
E
~ -o Z
21~
~ J ~ o a) u ~ o ~.
0 ~ o o 0 o ~ ~ ,,, ~s o o a, :~ ~D O ~ a, . . o 0 ~n ~ ~ .c ~
O a I ~ ~
~V ~C) ~ ~ X
0 [~ ~ ~--V--C) ~ V
a) ~~
~ ~ c ~ a~
~ 0 1 X O ~ O <n ~ O C~ = O
E ~ O=C) ~) O=C~ C~ O
0=0 o=O ~ ~
O=~) o=O
~ O=(~ o=
_ O
Z d' ~ ~D
21.~ 222 as ~ ~
o o o a5 O ~ V
~ o -I ~ rY rY ~
a) ~ o g o o S , ~
o--I
o ,.
_~ Y ~ ~
o a) q~ 0 _, ,~ ._, r O (~
I
X
1 ~
~a) ~ ~ O ~
C O I ~
<~ ~ I ~ X
o ~} O=C.) (,~=0 O ~ N
Q' ~ ~
O = C~) C.) = O ~ O
C o=(~ o=O o=~O=O
Z r~ ~
21.~?;~
1 Table 3 Alignment Number of Exam- film LB film Ratio of Delay in ple No.* layers contrast optical response 3 1 8 55:1 0.2 sec or less 4 2 8 40:1 0.8 sec 3 8 52:1 0.2 sec or less 6 4 8 50:1 0.2 sec or less 7 5 8 58:1 0.2 sec or less 8 6 8 58:1 0.2 sec or less 9 7 8 53:1 0.2 sec or less 8 8 50:1 0.2 sec or less * No. in Table 2 Examples 11 to 15 Cells were obtained in the same manner as in Example 2 except that the alignment control films (alignment films) and liquid crystal materials as shown in Table 2 were used. The respective cells were tested in the same manner as in Example 1. Results obtained in respect of the ratio of contrast and the delay in optical response are shown in Table 4.
Display was also carried out according to multiplexing drive in the same manner as in Example 1 21.'2~22 _ 1 to obtain the same results as in Example 1 in respect of contrast and after-image.
Table 4 Alignment Number of Exam- film LB film Ratio of Delay in ple No.*layers contrast optical response 11 3 200 50:1 0.4 sec 12 4 190 47:1 0.4 sec 13 5 200 53:1 0.4 sec 14 7 220 49:1 0.4 sec 8 210 44:1 0.4 sec * No. in Table 2 Comparative Examples 1 to 4 Cells were fabricated in the same manner as in Example 2 except that the alignment control films (alignment films) and liquid crystal materials as shown in Table 5 were used. The respective cells were tested in the same manner as in Example 1. Results obtained in respect of the ratio of contrast and the delay in optical response are shown in Table 6.
Display was also carried out according to multiplexing drive in the same manner as in Exampie 1 2~ 2 1 to obtain the results that the contrast was lower than that of Examples of the present invention and also after-image occurred.
Table 5 Alignment film Llquld crystal (polyamide acid varnish) material Comparative Example:
1SP-710 (trade name)* CS1014***
2ditto ditto 3LQ-5200 (trade name)** CS1014***
4ditto ditto * An aromatic polyimide varnish, a product of Toray Industries, Inc.
** A polyimide varnish, a product of Hitachi Chemical Co., Ltd.
*** FLC, a product of Chisso Corporation 21.~
1 Table 6 Delay in Ratio of contrast optical response Comparative Example:
1 8:1 1.5 sec 2 7:1 2.5 sec 3 10:1 1.2 sec 4 8:1 2.2 sec In the above Examples, characteristics of liquid crystal devices prepared using the ferroelectric liquid crystal CS1014 were evaluated.
The liquid crystal materials used are by no means limited to ferroelectric liquid crystals. For example, nematic liquid crystals, cholesteric liquid crystals and smectic liquid crystals can also be used alone or in the form of a mixture. An example of a device in which a nematic liquid crystal is used is shown below.
Example 16 Substrates were prepared in the same manner as in Example 2. The substrates were put together in such a manner that the rubbing directions may cross at right angles, and peripheral edges thereof were sealed 21.~
1 using a heat-curable epoxy resin, except for an injection opening. The space between the substrates was 6 ~um.
Next, a nematic liquid crystal (ZLI-1285, a product of Merck AG., West Germany) was injected into the cell, and then the injection opening was sealed.
A pair of polarizers were disposed in parallel to the rubbing direction of an adjacent substrate, and the liquid crystal was observed with a microscope to confirm that twisted alignment was achieved in a superior uniformity.
Using this liquid crystal device, a continuous operation test was carried out.
As a result, a good twisted alignment was retained even after drive for 30 days using an alternating current of 10 V at 50 Hz, and thus superior durability was confirmed.
Example 17 Two sheets of 1.1 mm thick glass plates each comprising a 1,500 A thick IT0 film provided thereon with a 600 A thick Ta205 film were prepared as substrates. The resulting substrates were subjected to ultrasonic cleaning using isopropyl alcohol and thereafter left to stand for 24 hours in saturated vapor of hexamethyldisilazane to carry out hydrophobic treatment. Subsequently, on each substrate thus 21.~
1 treated, a polyimide aligning film was formed by the LB process, The process of forming the polyimide alignment film will be detailed below.
The polyamide acid represented by the formula (3) was dissolved in a solvent N,N'-dimethylacetamide (in concentration of 1 x 10 M in terms of the monomer), and thereafter the solution and a 1 x 10 3 M
solution separately prepared by dissolving di-n-decylamine in the same solvent were mixed in a ratio of 1:2 (v/v). A solution of the polyamide acid di-n-decylamine salt represented by the formula (4) was thus prepared.
- O O
C C -NH ~ O ~ NH
_ O (3) - O O
O- C -NH ~ O ~ (4) O O H 2 N [(CH 2 ) 9 CH 3 ] 2 n ~3 H 2 N [.(CH z) g CH 3 ] 2 The resulting solution was spread over an _ 50 2~.~2~2 1 aqueous phase comprised of pure water of 20C in water temperature to form a monomolecular film on the water surface. After removal of the solvent, the surface pressure was raised up to 20 mN/m. While keeping constant the surface pressure, the above substrate was gently immersed at a rate of 5 mm/min in the direction crossing the water surface, and thereafter subsequently gently drawn up at a rate of 5 mm/min, thus making a built-up film of two-layer Y-type monomolecular films. Such operations were repeated to form a built-up film of seven-layer monomolecular films comprising the polyamide acid di-n-decylamine salt of the formula (4). Here, the substrate was kept immersed in the water. While keeping such a state, the monomolecular film of the polyamide acid di-n-decylamine salt on the aqueous phase was once removed, and a monomolecular film of a fluorine-containing polyamide acid di-n-decylamine salt represented by the formula (5) was afresh formed on the aqueous phase.
This was carried out by the same method as described above.
O-- C C--NH ~ 0~ CF 3 o o (~3 -- H 2 N t(CH 2) 9 CH 3] 2 ~3 H2 N [(CH2) 9 CH 3] 2 (~ O ~ NH
O (5) The surface pressure was raised up to 15 mN/m.
lS Thereafter, while keeping constant the surface pressure, the above substrate kept immersed in water was gently drawn up at a rate of 5 mm/min in the direction crossing the water surface. A built-up film of a single-layer monomolecular film of the fluorine-containing polyamide acid di-n-decylamine salt ( 5 ) was thus formed on the built-up film of the seven-layer monomolecular films of the polyamide acid di-n-decylamine salt (4). Next, such a substrate was subjected to heat treatment at 300C for 20 minutes to carry out imidization (formulas (6) and (7)) of the respective polyamide acid salts.
1 (4) ~
- O O
Il 11 C C ~ ~
C C (6) O O
(5) --~_ - O O
lO - N ~ N ~ CF 3 ll ll CF 3 O O
- - (7) Polyimide alignment films each comprising a built-up film of polyamide monomolecular films of 8 layers in total were thus obtained. Thereafter, alumina beads with an average particle diameter of l.S ~m were sprayed on one of the substrates. Then, the two sheets of substrates were put together in such a way that the drawing-up directions of the respective substrates were in parallel and in the same directions each other. A liquid crystal cell was thus fabricated.
Into the resulting cell, a ferroelectric smectic liquid crystal "CS-1014" (trade name; a product of Chisso Corporation) was vacuum-injected in Zl.~;~2;'`2 l the state of an isotropic phase, and then cooled slowly up to 30C at a rate of 0.5C/hr from the state of the isotropic phase to from an aligned state.
Thus, it was possible to align the liquid crystal. In the cell of the present Example in which this "CS-1014" was used, the phase changes were as follows:
80.5C 69.1C 50C
Iso > Ch ) SmA ) SmC*
(Iso: isotropic phase, Ch: cholesteric pahse, SmA:
smectic A phase, SmC*: chiral smectic C phase) The above liquid crystal cell was inserted between a pair of 90 crossed nicols polarizers.
Thereafter, a 30 V pulse for 50 ,usec was applied thereto and then the 90 crossed nicols were set to the position of extinction (a darkest state).
Transmittance at this time was measured using a photomultiplier. Subsequently, a -30 V pulse for 50 ,usec was applied, and transmittance at this time (a bright state) was measured in the same manner. As a 0 result, it was revealed that the tilt angle ~ was 15, the transmittance in the darkest state was 0.9 % and on the other hand the transmittance in the bright state was 45 %, and hence the ratio of contrast was 50:1. The delay in optical response that causes an after-image was 0.2 second or less.
Using this liquid crystal cell, display was _ 54 _ 21~
1 carried out according to multiplexing drive in which the drive wave forms as shown in Fig. 10 were used.
