CA1293496C - Catalytic system for epoxidation of alkenes employing low sodium catalyst supports - Google Patents
Catalytic system for epoxidation of alkenes employing low sodium catalyst supportsInfo
- Publication number
- CA1293496C CA1293496C CA000515866A CA515866A CA1293496C CA 1293496 C CA1293496 C CA 1293496C CA 000515866 A CA000515866 A CA 000515866A CA 515866 A CA515866 A CA 515866A CA 1293496 C CA1293496 C CA 1293496C
- Authority
- CA
- Canada
- Prior art keywords
- catalyst
- silver
- support
- efficiency
- redox
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Abstract:
A process is provided for the epoxidation of an alkene in the presence of an oxygen-containing gas which comprises contacting the alkene and the oxygen-containing gas under epoxidation conditions in the presence of at least one efficiency-enhancing gaseous member of a redox-half reaction pair and a solid catalyst, the catalyst comprising a catalytically-effective amount of silver on a solid support and an efficiency-enhancing amount of at least one efficien-cy-enhancing salt of a member of a redox-half reac-tion pair, the support having less than about 50 ppm, by weight, of leachable sodium.
A process is provided for the epoxidation of an alkene in the presence of an oxygen-containing gas which comprises contacting the alkene and the oxygen-containing gas under epoxidation conditions in the presence of at least one efficiency-enhancing gaseous member of a redox-half reaction pair and a solid catalyst, the catalyst comprising a catalytically-effective amount of silver on a solid support and an efficiency-enhancing amount of at least one efficien-cy-enhancing salt of a member of a redox-half reac-tion pair, the support having less than about 50 ppm, by weight, of leachable sodium.
Description
IMPROVED CATALYTIC SYSTEM FOR EPOXIDATION OF
ALR~NES EMPLOYING LOW SODIUM_CATA~YST SUPPORTS
Technical Field:
The present invention i5 directed to an impro~ed system ~or the preparation of alkene oxide from al-i5 kene and an oxygen-containin~ gas employing a sup-ported silver catalyst. More particularly, the pre-sent inven~ion relates to a direct oxidation of al-kene to the corresponding epoxide in which both effi-ciency of the catalytic system and stability o~ the catalyst are enhanced by combination of a gaseous member of a redox-half reaction pair present in the gaseous mixture of oxygen and alkene, a salt of a member of a redox-half reaction pair in combination with the catalyst, and use of a stability-enhancing 5upport.
; ~ Background Ar~:
The production of alkene oxides, or epoxides, particularly ethylene~oxide by the direct:oxidation of the corresponding alkene in the presence of a silver containing catalyst has been known for many years. For example, the basic process was described by Lefort in U. S. Patent 1,998,878 and by Van Peski in U. S. Patent 2,040,782. The basic reaction pro-, ~4 .
3~
ceeds, as illustrated for ethylene, according to the equation:
/o\
ALR~NES EMPLOYING LOW SODIUM_CATA~YST SUPPORTS
Technical Field:
The present invention i5 directed to an impro~ed system ~or the preparation of alkene oxide from al-i5 kene and an oxygen-containin~ gas employing a sup-ported silver catalyst. More particularly, the pre-sent inven~ion relates to a direct oxidation of al-kene to the corresponding epoxide in which both effi-ciency of the catalytic system and stability o~ the catalyst are enhanced by combination of a gaseous member of a redox-half reaction pair present in the gaseous mixture of oxygen and alkene, a salt of a member of a redox-half reaction pair in combination with the catalyst, and use of a stability-enhancing 5upport.
; ~ Background Ar~:
The production of alkene oxides, or epoxides, particularly ethylene~oxide by the direct:oxidation of the corresponding alkene in the presence of a silver containing catalyst has been known for many years. For example, the basic process was described by Lefort in U. S. Patent 1,998,878 and by Van Peski in U. S. Patent 2,040,782. The basic reaction pro-, ~4 .
3~
ceeds, as illustrated for ethylene, according to the equation:
/o\
2 C~2 CH2 + 2 ~ 2 CH2-CH2 (I) and production of an unwanted by~product according to the reaction:
CH2=CH2 + 3 2 > 2 CO2 + 2 H20 (II) or by further oxidation of the epoxide.
In the years between the Van Peski patent and the present inventions, research efforts have been lS directed to improving both the activity and longevity or useful life of the catalyst and the efficiency of the overall catalytic reaction. As is indicated by reactions I and II, the oxidation of an alkene may produce either the alkene oxide (I) sought in the process or the by-products CO2 and H2O.
Several terms are commonly used to describe some of the parameters of the catalytic system. For in-stance, "conversion" has been defined as the percent-age of alk~ fed to the reactor which undergoes reaction. The "efficiency" or, as it is sometimes called, the "selectivity" of the overall process is an indication of the proportion, usually represented by a percentage, of the converted material or product which is alkene oxide. The commercial success of a 30 reaction system depends in large measure on the effi-ciency of the system. At present, maximum efficien-cies in commercial production of ethylene oxide by epoxidation are in the low 80s, e.g., 80 or 81 per-cent. Even a very small increase in efficiency will - 35 provide substantial cost benefits in large-scale -3- ~293~9~
operation. For example, taking 100,000 metric tons as a typical yearly yield for a conventional ethylene oxide plant and assuming 80 percent conversion, an increase in efficiency of from 80 to 84 percent, all other things being equal, would result in a savings of 3790 metric tons of ethylene per year. In addi-tion, the heat of reaction for reaction II ~formation of carbon dioxide) is much greater than that of reac-tion I (formation of ethylene oxide) so heat-removal problems are more burdensome as the efficiency de-creases. Furthermore, as the efficiency decreases, there is the potential for a greater amount of impur-ities to be present in the reactor effluent which can complicate separation of the desired alkene oxide product. It would be desirable, therefore, to de-velop a process for the epoxidation of alkene in which the efficiency is greater than that obtained in conventional commercial processes, e.g., with ethy-lene, efficiencies of 84 percent or greater, while maintaining other performance characteristics, parti-cularly the activity, as described below, in a satis-factory range.
The product of the efficiency and the conversion is equal to the yield, or the percentage of the al-kene fed that is converted into the correspondingoxide.
The "activity" of the catalyst is a term used to indicate the amount of alkene oxide contained in the outlet stream of the reactor relative to tha~ in the inlet stream. Activity i5 generally expressed in terms of pounds of alkene oxide produced per cubic foot o~ catalyst per hour at specified reaction con-ditions and rate of feed. The activity may also be stated in terms of the amount of ethylene oxide in 35 the outlet stream or the difference between the ethy--4- 1293~9~
lene oxide content of the inlet and outlet streams.
If the activity of a reaction system is low, then, all other things being equal, the commercial value of that system will be low. The lower the activity of a reaction system, the less product pro-duced in a unit time for a given feed rate, reactor temperature, catalyst, surface area, etcetera. A low activity can render even a high efficiency process com~ercially impractical. For production of ethylene oxide, an activity below 4 pounds of ethylene oxide per hour per cubic foot of catalyst is unacceptable for commercial practice. The activity is preferably greater than 8 pounds, and in some instances an acti-vity greater than 11 pounds of alkene oxide per hour lS per cubic foot of catalyst is desired.
In some instances, activity is measured over a period of time in terms of the amount of alkene oxide produced at a specified constant temperature. Alter-natively, activity may be measured as a function of the temperature required to sustain production of a specified constant amount of alkene oxide. Plots of such measurements yield "aging rates" which reflect the stability or useful life of the catalyst. The useful life of a reaction system is the length of time that reactants can be passed through the reac-tion system during which acceptable activity is ob-served. The area under a plot of activity versus time is equal to the number of pounds of alkene oxide produced during the useful life of the catalyst per cubic foot of catalyst. The greater the area under such a plot, the more valuable the process is since regeneration or replacement of the catalyst involves a number of expenses, sometimes referred to as turn-around costs. The rate at which activity decreases, i.e., the rate of deactivation at a given point in ~ _5~ 3~
time, can be represented by the slope of the activity plot, i.e., the derivative of activity with respect to time:
s deactivation = d[activity~/dt.
The average rate of deactivation over a period of time can be represented then by the change in activity divided by the time period:
average deactivation = a activity/ a t.
At some point, the activity decreases to an unacceptable level, for example, the temperature required to maintain the activity of the system be-comes unacceptably hi~h or the rate of production becomes unacceptably low. At this point, the cata-lyst must either be regenerated or replaced. Some of these definitions may be represented as set out be-~0 low:
Conversion = moles alkene reacted x 1~0moles alkene fed ~ Efficiency = moles alkene oxide produced x 100 moles alkene reacted Typically, in commercial production, since the outlet or~effluent stream emanating from the reactor may contain substantial amounts of unreacted alkene, the effluent stream is recycled and combined with the feedstream after removal of at least a portion of the alkene oxide. Generally, as the activity of a cata-lyst decreases with time, in order to obtain the same ultimate yield of epoxide product, the effluent -6~ 9~
stream must either be recycled a greater number of times or the temperature within the reactor must be raised to increase the activity of the catalyst. The former approach to increasing the yield of product requires additional energy expenditures and the lat-ter, which is most frequently used~ causes faster catalyst deterioration.
As used herein, an activity-reaucing compound refers to a compound which, when present in an acti-vity-reducing amoun~, causes a reduction in activity, some or all of which activity may subsequen~ly be regained by returning to a situation in which the concentration of the compound is below the minimum actLvity-reducing amount. The minimum activity-reducing amount varies depending on the particularsystem, the feedstream and the activity-reducing compound.
Conversely, deactivation, as used herein, refers to a permanent loss of activity, i~e., a decrease in activity which cannot be recovered. As noted above, activity can be increased by raising the temperature, but the need to operate at a higher temperature to maintain a particular activity is representative of deactivation. Furthermore, catalysts tend to deacti-vate more rapidly when reaction is carried out athigher temperatures.
In contrast to problems associated with low or decreasing catalyst activities, less than satisfac-tory efficiencies result in loss of starting mater-ial, the alkene, as the unwanted product CO2. Ulti-mately, this also increases product costs.
To be considered satisfactory, a catalyst must not only have a sufficient activity and the catalytic system provide an acceptable efficiency, but the catalyst must also demonstrate a minimum useful life -7~
or stability. When a catalyst is spent, typically the reactor must be shut down and partially disman-tled to remove the spent catalyst. This results in losses in time and productivity. In addition, the S catalyst must be replaced and the si`,ver salvaged or, where possible, regenerated. Even when a catalyst is capable of regeneration in situ, generally production must be halted for some period of time. ~t best, replacement or regeneration of catalyst requires additional los~es in time to treat the spent catal~st and, at worst, requires replacement of the catalyst with the associated costs.
Since even small improvements in activity, ef-ficiency or useful life may have significance in large scale commercial production, such improvements have been the object of a great deal of research in the direct epoxidation of alkenesO The focus Oe attempts to improve performance, such as the activity and useful life of the catalyst and the efficiency of the system, has included such areas as feedstream additives or removal of components therefrom; methods o~ preparation of the catalyst; deposition or impreg-nation of a particular type or form of silver; com-position, rormation, physical properties and morpho-logy of the support; additives deposited on or im-pregnated in the support; shape of support aggregates used in the reactor; and various types o~ reactors and bed designs, such as stationary and fluidized beds.
Early work on the silver-catalyzed direct oxida-tion of alkenes to alkene oxides in many instances resulted in improvements in activity and particularly the selectively of the system, in many cases the efficiency increasing by several percent. However, recent modifications in such systems have resulted in 13~57 ~ -8- ~3496 only small incremental improvements in efficiency.
In terms of operating cos~s, even fractions of a percent improvement in efficiency can translate into large savings in production. Accordingly, current research is still being directed to improvements in the activity and useful life of the catalyst and selectivi~y of the system.
Although a vast number o~ elements and compounds are known to have effective catalytic properties in 1~ various reactions, many have at least one shortcom-ing, such as very high cost and/or limited availabil-ity, thermal instability in the temperature range in which the reaction is to be conducted, low mechanical strength, small surface area per unit of volume, susceptibility to poisoning, short useful lifetime, etcetera. Such undesirable characteristics make such substances of limited utility as catalys~s. Some of these shortcomings, however, may be overcome and in some instances the effectiveness of the catalyst may be improved by applying the substance to a carrier or support.
New support materials are continuously being tried. ~owever, many of those which were employed in the early development of the silver-bearing catalysts are, with some modifications, still being used.
Materials which have found most widespread use are typically inorganic and generally are of a mineral nature. Such materials commonly include alumina, fire brick, clay, bauxite~ bentoniter kieselguhr, carbon, silicates, silica, silicon carbide, zirconia, diatomaceous earth, and pumice.
In addition to the physical strength of the support materials, other physical properties, such as surface area, pore volume, pore dimensions, and par-ticle size have drawn considerable attention. These 13~57 . ~ ~
3~ 3~
properties have been examined with great scrutinywhen evidence indicated that there was a correlation between the size o~ silver particles and the effici-ency of the overall system or useful life of the catalyst. Some materials are also preferred for their chemical properties, i.e., their "inertness" or "promoting" properties.
The support serves a number o~ functions in a heterogeneous catalytic system. Ease of handling is facilitated by a support which generally takes the form of discrete particles or aggrega~es of varying shape or size which, depending on usage, have a major dimension of about 1 millimeter to about 20 milli-meters~ Thus it is not necessary for the catalyst to form a permanent or semi-permanent part of the reac-tor.
The support, however, serves primarily to in-crease the surface area of the "active" component of the catalyst, silver, which is important in that most epoxidation occurs at the silver surface-fluid inter-face. Many of the substances commonly employed as catalyst supports not only have the usual external surface, which provides a varying surface area, de-pending on the shape of the support bodies and the packing of the bodies, but are also of a porous na-ture and, therefore, have a large internal surface which contributes to the overall surface area of the supported catalyst. Such support materials provide a greater capacity for sorbing not only the catalyst material during catalyst preparation, when the sup-- port is impregnated with a solution containing the catalyst component(s) in soluble form, but also a greater capacity for the flow of the fluid reactants within the catalyst during the reaction for which the catalyst is intended. The support also improves "` lo 1~3~
performance by lo~ering the pressure drop through the reactor and by facilitating heat and mass transfer.
Among the large variety of substances employed in the past as supports for catalytic materials, alumina has exhibited superiority in many respects as a catalyst support material. In addition to the low cost of the material, alumina has good thermal sta-bility and some forms have a relatively large surface area.
Alumina, in its various forms, particularly alpha-alumina, has been preferred as a support mater-ial for silver-containing catalysts in the prepara-tion of alkene oxides. Numerous variations of sur-face area, pore dimensions, pore volume and particle size have been suggested as providing the ideal phys-ical property or combination of properties for im-proving efficiency, activity or useful life of the catalyst.
Holler (U. S. Paten~ 3,908,002) discloses an al-pha-alumina, useful as a catalyst support for reac-tions conducted at temperatures below 800 degrees C, such as oxidation reactions of hydrocarbons to oxyhy-drocarbons. The support, having a surface area re-ported to be at least about 4~ m2/g, is produced by thermally decomposing a porous aluminum ion chain-bridged, polymeric carboxylate. Indicating that a large surface area in a carrier may be detrimental to its efficient operation and catalyst activity, Belon (U. S. Patent 3,172,866) describes a method of pro-ducing a macroporous catalyst carrier which may beused in the catalytic production of ethylene oxide having pore diameters of between 0.1 and 8.0 microns and a specific surface area between a few square meters and one square decimeter per gram. The sup-port is prepared by heating a mixture of active and .
~ 13457 3~
calcined aluminum oxides and a small amount of boronoxide at temperatures of between about 1,600 and 1,800 degrees C. Waterman ~U. SO Patent 2,901,441) describes a process for preparing highly active and selective catalysts for the oxidation of olefins to olefin oxides on a support having an average porosity of at least 35 percent. The method involves washing an alpha-alumina or silicon carbide support having an average porosity of between 35 and 65 percent with an aqueous solution of lactic acid, washing with water until neutral, and then impregnating the support with an aqueous solution of silver lactate. The impreg-nated support is thereafter heat-treated to deposit elemental sllver. A silver-supported catalyst for the vapor phase oxidation of ethylene to ethylene oxide, exhibiting improved production of ethylene oxide and catalyst longevity, is described by Brown et al (U. S. Patent 3,725,307). The catalyst is disclosed as being formed from support particles having an average pore diameter of at least 10 mi-crons up to, preferably, 70 microns and a surface area of less than about l m2/g. The selectivities reported do not range above about 73 percent. The support is preferably composed of silica-alumina. A
silver-supported catalyst which includes a support of alpha-alumina, silicon carbide, fused aluminum oxide, or mixtures of alumina and silica was asserted by DeMaio (U. S. Patent 3,664,970) to eliminate the need for halogenated inhibitors in the oxidation of ethy-lene to ethylene oxide. The support is composed ofparticles having a minimum apparent porosity of about 30 percent and wherein at least 90 percent o the pores have diameters in the range of l to 30 microns, the average of the diameters being in the range of 4 to 10 microns. Wattimena ~U. S. Patent 3,563,914) -12~
discloses silver catalysts using aluminum oxide sup-ports having pore volumes between 15 and 30 ml/g and surface areas below about 10 m2/g.
~ayden et al tU. K. Patent Application 2,014,133) disclose a silver catalyst employing a support having a specific surface area in the range of 0.05 to 10 m2/g, an apparent porosity of at least 20 percent, and mean pore diameters of 0.1 to 20 microns, the pore size distribution being bimodal, in which the smaller pores preferably account for at least 70 percent of the total pore volume. Alpha-alumina supports are described by Rashkin (U. K.
Patent Application 2,122,913A) having a "relatively low surface area" of less than 30 m2/g. Mitsuhata et al (Japanese Published Patent Application 56-089843) and ~itsuhata et al ~U. S. Patent 4,368,144) describe supported silver catalysts in which the support is formed from alpha-alumina having a specific surface area of 0.5 to 5 m2/g. Watanabe et al (Japanese Published Patent Application 56-105750) employ a similar catalyst suppor having a surface area of 1 to 5 m2/g. Hayden et al (U. S. Patent 4,007,135) describe silver-containing catalysts in which the porous neat-resisting support has a specific surface area in the range of 0.04 to 10 m2/g, an apparent porosity of at least 20 percent, and a median pore diameter of 0.3 to lS microns. Mitsuhata et al (U.
S. Patent 4,248,740) describe the use of high alpha-alumina content supports having a specific surface area of not more than 10 m2/g, an apparent porosity of 40 to 60 percent by volume, and a pore volume of 0.1 to 0.5 cc~g. Armstrong et al (U. S. Patent 4,342,667) disclose a supported silver catalyst, useful in the oxidation of ethylene to ethylene ox-3s ide, in which the support has a surface area of 0.02 -13- ~ ~3~
to 2 m~/g, an average pore diameter of 0.5 to 50 microns and an average pore volume of 0.2 to 0 5 cc/g.
There has also been some interes~ in the purity of supports employed, both as to composition and phase. Examples of high purity alumina include U. S.
Patent 2,901,441 which uses alpha-alumina having a purity of about g9.5 percent as a support for cata-lysts used to oxidize olefins to olefin oxides. An ethylene oxidation catalyst is disclosed in German Patent Publication DE 2,933,950 which attains a long catalyst life without a loss in activity or selec-tivity by using an alpha-alumina support having less than 0.001 weight percent of alkali-soluble silicon compounds. The catalyst is prepared by boiling com-mercial quality alpha-alumina with l weight percent sodium hydroxide solution and washing to a pH value of 8. If desired, the silicon compound concentration may be reduced below l part per million (ppm) by washing further with l weight percent HF. U. K.
