BR122023025296A2 - COATING COMPOSITION - Google Patents
COATING COMPOSITION Download PDFInfo
- Publication number
- BR122023025296A2 BR122023025296A2 BR122023025296-9A BR122023025296A BR122023025296A2 BR 122023025296 A2 BR122023025296 A2 BR 122023025296A2 BR 122023025296 A BR122023025296 A BR 122023025296A BR 122023025296 A2 BR122023025296 A2 BR 122023025296A2
- Authority
- BR
- Brazil
- Prior art keywords
- coating
- acceptor
- donor
- composition
- fact
- Prior art date
Abstract
Composições e métodos envolvendo reação de adição de Michael catalisada por base latente são descritos aqui. As composições descritas aqui são derivadas de uma reação de adição de Michael e proveem revestimentos, incluindo revestimentos primários e revestimentos diretos com metal que têm adesão, resistência à corrosão e resposta de cura ótimos quando aplicadas a um substrato e curadas.Compositions and methods involving latent base-catalyzed Michael addition reaction are described herein. The compositions described herein are derived from a Michael addition reaction and provide coatings, including primer coatings and direct metal coatings, that have optimal adhesion, corrosion resistance and curing response when applied to a substrate and cured.
Description
[001] Revestimentos são frequentemente aplicados a vários substratos, incluindo substratos de metal e aço para prevenir corrosão. Estes revestimentos são frequentemente revestimentos em multicamadas, apresentando um ou mais revestimentos primários com revestimentos finais aplicados sobre eles. Estes revestimentos são econômicos e relativamente fáceis de aplicar. Os revestimentos secam rapidamente e têm boa resistência à corrosão e resistência química, tornando os revestimentos especialmente úteis para revestir componentes de metal a serem usados por longos períodos de tempo e/ou em ambientes corrosivos.[001] Coatings are often applied to various substrates, including metal and steel substrates to prevent corrosion. These coatings are often multi-layer coatings, featuring one or more primer coats with top coats applied over them. These coatings are economical and relatively easy to apply. The coatings dry quickly and have good corrosion resistance and chemical resistance, making the coatings especially useful for coating metal components to be used for long periods of time and/or in corrosive environments.
[002] Convencionalmente, revestimentos primários são aplicados a superfícies de metal para prover proteção contra corrosão. Estes revestimentos primários são tipicamente resinas epóxi, resinas de poliuretano resinas e similares. Tipicamente, tais sistemas de revestimento são composições de dois componentes reticuláveis, onde os componentes são armazenados separadamente e misturados antes do uso. Os dois componentes são altamente reativos e vão começar a reticular assim que eles são misturados. É convencional incluir um catalisador em tais revestimento primário sistemas para aumentar a taxa de reação de reticulação entre os dois componentes.[002] Conventionally, primer coatings are applied to metal surfaces to provide protection against corrosion. These primer coatings are typically epoxy resins, polyurethane resins and the like. Typically, such coating systems are crosslinkable two-component compositions, where the components are stored separately and mixed before use. The two components are highly reactive and will begin to crosslink as soon as they are mixed. It is conventional to include a catalyst in such primer coating systems to increase the rate of cross-linking reaction between the two components.
[003] A reação de reticulação pode ser catalisada por base ou catalisada por ácido. Sistemas catalisados por base são às vezes preferidos, porque eles são capazes de cura rápida ou acelerada. Porém, por causa da rápida taxa de cura, estas composições só podem ser usadas por um período de tempo relativamente curto depois que os componentes são misturados, definido como o tempo de vida útil em armazenamento da composição de revestimento. Em alguns sistemas catalisados por base, a viscosidade aumenta tão rapidamente que o revestimento cura antes dele poder ser integralmente aplicado a uma superfície e consequentemente, estes sistemas são de uso prático limitado.[003] The crosslinking reaction can be base-catalyzed or acid-catalyzed. Base-catalyzed systems are sometimes preferred because they are capable of rapid or accelerated curing. However, because of the rapid cure rate, these compositions can only be used for a relatively short period of time after the components are mixed, defined as the shelf life of the coating composition. In some base-catalyzed systems, the viscosity increases so rapidly that the coating cures before it can be fully applied to a surface and consequently, these systems are of limited practical use.
[004] Devido a questões regulatórias com respeito ao uso do uso de compostos orgânicos voláteis (VOC) em revestimentos transportados em solvente, sistemas com altos sólidos com baixo teor de solvente são preferidos. Porém, sistemas de altos sólidos apresentam diversos desafios com respeito a balancear o tempo de vida útil em armazenamento e a velocidade de cura. Por exemplo, uma composição com altos sólidos inclui tipicamente menos solvente que pode evaporar quando o revestimento é aplicado e como resultado, o tempo de vida útil em armazenamento é muito menor do que preferido. Por outro lado, o aumento da taxa de reação quando o revestimento é aplicado é também reduzido com menos solvente no sistema, levando à cura mais lenta. Uma combinação de cura rápida e longo tempo de vida útil em armazenamento é, portanto, difícil de conseguir para sistemas de revestimento convencionais com altos sólidos.[004] Due to regulatory issues regarding the use of volatile organic compounds (VOC) in solvent-borne coatings, high solids systems with low solvent content are preferred. However, high solids systems present several challenges with respect to balancing storage life and cure speed. For example, a high solids composition typically includes less solvent that can evaporate when the coating is applied and as a result, the shelf life is much shorter than preferred. On the other hand, the increase in reaction rate when the coating is applied is also reduced with less solvent in the system, leading to slower curing. A combination of fast curing and long shelf life is therefore difficult to achieve for conventional high solids coating systems.
[005] Uma possível solução para o problema de tempo de vida útil em armazenamento reduzido em sistemas catalisados por base é o uso de um catalisador latente. Estes catalisadores só são ativados depois que o revestimento é aplicado e proveem tempo de vida útil em armazenamento mais longo sem comprometer a velocidade de cura. Por exemplo, os use de sais de carbonato substituídos como catalisadores latentes para um sistema catalisado por base é descrito na patente US 8.962.725, incorporada aqui por referência.[005] A possible solution to the problem of reduced storage lifetime in base-catalyzed systems is the use of a latent catalyst. These catalysts are only activated after the coating is applied and provide longer shelf life without compromising curing speed. For example, the use of substituted carbonate salts as latent catalysts for a base-catalyzed system is described in US patent 8,962,725, incorporated herein by reference.
[006] Porém, não é sabido se composições de revestimento que usam tais sistemas de catalisador latente podem ser usadas comas composições de revestimento primário. Para ser útil como uma composição de revestimento primário, uma composição de revestimento deve demonstrar uma adesão ótima ao substrato e uma resistência ótima à corrosão. O sistema com um revestimento descrito na patente US 8.962.725 não é conhecido por oferecer resistência à corrosão suficiente quando aplicado diretamente a um substrato metálico. Ademais, quando algumas composições catalisadas por base atualmente conhecidas são aplicadas diretamente a substratos de metal, particularmente substratos ácidos ou tratados com ácido, uma perda de cura e/ou adesão é observada.[006] However, it is not known whether coating compositions using such latent catalyst systems can be used with primary coating compositions. To be useful as a primer coating composition, a coating composition must demonstrate optimum adhesion to the substrate and optimum corrosion resistance. The coating system described in US patent 8,962,725 is not known to offer sufficient corrosion resistance when applied directly to a metallic substrate. Furthermore, when some currently known base-catalyzed compositions are applied directly to metal substrates, particularly acidic or acid-treated substrates, a loss of cure and/or adhesion is observed.
[007] Consequentemente, há uma necessidade de sistemas de revestimento primário que demonstrem adesão e resistência ótimos à corrosão, enquanto aproveitam a rápida velocidade de cura e o tempo de vida útil em armazenamento ótimo demonstrados por sistemas catalisados por base latentes que reticulam via reações de adição de Michael para produzir uma composição de revestimento superior.[007] Consequently, there is a need for primer coating systems that demonstrate optimal adhesion and corrosion resistance, while taking advantage of the rapid cure rate and optimal storage life demonstrated by latent base-catalyzed systems that cross-link via addition of Michael to produce a superior coating composition.
[008] A presente descrição provê composições e métodos envolvendo uma reação de adição de Michael. As composições descritas aqui são derivadas de uma reação de adição de Michael e proveem revestimentos que têm adesão, resistência à corrosão e resposta de cura ótimas quando aplicadas a um substrato e curadas.[008] The present description provides compositions and methods involving a Michael addition reaction. The compositions described here are derived from a Michael addition reaction and provide coatings that have optimal adhesion, corrosion resistance and curing response when applied to a substrate and cured.
[009] Em uma modalidade, a presente descrição provê uma composição de revestimento incluindo pelo menos uma resina. A composição de resina inclui pelo menos um aceitador de adição de Michael tendo pelo menos um grupo funcional aceitador de adição de Michael. Pelo menos uma porção do aceitador de adição de Michael inclui uma espinha dorsal de epóxi. A composição de resina também inclui um doador de adição de Michael tendo pelo menos um grupo funcional doador de adição de Michael. Pelo menos uma porção do doador de adição de Michael inclui uma espinha dorsal de epóxi. Em um aspecto, pelo menos uma porção da composição de resina total, isto é, a partir de menos do que 1% a 100%, inclui uma espinha dorsal de epóxi, que pode ser derivada do aceitador de adição de Michael, do doador de adição de Michael, ou de uma combinação do aceitador de adição de Michael e do doador de adição de Michael.[009] In one embodiment, the present description provides a coating composition including at least one resin. The resin composition includes at least one Michael addition acceptor having at least one Michael addition acceptor functional group. At least a portion of Michael's addition acceptor includes an epoxy backbone. The resin composition also includes a Michael addition donor having at least one Michael addition donor functional group. At least one portion of Michael's addition donor includes an epoxy backbone. In one aspect, at least a portion of the total resin composition, i.e., from less than 1% to 100%, includes an epoxy backbone, which may be derived from the Michael addition acceptor, the Michael addition donor, the Michael addition, or a combination of the Michael addition acceptor and the Michael addition donor.
[0010] A composição de revestimento inclui adicionalmente um catalisador latente de base e opcionalmente, pelo menos um componente removedor de ácido e pelo menos um componente promotor de adesão. A composição de revestimento é capaz de curar em cerca de 1 a 10 minutos a 65,5°C (150°F) e o revestimento curado formado a partir da composição é resistente à corrosão.[0010] The coating composition additionally includes a latent base catalyst and optionally, at least one acid-scavenging component and at least one adhesion-promoting component. The coating composition is capable of curing in about 1 to 10 minutes at 65.5°C (150°F) and the cured coating formed from the composition is corrosion resistant.
[0011] Em uma outra modalidade, a presente descrição provê uma composição de revestimento incluindo pelo menos uma resina. A resina inclui grupos funcionais tanto de aceitador de adição de Michael quanto de doador de adição de Michael. Pelo menos uma porção do aceitador/doador de adição de Michael inclui uma espinha dorsal de epóxi. A composição de revestimento inclui adicionalmente um catalisador latente de base. A composição de revestimento é capaz de curar em cerca de 1 a 10 minutos a 65,5°C (150°F) e o revestimento curado formado a partir da composição é resistente à corrosão.[0011] In another embodiment, the present description provides a coating composition including at least one resin. The resin includes both Michael addition acceptor and Michael addition donor functional groups. At least a portion of Michael's addition acceptor/donor includes an epoxy backbone. The coating composition further includes a base latent catalyst. The coating composition is capable of curing in about 1 to 10 minutes at 65.5°C (150°F) and the cured coating formed from the composition is corrosion resistant.
[0012] Em ainda uma outra modalidade, a presente descrição provê um método para produzir um revestimento primário resistente à corrosão. O método inclui as etapas de prover um substrato, e aplicar sobre o substrato uma composição de revestimento que inclui uma composição de resina. A composição de resina inclui pelo menos um aceitador de adição de Michael e pelo menos um doador de adição de Michael. O aceitador de adição de Michael, o doador de adição de Michael, ou ambos, podem incluir uma espinha dorsal de epóxi, de maneira tal que pelo menos uma porção da composição de resina total, isto é, a partir de menos do que 1% a 100%, inclui uma espinha dorsal de epóxi. A composição inclui adicionalmente um catalisador latente. Depois que a composição de revestimento é aplicada, a composição de revestimento é curada em um máximo de cerca de 12 horas a temperaturas ambientes para obter um revestimento resistente à corrosão com uma dureza de lápis mínima de H. Se permitida curar a temperaturas mais altas, tais como, por exemplo, a cerca de 48,8°C a 76,6°C (120°F a 170°F), preferivelmente cerca de 65,5°C (150°F), a composição de revestimento pode ser curada em tão pouco tempo quanto 30 segundos a 15 minutos, preferivelmente 1 a 10 minutos para obter um revestimento resistente à corrosão com uma dureza de lápis mínima de H.[0012] In yet another embodiment, the present description provides a method for producing a corrosion-resistant primary coating. The method includes the steps of providing a substrate, and applying to the substrate a coating composition that includes a resin composition. The resin composition includes at least one Michael addition acceptor and at least one Michael addition donor. The Michael addition acceptor, the Michael addition donor, or both, may include an epoxy backbone such that at least a portion of the total resin composition, i.e., from less than 1% 100%, includes an epoxy backbone. The composition additionally includes a latent catalyst. After the coating composition is applied, the coating composition is cured for a maximum of about 12 hours at ambient temperatures to obtain a corrosion-resistant coating with a minimum pencil hardness of H. If allowed to cure at higher temperatures, such as, for example, at about 48.8°C to 76.6°C (120°F to 170°F), preferably about 65.5°C (150°F), the coating composition may be cured in as little time as 30 seconds to 15 minutes, preferably 1 to 10 minutes to obtain a corrosion resistant coating with a minimum pencil hardness of H.