As a result, a display with a high contrast and high grade was obtained. After an image was displayed by inputting given characters, the whole screen was turned off to a white state to confirm that no after-image was seen to have occurred. The letter symbols SN, SN+1 and SN+2 in Fig. 10 represent wave forms of the voltages applied to scanning lines. The letter symbol I represents a wave form of the voltage applied to a typical information line. I-SN is a synthetic wave form of the voltage applied to the crossing area of the information line I and the scanning line SN.
In the present Example, experiments were made under conditions of V0 = 5 V to 8 V and AT = 20 ~sec to 70 ~sec.
Example 18 A liquid crystal cell was prepared in entirely the same manner as in Example 17, except that as the method of forming the polyimide film A (Fig. 12A) the LB process was replaced with coating. Different points are described below.
The substrates were coated with a solution of 3.0 % by weight of the polyamide acid (3) dissolved in a 5/1 mixed solvent of N-methylpyrrolidone/n-butyl cellosolve., for 10 minutes using a spin coater of .2Z
1 3,000 rpm. After films were formed, each film was heated and baked at 270C for about 1 hour to carry out imidization. A polyimide film A of 200 A thick comprising the polyimide (6) was thus formed. On the resulting substrate, 6 layers of monomolecular films of the fluorine-containing polyamide acid di-n-decylamine salt (5) were built up by the LB process in the same manner as in Example 17. Thereafter, the resulting substrate was subjected to heat treatment at 300C for 20 minutes to form a polyimide film B
comprising a built-up film of monomolecular films (6 layers). Thereafter, in the same manner as in Example 17, a cell was fabricated and the ratio of contrast and the delay in optical response were measured to reveal that former was 50:1 or more and the latter was 0.7 seconds or less. Display was also carried out according to multiplexing drive in the same manner as in Example 17 to obtain the same results as in Example 17 in respect of contrast and after-image.
Examples 19 to 22 Liquid crystal cells were obtained in the same manner as in Example 17 except that the alignment films having the aligning film constitution and polyimide structure as shown in Table 7 were used.
Test results on the ratio of contrast and the delay in optical response are shown in Table 8. Display was Zl.~;222 1 also carried out according to multiplexing drive in the same manner as in Example 17 to obtain the same results as in Example 17 in respect of contrast and after-image.
Comparative Examples 5 to 7 Liquid crystal cells were fabricated in the same manner as in Example 17 except that the alignment control films (aligning films) as shown in Table 9 were used. Test results on the ratio of contrast and the delay in optical response are shown in the same Table 9. Display was also carried out according to multiplexing drive in the same manner as in Example 17 to obtain the results that the contrast was lower than that of Examples of the present invention and also after-image occurred.
;~1 .~æ
~ o, _ ~ n ~ ~
~s a ~ ~ v a o ~ s . .
o o ~ ~ o o S --I ~ o ~ ~s o ~ o ~ m ~
O O
~o [~
~ --V
r~ ~ O ~ ~
Q ~ ~
0 ~ ~ G
~ ~ ,~ .
.. .. :Z
m / \ / \
0=~) o=o O=C~)=O
~ ~ / \ ~
~ ~ O=C) C>=O
--~ 7 O=C~ =0 /
a C:
.,, ~ ~ o o ~ ,~
p., ,¢ ~ ~) ~ rL, I I ~
X ~ ~ cn Z~ 2 h X X ~
a) ~ ~ ,. ..
'{S 0 --I . 0 d5 ~ h 0 q ~
'~ ~ 0 .t ~ 0 0 ~ ~
o~ O
_I _I ~ o6 o~ ~ o~ ~J
O ~ S o~ o o~¢ o~
~, ~, ~ ~ O O ~O
. . . ..
O O O
~ O O ~ O O O
I ~D ~1 0 ~ ~
o ~ oq~ m m om mm -cn ~ X
~--v ~ o 0 ~
z ~ ~ 0~
15 Q ~ O=~) ()=O
0 1:) \ / / \ O ~:: O O
E~ ~ _ / \ ~ E~
oq .. C ~ 0=~ =O
m m rl / O=~ =O ~ ~ ~ ~
=C-) ~)= ~ \ / a) o a) o o ~ \ /
~ ~ O ~ ~ ~ ~
O -- -- ~ O O O O
CL ~ ~ lL
~ c ~ ~: m JJ O
o ~ ~ o I I a X ~ ~ O ~ C~
Zl.~ 2 l Table 8 Exam- Delay in optical ple Ratio of contrast response (sec) 19 45:1 0.2 50:1 0.2 21 45:1 0.8 22 55:1 0.2 Table 9 Delay in PolyimideFilm form- Ratio of optical alignment film ing process contrast response, 15 Comparative (sec) Example:
5 SP-710*1Coating*3 8:1 1.5 6 LQ-5200*2 " 10:1 1.2 7 SP-510*LB process* 10:1 0.7 *1 (trade name; a product of Toray Industries, Inc.) *~: (trade name; a product of Hitachi Chemical Co.) * : 200 A thick, rubbing treatment *4: 32 A thick, 8 layers, no rubbing treatment - 60 - 21,~
1 As will be evident from the above Examples and Comparative Example, the present invention has the effect that it can achieve a high contrast between a bright state and a dark state, in particular, can achieve a very high display contrast in multiplexing drive to obtain a display of high quality level, and also may not cause the after-image phenomenon that is offensive to the eye.
Il 11 ~C/O
(R)m In the foregoing, m and n each represent an integer of 0 to 3; R is selected from the group consisting of:
normal-CQH2Q+1-, Q = an integer of 2 to 10;
normal-CQH2Q+1CO-, Q = an integer of 2 to 10;
nrmal-CQH2Q+1-~ Q = an integer of 2 to 10;
normal CF3(C~2)k(CH2)Q ' Q+k = an integer of 2 to 10 and k =
2, 3 or 5;
normal CF3(~F2)k(CH2)Q
Q+k = an integer of 2 to 10 and k =
2, 3 or 5;
2~.~?22;~
l (CF3)2CF(CH2)Q-, Q = an integer of 0, 1 to 8; or (CF3)2CF(CH2)QCO-, Q = an integer of 0, 1 to 8. And R can be combined with different two or more kinds of the group above.
In the present invention, it is possible to use two or more kinds of the above R-substituted diamine and/or two or more kinds of the carboxylic acid anhydride. Alternatively, it is also possible to use a polyamide acid synthesised by condensation reaction of the above R-substituted diamine or carboxylic anhydride with a conventionally known carboxylic anhydride or unsubstituted diamine. These can be used in the form of a copolymer comprised of various combinations.
The polyimide film used in the present invention can be provide on a substrate in the following method: First, the polyamide acid, which is a precursor of a polyimide, and a long-chain alkylamine are mixed in a solvent such as dimehtylformamide, dimethylacetamide, dimethyl sulfoxide or N-methylpyrrolidone, in a molar ratio of 1:2 to form a 0.1 to 1.0 mM solution (monomer units).
The resulting solution is spread on an interface between air and water, and a film is built up on the substrate by a conventionally known LB process.
Zl.~
1 Thereafter, the built-up film is heated to a temperature of from 100 to 350C, and preferably from 200 to 300C, to effect dehydration, cyclization and removal of amines. A polyimide film can be thus formed. This LB polyimide film can obtain uniform monoaxial aligning properties without rubbing treatment, and thus the LB process is suitable as a method of forming an alignment film.
For the purpose of achieving the object of the present invention, the film formation method is by no means limited to the above LB process. A film formed by conventionally known spin coating, spray coating or roll coating, which is then subjected to rubbing treatment using a cloth or the like, can also exhibit a superior performance as an alignment film. The rubbing may preferably be carried out in the direction A as shown in Fig. 1 so as to be in the same directions for the upper and lower substrates.
The polyimide film used in the first embodiment of the present invention may be formed to have a film thickness of from about 10 A to about 1 ~um, preferably from 30 A to 2,000 A, and more preferably from 30 A to 300 A.
Use of the insulating films 13a and 13b shown in Fig. 1 may be omitted. In the present invention, in the case when the polyimide films are provided on 21.~?,2 _ - 15 -l the insulating films 13a and 13b (each preferably having a film thickness of from 200 A to 1,000 A), such polyimide aligning films may be formed to each have a film thickness of not more than 200 A, and preferably not more than 100 A.
As the second embodiment of the present invention, the above alignment control films 14a and 14b may each be formed of a laminated film comprised of films comprising a polyimide containing a structural unit represented by the above Formula (I) and a polyimide containing a structural unit represented by the above Formula (II), respectively.
These polyimide films can be obtained by subjecting a polyamide acid synthesized by condensation reaction of a carboxylic anhydride with a diamine, to imidation.
In the case of the polyimide containing the structure of Formula (I), the carboxylic acid anhydride used in the present invention includes, for example, pyromellitic anhydride, 2,3,6,7-naphthalenetetracarboxylic anhydride, 3,3',4,4'-diphenyltetracarboxylic anhydride, 1,2,5,6-naphthalenetetracarboxylic anhydride, 2,2',3,3'-diphenyltetracarboxylic anhydride, thiophene-2,3,4,5-tetracarboxylic anhydride, 3,3',4,4'-diphenyl propanetetracarboxylic anhydride, 3,3',4,4'- -diphenylsulfonetetracarboxylic anhydride, 3,3',4,4'-i~ Z1.'2;;l,`2;~2 1 diphenylethertetracarboxylic anhydride, 3,3~,4,4'-diphenylsulfidetetracarboxylic anhydride,(hereinafter called "Group A"), and also includes derivatives of any of the compounds of Group A on which at least one methyl group or ethyl group is substituted .(hereinafter called "Group B"). In the case of the polyimide containing the structure of Formula (II), the carboxylic anhydride includes, in addition to those shown as Group A and Group B, 1,1,1,3,3,3-hexafluoro-2,2-bis(3,4-phenyldicarboxylic anhydride)propane, and derivatives of any of the compounds of Groups A and B or the above 1,1,1,3,3,3-hexafluoro-2,2-bis(3,4-phenyldicarboxylic anhydride)propane, on which at least one trifluoromethyl group is substituted.