Patent Application 2,122,913A describes supported silver catalysts in which the support is composed of silica, alumina or mixtures thereof, one example of which is an alumina having a purity of 9~.3 percent by weight. The silver-supported catalyst described in Japanese Published Patent Application 56-089843 employs an alpha-alumina carrier having a sodium content of less than 0.07 weight percent. Japanese Published Patent Application 56-105750 describes the use of an alpha-alumina support in conjunction with a silver catalyst for producing ethylene oxide, which support has a sodium content less than 0.07 weight percent. A silver catalyst including an alpha-alumina carrier having a sodium content of not more ~ 35 than 0.07 percent is described by Mitsuhata et al ':
~ " ~
-14- ~ 3~
~U. S. Patent 4,368,144). The support also has a surface area within the range of 0.5 to 5 m2/g, an apparent porosity of 25 to 60 percen~, a specific pore volume of 0.2 to 0.5 ccjg, and a particle dia-meter within the range of 3 to 20 mm. An alpha-alumina support having a purity of 98~ weight per-cent, for use with silver in the catalytic oxidation of ethylene, is described by Warner et al in U. 5.
Paten~ 4,455,392. The patent additionally discloses that the carrier is generally a conventional micro-porous support with surface areas of less than 10 m2~g, pore volumes ranging from about 0.15 to 0.8 cc/g, and pore diameters of about 0.1 to 100 microns.
In addition to compositional purity, both phase lS purity and morphology of the support have been areas in which improvements in eEficiency, selectivity or stability of the catalyst have been sought. Examples include U. S. Patent 2,901,441 in which aluminum oxide is substantially completely converted to the alpha form of alumina by heating aluminum oxide to a temperature of about 1,500 to 2,050 degrees C. Weiss (U. S. Patent 2,209,908) and Carter tU. S. Patent 2,294,383) d-escribe the use of "Tabular Corundum" as : . a catalyst support for metallic oxides, such as those oxides of metals selected from the fifth and sixth group of the periodic system, for example, vanadium, molybdenum, uranium, etcetera, in the oxidation of various organic materials to maleic acid and maleic anhydride and silver for the catalytic oxidation of ~` 30 ethylene to ethylene oxide, respectively. Weiss indicates that Tabular Corundum, which is almost entirely aluminum oxide and has the alpha-corundum : crystalline form of aluminum oxide, may be formed by mixing aluminum oxide with one or more of several compounds, such as sodium oxide and chromic oxide, : 13457 and heating the mixture to a temperature in the range of about 800 to about 1,800 degrees C. Tabular Co-rundum is further described as having impurities present in only small quantities, the material also includes "readily bonded surfaces and consisting essentially of interlocked corundum crystals in tabu-lar form, having the contained impurities disseminat-ed in minute globules throughout the crystalline aluminan. Brengle et al (U. S. Patent 2,709,173) also employ Tabular Corundum as a support in one of their examples.
U. S. Patents 4,039,481 and 4,136,063 to Kimura et al disclose a catalyst carrier and a method for making same, the catalyst being the type used in catalytic converters in automobile exhaust systems.
Specifically, the catalysts have a surface layer containing alpha-phase alumina and an inner portion consisting essentially of alumina of a phase other than that of the alpha phase. The pores in the al-pha-alumina surface layer are larger than those in the inner portion of the catalyst body. A method of preparing the phase gradient support particles is described which provides for treating the surface of the alumina to a depth o about 400 microns with a transition element, particularly iron, and thereafter firing the carrier particles.
Weber et al ~U. S~ Patent 4,379,134) describe high purity alpha-alumina bodies, at least 85 percent of the pore volume of the bodies having pores with a diameter of from 10,000 to 200,000 Angstroms. The high purity alpha-alumina bodies are prepared by peptizing boehmite in an acidic aqueous, fluoride anion-containing mixture. An extrudable mixture is formed thereby which is extruded and shaped into formed bodies which are thereafter dried at 100 to -16~ 36 300 degrees C, calcined at a temperature of from 400 to 700 degrees C to convert the alumina to the gamma phase, and subsequently calcined further at a temper-ature of from 1,200 to 1,700 degrees C to convert the gamma phase to alpha-alumina phase.
A method of producing granulated porous corundum having a homogeneous porous structure with a total pore volume of 0.3 to 1.0 cm3/g and a predominant pore size of 5,000 to 30,000 A is described by Bores-kov et al (U. S. Patent 3,950,507). The method opreparing the alpha-alumina includes treating active alumina or aluminum hydroxide having a porous struc-ture to a first heat treatment in which the tempera-ture is increased from 20 to 700 degrees C, a second heat treatment in the range of from 700 to 1,000 degrees C, and a third treatment in the range of from l,OU0 to 1,400 degrees C. Each of the heat treat-ments is for a period of at least one-half hour, the first heat treatment being conducted in an atmosphere of hydrogen 1uoride in which the alumina absorbs the hydrogen fluoride and the second heat treatment de-sorbs the hydrogen fluoride. The patent also de-scribes a similar procedure employing stationary thermal conditions in which the granules of alumina or aluminum hydroxide are impregnated with other fluorine-containing compounds prior to the first thermal treatment. The recommended starting mater-ials used to form alpha-alumina include granulated pseudo-boehmite, boehmite or bayerite as the granu-lated aluminum hydroxide and granulated alpha-, eta-, or theta-alumina as the ac~ive alumina.
Although alpha-alumina has been considered by most to be the preferred alumina support material, ; Smith e~ al (U. S. Patent 2,422,172) have suggested that beta-aluminas are more desirable than the alpha -17- ~ ?3~
phase as a support material for catalysts, particu-larly those used in catalytic conversion processes such as dehydrogenation and hydroforming.
In seeking the ideal support material, there has S been some departure from the commonly employed sub-stances. For example, some use has been made of alkali metal and alkaline earth metal carbonates, both as the sole support material and in combination with other materials as the carrier for processes such as direct oxidation of alkenes to epoxides.
A number of supported silver-containing cata-lysts have been employed for epoxidation of alkenes in which the carrier includes, sometimes labelled as a promoter, a carbonate of a metal, generally an alkali metal or alkaline earth metal. Some examples of the use of one or more al~ali and/or alkaline earth carbonates may be found in U. S. Patents 2,424,084, 2,424,086, 2,615,900, 2,713,586, 3,121,099, 3,258,433, 3,563,913, 3,563,914, 3,585,217, 4,007,135, 4,033,9~3, 4,039,561, - 4,~66,575, 4,094,889, 4,123,385, 4,125,480, 4,168,247, 4,186,1~6, 4,226,782, 4,229,321, 4,324,699, European Patent Publications 0,003,542 and 0,011 .' " Japanese Patents 41-11847 and 57-107242, U. K. Patents 590,479, 1,571,123 and 2,014,133A, and Murray, "A Study Of The Oxidation Of Ethylene To Ethylene Oxide On A Silver Catalyst~, Australian 3Ournal of Scientific Research, Volume 3A, Pages 433-; 449 (1950). In additionl U. S. Patent 3,332,837 ; 30 employs zinc and/or cadmium carbonates, Gelbstein, (DS 2,352,608) aiscloses the use of the latter car-bonate and European Patent Publication 0,003,642 mentions the use of molybdenum carbonate.
Several patents have described the use of fluo-rine-con~aining co~pounds to treat support materials, in some cases to provide a compositionally pure sup-port, and in other cases as a fluxing agent to im-prove the phase purity of the support. Thus, U. R.
Published Patent Specification 590,479 and U. S.
Patent 2,424,086 indicate that a more active catalyst is formed if the support material ha~ undergone a preliminary treatment with a dilute solution of hy-drofluoric acid prior to impregnation with silver.
U. S. Patent 4,379,134 teaches the preparation of high purity alpha-alumina bodies by peptizing boeh-mite alumina in an aqueous acidic mixture containing fluoride anions and water. German Patent 2,933,950 teaches the reduction of silicon content by treatment with HF. U. S. Patent 3,950,507 teaches the prepara-tion of granulated porous corundum by a multiple stepheat treatment in which initial steps may be carried out in an atmosphere of hydrogen fluoride. Hosoda et al (U. S. Patent 3,144,416) suggest that a small amount o~ a halogen compound, sulfur compound, nitro-gen compound, or phosphorous compound may be addedeither to the reaction gas or the catalyst to improve the selectivity of the catalyst.
The nature of the silver itself has also been examined and modified in attempts to impro~e the ef f iciency and stability of the catalyst. Cavitt (U.
S. Patent 4,229,321) teaches that a supported silver catalyst of improved selectivity and activity may be prepared by mechanically removing the outer surface or skin of the catalyst after the impregnated cata-lyst has been heated to évaporate volatile materialand reduction of the silver salt to silver metal, thereby activating the catalyst.
Since the early work on the direct catalytic oxidation of ethylene to ethylene oxide, workers in the field have suggested that the addition of certain -19- ~Z~3~
compounds to the gaseous feedstream or direct incor-poration of metals or compounds in the catalyst could enhance or promote the production of ethylene ox-ide. Such metals or compounds have been known vari-ously as "anti-catalysts", "promoters" and "inhi-bitorsn. These substances, which are not themselves considered catalysts, have been proposed by prior workers to contribute to the efficiency of the pro-cess by inhibiting the formation of carbon dioxide or promoting the production of ethylene oxide. The scientific literature is replete with examples o the use of alkali metals and alkaline earth metals and their cations to promote the efficiency of silver catalysts used in epoxidation reactions. For exam-ple, ~odium, potassium and calcium were disclosed asbeing suitable promoters in U. S. Patent 2,177,361.
Numerous examples may be found in literature of pref-erence for one or several metals or cations and ex-clusion of one or more metals or cations as promoters in silver catalysts.
~; Among those anions associated with the cation used in preparing silver-con~aining catalysts em-ployed in direct epoxidation reactions that have been suggested as being suitable include carboxylates, for example, formate, acetate, malonate, oxalate, lac-tate, tartrate, and/or citrate, and inorganic salts, such as carbonates, bicarbonates, phosphates, ni-trates, and/or nitrites, chlorides, iodides, bro-mates, and isopropoxides. However, although many examples may be found in the literature indicating that such compounds are suitable, numerous patents, such as U. S. Patents 3,962,136; 4,012,425;
4,066,575; 4,207,210; and 4,471,071, suggest that no unusual effectiveness, particularly with regard to catalytic activity, is observed with any particular ~3~
anion of an alkali metal promoter. U. S. Pa~ents 4,007,135; 4,094,889; 4,125,480; 4,226,782;
4,235,757; 4,324,699; 4,342,667; 4,356,312;
4,368,144; and 4,455,392 disclose that potassium nitrate may be added to the catalyst as a suitable promoting ma~erial. Potassium nitrat:e may also be formed in situ when a carrier material is treated with certain amines in the presence of potassium ions as, for instance! when silver is introduced to a 1~ carrier material in a silver-impregnating solution containing an amine and potassium ions, followed by roasting.
A number of compounds have been proposed in the literature as additives to the feedstream or reactants to improve the efficiency of the direct, silver-catalyzed oxidation of alkenes to alkene oxides. For example, Law and Chitwood ~U. S. Patene 2,194,602) disclose the use of a "repressantr, i.e., anti-catalyst, such as ethylene dichloride, ch~orine, 2~ sulfur chloride, sulfur trioxide, nitrogen dioxide, or other halogen-containing or acid-forming mater-ials. Numerous additional anti-ca~alysts are pre-sented by the same patentees in U. S. Patent 2,279,469. The anti-catalysts, broadly listed in categories such as halogens and compounds containing halogen, hydrocarbons, compounds containing carbon, hydrogen and oxygen, compounds containing sulfur, and compounds containing nitrogen are represented and, in addition to those compounds already mentioned above, additional representative compounds include, as ni-trogen-containing compounds, nitric oxide, ammonia, amines such as ethylenediamine, diphenylamine and analine, nitro compounds such as o-nitroanisole and o-nitrotoluene as organic oxygen-containing organic compounds, alcohols such as methyl, ethyl and iso-propyl alcohols~ ethers such as isopropyl and dibutyl ethers, as well as glycol ekhers, ketones such as methyl ethyl ketone and acetone, as hydrocarbons such as benzene, and N-hexane; sulfur compounds such as sulfur dioxide, hydrogen sulfide and diethylsulfide;
chlorine-containing compounds such as carbon tetra-chloride, chlorobenzene and dichloroethyl ether.
Berl (U. S. Patent 2,270,780) lists a number of com-pounds as anti-detonating or anti-knock materials to control the oxidation of ethylene and propylene to their oxides. Oisclosures of other feedstream addi-tives used in the production of alkene oxides, parti-cularly halogen compounds, may be found in U. S.
Patents 2,279,470; 2,799,687; 3,144,416; 4,007,135;
4,206,128; and 4,368,144. In addition, EPO Patent 0,003,642 and U. R. Patent Application 2,014,133A
disclose processes for the production of olefin ox-ides employing silver-containing catalysts in which a chlorine-containing reaction modiier and a nitrite or nitrite-forming substance are described. Rumanian Patent 53,012, published December 2, 1971, discloses a direct, silver-catalyzed direct epoxidation proce-dure which employs oxides of nitrogen in the feed-stream. U. K. Patent 524,007 includes ethylene di-chloride or nitrogen dioxide in the feedstream of a silver-catalyzed epoxidation procedure.
Although much of the art discussed above has resulted in improvements in the efficiency, activity or stability of the catalytic system, many of the -22- lZ~3~
improvements have individually been rather slight.
In some of the catalytic systems, gains in one of these performance parameters have been frequently offset by losses in another; that is, enhancement of one index of performance has been accompanied by a deleterious effect on another of the indices. For example, if a reaction system is designed which has a very short useful life, the system may be commer-cially impractical even though the efficiency and initial activity o the catalyst are outstanding.
Accordingly, a system that provides an increase in the efficiency of the overall catalytic reaction system, while only minimally affecting the activity and useful life of the catalyst, or perhaps increas-ing one o these performance indices, would be parti-cularly bene~icial.
The presence of leachable sodium in a silver catalyst employed for epoxidation tends, in some instances, to improve the efficiency of the system ~20 under epoxidation conditions generally used. In the ;presence of CO2 and certain efficiency-enhancing compounds, however, sodium exhibits deactivating and effective life-shortening effects on epoxidation ca~,ysts and systems. The loss of stability or life-shortening effect may be so marked, particularly when the sodium is added as a promoter, that any gains in efEiciency provided by the sodium are lost several days after the catalyst is placed in ser-vice. In many commercially used epoxidation reactors the effluent stream contains relatively high propor-tions of unreacted alkene. To diminish losses of the alkene, the effluent stream is recycled and i~tro-duced to the reactor with the feedstream. Since efficiency in such reactions never reaches 100 per-cent, the effluent stream al~ays contains some carbon ~ -23~ 3~r~
dioxide. In a reactor in which the effluent stream is recycled to the reactor, therefore, the feedstream always contains some carbon dioxide which, in combin-ation with sodium and certain efficiency-enhancing compounds, results in losses of activity and stabil-i~y of the catalyst and system. Commonly, the carbon dioxide is removed by a scrubbing device, such as a Benfield scrubber, placed in the effluent stream between the effluent outtet and the reactor inlet.
Such devices require, however, a substantial capital expenditure and additional plant space. The catalyst and process of the present invention diminish the deactivating and life-shortening effects of CO2.
Disclosure Of The Invention:
The present invention is directed to a high ~; performance catalytic process for epoxidation of alkene in the presence of an oxygen-containin~ gas which comprises contacting the alkene and the oxygen-containing gas under epoxidation conditions in the ; presence of at least one efficiency-enhancing gaseous member of a redox-half reaction pair and a solld catalyst. The catalyst contemplated by ~ present ; 25 invention comprises a catalytically-effective amount of silver on a solid support and an efficiency-enhancing amount of at least one efficiency-enhancing salt of a member of a redox-half reaction pair. The support has less than about 50 and most frequently less than about 20 parts per million, by weightj of leachable sodium.
The invention, described in greater detail be-low, is also directed to a catalyst suitable for use in a process in which an epoxide is formed from an alkene. The catalyst of the present invention, as -24- ~ 3~9~
suggested above, comprises a catalytically-effective amount of silver on 3 substantially inert support and an efficiency-enhancing amount of at least one effi-ciency-enhancing salt of a member of a redox-half reaction pair. The support contains less than about 50 and most frequen~ly less than about 20 parts per million, by weight, of leachable sodium.
The present invention provides a catalytic sys-tem which includes a stable catalyst even when used with recycled effluent streams containing carbon dioxide. In some aspects, the present invention allows a collateral benefit in that it obviates the need for a costly scrubbing unit in the effluent stream while still maintaining desired efficiencies and activities ~or useful periods of time.
In additlon to providing an enhanced stability, the present invention also furnishes an additional benefit of enhanced efficiency.
2~ Brief Descri~on Of The Drawings-Figure 1 is a graphical comparison of aging rates or plo~s of activity (percent ethy~ene oxide in the outlet) of a catalyst according to the present invention having low sodium and one having 80 ppm sodium;
Figure 2 is a graphical comparison similar to Figure 1 comparing a catalyst having 40 and 100 ppm of sodium, respectively, and a feedstream having 3 percent CO2; and Figure 3 is a graphicaI comparison of the cata-lysts and conditions o~ Figure 2 in which effi~ien-cies are compared.
:, -25- ~Z~3~
Detailed DescriPtion Of The Invention:
The present invention is directed to a process for the vapor phase oxida~ion of alkenes to alkene 5 oxides, i.e., an epoxidation process, in the presence of an oxygen-containing gas and to the silver cata-lysts employed therein.
The process and catalyst of the present inven-tion are useful in the epoxidation of the alkenes 10 ethylene and propylene, the epoxides of which are in great demand for use as intermediates in producing such materials as polymers, surfactants, synthetic fibers and antifreeze. However, the present inven-tion is not limited to these compounds but may be used to oxidize cyclic and acyclic alkenes which are in the gaseous state or have signiicant vapor pres-sures-under epoxidation conditions. Typically these compounds are characterized as having on the order of 12 carbon atoms or less which are gaseous under epox-idation conditions. In addition to ethylene andpropylene, examples of alkenes which may be used in the present invention include such compounds as bu-tene, dodecene, cyclohexene, 4-vinylcyclohexene, sty-rene and norbornene.
Supeort:
The support material used in the present inven-tion may be any solid! porous, reractory material which can withstand the roasting temperatures, if that is the method employed to reduce the silver to its free metallic state, and which can also withstand the temperatures employed within the reactor during the epoxidation process. Regardless of the method used to reduce the silver, the support should also be ~ -26-~3~316 able to withstand the temperatures employed within the reactor under epoxidation process conditions.
The support should not have any undue deleterious effect on the performance of the system. Examples of - S suitable materials include magnesia~ zirconia, sili-ca, silicon carbide, and alumina, preferably alpha-alumina.
The carrier materials of the present invention may generally be described as porous or microporous, 10 having median pore diameters of about 0.01 to about 100 microns, preferably about 0.5 to about 50 mi-crons, and most preferably about 1 to about 5 mi-crons. Generally, they have pore volumes of about 0.6 to about 1.4 cc/g, preferably about 0.8 to about 15 1.2 cc/g. Pore vol~lmes may be measured by any con-ventional technique, such as conventional mercury porosity or water absorption technique.
Generally improved results have been demon-strated when the support material is compositionally pure and also phase pure. By "compositionally pure"
is meant a material which is substantially a single substance, such as alumina, with only trace impuri-ties being present. "Phase purity" or like terms refer to the homogeneity of the support with respect to its phase. In the present invention, alumina, having a high or exclusive alpha-phase purity (i.e., alpha-alumina), is preferred. Most preferred is a material composed of at least 98 percent, by weight, of alpha-alumina. Under some conditions, as when used in conjunction with the salt and gaseous members of redox-half reaction pairs, even small amounts of sodium can adversely affect the activity and useful life of the catalyst, i.e., have a deactivating ef-fect on the catalyst. Improved results have been observed when the support contains leachable sodium -27~
levels less than about 50 parts per million (ppm) by weight, preferably less than about 40 ppm, based on the weight of the to~al support. Most preferred are supports having a leachable sodium content of less 5 than about 20 ppm, by weight. Supports which are also useful in the present invention are those having less than a catalyst deactivating amount of ~otal sodium. This corresponds in some instances to a concentration of about 200 ppm. Suitable alpha-10 aluminas having concentrations of leachable sodiumbelow 50 ppm may be obtained commercially from sup-pliers, such as the Norton Company.
