CA1049793A - Process for producing vanadium-containing alloys - Google Patents
Process for producing vanadium-containing alloysInfo
- Publication number
- CA1049793A CA1049793A CA221,242A CA221242A CA1049793A CA 1049793 A CA1049793 A CA 1049793A CA 221242 A CA221242 A CA 221242A CA 1049793 A CA1049793 A CA 1049793A
- Authority
- CA
- Canada
- Prior art keywords
- vanadium
- oxides
- melt
- slag
- furnace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
ABSTRACT OF THE DISCLOSURE
A process for producing vanadium-containing alloys comprises the step of melting in a furnace a charge providing a content of vanadium oxides in a melt from 25 to 35 wt.% of vanadium oxides, and calcium oxides. The melt is discharged from the furnace into a receptacle in which vanadium is reduced from oxides thereof with liquid or solid silicon-con-taining reducing agent. Then vanadium oxides and calcium oxides are additionally introduced to oxidize the residual silicon, or from 1 to 10 wt.% of vanadium oxides remain in the slag, and vanadium is reduced from these oxides in another receptacle.
The process permits to reduce the production cost of the alloy, increase the vanadium content in the alloy to 80 wt.% and lower the carbon content to 0.03 wt.% and less.
A process for producing vanadium-containing alloys comprises the step of melting in a furnace a charge providing a content of vanadium oxides in a melt from 25 to 35 wt.% of vanadium oxides, and calcium oxides. The melt is discharged from the furnace into a receptacle in which vanadium is reduced from oxides thereof with liquid or solid silicon-con-taining reducing agent. Then vanadium oxides and calcium oxides are additionally introduced to oxidize the residual silicon, or from 1 to 10 wt.% of vanadium oxides remain in the slag, and vanadium is reduced from these oxides in another receptacle.
The process permits to reduce the production cost of the alloy, increase the vanadium content in the alloy to 80 wt.% and lower the carbon content to 0.03 wt.% and less.
Description
10~9'793 PROCESS FOR PRODUCING VANADIUM-CONTAINING ALLOYS
The present invention relates to metallurgy, and more specifically to a process for producing vanadium-containing alloys.
At present, in alloying steel use is preferably made of ferrovanadium which is produced in an electric furnace by the sillicoalumothermal method. The melting process generally compri-se two stages: reduction and refining. After the reduction of vanadium from oxides thereof, first an alloy containing up to 35 wt.% of vanadium and 9-12 wt.% of silicon is obtained, then slag containing about 0.35 wt.% of vanadium oxides is drained. After the draining of slag, the alloy is refined in the same furnace after adding thereto vanadium pentoxide and lime. Thus, ferrova-nadium is produced containing from 35 to 50 wt.% of vanadium, from 0.5 to 0.7 wt.% of carbon and up to 2 wt.% of silicon, as well as slag containing up to 14 wt.% of vanadium oxides to be used in a charge for a next melting cycle.
However, when using this method, vanadium is reduced form oxides thereof concurrently with the melting of the charge so that difficu3tly reducible lower vanadium oxides are formed which are bound into silicates from which vanadium can be reduced only with difficulty as well. In addition, the reduction of va-nadium takes place only at the metal-slag interface. This metal-slag interface has àn insufficient surface area so that the reduc-tion reaction proceeds at a low rate.
Due to a long residence t`ime of the metal being reduced in an electric furnace and its contact with the electrodes an alloy thus obtained has a high content of carbon, Average tempe-rature in the furnace reaches 1650 C because both melting of the charge and reduction of vanadium from oxides thereof concurrently take place in the furnace. This temperature is insufficient to obtain an alloy containing more than 50 wt.% of vanadium.
. : :.
Furthermore, slags deleterious to the lining are formed in the furnace during the reduction of vanadium from oxides thereof.
Known in the art is an aluminothermal non-furnace meth-od of producing vanadium-containing alloys. This method permits obtaining alloys containing up to 80 wt.% of vanadium and up to 0.1 wt.% of carbon.
This method requires, however, to use expensive vanadium pentoxide and high-grade aluminium with a low content of impurities.
This method is deficient in a low productivity inherent in all non-furnace aluminothermal processes, and the resulting alloy is costly due to such a low productivity. In addition, a low degree of vanadium extraction into the alloy also contributes to a high cost of the resulting alloy.