As for the diamine also used in the present invention, it includes, for example, in the case of the polyimide containing the structure of Formula (I), m-phenylene diamine, p-phenylene diamine, m-xylene diamine, p-xylene diamine, 4,4'-diaminodiphenyl ether, 4,4'-diaminodiphenyl methane, 2,2'-bis(4-aminophenyl)propane, 4,4'-methylenedianiline, 4,4'-diaminodiphenyl sulfide, 4,4'-diaminodiphenylsulfonic acid, 1,5-diaminonaphthalene, and 3,3'-dimethylbenzidine (hereinafter called "Group C"), andalso includes derivatives of any of the compounds of 21.'~?,;'`;~;~
' 1 Group C on which at least one methyl group or ethyl group is substituted. In the case of the polyimide containing the structure of Formula (II), the diamine includes, for example, 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(3-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(2-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis(4-aminophenyl)hexafluoropropane, 2,2-bis[4-(4-aminophenyl sulfide)phenyl]hexafluoropropane, 2,2-bis[4-(4-aminobenzyl)phenyl]hexafluoropropane, 2,2-bis[4-(4-aminophenylsulfonic acid)phenyl]
hexafluoropropane, and 2,2-bis(5-aminonaphthyl) hexafluoropropane (hereinafter called "Group D"), and also includes derivatives of any of the compounds of Group D on which at least one methyl group, ethyl group and/or trifluoromethyl group is or are substituted. Since the polyimide used in the present invention may only partially contain the above structural unit in its polymer main chain, it is also possible to utilize a copolymer polyimide comprised of two or more kinds of carboxylic anhydrides and/or two or more kinds of diamines.
A method of building up on a substrate the polyimide alignment layer used in the second embodiment of the present invention will be described below. The polyimide alignment layer of the present 21.~ 2 1 invention can be formed by laminating the polyimide film contaihing the structure represented by Formula (I) (hereinafter called"polyimide film A") and the polyimide film containing the structure represented by Formula (II) (hereinafter called "polyimide film B") as previously described. Fig. 12 illustrates its constitution. Such alignment layer constitution can be roughly grouped into an instance in which a polyimide film B 101 is provided on a polyimide film A
(Fig. 12A) and an instance in which these are alternately laminated (Fig. 12B). In the alignment film of the present invention, at least an outermost polyimide layer is required to be formed by the Langmuir-Brodgett process (herein after called "LB
process"). In respect of a lower polyimide layer than the outermost layer, it may be formed either by coating methods hitherto widely used or by the LB
process. More specifically, in the case when an alignment film having the constitution as shown in Fig. 12A is prepared, the following instances are possible: (i) an instance in which the polyimide film A is formed by coating and the polyimide film B is formed by the LB process, (ii) an instance in which the polyimide film A and part of the polyimide film B
(on the side contiguous to the polyimide film A) are formed by coating, and only its upper, outermost 21.~2;~
1 polyimide film B is formed by the LB process, and (iii) all polyimide films are formed by the LB
process. In the case when aligning films are formed to have the constitution as shown in Fig. 12B, it is preferred to form all the polyimide layers by the LB
process. The LB process is a process of making a monomolecular film or a built-up film thereof by utilizing the mechanism that when the hydrophilic part and hydrophobic part are appropriately balanced (i,e, amphiphatic balance) in a structure having the both parts in the molecule, the molecule forms a monomolecular layer on a water surface with its hydrophilic group downward, where the monomolecular layer thus formed is transferred to a substrate.
lS Hence, using such an LB process, an organic ultra-thin film having a film thickness controlled in a molecule length order can be provided in a uniform, homogeneous and stable state over a large area.
In order to form the polyimide alignment film of the present invention by the use of the above LB
process, a precursor polyamide acid is spread over a water surface. At this time, the hydrophobic part and hydrophilic part must be introduced into the molecule as described above. This can be achieved by mixing a long-chain alkylamine to form an amine salt on a -carboxyl group of the polyamide acid. More 21.~22;~2 1 specifically, quaternizing the nitrogen of a long-chain alkylamine brings about the introduction of the hydrophilic part, and a long-chain alkyl moiety is attributable to the introduction of the hydrophobic part. The long-chain alkyl amine that can be used includes primary amines such as n-hexadecylamine, n-octadecylamine and n-docosylamine, secondary amines such as di-n-decylamine, di-n-dodecylamine and di-n-tetradecylamine, and tertiary amines such as N,N-dimethyl-n-hexadecylamine, N,N-dimethyl-n-octadecylamine, N-methyl-di-n-decylamine, N-methyl-di-n-dodecylamine, N-methyl-di-n-tetradecylamine, tri-n-nonylamine, tri-n-decylamine and tri-n-dodecylamine.
These may be mixed in such a ratio that may form all lS carboxyl groups of the polyamide acid into amine salts. More specifically, there are usually two carboxyl groups per repeating unit of a polyamide acid, and in such an instance the molar ratio of repeating units of the polyamide acid to an amine may preferably be 1:2 to 1:3, and more preferably from 1:2 to 1:2.5. As a solvent used here, N,N-dimethylacetamide is preferred, but any solvents may be used so long as they can well dissolve the polyamide acid and make the resulting solution to be readily spread over a water surface. There are no particular limitations on the concentration of the ~ 21 - 21.~22~,2 l polyamide acid. From the viewpoint of spreadability, it may preferably be in a concentration ranging from 1 x 10 to 1 x 10 M for the repeating unit of a polyimide acid. A polyamide acid amine salt solution prepared in this way is gently spread over an aqueous phase. Here, pure water of 5 to 20C is commonly used as the aqueous phase. Its pH may be adjusted by adding every sort of metal ions or adding an alkali.
Next, the polyamide acid amine salt thus spread over the water surface is compressed to form a monomolecular film of the polyamide acid amine salt.
The surface pressure for this compression depends on the types of the polyamide or acid amine salt used.
It may be approximately in the range of from 5 to 35 mN/m. To the monomolecular film on the water surface, thus prepared, the liquid crystal cell substrate previously described may be immersed and then drawn up in the direction crossing the monomolecular film on the water surface while the surface pressure is kept constant, so that two layers of monomolecular films can be built up on the substrate. The rate at which the substrate is immersed and drawn up here depends on the types of the polyamide acid amine salt. It may be approximately from 3 to 50 mm/min. Such an operation may be repeated, whereby a built-up film of monomolecular films comprising the polyamide acid - 22 - 2~ ?~
1 amine salt can be obtained in the desired layers. In order to obtain the alternately laminated film as shown in Fig. 12B, the monomolecular film on the water surface is removed for each step of immersing and drawing-up when the formation of a film on the substrate is completed, and another monomolecular film may be formed afresh so that film formation can be further carried out. This operation may be repeated.
In order to obtain a single layer film, two methods can be used. One of them is a method in which a substrate is previously kept immersed in an aqueous phase, thereafter a monomolecular film is formed on a water surface, and this monomolecular film is transferred to the substrate through a drawing-up step. The other of them is a method in which a monomolecular film is formed on the water surface, then a substrate is immersed in it so that the monomolecular film is transferred to the substrate, thereafter the monomolecular film on the water surface is removed, and the substrate on which a single layer film has been formed is drawn up. From the viewpoint of the stability of the film transferred to the substrate, it is desirable to use the former method.
The monomolecular film or a built-up film of monomolecular films comprising the polyamide acid-amine salt, formed on the substrate in this way, may _ - 23 -1 be heated to carry out a dehydration and cyclization (imidization) reaction and an deamination reaction.
The desired polyimide film can be thus obtained.
Baking, carried out here, should preferably be carried out at 150C to 300C 10 to 60 minutes in approximation, and in a nitrogen atmosphere or under reduced pressure. In either constitution of Figs. 12A
and 12B, the polyamide film formed by the LB process may preferably be formed in a layer number within the range of from 1 to 10, and in a film thickness of from 8 to 400 A in total (each layer has a film thickness of approximately from 4 to 80 A, though depending on the type of the polyimide). In regard to the direction in which the substrate is drawn up, the films should preferably be so formed as to be in the same direction (for example, the direction A shown in Fig. 1) between the upper and lower substrates when a cell has been made up.
As previously described, in the lower layer of the polyimide monomolecular film or the built-up film of polyimide monomolecular films, coating methods hitherto widely used may be used to form a polyimide film. In order to provide such a polyimide film on the substrate, a polyamide acid, which is a precursor of the polyimide, may be dissolved in a solvent such as N,N-dimethylformamide, N,N-dimethylacetamide, - 24 - Zl-~,2~2 1 N,N-dimethyl sulfoxide or N-methylpyrrolidone to form a 0.01 to 40 wt.% solution, and the resulting solution may be coated on a substrate by spin coating, spray coating or roll coating, followed by heating at a temperature of from 100 to 350C, and preferably from 200 to 300C, to carry out dehydration and cyclization(imidation). The desired polyimide film can be thus formed. The polyi`mide film formed by such coating methods may preferably have a film thickness of from about 30 A to about 2,000 A, and more preferably from 200 A to 1,000 A . Use of the insulating layers 13a and 13b as shown in Fig. 1 can be omitted.
Liquid crystal materials used in the present invention may preferably be liquid crystals that produce a chiral smectic phase through an isotropic phase, a cholesteric phase, and a smectic A phase in the temperature-decreasing process. Particularly preferred is a liquid crystal with a pitch of not less than 0.8 ,um when it is in a cholesteric phase (the pitch in a cholesteric phase is measured at the middle in the temperature range of the cholesteric phase).