The low sodium carrier materials of the present invention may be prepared by any conventional method L5 of removing sodium from a solid, particularly mineral or mineral-type material suitable in other respects as a support material. Such treatment should not, however, substantially adversely affect the mechani-cal O structural characteristics of the support material nor chemically alter the support material in a manner which adversely affects the catalytic per-formance indices of efficiency, activity, or catalyst stability. Typically, the techniques involve extrac-~L~n and/or volatilization of the sodium present. A
suitable extraction procedure may involve conversion of the sodium present to a more easily extractabIe material either in the same step in which extraction takes place or in separate conversion and extraction steps. A suitable volatilization procedure typically 3~ includes an initial step in which the sodium present in the support is converted to a material which is volatile upon heating. In some instances, it ~ay be preferable to initially extract as much of the sodium present as possible, followed by a volatilization procedure to remove-residuaI sodium. Exemplary of .~ .
~ 13457 ~2~3~L9~
extrac~ion or leaching procedures is treatment of the support material with a mineral acid, particularly nitric acid in a concentration of about 10 percent, by volume, at a temperature of about 90 degrees C, 5 for a period of about l hour and thereafter washing the support with water. The rinsed support material i5 then dried at a temperature of from abou~ lO0 to 1,000 degrees C for a period of from about 1 to about 3 hours. The leaching procedure described above also 10 forms the basis of a method of analysis of ~leachable sodium~ and the definition of this term.
Alternatively, suitable alpha-alumina support materials may be prepared so as to obtain sodium concentrations below 50 ppm by the method described 15 by Weber et al in U. S. Patent 4,379,134.
A preferred procedure for preparing a low-sodium support involves treatment of a support material, particularly gamma-alumina, with an organic or inor-ganic fluorine-co~taining substance, preferably in aqueous solution, and thereafter firing the treated support material at a suitable temperature. In the present invention, the support material may either be extruded by conventional techniques known to the art and formed into pellets after fluori~.~ reatment and before firing or, alternatively, formed, i.eO, ex-truded, pellets may be fluorine-treated and then fired. The fluorine-containing substance i9, prefer-ably, a volatile material or one which can be readily volatilized under firing conditions. Examples of ~ suitable fluorine-containing materials include alumi-num trifluoride, ammonium fluoride, hydrofluoric acid, and dichlorodifluoromethane.
The fluorine compound is used in an amount suf-ficient to remove a major portion of the sodium ; 35 present in the sample. This amount will, o~ course, 33~
vary with the amount of sodium present in the sample but will also depend on other factors, such as the condition under which the support material is treated, such as the firing temperature and heating S rate, as well as the depth of ~he b~d of material being treated, the amount of gamma-alumina being treated, the level of contamination of the gamma-alumina, and how well the firing chamber is sealed.
Typically, a suitable amount of fluorine compound is 10 not more than about 3 percent, by weight, based on the weight of the support material being treated.
Preferably, the fluorine compound is present in an amount of about 0.8 to about 2 percent, by weight. A
suitable firing temperature for fluorine-treated alumina is generally less than about 1,200 degrees C, preferably from a temperature over 750 to about 1,100 degrees C. The rate of heating depends in part on the amount of fluorine compound used. Thus, with lower levels of fluorine, support materials having desirable properties are generally obtained with rapid heating. As used herein, "rapid heating"
; refers to heating from room temperature to the - desired temperature in about 1 hour. However, with lower concentrations of fluorine compound, slower heating rates are yenerally preferred to achieve the same type of product. The "slow heating" treatments generally consist of heating from room temperature to about 750 degrees C in about 0.5 to 1 hour and from 750 degrees C to the final temperature at a rate of about 100 degrees C per hour.
The treatment of support materials with fluo-rine-containing substances may provide a collateral benefit in converting the support material to one having a preferred "platelet" morphology. This sup-port is described by Notermann in an application .
~ 30 ~3~
entitled "Improved Catalytic System for Epoxidationof Alkenes", in Canadian Application No. 515,865, filed August 13, 1986, in the name of Thomas M.
Notermann.
The support particles are preferably formed into aggregates or "pills" of a size and configuration to be usable in commercially operated ethylene dioxide tubular reactors. These pills may be formed by conventional extrusion and firing, as discussed above. When gamma-alumina is the precursor to an alpha-alumina support material, treatment with the fluorine recrystallizing agent may be preformed before or after extrusion. The pills generally range in size from about 2 mm to about 15 mm, preferably about 3 mm to about 12 mm. The size is chosen to be consistent with the type of reactor employed. In general, in fixed bed reactor applicationsJ sizes ranging from about 3 mm to about 10 mm have been found to be most suitable in the typical tubular reactors used in commerce. The shapes of the carrier aggregates useful for purposes of the present invention can vary widely. Common shapes include spheres and cylinders, especially hollow cylinders.
Other shapes include amphora (such as defined in U.S.
Patents 3,848,033, 3,966,639 and 4,170,569), amorphous, Raschig rings, saddles, cross-partitioned hollow cylinders (e.g.~ having at least one partition extending between walls), cylinders having gas channels from side wall to side wall, cylinders having two or more gas channels, and ribbed or finned structures. While the cylinders are often circular, other cross-sections, such as oval, hexagonal, quadrilateral, trilateral, etcetera, may be useful.
.~, ~ 13457-C
,A.
-31- ~3~6 Ca~alysts:
The catalysts of the present invention are con-ventional to the extent that silver is coated or deposited on and/or within a solid porous carrier.
Any known method of introducing the silver to the catalyst support may be employed. Numerous examples and procedures are given in the patents discussed above. In brief, in a coating or suspension process a slurry, preferably aqueous, of ~he active catlytic material, such as silver or its oxide, is applied to the support to form a coherent silver layer on the support. In the preferred impregnation process, a solution of a soluble salt or complex of silYer in an amount sufficient to deposit the desired weight of silver upon the carrier is dissolved in a suitable solvent or "complexing/solubilizing~ agent. This solution may be used to impregnate a porous catalyst support or carrier by immersing the carrier in the silver-containing impregnating solution. Alterna-tively, the support may be sprayed or sprinkled with the impregnating solution. The excess solution may then be allowed to drain off or the solvent may be removed by evaporation under reduced pressure at a suitable temperature. The silver salt or compound used to form the silver-containing impregna~ing solu-tion in a solvent or a complexing/solubilizing agent is not particularly critical and any silver salt or compound generally known to the art which is both soluble in and does not react with the solvent or complexing/solubilizing agent to form an unwanted product may be employed. Thus, the silver may be introduced to the solvent or complexing/solubilizing agent as an oxide or a salt, such as nitrate or car-boxylate, for example, an acetate, propionate, buty-,9~i rate, oxalate, malonate, malate, maleate, lactate,citrate, phthalate, generally the silver salts of higher fatty acids, and the like.
The chemical practitioner may choose from a 5 large number of suitable solvents or complexing/solu-bilizing agents to form the silver-containing impreg-nating solution. Besides aaequately dissolving the silver or converting it to a soluble form, a suitable solvent or complexing/solubilizing agent should be 10 capable of being readily removed in subsequent steps, either by a washing, volatilizing or oxidation proce-dure, or the like. The complexing/solubilizing agent, preferably, should also permit solution to provide silver in the finished catalyst to the extent of about ~ to about 60 percent silver or higher, based on the total weight of the catalyst. It is also generally preferred that the solvents or com-plexing/solubilizing agents be readily miscible with water since aqueous solutions may be conveniently em-ployed. Among the materials found suitable as sol-vents or complexing/solubilizing agents for the pre-paration the silver-containing solutions are alco-hols, including g]ycols, such as ethylene glycol ~U. S. Patents 2,825,701 to Endler et al and 3,563,914 to Wattimena), ammonia ~U. S. Patent 2,463,228 to West et al), amines and aqueous mixtures of amines (U. S. Patents 2,459,896 to Schwartz, 3,563,914 to Wattimena, 3,702,259 to Nielsen, and 4,097,414 to Cavitt, and carboxylic acids, such as lactic acid (U. S Patents 2,477,435 to ~ries and 3,501,417 to DeMaio) Typically, a silver-containing solution is pre-pared by dissolviny silver in a suitable solvent or complexing/solubilizing agent as, for example, a mixture of water, ethyienediamine, oxalic acid, sil-ver oxide, and monoethanolamine. The solution is then mixed with support particles and drained.
Thereafter the particles are suitably dried.
After impregnation, the silver-impregnated car-S rier particles are treated to convert the silver salt or complex to silver metal and thereby effect deposi-tion of silver on the surface of the support. As used herein, the term "surface", as applied to the support, includes not only the external surfaces of 10 the carrier but also the internal surfaces, that is, the surfaces defining the pores or internal portion of the support particles. This may be done by treat-ing the impregnated particles with a reducing agent, such as oxalic acid or alkanolamine and/or by roast-ing, at an elevated temperature on the order oE about100 to about 900 degrees C, preferably about 200 to about 650 degrees C to decompose the silver co~pound and reduce the silver to its free metallic state.
The duration of roasting is generally for a period of about 1 to about 10 minutes for temperatures above 200 degrees C, depending on the temperature used, and is commonly effectuated in a hot-air belt roaster.
The concentration of silver in the finished catalyst may vary from about 2 per~ to 60 percent, by weight, based on the total weight of the catalyst, more preferably the silver concentration ranges from about 8 percent to about 5~ percent, by weight. When a ~high silver" content catalyst is preferred, the silver ranges from about 30 to about 60 percent, by weight. The preferred concentration for "low silver"
content catalysts ranges from about 2 to about 20 weight percent. When a catalyst having a silver concentration in the preferred high silver range is prepared, the silver is preferably introduced in a series of at least two sequential impregnation and ~` -34- ~3~
roasting cycles, as discussed in greater detail be-low. Lower silver concentrations are preferred from a capital expense standpoin~. Xowever, the optimum silver concentration for a particular catalyst should also take into consideration increased productivity resulting from performance characteristics, such as catalyst activity, system efficiency and the rate of catalyst aging. In many instances higher concentra-tions of silver are preferred since they demonstrate levels of enhanced performance, particularly catalyst stability, which compensates for the greater capital expenditure.
Efficiency-Enhancinq Compound:
A preferred aspect of the present invention includes an efficiency-enhancing amount of at least one efficiency-enhancing salt of a member of a redox-half reaction pair. The term "redox-half reaction"
~`20 is defined herein to mean half-reactions like those found in equations presented in tables of standard reduction or oxidation potentials, also known as standard or single electrode potentials, of the type ;found in, for instance, "~andbook of Chemistry", N.
A. Lange, Editor, McGraw-Hill Book Company, Inc., pages 1213-1218 (1961) or "CRC Handbook of Chemistry and Physics", 65th Edition, CRC Press, Inc., Boca Raton, Florida, pages D155-162 (1984). The term nredox-half reaction pair" refers to the pairs of atoms, molecules or ions or mixtures thereof which undergo oxidation or reduction in such half-reaction ~equations. Such terms as redox-half reaction pairs -are used herein to include those members of the class of substance which provide the desired performance ~35 enhancement, rather than a meshanism of the chemistry :
occurring. Preferably, such compounds, when associ-ated with the catalyst as salts of members of a half reaction pair, are salts in which the anions are oxyanions, preferably an oxyanion of a polyvalent 5 atom, that is, the atom of the anion to which oxygen is bonded is capable of existing, when bonded to a dissimilar atom, in different valence states. Potas-sium is the preferred cation and the preferred anions are nitrate, nitrite and other anions capable of lO undergoing displacement or other chemical reaction and forming nitrate anions under epoxidation condi-tions. Preferred salts include KN03 and KN02, with KN03 being most preferred.
Introduction 0~ Ef~iciency-Enhancing Salt To The Carrier:
The efficiency-enhancing salt of a member of a redox-half reaction pair may be introduced to the catalyst in any known manner. Various sequences of impregnating or depositing silver and efficiency-enhancing salt on the surfaces of the carrier may be employed. Thus, impregnation and deposition of sil-ver and an efficl~ncy-enhancing salt of a member of a redox-half reaction pair may be effected coinciden-tally or sequentially, i.e., the salt or salts may be deposited prior to, during or subsequent to silver addition to the carrier. When more than one salt of a member of a redox-half reaction pair is employed, they may be deposited together or sequentially.
Typical, and in many cases preferred, of such~me~hods include concurrent, or coincidental, impregnation in which the solution which is used to impregnate the support with silver also contains the dissolved effi-ciency-enhancing salt member of a redox-half reaction pair. This procedure permits introduction of both the silver compound and the efficiency-enhancing salt to the support in a single step and solution. The other commonly employed method is the sequential impregnation of the support in which initial intro-duction of the silver-containing solution or effi-ciency-enhancing salt solution (depending upon the sequence employed) is followed by drying o the sil-ver-containing support (and heating and/or chemical reduction of the silver if this is the first added substance). This support is then impregnated with a solution of the second substance, that is, the effi-ciency-enhancing salt (if the silver was the first added substance). In order to perform the former L5 procedure, i.e., coincidental impregnation, the effi-ciency-enhancing salt must be soluble in the same solvent or complexing/solubilizing liquid used with the silver-impregnating solution. With the sequen-tial procedure in which the silver is added firstl any solvent capable of dissolving the salt which will neither react with the slIver nor leach it from the support is suitable. Aqueous solutions are generally preferred, but organic liquids, such as alcohols, may also be employed. Suitable procedures for effectin~
introduction of the efficiency-enhancing salt to the solid support may be found in many of the patents listed above.
In some instances, the coincidental method of preparation of the catalyst is decidedly less prefer-red or may not be used as, ~or examptel where a bari-um, calcium or magnesium salt is intended to be solu-bilized and the solution contains materials which may precipitate the cation as, for instance, a carboxylic acid or dicarboxylic acid such as oxalic acid.
; 35 ~37~ 1 Z ~3 ~
The salt of a member of a redox-half reaction pair is added in an amount sufficient to enhance the efficiency of the epoxidation reaction. The precise amount will vary depending u~on such variables as the 5 gaseous efficiency-enhancing member of a redox-half reaction used and concentration thereof, the concen-tration of other components in the gas phase, the amount of silver contained in the catalyst, the sur-face area of the support, the process conditions, 10 e.g., space velocity and temperature, and morphology of support. Generally, however, a suita~le range of concentration of the added efficiency-enhancing salt, calculated as cation, is about 0.01 to about 5 per-cent, preferably about 0.02 to about 3 percent, by weight, based on the total weight of the catalyst.
Most preferably the salt is added in an amount of about 0.03 to about 2 weight percent.
It has been noted that when conventional analyses have been conducted with catalysts prepared by co-impregnation with silver and efficiency-enhancing salt, not all the anion associated with the cation has been accounted for. For example, cata-lysts prepared by co-impregnation with a potassium nitrate solution have been analyzed by conventional techniques and about 3 moles of the nitrate anion have been observed for every 4 moles of the potassium cation. This is believed to be due to limitations in the conventional analytical techniques and does not ~ necessarily mean that the unaccounted for anions are not nitrate. For this reason, the amount of the efficiency-enhancing salt in the catalyst is given, in some instances, in terms of the weight percentage of the cation of the efficiency-enhancing salt (based on the weight of the entire catalyst), with the un-derstanding that the anion associated with the cation ~ 13457 :~
, ~ -38- ~93~9~
is also present in the catalyst in an amount roughly proportional (on a molar basis) to the ca~ion.
As indicated above, when the catalyst is in-tended to contain higher concentrations of silver, it S is generally preferred to use multip}e cycles of impregnation and reduction to elemental silver. This seems to result in a more uniform distribution of silver throughout the catalyst pill. As with the catalyst containing lower amounts of silver intro-1~ duced in a single impregnation, the introduction ofthe efficiency-enhancing salt of a member of a redox-half reaction pair may also be introduced in a se-quential or coincidental procedure. Regardless of the method employed, a first cycle includes impregna-5 tion only with silver in an appropriate complex-ing/solubilizing agent followed by reduction to metallic silver, such as by roasting. (This is known as a "silver only" procedure.) If the sequential procedure is to be followed, the first cycle of im-20 pregnation and reduction is repeated one or more times. The final step includes impregnation with a solution of the efficiency-enhancing salt of a member of a redox-half reaction pair, draining and drying, as discussed above.
When the coincidental or concurrent procedure is employed in preparing catalysts containing high con-centrations of silver, the first cycle is the same as in the sequential technique, i.e., a silver only procedure~ This is then followed either directly by 3~ a conventional coincidental impregnation (i.e., im-pregnation with a solution containing both silver in a soluble form and the efficiency-enhancing salt of a member of a redox-half reaction pair, followed by a reduction of silver to its elemental form, as by roasting) or by one or more repetitions of the im-~ _39- .~ 3~
pregnation cycle with a silver only procedure inter-posed between the silver only cycle and the coinci-dental impregnation and reduction cycle with a solu-tion of silver and at least one efficiency-enhancing salt. Suitable results have been obtained with both the sequential and coincidental procedures with two silver impregnation cycles, although there are indi-cations that greater amounts of silver with more uniform distribution of silver throughout the pill can be obtained by three or possibly more silver-impregnation cycles. High silver-containing cata-lysts prepared by the coincidental impregnation tech-nique provide somewhat better performance than those prepared by the sequential technique.
EpoxidatLon Procedure:
As in conventional processes of this type, an alkene and an oxygen-containing gas are brought to-gether in a reactor in the presence of a suitableepoxidation catalyst under epoxidation conditions.
Typical epoxidation conditions include temperatures within the reaction zone of the reactor on the order of about 180 to 300 degrees C and pressures from about 1 to about 30 atmospheres.
The gaseous eficiency-enhancing member of a redox-half reac~ion pair may generally be supplied to the reaction zone within the reactor by introducing the component to the feedstream containing alkene and oxygen Under commercial epoxidation conditions, such as those used in the present invention, the feedstream also contains a gas phase halogen com-pound, such as an alkyl halide, a hydrocarbon, and, when the effluent stream from the reactor is recy-cled, unreacted alkene. When recycle of the eefluent -~ _40~ 3~
stream is used, carbon dioxide may also be present.
The presence and amount of carbon dioxide depends, at least in part, on whether a scrubbing device is em-ployed.
The terms "gaseous member of a redox-half reac-tion pair~, "gaseous efficiency-enhancing member o~ a redox-half reaction pair", or like terms referred to herein have a meaning similar to that for the "sal~
of a member of a redox-half reaction pair" or like terms, defined above. That is, these terms refer to members of half-reactions, represented in standard or single electrode potential tables in standard refer-ence texts or handbooks which are in a gaseous state and are substances which~ in the reaction equations lS represented in the texts, are either oxidized or re-duced~ The preferred gaseous efficiency enhancing materials are compounds containing an element capable o~ existing in more than two valence states, prefer-ably nitrogen and another element which is, prefer-ably, oxygen. Examples of preferred gaseous effi-ciency-enhancing members of redox-half reaction pairs include at least one of NO, NO2, N2O4, N2O3 or any gaseous substance capable of forming one of the aforementione~ gases, particularly NO and NO2, under ~5 epoxidation conditions, and mixtures of one of the foregoing, particuIarly ~O, with one or more of PH3, CO, SO3, SO2, P2O5, and P2O3. NO is most preferred as the gaseous efficiency-enhancing compound.
Although in some cases it is preferred to employ members of the same half-reaction pair in the reac-tion system, i.e., both the efficiency-enhancing salt member associated with the catalyst and the gaseous member in the feedstream, as, for example, with a preferred combination of potassium nitrate and nitric oxide, this is not necessary in all cases to achieve ;3L2~3~;
satisfactory results. Other combinations, such as KNO3/N2O3, KNO3/NO2~ KN3/N24~ KNO3/S2' KN2/N' KNO2/NO2, and KNO3/a mixture of SO2 and NO, may also be employed in the same system. In some instances, S the salt and gaseous members may be found in differ-ent half-reactions which represent the first and last reactions in a series of half-reaction equations of an overall reaction.