[0013] O sumário acima da presente invenção não é destinado a descrever cada modalidade descrita ou cada implementação da presente invenção. A descrição que se segue exemplifica mais particularmente modalidades ilustrativas. Em diversos lugares por todo o pedido, é provido um guia através de listas de exemplos, exemplos estes que podem ser usados em várias combinações. Em cada instância, a lista citada serve apenas como um grupo representativo e não devem ser interpretados como uma lista exclusiva.[0013] The above summary of the present invention is not intended to describe each described embodiment or each implementation of the present invention. The following description more particularly exemplifies illustrative embodiments. In several places throughout the application, a guide is provided by lists of examples, which examples can be used in various combinations. In each instance, the list cited serves only as a representative group and should not be construed as an exclusive list.
[0014] Os detalhes de uma ou mais modalidades da invenção são dados nos desenhos anexos e na descrição abaixo. Outras características, objetos e vantagens da invenção vão ficar evidentes a partir da descrição e desenhos e a partir das reivindicações.[0014] Details of one or more embodiments of the invention are given in the attached drawings and in the description below. Other features, objects and advantages of the invention will become apparent from the description and drawings and from the claims.
[0015] Figura 1 é uma representação gráfica do efeito de diferentes níveis de epóxi acrilato sobre o desempenho sob intempéries das composições de revestimento final descritas aqui.[0015] Figure 1 is a graphical representation of the effect of different levels of epoxy acrylate on the weathering performance of the topcoat compositions described here.
[0016] A menos que especificado de outro modo, os seguintes termos como usados aqui têm os significados providos abaixo.[0016] Unless otherwise specified, the following terms as used herein have the meanings provided below.
[0017] Como usado aqui, o termo “grupo orgânico” significa um grupo hidrocarboneto (com elementos opcionais diferentes de carbono e hidrogênio, tais como oxigênio, nitrogênio, enxofre e silício) que é classificado como um grupo alifático, um grupo cíclico, ou combinação de grupos alifático e cíclico (por exemplo, grupos alcarila e aralquila). O termo “grupo alifático” significa um grupo hidrocarboneto saturado ou insaturado linear ou ramificado. Este termo é usado para englobar grupos alquila, alquenila e alquinila, por exemplo. O termo “grupo alquila” significa um grupo hidrocarboneto saturado linear ou ramificado incluindo, por exemplo, metila, etila, isopropila, t-butila, heptila, dodecila, octadecila, amila, 2-etil- hexila e similares. O termo “grupo alquenila” significa um grupo hidrocarboneto insaturado, linear ou ramificado com uma ou mais duplas ligações carbono-carbono, tais como um grupo vinila. O termo “grupo alquinila” significa um grupo hidrocarboneto insaturado, linear ou ramificado com uma ou mais triplas ligações carbono-carbono. O termo “grupo cíclico” significa um grupo hidrocarboneto de anel fechado que é classificado como um grupo alicíclico ou um grupo aromático, ambos os quais podem incluir heteroátomos. O termo “grupo alicíclico” significa um grupo hidrocarboneto cíclico tendo propriedades que se assemelham àquelas de grupos alifáticos. O termo “Ar” se refere a um grupo arila divalente (isto é, um grupo arileno), que se refere a um anel aromático fechado ou sistema de anel tal como fenileno, naftileno, bifenileno, fluorenileno e indenila, assim como grupos heteroarileno (isto é, um hidrocarboneto de anel fechado em que um ou mais dos átomos no anel é um elemento diferente de carbono (por exemplo, nitrogênio, oxigênio, enxofre, etc.)). Grupos heteroarila apropriados incluem furila, tienila, piridila, quinolinila, isoquinolinila, indolila, isoindolila, triazolila, pirrolila, tetrazolila, imidazolila, pirazolila, oxazolila, tiazolila, benzofuranila, benzotiofenila, carbazolila, benzoxazolila, pirimidinila, benzimidazolila, quinoxalinila, benzotiazolila, naftiridinila, isoxazolila, isotiazolila, purinila, quinazolinila, pirazinila, 1-oxidopiridila, piridazinila, triazinila, tetrazinila, oxadiazolila, tiadiazolila e assim por diante. Quando tais grupos são divalente, eles são tipicamente referidos como grupos “heteroarileno” (por exemplo, furileno, piridileno, etc.)[0017] As used herein, the term “organic group” means a hydrocarbon group (with optional elements other than carbon and hydrogen, such as oxygen, nitrogen, sulfur and silicon) that is classified as an aliphatic group, a cyclic group, or combination of aliphatic and cyclic groups (e.g. alkaryl and aralkyl groups). The term “aliphatic group” means a linear or branched saturated or unsaturated hydrocarbon group. This term is used to encompass alkyl, alkenyl and alkynyl groups, for example. The term "alkyl group" means a linear or branched saturated hydrocarbon group including, for example, methyl, ethyl, isopropyl, t-butyl, heptyl, dodecyl, octadecyl, amyl, 2-ethylhexyl and the like. The term "alkenyl group" means an unsaturated, linear or branched hydrocarbon group with one or more carbon-carbon double bonds, such as a vinyl group. The term “alkynyl group” means an unsaturated, linear or branched hydrocarbon group with one or more carbon-carbon triple bonds. The term “cyclic group” means a closed-ring hydrocarbon group that is classified as an alicyclic group or an aromatic group, both of which may include heteroatoms. The term “alicyclic group” means a cyclic hydrocarbon group having properties that resemble those of aliphatic groups. The term “Ar” refers to a divalent aryl group (i.e., an arylene group), which refers to a closed aromatic ring or ring system such as phenylene, naphthylene, biphenylene, fluorenylene and indenyl, as well as heteroarylene groups ( that is, a closed-ring hydrocarbon in which one or more of the atoms in the ring is an element other than carbon (e.g., nitrogen, oxygen, sulfur, etc.)). Suitable heteroaryl groups include furyl, thienyl, pyridyl, quinolinyl, isoquinolinyl, indolyl, isoindolyl, triazolyl, pyrrolyl, tetrazolyl, imidazolyl, pyrazolyl, oxazolyl, thiazolyl, benzofuranyl, benzothiophenyl, carbazolyl, benzoxazolyl, pyrimidinyl, benzimidazolyl, quinoxalinyl, benzothiazolyl, dinila, isoxazolyl, isothiazolyl, purinyl, quinazolinyl, pyrazinyl, 1-oxidopyridyl, pyridazinyl, triazinyl, tetrazinyl, oxadiazolyl, thiadiazolyl and so on. When such groups are divalent, they are typically referred to as “heteroarylene” groups (e.g., furylene, pyridylene, etc.)
[0018] Um grupo que pode ser o mesmo ou diferente é referido como sendo “independentemente” alguma coisa. A substituição é antecipada sobre os grupos orgânicos dos compostos da presente invenção. Como um meio de simplificar a discussão e a citação de uma certa terminologia usada ao longo de todo este pedido, os termos “grupo” e “unidade” são usados para diferenciar as espécies químicas que permitem substituição ou que podem ser substituídas e daquelas que não permitem ou podem não ser substituídas de mesmo modo. Assim, quando o termo “grupo” é usado para descrever um substituinte químico, o material químico descrito inclui o grupo insubstituído e que se agrupa com átomos de O, N, Si, ou S, por exemplo, na cadeia (como em um grupo alcóxi) assim como grupos carbonila ou outra substituição convencional. Onde o termo “unidade” é usado para descrever um composto químico ou substituinte, apenas um material químico insubstituído é destinado a ser incluído. Por exemplo, a frase “grupo alquila” é destinada a incluir não apenas substituintes de alquila de hidrocarboneto saturado de cadeia aberta puro, tais como metila, etila, propila, t-butila e similares, mas também substituintes de alquila portando outros substituintes conhecidos na técnica, taus como hidróxi, alcóxi, alquilasulfonila, átomos de halogênio, ciano, nitro, amino, carboxila, etc. Assim, “grupo alquila” inclui grupos éter, haloalquilas, nitroalquilas, carboxialquilas, hidroxialquilas, sulfoalquilas, etc. Por outro lado, a frase “unidade alquila” é limitada à inclusão de apenas substituintes de alquila de hidrocarboneto saturado de cadeia aberta puro, tais como metila, etila, propila, t-butila e similares.[0018] A group that can be the same or different is referred to as being “independently” something. Substitution is anticipated on the organic groups of the compounds of the present invention. As a means of simplifying the discussion and citation of certain terminology used throughout this application, the terms “group” and “unit” are used to differentiate between those chemical species that allow substitution or that can be substituted and those that do not. allow or may not be replaced in the same way. Thus, when the term “group” is used to describe a chemical substituent, the chemical material described includes the group that is unsubstituted and that groups with atoms of O, N, Si, or S, for example, in the chain (as in a group alkoxy) as well as carbonyl groups or other conventional substitution. Where the term “unit” is used to describe a chemical compound or substituent, only an unsubstituted chemical material is intended to be included. For example, the phrase "alkyl group" is intended to include not only pure open-chain saturated hydrocarbon alkyl substituents, such as methyl, ethyl, propyl, t-butyl and the like, but also alkyl substituents bearing other substituents known in the art. technique, taus such as hydroxy, alkoxy, alkylsulfonyl, halogen, cyano, nitro, amino, carboxyl atoms, etc. Thus, “alkyl group” includes ether groups, haloalkyls, nitroalkyls, carboxyalkyls, hydroxyalkyls, sulfoalkyls, etc. On the other hand, the phrase "alkyl moiety" is limited to the inclusion of only pure open-chain saturated hydrocarbon alkyl substituents, such as methyl, ethyl, propyl, t-butyl and the like.
[0019] O termo “componente” se refere a qualquer composto que inclui uma característica ou estrutura particular. Exemplos de componentes incluem compostos, monômeros, oligômeros, polímeros e grupos orgânicos neles contidos.[0019] The term “component” refers to any compound that includes a particular characteristic or structure. Examples of components include compounds, monomers, oligomers, polymers and organic groups contained therein.
[0020] O termo “dupla ligação” é não limitativo e se refere a qualquer tipo de dupla ligação entre quaisquer átomos apropriados (por exemplo, C, O, N, etc.).[0020] The term “double bond” is non-limiting and refers to any type of double bond between any appropriate atoms (e.g., C, O, N, etc.).
[0021] O termo “tripla ligação” é não limitativo e se refere a qualquer tipo de tripla ligação entre quaisquer átomos apropriados.[0021] The term “triple bond” is non-limiting and refers to any type of triple bond between any appropriate atoms.
[0022] A “adição de Michael”, como usada aqui se refere à adição nucleofílica de um carbânion ou outro nucleófilo e a um composto etilenicamente insaturado deficiente em elétron, tal como um composto carbonila α,β-insaturado, por exemplo. A forma abreviada “MA” é usada intercambiavelmente aqui com o termo “adição de Michael”.[0022] “Michael addition” as used here refers to the nucleophilic addition of a carbanion or other nucleophile and to an electron-deficient ethylenically unsaturated compound, such as an α, β-unsaturated carbonyl compound, for example. The short form “MA” is used interchangeably here with the term “Michael addition.”
[0023] A reação de adição de Michael segue o esquema geral de reação mostrado aqui: [0023] The Michael addition reaction follows the general reaction scheme shown here:
[0024] No esquema de reação mostrado acima, B é um catalisador latente de base que reage com o doador de adição de Michael (MA) por desprotonação para formar um carbânion para uma subsequente adição com o aceitador de MA.[0024] In the reaction scheme shown above, B is a latent base catalyst that reacts with the Michael addition donor (MA) by deprotonation to form a carbanion for subsequent addition with the MA acceptor.