Preferably usable as a specific liquid crystal is a liquid crystal composition containing the following liquid crystal materials "LC-1", "80B" and "80SI*" in the following percentage.
- 25 - 21~ 2 o CH 3 C8 H 17~C--(~)CH 2 CHC 2 H 5 C 2 H 5 CHCH 2~C--O~){)c 8 H
80SI *
C 8 H 17 ~C--O~H 2 CHC 2 H 5 Liquid crystal Composition ( 1 ) ( C ) go/ ( ) 10 (2) (LC-l)80/(8B)20 (3) (LC-1)70/(80B)30 (4) (LC-1)60/(80B)40 (5) 80SI*
(In the table, the subscript numerals are each expressed in weight ratio.) Fig. 2 is a diagramatical drawing of an example of a cell, to illustrate the operation of a ferroelectric liquid crystal. The numerals 21a and 2lb each denotes a substrate (a glass plate) covered 21.~ 2~, 1 with a transparent electrode comprised of a thin film made of In2O2, SnO2, ITO or the like. Between the substrates, a liquid crystal of an SmC* (chiral smectic C) phase or an SmH* (chiral smectic H) phase is sealed, which is so aligned that its liquid crystal molecular layer 22 may be perpendicular to the glass surfaces. A line 23 shown by a thick line indicates a liquid crystal molecule. This liquid crystal molecule 23 has a dipole moment (Pl) 24 in the direction falling at right angles with its molecule. When a voltage higher than a given threshold value is applied between the electrodes provided on the substrates 21a and 21b, the spiral structure of the liquid crystal molecule 23 comes loose, and thus the liquid crystal molecule 23 can change its direction of alignment so that all of dipole moments (Pl) 24 face toward the direction of the electric field. The liquid crystal molecule 23 has a slender shape, and shows refractive index anisotropy between its direction of the longitudinal axis and direction of the lateral axis.
Hence, it can be easily understood that if, for example, polarizers which are in crossed nicols each other are placed on both sides of a glass surface, there can be provided a liquid crystal optical modulation device capable of changing optical characteristics depending on the polarity of the Z~ 222 1 applied voltage.
A surface stabilized ferroelectric liquid crystal cell in the state of bistable alignment, which is used in the liquid crystal device of the present invention, can be made to have a sufficiently small thickness, for example, of from 0.1 ~m to 3 ~m. As the thickness of a liquid crystal layer becomes smaller in this way, the spiral structure of a liquid crystal molecule comes loose even in the state where no electric field is applied, and turns to have a non-spiral structure, so that its dipole moment P or P' results in either an upward state (34a) or a downward state (34b), as shown in Fig. 3. When as shown in Fig. 3 an electric field Ea or Eb of a voltage higher than a given threshold value and having a different polarity is applied to such a cell through means of applying a voltage (31a) and (31b), the dipole moment changes its direction to an upward direction 34a or a downward direction 34b corresponding to the electric field vector of the electric field Ea or Eb, and, corresponding therewith, the liquid crystal molecule is aligned in the direction of either a first stable state 33a or a second stable state 33b.
The effects obtainable from this ferroelectric liquid crystal cell are firstly that the response speed is very high, and secondly that the alignment of '~ - 28 - Zl.~22~, l the liquid crystal molecule is bistable. The second effect will-be further described with reference to, for example, Fig. 3. When the electric field Ea is applied, the liquid crystal molecule is aligned in the first stable state 33a and this state is stable even when the electric field has been removed. On the other hand, when the electric field Eb of a reverse direction is applied, the liquid crystal molecule is aligned in the second stable state 33b to change their direction, and still remain in this state even when the electric field has been removed. The respective states of alignment are also maintained so long as the electric field Ea to be applied does not exceed a given threshold value.
Fig. 4A is a cross-sectional view to diagramatically explain the state of alignment of liquid crystal molecules as produced in the direction of alignment according to the present invention.
The numerals 61a and 61b shown in Fig. 4A
denote an upper substrate and a lower substrate, respectively. The numeral 60 denotes a molecular layer formed of liquid crystal molecules 62, and the liquid crystal molecules 62 are arranged with changes in their positions along the base 64 (circular) of a cone 63.
Fig. 4B illustrates C-directors in the state Zl.~?;~Z
1 of uniform alignment. U1 in Fig. 4B shows C-directors 81 which are in one state of stable alignment, and U2, C-directors 81 which are the other state of stable alignment. Each C-director 81 is a projection of a molecular longitudinal axis (molecular axis) on an imaginary face perpendicular to the normal of the molecular layer 60 shown in Fig. 4A.
On the other hand, the state of alignment as produced using a conventional rubbed polyamide film is illustrated by the C-directors in Fig. 4C. For the state of alignment as shown in Fig. 4C, the molecular axis is so largely twisted from the upper substrate 61a toward the lower substrate 61b that the tilt angle ~ is small.
Fig. 5A is a plan to show the tilt angle ~
when the C-directors 81 are in the state of Fig. 4B
(herein called "the state of uniform alignment"), and Fig. 5B is a plan to show the tilt angle ~ when the C-directors 81 are in the state of Fig. 4C (herein called "the state of spray alignment"). In Figs. 5A
and 5B, the numeral 50 denotes the axis of rubbing treatment applied to the above-described polyimide film of the present invention, or the direction in which a substrate is drawn up when the above-described polyimide film of the present invention is formed-by the LB process. The numeral 5la denotes an average - 30 - 21.~
1 molecular axis formed in the state of alignment U1;
51b, an average molecular axis formed in the state of alignment U2; 52a, an average molecular axis formed in the state of alignment S1; and 52b, an average molecular axis formed in the state of alignment S2.
The average molecular axes 5la and 5lb can be converted by applying a voltage of reverse polarity which exceeds a threshold voltage each other. The same may also takes place between the average molecular axes 52a and 52b.
Usefulness of the state of uniform alignment to the delay of optical response (after-image) caused by a reverse electric field Vrev will be explained below. When the capacity of an insulating layer lS (alignment control film) of a liquid crystal cell is represented by Ci, the capacity of a liquid crystal layer by CLc, and the spontaneous polarization of a liquid crystal by Ps, the Vrev that causes the after-image is represented by the following expression:
Vrev 2 Ps / (Ci + CLC) Figs. 6A to 6C are cross-sectional views to illustrate the distribution of electric charges in a ferroelectric liquid crystal, the direction of spontaneous polarization Ps, and the direction of a reverse electric field Vrev, respectively. Fig. 6A
shows the state of distribution of plus and minus 21.~
~~ - 31 -electric charges in a memory state before application of a pulse electric field. The spontaneous polarization Ps is in the direction from the plus electric charges to the minus electric charges. In Fig. 6B, immediately after removing the pulse electric field the spontaneous polarization Ps is in a reverse direction to the direction in the state shown in Fig. 6A (hence, the liquid crystal molecules are reversed from the one state of stable alignment to the other state of stable alignment).
Since, however, the state of distribution of plus and minus electric charges is the same as in the state shown in Fig. 6A, a reverse electric field Vrev is produced in the liquid crystal in the direction of the arrow. This reverse electric field Vrev disappears after a while as shown in Fig. 6C, and the state of distribution of plus and minus electric charges is changed.
Fig. 7 illustrates changes of optical response occurring in the state of spray alignment as produced using a conventional polyimide aligning film, which are converted to changes of the tilt angle e. As shown in Fig. 7, when a pulse electric field is applied, the molecular axis is overshot from the average molecular axis S(A) formed in the state of spray alignment to the average molecular axis U2 formed in the state of uniform alignment, which is in the vicinity of the maximum tilt angle e, along the 21.~ Z
1 direction of an arrow X1. Immediately after removal of the pulse electric field, the reverse electric field Vrev as shown in Fig. 6B acts, and the tilt angle ~ is decreased, along the direction of an arrow X2, to the average molecular axis S(B) formed in the state of spray alignment. Then, a state of stable alignment can be obtained in which, because of the action of attenuation of the reverse electric field Vrev as shown in Fig. 6C, the tilt angle ~ has been a little increased, along the direction of an arrow X3, to the average molecular axis S(C) formed in the state of spray alignment. Optical response obtained here is made clear in Fig. 8.
According to the present invention, employment of the aligning film of the present invention does not bring about such a state of alignment of a liquid crystal that the average molecular axes S(A), S(B) and S(C) are formed in the state of spray alignment as shown in Fig. 7, and hence makes it possible to align 0 a liquid crystal to form an average molecular axis that may give a tilt angle ~ approximate to the maximum tilt angle e. Here, in the second embodiment of the present invention, the lower layer polyimide film mainly containing the structure represented by Formula (I) (i.e., the polyimide film A shown in Fig.
12A and the alternately laminated films of the Zl.~?,~2 1 polyimide films A and B other than the outermost layer, shown in Fig. 12B) is formed for the purposes of assuring the monoaxialness concerning initial liquid crystal alignment and also eliminating the influence the irregularities or the like of substrate surfaces (in practice, the insulating layers 13a and 13b) may have on the state of alignment of a liquid crystal. Hence, depending on the state of the lower layer polyimide film, the polyimide film B shown in Fig. 12A can be a single layer monomolecular film.
Fig. 9 shows optical response obtained when the polyimide aligning film of the present invention is used. As is evident from Fig. 9, no delay of optical response caused by the after-image occurs and lS also a high contrast is produced in a memory state.