The gaseous efficiency-enhancing member of a redox-half reaction pair is also present in an amount sufficient to enhance the performance, such as the activity of the catalyst, and, particularly, the efficiency of the epoxidation reaction. The precise amount is determined, in part, by the particular efficiency-enhancing salt of a member of a redox-half reaction pair used and the concentration thereof, the particular alkene undergoing oxidation, and by other factors noted above which influence the amount of efficiency-enhancing salt of a member of a redox-half reaction pair. Typically a suitable concentration of the gaseous member of a redox-half reaction pair for epoxidation of most alkenes, including propylene, is about 0.1 to about 2,000 ppm, by volume, of the gas-eous feedstream when N2 is used as ballast. When a preferred gaseous member of a redox-half reaction pair, such as NO, is used in the epoxidation of pro-pylene, the preferred concentration is about 2,000 ppm, by volume, with an N2 ballast. However, when ethylene is being oxidized, a suitable concentration for ethylene is from about 0.1 to about 100 ppm, by volume, of the gaseous feedstream components. Pref-erably, the gaseous efficiency-enhancing member of a redox-half reaction pair is present in an amount of about 1 to about 80 ppm when about 3 percent, by ~ .
-42~ 9~
volume, CO2 is present. When nitric oxide is em-ployed as the gaseous efficiency enhancing compound in an ethylene epoxidation system, it is present in an amount of about 0.1 to about 60 ppm, preferably about l to about 40 ppm, when CO2 is present.
The oxygen employed in the reaction may be in-troduced to the reactor either as air, commercially pure oxygen or other substance which under epoxida-tion conditions both exists in a gaseous state and forms molecular oxygen. The gaseous components which are supplied to the reaction zone, or that region of the reactor where reactants and catalyst are brought together under epoxidation conditions, are generally combined before being introduced to the reactor. The reactors in which the process and catalyst of the present invention are employed may be of any type known to the art.
In addition to an alkene, oxygen, and the gas-eous efficiency-enhancing member, the feedstream also contains a halogen-containing compound, preferably an organic halide, including both saturated and unsatur-ated halides, such as ethylene dichloride, ethyl chloride, vinyl chloride, methyl chloride and methy-lene chloride. Preferably, ethyl chloride is em-ployed as the halogen-containing compound. The amount of halide employed will vary depending upon a variety of factors, including the particular alkene being oxidized and the concentration thereof, the particular efficiency-enhancing gaseous component and salt ar.d the concentrations thereof, as well as other ~ factors noted above as influencing the amount of ; efficiency-enhancing gaseous compound and salt.
suitable range, however, of concentration for the halogen-containing compound is typically about 0.1 to about 60 ppm, by volumie, of the gaseous makeup feed-' .
~ 13457 _ ~ Z~ 3 ~3~
stream. In addition, a hydrocarbon, such as ethane,can be included in the feedstream. The feedstream may also contain a diluent, such as nitrogen, or other inert gas, particularly when air is used as the 5 oxygen containing gas. Varying amounts of carbon dioxide and water vapor may also be present, depend-ing upon whether means have been provided to remove such substances from the effluent stream prior to combination of at least a portion of the effluent stream with the inlet stream. Other than the gaseous efficiency-enhancing member of a redox-half reaction pair, the other components are present in convention-ally used amounts, as shown in the following table.
Volume Percent ~or ppm) Component for Propylene Oxidation propylene about 2 to about 50 oxygen about 2 to about 10 20 alkyl halide about 5 to about 2,000 ppm hydrocarbon 0 to about 5 carbon dioxide up to about 15 nitrogen remainder or other ballast gas, e.g., methane -44- .~Z~3~
Volume Percent (or ppm3 Component for Ethylene Oxidation ethylene at least about 2, often about 5 to about 50 oxygen about 2 to about 8 alkyl halide about 0.1 to about 60 ppm hydrocarbon about 0 ~o about 5 carbon dioxide up to about 7 10 nitrogen remainder or other ballast gas, e.g., methane When higher alkenes, such as those previously discussed, are epoxidized, conditions and concentra-tions typically used for the epoxidation of propylene may be employed.
Standard Alkene Oxide Process Test Conditions-The successful commercial production of alkene oxides, particularly ethylene oxide, by the silver-catalyzed oxidation of alkene, particularly ethylene, depends upon a variety of factors. Many of these factors influence, either directly or indirectly, the performance indices, such as the efficiency of the catalytic system, the activity or the aging rate, i.e., stability, of the catalyst. The manner in which catalysts and catalytic systems are evaluated in the laboratory strongly influences the values obtained for these parameters. Techniques and exper-iments designed to assess such catalysts and cata-lytic systems commonly employ microreactors (i.e., tiny tubular reactors for testing crushed catalyst particles) or back-mixed autoclaves of the Berty type . .
_~5- ~Z93~
ti~e.~ larger reactors which test full-sized catalyst pellets and generally employ full gas recycle) as described in Figure 2 of the article by J~ M. 8erty, "Reactor For Vapor Phase-Catalytic Studies", Chemical 5 ~n~ineerinq Progress, 70, Number 5, pages 78-84 (1974), and particularly Figure 2. Microreactors are capable of yielding, in most test situations, the highest efficiency numbers, typically approximately the same as or somewhat greater than those obtainable in commercial tubular reactor operations employing the same catalysts in non-crushed condition. Back-mixed autoclaves commonly provide lower efficiency values because, although conditions can be varied, generally the entLre catalyst is exposed to the out-let gas which has the lowest concentration of re-actants and the highest concentration of products.
Values obtained using one type of reactor are seldom directly comparable to those obtained in another reactor system. As a result, claims of superior results or the desirabi~ity of one catalyst over another are preferably based on tests conducted under controlled and comparable conditions.
Although the conditions set forth supra may be employed boti~ for reactors employed in commercial production as well as those employed in a laboratory, as a basis of comparison, the catalysts and catalytic systems for epoxidation of ethylene employed in the examples set forth below have been tested u*der com-parable conditions known as Standard Alkene Oxide Process Test Conditions, or Standard Test Conditions (referred to hereinafter as STC). The STC employed for testing and characterizing the catalysts and the catalytic systems of the present invention involve the use of a standard back-mixed bottom-agitated nMagnedrive" autoclave or Berty autoclave, as de-46~ 3 scribed above.
In discussing the enhancement of efficiencyprovided by the present invention, it may be noted that, when an efficiency-enhancing amount of a salt of a member redox-half reaction pair is employed, an efficiency of at least about 84 percen~ i5 obtained under Standard Test Conditions. "S~andard Test Con-ditions" may be deined as comprising the following:
by volume, 30 percent C2H4, 8 percent 2~ 5 ppm ethyl chloride, 5 ppm, by weight, NO, no added C2H6 or CO2, N2, ballast, 240 degrees C, 275 psig, gas hourly space velocity (GHSV) = 8,000 hr 1.
Although the present invention can be used with any size and type of alkene oxide reactor, including both fixed bed and ~luidized bed reactors known to the art, it ls contemplated that the present inven-tion will ind most widespread application in standard fixed bed, multi-tubular reactors. These generally include wall-cooled as well as adiabatic or non-wall-cooled reactors. Tube lengths may typically range from about 5 to about 60 feet but will fre-quently be in the range of from about 15 to about 40 feet. The tubes may have internal diameters from about 0.5 to about 2 inches and are expected to u~
typically from about 0.8 to about 1.5 inches. G~SV
range from about 16,000 to about l,000 hr~l.
Typically GHSV values range from about 2,000 to about 8,000 hours~l at pressures from about 1 to about 30 atmospheres, commonly about 10 to about 25 atmos-pheres.
While the invention is susceptible to variousmodifications and alternative forms, certain specific embodiments thereof are described in the examples set forth below. It should be understood, however, that these examples are not intended to limit the inven-` ~~7~ lZ~3~6 tion to the particular forms disclos~d but, on thecontrary, the invention is to cover all modifica-tions, equivalents and alternatives falling within the spirit and scope of the invention.
s Example 1 - Preparation Of Alpha-Alumina Support Havin~o~ Sodium:
Approximately 1,200 grams of 1/4 inch hollow gamma-alumina pills or rings (obtained from ~orton Corporation as Alumina 6573) were soaked for one-half hour in 1 molar NH4F with occasional shaking to li-berate bubbles that formed durinq impregnation.
Excess solution was drained from the rings, which were then dried overnight at 120 degrees C. The dried rings were distributed between four 3 inch diameter x 6 inch deep cylindrical alumina crucibles and were fired in a P. D. H. high-temperature fur-nace. Lids for the crucibles were placed askew so that crucible openings were covered approximately 70 percent to maintain a fluoride atmosphere in the cru-cible but at the same time permit escape of excess fluoride. The firing schedule was one hour to raise the temperature to 700 degrees C, four hours to raise 2S the temperature from 700 to 1,100 degrees C, and a hold temperature at 1,100 degrees C for one hour.
The product had a surface area of 1.56 m~/g and a sodium content of less than 50 ppm.
Example 2 - Sequential Preparation Of A Potassium Nitrate-Containing Suppor~ed Silver Catalyst:
.
Formation of a potassium nitrate-containing supported silver ca~alyst resulted from a multi-step procedure in which a support was initially impreg-~` -48- ~ 2~
nated with a silver-containing solution, the impreg-nated support was roasted, and the silver-inpregnated catalyst was thereafter impregnated with a potassium nitrate solution and then dried.
S The silver-containing solution used in the first step was prepared by dissolving 51.49 grams ethylene-diamine in 51.03 grams of distilled water and stir-ring the mix~ure for a period of 10 minutes. To the stirred solution was slowly added 51 56 grams of 10 oxalic acid dihydrate. The resulting solution was stirred for 10 minutes. To this solution was added, in portions, ga.34 grams silver oxide. The resulting silver-containing solution was thereafter stirred for an additional hour and 18.07 grams of monoethanol-amine was then added to the stirred silver-containing solution. Stirring was continued for an additional 10 minutes. This solution was then diluted to a total volume of 437 ml by addition of distilled ~ater.
2~ In a catalyst-impregnation tube were placed 177.85 grams of an alpha-alumina carrier, similar to that prepare~ in Example 1. A catalyst-impregnation tube is an elongated tube, which in use is arranged vertically. The upper end of the tube is provided with an inlet to supply impregnation solution to the carrier contained in the tube and the lower end with an outlet from which solution may be drained. The - tube is also provided with a means to connect the tube to a vacuum source. Prior to introduction o~
impregnation solution the tube was evacuated. The solution described immediately above was slowly poured into the tube to totally immerse the support. The carrier was allowed ~o remain in the impregnating solution for about l hour to achieve saturation of the support. The unabsorbed solution :~293~96 was thereafter drained from the support with drainlng continuing for about 30 minutes. The wet, impregnated carrier was then roasted in a hot-air belt roaster for 2.5 minutes at 500 degrees C ~66 SCFH air flow) to produce a catalyst containing 11.39 percent silver.
~ pon cooling, 44.57 grams of the roasted, im-pregnated carrier was placed in an impregnation tube and covered with a solution formed by dissolving 2.08 grams potassium nitrate in lO0 ml distilled water.
After covering the roasted silver-containing carrier with the KNO3-containing solution and allowing to stand for 15 minutes, the catalyst pellets were drained on a funnel for 5 minutes. The resulting drained pellets were dried in an oven for 2 hou~s at 120 degrees C, producing a catalyst containing 0.46 percent K, calculated as 1.20 percent KNO3, by weight.
Example 3 - Sequential Preparation Of Sodium- And Potassium Nitrate-Containing Su~orted Silver CatalYst: ~
An impregnated and roasted silver-containing 25` catalyst was prepared as described in Example 2.
Into an impregnation tube was placed 44.57 grams of the silver-containing catalyst (11.39 percent, by weight, Ag) and a solution prepared by dissolving 2.08 grams potassium nitrate and 0.04 grams sodium nitrate in lO0 ml distilled water was placed in the tube after evacuation of the tube to totally cover the silver-containing. The pellets were allowed to stand in the solution for 15 minutes, the excess solution was drained from the pellets on a funnel for 5 minutes, and the impregnated catalyst was oven-~33~9~
dried for 2 hours at 100 degrees C. The catalyst pellets contained, by weight, 0.44 percent K, calcu-lated as 1.15 percent KNO3 , and 0.008 percent ~80 ppm) Na.
Example 4 - Preparation Of A Potassium Nitrate-Containing Silver Catalyst BY A Co-Impre~nation Technique: _ A co-impregnation solution was prepared by plac-ing 18.77 grams of ethylenediamine into a 400 ml beaker and mixing therewith 25 grams of distilled water to form a solution. To the stirred solution was slowly added 18.7 grams oxalic acid and, with continuous stirring, 3$.2 grams of silver oxide was slowly added. When solution was complete, 6.55 grams of monoethanola~ine was added directly to the solu-tion. To the silver-containing solution was added 7.14 gra~s of potassium nitrate solution, 10 percent with respect to potassium (0.258 grams KNO3/g solu-tion). Sufficient water was added to the resulting solution to dilute the solution to 100 ml.
i To make 100 ml of finished catalyst, 53.5 grams of an alpha-alumina support material of the type prepared in Example 1 but fired at a temperature of 1,000 degrees C in the form of quarter-inch ring ` extrudate and having a pore volume of ~.62 g H2O/g support was placed in a suitable container. A source of vacuum was attached to the container and evacuated and thereafter-the silver/potassium-containing im-pregnating solution was added until the carrier was completely covered. After about one hour the excess solution was drained from the catalyst.
Roasting of the impregnated catalyst was con-ducted as indicated above in Example 2. The result-~` sl ~93~
ing catalyst in~luded! by weight, 17.5 percent silverand, as calculated, about 1 percent potassium nitrate.
Example ~ - Sequ~rltial Preparation Of A Potassium Nitrate-Containing Sup~orted Hi~h Sllver Concentr_tion Catalyst A solution containing 17.5 g ethylenediamine, 17.3 g distilled water, 17.5 g oxalic acid, 30.7 g silver oxide, 6.1 g monoethanolamine, diluted to 125 ml, was prepared in the manner described in Example 2.
Into a catalyst impregnation tuhe were placed 43.9 g of an alpha-alumina carriee, similar to that prepared in Example 1, and having a surface area of 1.12 m2/g, a pore volume of 0.8 cc/g, less than 50 ppm, by weight, leachable sodium, and a platelet morphology of the type disclosed in Canadian Application ~o. 515,865. The support pellets were initially vacuum-impregnated at 28 inches mercury vacuum, releasing the vacuum when the pellets were completely covered with the aqueous silver amine solution, permitting them to stand in the amine solution for an additional hour at 1 atmosphere before draining. The impregnated pellets were then belt-roasted at 500 degrees C in an oven having an air flow of 66 SCFH for 2.5 minutes. The material contained 14.9 percent silver as determined by weight gain. This material was then impregnated a second and third time with fresh silver/amine solution having the composition indicated above. The impregnations and belt-roastings were conducted in the same manner as described above. The catalyst material was ~ .
--52~ 3~
then impregnated with KNO3 by placing 67.4 9 of the silver-impregnated pellets into a solution containing 2.1 g KNO3 dissolved in 100 ml distilled water. The KNO3-impregnated silver catalyst material was then 5 dried at 120 degrees C for 1 hour to yield a catalyst containing, by weight, 34.7 percent silver and 0.33 percent K (calculated as 0.86 percent K~03), as de-termined by weight gain.
10 Example 6 - Coincidental Preparation Of A Potassium Nitrate-Containing Supported High Silver Concentration Catalyst:
A silver impregnation solut;on was prepared in a 15 manner similar to that described in Example 2 by mixing 196.8 g ethylenediamine, 195.0 g distilled water, 197.1 g oxalic acid, 345.2 g silver oxide, 69.1 g monoethanolamine and diluting to a total vol-ume of 780 ml with distilled water. After evacuation of an impregnation tube containing pellets of an alpha-alumina support material ~293.1 g) similar to those described in Example 1 and having a B. E. T.
surface area of 1.16 m2/g by a Quantasorb apparatus, the pellets were impregnated by allowing them to stand in the silver impregnation solution for a per-iod of 1 hour and then draining. The impregnated pellets were then belt-roasted at 500 degrees C in a 66 SCFH air flow for 2.5 minutes. As determined by gain in weigh~t, the material contained 24.6 percent silver A co-impregnation solution was prepared in a manner similar to that described in Example 3 by mixing 37.5 g ethylenediamine, 37.2 g distilled ~water, 37.6 g oxalic acid, 65.9 g silver oxide, 13.2 ;;35 g monoethanolamine, and 0.80 g potassium nitrate and diluting to 150 ml total solution with distilled water. The silver-impregnated catalyst pellets (77.8 g) were impregnated by immersing them in the sil-ver/potassium nitrate-impregnating solution for 1 hour and then draining. The resulting pellets were then belt-roasted as described above. The pellets resulting from the two impregnations yielded a mater-ial, as determined by an analysis, containing, by weight, 39.8 percent silver and 0.098 percent K (cal-culated as 0.25 percent KNO3).
Examples 7 to 12 Production OfEthylene Oxide With Potassium Nitrate-Containing Supported Silver Catalyst:
The examples set forth below were conducted employing catalyts using carriers of the type pre-pared in Example 1, the catalysts themselves being prepared in the manner described in Examples 2 to 6 and identified as being prepared by either a sequen-tial (S) procedure or a coincidental impregnation (C) procedureO The epoxidation studies for which data are presented below were conducted in a continuously stirred tank reactor, alsG ~.~own as a back-mixed autoclave of the type described above. The procedure involved charging approximately 80 ml of catalyst to the autoclave. The volume of catalyst was measured in a one inch I. D. graduated cylinder after tapping the cylinder several times to thoroughly pack the catalyst. The weight of the catalyst was noted and is indicated in the table appearing below. The back-mixed autoclave was heated to about reaction tempera-ture in a nitrogen flow of 11.3 SCFH with the fan ~ operating at about 1,500 rpm. The nitrogen flow was ; 35 then discontinued and the feedstream was introduced to the reactor.
All ethylene epoxidation reactions, except where indicated otherwise, were examined under Standard Test Conditions comprising, by volume, 30 percent C~H4~ 8 percent 2' 5 ppm ethyl chloride, 5 ppm, by weight, NO, no added C2H6 or CO2, N2 ballast, 240 degrees C, 275 psig, GHSV = 8,000 hr 1. The data summarized below includes surface areas of the cata-lysts, Ag and calculated KNO3 contents, maximum ob-served outlet ethylene oxide, maximum observed effi-ciency, and aging rate.
T~BLE
Pre-para- Calcu-tion lated Example Proce- Na ~ Ag % RN03 Activity Effi-dure ~m ~EØ) ciency 7 C 12 19.7 2.0 1.18 91~0 108 C 12 20.0 2.0 1.41 90.3 9 C 12 19.7 2.0 1.23 90.0 C 12 20.4 2.0 1.35 ~0.3 11 S 12 15.6 1.0 1.12 86.5 12* C 12 39.8 0.1 2.03 8~.0 1513** S 12 11.4 1.2 See 88.2 Figure 14** S 80 11.4 1.2 See 87.8 Figure 15*** C 40 39.8 0.1 See See Figure Figure 16*~ C 100 39.8 0.1 See See Figure Figure *Test conditions, by volume, 30 percent C2H4, 8 per-cent 2~ 20 ppm ethyl chloride, 15 ppm N0, 270 de-grèes C, 270 psig, GHSV = 8,000 hour 1. The catalyst Of Example 6 is used. The catalyst of Example 3 is used.
**GHSV = 4,000 hr~l, all other conditions the same as for Examples 7-11.
***Conditions the same as Example 12 but additionally includes 3 percent C02 in the feedstream. The cata-~39~
lyst of Example 6 is used.
Example 13 - Production of Propylene Oxide With Potassium Nitrate-1 Supported Silver Ca a~st:
Into a back-mixed autoclave, having a slightly smaller volume than the autoclave employed in the previous examples, were placed 5.0 grams (10.0 ml) of a catalyst having a support prepared as in Example 1, The support was an alpha-alumina having a surface area of 1.12 m2/g, a pore volume of 0.8 cc/g, less than 50 ppm, by weight, of leachable sodium, a residual fluorine concentration o-f 0.7 percent, and a platelet morp~ology of the type disclosed in Canadian Application No. 515,865. The catalyst included, by weight, a silver con~entration of 17.7 percent and a potassium concentration of 0.38 percent (calculated as 1 percent potassium nitrate).