[0025] O termo “composição de resina”, como usado aqui se refere à porção contendo resina da composição. A composição de resina pode incluir uma ou mais resinas. Exemplos apropriados incluem, sem limitação, doadores de MA, aceitadores de MA, resinas não funcionais e resinas com funcionalidade diferente daquelas requeridas para adição de Michael.[0025] The term “resin composition” as used herein refers to the resin-containing portion of the composition. The resin composition may include one or more resins. Suitable examples include, without limitation, MA donors, MA acceptors, non-functional resins, and resins with functionality other than those required for Michael addition.
[0026] Por “aceitador de adição de Michael” ou “aceitador de MA” entende-se uma molécula tendo pelo menos um grupo funcional aceitador de MA.[0026] By “Michael addition acceptor” or “MA acceptor” is meant a molecule having at least one MA acceptor functional group.
[0027] Por “doador de adição de Michael” ou “doador de MA” entende-se uma molécula tendo pelo menos um grupo funcional doador de MA.[0027] By “Michael addition donor” or “MA donor” is meant a molecule having at least one MA donor functional group.
[0028] O termo “espinha dorsal de epóxi” como usado aqui se refere àquela porção de uma resina que é derivada de uma resina epóxi. Se derivada de uma resina epóxi, a espinha dorsal de epóxi pode ser derivada de resinas epóxi ou aromáticas ou alifáticas. Exemplos apropriados de resinas epóxi aromáticas são conhecidas aos versados na técnica e incluem, sem limitação, resinas epóxi derivadas de bisfenol A (BPA), BPF, novolac ou cresol. Além do mais, depois da modificação, grupos funcionais epóxi podem não mais ser parte da espinha dorsal de epóxi.[0028] The term “epoxy backbone” as used herein refers to that portion of a resin that is derived from an epoxy resin. If derived from an epoxy resin, the epoxy backbone may be derived from either aromatic or aliphatic epoxy resins. Suitable examples of aromatic epoxy resins are known to those skilled in the art and include, without limitation, epoxy resins derived from bisphenol A (BPA), BPF, novolac or cresol. Furthermore, after modification, epoxy functional groups may no longer be part of the epoxy backbone.
[0029] Como usado aqui, o termo “aceitador de MA epóxi” se refere a um aceitador de MA como definido aqui que inclui uma espinha dorsal de epóxi.[0029] As used herein, the term “epoxy MA acceptor” refers to an MA acceptor as defined herein that includes an epoxy backbone.
[0030] O termo “aceitador de MA não epóxi” como usado aqui se refere a um aceitador de MA como definido aqui que não inclui uma espinha dorsal de epóxi.[0030] The term “non-epoxy MA acceptor” as used herein refers to an MA acceptor as defined herein that does not include an epoxy backbone.
[0031] Como usado aqui, o termo “doador de MA epóxi” significa um doador de MA como definido aqui que inclui uma espinha dorsal de epóxi.[0031] As used herein, the term “epoxy MA donor” means an MA donor as defined herein that includes an epoxy backbone.
[0032] Como usado aqui, o termo “doador de MA não epóxi” significa um doador de MA como definido aqui que não inclui uma espinha dorsal de epóxi.[0032] As used herein, the term “non-epoxy MA donor” means an MA donor as defined herein that does not include an epoxy backbone.
[0033] Por “aceitador de MA/doador” entende-se uma molécula tendo pelo menos um grupo funcional de aceitador de adição de Michael (MA) e pelo menos um grupo funcional de doador de adição de Michael (MA).[0033] By “MA acceptor/donor” is meant a molecule having at least one Michael addition acceptor (MA) functional group and at least one Michael addition donor (MA) functional group.
[0034] O termo “reticulador” se refere a uma molécula capaz de formar uma ligação covalente entre polímeros ou entre duas regiões diferentes do mesmo polímero.[0034] The term “crosslinker” refers to a molecule capable of forming a covalent bond between polymers or between two different regions of the same polymer.
[0035] O termo “autorreticulável”, quando usado no contexto de um polímero autorreticulável, se refere à capacidade de um polímero de entrar em uma reação de reticulação consigo mesmo e/ou com uma outra molécula do polímero, na ausência de um reticulador externo, para formar uma ligação covalente entre os mesmos. Tipicamente, esta reação de reticulação ocorre através de reação de grupos funcionais reativos complementares presentes sobre o próprio polímero autorreticulável ou duas moléculas separadas do polímero autorreticulável.[0035] The term “self-crosslinkable”, when used in the context of a self-crosslinkable polymer, refers to the ability of a polymer to enter into a crosslinking reaction with itself and/or with another molecule of the polymer, in the absence of an external crosslinker. , to form a covalent bond between them. Typically, this crosslinking reaction occurs through the reaction of complementary reactive functional groups present on the self-crosslinking polymer itself or two separate molecules of the self-crosslinking polymer.
[0036] O termo “dispersão” no contexto de um polímero dispersável se refere à mistura de um polímero dispersável e um veículo. O termo “dispersão” é destinado a incluir o termo “solução”.[0036] The term “dispersion” in the context of a dispersible polymer refers to the mixture of a dispersible polymer and a carrier. The term “dispersion” is intended to include the term “solution”.
[0037] O termo “temperatura ambiente”, como usado aqui se refere à temperatura circundante em um típico ambiente interno ou temperatura do recinto, isto é, uma temperatura de cerca de 20°C a 25°C (68°F a 77°F).[0037] The term “ambient temperature” as used herein refers to the surrounding temperature in a typical indoor environment or room temperature, that is, a temperature of about 20°C to 25°C (68°F to 77° F).
[0038] O termo “sobre”, quando usado no contexto de um revestimento aplicado sobre uma superfície ou substrato, inclui revestimentos aplicados ou diretamente ou indiretamente à superfície ou substrato. Assim, por exemplo, um revestimento aplicado a uma camada primária sobrejacente a um substrato constitui um revestimento aplicado sobre o substrato.[0038] The term “on”, when used in the context of a coating applied to a surface or substrate, includes coatings applied either directly or indirectly to the surface or substrate. Thus, for example, a coating applied to a primary layer overlying a substrate constitutes a coating applied to the substrate.
[0039] O termo “composto orgânico volátil” (“VOC”) se refere a qualquer composto de carbono, excluindo monóxido de carbono, dióxido de carbono, ácido carbônico, carbonetos ou carbonatos metálicos e carbonato de amônio, que participa de reações fotoquímicas atmosféricas. Tipicamente, compostos orgânicos voláteis têm uma pressão de vapor igual ou superior a 0,1 mm Hg. Como usado aqui, “teor de composto orgânico volátil” (“teor de VOC”) significa o peso de VOC por volume dos sólidos do revestimento e é reportado, por exemplo, como quilogramas (kg) de VOC por litro.[0039] The term “volatile organic compound” (“VOC”) refers to any carbon compound, excluding carbon monoxide, carbon dioxide, carbonic acid, metal carbides or carbonates, and ammonium carbonate, that participates in atmospheric photochemical reactions . Typically, volatile organic compounds have a vapor pressure of 0.1 mm Hg or greater. As used herein, “volatile organic compound content” (“VOC content”) means the weight of VOC per volume of coating solids and is reported, for example, as kilograms (kg) of VOC per liter.
[0040] A menos de indicado de outra maneira, o termo “polímero” inclui tanto homopolímeros quanto copolímeros (isto é, polímeros de dois ou mais monômeros diferentes).[0040] Unless otherwise indicated, the term “polymer” includes both homopolymers and copolymers (that is, polymers of two or more different monomers).
[0041] O termo “compreende” e suas variações não tem um significado limitativo onde estes termos aparecem na descrição e nas reivindicações.[0041] The term “comprises” and its variations do not have a limiting meaning where these terms appear in the description and claims.
[0042] Os termos “preferido” e “preferivelmente” se referem a modalidades da invenção que podem propiciar certos benefícios, sob certas circunstâncias. Porém, outras modalidades podem também ser preferidas, sob as mesmas ou outras circunstâncias. Além do mais, a citação de uma ou mais modalidades preferidas não implica que outras modalidades não são utilizáveis e não se pretende excluir outras modalidades do escopo da invenção.[0042] The terms “preferred” and “preferably” refer to embodiments of the invention that may provide certain benefits, under certain circumstances. However, other modalities may also be preferred, under the same or different circumstances. Furthermore, the citation of one or more preferred embodiments does not imply that other embodiments are not usable and it is not intended to exclude other embodiments from the scope of the invention.
[0043] Como usado aqui, “um”, “uma”, “o(a)” “pelo menos um(a)” e “um(a) ou mais” são usados intercambiavelmente. Assim, por exemplo, uma composição de revestimento que compreende “um” aditivo pode ser interpretada como significando que a composição de revestimento inclui “um ou mais” aditivos.[0043] As used herein, “a”, “an”, “the”, “at least one” and “one or more” are used interchangeably. Thus, for example, a coating composition comprising "one" additive may be interpreted to mean that the coating composition includes "one or more" additives.
[0044] Também aqui, as citações de faixas numéricas por pontos extremos incluem todos os números agrupados dentro dessa faixa (por exemplo, 1 a 5 inclui 1; 1,5; 2; 2,75; 3; 3,80; 4; 5; etc.). Além do mais, a revelação de uma faixa inclui a revelação de todas subfaixas incluídas dentro da faixa mais ampla (por exemplo, 1 a 5 descreve 1 a 4; 1,5 a 4.5; 1 a 2; etc.).[0044] Also here, citations of numerical ranges by endpoints include all numbers grouped within that range (e.g., 1 to 5 includes 1; 1.5; 2; 2.75; 3; 3.80; 4; 5; etc.). Furthermore, revealing a range includes revealing all subranges included within the broader range (e.g., 1 to 5 describes 1 to 4; 1.5 to 4.5; 1 to 2; etc.).
[0045] A presente descrição provê métodos e composições para revestimentos resistentes à corrosão para uma variedade de substratos incluindo substratos de metal e substratos de aço. Especificamente, a presente descrição provê revestimentos primários resistentes à corrosão para substratos de aço não tratados ou pré-tratados, onde os revestimentos primários são derivados de componentes que curam via uma reação de adição de Michael.[0045] The present description provides methods and compositions for corrosion resistant coatings for a variety of substrates including metal substrates and steel substrates. Specifically, the present disclosure provides corrosion-resistant primer coatings for untreated or pretreated steel substrates, where the primer coatings are derived from components that cure via a Michael addition reaction.
[0046] Em uma modalidade, a presente descrição provê uma composição de revestimento. A composição inclui pelo menos um doador de MA, isto é, uma molécula tendo pelo menos um grupo funcional de doador de MA.[0046] In one embodiment, the present description provides a coating composition. The composition includes at least one MA donor, that is, a molecule having at least one MA donor functional group.
[0047] Exemplos apropriados de doadores de MA incluem, sem limitação, malonatos de dialquila (por exemplo, malonato de dimetila, malonato de dietila e similares), cianoacetatos (por exemplo, cianoacetato de metila, cianoacetato de etila e similares), cloroacetatos, acetoacetatos, acetatos de propionila, malononitrila, acetonitrila, acetilacetona, dipropionil metano e similares e misturas ou combinações dos mesmos. Exemplos preferidos de doadores de MA incluem, sem limitação, grupo malonato ou acetoacetato contendo compostos oligoméricos e poliméricos tais como, por exemplo, poliésteres, poliuretanos, poliacrilatos, resinas epóxi, poliamidas e resinas de polivinila contendo grupos funcionais malonato ou acetoacetato na cadeia principal, pendentes, ou ambos.[0047] Suitable examples of MA donors include, without limitation, dialkyl malonates (e.g., dimethyl malonate, diethyl malonate and the like), cyanoacetates (e.g., methyl cyanoacetate, ethyl cyanoacetate and the like), chloroacetates, acetoacetates, propionyl acetates, malononitrile, acetonitrile, acetylacetone, dipropionyl methane and the like and mixtures or combinations thereof. Preferred examples of MA donors include, without limitation, malonate or acetoacetate group containing oligomeric and polymeric compounds such as, for example, polyesters, polyurethanes, polyacrylates, epoxy resins, polyamides and polyvinyl resins containing malonate or acetoacetate functional groups in the main chain, pending, or both.