According to experiments made by the present inventors, employment of the aligning method using the particular polyimide alignment film as will be made clearer in the following Examples has achieved a state O of alignment that gives a high optical contrast between a light state and a dark state, in particular, gives a high contrast to unselected picture elements at the time of the multiplexing drive as disclosed in U.S. Patent No. 4,655,561, etc., and also brings about no delay in optical response at the time of switching (at the time of multiplexing drive), which may cause 21.~?,2;~2 _ - 34 -1 the after-image at the time of display.
The present invention will be described below by giving Examples.
Example l Two sheets of l.l mm thick glass plates each provided with a l,000 A thick IT0 film were prepared.
The respective glass substrates were left to stand in saturated vapor of hexamethyldisilazane (HMDS) to carry out hydrophobic treatment. Thereafter, on each substrate thus treated, a built-up film of polyimide monomolecular films built up in 2, 4, 6, 8, lO, 20, 30 or 40 layers was formed by the LB process to provide an aligning film without rubbing treatment.
The process of forming the built-up film of polyimide monomolecular films will be detailed below.
The polyamide acid represented by the formula (l) was dissolved in N,N-dimethylacetamide (in concentration of l x lO M in terms of the repeating unit polyamide acid), and thereafter the solution and a 2 x lO 3 M solution separately prepared by dissolving N,N-dimethyloctadecylamine in the same solvent were mixed in equimolar amounts (v/v). A
solution of the polyamide acid octadecylamine salt represented by the formula (2) was thus prepared.
21.~ 2 O O
C C NH ~O~ NH
HOC COH C 6 H g C 6 H g ~- O O
O O
C~C --NH ~O~ NH
O=C C--O C 6 H g C 6 H g 0 I ~3 11 (~3 (2) HN (CH 3 ) 2 HN (CH 3 ) 2 (CH 2 ) 17 CH 3 (CH 2 ) 17 CH 3 The resulting solution was spread over an aqueous phase 111 (Fig. 11) comprised of pure water of 20C in water temperature to form a monomolecular film on the water surface. After removal of the solvent, a float as the partition plate 113 was moved to reduce the spreading area until the surface pressure was raised up to 25 mN/m. While keeping constant the surface pressure, the above ITO glass substrate was gently immersed at a rate of 5 mm/min in the direction crossing the water surface, and thereafter subsequently gently drawn up at a rate of 3 mm/min, thus making a two-layer Y-type monomolecular built-up film. Such operations were repeated to form a Zl.~?,22Z
_ 1 monomolecular built-up film (LB film) having a given number of monomolecular layers and comprising the polyamide acid octadecyl salt. Next, such a substrate was heated in vacuo under conditions of a rate of temperature rise of 20C/min and 300C constant-temperature heating for 10 minutes to carry out imidization. The desired aligning films were thus obtained.
Thereafter, alumina beads with an average particle diameter of 1.5 ~m were sprayed on one of the glass substrates. Then, the two sheets of glass substrates were put together in such a way that the axes of dipping directions (directions on the upper and lower substrates) of the respective aligning films were in parallel and in the same treatment directions each other. A cell was thus fabricated.
Into the resulting cell, a ferroelectric smectic liquid crystal "CS-1014" (trade name; a product of Chisso Corporation) was vacuum-injected in the state of an isotropic phase, and then annealed to 30C at a rate of 0.5C/hr from the state of the isotropic phase. Thus, it was possible to align the liquid crystal. In the cell of the present Example in which this "CS-1014" was used, the phase changes were 25 as follows: --- 21.~?,~;2 l 80.5C 69.1C 50C
Iso ) Ch ) SmA ) SmC*
(Iso: isotropic phase, Ch: cholesteric phase, SmA:
smectic A phase, SmC*: chiral smectic C phase) The liquid crystal cell provided with the aligning films each comprising the 10-layer LB film prepared as described above was inserted between a pair of 90 crossed nicols polarizers. Thereafter, a 30 V pulse for 50 ~sec was applied thereto and then the 90 crossed nicols were set to the position of extinction (a darkest state). Transmittance at this time was measured using a photomultiplier.
Subsequently, a -30 V pulse for 50 ~sec was applied, and transmittance at this time (a bright state) was measured in the same manner. As a result, it was revealed that the tilt angle ~ was 16, the transmittance in the darkest state was 0.9 %, the transmittance in the bright state was 50 %, and hence the ratio of contrast was 55:1.
The delay in optical response that causes an after-image was 0.2 second or less.
Using this liquid crystal cell, display was carried out according to multiplexing drive in which the drive wave forms as shown in Fig. 10 were used.
As a result, a display with a high contrast and high grade was obtained. After an image was displayed by Zl.~ 2 l inputting given characters, the whole screen was turned off to a white state to confirm that no after-image was seen to have occurred. The letter symbols SN, SN+1 and SN+2 in Fig. 10 represent wave forms of the voltages applied to scanning lines. The letter symbol I represents a wave form of the voltage applied to a typical information line. I-SN is a synthetic wave form of the voltage applied to the crossing area of the information line I and the scanning line SN.
In the present Example, experiments were made under conditions of V0 = 5 V to 8 V and ~T = 20 ~sec to 70 ~usec. Results of experiments on dependence to the number of LB film layers are shown in Table 1.
Table 1 Number of Delay in LB film layers Ratio of contrast optical response 2 42:1 0.2 sec or less 4 43:1 0.2 sec or less 6 53:1 0.2 sec or less 8 55:1 0.2 sec or less 55:1 0.2 sec or less 51:1 0.2 sec 51:1 0.3 sec 51:1 0.4 sec 21.~;~;22;~
1 Regardeless of the number of the LB film layers, it was possible to obtain alignment films with superior switching characteristics compared with conventional aligning films.
Example 2 Two sheets of 1.1 mm thick glass plates each provided with a 1,000 A thick IT0 film were prepared in the same manner as in Example 1. The respective glass substrates were coated with a solution of 3.0 %
by weight of the polyamide acid represented by Formula (1) as used in Example 1, dissolved in a 5/1 mixed solvent of N-methylpyrrolidone/n-butyl cellosolve, for 30 minutes using a spin coater of 3,000 rpm. After films were formed, each film was heated and baked at 300C for about 1 hour. The film hereby formed had a thickness of 250 A. The resulting coating film was subjected to rubbing in one direction using a nylon cloth. Thereafter, in the same manner as in Example 1, a cell was fabricated and the ratio of contrast and the delay in optical response were measured to reveal that excellent device characteristics were obtainable like the case when films were prepared by the LB
process.
Ratio of contrast: 50:1 Delay in optical response: 0.4 sec.
Display was also carried out according to ~_ - 40 - Zl.~
1 multiplexing drive in the same manner as in Example 1 to obtain the same results as in Example 1 in respect of contrast and after-image.
Examples 3 to 10 Cells were obtained in the same manner as in Example 1 except that the alignment control films (alignment films) and liquid crystal materials as shown in Table 2 were used. The respective cells were tested in the same manner as in Example 1. Results obtained in respect of the ratio of contrast and the delay in optical response are shown in Table 3.
Display was also carried out according to multiplexing drive in the same manner as in Example 1 to obtain the same results as in Example 1 in respect of contrast and after-image.
-- - 41 - 21~ 2 0 ~
o ~_, C) o 00 .~ ~ -o q~
o a~~ J Q. O
Ji C) I ~D 0 ~ O O
O ~
~r ~, ~ o --o ~ ~ 0 ' I
J
0=1~o=0 0=~ o=o O=I~U=O
=C~ o=O o=C~ Vo~= O=V o=O
E
~ -o Z
21~
~ J ~ o a) u ~ o ~.
0 ~ o o 0 o ~ ~ ,,, ~s o o a, :~ ~D O ~ a, . . o 0 ~n ~ ~ .c ~
O a I ~ ~
~V ~C) ~ ~ X
0 [~ ~ ~--V--C) ~ V
a) ~~
~ ~ c ~ a~
~ 0 1 X O ~ O <n ~ O C~ = O
E ~ O=C) ~) O=C~ C~ O
0=0 o=O ~ ~
O=~) o=O
~ O=(~ o=
_ O
Z d' ~ ~D
21.~ 222 as ~ ~
o o o a5 O ~ V
~ o -I ~ rY rY ~
a) ~ o g o o S , ~
o--I
o ,.
_~ Y ~ ~
o a) q~ 0 _, ,~ ._, r O (~
I
X
1 ~
~a) ~ ~ O ~
C O I ~
<~ ~ I ~ X
o ~} O=C.) (,~=0 O ~ N
Q' ~ ~
O = C~) C.) = O ~ O
C o=(~ o=O o=~O=O
Z r~ ~
21.~?;~
1 Table 3 Alignment Number of Exam- film LB film Ratio of Delay in ple No.* layers contrast optical response 3 1 8 55:1 0.2 sec or less 4 2 8 40:1 0.8 sec 3 8 52:1 0.2 sec or less 6 4 8 50:1 0.2 sec or less 7 5 8 58:1 0.2 sec or less 8 6 8 58:1 0.2 sec or less 9 7 8 53:1 0.2 sec or less 8 8 50:1 0.2 sec or less * No. in Table 2 Examples 11 to 15 Cells were obtained in the same manner as in Example 2 except that the alignment control films (alignment films) and liquid crystal materials as shown in Table 2 were used. The respective cells were tested in the same manner as in Example 1. Results obtained in respect of the ratio of contrast and the delay in optical response are shown in Table 4.
Display was also carried out according to multiplexing drive in the same manner as in Example 1 21.'2~22 _ 1 to obtain the same results as in Example 1 in respect of contrast and after-image.