A mixture, by volume, of 9.9 percent propylene, 7.75 percent oxygen, 200 ppm ethyl chloride, 200 ppm nitric oxide, 2 percent methane, and the remainder being nitrogen ballast gas, was fed to the reactor at a temperature of 252 degrees C, a pressure of 25 psi and a gas hourly space velocity of 832 hr 1 After 22.5 hours, a selectivity of 47.3 percent was observed with an activity of 0.6 pounds of propylene oxide/cubic foot of catalyst/hour (corresponding to an outlet percent of propylene oxide of 0.465 percent).
., .~
CH2=CH2 + 3 2 > 2 CO2 + 2 H20 (II) or by further oxidation of the epoxide.
In the years between the Van Peski patent and the present inventions, research efforts have been lS directed to improving both the activity and longevity or useful life of the catalyst and the efficiency of the overall catalytic reaction. As is indicated by reactions I and II, the oxidation of an alkene may produce either the alkene oxide (I) sought in the process or the by-products CO2 and H2O.
Several terms are commonly used to describe some of the parameters of the catalytic system. For in-stance, "conversion" has been defined as the percent-age of alk~ fed to the reactor which undergoes reaction. The "efficiency" or, as it is sometimes called, the "selectivity" of the overall process is an indication of the proportion, usually represented by a percentage, of the converted material or product which is alkene oxide. The commercial success of a 30 reaction system depends in large measure on the effi-ciency of the system. At present, maximum efficien-cies in commercial production of ethylene oxide by epoxidation are in the low 80s, e.g., 80 or 81 per-cent. Even a very small increase in efficiency will - 35 provide substantial cost benefits in large-scale -3- ~293~9~
operation. For example, taking 100,000 metric tons as a typical yearly yield for a conventional ethylene oxide plant and assuming 80 percent conversion, an increase in efficiency of from 80 to 84 percent, all other things being equal, would result in a savings of 3790 metric tons of ethylene per year. In addi-tion, the heat of reaction for reaction II ~formation of carbon dioxide) is much greater than that of reac-tion I (formation of ethylene oxide) so heat-removal problems are more burdensome as the efficiency de-creases. Furthermore, as the efficiency decreases, there is the potential for a greater amount of impur-ities to be present in the reactor effluent which can complicate separation of the desired alkene oxide product. It would be desirable, therefore, to de-velop a process for the epoxidation of alkene in which the efficiency is greater than that obtained in conventional commercial processes, e.g., with ethy-lene, efficiencies of 84 percent or greater, while maintaining other performance characteristics, parti-cularly the activity, as described below, in a satis-factory range.
The product of the efficiency and the conversion is equal to the yield, or the percentage of the al-kene fed that is converted into the correspondingoxide.
The "activity" of the catalyst is a term used to indicate the amount of alkene oxide contained in the outlet stream of the reactor relative to tha~ in the inlet stream. Activity i5 generally expressed in terms of pounds of alkene oxide produced per cubic foot o~ catalyst per hour at specified reaction con-ditions and rate of feed. The activity may also be stated in terms of the amount of ethylene oxide in 35 the outlet stream or the difference between the ethy--4- 1293~9~
lene oxide content of the inlet and outlet streams.
If the activity of a reaction system is low, then, all other things being equal, the commercial value of that system will be low. The lower the activity of a reaction system, the less product pro-duced in a unit time for a given feed rate, reactor temperature, catalyst, surface area, etcetera. A low activity can render even a high efficiency process com~ercially impractical. For production of ethylene oxide, an activity below 4 pounds of ethylene oxide per hour per cubic foot of catalyst is unacceptable for commercial practice. The activity is preferably greater than 8 pounds, and in some instances an acti-vity greater than 11 pounds of alkene oxide per hour lS per cubic foot of catalyst is desired.
In some instances, activity is measured over a period of time in terms of the amount of alkene oxide produced at a specified constant temperature. Alter-natively, activity may be measured as a function of the temperature required to sustain production of a specified constant amount of alkene oxide. Plots of such measurements yield "aging rates" which reflect the stability or useful life of the catalyst. The useful life of a reaction system is the length of time that reactants can be passed through the reac-tion system during which acceptable activity is ob-served. The area under a plot of activity versus time is equal to the number of pounds of alkene oxide produced during the useful life of the catalyst per cubic foot of catalyst. The greater the area under such a plot, the more valuable the process is since regeneration or replacement of the catalyst involves a number of expenses, sometimes referred to as turn-around costs. The rate at which activity decreases, i.e., the rate of deactivation at a given point in ~ _5~ 3~
time, can be represented by the slope of the activity plot, i.e., the derivative of activity with respect to time:
s deactivation = d[activity~/dt.
The average rate of deactivation over a period of time can be represented then by the change in activity divided by the time period:
average deactivation = a activity/ a t.
At some point, the activity decreases to an unacceptable level, for example, the temperature required to maintain the activity of the system be-comes unacceptably hi~h or the rate of production becomes unacceptably low. At this point, the cata-lyst must either be regenerated or replaced. Some of these definitions may be represented as set out be-~0 low:
Conversion = moles alkene reacted x 1~0moles alkene fed ~ Efficiency = moles alkene oxide produced x 100 moles alkene reacted Typically, in commercial production, since the outlet or~effluent stream emanating from the reactor may contain substantial amounts of unreacted alkene, the effluent stream is recycled and combined with the feedstream after removal of at least a portion of the alkene oxide. Generally, as the activity of a cata-lyst decreases with time, in order to obtain the same ultimate yield of epoxide product, the effluent -6~ 9~
stream must either be recycled a greater number of times or the temperature within the reactor must be raised to increase the activity of the catalyst. The former approach to increasing the yield of product requires additional energy expenditures and the lat-ter, which is most frequently used~ causes faster catalyst deterioration.
As used herein, an activity-reaucing compound refers to a compound which, when present in an acti-vity-reducing amoun~, causes a reduction in activity, some or all of which activity may subsequen~ly be regained by returning to a situation in which the concentration of the compound is below the minimum actLvity-reducing amount. The minimum activity-reducing amount varies depending on the particularsystem, the feedstream and the activity-reducing compound.
Conversely, deactivation, as used herein, refers to a permanent loss of activity, i~e., a decrease in activity which cannot be recovered. As noted above, activity can be increased by raising the temperature, but the need to operate at a higher temperature to maintain a particular activity is representative of deactivation. Furthermore, catalysts tend to deacti-vate more rapidly when reaction is carried out athigher temperatures.
In contrast to problems associated with low or decreasing catalyst activities, less than satisfac-tory efficiencies result in loss of starting mater-ial, the alkene, as the unwanted product CO2. Ulti-mately, this also increases product costs.
To be considered satisfactory, a catalyst must not only have a sufficient activity and the catalytic system provide an acceptable efficiency, but the catalyst must also demonstrate a minimum useful life -7~
or stability. When a catalyst is spent, typically the reactor must be shut down and partially disman-tled to remove the spent catalyst. This results in losses in time and productivity. In addition, the S catalyst must be replaced and the si`,ver salvaged or, where possible, regenerated. Even when a catalyst is capable of regeneration in situ, generally production must be halted for some period of time. ~t best, replacement or regeneration of catalyst requires additional los~es in time to treat the spent catal~st and, at worst, requires replacement of the catalyst with the associated costs.
Since even small improvements in activity, ef-ficiency or useful life may have significance in large scale commercial production, such improvements have been the object of a great deal of research in the direct epoxidation of alkenesO The focus Oe attempts to improve performance, such as the activity and useful life of the catalyst and the efficiency of the system, has included such areas as feedstream additives or removal of components therefrom; methods o~ preparation of the catalyst; deposition or impreg-nation of a particular type or form of silver; com-position, rormation, physical properties and morpho-logy of the support; additives deposited on or im-pregnated in the support; shape of support aggregates used in the reactor; and various types o~ reactors and bed designs, such as stationary and fluidized beds.
Early work on the silver-catalyzed direct oxida-tion of alkenes to alkene oxides in many instances resulted in improvements in activity and particularly the selectively of the system, in many cases the efficiency increasing by several percent. However, recent modifications in such systems have resulted in 13~57 ~ -8- ~3496 only small incremental improvements in efficiency.
In terms of operating cos~s, even fractions of a percent improvement in efficiency can translate into large savings in production. Accordingly, current research is still being directed to improvements in the activity and useful life of the catalyst and selectivi~y of the system.
Although a vast number o~ elements and compounds are known to have effective catalytic properties in 1~ various reactions, many have at least one shortcom-ing, such as very high cost and/or limited availabil-ity, thermal instability in the temperature range in which the reaction is to be conducted, low mechanical strength, small surface area per unit of volume, susceptibility to poisoning, short useful lifetime, etcetera. Such undesirable characteristics make such substances of limited utility as catalys~s. Some of these shortcomings, however, may be overcome and in some instances the effectiveness of the catalyst may be improved by applying the substance to a carrier or support.
New support materials are continuously being tried. ~owever, many of those which were employed in the early development of the silver-bearing catalysts are, with some modifications, still being used.
Materials which have found most widespread use are typically inorganic and generally are of a mineral nature. Such materials commonly include alumina, fire brick, clay, bauxite~ bentoniter kieselguhr, carbon, silicates, silica, silicon carbide, zirconia, diatomaceous earth, and pumice.
In addition to the physical strength of the support materials, other physical properties, such as surface area, pore volume, pore dimensions, and par-ticle size have drawn considerable attention. These 13~57 . ~ ~
3~ 3~
properties have been examined with great scrutinywhen evidence indicated that there was a correlation between the size o~ silver particles and the effici-ency of the overall system or useful life of the catalyst. Some materials are also preferred for their chemical properties, i.e., their "inertness" or "promoting" properties.
The support serves a number o~ functions in a heterogeneous catalytic system. Ease of handling is facilitated by a support which generally takes the form of discrete particles or aggrega~es of varying shape or size which, depending on usage, have a major dimension of about 1 millimeter to about 20 milli-meters~ Thus it is not necessary for the catalyst to form a permanent or semi-permanent part of the reac-tor.
The support, however, serves primarily to in-crease the surface area of the "active" component of the catalyst, silver, which is important in that most epoxidation occurs at the silver surface-fluid inter-face. Many of the substances commonly employed as catalyst supports not only have the usual external surface, which provides a varying surface area, de-pending on the shape of the support bodies and the packing of the bodies, but are also of a porous na-ture and, therefore, have a large internal surface which contributes to the overall surface area of the supported catalyst. Such support materials provide a greater capacity for sorbing not only the catalyst material during catalyst preparation, when the sup-- port is impregnated with a solution containing the catalyst component(s) in soluble form, but also a greater capacity for the flow of the fluid reactants within the catalyst during the reaction for which the catalyst is intended. The support also improves "` lo 1~3~
performance by lo~ering the pressure drop through the reactor and by facilitating heat and mass transfer.
Among the large variety of substances employed in the past as supports for catalytic materials, alumina has exhibited superiority in many respects as a catalyst support material. In addition to the low cost of the material, alumina has good thermal sta-bility and some forms have a relatively large surface area.
Alumina, in its various forms, particularly alpha-alumina, has been preferred as a support mater-ial for silver-containing catalysts in the prepara-tion of alkene oxides. Numerous variations of sur-face area, pore dimensions, pore volume and particle size have been suggested as providing the ideal phys-ical property or combination of properties for im-proving efficiency, activity or useful life of the catalyst.
Holler (U. S. Paten~ 3,908,002) discloses an al-pha-alumina, useful as a catalyst support for reac-tions conducted at temperatures below 800 degrees C, such as oxidation reactions of hydrocarbons to oxyhy-drocarbons. The support, having a surface area re-ported to be at least about 4~ m2/g, is produced by thermally decomposing a porous aluminum ion chain-bridged, polymeric carboxylate. Indicating that a large surface area in a carrier may be detrimental to its efficient operation and catalyst activity, Belon (U. S. Patent 3,172,866) describes a method of pro-ducing a macroporous catalyst carrier which may beused in the catalytic production of ethylene oxide having pore diameters of between 0.1 and 8.0 microns and a specific surface area between a few square meters and one square decimeter per gram. The sup-port is prepared by heating a mixture of active and .
~ 13457 3~
calcined aluminum oxides and a small amount of boronoxide at temperatures of between about 1,600 and 1,800 degrees C. Waterman ~U. SO Patent 2,901,441) describes a process for preparing highly active and selective catalysts for the oxidation of olefins to olefin oxides on a support having an average porosity of at least 35 percent. The method involves washing an alpha-alumina or silicon carbide support having an average porosity of between 35 and 65 percent with an aqueous solution of lactic acid, washing with water until neutral, and then impregnating the support with an aqueous solution of silver lactate. The impreg-nated support is thereafter heat-treated to deposit elemental sllver. A silver-supported catalyst for the vapor phase oxidation of ethylene to ethylene oxide, exhibiting improved production of ethylene oxide and catalyst longevity, is described by Brown et al (U. S. Patent 3,725,307). The catalyst is disclosed as being formed from support particles having an average pore diameter of at least 10 mi-crons up to, preferably, 70 microns and a surface area of less than about l m2/g. The selectivities reported do not range above about 73 percent. The support is preferably composed of silica-alumina. A
silver-supported catalyst which includes a support of alpha-alumina, silicon carbide, fused aluminum oxide, or mixtures of alumina and silica was asserted by DeMaio (U. S. Patent 3,664,970) to eliminate the need for halogenated inhibitors in the oxidation of ethy-lene to ethylene oxide. The support is composed ofparticles having a minimum apparent porosity of about 30 percent and wherein at least 90 percent o the pores have diameters in the range of l to 30 microns, the average of the diameters being in the range of 4 to 10 microns. Wattimena ~U. S. Patent 3,563,914) -12~
discloses silver catalysts using aluminum oxide sup-ports having pore volumes between 15 and 30 ml/g and surface areas below about 10 m2/g.
~ayden et al tU. K. Patent Application 2,014,133) disclose a silver catalyst employing a support having a specific surface area in the range of 0.05 to 10 m2/g, an apparent porosity of at least 20 percent, and mean pore diameters of 0.1 to 20 microns, the pore size distribution being bimodal, in which the smaller pores preferably account for at least 70 percent of the total pore volume. Alpha-alumina supports are described by Rashkin (U. K.
Patent Application 2,122,913A) having a "relatively low surface area" of less than 30 m2/g. Mitsuhata et al (Japanese Published Patent Application 56-089843) and ~itsuhata et al ~U. S. Patent 4,368,144) describe supported silver catalysts in which the support is formed from alpha-alumina having a specific surface area of 0.5 to 5 m2/g. Watanabe et al (Japanese Published Patent Application 56-105750) employ a similar catalyst suppor having a surface area of 1 to 5 m2/g. Hayden et al (U. S. Patent 4,007,135) describe silver-containing catalysts in which the porous neat-resisting support has a specific surface area in the range of 0.04 to 10 m2/g, an apparent porosity of at least 20 percent, and a median pore diameter of 0.3 to lS microns. Mitsuhata et al (U.
S. Patent 4,248,740) describe the use of high alpha-alumina content supports having a specific surface area of not more than 10 m2/g, an apparent porosity of 40 to 60 percent by volume, and a pore volume of 0.1 to 0.5 cc~g. Armstrong et al (U. S. Patent 4,342,667) disclose a supported silver catalyst, useful in the oxidation of ethylene to ethylene ox-3s ide, in which the support has a surface area of 0.02 -13- ~ ~3~
to 2 m~/g, an average pore diameter of 0.5 to 50 microns and an average pore volume of 0.2 to 0 5 cc/g.
There has also been some interes~ in the purity of supports employed, both as to composition and phase. Examples of high purity alumina include U. S.
Patent 2,901,441 which uses alpha-alumina having a purity of about g9.5 percent as a support for cata-lysts used to oxidize olefins to olefin oxides. An ethylene oxidation catalyst is disclosed in German Patent Publication DE 2,933,950 which attains a long catalyst life without a loss in activity or selec-tivity by using an alpha-alumina support having less than 0.001 weight percent of alkali-soluble silicon compounds. The catalyst is prepared by boiling com-mercial quality alpha-alumina with l weight percent sodium hydroxide solution and washing to a pH value of 8. If desired, the silicon compound concentration may be reduced below l part per million (ppm) by washing further with l weight percent HF. U. K.
Patent Application 2,122,913A describes supported silver catalysts in which the support is composed of silica, alumina or mixtures thereof, one example of which is an alumina having a purity of 9~.3 percent by weight. The silver-supported catalyst described in Japanese Published Patent Application 56-089843 employs an alpha-alumina carrier having a sodium content of less than 0.07 weight percent. Japanese Published Patent Application 56-105750 describes the use of an alpha-alumina support in conjunction with a silver catalyst for producing ethylene oxide, which support has a sodium content less than 0.07 weight percent. A silver catalyst including an alpha-alumina carrier having a sodium content of not more ~ 35 than 0.07 percent is described by Mitsuhata et al ':
~ " ~
-14- ~ 3~
~U. S. Patent 4,368,144). The support also has a surface area within the range of 0.5 to 5 m2/g, an apparent porosity of 25 to 60 percen~, a specific pore volume of 0.2 to 0.5 ccjg, and a particle dia-meter within the range of 3 to 20 mm. An alpha-alumina support having a purity of 98~ weight per-cent, for use with silver in the catalytic oxidation of ethylene, is described by Warner et al in U. 5.
Paten~ 4,455,392. The patent additionally discloses that the carrier is generally a conventional micro-porous support with surface areas of less than 10 m2~g, pore volumes ranging from about 0.15 to 0.8 cc/g, and pore diameters of about 0.1 to 100 microns.
In addition to compositional purity, both phase lS purity and morphology of the support have been areas in which improvements in eEficiency, selectivity or stability of the catalyst have been sought. Examples include U. S. Patent 2,901,441 in which aluminum oxide is substantially completely converted to the alpha form of alumina by heating aluminum oxide to a temperature of about 1,500 to 2,050 degrees C. Weiss (U. S. Patent 2,209,908) and Carter tU. S. Patent 2,294,383) d-escribe the use of "Tabular Corundum" as : . a catalyst support for metallic oxides, such as those oxides of metals selected from the fifth and sixth group of the periodic system, for example, vanadium, molybdenum, uranium, etcetera, in the oxidation of various organic materials to maleic acid and maleic anhydride and silver for the catalytic oxidation of ~` 30 ethylene to ethylene oxide, respectively. Weiss indicates that Tabular Corundum, which is almost entirely aluminum oxide and has the alpha-corundum : crystalline form of aluminum oxide, may be formed by mixing aluminum oxide with one or more of several compounds, such as sodium oxide and chromic oxide, : 13457 and heating the mixture to a temperature in the range of about 800 to about 1,800 degrees C. Tabular Co-rundum is further described as having impurities present in only small quantities, the material also includes "readily bonded surfaces and consisting essentially of interlocked corundum crystals in tabu-lar form, having the contained impurities disseminat-ed in minute globules throughout the crystalline aluminan. Brengle et al (U. S. Patent 2,709,173) also employ Tabular Corundum as a support in one of their examples.
U. S. Patents 4,039,481 and 4,136,063 to Kimura et al disclose a catalyst carrier and a method for making same, the catalyst being the type used in catalytic converters in automobile exhaust systems.
Specifically, the catalysts have a surface layer containing alpha-phase alumina and an inner portion consisting essentially of alumina of a phase other than that of the alpha phase. The pores in the al-pha-alumina surface layer are larger than those in the inner portion of the catalyst body. A method of preparing the phase gradient support particles is described which provides for treating the surface of the alumina to a depth o about 400 microns with a transition element, particularly iron, and thereafter firing the carrier particles.