[0048] Em uma modalidade, o doador de MA descrito aqui é pelo menos uma resina polimérica tendo grupos funcionais de doador de adição de Michael. Em um aspecto, a espinha dorsal do doador de MA inclui espinha dorsal de epóxi. Em um aspecto preferido, a espinha dorsal de epóxi dos doadores de MA é aromática. Resinas epóxi aromáticas apropriadas que podem ser funcionalizadas para agir como doadores de MA incluem, sem limitação, epóxi bisfenol A e resinas epóxi de novolac. Em um aspecto, as resinas epóxi podem ser funcionalizadas por reação com diceteno, transesterificação com um acetoacetato de alquila ou malonato de dialquila, esterificação da resina epóxi com ácido malônico ou um monoéster ou poliéster malonatado funcional ácido e similares.[0048] In one embodiment, the MA donor described here is at least one polymeric resin having Michael addition donor functional groups. In one aspect, the backbone of the MA donor includes epoxy backbone. In a preferred aspect, the epoxy backbone of the MA donors is aromatic. Suitable aromatic epoxy resins that can be functionalized to act as MA donors include, without limitation, bisphenol A epoxy and novolac epoxy resins. In one aspect, epoxy resins can be functionalized by reaction with diketene, transesterification with an alkyl acetoacetate or dialkyl malonate, esterification of the epoxy resin with malonic acid or an acid functional malonated monoester or polyester, and the like.
[0049] Em uma modalidade, o doador de MA descrito aqui é uma resina que inclui uma espinha dorsal de epóxi aromática que foi funcionalizada com grupos doadores de adição de Michael.[0049] In one embodiment, the MA donor described here is a resin that includes an aromatic epoxy backbone that has been functionalized with Michael addition donor groups.
[0050] Em uma modalidade, a presente descrição provê uma composição de revestimento. A composição inclui pelo menos um aceitador de MA, isto é, uma molécula tendo pelo menos um grupo funcional doador de MA.[0050] In one embodiment, the present description provides a coating composition. The composition includes at least one MA acceptor, that is, a molecule having at least one MA donor functional group.
[0051] Exemplos apropriados de aceitadores de MA incluem, sem limitação, ésteres de ácido (met)acrílico, isto é um composto funcional de (met)acrilato derivado da reação de um composto funcional hidroxila (i) com ácido (met)acrílico ou seus derivados de éster (ii), em que o composto funcional hidroxila pode ser mono-, di-, ou polifuncional e tem como uma espinha dorsal que contém uma cadeia alifática, cicloalifática ou aromática, um (poli)epóxi, (poli)éter, (poli)éster por exemplo (poli)caprolactona, (poli)alquida, (poli)uretano, (poli)amina, (poli)amida, (poli)carbonato, (poli)olefina, (poli)siloxano, (poli)acrilato, halogênio (por exemplo flúor), um derivado de melamina, copolímeros de qualquer um deles e similares e suas misturas e combinações.[0051] Suitable examples of MA acceptors include, without limitation, esters of (meth)acrylic acid, i.e. a (meth)acrylate functional compound derived from the reaction of a hydroxyl functional compound (i) with (meth)acrylic acid or its ester derivatives (ii), in which the hydroxyl functional compound can be mono-, di-, or polyfunctional and has as a backbone containing an aliphatic, cycloaliphatic or aromatic chain, a (poly)epoxy, (poly)ether , (poly)ester e.g. (poly)caprolactone, (poly)alkyd, (poly)urethane, (poly)amine, (poly)amide, (poly)carbonate, (poly)olefin, (poly)siloxane, (poly) acrylate, halogen (e.g. fluorine), a melamine derivative, copolymers of any of them and the like and mixtures and combinations thereof.
[0052] Exemplos apropriados de ácidos que podem ser usados para funcionalizar a espinha dorsal de epóxi aromática incluem, sem limitação, ácido acrílico, ácido metacrílico e similares.[0052] Suitable examples of acids that can be used to functionalize the aromatic epoxy backbone include, without limitation, acrylic acid, methacrylic acid and the like.
[0053] Exemplos preferidos de tais aceitadores de MA incluem, sem limitação, os derivados de acrilato multifuncionais de resinas epóxi de glicidila (por exemplo, éter diglicidílico de bisfenol A) e resinas epóxi fenólicas de novolac. Em um aspecto particularmente preferido, o aceitador de MA descrito aqui é um epóxi acrilato aromático.[0053] Preferred examples of such MA acceptors include, without limitation, multifunctional acrylate derivatives of glycidyl epoxy resins (e.g., bisphenol A diglycidyl ether) and novolac phenolic epoxy resins. In a particularly preferred aspect, the MA acceptor described herein is an aromatic epoxy acrylate.
[0054] Em uma modalidade, o aceitador de MA descrito aqui pode ser pelo menos uma resina polimérica tendo grupos funcionais de aceitador de adição de Michael. Em um aspecto, o aceitador de MA é uma resina com uma espinha dorsal de epóxi aromática funcionalizada por reação com um ou mais grupos funcionais de aceitador de MA.[0054] In one embodiment, the MA acceptor described here may be at least one polymeric resin having Michael addition acceptor functional groups. In one aspect, the MA acceptor is a resin with an aromatic epoxy backbone functionalized by reaction with one or more MA acceptor functional groups.
[0055] Em uma modalidade, o aceitador de MA descrito aqui é uma resina que inclui uma espinha dorsal de epóxi aromática tendo grupos funcionais de aceitador de adição de Michael. Em um aspecto, o aceitador de MA é multifuncional, isto é, o aceitador de MA tem uma funcionalidade de preferivelmente 2 ou mais.[0055] In one embodiment, the MA acceptor described here is a resin that includes an aromatic epoxy backbone having Michael addition acceptor functional groups. In one aspect, the MA acceptor is multifunctional, that is, the MA acceptor has a functionality of preferably 2 or more.
[0056] Exemplos apropriados de aceitadores de MA com espinha dorsal de epóxi aromática incluem, sem limitação, resinas epóxi de glicidila acriladas (por exemplo, éter diglicidílico de bisfenol A (BPA)) e resinas epóxi acriladas de novolac. Em um aspecto preferido, o aceitador de MA descrito aqui é um epóxi acrilato BPA difuncional.[0056] Suitable examples of MA acceptors with aromatic epoxy backbone include, without limitation, acrylated glycidyl epoxy resins (e.g., bisphenol A diglycidyl ether (BPA)) and novolac acrylated epoxy resins. In a preferred aspect, the MA acceptor described herein is a difunctional BPA epoxy acrylate.
[0057] Em uma modalidade, a composição de resina pode incluir um ou mais componentes MA funcionalizados com epóxi e um ou mais componentes MA não funcionalizados com epóxi. Em um aspecto, a espinha dorsal da composição de resina inclui preferivelmente perto de 100%, mais preferivelmente 100% da espinha dorsal de epóxi. Em um outro aspecto, a espinha dorsal da composição de resina pode incluir menos do que 100% da espinha dorsal de epóxi.[0057] In one embodiment, the resin composition may include one or more epoxy-functionalized MA components and one or more non-epoxy-functionalized MA components. In one aspect, the backbone of the resin composition preferably includes close to 100%, more preferably 100% of the epoxy backbone. In another aspect, the backbone of the resin composition may include less than 100% epoxy backbone.
[0058] Exemplos apropriados de aceitadores de MA não epóxi incluem, sem limitação, vários ésteres de (met)acrilato de álcoois C1-C15 insubstituídos ou substituídos tais como, por exemplo, tripropileno glicol, álcool isobornilico, álcool isodecilico, álcool fenoxietílico, isocianurato de tris-hidroxietila, trimetilolpropano, etoxilato de ditrimetilolpropano (diTMPTA), hexanodiol, neopentil glicol etoxilado, neopentil glicol propoxilado, fenol etoxilado, polietileno glicol, trimetilolpropano, glicerol propoxilado, pentaeritritol, álcool tetra-hidrofurfurílico, álcool β- carboxietílico, ou combinações dos mesmos. Por exemplo, o monômero olefinico pode ser (met)acrilato de isobornila, (met)acrilato de isodecila, (met)acrilato de fenoxietila, tri(met)acrilato de trimetilolpropano, di(met)acrilato de ciclo-hexano dimetanol alcoxilado, tri(met)acrilato de etoxilato de trimetilolpropano, di(met)acrilato de dipropileno glicol, di(met)acrilato de tripropileno glicol, di(met)acrilato de hexanodiol, (met)acrilato tetra-hidrofurfurila, tri(met)acrilato de pentaeritritol, tetra(met)acrilato de pentaeritritol, penta(met)acrilato de di-pentaeritritol, hexa(met)acrilato de di-pentaeritritol, tetra(met)acrilato de di- (trimetiolpropano), tetra(met)acrilato de glicerol propoxilado, (met)acrilato de beta-carboxietila, di(met)acrilato de neopentil glicol etoxilado, di(met)acrilato de neopentil glicol propoxilado, tetra(met)acrilato e di-(trimetiolpropano) ou suas combinações. Em um aspecto preferido, o aceitador de MA de acrilato de não epóxi é tetra-acrilato de di-trimetilolpropano (DTMPTA).[0058] Suitable examples of non-epoxy MA acceptors include, without limitation, various (meth)acrylate esters of unsubstituted or substituted C1-C15 alcohols such as, for example, tripropylene glycol, isobornyl alcohol, isodecyl alcohol, phenoxyethyl alcohol, isocyanurate trishydroxyethyl, trimethylolpropane, ditrimethylolpropane ethoxylate (diTMPTA), hexanediol, ethoxylated neopentyl glycol, propoxylated neopentyl glycol, ethoxylated phenol, polyethylene glycol, trimethylolpropane, propoxylated glycerol, pentaerythritol, tetrahydrofurfuryl alcohol, β-carboxyethyl alcohol, or combinations thereof same. For example, the olefinic monomer may be isobornyl (meth)acrylate, isodecyl (meth)acrylate, phenoxyethyl (meth)acrylate, trimethylolpropane tri(meth)acrylate, cyclohexane di(meth)acrylate alkoxylated dimethanol, tri Trimethylolpropane ethoxylate (meth)acrylate, dipropylene glycol di(meth)acrylate, tripropylene glycol di(meth)acrylate, hexanediol di(meth)acrylate, tetrahydrofurfuryl (meth)acrylate, pentaerythritol tri(meth)acrylate , pentaerythritol tetra(meth)acrylate, di-pentaerythritol penta(meth)acrylate, di-pentaerythritol hexa(meth)acrylate, di-(trimethiolpropane tetra(meth)acrylate), propoxylated glycerol tetra(meth)acrylate, beta-carboxyethyl (meth)acrylate, ethoxylated neopentyl glycol di(meth)acrylate, propoxylated neopentyl glycol di(meth)acrylate, tetra(meth)acrylate and di-(trimethyolpropane) or combinations thereof. In a preferred aspect, the non-epoxy acrylate MA acceptor is di-trimethylolpropane tetraacrylate (DTMPTA).
[0059] Em um aspecto, os um ou mais aceitadores de MA de acrilato não epóxi têm uma funcionalidade de preferivelmente pelo menos 2 ou mais.[0059] In one aspect, the one or more non-epoxy acrylate MA acceptors have a functionality of preferably at least 2 or more.
[0060] Sem limitação à teoria, acredita-se que um doador de MA multifuncional e um aceitador de MA multifuncional vão reagir por meio de uma reação de adição de Michael e desse modo ajudar a melhorar a velocidade de cura, densidade de reticulado e desenvolvimento de dureza para as composições de revestimento descritas aqui. A densidade melhorada de reticulado curado e aumentado vai levar a características de desempenho melhoradas.[0060] Without limiting theory, it is believed that a multifunctional MA donor and a multifunctional MA acceptor will react via a Michael addition reaction and thereby help improve cure speed, crosslink density and development. of hardness for the coating compositions described herein. The improved density of cured and increased crosslinking will lead to improved performance characteristics.
[0061] Em uma modalidade, o doador de MA e o aceitador de MA são misturados entre si para obter uma composição de revestimento. Em um aspecto, cada um dentre o doador de MA e o aceitador de MA vai estar independentemente presentes em uma quantidade de cerca de 5 a 50 por cento em peso, preferivelmente 10 a 40 por cento em peso, com base no peso total da composição de revestimento. Em um aspecto, o índice estequiométrico de prótons ácidos de doador de MA para grupos insaturados de aceitador de MA é 10:1 a 0,1:1, preferivelmente 5:1 a 0,2:1, mais preferivelmente 1,5:1 a 0.,7:1.[0061] In one embodiment, the MA donor and the MA acceptor are mixed together to obtain a coating composition. In one aspect, each of the MA donor and the MA acceptor will be independently present in an amount of about 5 to 50 weight percent, preferably 10 to 40 weight percent, based on the total weight of the composition. of coating. In one aspect, the stoichiometric ratio of acidic MA donor protons to unsaturated MA acceptor groups is 10:1 to 0.1:1, preferably 5:1 to 0.2:1, more preferably 1.5:1 to 0.7:1.
[0062] Em uma modalidade, a composição de revestimento descrita aqui é uma composição reticulável obtida por uma reação de adição de Michael entre um ou mais doadores de MA e um ou mais aceitadores de MA. A reação de adição de Michael é catalisada por um catalisador de reticulação. Em um aspecto, o catalisador de reticulação é um catalisador latente de base.[0062] In one embodiment, the coating composition described here is a crosslinkable composition obtained by a Michael addition reaction between one or more MA donors and one or more MA acceptors. The Michael addition reaction is catalyzed by a cross-linking catalyst. In one aspect, the crosslinking catalyst is a base latent catalyst.