Table 4 Alignment Number of Exam- film LB film Ratio of Delay in ple No.*layers contrast optical response 11 3 200 50:1 0.4 sec 12 4 190 47:1 0.4 sec 13 5 200 53:1 0.4 sec 14 7 220 49:1 0.4 sec 8 210 44:1 0.4 sec * No. in Table 2 Comparative Examples 1 to 4 Cells were fabricated in the same manner as in Example 2 except that the alignment control films (alignment films) and liquid crystal materials as shown in Table 5 were used. The respective cells were tested in the same manner as in Example 1. Results obtained in respect of the ratio of contrast and the delay in optical response are shown in Table 6.
Display was also carried out according to multiplexing drive in the same manner as in Exampie 1 2~ 2 1 to obtain the results that the contrast was lower than that of Examples of the present invention and also after-image occurred.
Table 5 Alignment film Llquld crystal (polyamide acid varnish) material Comparative Example:
1SP-710 (trade name)* CS1014***
2ditto ditto 3LQ-5200 (trade name)** CS1014***
4ditto ditto * An aromatic polyimide varnish, a product of Toray Industries, Inc.
** A polyimide varnish, a product of Hitachi Chemical Co., Ltd.
*** FLC, a product of Chisso Corporation 21.~
1 Table 6 Delay in Ratio of contrast optical response Comparative Example:
1 8:1 1.5 sec 2 7:1 2.5 sec 3 10:1 1.2 sec 4 8:1 2.2 sec In the above Examples, characteristics of liquid crystal devices prepared using the ferroelectric liquid crystal CS1014 were evaluated.
The liquid crystal materials used are by no means limited to ferroelectric liquid crystals. For example, nematic liquid crystals, cholesteric liquid crystals and smectic liquid crystals can also be used alone or in the form of a mixture. An example of a device in which a nematic liquid crystal is used is shown below.
Example 16 Substrates were prepared in the same manner as in Example 2. The substrates were put together in such a manner that the rubbing directions may cross at right angles, and peripheral edges thereof were sealed 21.~
1 using a heat-curable epoxy resin, except for an injection opening. The space between the substrates was 6 ~um.
Next, a nematic liquid crystal (ZLI-1285, a product of Merck AG., West Germany) was injected into the cell, and then the injection opening was sealed.
A pair of polarizers were disposed in parallel to the rubbing direction of an adjacent substrate, and the liquid crystal was observed with a microscope to confirm that twisted alignment was achieved in a superior uniformity.
Using this liquid crystal device, a continuous operation test was carried out.
As a result, a good twisted alignment was retained even after drive for 30 days using an alternating current of 10 V at 50 Hz, and thus superior durability was confirmed.
Example 17 Two sheets of 1.1 mm thick glass plates each comprising a 1,500 A thick IT0 film provided thereon with a 600 A thick Ta205 film were prepared as substrates. The resulting substrates were subjected to ultrasonic cleaning using isopropyl alcohol and thereafter left to stand for 24 hours in saturated vapor of hexamethyldisilazane to carry out hydrophobic treatment. Subsequently, on each substrate thus 21.~
1 treated, a polyimide aligning film was formed by the LB process, The process of forming the polyimide alignment film will be detailed below.
The polyamide acid represented by the formula (3) was dissolved in a solvent N,N'-dimethylacetamide (in concentration of 1 x 10 M in terms of the monomer), and thereafter the solution and a 1 x 10 3 M
solution separately prepared by dissolving di-n-decylamine in the same solvent were mixed in a ratio of 1:2 (v/v). A solution of the polyamide acid di-n-decylamine salt represented by the formula (4) was thus prepared.
- O O
C C -NH ~ O ~ NH
_ O (3) - O O
O- C -NH ~ O ~ (4) O O H 2 N [(CH 2 ) 9 CH 3 ] 2 n ~3 H 2 N [.(CH z) g CH 3 ] 2 The resulting solution was spread over an _ 50 2~.~2~2 1 aqueous phase comprised of pure water of 20C in water temperature to form a monomolecular film on the water surface. After removal of the solvent, the surface pressure was raised up to 20 mN/m. While keeping constant the surface pressure, the above substrate was gently immersed at a rate of 5 mm/min in the direction crossing the water surface, and thereafter subsequently gently drawn up at a rate of 5 mm/min, thus making a built-up film of two-layer Y-type monomolecular films. Such operations were repeated to form a built-up film of seven-layer monomolecular films comprising the polyamide acid di-n-decylamine salt of the formula (4). Here, the substrate was kept immersed in the water. While keeping such a state, the monomolecular film of the polyamide acid di-n-decylamine salt on the aqueous phase was once removed, and a monomolecular film of a fluorine-containing polyamide acid di-n-decylamine salt represented by the formula (5) was afresh formed on the aqueous phase.
This was carried out by the same method as described above.
O-- C C--NH ~ 0~ CF 3 o o (~3 -- H 2 N t(CH 2) 9 CH 3] 2 ~3 H2 N [(CH2) 9 CH 3] 2 (~ O ~ NH
O (5) The surface pressure was raised up to 15 mN/m.
lS Thereafter, while keeping constant the surface pressure, the above substrate kept immersed in water was gently drawn up at a rate of 5 mm/min in the direction crossing the water surface. A built-up film of a single-layer monomolecular film of the fluorine-containing polyamide acid di-n-decylamine salt ( 5 ) was thus formed on the built-up film of the seven-layer monomolecular films of the polyamide acid di-n-decylamine salt (4). Next, such a substrate was subjected to heat treatment at 300C for 20 minutes to carry out imidization (formulas (6) and (7)) of the respective polyamide acid salts.
1 (4) ~
- O O
Il 11 C C ~ ~
C C (6) O O
(5) --~_ - O O
lO - N ~ N ~ CF 3 ll ll CF 3 O O
- - (7) Polyimide alignment films each comprising a built-up film of polyamide monomolecular films of 8 layers in total were thus obtained. Thereafter, alumina beads with an average particle diameter of l.S ~m were sprayed on one of the substrates. Then, the two sheets of substrates were put together in such a way that the drawing-up directions of the respective substrates were in parallel and in the same directions each other. A liquid crystal cell was thus fabricated.
Into the resulting cell, a ferroelectric smectic liquid crystal "CS-1014" (trade name; a product of Chisso Corporation) was vacuum-injected in Zl.~;~2;'`2 l the state of an isotropic phase, and then cooled slowly up to 30C at a rate of 0.5C/hr from the state of the isotropic phase to from an aligned state.
Thus, it was possible to align the liquid crystal. In the cell of the present Example in which this "CS-1014" was used, the phase changes were as follows:
80.5C 69.1C 50C
Iso > Ch ) SmA ) SmC*
(Iso: isotropic phase, Ch: cholesteric pahse, SmA:
smectic A phase, SmC*: chiral smectic C phase) The above liquid crystal cell was inserted between a pair of 90 crossed nicols polarizers.
Thereafter, a 30 V pulse for 50 ,usec was applied thereto and then the 90 crossed nicols were set to the position of extinction (a darkest state).
Transmittance at this time was measured using a photomultiplier. Subsequently, a -30 V pulse for 50 ,usec was applied, and transmittance at this time (a bright state) was measured in the same manner. As a 0 result, it was revealed that the tilt angle ~ was 15, the transmittance in the darkest state was 0.9 % and on the other hand the transmittance in the bright state was 45 %, and hence the ratio of contrast was 50:1. The delay in optical response that causes an after-image was 0.2 second or less.
Using this liquid crystal cell, display was _ 54 _ 21~
1 carried out according to multiplexing drive in which the drive wave forms as shown in Fig. 10 were used.
As a result, a display with a high contrast and high grade was obtained. After an image was displayed by inputting given characters, the whole screen was turned off to a white state to confirm that no after-image was seen to have occurred. The letter symbols SN, SN+1 and SN+2 in Fig. 10 represent wave forms of the voltages applied to scanning lines. The letter symbol I represents a wave form of the voltage applied to a typical information line. I-SN is a synthetic wave form of the voltage applied to the crossing area of the information line I and the scanning line SN.
In the present Example, experiments were made under conditions of V0 = 5 V to 8 V and AT = 20 ~sec to 70 ~sec.
Example 18 A liquid crystal cell was prepared in entirely the same manner as in Example 17, except that as the method of forming the polyimide film A (Fig. 12A) the LB process was replaced with coating. Different points are described below.
The substrates were coated with a solution of 3.0 % by weight of the polyamide acid (3) dissolved in a 5/1 mixed solvent of N-methylpyrrolidone/n-butyl cellosolve., for 10 minutes using a spin coater of .2Z
1 3,000 rpm. After films were formed, each film was heated and baked at 270C for about 1 hour to carry out imidization. A polyimide film A of 200 A thick comprising the polyimide (6) was thus formed. On the resulting substrate, 6 layers of monomolecular films of the fluorine-containing polyamide acid di-n-decylamine salt (5) were built up by the LB process in the same manner as in Example 17. Thereafter, the resulting substrate was subjected to heat treatment at 300C for 20 minutes to form a polyimide film B
comprising a built-up film of monomolecular films (6 layers). Thereafter, in the same manner as in Example 17, a cell was fabricated and the ratio of contrast and the delay in optical response were measured to reveal that former was 50:1 or more and the latter was 0.7 seconds or less. Display was also carried out according to multiplexing drive in the same manner as in Example 17 to obtain the same results as in Example 17 in respect of contrast and after-image.
Examples 19 to 22 Liquid crystal cells were obtained in the same manner as in Example 17 except that the alignment films having the aligning film constitution and polyimide structure as shown in Table 7 were used.
Test results on the ratio of contrast and the delay in optical response are shown in Table 8. Display was Zl.~;222 1 also carried out according to multiplexing drive in the same manner as in Example 17 to obtain the same results as in Example 17 in respect of contrast and after-image.