Weber et al ~U. S~ Patent 4,379,134) describe high purity alpha-alumina bodies, at least 85 percent of the pore volume of the bodies having pores with a diameter of from 10,000 to 200,000 Angstroms. The high purity alpha-alumina bodies are prepared by peptizing boehmite in an acidic aqueous, fluoride anion-containing mixture. An extrudable mixture is formed thereby which is extruded and shaped into formed bodies which are thereafter dried at 100 to -16~ 36 300 degrees C, calcined at a temperature of from 400 to 700 degrees C to convert the alumina to the gamma phase, and subsequently calcined further at a temper-ature of from 1,200 to 1,700 degrees C to convert the gamma phase to alpha-alumina phase.
A method of producing granulated porous corundum having a homogeneous porous structure with a total pore volume of 0.3 to 1.0 cm3/g and a predominant pore size of 5,000 to 30,000 A is described by Bores-kov et al (U. S. Patent 3,950,507). The method opreparing the alpha-alumina includes treating active alumina or aluminum hydroxide having a porous struc-ture to a first heat treatment in which the tempera-ture is increased from 20 to 700 degrees C, a second heat treatment in the range of from 700 to 1,000 degrees C, and a third treatment in the range of from l,OU0 to 1,400 degrees C. Each of the heat treat-ments is for a period of at least one-half hour, the first heat treatment being conducted in an atmosphere of hydrogen 1uoride in which the alumina absorbs the hydrogen fluoride and the second heat treatment de-sorbs the hydrogen fluoride. The patent also de-scribes a similar procedure employing stationary thermal conditions in which the granules of alumina or aluminum hydroxide are impregnated with other fluorine-containing compounds prior to the first thermal treatment. The recommended starting mater-ials used to form alpha-alumina include granulated pseudo-boehmite, boehmite or bayerite as the granu-lated aluminum hydroxide and granulated alpha-, eta-, or theta-alumina as the ac~ive alumina.
Although alpha-alumina has been considered by most to be the preferred alumina support material, ; Smith e~ al (U. S. Patent 2,422,172) have suggested that beta-aluminas are more desirable than the alpha -17- ~ ?3~
phase as a support material for catalysts, particu-larly those used in catalytic conversion processes such as dehydrogenation and hydroforming.
In seeking the ideal support material, there has S been some departure from the commonly employed sub-stances. For example, some use has been made of alkali metal and alkaline earth metal carbonates, both as the sole support material and in combination with other materials as the carrier for processes such as direct oxidation of alkenes to epoxides.
A number of supported silver-containing cata-lysts have been employed for epoxidation of alkenes in which the carrier includes, sometimes labelled as a promoter, a carbonate of a metal, generally an alkali metal or alkaline earth metal. Some examples of the use of one or more al~ali and/or alkaline earth carbonates may be found in U. S. Patents 2,424,084, 2,424,086, 2,615,900, 2,713,586, 3,121,099, 3,258,433, 3,563,913, 3,563,914, 3,585,217, 4,007,135, 4,033,9~3, 4,039,561, - 4,~66,575, 4,094,889, 4,123,385, 4,125,480, 4,168,247, 4,186,1~6, 4,226,782, 4,229,321, 4,324,699, European Patent Publications 0,003,542 and 0,011 .' " Japanese Patents 41-11847 and 57-107242, U. K. Patents 590,479, 1,571,123 and 2,014,133A, and Murray, "A Study Of The Oxidation Of Ethylene To Ethylene Oxide On A Silver Catalyst~, Australian 3Ournal of Scientific Research, Volume 3A, Pages 433-; 449 (1950). In additionl U. S. Patent 3,332,837 ; 30 employs zinc and/or cadmium carbonates, Gelbstein, (DS 2,352,608) aiscloses the use of the latter car-bonate and European Patent Publication 0,003,642 mentions the use of molybdenum carbonate.
Several patents have described the use of fluo-rine-con~aining co~pounds to treat support materials, in some cases to provide a compositionally pure sup-port, and in other cases as a fluxing agent to im-prove the phase purity of the support. Thus, U. R.
Published Patent Specification 590,479 and U. S.
Patent 2,424,086 indicate that a more active catalyst is formed if the support material ha~ undergone a preliminary treatment with a dilute solution of hy-drofluoric acid prior to impregnation with silver.
U. S. Patent 4,379,134 teaches the preparation of high purity alpha-alumina bodies by peptizing boeh-mite alumina in an aqueous acidic mixture containing fluoride anions and water. German Patent 2,933,950 teaches the reduction of silicon content by treatment with HF. U. S. Patent 3,950,507 teaches the prepara-tion of granulated porous corundum by a multiple stepheat treatment in which initial steps may be carried out in an atmosphere of hydrogen fluoride. Hosoda et al (U. S. Patent 3,144,416) suggest that a small amount o~ a halogen compound, sulfur compound, nitro-gen compound, or phosphorous compound may be addedeither to the reaction gas or the catalyst to improve the selectivity of the catalyst.
The nature of the silver itself has also been examined and modified in attempts to impro~e the ef f iciency and stability of the catalyst. Cavitt (U.
S. Patent 4,229,321) teaches that a supported silver catalyst of improved selectivity and activity may be prepared by mechanically removing the outer surface or skin of the catalyst after the impregnated cata-lyst has been heated to évaporate volatile materialand reduction of the silver salt to silver metal, thereby activating the catalyst.
Since the early work on the direct catalytic oxidation of ethylene to ethylene oxide, workers in the field have suggested that the addition of certain -19- ~Z~3~
compounds to the gaseous feedstream or direct incor-poration of metals or compounds in the catalyst could enhance or promote the production of ethylene ox-ide. Such metals or compounds have been known vari-ously as "anti-catalysts", "promoters" and "inhi-bitorsn. These substances, which are not themselves considered catalysts, have been proposed by prior workers to contribute to the efficiency of the pro-cess by inhibiting the formation of carbon dioxide or promoting the production of ethylene oxide. The scientific literature is replete with examples o the use of alkali metals and alkaline earth metals and their cations to promote the efficiency of silver catalysts used in epoxidation reactions. For exam-ple, ~odium, potassium and calcium were disclosed asbeing suitable promoters in U. S. Patent 2,177,361.
Numerous examples may be found in literature of pref-erence for one or several metals or cations and ex-clusion of one or more metals or cations as promoters in silver catalysts.
~; Among those anions associated with the cation used in preparing silver-con~aining catalysts em-ployed in direct epoxidation reactions that have been suggested as being suitable include carboxylates, for example, formate, acetate, malonate, oxalate, lac-tate, tartrate, and/or citrate, and inorganic salts, such as carbonates, bicarbonates, phosphates, ni-trates, and/or nitrites, chlorides, iodides, bro-mates, and isopropoxides. However, although many examples may be found in the literature indicating that such compounds are suitable, numerous patents, such as U. S. Patents 3,962,136; 4,012,425;
4,066,575; 4,207,210; and 4,471,071, suggest that no unusual effectiveness, particularly with regard to catalytic activity, is observed with any particular ~3~
anion of an alkali metal promoter. U. S. Pa~ents 4,007,135; 4,094,889; 4,125,480; 4,226,782;
4,235,757; 4,324,699; 4,342,667; 4,356,312;
4,368,144; and 4,455,392 disclose that potassium nitrate may be added to the catalyst as a suitable promoting ma~erial. Potassium nitrat:e may also be formed in situ when a carrier material is treated with certain amines in the presence of potassium ions as, for instance! when silver is introduced to a 1~ carrier material in a silver-impregnating solution containing an amine and potassium ions, followed by roasting.
A number of compounds have been proposed in the literature as additives to the feedstream or reactants to improve the efficiency of the direct, silver-catalyzed oxidation of alkenes to alkene oxides. For example, Law and Chitwood ~U. S. Patene 2,194,602) disclose the use of a "repressantr, i.e., anti-catalyst, such as ethylene dichloride, ch~orine, 2~ sulfur chloride, sulfur trioxide, nitrogen dioxide, or other halogen-containing or acid-forming mater-ials. Numerous additional anti-ca~alysts are pre-sented by the same patentees in U. S. Patent 2,279,469. The anti-catalysts, broadly listed in categories such as halogens and compounds containing halogen, hydrocarbons, compounds containing carbon, hydrogen and oxygen, compounds containing sulfur, and compounds containing nitrogen are represented and, in addition to those compounds already mentioned above, additional representative compounds include, as ni-trogen-containing compounds, nitric oxide, ammonia, amines such as ethylenediamine, diphenylamine and analine, nitro compounds such as o-nitroanisole and o-nitrotoluene as organic oxygen-containing organic compounds, alcohols such as methyl, ethyl and iso-propyl alcohols~ ethers such as isopropyl and dibutyl ethers, as well as glycol ekhers, ketones such as methyl ethyl ketone and acetone, as hydrocarbons such as benzene, and N-hexane; sulfur compounds such as sulfur dioxide, hydrogen sulfide and diethylsulfide;
chlorine-containing compounds such as carbon tetra-chloride, chlorobenzene and dichloroethyl ether.
Berl (U. S. Patent 2,270,780) lists a number of com-pounds as anti-detonating or anti-knock materials to control the oxidation of ethylene and propylene to their oxides. Oisclosures of other feedstream addi-tives used in the production of alkene oxides, parti-cularly halogen compounds, may be found in U. S.
Patents 2,279,470; 2,799,687; 3,144,416; 4,007,135;
4,206,128; and 4,368,144. In addition, EPO Patent 0,003,642 and U. R. Patent Application 2,014,133A
disclose processes for the production of olefin ox-ides employing silver-containing catalysts in which a chlorine-containing reaction modiier and a nitrite or nitrite-forming substance are described. Rumanian Patent 53,012, published December 2, 1971, discloses a direct, silver-catalyzed direct epoxidation proce-dure which employs oxides of nitrogen in the feed-stream. U. K. Patent 524,007 includes ethylene di-chloride or nitrogen dioxide in the feedstream of a silver-catalyzed epoxidation procedure.
Although much of the art discussed above has resulted in improvements in the efficiency, activity or stability of the catalytic system, many of the -22- lZ~3~
improvements have individually been rather slight.
In some of the catalytic systems, gains in one of these performance parameters have been frequently offset by losses in another; that is, enhancement of one index of performance has been accompanied by a deleterious effect on another of the indices. For example, if a reaction system is designed which has a very short useful life, the system may be commer-cially impractical even though the efficiency and initial activity o the catalyst are outstanding.
Accordingly, a system that provides an increase in the efficiency of the overall catalytic reaction system, while only minimally affecting the activity and useful life of the catalyst, or perhaps increas-ing one o these performance indices, would be parti-cularly bene~icial.
The presence of leachable sodium in a silver catalyst employed for epoxidation tends, in some instances, to improve the efficiency of the system ~20 under epoxidation conditions generally used. In the ;presence of CO2 and certain efficiency-enhancing compounds, however, sodium exhibits deactivating and effective life-shortening effects on epoxidation ca~,ysts and systems. The loss of stability or life-shortening effect may be so marked, particularly when the sodium is added as a promoter, that any gains in efEiciency provided by the sodium are lost several days after the catalyst is placed in ser-vice. In many commercially used epoxidation reactors the effluent stream contains relatively high propor-tions of unreacted alkene. To diminish losses of the alkene, the effluent stream is recycled and i~tro-duced to the reactor with the feedstream. Since efficiency in such reactions never reaches 100 per-cent, the effluent stream al~ays contains some carbon ~ -23~ 3~r~
dioxide. In a reactor in which the effluent stream is recycled to the reactor, therefore, the feedstream always contains some carbon dioxide which, in combin-ation with sodium and certain efficiency-enhancing compounds, results in losses of activity and stabil-i~y of the catalyst and system. Commonly, the carbon dioxide is removed by a scrubbing device, such as a Benfield scrubber, placed in the effluent stream between the effluent outtet and the reactor inlet.
Such devices require, however, a substantial capital expenditure and additional plant space. The catalyst and process of the present invention diminish the deactivating and life-shortening effects of CO2.
Disclosure Of The Invention:
The present invention is directed to a high ~; performance catalytic process for epoxidation of alkene in the presence of an oxygen-containin~ gas which comprises contacting the alkene and the oxygen-containing gas under epoxidation conditions in the ; presence of at least one efficiency-enhancing gaseous member of a redox-half reaction pair and a solld catalyst. The catalyst contemplated by ~ present ; 25 invention comprises a catalytically-effective amount of silver on a solid support and an efficiency-enhancing amount of at least one efficiency-enhancing salt of a member of a redox-half reaction pair. The support has less than about 50 and most frequently less than about 20 parts per million, by weightj of leachable sodium.
The invention, described in greater detail be-low, is also directed to a catalyst suitable for use in a process in which an epoxide is formed from an alkene. The catalyst of the present invention, as -24- ~ 3~9~
suggested above, comprises a catalytically-effective amount of silver on 3 substantially inert support and an efficiency-enhancing amount of at least one effi-ciency-enhancing salt of a member of a redox-half reaction pair. The support contains less than about 50 and most frequen~ly less than about 20 parts per million, by weight, of leachable sodium.
The present invention provides a catalytic sys-tem which includes a stable catalyst even when used with recycled effluent streams containing carbon dioxide. In some aspects, the present invention allows a collateral benefit in that it obviates the need for a costly scrubbing unit in the effluent stream while still maintaining desired efficiencies and activities ~or useful periods of time.
In additlon to providing an enhanced stability, the present invention also furnishes an additional benefit of enhanced efficiency.
2~ Brief Descri~on Of The Drawings-Figure 1 is a graphical comparison of aging rates or plo~s of activity (percent ethy~ene oxide in the outlet) of a catalyst according to the present invention having low sodium and one having 80 ppm sodium;
Figure 2 is a graphical comparison similar to Figure 1 comparing a catalyst having 40 and 100 ppm of sodium, respectively, and a feedstream having 3 percent CO2; and Figure 3 is a graphicaI comparison of the cata-lysts and conditions o~ Figure 2 in which effi~ien-cies are compared.
:, -25- ~Z~3~
Detailed DescriPtion Of The Invention:
The present invention is directed to a process for the vapor phase oxida~ion of alkenes to alkene 5 oxides, i.e., an epoxidation process, in the presence of an oxygen-containing gas and to the silver cata-lysts employed therein.
The process and catalyst of the present inven-tion are useful in the epoxidation of the alkenes 10 ethylene and propylene, the epoxides of which are in great demand for use as intermediates in producing such materials as polymers, surfactants, synthetic fibers and antifreeze. However, the present inven-tion is not limited to these compounds but may be used to oxidize cyclic and acyclic alkenes which are in the gaseous state or have signiicant vapor pres-sures-under epoxidation conditions. Typically these compounds are characterized as having on the order of 12 carbon atoms or less which are gaseous under epox-idation conditions. In addition to ethylene andpropylene, examples of alkenes which may be used in the present invention include such compounds as bu-tene, dodecene, cyclohexene, 4-vinylcyclohexene, sty-rene and norbornene.
Supeort:
The support material used in the present inven-tion may be any solid! porous, reractory material which can withstand the roasting temperatures, if that is the method employed to reduce the silver to its free metallic state, and which can also withstand the temperatures employed within the reactor during the epoxidation process. Regardless of the method used to reduce the silver, the support should also be ~ -26-~3~316 able to withstand the temperatures employed within the reactor under epoxidation process conditions.
The support should not have any undue deleterious effect on the performance of the system. Examples of - S suitable materials include magnesia~ zirconia, sili-ca, silicon carbide, and alumina, preferably alpha-alumina.
The carrier materials of the present invention may generally be described as porous or microporous, 10 having median pore diameters of about 0.01 to about 100 microns, preferably about 0.5 to about 50 mi-crons, and most preferably about 1 to about 5 mi-crons. Generally, they have pore volumes of about 0.6 to about 1.4 cc/g, preferably about 0.8 to about 15 1.2 cc/g. Pore vol~lmes may be measured by any con-ventional technique, such as conventional mercury porosity or water absorption technique.
Generally improved results have been demon-strated when the support material is compositionally pure and also phase pure. By "compositionally pure"
is meant a material which is substantially a single substance, such as alumina, with only trace impuri-ties being present. "Phase purity" or like terms refer to the homogeneity of the support with respect to its phase. In the present invention, alumina, having a high or exclusive alpha-phase purity (i.e., alpha-alumina), is preferred. Most preferred is a material composed of at least 98 percent, by weight, of alpha-alumina. Under some conditions, as when used in conjunction with the salt and gaseous members of redox-half reaction pairs, even small amounts of sodium can adversely affect the activity and useful life of the catalyst, i.e., have a deactivating ef-fect on the catalyst. Improved results have been observed when the support contains leachable sodium -27~
levels less than about 50 parts per million (ppm) by weight, preferably less than about 40 ppm, based on the weight of the to~al support. Most preferred are supports having a leachable sodium content of less 5 than about 20 ppm, by weight. Supports which are also useful in the present invention are those having less than a catalyst deactivating amount of ~otal sodium. This corresponds in some instances to a concentration of about 200 ppm. Suitable alpha-10 aluminas having concentrations of leachable sodiumbelow 50 ppm may be obtained commercially from sup-pliers, such as the Norton Company.
The low sodium carrier materials of the present invention may be prepared by any conventional method L5 of removing sodium from a solid, particularly mineral or mineral-type material suitable in other respects as a support material. Such treatment should not, however, substantially adversely affect the mechani-cal O structural characteristics of the support material nor chemically alter the support material in a manner which adversely affects the catalytic per-formance indices of efficiency, activity, or catalyst stability. Typically, the techniques involve extrac-~L~n and/or volatilization of the sodium present. A
suitable extraction procedure may involve conversion of the sodium present to a more easily extractabIe material either in the same step in which extraction takes place or in separate conversion and extraction steps. A suitable volatilization procedure typically 3~ includes an initial step in which the sodium present in the support is converted to a material which is volatile upon heating. In some instances, it ~ay be preferable to initially extract as much of the sodium present as possible, followed by a volatilization procedure to remove-residuaI sodium. Exemplary of .~ .
~ 13457 ~2~3~L9~
extrac~ion or leaching procedures is treatment of the support material with a mineral acid, particularly nitric acid in a concentration of about 10 percent, by volume, at a temperature of about 90 degrees C, 5 for a period of about l hour and thereafter washing the support with water. The rinsed support material i5 then dried at a temperature of from abou~ lO0 to 1,000 degrees C for a period of from about 1 to about 3 hours. The leaching procedure described above also 10 forms the basis of a method of analysis of ~leachable sodium~ and the definition of this term.
Alternatively, suitable alpha-alumina support materials may be prepared so as to obtain sodium concentrations below 50 ppm by the method described 15 by Weber et al in U. S. Patent 4,379,134.
A preferred procedure for preparing a low-sodium support involves treatment of a support material, particularly gamma-alumina, with an organic or inor-ganic fluorine-co~taining substance, preferably in aqueous solution, and thereafter firing the treated support material at a suitable temperature. In the present invention, the support material may either be extruded by conventional techniques known to the art and formed into pellets after fluori~.~ reatment and before firing or, alternatively, formed, i.eO, ex-truded, pellets may be fluorine-treated and then fired. The fluorine-containing substance i9, prefer-ably, a volatile material or one which can be readily volatilized under firing conditions. Examples of ~ suitable fluorine-containing materials include alumi-num trifluoride, ammonium fluoride, hydrofluoric acid, and dichlorodifluoromethane.
The fluorine compound is used in an amount suf-ficient to remove a major portion of the sodium ; 35 present in the sample. This amount will, o~ course, 33~
vary with the amount of sodium present in the sample but will also depend on other factors, such as the condition under which the support material is treated, such as the firing temperature and heating S rate, as well as the depth of ~he b~d of material being treated, the amount of gamma-alumina being treated, the level of contamination of the gamma-alumina, and how well the firing chamber is sealed.
Typically, a suitable amount of fluorine compound is 10 not more than about 3 percent, by weight, based on the weight of the support material being treated.
Preferably, the fluorine compound is present in an amount of about 0.8 to about 2 percent, by weight. A
suitable firing temperature for fluorine-treated alumina is generally less than about 1,200 degrees C, preferably from a temperature over 750 to about 1,100 degrees C. The rate of heating depends in part on the amount of fluorine compound used. Thus, with lower levels of fluorine, support materials having desirable properties are generally obtained with rapid heating. As used herein, "rapid heating"
; refers to heating from room temperature to the - desired temperature in about 1 hour. However, with lower concentrations of fluorine compound, slower heating rates are yenerally preferred to achieve the same type of product. The "slow heating" treatments generally consist of heating from room temperature to about 750 degrees C in about 0.5 to 1 hour and from 750 degrees C to the final temperature at a rate of about 100 degrees C per hour.