[0063] Em uma modalidade, o catalisador latente de base descrito aqui é um sal de carbonato substituído tendo a estrutura de um composto de Fórmula (I): X+é um cátion não ácido. Exemplos apropriados incluem, sem limitação, íon de metal alcalino, íon de metal alcalino-terroso, íon de amônio, íon de fosfônio e similares. Em um aspecto preferido, X+é um íon de lítio, sódio, ou potássio e similares. Mais preferivelmente, X+é um íon de amônio quaternário NR'4 ou um íon fosfônio PR'4, em que R é H, alquila C1-C10 insubstituída, arila, aralquila, alquila C1-C10 substituída, arila, aralquila e misturas ou combinações das mesmas. Em um aspecto preferido, R é um grupo alquila insubstituído tendo 1 a 4 átomos de carbono. Se o grupo R é substituído, os substituintes são selecionados de modo a não interferir substancialmente com a reação de reticulação. Em um aspecto, para evitar interferência com a ação do catalisador de base, substituintes ácidos, tais como, por exemplo, substituintes de ácido carboxílico estão presentes apenas em quantidades não substancias, ou totalmente ausentes.[0063] In one embodiment, the base latent catalyst described here is a substituted carbonate salt having the structure of a compound of Formula (I): X+ is a non-acidic cation. Suitable examples include, without limitation, alkali metal ion, alkaline earth metal ion, ammonium ion, phosphonium ion and the like. In a preferred aspect, X+ is a lithium, sodium, or potassium ion and the like. More preferably, combinations thereof. In a preferred aspect, R is an unsubstituted alkyl group having 1 to 4 carbon atoms. If the R group is substituted, the substituents are selected so as not to substantially interfere with the crosslinking reaction. In one aspect, to avoid interference with the action of the base catalyst, acidic substituents, such as, for example, carboxylic acid substituents are present only in insubstantial amounts, or absent altogether.
[0064] Em uma modalidade, o catalisador latente de base descrito aqui é um composto com a estrutura geral mostrada na Fórmula (I), em que o cátion X+ é ligado com o grupo carbonato de Fórmula (I) em uma única molécula, isto é, o catalisador latente de base tem a estrutura geral mostrada na Fórmula (II) [0064] In one embodiment, the base latent catalyst described here is a compound with the general structure shown in Formula (I), in which the X+ cation is linked with the carbonate group of Formula (I) in a single molecule, i.e. is, the base latent catalyst has the general structure shown in Formula (II)
[0065] Em uma outra modalidade, o catalisador latente de base descrito aqui é um composto com a estrutura geral mostrado na Fórmula (I), em que o grupo R é um polímero, e/ou o cátion X+ é um íon amônio quaternário NR'4 ou um íon fosfônio PR'4, em que pelo menos um R' é um polímero.[0065] In another embodiment, the base latent catalyst described here is a compound with the general structure shown in Formula (I), in which the R group is a polymer, and/or the X+ cation is a quaternary ammonium ion NR '4 or a phosphonium ion PR'4, wherein at least one R' is a polymer.
[0066] Em uma modalidade preferida, o catalisador latente de base descrito aqui é um composto com a estrutura geral mostrada na Fórmula (I), preferivelmente um carbonato de alquil amônio quaternário. Exemplos apropriados incluem, sem limitação, metil carbonato de tetra-hexilamônio, metil carbonato de tetradecil-(isto é, C14)-tri-hexilamônio e metil carbonato de tetradecilamônio, metilcarbonato de tetrabutilamônio, etilcarbonato de tetrabutilamônio, metil carbonato de benziltrimetilamônio ou metil carbonato de tri-hexilmetilamônio ou metil carbonato de trioctilmetilamônio e misturas ou combinações dos mesmos. Em um aspecto preferido, o catalisador latente de base descrito aqui inclui alquil carbonato de tetrabutilamônio.[0066] In a preferred embodiment, the base latent catalyst described here is a compound with the general structure shown in Formula (I), preferably a quaternary alkyl ammonium carbonate. Suitable examples include, without limitation, tetrahexylammonium methyl carbonate, tetradecyl-(i.e., C14)-trihexylammonium methyl carbonate and tetradecylammonium methyl carbonate, tetrabutylammonium methyl carbonate, tetrabutylammonium ethylcarbonate, benzyltrimethylammonium methyl carbonate or methyl carbonate of trihexylmethylammonium or trioctylmethylammonium methyl carbonate and mixtures or combinations thereof. In a preferred aspect, the base latent catalyst described herein includes tetrabutylammonium alkyl carbonate.
[0067] Em uma modalidade, a quantidade de catalisador latente de base usado aqui pode variar dependendo das propriedades da composição de revestimento. Preferivelmente, a composição inclui cerca de 0,001 a 1 meq de catalisador por grama de sólidos da resina, mais preferivelmente 0,02 a 0,07 meq por grama de sólidos da resina. Catalisadores latentes deste tipo são conhecidos na técnica. Por exemplo, uma versão comercialmente disponível do catalisador latente descrito aqui é chamada A-CURE 500 (Allnex, Frankfurt, Alemanha).[0067] In one embodiment, the amount of base latent catalyst used herein may vary depending on the properties of the coating composition. Preferably, the composition includes about 0.001 to 1 meq of catalyst per gram of resin solids, more preferably 0.02 to 0.07 meq per gram of resin solids. Latent catalysts of this type are known in the art. For example, a commercially available version of the latent catalyst described here is called A-CURE 500 (Allnex, Frankfurt, Germany).
[0068] Sem limitação à teoria, acredita-se que o catalisador latente de base de Fórmula (I) funciona liberando dióxido de carbono quando o sal de carbonato se decompõe. Isto produz uma base forte, isto é, um hidróxido, um alcóxi, ou uma base de aralquiloxi. Em um pote fechado, esta reação acontece lentamente, permitindo tempo de vida útil em armazenamento estendido. Quando o revestimento é aplicado e a área de superfície aumenta, a base é regenerada rapidamente à medida que dióxido de carbono escapa da superfície, permitindo uma cura mais rápida (isto é, secagem e desenvolvimento de dureza) do revestimento. Consequentemente, o uso de um catalisador latente de base de Fórmula (I) permite um tempo de vida útil em armazenamento, desempenho de cura e tempo de vida útil pós-abertura ótimos para as composições de revestimento reticuláveis descritas aqui.[0068] Without limiting theory, it is believed that the base latent catalyst of Formula (I) works by releasing carbon dioxide when the carbonate salt decomposes. This produces a strong base, that is, a hydroxide, an alkoxy, or an aralkyloxy base. In a closed jar, this reaction happens slowly, allowing for extended shelf life. When the coating is applied and the surface area increases, the base is rapidly regenerated as carbon dioxide escapes from the surface, allowing for faster curing (i.e., drying and hardness development) of the coating. Consequently, the use of a base latent catalyst of Formula (I) allows for optimal storage life, curing performance and post-opening shelf life for the crosslinkable coating compositions described herein.
[0069] Em uma modalidade, um catalisador de base não latente pode ser usado isoladamente ou em combinação com o catalisador latente de base descrito aqui para acelerar a reação de adição de Michael. Exemplos de catalisadores não latentes apropriados incluem, sem limitação, hidróxido de tetrabutil amônio, hidróxido de amônio, DBU (8-Diazabiciclo[5.4.0]undec-7- eno), DBN (1,5-Diazabiciclo[4.3.0]non-5-eno) e TMG (1,1,3,3- tetrametilguanidina).[0069] In one embodiment, a non-latent base catalyst can be used alone or in combination with the base latent catalyst described here to accelerate the Michael addition reaction. Examples of suitable non-latent catalysts include, without limitation, tetrabutyl ammonium hydroxide, ammonium hydroxide, DBU (8-Diazabicyclo[5.4.0]undec-7-ene), DBN (1,5-Diazabicyclo[4.3.0]non -5-ene) and TMG (1,1,3,3-tetramethylguanidine).
[0070] Exemplos adicionais apropriados de catalisadores não latentes incluem, sem limitação, sais de cátions não ácidos tais como K+, Na+, Li+, ou cátions fracamente ácidos tais como, por exemplo, espécies protonadas de bases orgânicas fortes tais como, por exemplo, DBU, DBN e similares, ou TMG e similares, emparelhadas com um ânion básico X- proveniente de um composto contendo grupo X-H ácido, onde X é N, P, O, S ou C e o ânion X-é um doador de MA capaz de reação com o aceitador de MA (por exemplo acrilato) e o ânion X- tem um pKa do correspondente ácido X-H que é mais do que duas unidades mais baixo do que o pKa do componente majoritário do doador (por exemplo resina acetoacetato-funcional). Exemplos apropriados de tais sais incluem, sem limitação, sais formados a partir da reação de KOH e benzotriazol, TBAH e benzotriazol, ou KOH e 1,2,4-triazola, incluídos em um nível entre 0,001 e 1 meq/grama sólido de resina. Misturas ou combinações dos acima podem ser usadas. O catalisador não latente preferido é uma solução de benzotriazolida de potássio formada a partir da reação de KOH e benzotriazol em uma razão molar igual em etanol.[0070] Additional suitable examples of non-latent catalysts include, without limitation, salts of non-acidic cations such as K+, Na+, Li+, or weakly acidic cations such as, for example, protonated species of strong organic bases such as, for example, DBU, DBN and the like, or TMG and the like, paired with a basic anion of reaction with the MA acceptor (e.g. acrylate) and the anion X- has a pKa of the corresponding acid . Suitable examples of such salts include, without limitation, salts formed from the reaction of KOH and benzotriazole, TBAH and benzotriazole, or KOH and 1,2,4-triazole, included at a level between 0.001 and 1 meq/gram solid resin. . Mixtures or combinations of the above can be used. The preferred non-latent catalyst is a solution of potassium benzotriazolide formed from the reaction of KOH and benzotriazole in an equal molar ratio in ethanol.
[0071] Opcionalmente, para estender o tempo de vida útil em armazenamento e o tempo de vida útil pós-abertura, um ou mais componentes adicionais podem ser incluídos tais como, por exemplo um ou mais grupos X- H ácidos, onde X é N, P, O, S, ou C, onde o ânion X é um doador de MA capaz de reação com o aceitador de MA e o pKa do grupo X-H é mais baixo do que o pKa do doador de MA majoritário (por exemplo resina acetoacetato- funcional), preferivelmente mais do que 2 unidades mais baixo. Exemplos apropriados incluem, sem limitação, etilacetoacetato, benzotriazol, succinimida, acetil acetona, ou 1,2,4-triazolem e misturas ou combinações dos mesmos. Em um aspecto preferido, o componente é benzotriazol, presente em uma quantidade de entre cerca de 0,5 e 5%, mais preferivelmente entre cerca de 0,5% e 1,5%, com base no peso total de sólidos da resina.[0071] Optionally, to extend the shelf life in storage and the shelf life after opening, one or more additional components may be included such as, for example, one or more acidic X-H groups, where X is N , P, O, S, or C, where the anion - functional), preferably more than 2 units lower. Suitable examples include, without limitation, ethylacetoacetate, benzotriazole, succinimide, acetyl acetone, or 1,2,4-triazolem and mixtures or combinations thereof. In a preferred aspect, the component is benzotriazole, present in an amount of between about 0.5 and 5%, more preferably between about 0.5% and 1.5%, based on the total solids weight of the resin.