Comparative Examples 5 to 7 Liquid crystal cells were fabricated in the same manner as in Example 17 except that the alignment control films (aligning films) as shown in Table 9 were used. Test results on the ratio of contrast and the delay in optical response are shown in the same Table 9. Display was also carried out according to multiplexing drive in the same manner as in Example 17 to obtain the results that the contrast was lower than that of Examples of the present invention and also after-image occurred.
;~1 .~æ
~ o, _ ~ n ~ ~
~s a ~ ~ v a o ~ s . .
o o ~ ~ o o S --I ~ o ~ ~s o ~ o ~ m ~
O O
~o [~
~ --V
r~ ~ O ~ ~
Q ~ ~
0 ~ ~ G
~ ~ ,~ .
.. .. :Z
m / \ / \
0=~) o=o O=C~)=O
~ ~ / \ ~
~ ~ O=C) C>=O
--~ 7 O=C~ =0 /
a C:
.,, ~ ~ o o ~ ,~
p., ,¢ ~ ~) ~ rL, I I ~
X ~ ~ cn Z~ 2 h X X ~
a) ~ ~ ,. ..
'{S 0 --I . 0 d5 ~ h 0 q ~
'~ ~ 0 .t ~ 0 0 ~ ~
o~ O
_I _I ~ o6 o~ ~ o~ ~J
O ~ S o~ o o~¢ o~
~, ~, ~ ~ O O ~O
. . . ..
O O O
~ O O ~ O O O
I ~D ~1 0 ~ ~
o ~ oq~ m m om mm -cn ~ X
~--v ~ o 0 ~
z ~ ~ 0~
15 Q ~ O=~) ()=O
0 1:) \ / / \ O ~:: O O
E~ ~ _ / \ ~ E~
oq .. C ~ 0=~ =O
m m rl / O=~ =O ~ ~ ~ ~
=C-) ~)= ~ \ / a) o a) o o ~ \ /
~ ~ O ~ ~ ~ ~
O -- -- ~ O O O O
CL ~ ~ lL
~ c ~ ~: m JJ O
o ~ ~ o I I a X ~ ~ O ~ C~
Zl.~ 2 l Table 8 Exam- Delay in optical ple Ratio of contrast response (sec) 19 45:1 0.2 50:1 0.2 21 45:1 0.8 22 55:1 0.2 Table 9 Delay in PolyimideFilm form- Ratio of optical alignment film ing process contrast response, 15 Comparative (sec) Example:
5 SP-710*1Coating*3 8:1 1.5 6 LQ-5200*2 " 10:1 1.2 7 SP-510*LB process* 10:1 0.7 *1 (trade name; a product of Toray Industries, Inc.) *~: (trade name; a product of Hitachi Chemical Co.) * : 200 A thick, rubbing treatment *4: 32 A thick, 8 layers, no rubbing treatment - 60 - 21,~
1 As will be evident from the above Examples and Comparative Example, the present invention has the effect that it can achieve a high contrast between a bright state and a dark state, in particular, can achieve a very high display contrast in multiplexing drive to obtain a display of high quality level, and also may not cause the after-image phenomenon that is offensive to the eye.
Claims (14)
PROPERTY OR PRIVILEGE IS CLAIMED ARE DEFINED AS FOLLOWS:
1. A liquid crystal device comprising a pair of substrates and a liquid crystal material disposed between said pair of substrates, wherein at least one of said substrates is provided with a laminated film comprised of a film comprising a polyimide containing a structural unit represented by the following Formula (I) (I) and a film comprising a polyimide containing a structural unit represented by the following Formula (II) (II) wherein R1 represents a benzene group, a diphenyl group, a naphthalene group, a diphenylmethane group, a diphenyl sulfide group, a diphenyl ether group, or a derivative group thereof on which at least one methyl group or ethyl group is substituted; R2 represents a benzene group, a diphenyl group, a naphthalene group, a diphenyl sulfide group, a diphenyl sulfone group, a diphenyl ether group, a phenoxyphenyl group, or a derivative group thereof on which at least one methyl group or ethyl group is substituted; R3 represents the same as defined for R1, a derivative group thereof on which at least one trifluoromethane group is substituted, or a 2,2-bisphenylhexafluoropropane group or a derivative group thereof on which at least one trifluoromethane group is substituted; R4 and R5 may be the same or different, and each represent the same as defined for R2 or a derivative group thereof on which at least one trifluoromethane group is substituted, and 2,2-bisphenylhexafluoropropane group or a derivative group thereof on which at least one trifluoromethane group is substituted.
2. A liquid crystal device according to Claim 1, wherein said film comprising a polyimide containing a structural unit represented by Formula (II) is a monomolecular film or a built-up film thereof formed by the Langmuir-Blodgett process.
3. A liquid crystal device according to Claim 1, wherein both of said film comprising a polyimide containing a structural unit represented by Formula (I) and said film comprising a polyimide containing a structural unit represented by Formula (II) each comprise a monomolecular film or a built-up film thereof formed by the Langmuir-Blodgett process.
4. A liquid crystal device according to Claim 1, wherein said laminated film comprises films of an alternately laminated structure of a monomolecular film or a built-up film thereof comprising said polyimide containing a structural unit represented by Formula (I) and a monomolecular film or a built-up film thereof comprising said polyimide containing a structural unit represented by Formula (II).
5. A liquid crystal device according to Claim 1, wherein said laminated film has a total film thickness of 8 to 400 .ANG..
6. A liquid crystal device according to Claim 1, wherein said polyimide containing a structural unit represented by Formula (I) is obtained by imidation of a polyamide acid synthesized by condensation reaction of;
a carboxylic anhydride selected from the group consisting of pyromellitic anhydride, 2,3,6,7-naphthalenetetracarboxylic anhydride, 3,3',4,4'-diphenyltetracarboxylic anhydride, 1,2,5,6-naphthalenetetracarboxylic anhydride, 2,2',3,3'-diphenyltetracarboxylic anhydride, 2,3,4,5-thiophentetracarboxylic anhydride, 3,3',4,4'-diphenylpropanetetracarboxylic anhydride, 3,3',4,4'-diphenylsulfonetetracarboxylic anhydride, 3,3',4,4'-diphenylethertetracarboxylic anhydride, 3,3',4,4'-diphenylsulfidetetracarboxylic anhydride, and a derivative thereof on which at least one methyl group or ethyl group is substituted; with a diamine selected from the group consisting of m-phenylene diamine, p-phenylene diamine, m-xylene diamine, p-xylene diamine, 4,4'-diaminodiphenyl ether, 4,4'-diaminodiphenyl methane, 2,2'-bis(4-aminophenyl) propane, 4,4'-methylenedianiline, 4,4'-diaminodiphenyl sulfide, 4,4'-diaminodiphenylsulfonic acid, 1,5-diaminonaphthalene, 3,3'-dimethylbenzidine, and a derivative thereof on which at least one methyl group or ethyl group is substituted.
a carboxylic anhydride selected from the group consisting of pyromellitic anhydride, 2,3,6,7-naphthalenetetracarboxylic anhydride, 3,3',4,4'-diphenyltetracarboxylic anhydride, 1,2,5,6-naphthalenetetracarboxylic anhydride, 2,2',3,3'-diphenyltetracarboxylic anhydride, 2,3,4,5-thiophentetracarboxylic anhydride, 3,3',4,4'-diphenylpropanetetracarboxylic anhydride, 3,3',4,4'-diphenylsulfonetetracarboxylic anhydride, 3,3',4,4'-diphenylethertetracarboxylic anhydride, 3,3',4,4'-diphenylsulfidetetracarboxylic anhydride, and a derivative thereof on which at least one methyl group or ethyl group is substituted; with a diamine selected from the group consisting of m-phenylene diamine, p-phenylene diamine, m-xylene diamine, p-xylene diamine, 4,4'-diaminodiphenyl ether, 4,4'-diaminodiphenyl methane, 2,2'-bis(4-aminophenyl) propane, 4,4'-methylenedianiline, 4,4'-diaminodiphenyl sulfide, 4,4'-diaminodiphenylsulfonic acid, 1,5-diaminonaphthalene, 3,3'-dimethylbenzidine, and a derivative thereof on which at least one methyl group or ethyl group is substituted.
7. A liquid crystal device according to Claim 1, wherein said polyimide containing a structural unit represented by Formula (II) is obtained by heat cyclization of a polyamide acid synthesized by condensation reaction of;
a carboxylic anhydride selected from the group consisting of pyromellitic anhydride, 2,3,6,7-naphthalenetetracarboxylic anhydride, 3,3',4,4'-diphenyltetracarboxylic anhydride, 1,2,5,6-naphthalenetetracarboxylic anhydride, 2,2',3,3'-diphenyltetracarboxylic anhydride, 2,3,4,5-thiophenetetracarboxylic anhydride, 3,3',4,4'-diphenylpropanetetracarboxylic anhydride, 3,3',4,4'-diphenylsulfonetetracarboxylic anhydride, 3,3',4,4'-diphenylehtertetracarboxylic anhydride, 3,3',4,4'-diphnylsulfidetetracarboxylic anhydride, (hereinafter called "Group A"); a derivative of any of the compounds of Group A on which at least one methyl group or ethyl group is substituted (hereinafter called "Group B"); and 1,1,1,3,3,3-hexafluoro-2,2-bis(3,4-phenyldicarboxylic anhydride) propane, and a derivative of any of the compounds of Groups A and B or 1,1,1,3,3,3-hexafluoro-2,2-bis(3,4-phenyldicarboxylic anhydride) propane, on which at least one trifluoromethyl group is substituted; with a diamine selected from the group consisting of 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(3-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(2-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis(4-aminophenyl)hexafluoropropane, 2,2-bis[4-(4-aminophenyl sulfide)phenyl]hexafluoropropane, 2,2-bis[4-(4-aminobenzyl)phenyl]hexafluoropropane, 2,2-bis[4-(4-aminophenylsulfonic acid)phenyl]hexafluoropropane, 2,2-bis(5-aminonaphthyl)hexafluoropropane, and a derivative thereof on which at least one methyl group, ethyl group and/or trifluoromethyl group is substituted.