The treatment of support materials with fluo-rine-containing substances may provide a collateral benefit in converting the support material to one having a preferred "platelet" morphology. This sup-port is described by Notermann in an application .
~ 30 ~3~
entitled "Improved Catalytic System for Epoxidationof Alkenes", in Canadian Application No. 515,865, filed August 13, 1986, in the name of Thomas M.
Notermann.
The support particles are preferably formed into aggregates or "pills" of a size and configuration to be usable in commercially operated ethylene dioxide tubular reactors. These pills may be formed by conventional extrusion and firing, as discussed above. When gamma-alumina is the precursor to an alpha-alumina support material, treatment with the fluorine recrystallizing agent may be preformed before or after extrusion. The pills generally range in size from about 2 mm to about 15 mm, preferably about 3 mm to about 12 mm. The size is chosen to be consistent with the type of reactor employed. In general, in fixed bed reactor applicationsJ sizes ranging from about 3 mm to about 10 mm have been found to be most suitable in the typical tubular reactors used in commerce. The shapes of the carrier aggregates useful for purposes of the present invention can vary widely. Common shapes include spheres and cylinders, especially hollow cylinders.
Other shapes include amphora (such as defined in U.S.
Patents 3,848,033, 3,966,639 and 4,170,569), amorphous, Raschig rings, saddles, cross-partitioned hollow cylinders (e.g.~ having at least one partition extending between walls), cylinders having gas channels from side wall to side wall, cylinders having two or more gas channels, and ribbed or finned structures. While the cylinders are often circular, other cross-sections, such as oval, hexagonal, quadrilateral, trilateral, etcetera, may be useful.
.~, ~ 13457-C
,A.
-31- ~3~6 Ca~alysts:
The catalysts of the present invention are con-ventional to the extent that silver is coated or deposited on and/or within a solid porous carrier.
Any known method of introducing the silver to the catalyst support may be employed. Numerous examples and procedures are given in the patents discussed above. In brief, in a coating or suspension process a slurry, preferably aqueous, of ~he active catlytic material, such as silver or its oxide, is applied to the support to form a coherent silver layer on the support. In the preferred impregnation process, a solution of a soluble salt or complex of silYer in an amount sufficient to deposit the desired weight of silver upon the carrier is dissolved in a suitable solvent or "complexing/solubilizing~ agent. This solution may be used to impregnate a porous catalyst support or carrier by immersing the carrier in the silver-containing impregnating solution. Alterna-tively, the support may be sprayed or sprinkled with the impregnating solution. The excess solution may then be allowed to drain off or the solvent may be removed by evaporation under reduced pressure at a suitable temperature. The silver salt or compound used to form the silver-containing impregna~ing solu-tion in a solvent or a complexing/solubilizing agent is not particularly critical and any silver salt or compound generally known to the art which is both soluble in and does not react with the solvent or complexing/solubilizing agent to form an unwanted product may be employed. Thus, the silver may be introduced to the solvent or complexing/solubilizing agent as an oxide or a salt, such as nitrate or car-boxylate, for example, an acetate, propionate, buty-,9~i rate, oxalate, malonate, malate, maleate, lactate,citrate, phthalate, generally the silver salts of higher fatty acids, and the like.
The chemical practitioner may choose from a 5 large number of suitable solvents or complexing/solu-bilizing agents to form the silver-containing impreg-nating solution. Besides aaequately dissolving the silver or converting it to a soluble form, a suitable solvent or complexing/solubilizing agent should be 10 capable of being readily removed in subsequent steps, either by a washing, volatilizing or oxidation proce-dure, or the like. The complexing/solubilizing agent, preferably, should also permit solution to provide silver in the finished catalyst to the extent of about ~ to about 60 percent silver or higher, based on the total weight of the catalyst. It is also generally preferred that the solvents or com-plexing/solubilizing agents be readily miscible with water since aqueous solutions may be conveniently em-ployed. Among the materials found suitable as sol-vents or complexing/solubilizing agents for the pre-paration the silver-containing solutions are alco-hols, including g]ycols, such as ethylene glycol ~U. S. Patents 2,825,701 to Endler et al and 3,563,914 to Wattimena), ammonia ~U. S. Patent 2,463,228 to West et al), amines and aqueous mixtures of amines (U. S. Patents 2,459,896 to Schwartz, 3,563,914 to Wattimena, 3,702,259 to Nielsen, and 4,097,414 to Cavitt, and carboxylic acids, such as lactic acid (U. S Patents 2,477,435 to ~ries and 3,501,417 to DeMaio) Typically, a silver-containing solution is pre-pared by dissolviny silver in a suitable solvent or complexing/solubilizing agent as, for example, a mixture of water, ethyienediamine, oxalic acid, sil-ver oxide, and monoethanolamine. The solution is then mixed with support particles and drained.
Thereafter the particles are suitably dried.
After impregnation, the silver-impregnated car-S rier particles are treated to convert the silver salt or complex to silver metal and thereby effect deposi-tion of silver on the surface of the support. As used herein, the term "surface", as applied to the support, includes not only the external surfaces of 10 the carrier but also the internal surfaces, that is, the surfaces defining the pores or internal portion of the support particles. This may be done by treat-ing the impregnated particles with a reducing agent, such as oxalic acid or alkanolamine and/or by roast-ing, at an elevated temperature on the order oE about100 to about 900 degrees C, preferably about 200 to about 650 degrees C to decompose the silver co~pound and reduce the silver to its free metallic state.
The duration of roasting is generally for a period of about 1 to about 10 minutes for temperatures above 200 degrees C, depending on the temperature used, and is commonly effectuated in a hot-air belt roaster.
The concentration of silver in the finished catalyst may vary from about 2 per~ to 60 percent, by weight, based on the total weight of the catalyst, more preferably the silver concentration ranges from about 8 percent to about 5~ percent, by weight. When a ~high silver" content catalyst is preferred, the silver ranges from about 30 to about 60 percent, by weight. The preferred concentration for "low silver"
content catalysts ranges from about 2 to about 20 weight percent. When a catalyst having a silver concentration in the preferred high silver range is prepared, the silver is preferably introduced in a series of at least two sequential impregnation and ~` -34- ~3~
roasting cycles, as discussed in greater detail be-low. Lower silver concentrations are preferred from a capital expense standpoin~. Xowever, the optimum silver concentration for a particular catalyst should also take into consideration increased productivity resulting from performance characteristics, such as catalyst activity, system efficiency and the rate of catalyst aging. In many instances higher concentra-tions of silver are preferred since they demonstrate levels of enhanced performance, particularly catalyst stability, which compensates for the greater capital expenditure.
Efficiency-Enhancinq Compound:
A preferred aspect of the present invention includes an efficiency-enhancing amount of at least one efficiency-enhancing salt of a member of a redox-half reaction pair. The term "redox-half reaction"
~`20 is defined herein to mean half-reactions like those found in equations presented in tables of standard reduction or oxidation potentials, also known as standard or single electrode potentials, of the type ;found in, for instance, "~andbook of Chemistry", N.
A. Lange, Editor, McGraw-Hill Book Company, Inc., pages 1213-1218 (1961) or "CRC Handbook of Chemistry and Physics", 65th Edition, CRC Press, Inc., Boca Raton, Florida, pages D155-162 (1984). The term nredox-half reaction pair" refers to the pairs of atoms, molecules or ions or mixtures thereof which undergo oxidation or reduction in such half-reaction ~equations. Such terms as redox-half reaction pairs -are used herein to include those members of the class of substance which provide the desired performance ~35 enhancement, rather than a meshanism of the chemistry :
occurring. Preferably, such compounds, when associ-ated with the catalyst as salts of members of a half reaction pair, are salts in which the anions are oxyanions, preferably an oxyanion of a polyvalent 5 atom, that is, the atom of the anion to which oxygen is bonded is capable of existing, when bonded to a dissimilar atom, in different valence states. Potas-sium is the preferred cation and the preferred anions are nitrate, nitrite and other anions capable of lO undergoing displacement or other chemical reaction and forming nitrate anions under epoxidation condi-tions. Preferred salts include KN03 and KN02, with KN03 being most preferred.
Introduction 0~ Ef~iciency-Enhancing Salt To The Carrier:
The efficiency-enhancing salt of a member of a redox-half reaction pair may be introduced to the catalyst in any known manner. Various sequences of impregnating or depositing silver and efficiency-enhancing salt on the surfaces of the carrier may be employed. Thus, impregnation and deposition of sil-ver and an efficl~ncy-enhancing salt of a member of a redox-half reaction pair may be effected coinciden-tally or sequentially, i.e., the salt or salts may be deposited prior to, during or subsequent to silver addition to the carrier. When more than one salt of a member of a redox-half reaction pair is employed, they may be deposited together or sequentially.
Typical, and in many cases preferred, of such~me~hods include concurrent, or coincidental, impregnation in which the solution which is used to impregnate the support with silver also contains the dissolved effi-ciency-enhancing salt member of a redox-half reaction pair. This procedure permits introduction of both the silver compound and the efficiency-enhancing salt to the support in a single step and solution. The other commonly employed method is the sequential impregnation of the support in which initial intro-duction of the silver-containing solution or effi-ciency-enhancing salt solution (depending upon the sequence employed) is followed by drying o the sil-ver-containing support (and heating and/or chemical reduction of the silver if this is the first added substance). This support is then impregnated with a solution of the second substance, that is, the effi-ciency-enhancing salt (if the silver was the first added substance). In order to perform the former L5 procedure, i.e., coincidental impregnation, the effi-ciency-enhancing salt must be soluble in the same solvent or complexing/solubilizing liquid used with the silver-impregnating solution. With the sequen-tial procedure in which the silver is added firstl any solvent capable of dissolving the salt which will neither react with the slIver nor leach it from the support is suitable. Aqueous solutions are generally preferred, but organic liquids, such as alcohols, may also be employed. Suitable procedures for effectin~
introduction of the efficiency-enhancing salt to the solid support may be found in many of the patents listed above.
In some instances, the coincidental method of preparation of the catalyst is decidedly less prefer-red or may not be used as, ~or examptel where a bari-um, calcium or magnesium salt is intended to be solu-bilized and the solution contains materials which may precipitate the cation as, for instance, a carboxylic acid or dicarboxylic acid such as oxalic acid.
; 35 ~37~ 1 Z ~3 ~
The salt of a member of a redox-half reaction pair is added in an amount sufficient to enhance the efficiency of the epoxidation reaction. The precise amount will vary depending u~on such variables as the 5 gaseous efficiency-enhancing member of a redox-half reaction used and concentration thereof, the concen-tration of other components in the gas phase, the amount of silver contained in the catalyst, the sur-face area of the support, the process conditions, 10 e.g., space velocity and temperature, and morphology of support. Generally, however, a suita~le range of concentration of the added efficiency-enhancing salt, calculated as cation, is about 0.01 to about 5 per-cent, preferably about 0.02 to about 3 percent, by weight, based on the total weight of the catalyst.
Most preferably the salt is added in an amount of about 0.03 to about 2 weight percent.
It has been noted that when conventional analyses have been conducted with catalysts prepared by co-impregnation with silver and efficiency-enhancing salt, not all the anion associated with the cation has been accounted for. For example, cata-lysts prepared by co-impregnation with a potassium nitrate solution have been analyzed by conventional techniques and about 3 moles of the nitrate anion have been observed for every 4 moles of the potassium cation. This is believed to be due to limitations in the conventional analytical techniques and does not ~ necessarily mean that the unaccounted for anions are not nitrate. For this reason, the amount of the efficiency-enhancing salt in the catalyst is given, in some instances, in terms of the weight percentage of the cation of the efficiency-enhancing salt (based on the weight of the entire catalyst), with the un-derstanding that the anion associated with the cation ~ 13457 :~
, ~ -38- ~93~9~
is also present in the catalyst in an amount roughly proportional (on a molar basis) to the ca~ion.
As indicated above, when the catalyst is in-tended to contain higher concentrations of silver, it S is generally preferred to use multip}e cycles of impregnation and reduction to elemental silver. This seems to result in a more uniform distribution of silver throughout the catalyst pill. As with the catalyst containing lower amounts of silver intro-1~ duced in a single impregnation, the introduction ofthe efficiency-enhancing salt of a member of a redox-half reaction pair may also be introduced in a se-quential or coincidental procedure. Regardless of the method employed, a first cycle includes impregna-5 tion only with silver in an appropriate complex-ing/solubilizing agent followed by reduction to metallic silver, such as by roasting. (This is known as a "silver only" procedure.) If the sequential procedure is to be followed, the first cycle of im-20 pregnation and reduction is repeated one or more times. The final step includes impregnation with a solution of the efficiency-enhancing salt of a member of a redox-half reaction pair, draining and drying, as discussed above.
When the coincidental or concurrent procedure is employed in preparing catalysts containing high con-centrations of silver, the first cycle is the same as in the sequential technique, i.e., a silver only procedure~ This is then followed either directly by 3~ a conventional coincidental impregnation (i.e., im-pregnation with a solution containing both silver in a soluble form and the efficiency-enhancing salt of a member of a redox-half reaction pair, followed by a reduction of silver to its elemental form, as by roasting) or by one or more repetitions of the im-~ _39- .~ 3~
pregnation cycle with a silver only procedure inter-posed between the silver only cycle and the coinci-dental impregnation and reduction cycle with a solu-tion of silver and at least one efficiency-enhancing salt. Suitable results have been obtained with both the sequential and coincidental procedures with two silver impregnation cycles, although there are indi-cations that greater amounts of silver with more uniform distribution of silver throughout the pill can be obtained by three or possibly more silver-impregnation cycles. High silver-containing cata-lysts prepared by the coincidental impregnation tech-nique provide somewhat better performance than those prepared by the sequential technique.
EpoxidatLon Procedure:
As in conventional processes of this type, an alkene and an oxygen-containing gas are brought to-gether in a reactor in the presence of a suitableepoxidation catalyst under epoxidation conditions.
Typical epoxidation conditions include temperatures within the reaction zone of the reactor on the order of about 180 to 300 degrees C and pressures from about 1 to about 30 atmospheres.
The gaseous eficiency-enhancing member of a redox-half reac~ion pair may generally be supplied to the reaction zone within the reactor by introducing the component to the feedstream containing alkene and oxygen Under commercial epoxidation conditions, such as those used in the present invention, the feedstream also contains a gas phase halogen com-pound, such as an alkyl halide, a hydrocarbon, and, when the effluent stream from the reactor is recy-cled, unreacted alkene. When recycle of the eefluent -~ _40~ 3~
stream is used, carbon dioxide may also be present.
The presence and amount of carbon dioxide depends, at least in part, on whether a scrubbing device is em-ployed.
The terms "gaseous member of a redox-half reac-tion pair~, "gaseous efficiency-enhancing member o~ a redox-half reaction pair", or like terms referred to herein have a meaning similar to that for the "sal~
of a member of a redox-half reaction pair" or like terms, defined above. That is, these terms refer to members of half-reactions, represented in standard or single electrode potential tables in standard refer-ence texts or handbooks which are in a gaseous state and are substances which~ in the reaction equations lS represented in the texts, are either oxidized or re-duced~ The preferred gaseous efficiency enhancing materials are compounds containing an element capable o~ existing in more than two valence states, prefer-ably nitrogen and another element which is, prefer-ably, oxygen. Examples of preferred gaseous effi-ciency-enhancing members of redox-half reaction pairs include at least one of NO, NO2, N2O4, N2O3 or any gaseous substance capable of forming one of the aforementione~ gases, particularly NO and NO2, under ~5 epoxidation conditions, and mixtures of one of the foregoing, particuIarly ~O, with one or more of PH3, CO, SO3, SO2, P2O5, and P2O3. NO is most preferred as the gaseous efficiency-enhancing compound.
Although in some cases it is preferred to employ members of the same half-reaction pair in the reac-tion system, i.e., both the efficiency-enhancing salt member associated with the catalyst and the gaseous member in the feedstream, as, for example, with a preferred combination of potassium nitrate and nitric oxide, this is not necessary in all cases to achieve ;3L2~3~;
satisfactory results. Other combinations, such as KNO3/N2O3, KNO3/NO2~ KN3/N24~ KNO3/S2' KN2/N' KNO2/NO2, and KNO3/a mixture of SO2 and NO, may also be employed in the same system. In some instances, S the salt and gaseous members may be found in differ-ent half-reactions which represent the first and last reactions in a series of half-reaction equations of an overall reaction.
The gaseous efficiency-enhancing member of a redox-half reaction pair is also present in an amount sufficient to enhance the performance, such as the activity of the catalyst, and, particularly, the efficiency of the epoxidation reaction. The precise amount is determined, in part, by the particular efficiency-enhancing salt of a member of a redox-half reaction pair used and the concentration thereof, the particular alkene undergoing oxidation, and by other factors noted above which influence the amount of efficiency-enhancing salt of a member of a redox-half reaction pair. Typically a suitable concentration of the gaseous member of a redox-half reaction pair for epoxidation of most alkenes, including propylene, is about 0.1 to about 2,000 ppm, by volume, of the gas-eous feedstream when N2 is used as ballast. When a preferred gaseous member of a redox-half reaction pair, such as NO, is used in the epoxidation of pro-pylene, the preferred concentration is about 2,000 ppm, by volume, with an N2 ballast. However, when ethylene is being oxidized, a suitable concentration for ethylene is from about 0.1 to about 100 ppm, by volume, of the gaseous feedstream components. Pref-erably, the gaseous efficiency-enhancing member of a redox-half reaction pair is present in an amount of about 1 to about 80 ppm when about 3 percent, by ~ .
-42~ 9~
volume, CO2 is present. When nitric oxide is em-ployed as the gaseous efficiency enhancing compound in an ethylene epoxidation system, it is present in an amount of about 0.1 to about 60 ppm, preferably about l to about 40 ppm, when CO2 is present.
The oxygen employed in the reaction may be in-troduced to the reactor either as air, commercially pure oxygen or other substance which under epoxida-tion conditions both exists in a gaseous state and forms molecular oxygen. The gaseous components which are supplied to the reaction zone, or that region of the reactor where reactants and catalyst are brought together under epoxidation conditions, are generally combined before being introduced to the reactor. The reactors in which the process and catalyst of the present invention are employed may be of any type known to the art.
In addition to an alkene, oxygen, and the gas-eous efficiency-enhancing member, the feedstream also contains a halogen-containing compound, preferably an organic halide, including both saturated and unsatur-ated halides, such as ethylene dichloride, ethyl chloride, vinyl chloride, methyl chloride and methy-lene chloride. Preferably, ethyl chloride is em-ployed as the halogen-containing compound. The amount of halide employed will vary depending upon a variety of factors, including the particular alkene being oxidized and the concentration thereof, the particular efficiency-enhancing gaseous component and salt ar.d the concentrations thereof, as well as other ~ factors noted above as influencing the amount of ; efficiency-enhancing gaseous compound and salt.
suitable range, however, of concentration for the halogen-containing compound is typically about 0.1 to about 60 ppm, by volumie, of the gaseous makeup feed-' .
~ 13457 _ ~ Z~ 3 ~3~
stream. In addition, a hydrocarbon, such as ethane,can be included in the feedstream. The feedstream may also contain a diluent, such as nitrogen, or other inert gas, particularly when air is used as the 5 oxygen containing gas. Varying amounts of carbon dioxide and water vapor may also be present, depend-ing upon whether means have been provided to remove such substances from the effluent stream prior to combination of at least a portion of the effluent stream with the inlet stream. Other than the gaseous efficiency-enhancing member of a redox-half reaction pair, the other components are present in convention-ally used amounts, as shown in the following table.