A growing demand for vanadium-containing alloys for alloying steel and low-carbon alloys with high percentage of vana-dium poses the problem of the provision of an economically reaso-nable and highly productive process for producing such alloys.
The main object of the invention is to provide a process for producing vanadium-containing alloys containing more vanadium than with known silicothermal processes for producing alloys in electric furnaces.
Another not least important object of the invention is t~ reduce the production cost of said alloy.
A~ important object of the invention is also to reduce the content of carbon in said alloy from 0.03 wt.% to 0.005 wt.%.
Still another object of the invention is to prolong the service life of the furnace lining and to improve the productivi-ty of the furnace used to melt a charge for said alloy due to the reduction of vanadium from oxides thereof in a melt outside the furnace.
These and other objects are accomplished by the
The present invention relates to metallurgy, and more specifically to a process for producing vanadium-containing alloys.
At present, in alloying steel use is preferably made of ferrovanadium which is produced in an electric furnace by the sillicoalumothermal method. The melting process generally compri-se two stages: reduction and refining. After the reduction of vanadium from oxides thereof, first an alloy containing up to 35 wt.% of vanadium and 9-12 wt.% of silicon is obtained, then slag containing about 0.35 wt.% of vanadium oxides is drained. After the draining of slag, the alloy is refined in the same furnace after adding thereto vanadium pentoxide and lime. Thus, ferrova-nadium is produced containing from 35 to 50 wt.% of vanadium, from 0.5 to 0.7 wt.% of carbon and up to 2 wt.% of silicon, as well as slag containing up to 14 wt.% of vanadium oxides to be used in a charge for a next melting cycle.
However, when using this method, vanadium is reduced form oxides thereof concurrently with the melting of the charge so that difficu3tly reducible lower vanadium oxides are formed which are bound into silicates from which vanadium can be reduced only with difficulty as well. In addition, the reduction of va-nadium takes place only at the metal-slag interface. This metal-slag interface has àn insufficient surface area so that the reduc-tion reaction proceeds at a low rate.
Due to a long residence t`ime of the metal being reduced in an electric furnace and its contact with the electrodes an alloy thus obtained has a high content of carbon, Average tempe-rature in the furnace reaches 1650 C because both melting of the charge and reduction of vanadium from oxides thereof concurrently take place in the furnace. This temperature is insufficient to obtain an alloy containing more than 50 wt.% of vanadium.
. : :.
Furthermore, slags deleterious to the lining are formed in the furnace during the reduction of vanadium from oxides thereof.
Known in the art is an aluminothermal non-furnace meth-od of producing vanadium-containing alloys. This method permits obtaining alloys containing up to 80 wt.% of vanadium and up to 0.1 wt.% of carbon.
This method requires, however, to use expensive vanadium pentoxide and high-grade aluminium with a low content of impurities.
This method is deficient in a low productivity inherent in all non-furnace aluminothermal processes, and the resulting alloy is costly due to such a low productivity. In addition, a low degree of vanadium extraction into the alloy also contributes to a high cost of the resulting alloy.
A growing demand for vanadium-containing alloys for alloying steel and low-carbon alloys with high percentage of vana-dium poses the problem of the provision of an economically reaso-nable and highly productive process for producing such alloys.
The main object of the invention is to provide a process for producing vanadium-containing alloys containing more vanadium than with known silicothermal processes for producing alloys in electric furnaces.
Another not least important object of the invention is t~ reduce the production cost of said alloy.
A~ important object of the invention is also to reduce the content of carbon in said alloy from 0.03 wt.% to 0.005 wt.%.
Still another object of the invention is to prolong the service life of the furnace lining and to improve the productivi-ty of the furnace used to melt a charge for said alloy due to the reduction of vanadium from oxides thereof in a melt outside the furnace.
These and other objects are accomplished by the
-2-~04g793 provision of a process for producing vanadium-containing alloys comprising the steps of melting in a furnace a charge containing vanadium and calcium oxides and xeducing vanadium from oxides thereof in a melt with silicon, wherein, according to the inven-tion the process comprises melting a charge ensuring the content of vanadium oxides in the melt from 25 to 35 wt.%, discharging said melt from the furnace into a receptacle, and reducing vana-dium with silicon in said receptacle by adding silicon in an amount sufficient to reduce vanadium from the oxides thereof con-taining in said melt.