a carboxylic anhydride selected from the group consisting of pyromellitic anhydride, 2,3,6,7-naphthalenetetracarboxylic anhydride, 3,3',4,4'-diphenyltetracarboxylic anhydride, 1,2,5,6-naphthalenetetracarboxylic anhydride, 2,2',3,3'-diphenyltetracarboxylic anhydride, 2,3,4,5-thiophenetetracarboxylic anhydride, 3,3',4,4'-diphenylpropanetetracarboxylic anhydride, 3,3',4,4'-diphenylsulfonetetracarboxylic anhydride, 3,3',4,4'-diphenylehtertetracarboxylic anhydride, 3,3',4,4'-diphnylsulfidetetracarboxylic anhydride, (hereinafter called "Group A"); a derivative of any of the compounds of Group A on which at least one methyl group or ethyl group is substituted (hereinafter called "Group B"); and 1,1,1,3,3,3-hexafluoro-2,2-bis(3,4-phenyldicarboxylic anhydride) propane, and a derivative of any of the compounds of Groups A and B or 1,1,1,3,3,3-hexafluoro-2,2-bis(3,4-phenyldicarboxylic anhydride) propane, on which at least one trifluoromethyl group is substituted; with a diamine selected from the group consisting of 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(3-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(2-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis(4-aminophenyl)hexafluoropropane, 2,2-bis[4-(4-aminophenyl sulfide)phenyl]hexafluoropropane, 2,2-bis[4-(4-aminobenzyl)phenyl]hexafluoropropane, 2,2-bis[4-(4-aminophenylsulfonic acid)phenyl]hexafluoropropane, 2,2-bis(5-aminonaphthyl)hexafluoropropane, and a derivative thereof on which at least one methyl group, ethyl group and/or trifluoromethyl group is substituted.
8. A method of driving a liquid crystal device, comprising bringing the liquid crystal device according to Claim 1 into multiplexing drive.
9. A method of driving a liquid crystal device according to Claim 8, wherein said film comprising a polyimide containing a structural unit represented by Formula (II) is a monomolecular film or a built-up film thereof formed by the Langmuir-Blodgett process.
10. A method of driving a liquid crystal device according to Claim 8, wherein both of said film comprising a polyimide containing a structural unit represented by Formula (I) and said film comprising a polyimide containing a structural unit represented by Formula (II) each comprise a monomolecular film or a built-up film thereof formed by the Langmuir-Blodgett process.
11. A method of driving a liquid crystal device according to Claim 8, wherein said laminated film comprises films of an alternately laminated structure of a monomolecular film or a built-up film thereof comprising said polyimide containing a structural unit represented by Formula (I) and a monomolecular film or a built-up film thereof comprising said polyimide containing a structural unit represented by Formula (II).
12. A method of driving a liquid crystal device according to Claim 8, wherein said laminated film has a total film thickness of 8 to 400 .ANG..
13. A method of driving a liquid crystal device according to Claim 8, wherein said polyimide containing a structural unit represented by Formula (I) is obtained by heat cyclization of a polyamide acid synthesized by condensation reaction of;
a carboxylic anhydride selected from the group consisting of pyromellitic anhydride, 2,3,6,7-naphthalenetetracarboxylic anhydride, 3,3',4,4'-diphenyltetracarboxylic anhydride, 1,2,5,6-naphthalenetetracarboxylic anhydride, 2,2',3,3'-diphenyltetracarboxylic anhydride, thiophene-2,3,4,5-tetracarboxylic anhydride, 3,3',4,4'-diphenylpropanetetracarboxylic anhydride, 3,3',4,4'-diphenylsulfonetetracarboxylic anhydride, 3,3',4,4'-diphenylethertetracarboxylic anhydride, 3,3',4,4'-diphenylsulfidetetracarboxylic anhydride, and a derivative group thereof on which at least one methyl group or ethyl group is substituted; with a diamine selected from the group consisting of m-phenylene diamine, p-phenylene diamine, m-xylene diamine, p-xylene diamine, 4,4'-diaminodiphenyl ether, 4,4'-diaminodiphenyl methane, 2,2'-bis(4-aminophenyl)propane, 4,4'-methylenedianiline, 4,4'-diaminodiphenyl sulfide, 4,4'-diaminodiphenylsulfonic acid, 1,5-diaminonaphthalene, 3,3'-dimethylbenzidine, and a derivative thereof on which at least one methyl group or ethyl group is substituted.
a carboxylic anhydride selected from the group consisting of pyromellitic anhydride, 2,3,6,7-naphthalenetetracarboxylic anhydride, 3,3',4,4'-diphenyltetracarboxylic anhydride, 1,2,5,6-naphthalenetetracarboxylic anhydride, 2,2',3,3'-diphenyltetracarboxylic anhydride, thiophene-2,3,4,5-tetracarboxylic anhydride, 3,3',4,4'-diphenylpropanetetracarboxylic anhydride, 3,3',4,4'-diphenylsulfonetetracarboxylic anhydride, 3,3',4,4'-diphenylethertetracarboxylic anhydride, 3,3',4,4'-diphenylsulfidetetracarboxylic anhydride, and a derivative group thereof on which at least one methyl group or ethyl group is substituted; with a diamine selected from the group consisting of m-phenylene diamine, p-phenylene diamine, m-xylene diamine, p-xylene diamine, 4,4'-diaminodiphenyl ether, 4,4'-diaminodiphenyl methane, 2,2'-bis(4-aminophenyl)propane, 4,4'-methylenedianiline, 4,4'-diaminodiphenyl sulfide, 4,4'-diaminodiphenylsulfonic acid, 1,5-diaminonaphthalene, 3,3'-dimethylbenzidine, and a derivative thereof on which at least one methyl group or ethyl group is substituted.
14. A method of driving a liquid crystal device according to Claim 8, wherein said polyimide containing a structural unit represented by Formula (II) is obtained by heat cyclization of a polyamide acid synthesized by condensation reaction of;
a carboxylic anhydride selected from the group consisting of pyromellitic anhydride, 2,3,6,7-naphthalenetetracarboxylic anhydride, 3,3',4,4'-diphenyltetracarboxylic anhydride, 1,2,5,6-naphthalenetetracarboxylic anhydride, 2,2',3,3'-diphenyltetracarboxylic anhydride, thiophene-2,3,4,5-tetracarboxylic anhydride, 3,3',4,4'-diphenylpropanetetracarboxylic anhydride, 3,3',4,4'-diphenylsulfonetetracarboxylic anhydride, 3,3',4,4'-diphenylethertetracarboxylic anhydride, 3,3',4,4'-diphenylsulfidetetracarboxylic anhydride, (hereinafter called "Group A" ); a derivative of any of the compounds of Group A on which at least one methyl group or ethyl group is substituted (hereinafter called "Group B" ); and 1,1,1,3,3,3-hexafluoro-2,2-bis(3,4-phenyldicarboxlic anhydride)propane anhydride, and a derivative of any of the compounds of Groups A and B or the anhydride 1,1,1,3,3,3-hexafluoro-2,2-bis(3,4-phenyldicarboxylic anhydride) propane on which at least one trifluoromethyl group is substituted; with a diamine selected from the group consisting of 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(3-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(2-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis(4-aminophenyl)hexafluoropropane, 2,2-bis[4-(4-aminophenyl sulfide)phenyl]hexafluoropropane, 2,2-bis[4-(4-aminobenzyl)phenyl]hexafluoropropane, 2,2-bis[4-(4-aminophenylsulfonic acid)phenyl]hexafluoropropane, 2,2-bis(5-aminonaphthyl)hexafluoropropane, and a derivative thereof on which at least one methyl group, ethyl group and/or trifluoromethyl group is substituted.
a carboxylic anhydride selected from the group consisting of pyromellitic anhydride, 2,3,6,7-naphthalenetetracarboxylic anhydride, 3,3',4,4'-diphenyltetracarboxylic anhydride, 1,2,5,6-naphthalenetetracarboxylic anhydride, 2,2',3,3'-diphenyltetracarboxylic anhydride, thiophene-2,3,4,5-tetracarboxylic anhydride, 3,3',4,4'-diphenylpropanetetracarboxylic anhydride, 3,3',4,4'-diphenylsulfonetetracarboxylic anhydride, 3,3',4,4'-diphenylethertetracarboxylic anhydride, 3,3',4,4'-diphenylsulfidetetracarboxylic anhydride, (hereinafter called "Group A" ); a derivative of any of the compounds of Group A on which at least one methyl group or ethyl group is substituted (hereinafter called "Group B" ); and 1,1,1,3,3,3-hexafluoro-2,2-bis(3,4-phenyldicarboxlic anhydride)propane anhydride, and a derivative of any of the compounds of Groups A and B or the anhydride 1,1,1,3,3,3-hexafluoro-2,2-bis(3,4-phenyldicarboxylic anhydride) propane on which at least one trifluoromethyl group is substituted; with a diamine selected from the group consisting of 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(3-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis[4-(2-aminophenoxy)phenyl]hexafluoropropane, 2,2-bis(4-aminophenyl)hexafluoropropane, 2,2-bis[4-(4-aminophenyl sulfide)phenyl]hexafluoropropane, 2,2-bis[4-(4-aminobenzyl)phenyl]hexafluoropropane, 2,2-bis[4-(4-aminophenylsulfonic acid)phenyl]hexafluoropropane, 2,2-bis(5-aminonaphthyl)hexafluoropropane, and a derivative thereof on which at least one methyl group, ethyl group and/or trifluoromethyl group is substituted.