[0072] Em uma modalidade, a composição de revestimento descrita aqui inclui um componente removedor de ácido ou de tamponamento de pH-. Exemplos apropriados incluem, sem limitação, óxido metálico (por exemplo, óxido de zinco, óxido de zinco nanoparticulado, óxido de magnésio, óxido de cálcio, óxido de estrôncio, óxido de bário, óxido de lantânio, óxido de itérbio, óxido de zircônio e similares), óxidos de metal mistos (por exemplo, MgO- TiO2 e similares), zeólitas (por exemplo, zeólita trocada com césio, zeólita ocluída com X,Y-Cs e similares), materiais mesoporosos modificados (por exemplo, sílica mesoporosa revestida com MgO (SBA-15), sílica mesoporosa amino-funcionalizada (MCM-41), oxinitreto de silício mesoporoso e similares), hidróxido metálico (por exemplo, hidróxido de cálcio, Na/NaOH/Al2O3, Na/MgO e similares), nitreto metálico, oxinitreto metálico (por exemplo, oxinitreto de silício, oxinitreto de aluminofosfato, oxinitreto de zirconofosfato, NaNO3 calcinado e similares), carbonato metálico (por exemplo, carbonato de cálcio, carbonato de sódio, carbonato de potássio e similares), silicato metálico (por exemplo, silicato de cálcio, borossilicato de cálcio, silicato de magnésio, hidrotalcita de Mg-Al, crisotila e similares), sais de carboxilato metálico (por exemplo, acetilacetato de titânio e similares), compostos de metal orgânicos (por exemplo, zirconato orgânico, titanato de base fraca, titanato de tetraalquila e similares), aminas (por exemplo, guanidina, aziridina, amidina, trietanolamina, DMP30 e similares), imidas (por exemplo, carbodi-imida e similares), compostos diaza-biciclo (por exemplo, DABCO e similares) e misturas ou combinações dos mesmos.[0072] In one embodiment, the coating composition described herein includes an acid-scavenging or pH-buffering component. Suitable examples include, without limitation, metal oxide (e.g., zinc oxide, nanoparticulate zinc oxide, magnesium oxide, calcium oxide, strontium oxide, barium oxide, lanthanum oxide, ytterbium oxide, zirconium oxide and the like), mixed metal oxides (e.g. MgO-TiO2 and the like), zeolites (e.g. cesium exchanged zeolite, X,Y-Cs occluded zeolite and the like), modified mesoporous materials (e.g. coated mesoporous silica with MgO (SBA-15), amino-functionalized mesoporous silica (MCM-41), mesoporous silicon oxynitride and the like), metal hydroxide (for example, calcium hydroxide, Na/NaOH/Al2O3, Na/MgO and the like), metal nitride, metal oxynitride (e.g. silicon oxynitride, aluminophosphate oxynitride, zirconophosphate oxynitride, calcined NaNO3 and the like), metal carbonate (e.g. calcium carbonate, sodium carbonate, potassium carbonate and the like), metal silicate (e.g., calcium silicate, calcium borosilicate, magnesium silicate, Mg-Al hydrotalcite, chrysotile and the like), metal carboxylate salts (e.g., titanium acetylacetate and the like), organic metal compounds (e.g., organic zirconate, weak base titanate, tetraalkyl titanate and the like), amines (e.g. guanidine, aziridine, amidine, triethanolamine, DMP30 and the like), imides (e.g. carbodiimide and the like), diaza-bicycle compounds ( e.g. DABCO and the like) and mixtures or combinations thereof.
[0073] Consequentemente, em uma modalidade, as composições de revestimento descritas aqui são aplicadas sobre um substrato ácido, tal como por exemplo, um substrato metálico com um pré-tratamento aplicado sobre ele. Exemplos apropriados de pré-tratamento incluem, sem limitação, fosfato de ferro, fosfato de zinco, silano, zircônio e similares. Muitos outros pré- tratamentos são conhecidos na indústria de pré-tratamento de metal. Em um aspecto preferido, o substrato metálico tem um tratamento de fosfato de ferro aplicado sobre ele.[0073] Consequently, in one embodiment, the coating compositions described here are applied to an acidic substrate, such as, for example, a metallic substrate with a pretreatment applied thereto. Suitable examples of pretreatment include, without limitation, iron phosphate, zinc phosphate, silane, zirconium and the like. Many other pretreatments are known in the metal pretreatment industry. In a preferred aspect, the metal substrate has an iron phosphate treatment applied thereto.
[0074] Em algumas modalidades, as composições de revestimento descritas aqui incluem opcionalmente um ou mais promotores de adesão. Por “promotor de adesão” entende-se um aditivo que é incluído em uma composição de revestimento para formar ligações primárias com ou a superfície do substrato ou com qualquer revestimento ou pré-tratamento previamente aplicado. Como usados aqui, o um ou mais promotores de adesão funcionam para melhorar a adesão a seco, adesão a úmido, ou preferivelmente, ambas, de uma composição de revestimento primário ao substrato.[0074] In some embodiments, the coating compositions described here optionally include one or more adhesion promoters. By "adhesion promoter" is meant an additive that is included in a coating composition to form primary bonds with either the surface of the substrate or with any previously applied coating or pretreatment. As used herein, the one or more adhesion promoters function to improve dry adhesion, wet adhesion, or preferably both, of a primer coating composition to the substrate.
[0075] Exemplos apropriados de promotores de adesão úteis com as composições de revestimento descritas aqui incluem, sem limitação, silanos, silicones, metais catalíticos e similares. Destes, promotores de adesão ou agentes de copulação de organossilano são preferidos.[0075] Suitable examples of adhesion promoters useful with the coating compositions described herein include, without limitation, silanes, silicones, catalytic metals and the like. Of these, adhesion promoters or organosilane coupling agents are preferred.
[0076] Em uma modalidade, se presente na composição de revestimento, o promotor de adesão está presente em uma quantidade de preferivelmente 2 a 20, mais preferivelmente 5 a 15 e ainda mais preferivelmente 7 a 10 por cento em peso, com base no peso total de sólidos da resina na composição de revestimento.[0076] In one embodiment, if present in the coating composition, the adhesion promoter is present in an amount of preferably 2 to 20, more preferably 5 to 15 and even more preferably 7 to 10 weight percent, based on weight total resin solids in the coating composition.
[0077] A composição de revestimento descrita aqui pode também incluir outros ingredientes opcionais que não afetam adversamente a composição de revestimento ou uma composição de revestimento curada resultando da mesma. Tais ingredientes opcionais são tipicamente incluídos em uma composição de revestimento para realçar a estética do revestimento; para facilitar fabricação, processamento, manipulação e aplicação da composição; e para melhorar ainda mais uma propriedade funcional particular de uma composição de revestimento ou uma composição de revestimento curada resultando da mesma. Por exemplo, a composição descrita aqui pode incluir opcionalmente cargas, catalisadores, lubrificantes, pigmentos, tensoativos, corantes, colorantes, tonalizadores, coalescentes, extensores, agentes anticorrosão, agentes de controle de fluxo, agentes tixotrópicos, agentes dispersantes, antioxidantes, promotores de adesão, light estabilizadores à luz e suas misturas, como requerido para prover as propriedades de filme desejadas. Cada ingrediente opcional é preferivelmente incluído em uma quantidade suficiente para servir à sua finalidade pretendida, mas não em uma quantidade tal a afetar adversamente uma composição de revestimento ou uma composição de revestimento curada resultando dela.[0077] The coating composition described here may also include other optional ingredients that do not adversely affect the coating composition or a cured coating composition resulting therefrom. Such optional ingredients are typically included in a coating composition to enhance the aesthetics of the coating; to facilitate manufacture, processing, handling and application of the composition; and to further improve a particular functional property of a coating composition or a cured coating composition resulting therefrom. For example, the composition described herein may optionally include fillers, catalysts, lubricants, pigments, surfactants, dyes, colorants, toners, coalescers, extenders, anticorrosion agents, flow control agents, thixotropic agents, dispersing agents, antioxidants, adhesion promoters. , light light stabilizers and mixtures thereof, as required to provide the desired film properties. Each optional ingredient is preferably included in an amount sufficient to serve its intended purpose, but not in an amount such as to adversely affect a coating composition or a cured coating composition resulting therefrom.
[0078] Em uma modalidade, a composição descrita aqui pode incluir componentes de resina que não sofrem reação de adição de Michael, além dos doadores de MA e aceitadores de MA descritos aqui. Estes componentes de resina adicionais podem não ter nenhum grupo funcional reativo ou ter grupos funcionais reativos que sofrem reações diferentes da reação de adição de Michael.[0078] In one embodiment, the composition described here may include resin components that do not undergo a Michael addition reaction, in addition to the MA donors and MA acceptors described here. These additional resin components may have no reactive functional groups or have reactive functional groups that undergo reactions other than the Michael addition reaction.
[0079] Por exemplo, em um aspecto, a composição descrita aqui pode incluir um correagente, tal como, sem limitação, um correagente de amina. A presença de um tal correagente ajuda a melhorar certas características de desempenho da composição descrita aqui, tais como resistência à corrosão. Em um aspecto, onde a composição descrita aqui é uma composição em duas partes, o correagente pode ser incluído na primeira parte (parte A) ou na segunda parte (parte B) da composição. Em um aspecto preferido, o correagente é um correagente de amina presente na parte B da composição. Se presentem o correagente de amina está presente em uma quantidade de cerca de 0,01 a 1 por cento em peso, preferivelmente 0,05 a 0,1 por cento em peso, com base no peso total dos sólidos da resina.[0079] For example, in one aspect, the composition described herein may include a co-agent, such as, without limitation, an amine co-agent. The presence of such a co-agent helps to improve certain performance characteristics of the composition described herein, such as corrosion resistance. In one aspect, where the composition described herein is a two-part composition, the co-agent may be included in the first part (part A) or the second part (part B) of the composition. In a preferred aspect, the co-agent is an amine co-agent present in part B of the composition. If present the amine co-agent is present in an amount of about 0.01 to 1 weight percent, preferably 0.05 to 0.1 weight percent, based on the total weight of the resin solids.
[0080] Em uma modalidade, a composição de revestimento descrita aqui pode incluir um solvente. Solventes apropriados podem ser aquosos, orgânicos ou suas misturas. Exemplos apropriados de solventes orgânicos incluem, sem limitação, solventes alifáticos, solventes aromáticos e/ou aromáticos alquilados (por exemplo, tolueno, xileno e similares), álcoois (por exemplo, isopropanol), ésteres (por exemplo, acetato de metoxi propanol, acetato de butila, acetato de isobutila e similares), cetonas (por exemplo, metil etil cetona, metil amil cetona e similares), éteres de glicol, ésteres éter glicílicos e misturas ou combinações dos mesmos. Em um aspecto, a composição de revestimento descrita aqui tem um baixo teor de composto orgânico volátil (VOC), preferivelmente menos do que 400 g/L, mais preferivelmente menos do que 300 g/L e o mais preferivelmente menos do que 250 g/L.[0080] In one embodiment, the coating composition described here may include a solvent. Suitable solvents may be aqueous, organic or mixtures thereof. Suitable examples of organic solvents include, without limitation, aliphatic solvents, aromatic and/or alkylated aromatic solvents (e.g., toluene, xylene and the like), alcohols (e.g., isopropanol), esters (e.g., methoxy propanol acetate, butyl acetate, isobutyl acetate and the like), ketones (for example, methyl ethyl ketone, methyl amyl ketone and the like), glycol ethers, glycyl ether esters and mixtures or combinations thereof. In one aspect, the coating composition described herein has a low volatile organic compound (VOC) content, preferably less than 400 g/L, more preferably less than 300 g/L and most preferably less than 250 g/L. L.
[0081] Em uma modalidade, a composição de revestimento descrita aqui pode ser usada as um revestimento primário ou pode ser parte de uma formulação de revestimento primário. Quando usado como um revestimento primário ou em uma formulação de revestimento primário, a composição descrita aqui pode ser aplicada sobre um substrato não tratado, um substrato pré-tratado, um substrato com um revestimento temporário aplicado sobre ele e similares. Em um aspecto preferido, a composição descrita aqui é aplicada sobre um substrato metálico com um pré-tratamento ácido, preferivelmente um pré-tratamento com fosfato.[0081] In one embodiment, the coating composition described here can be used as a primer coating or can be part of a primer coating formulation. When used as a primer coating or in a primer coating formulation, the composition described herein can be applied to an untreated substrate, a pretreated substrate, a substrate with a temporary coating applied thereon, and the like. In a preferred aspect, the composition described herein is applied to a metal substrate with an acid pretreatment, preferably a phosphate pretreatment.
[0082] Em uma modalidade, a composição de revestimento descrita aqui pode ser usada como um revestimento final. Em um aspecto, um primeiro revestimento (tal como um revestimento primário, por exemplo) é aplicado sobre um substrato não tratado, um substrato pré-tratado, um substrato com um revestimento temporário aplicado sobre ele e similares. Então, um segundo revestimento (tal como um revestimento final, por exemplo) é aplicado sobre o revestimento primário. Em um aspecto, o segundo revestimento é aplicado somente depois que o primeiro revestimento secou ou curou completamente. Em um aspecto alternativo, o segundo revestimento é aplicado sobre o primeiro revestimento antes que o primeiro revestimento tenha secado ou curado completamente. Quando a composição de revestimento é destinada a uso exterior e/ou destinada a ser um revestimento sujeito a intempéries, por exemplo como uma aplicação como revestimento final ou direto sobre metal (monorrevestimento), é preferido que a espinha dorsal de resina de todos aceitadores de MA e doadores de MA dentro da composição inclua menos do que 100%, preferivelmente menos do que 75% e mais preferivelmente menos do que 50% da espinha dorsal de epóxi.[0082] In one embodiment, the coating composition described here can be used as a top coat. In one aspect, a first coat (such as a primer coat, for example) is applied to an untreated substrate, a pretreated substrate, a substrate with a temporary coating applied thereto, and the like. Then, a second coat (such as a top coat, for example) is applied over the primary coat. In one aspect, the second coat is applied only after the first coat has completely dried or cured. In an alternative aspect, the second coat is applied over the first coat before the first coat has completely dried or cured. When the coating composition is intended for exterior use and/or intended as a weatherable coating, for example as a topcoat or direct coating application on metal (monocoat), it is preferred that the resin backbone of all heat acceptors MA and MA donors within the composition include less than 100%, preferably less than 75% and more preferably less than 50% of the epoxy backbone.