Volume Percent ~or ppm) Component for Propylene Oxidation propylene about 2 to about 50 oxygen about 2 to about 10 20 alkyl halide about 5 to about 2,000 ppm hydrocarbon 0 to about 5 carbon dioxide up to about 15 nitrogen remainder or other ballast gas, e.g., methane -44- .~Z~3~
Volume Percent (or ppm3 Component for Ethylene Oxidation ethylene at least about 2, often about 5 to about 50 oxygen about 2 to about 8 alkyl halide about 0.1 to about 60 ppm hydrocarbon about 0 ~o about 5 carbon dioxide up to about 7 10 nitrogen remainder or other ballast gas, e.g., methane When higher alkenes, such as those previously discussed, are epoxidized, conditions and concentra-tions typically used for the epoxidation of propylene may be employed.
Standard Alkene Oxide Process Test Conditions-The successful commercial production of alkene oxides, particularly ethylene oxide, by the silver-catalyzed oxidation of alkene, particularly ethylene, depends upon a variety of factors. Many of these factors influence, either directly or indirectly, the performance indices, such as the efficiency of the catalytic system, the activity or the aging rate, i.e., stability, of the catalyst. The manner in which catalysts and catalytic systems are evaluated in the laboratory strongly influences the values obtained for these parameters. Techniques and exper-iments designed to assess such catalysts and cata-lytic systems commonly employ microreactors (i.e., tiny tubular reactors for testing crushed catalyst particles) or back-mixed autoclaves of the Berty type . .
_~5- ~Z93~
ti~e.~ larger reactors which test full-sized catalyst pellets and generally employ full gas recycle) as described in Figure 2 of the article by J~ M. 8erty, "Reactor For Vapor Phase-Catalytic Studies", Chemical 5 ~n~ineerinq Progress, 70, Number 5, pages 78-84 (1974), and particularly Figure 2. Microreactors are capable of yielding, in most test situations, the highest efficiency numbers, typically approximately the same as or somewhat greater than those obtainable in commercial tubular reactor operations employing the same catalysts in non-crushed condition. Back-mixed autoclaves commonly provide lower efficiency values because, although conditions can be varied, generally the entLre catalyst is exposed to the out-let gas which has the lowest concentration of re-actants and the highest concentration of products.
Values obtained using one type of reactor are seldom directly comparable to those obtained in another reactor system. As a result, claims of superior results or the desirabi~ity of one catalyst over another are preferably based on tests conducted under controlled and comparable conditions.
Although the conditions set forth supra may be employed boti~ for reactors employed in commercial production as well as those employed in a laboratory, as a basis of comparison, the catalysts and catalytic systems for epoxidation of ethylene employed in the examples set forth below have been tested u*der com-parable conditions known as Standard Alkene Oxide Process Test Conditions, or Standard Test Conditions (referred to hereinafter as STC). The STC employed for testing and characterizing the catalysts and the catalytic systems of the present invention involve the use of a standard back-mixed bottom-agitated nMagnedrive" autoclave or Berty autoclave, as de-46~ 3 scribed above.
In discussing the enhancement of efficiencyprovided by the present invention, it may be noted that, when an efficiency-enhancing amount of a salt of a member redox-half reaction pair is employed, an efficiency of at least about 84 percen~ i5 obtained under Standard Test Conditions. "S~andard Test Con-ditions" may be deined as comprising the following:
by volume, 30 percent C2H4, 8 percent 2~ 5 ppm ethyl chloride, 5 ppm, by weight, NO, no added C2H6 or CO2, N2, ballast, 240 degrees C, 275 psig, gas hourly space velocity (GHSV) = 8,000 hr 1.
Although the present invention can be used with any size and type of alkene oxide reactor, including both fixed bed and ~luidized bed reactors known to the art, it ls contemplated that the present inven-tion will ind most widespread application in standard fixed bed, multi-tubular reactors. These generally include wall-cooled as well as adiabatic or non-wall-cooled reactors. Tube lengths may typically range from about 5 to about 60 feet but will fre-quently be in the range of from about 15 to about 40 feet. The tubes may have internal diameters from about 0.5 to about 2 inches and are expected to u~
typically from about 0.8 to about 1.5 inches. G~SV
range from about 16,000 to about l,000 hr~l.
Typically GHSV values range from about 2,000 to about 8,000 hours~l at pressures from about 1 to about 30 atmospheres, commonly about 10 to about 25 atmos-pheres.
While the invention is susceptible to variousmodifications and alternative forms, certain specific embodiments thereof are described in the examples set forth below. It should be understood, however, that these examples are not intended to limit the inven-` ~~7~ lZ~3~6 tion to the particular forms disclos~d but, on thecontrary, the invention is to cover all modifica-tions, equivalents and alternatives falling within the spirit and scope of the invention.
s Example 1 - Preparation Of Alpha-Alumina Support Havin~o~ Sodium:
Approximately 1,200 grams of 1/4 inch hollow gamma-alumina pills or rings (obtained from ~orton Corporation as Alumina 6573) were soaked for one-half hour in 1 molar NH4F with occasional shaking to li-berate bubbles that formed durinq impregnation.
Excess solution was drained from the rings, which were then dried overnight at 120 degrees C. The dried rings were distributed between four 3 inch diameter x 6 inch deep cylindrical alumina crucibles and were fired in a P. D. H. high-temperature fur-nace. Lids for the crucibles were placed askew so that crucible openings were covered approximately 70 percent to maintain a fluoride atmosphere in the cru-cible but at the same time permit escape of excess fluoride. The firing schedule was one hour to raise the temperature to 700 degrees C, four hours to raise 2S the temperature from 700 to 1,100 degrees C, and a hold temperature at 1,100 degrees C for one hour.
The product had a surface area of 1.56 m~/g and a sodium content of less than 50 ppm.
Example 2 - Sequential Preparation Of A Potassium Nitrate-Containing Suppor~ed Silver Catalyst:
.
Formation of a potassium nitrate-containing supported silver ca~alyst resulted from a multi-step procedure in which a support was initially impreg-~` -48- ~ 2~
nated with a silver-containing solution, the impreg-nated support was roasted, and the silver-inpregnated catalyst was thereafter impregnated with a potassium nitrate solution and then dried.
S The silver-containing solution used in the first step was prepared by dissolving 51.49 grams ethylene-diamine in 51.03 grams of distilled water and stir-ring the mix~ure for a period of 10 minutes. To the stirred solution was slowly added 51 56 grams of 10 oxalic acid dihydrate. The resulting solution was stirred for 10 minutes. To this solution was added, in portions, ga.34 grams silver oxide. The resulting silver-containing solution was thereafter stirred for an additional hour and 18.07 grams of monoethanol-amine was then added to the stirred silver-containing solution. Stirring was continued for an additional 10 minutes. This solution was then diluted to a total volume of 437 ml by addition of distilled ~ater.
2~ In a catalyst-impregnation tube were placed 177.85 grams of an alpha-alumina carrier, similar to that prepare~ in Example 1. A catalyst-impregnation tube is an elongated tube, which in use is arranged vertically. The upper end of the tube is provided with an inlet to supply impregnation solution to the carrier contained in the tube and the lower end with an outlet from which solution may be drained. The - tube is also provided with a means to connect the tube to a vacuum source. Prior to introduction o~
impregnation solution the tube was evacuated. The solution described immediately above was slowly poured into the tube to totally immerse the support. The carrier was allowed ~o remain in the impregnating solution for about l hour to achieve saturation of the support. The unabsorbed solution :~293~96 was thereafter drained from the support with drainlng continuing for about 30 minutes. The wet, impregnated carrier was then roasted in a hot-air belt roaster for 2.5 minutes at 500 degrees C ~66 SCFH air flow) to produce a catalyst containing 11.39 percent silver.
~ pon cooling, 44.57 grams of the roasted, im-pregnated carrier was placed in an impregnation tube and covered with a solution formed by dissolving 2.08 grams potassium nitrate in lO0 ml distilled water.
After covering the roasted silver-containing carrier with the KNO3-containing solution and allowing to stand for 15 minutes, the catalyst pellets were drained on a funnel for 5 minutes. The resulting drained pellets were dried in an oven for 2 hou~s at 120 degrees C, producing a catalyst containing 0.46 percent K, calculated as 1.20 percent KNO3, by weight.
Example 3 - Sequential Preparation Of Sodium- And Potassium Nitrate-Containing Su~orted Silver CatalYst: ~
An impregnated and roasted silver-containing 25` catalyst was prepared as described in Example 2.
Into an impregnation tube was placed 44.57 grams of the silver-containing catalyst (11.39 percent, by weight, Ag) and a solution prepared by dissolving 2.08 grams potassium nitrate and 0.04 grams sodium nitrate in lO0 ml distilled water was placed in the tube after evacuation of the tube to totally cover the silver-containing. The pellets were allowed to stand in the solution for 15 minutes, the excess solution was drained from the pellets on a funnel for 5 minutes, and the impregnated catalyst was oven-~33~9~
dried for 2 hours at 100 degrees C. The catalyst pellets contained, by weight, 0.44 percent K, calcu-lated as 1.15 percent KNO3 , and 0.008 percent ~80 ppm) Na.
Example 4 - Preparation Of A Potassium Nitrate-Containing Silver Catalyst BY A Co-Impre~nation Technique: _ A co-impregnation solution was prepared by plac-ing 18.77 grams of ethylenediamine into a 400 ml beaker and mixing therewith 25 grams of distilled water to form a solution. To the stirred solution was slowly added 18.7 grams oxalic acid and, with continuous stirring, 3$.2 grams of silver oxide was slowly added. When solution was complete, 6.55 grams of monoethanola~ine was added directly to the solu-tion. To the silver-containing solution was added 7.14 gra~s of potassium nitrate solution, 10 percent with respect to potassium (0.258 grams KNO3/g solu-tion). Sufficient water was added to the resulting solution to dilute the solution to 100 ml.
i To make 100 ml of finished catalyst, 53.5 grams of an alpha-alumina support material of the type prepared in Example 1 but fired at a temperature of 1,000 degrees C in the form of quarter-inch ring ` extrudate and having a pore volume of ~.62 g H2O/g support was placed in a suitable container. A source of vacuum was attached to the container and evacuated and thereafter-the silver/potassium-containing im-pregnating solution was added until the carrier was completely covered. After about one hour the excess solution was drained from the catalyst.
Roasting of the impregnated catalyst was con-ducted as indicated above in Example 2. The result-~` sl ~93~
ing catalyst in~luded! by weight, 17.5 percent silverand, as calculated, about 1 percent potassium nitrate.
Example ~ - Sequ~rltial Preparation Of A Potassium Nitrate-Containing Sup~orted Hi~h Sllver Concentr_tion Catalyst A solution containing 17.5 g ethylenediamine, 17.3 g distilled water, 17.5 g oxalic acid, 30.7 g silver oxide, 6.1 g monoethanolamine, diluted to 125 ml, was prepared in the manner described in Example 2.
Into a catalyst impregnation tuhe were placed 43.9 g of an alpha-alumina carriee, similar to that prepared in Example 1, and having a surface area of 1.12 m2/g, a pore volume of 0.8 cc/g, less than 50 ppm, by weight, leachable sodium, and a platelet morphology of the type disclosed in Canadian Application ~o. 515,865. The support pellets were initially vacuum-impregnated at 28 inches mercury vacuum, releasing the vacuum when the pellets were completely covered with the aqueous silver amine solution, permitting them to stand in the amine solution for an additional hour at 1 atmosphere before draining. The impregnated pellets were then belt-roasted at 500 degrees C in an oven having an air flow of 66 SCFH for 2.5 minutes. The material contained 14.9 percent silver as determined by weight gain. This material was then impregnated a second and third time with fresh silver/amine solution having the composition indicated above. The impregnations and belt-roastings were conducted in the same manner as described above. The catalyst material was ~ .
--52~ 3~
then impregnated with KNO3 by placing 67.4 9 of the silver-impregnated pellets into a solution containing 2.1 g KNO3 dissolved in 100 ml distilled water. The KNO3-impregnated silver catalyst material was then 5 dried at 120 degrees C for 1 hour to yield a catalyst containing, by weight, 34.7 percent silver and 0.33 percent K (calculated as 0.86 percent K~03), as de-termined by weight gain.
10 Example 6 - Coincidental Preparation Of A Potassium Nitrate-Containing Supported High Silver Concentration Catalyst:
A silver impregnation solut;on was prepared in a 15 manner similar to that described in Example 2 by mixing 196.8 g ethylenediamine, 195.0 g distilled water, 197.1 g oxalic acid, 345.2 g silver oxide, 69.1 g monoethanolamine and diluting to a total vol-ume of 780 ml with distilled water. After evacuation of an impregnation tube containing pellets of an alpha-alumina support material ~293.1 g) similar to those described in Example 1 and having a B. E. T.
surface area of 1.16 m2/g by a Quantasorb apparatus, the pellets were impregnated by allowing them to stand in the silver impregnation solution for a per-iod of 1 hour and then draining. The impregnated pellets were then belt-roasted at 500 degrees C in a 66 SCFH air flow for 2.5 minutes. As determined by gain in weigh~t, the material contained 24.6 percent silver A co-impregnation solution was prepared in a manner similar to that described in Example 3 by mixing 37.5 g ethylenediamine, 37.2 g distilled ~water, 37.6 g oxalic acid, 65.9 g silver oxide, 13.2 ;;35 g monoethanolamine, and 0.80 g potassium nitrate and diluting to 150 ml total solution with distilled water. The silver-impregnated catalyst pellets (77.8 g) were impregnated by immersing them in the sil-ver/potassium nitrate-impregnating solution for 1 hour and then draining. The resulting pellets were then belt-roasted as described above. The pellets resulting from the two impregnations yielded a mater-ial, as determined by an analysis, containing, by weight, 39.8 percent silver and 0.098 percent K (cal-culated as 0.25 percent KNO3).
Examples 7 to 12 Production OfEthylene Oxide With Potassium Nitrate-Containing Supported Silver Catalyst:
The examples set forth below were conducted employing catalyts using carriers of the type pre-pared in Example 1, the catalysts themselves being prepared in the manner described in Examples 2 to 6 and identified as being prepared by either a sequen-tial (S) procedure or a coincidental impregnation (C) procedureO The epoxidation studies for which data are presented below were conducted in a continuously stirred tank reactor, alsG ~.~own as a back-mixed autoclave of the type described above. The procedure involved charging approximately 80 ml of catalyst to the autoclave. The volume of catalyst was measured in a one inch I. D. graduated cylinder after tapping the cylinder several times to thoroughly pack the catalyst. The weight of the catalyst was noted and is indicated in the table appearing below. The back-mixed autoclave was heated to about reaction tempera-ture in a nitrogen flow of 11.3 SCFH with the fan ~ operating at about 1,500 rpm. The nitrogen flow was ; 35 then discontinued and the feedstream was introduced to the reactor.
All ethylene epoxidation reactions, except where indicated otherwise, were examined under Standard Test Conditions comprising, by volume, 30 percent C~H4~ 8 percent 2' 5 ppm ethyl chloride, 5 ppm, by weight, NO, no added C2H6 or CO2, N2 ballast, 240 degrees C, 275 psig, GHSV = 8,000 hr 1. The data summarized below includes surface areas of the cata-lysts, Ag and calculated KNO3 contents, maximum ob-served outlet ethylene oxide, maximum observed effi-ciency, and aging rate.
T~BLE
Pre-para- Calcu-tion lated Example Proce- Na ~ Ag % RN03 Activity Effi-dure ~m ~EØ) ciency 7 C 12 19.7 2.0 1.18 91~0 108 C 12 20.0 2.0 1.41 90.3 9 C 12 19.7 2.0 1.23 90.0 C 12 20.4 2.0 1.35 ~0.3 11 S 12 15.6 1.0 1.12 86.5 12* C 12 39.8 0.1 2.03 8~.0 1513** S 12 11.4 1.2 See 88.2 Figure 14** S 80 11.4 1.2 See 87.8 Figure 15*** C 40 39.8 0.1 See See Figure Figure 16*~ C 100 39.8 0.1 See See Figure Figure *Test conditions, by volume, 30 percent C2H4, 8 per-cent 2~ 20 ppm ethyl chloride, 15 ppm N0, 270 de-grèes C, 270 psig, GHSV = 8,000 hour 1. The catalyst Of Example 6 is used. The catalyst of Example 3 is used.
**GHSV = 4,000 hr~l, all other conditions the same as for Examples 7-11.
***Conditions the same as Example 12 but additionally includes 3 percent C02 in the feedstream. The cata-~39~
lyst of Example 6 is used.
Example 13 - Production of Propylene Oxide With Potassium Nitrate-1 Supported Silver Ca a~st:
Into a back-mixed autoclave, having a slightly smaller volume than the autoclave employed in the previous examples, were placed 5.0 grams (10.0 ml) of a catalyst having a support prepared as in Example 1, The support was an alpha-alumina having a surface area of 1.12 m2/g, a pore volume of 0.8 cc/g, less than 50 ppm, by weight, of leachable sodium, a residual fluorine concentration o-f 0.7 percent, and a platelet morp~ology of the type disclosed in Canadian Application No. 515,865. The catalyst included, by weight, a silver con~entration of 17.7 percent and a potassium concentration of 0.38 percent (calculated as 1 percent potassium nitrate).
A mixture, by volume, of 9.9 percent propylene, 7.75 percent oxygen, 200 ppm ethyl chloride, 200 ppm nitric oxide, 2 percent methane, and the remainder being nitrogen ballast gas, was fed to the reactor at a temperature of 252 degrees C, a pressure of 25 psi and a gas hourly space velocity of 832 hr 1 After 22.5 hours, a selectivity of 47.3 percent was observed with an activity of 0.6 pounds of propylene oxide/cubic foot of catalyst/hour (corresponding to an outlet percent of propylene oxide of 0.465 percent).
., .~
Claims (16)
1. A process for the epoxidation of alkene in the presence of an oxygen-containing gas comprising contacting said alkene and said oxygen-containing gas under epoxidation conditions in the presence of at least one efficiency-enhancing gaseous member of a redox-half reaction pair and a solid catalyst, said catalyst comprising a catalytically-effective amount of silver on a solid support and an efficiency-enhancing amount of at least one efficiency-enhancing salt of a member of a redox-half reaction pair, said support having less than about 50 ppm, by weight, of leachable sodium.
2. The process of claim 1 wherein said effi-ciency enhancing gaseous and salt members of a redox-half reaction pair comprise members of the same re-dox-half reaction.
3. The process of claim 1 wherein said at least one gaseous member of a redox-half reaction is NO, NO2, N2O3, N2O4, or a gas capable of forming one of the aforementioned gases under epoxidation condi-tions.
4. The process of claim 3 wherein said gas capable of forming said one of the aforementioned gases is a gas which forms NO and/or NO2 under epoxi-dation conditions.
5. The process of claim 1 wherein said at least one efficiency-enhancing salt of a member of a redox-half reaction pair comprises potassium nitrate.
6. The process of claim 1 wherein said at least one gaseous member of a redox-half reaction pair comprises NO.
7. The process of claim 1 wherein said at least one gaseous member comprises NO and said at least one salt comprises potassium nitrate.
8. The process of claim 1 wherein said support contains less than 20 ppm, by weight, of leachable sodium.
9. The process of claim 1 wherein said solid support is alpha-alumina.
10. The process of claim 1 wherein said alkene is ethylene.
11. The process of claim 1 wherein said alkene is propylene.
12. The process of claim 1 wherein said gaseous member of a redox-half reaction pair is NO, said salt of a member of a redox-half reaction pair is KNO3, and said solid support is alpha-alumina containing less than 20 ppm, by weight, of leachable sodium.
13. A catalyst suitable for epoxidation of an alkene in the presence of an oxygen-containing gas comprising a catalytically-effective amount of silver on a substantially inert support and an efficiency-enhancing amount of at least one efficiency-enhancing salt of a member of a redox-half reaction pair, said support having less than about 50 ppm, by weight, of leachable sodium.
14. The catalyst of claim 13 wherein said solid support is alpha-alumina.
15. The catalyst of claim 13 wherein said sup-port contains less than 20 ppm, by weight, of leach-able sodium.
16. The catalyst of claim 13 wherein said sup-port is alpha-alumina containing less that 20 ppm, by weight, of sodium.