The extrafurnace reduction of vanadium from oxides the-reof provides for a lower carbon content in the resulting alloy which is from 0.005 to 0.03 wt.% due to the elimination of a contact of the reduced melt with the furnace electrodes.
; Where vanadium is reduced from oxides thereof in a melt, rather than in a solid charge, the rate of reduction is increased, and the content of vanadium in the resulting alloy is also increas-ed.
Since the furnace is used only to melt the charge, and the reduction is effected outside the furnace, vanadium oxides are present in a single valency state only, and namely in the ~-form of V205 along with calcium oxides, whereby the furnace lining is not damaged.
We have found that the melt containing the above-speci-fied quantities of vanadium oxides is the optimal one. A charge providing a content of vanadium oxides in a melt of less than 25 wt.% is high-melting so that the electric power consumption for melting the charge is increased. Where the content of vanadium oxides in a melt is more than 25 wt.%, the heat capacity of the melt becomes sufficient for effecting the reduction.
The reducing agent may be added to the melt in the mol-ten state.
,: :
As a result, during the melting, solid material rnay be added io the melt, such as wastes produced during the casting of the alloy, and if necessary, iron may be added so as to increase the yield of the alloy or modify its composition.
The above-specified reducing agent may be added to the melt in the form of lumps of a size not exceeding 80 mm. The heat released during the reduction is sufficient to melt the reducing agent and to ensure a high rate of reduction with the above-specified size of lumps.
Vanadium is preferably reduced from oxides thereof in the melt to obtain slag containing from 1 to 10 wt.% of vanadium oxides, whereafter,the slag is drained into another receptacle, and vanadium is reduced in that receptacle from oxides thereof in this slag.
Thus, the content of vanadium in the slag to be dispo-sed of may be lowered to 0.5 wt.% and lower.
During the reduction of vanadium from oxides thereof additional amount of vanadium oxides are preferably added to said melt sufficient to oxidize the residual silicon.
This permits to reduce the content of silicon in the alloy and to improve the yield of the final product.
A charge containing vanadium oxides may comprise vanadium convertor slag preliminarily calcinated with carbon at from 900 to 1000 C from which iron is withdrawn during the melting.
Enriched convertor slag is less expensive than vanadium pentoxide, but the content of vanadium in the resulting alloy will be somewhat when using such slag.
The invention will now be described with reference to specific embodiments of the process.
The process oDmprised melting in a furnace a charge 4_ .
1~)497~3 providing for obtaining a melt containing 30 wt.% of vanadium pentoxide, as well as calcium oxides (lime).
The melt was poured from the furnace into a ladle, weighed, and then 350 kg of liquid ferrosilicon containing 75 wt.%
of silicon were added per 2 tons of the melt. Subsequently 200 kg of a mixture containing vanadium pentoxide and 100 kg of metal scrap were added to the melt.
535 kg of ferrovanadium were thus obtained containing about 70 wt.% of vanadium and 0.015 wt.% of carbon. Slag contai-ned less th~n 1.0 wt.% of vanadium oxides.
A melt of vanadium oxides and lime was poured into a ladle from a furnace. 320 kg of liquid ferrosilicon per 2 tons of vanadium pentoxide melt were added to obtain an alloy contain-ing 58 wt.% of vanadium, 0.02 wt.% of carbon, and slag containing ~-5 wt.% of vanadiwm oxides. This slag was poured into another fur-nace, which has been used to melt ferrosilicon. In this furnace ferrosilicon was obtained containing 1 wt.% of vanadium and slag containing less than 0.3wt.% of vanadiwm oxides. The resulting -ferrosilicon was used for reducing vanadium during the next melt-ing cycle.
The process was conducted as described in Example 1, but liquid ferrosilicon was replaced by solid crushed ferrosilicon of a particle size not exceeding 50 mm.
400 kg of ferrosilicon containing 75 wt.% of silicon s were added per 2 tons of melt to obtain 490 kg of an alloy con-taining 75 wt.% of vanadiw~ and 4.2 wt.% of silicon. Slag was then drained, and a mixture containing vanadium pentoxide and lime was added to the metal, As a result of reaction of the mixture and metal, the content of silicon in the metal was lowered _5 ,' -~9793 to 1 wt.%.