[0083] Em uma modalidade, a composição de revestimento descrita aqui pode ser usada como um revestimento primário e qualquer revestimento final pode ser aplicado sobre o revestimento primário descrito. Em um aspecto, a composição de revestimento final é também obtida por uma reação de adição de Michael. O revestimento final derivado por adição de Michael pode ser o mesmo ou diferente do que a composição de revestimento primário derivada por adição de Michael descrita aqui. Em um outro aspecto, a composição de revestimento final pode ser um componente não derivado por uma reação de adição de Michael, mas conhecido na técnica como um material de revestimento final apropriado, tal como as um revestimento final se poliuretano, por exemplo. Revestimentos finais derivados por adição de Michael são conhecidos na técnica, como descrito na patente US 8.962.725, por exemplo, incorporada aqui por referência.[0083] In one embodiment, the coating composition described here can be used as a primer coat and any top coat can be applied over the described primer coat. In one aspect, the final coating composition is also obtained by a Michael addition reaction. The Michael addition-derived top coat may be the same or different from the Michael addition-derived primer coating composition described herein. In another aspect, the topcoat composition may be a component not derived by a Michael addition reaction, but known in the art as a suitable topcoat material, such as a polyurethane topcoat, for example. Topcoats derived by Michael addition are known in the art, as described in US patent 8,962,725, for example, incorporated herein by reference.
[0084] Convencionalmente, composições de revestimento derivadas por adição de Michael demonstravam resposta de cura melhorada em relação a revestimentos primários tradicionais feitos com poliuretano, epóxi, sistemas não isocianato e similares. Porém, o uso de tais revestimentos derivados por adição de Michael tem sido limitado devido à má adesão a vários substratos e devido a uma falta de resistência à corrosão, particularmente quando aplicados como um revestimento primário ou como um revestimento direto sobre metal (DTM) sobre um substrato metálico, particularmente um substrato de aço pré-tratado.[0084] Conventionally, coating compositions derived by Michael addition demonstrated improved curing response over traditional primer coatings made with polyurethane, epoxy, non-isocyanate systems and the like. However, the use of such Michael addition-derived coatings has been limited due to poor adhesion to various substrates and due to a lack of corrosion resistance, particularly when applied as a primer coating or as a direct-on-metal (DTM) coating on a metallic substrate, particularly a pretreated steel substrate.
[0085] Surpreendentemente e em contradição com os preceitos da indústria e conhecimento da técnica, as composições de revestimento derivadas por adição de Michael descritas aqui demonstram a esperada resposta de cura melhorada, mas também mostram adesão e resistência ótimas à corrosão. Consequentemente, estas composições podem ser usadas como composições de revestimento primário ou revestimentos diretos com metal aplicadas a substratos de metal ou substratos de aço pré-tratados.[0085] Surprisingly and in contradiction to industry precepts and knowledge of the art, the Michael addition-derived coating compositions described here demonstrate the expected improved curing response, but also show optimal adhesion and corrosion resistance. Accordingly, these compositions can be used as primer coating compositions or direct metal coatings applied to metal substrates or pretreated steel substrates.
[0086] As composições descritas aqui também mostram um prazo de durabilidade e tempo de vida útil em armazenamento melhorados em relação aos revestimentos convencionais e o conhecimento de tais revestimentos na técnica. Em um aspecto, as composições descritas aqui têm um prazo de durabilidade ótima e não demonstram nenhuma perda de resposta de cura ou qualquer aumento de viscosidade depois de armazenamento por pelo menos uma semana a temperaturas de cerca de 48,8°C (120°F). Em um outro aspecto, as composições de revestimento descritas aqui também demonstram tempo de vida útil em armazenamento ótima, onde a composição leva preferivelmente mais do que 60 minutos, mais preferivelmente mais do que 120 minutos, para dobrar em viscosidade depois de misturar.[0086] The compositions described here also show improved durability and shelf life over conventional coatings and the knowledge of such coatings in the art. In one aspect, the compositions described herein have an optimum shelf life and demonstrate no loss of curing response or any increase in viscosity after storage for at least one week at temperatures of about 48.8°C (120°F). ). In another aspect, the coating compositions described herein also demonstrate optimal shelf life, where the composition preferably takes more than 60 minutes, more preferably more than 120 minutes, to double in viscosity after mixing.
[0087] A composição de revestimento da presente invenção pode ser aplicada a um substrato ou antes, ou depois do substrato ser conformado em um artigo. Em um aspecto, a composição de revestimento descrita aqui pode ser aplicada sobre uma variedade de substratos. Exemplos apropriados incluem, sem limitação, construções naturais e projetadas e materiais de construção, contêineres de carga, materiais de piso, paredes, móveis, outros materiais de construção, veículos a motor, componentes de veículos a motor, componentes de aeronaves, caminhões, vagões ferroviários e motores a explosão, pontes, torres de água, torres de telefone celular, torres eólicas, torres de rádio, acessórios de iluminação, estátuas, suportes para cartazes, cercas, grades de proteção, túneis, tubos, componentes marítimos, componentes de maquinário, laminados, componentes de equipamentos, utensílios e embalagens. Materiais de substrato exemplificativos incluem, sem limitação, madeira, plásticos, termofixos, metais, ligas metálicas, composições, intermetálicas, compósitos contendo metal e combinações destes. Metais de substrato exemplificativos incluem, sem limitação, alumínio, aço, aço para intempéries e aço inoxidável. Em um aspecto preferido, o substrato é aço, preferivelmente aço com um pré-tratamento aplicado sobre ele.[0087] The coating composition of the present invention can be applied to a substrate either before or after the substrate is formed into an article. In one aspect, the coating composition described herein can be applied to a variety of substrates. Suitable examples include, without limitation, natural and engineered buildings and construction materials, cargo containers, flooring materials, walls, furniture, other construction materials, motor vehicles, motor vehicle components, aircraft components, trucks, railcars railway and explosion engines, bridges, water towers, cell phone towers, wind towers, radio towers, lighting fixtures, statues, sign stands, fences, guardrails, tunnels, pipes, marine components, machinery components , laminates, equipment components, utensils and packaging. Exemplary substrate materials include, without limitation, wood, plastics, thermosets, metals, metal alloys, intermetallic compositions, metal-containing composites, and combinations thereof. Exemplary substrate metals include, without limitation, aluminum, steel, weathering steel and stainless steel. In a preferred aspect, the substrate is steel, preferably steel with a pretreatment applied thereto.
[0088] A composição de revestimento descrita aqui pode ser aplicada por qualquer método conhecida na técnica. Métodos de aplicação padrões incluem, sem limitação, por exemplo por aplicação escova, pulverização, revestimento giratório, revestimento por rolo, revestimento em cortina, imersão, revestimento por gravura, aplicação em campânula e/ou similares. No caso de substratos de termofixos dois componentes, o revestimento pode ser aplicado via processos em molde. Quando a composição de revestimento é aplicada por métodos de pulverização, equipamento de pulverização convencional ou pneumático ou pneumaticamente assistido, ou equipamento de pulverização não pneumático podem ser usados. Equipamentos tanto eletrostáticos quanto não eletrostáticos podem ser usados.[0088] The coating composition described here can be applied by any method known in the art. Standard application methods include, without limitation, for example by brush application, spraying, spin coating, roller coating, curtain coating, dipping, gravure coating, bell application and/or the like. In the case of two-component thermoset substrates, the coating can be applied via in-mold processes. When the coating composition is applied by spraying methods, conventional or pneumatic or pneumatically assisted spray equipment, or non-pneumatic spray equipment can be used. Both electrostatic and non-electrostatic equipment can be used.
[0089] A espessura do revestimento de uma camada particular e do sistema de revestimento global vai variar dependendo do material de revestimento usado, do substrato, do método de aplicação do revestimento e do uso final para o artigo revestido. Quando usado como um revestimento primário aplicado sobre um substrato metálico não tratado ou pré-tratado, a espessura do filme de revestimento aplicado é preferivelmente cerca de 1,27 a 500 mícrons, mais preferivelmente 10 a 100 mícrons e ainda mais preferivelmente 25 a 70 mícrons).[0089] The coating thickness of a particular layer and the overall coating system will vary depending on the coating material used, the substrate, the method of applying the coating and the end use for the coated article. When used as a primary coating applied to an untreated or pretreated metal substrate, the thickness of the applied coating film is preferably about 1.27 to 500 microns, more preferably 10 to 100 microns, and even more preferably 25 to 70 microns. ).
[0090] Em uma modalidade, a composição descrita aqui provê um revestimento curado com cura e resistência ótimas à corrosão. Em um aspecto, depois que o revestimento é aplicado a um substrato, ele é curado dentro de 1 a 10 minutos a uma temperatura de cozimento de 65,5°C (150°F) , onde o termo “curado” significa pelo menos parcialmente, preferivelmente totalmente, reticulado. Como uma medida de cura ideal, o revestimento curado demonstra uma dureza de lápis de preferivelmente pelo menos H, mais preferivelmente pelo menos 2H, ainda mais preferivelmente pelo menos 5H.[0090] In one embodiment, the composition described here provides a cured coating with optimal cure and corrosion resistance. In one aspect, after the coating is applied to a substrate, it is cured within 1 to 10 minutes at a baking temperature of 65.5°C (150°F), where the term “cured” means at least partially , preferably fully, cross-linked. As a measure of ideal cure, the cured coating demonstrates a pencil hardness of preferably at least H, more preferably at least 2H, even more preferably at least 5H.
[0091] Em uma modalidade, a composição descrita aqui provê um revestimento curado com cura e resistência ideais à corrosão. Em um aspecto, a resistência à corrosão do revestimento curado é medida depois de exposição a névoa salina por pelo menos 500 horas. Como uma medida de resistência à corrosão, o revestimento curado demonstra fluência do traço de preferivelmente menos do que cerca de 3 mm, mais preferivelmente menos do que cerca de 2 mm e mostra pouca ou nenhuma ferrugem ou bolha por exposição estendida a pulverização de sal, testes de corrosão cíclica ou outros testes de corrosão acelerada comumente usados na indústria.[0091] In one embodiment, the composition described here provides a cured coating with ideal cure and corrosion resistance. In one aspect, the corrosion resistance of the cured coating is measured after exposure to salt spray for at least 500 hours. As a measure of corrosion resistance, the cured coating demonstrates trace creep of preferably less than about 3 mm, more preferably less than about 2 mm, and shows little or no rust or blistering upon extended exposure to salt spray. cyclic corrosion tests or other accelerated corrosion tests commonly used in industry.
[0092] A invenção é ilustrada pelos seguintes exemplos. Deve ficar entendido que os exemplos, materiais, quantidades e procedimentos particulares devem ser interpretados amplamente de acordo com o escopo e espirito das invenções como descritas aqui. A menos de indicado de outro modo, todas as partes e porcentagens são em peso e todos pesos moleculares são peso molecular médio em peso.[0092] The invention is illustrated by the following examples. It should be understood that particular examples, materials, quantities and procedures should be interpreted broadly in accordance with the scope and spirit of the inventions as described herein. Unless otherwise indicated, all parts and percentages are by weight and all molecular weights are weight average molecular weight.
[0093] A menos de indicado de outro modo, foram utilizados os seguintes métodos de teste nos Exemplos que se seguem.[0093] Unless otherwise indicated, the following test methods were used in the Examples that follow.
[0094] A resistência à corrosão de revestimentos curados preparados a partir da composição descrita aqui é testada usando o método de névoa salina, como descrito em ASTM B117 (Prática Padrão para Operar Aparelho de Névoa de Sal). Resultados são expressos por grau de formação de bolhas (ASTM D714), ferrugem (ASTM D610) e fluência proveniente de riscos (ASTM D1654-08). A fluência proveniente de riscos é expressa sobre uma escala de 0 a 10, onde 0 indica corrosão extensa no risco e 10 indica que o revestimento é inalterado por exposição ao ambiente corrosivo. As classificações de ferrugem para revestimentos submetidos a exposição a névoa salina em um ambiente úmido são também expressas sobre uma escala de 0 a 10 onde 0 indica ferrugem completa na superfície e 10 indica nenhuma ferrugem na superfície de acordo com ASTM D610. As classificações de formação de bolhas são expressas sobre uma escala de 0 ao 10 onde 0 é formação de bolhas excessiva e 10 é nenhuma formação de bolha de acordo com ASTM D714.[0094] The corrosion resistance of cured coatings prepared from the composition described here is tested using the salt fog method, as described in ASTM B117 (Standard Practice for Operating Salt Fog Apparatus). Results are expressed by degree of blistering (ASTM D714), rust (ASTM D610) and creep from scratches (ASTM D1654-08). Creep from scratches is expressed on a scale of 0 to 10, where 0 indicates extensive corrosion in the scratch and 10 indicates that the coating is unaffected by exposure to the corrosive environment. Rust ratings for coatings subjected to exposure to salt spray in a humid environment are also expressed on a scale of 0 to 10 where 0 indicates complete surface rust and 10 indicates no surface rust in accordance with ASTM D610. Blistering ratings are expressed on a scale of 0 to 10 where 0 is excessive blistering and 10 is no blistering in accordance with ASTM D714.
[0095] A resistência à corrosão de revestimentos curados preparados a partir da composição descrita aqui é também testada medindo a fluência depois de exposição a um ambiente corrosivo, como descrito em ASTM D 1654-08 (Método de Teste Padrão para Avaliação de Corpos de Prova Pintados ou Revestidos Submetidos a Ambientes Corrosivos). Um revestimento é aplicado a um painel e curado. O painel é então riscado no metal e exposto a névoa salina por um dado período de tempo. A perda de tinta a partis do risco é medida e resultados são expressos como a quantidade de fluência (in mm) a partir do risco. Para revestimentos comercialmente viáveis, fluência a partir de risco de 2 mm ou menos é desejada.[0095] The corrosion resistance of cured coatings prepared from the composition described here is also tested by measuring creep after exposure to a corrosive environment, as described in ASTM D 1654-08 (Standard Test Method for Evaluating Specimens Painted or Coated Subjected to Corrosive Environments). A coating is applied to a panel and cured. The panel is then scratched into the metal and exposed to salt spray for a set period of time. Paint loss from the scratch is measured and results are expressed as the amount of creep (in mm) from the scratch. For commercially viable coatings, creep from a scratch of 2 mm or less is desired.
[0096] A dureza de revestimentos curados preparados a partir da composição é testada usando o método de dureza de lápis, como descrito em ASTM D3363 (Método de Teste Padrão para Dureza de Filme pelo Teste do Lápis). Lápis de dureza variável, de 6B (o mais macio) até 6H (o mais duro) são usados. Resultados são reportados em termos do lápis o mais duro que não risca ou marca a superfície. Assim, por exemplo, se um revestimento não rompe com um lápis 2H, mas se rompe quando testado com um lápis 3H, o revestimento é reportado como tendo uma dureza de lápis de 2H.[0096] The hardness of cured coatings prepared from the composition is tested using the pencil hardness method, as described in ASTM D3363 (Standard Test Method for Film Hardness by Pencil Test). Pencils of varying hardness, from 6B (the softest) to 6H (the hardest) are used. Results are reported in terms of the hardest pencil that does not scratch or mark the surface. So, for example, if a coating does not break with a 2H pencil, but breaks when tested with a 3H pencil, the coating is reported as having a 2H pencil hardness.
[0097] O comportamento em intempéries da composição curada é determinado por exposição a luz de arco de xenônio em um medidor de intemperismo (WOM), como descrito em ASTM G155 (Prática Padrão para Operar Aparelho de Luz de Arco de Xenônio Light para Exposição de Materiais não Metálicos). Composições de revestimento são aplicadas a painéis de teste de alumínio e curadas integralmente. Os painéis são então expostos na câmara de teste por 2000 horas. A retenção de brilho a 20 graus é medida periodicamente através de todo o teste, como descrito em ASTM D523-14 (Método Padrão para Brilho Especular). O comportamento em intempéries é reportado como a porcentagem de brilho a 20 graus retido após um dado período de tempo de exposição.[0097] The weathering behavior of the cured composition is determined by exposure to xenon arc light in a weathering meter (WOM), as described in ASTM G155 (Standard Practice for Operating Xenon Arc Light Apparatus Light for Exposure of Non-Metallic Materials). Coating compositions are applied to aluminum test panels and fully cured. The panels are then exposed in the test chamber for 2000 hours. Gloss retention at 20 degrees is measured periodically throughout the test as described in ASTM D523-14 (Standard Method for Specular Gloss). Weathering behavior is reported as the percentage of brightness at 20 degrees retained after a given period of exposure time.
[0098] A fim de determinar o efeito de aceitadores de MA e doadores de MA sobre resposta de cura e resistência à corrosão, formulações de revestimento primário catalisadas 1 e 2 foram preparadas com componentes de resina como indicado na Tabela 1. As quantidades mostradas são porcentagens em peso com base no peso total dos componentes de resina em cada formulação. Além dos componentes de resina listados na Tabela 1, as formulações de revestimento primário 1 e 2 incluem quantidades equivalentes de pigmentos, solventes, promotores de adesão, agentes anti-decantação, tinturas, dispersantes, desespumantes, e/ou outros aditivos convencionalmente usados em formulações de tinta comerciais. As formulações eram preparadas usando equipamento tradicional de confecção de tinta tais como moinhos ou equipamento de mistura a alta velocidade. Tabela 1. Composição de Resina de Revestimento Primário Catalisado [0098] In order to determine the effect of MA acceptors and MA donors on curing response and corrosion resistance, catalyzed primer coating formulations 1 and 2 were prepared with resin components as indicated in Table 1. The amounts shown are weight percentages based on the total weight of the resin components in each formulation. In addition to the resin components listed in Table 1, primer coating formulations 1 and 2 include equivalent amounts of pigments, solvents, adhesion promoters, anti-settling agents, dyes, dispersants, defoamers, and/or other additives conventionally used in formulations. of commercial paint. Formulations were prepared using traditional paint-making equipment such as mills or high-speed mixing equipment. Table 1. Catalyzed Prime Coat Resin Composition
[0099] Para testar para desempenho de cura e resistência à corrosão, as formulações de revestimento primário catalisadas do Exemplo 1 foram aplicadas por pulverização a painéis de teste de metal tratados com fosfato de ferro (ACT B1000 P99X) a uma espessura de filme seco (DFT) de cerca de 38,1 a 50.0 μm. Os painéis de teste eram então colocados em uma estufa por 10 minutos a uma temperatura de cerca de 65,5°C (150°F) Depois dos 10 minutos iniciais de cura, cada painel foi removido da estufa e testado para dureza de lápis. Cada painel foi curado por 20 minutos adicionais a 65,5°C (150°F) e então deixados em pós-cura a temperatura ambiente de 20 a 25°C (68 a 77°F) aproximadamente). Cada painel foi então avaliado para resistência à corrosão em seguida a até 504 horas de exposição a pulverização salina. Resultados são mostrados na Tabela 2, onde “passa” para resposta de cura denota uma dureza de lápis de pelo menos H depois de 10 minutos de cura a 65,5°C (150°F)) e “passa” para pulverização salina denota uma classificação mínima ASTM de 10 para formação de bolha, 9 para ferrugem e menos do que 2 mm de fluência média a partir de risco depois raspar com uma espátula de metal. Tabela 2. Desempenho de Cura e Resistência à Corrosão [0099] To test for curing performance and corrosion resistance, the catalyzed primer coating formulations of Example 1 were spray applied to metal test panels treated with iron phosphate (ACT B1000 P99X) at a dry film thickness ( DFT) from about 38.1 to 50.0 μm. The test panels were then placed in an oven for 10 minutes at a temperature of about 65.5°C (150°F). After the initial 10 minutes of curing, each panel was removed from the oven and tested for pencil hardness. Each panel was cured for an additional 20 minutes at 65.5°C (150°F) and then left to post-cure at room temperature approximately 20 to 25°C (68 to 77°F). Each panel was then evaluated for corrosion resistance following up to 504 hours of salt spray exposure. Results are shown in Table 2, where “pass” for cure response denotes a pencil hardness of at least H after 10 minutes of curing at 65.5°C (150°F)) and “pass” for salt spray denotes a minimum ASTM rating of 10 for blistering, 9 for rust and less than 2 mm average creep from scratch after scraping with a metal putty knife. Table 2. Curing Performance and Corrosion Resistance
[00100] Formulações de revestimento final catalisadas por adição de Michael A a E foram preparadas, cada uma incluindo cerca de 2,8 por cento em peso de epóxi acrilato, com base no peso total de resina componentes. Além do componente de epóxi acrilato, cada revestimento final A-E inclui diferentes níveis de modificadores de cinética, dispersantes e outros aditivos convencionais encontrados em composições de revestimento final.[00100] Michael addition-catalyzed topcoat formulations A to E were prepared, each including about 2.8 weight percent epoxy acrylate, based on the total weight of resin components. In addition to the epoxy acrylate component, each A-E topcoat includes different levels of kinetic modifiers, dispersants, and other conventional additives found in topcoat compositions.
[00101] Para testar o impacto de adicionar epóxi acrilato à formulação de revestimento final, cada formulação de revestimento final foi aplicada sobre a Composição Experimental 2 de revestimento primário catalisado do Exemplo 1 já aplicado por pulverização a painéis de teste de metal tratado com fosfato de ferro (ACT B1000 P99X) e curados por 30 minutos a 65,6°C. Os painéis de teste foram então avaliados para adesão de interrevestimento (isto é, adesão entre revestimento primário e revestimento final). Cada formulação de revestimento final apresentou significante melhoria em adesão interrevestimento em relação às mesmas formulações de revestimento final sem o componente de epóxi acrilato.[00101] To test the impact of adding epoxy acrylate to the topcoat formulation, each topcoat formulation was applied over the catalyzed primer coat Experimental Composition 2 of Example 1 already spray applied to phosphate-treated metal test panels. iron (ACT B1000 P99X) and cured for 30 minutes at 65.6°C. The test panels were then evaluated for intercoat adhesion (i.e., adhesion between primer coat and topcoat). Each topcoat formulation showed significant improvement in intercoat adhesion over the same topcoat formulations without the epoxy acrylate component.
[00102] Para testar o efeito de epóxi acrilato sobre o desempenho de intemperismo do revestimento final, várias formulações de revestimento final catalisado foram preparadas, com cada formulação de revestimento final F a I incluindo diferentes níveis de epóxi acrilato. Cada formulação de revestimento final foi aplicada sobre o revestimento primário catalisado Composição Experimental 2 do Exemplo 1 já aplicado por pulverização a painéis de teste de metal tratado com fosfato de ferro (ACT B1000 P99X) e curado por 30 minutos a 65,5°C. Os painéis de teste foram então avaliados para desempenho de intemperismo medindo brilho a 20 graus a 500, 1000, 1500 e 2000 horas de exposição em um medidor de intemperismo, onde as amostras de teste são expostas a luz de arco de xenônio para simular o efeito de três anos de calor, unidade e luz solar. Resultados são representados como percentagem de retenção brilho a 20 graus depois um de um dado período de exposição e mostrados na Figura 1.[00102] To test the effect of epoxy acrylate on the weathering performance of the top coat, several catalyzed top coat formulations were prepared, with each top coat formulation F to I including different levels of epoxy acrylate. Each topcoat formulation was applied over the Catalyzed Primer Coat Experimental Composition 2 of Example 1 already spray applied to iron phosphate treated metal test panels (ACT B1000 P99X) and cured for 30 minutes at 65.5°C. The test panels were then evaluated for weathering performance by measuring brightness at 20 degrees at 500, 1000, 1500 and 2000 hours of exposure on a weathering meter, where the test samples are exposed to xenon arc light to simulate the effect. of three years of heat, unity and sunlight. Results are represented as percentage of brightness retention at 20 degrees after a given exposure period and shown in Figure 1.
[00103] A descrição completa de todas patentes, pedidos de patente, e publicações e material eletronicamente disponível citados aqui é incorporada por referência. A descrição detalhada e exemplos acima foram dados por clareza de compreensão apenas. Nenhuma limitação desnecessária deve ser inferida a partir disso. A invenção não é limitada aos detalhes exatos mostrados e descritos, pois variações óbvias a um versado na técnica serão incluídas dentro da invenção definida pelas reivindicações. A invenção ilustrativamente descrita aqui apropriadamente pode ser posta em prática, em algumas modalidades, na ausência de qualquer elemento que não é especificamente descrito aqui.[00103] The complete description of all patents, patent applications, and publications and electronically available material cited herein is incorporated by reference. The detailed description and examples above have been given for clarity of understanding only. No unnecessary limitations should be inferred from this. The invention is not limited to the exact details shown and described, as variations obvious to one skilled in the art will be included within the invention defined by the claims. The invention illustratively described herein can be practiced, in some embodiments, in the absence of any element that is not specifically described herein.
Claims (11)