300 kg of ferrosilicon were added per 2 tons of melt, ferrosilicon being used in pumps of a size up to 80 mm. Thus, slag containing up to 8 wt.% of vanadium oxides was obtained to be used for producing ferrovanadium by the silicothermal method in an electric furnace, and ferrovanadium containing 57 wt.% of vanadium and 0.01 wt.% of carbon.
There it is desired to obtain alloys containing chromium, manganese, nickel, tungsten, molybdenum, niobium in addition to vanadium, products containing oxides of such metals may be also added to the charge.
In addition to the above examples, a charge providing the content of vanadium oxides in the melt from 25 to 35 wt.% may also be melted. In that case, the content of the silicon reduc-ing agent should be either greater than that given in Example 1, when more than 30 wt.% of vanadium oxides are formed in the melt, or smaller than that given in Example 1, when less than 30 wt.%
of the reducing agent are formed in the melt.
T~e amount of the reducing agent is calculated by the reaction 2V2O5+5Si = 4V + 5SiO2 -in the stoichiometric ratio.
The effective utilization of silicon in the reducing agent is 100%.
In accordance with the process of the invention vanadium is reduced from oxides thereof in the melt to obtain slag contain-ing from 1 to 10 wt.% of vanadium oxides, whereafter the slag is drained into another receptacle, and vanadium is reduced from oxides thereof in that receptacle in this slag.
; A charge containing vanadium oxides compris~s vanadium convertor slag preliminarily calcinated with carbon at from 900 to loOOQC, iron being eliminated from the slag during the melting.
.
The extrafurnace reduction of vanadium from oxides the-reof provides for a lower carbon content in the resulting alloy which is from 0.005 to 0.03 wt.% due to the elimination of a contact of the reduced melt with the furnace electrodes.
; Where vanadium is reduced from oxides thereof in a melt, rather than in a solid charge, the rate of reduction is increased, and the content of vanadium in the resulting alloy is also increas-ed.
Since the furnace is used only to melt the charge, and the reduction is effected outside the furnace, vanadium oxides are present in a single valency state only, and namely in the ~-form of V205 along with calcium oxides, whereby the furnace lining is not damaged.
We have found that the melt containing the above-speci-fied quantities of vanadium oxides is the optimal one. A charge providing a content of vanadium oxides in a melt of less than 25 wt.% is high-melting so that the electric power consumption for melting the charge is increased. Where the content of vanadium oxides in a melt is more than 25 wt.%, the heat capacity of the melt becomes sufficient for effecting the reduction.
The reducing agent may be added to the melt in the mol-ten state.
,: :
As a result, during the melting, solid material rnay be added io the melt, such as wastes produced during the casting of the alloy, and if necessary, iron may be added so as to increase the yield of the alloy or modify its composition.
The above-specified reducing agent may be added to the melt in the form of lumps of a size not exceeding 80 mm. The heat released during the reduction is sufficient to melt the reducing agent and to ensure a high rate of reduction with the above-specified size of lumps.
Vanadium is preferably reduced from oxides thereof in the melt to obtain slag containing from 1 to 10 wt.% of vanadium oxides, whereafter,the slag is drained into another receptacle, and vanadium is reduced in that receptacle from oxides thereof in this slag.
Thus, the content of vanadium in the slag to be dispo-sed of may be lowered to 0.5 wt.% and lower.
During the reduction of vanadium from oxides thereof additional amount of vanadium oxides are preferably added to said melt sufficient to oxidize the residual silicon.
This permits to reduce the content of silicon in the alloy and to improve the yield of the final product.
A charge containing vanadium oxides may comprise vanadium convertor slag preliminarily calcinated with carbon at from 900 to 1000 C from which iron is withdrawn during the melting.
Enriched convertor slag is less expensive than vanadium pentoxide, but the content of vanadium in the resulting alloy will be somewhat when using such slag.
The invention will now be described with reference to specific embodiments of the process.
The process oDmprised melting in a furnace a charge 4_ .
1~)497~3 providing for obtaining a melt containing 30 wt.% of vanadium pentoxide, as well as calcium oxides (lime).
The melt was poured from the furnace into a ladle, weighed, and then 350 kg of liquid ferrosilicon containing 75 wt.%
of silicon were added per 2 tons of the melt. Subsequently 200 kg of a mixture containing vanadium pentoxide and 100 kg of metal scrap were added to the melt.
535 kg of ferrovanadium were thus obtained containing about 70 wt.% of vanadium and 0.015 wt.% of carbon. Slag contai-ned less th~n 1.0 wt.% of vanadium oxides.
A melt of vanadium oxides and lime was poured into a ladle from a furnace. 320 kg of liquid ferrosilicon per 2 tons of vanadium pentoxide melt were added to obtain an alloy contain-ing 58 wt.% of vanadium, 0.02 wt.% of carbon, and slag containing ~-5 wt.% of vanadiwm oxides. This slag was poured into another fur-nace, which has been used to melt ferrosilicon. In this furnace ferrosilicon was obtained containing 1 wt.% of vanadium and slag containing less than 0.3wt.% of vanadiwm oxides. The resulting -ferrosilicon was used for reducing vanadium during the next melt-ing cycle.
The process was conducted as described in Example 1, but liquid ferrosilicon was replaced by solid crushed ferrosilicon of a particle size not exceeding 50 mm.
400 kg of ferrosilicon containing 75 wt.% of silicon s were added per 2 tons of melt to obtain 490 kg of an alloy con-taining 75 wt.% of vanadiw~ and 4.2 wt.% of silicon. Slag was then drained, and a mixture containing vanadium pentoxide and lime was added to the metal, As a result of reaction of the mixture and metal, the content of silicon in the metal was lowered _5 ,' -~9793 to 1 wt.%.
300 kg of ferrosilicon were added per 2 tons of melt, ferrosilicon being used in pumps of a size up to 80 mm. Thus, slag containing up to 8 wt.% of vanadium oxides was obtained to be used for producing ferrovanadium by the silicothermal method in an electric furnace, and ferrovanadium containing 57 wt.% of vanadium and 0.01 wt.% of carbon.
There it is desired to obtain alloys containing chromium, manganese, nickel, tungsten, molybdenum, niobium in addition to vanadium, products containing oxides of such metals may be also added to the charge.
In addition to the above examples, a charge providing the content of vanadium oxides in the melt from 25 to 35 wt.% may also be melted. In that case, the content of the silicon reduc-ing agent should be either greater than that given in Example 1, when more than 30 wt.% of vanadium oxides are formed in the melt, or smaller than that given in Example 1, when less than 30 wt.%
of the reducing agent are formed in the melt.
T~e amount of the reducing agent is calculated by the reaction 2V2O5+5Si = 4V + 5SiO2 -in the stoichiometric ratio.
The effective utilization of silicon in the reducing agent is 100%.
In accordance with the process of the invention vanadium is reduced from oxides thereof in the melt to obtain slag contain-ing from 1 to 10 wt.% of vanadium oxides, whereafter the slag is drained into another receptacle, and vanadium is reduced from oxides thereof in that receptacle in this slag.
; A charge containing vanadium oxides compris~s vanadium convertor slag preliminarily calcinated with carbon at from 900 to loOOQC, iron being eliminated from the slag during the melting.
.
Claims (6)
1. A process for producing vanadium-containing alloys comprising the steps of: melting in a furnace a charge contain-ing vanadium and calcium oxides in an amount providing the content of vanadium oxides in the melt from 25 to 35 wt.%
discharging from said furnace said melt into a receptacle, adding to said melt a reducing agent containing silicon in an amount sufficient to reduce vanadium from the oxides thereof contained in said melt.
discharging from said furnace said melt into a receptacle, adding to said melt a reducing agent containing silicon in an amount sufficient to reduce vanadium from the oxides thereof contained in said melt.
2. A process according to claim 1, wherein said reducing agent is added to said melt in a molten state.
3. A process according to claim 1, wherein said reducing agent is added to said melt in a solid state with a size of lumps not exceeding 80 mm.
4. A process according to claim 1, wherein vanadium oxides are reduced to obtain slag containing from 1 to 10 wt.%, of vanadium oxides, whereafter the slag is drained into another receptacle, and vanadium is reduced in said receptacle from oxides thereof in this slag.
5. A process according to claim 1, wherein during the reduction of vanadium from oxides thereof, an additional amount of vanadium oxides is added to said melt sufficient to oxidize the residual silicon.
6. A process according to claim 1, wherein the charge containing vanadium oxides comprises vanadium convertor slag preliminarily calcinated with carbon at from 900 to 1000°C, iron being eliminated from the slag during the melting.