AU773259B2 - A process and an apparatus for producing metals and metal alloys - Google Patents

Description

WO 00/22176 PCT/AU99/00884 1 A PROCESS AND AN APPARATUS FOR PRODUCING METALS AND METAL ALLOYS The present invention relates to a process for producing molten metal (which term includes metal alloys), in particular, although by no means exclusively iron, from a metalliferous feed material, such as ores, partly reduced ores and metal-containing waste streams, in a metallurgical vessel containing a molten bath.

The present invention relates particularly to a process and an apparatus for producing molten metal from a metalliferous feed material which is based on the combination of: a means which partially reduces and at least partially melts the metalliferous feed material; and a means which completes reduction of the molten partially-reduced feed material.

One example of a pre-reduction/melting means is a cyclone converter.

One example of a reduction means is a vessel that contains a molten bath.

US patent 4,849,015 of Fassbinder et al and US patent 5,800,592 of Den Hartog et al disclose particular proposals for producing molten iron from iron ore using the above combination of pre-reduction/melting means and reduction means.

One object of the present invention is to provide 2 an alternative process/apparatus for producing molten iron from iron ore which is based on the above combination of pre-reduction/melting means and reduction means.

According to the present invention there is provided a process for producing metals from a metalliferous feed material which includes the steps of partially reducing and at least partially melting the metalliferous feed material in a pre-reduction/melting means and completely reducing the partially reduced feed material in a reduction means, which reduction means includes a vessel that contains a molten bath having a metal layer and a slag layer on the metal layer, and which process is characterised by: injecting solid carbonaceous material with a carrier gas into a metal rich region of the molten bath; causing upward movement of splashes, droplets, and streams of material from the metal layer which: promotes mixing of material from the metal layer in the slag layer and mixing of material from the slag layer in the metal layer; and (ii) extends into a space above the molten bath to form a transition zone; injecting an oxygen-containing gas into the vessel and post-combusting part of a reaction gas generated in the molten bath; allowing at least part of the reaction gas generated in the molten bath to flow upwardly from the reduction means into the pre- \\me lbfiles \home$\stella\Keep\Speci\TRPL\TPL.PP6471. doc 18/03/04 3 reduction/melting means and partially reduce the metalliferous feed material in the prereduction/melting mean; and injecting an oxygen-containing gas into the pre-reduction/melting means and postcombusting a part of the reaction gas and thereby generating heat which at least partially melts the partially-reduced metalliferous feed material, whereby steps and post-combust the reaction gas generated in the molten bath to a post combustion level of at least The term "metal rich region" is understood herein to mean the region (or regions) of the molten bath that has a high concentration of metal. By way of example, the metal layer is one metal rich region.

The term "metal layer" is understood herein to mean that region of the bath that is predominantly metal.

Specifically, the term covers a region or zone that includes a dispersion of molten slag in a metal continuous volume.

25 The term "slag layer" is understood herein to mean that region of the bath that is predominantly slag.

Specifically, the term covers a region or zone that includes a dispersion of molten metal in a slag continuous volume.

The term "transition zone" is understood herein to mean a gas continuous volume with splashes, droplets, and streams of molten material (which is at least predominantly slag) therein.

35 One option for generating the upward movement of *0 splashes, droplets and streams of molten material from the metal layer in step is to inject the solid carbonaceous \\melbfiles\home$\stella\Keep\Speci\TRPL\TRPL.PP6471.doc 18/03/04 4 material and carrier gas in step via one or more thanone lance/tuyere that extend downwards towards the metal layer.

More preferably the one or more than one lance/tuyere extend through side walls of the vessel and are angled inwardly and downwardly towards the metal layer.

It is preferred that the injection of solid carbonaceous material and carrier gas into the metal layer be sufficient to generate upward movement of splashes, droplets and streams of molten material in a fountain-like manner.

The injection of solid carbonaceous material and carrier gas into the metal layer via the downwardly extending lance(s)/tuyere(s) has the following consequences: the momentum of the solid carbonaceous material/carrier gas causes the solid 20 carbonaceous material and gas to penetrate the metal layer; (ii) the solid carbonaceous material, typically coal, is devolatilised and thereby produces S. 25 gas in the metal layer; (iii)carbon predominantly dissolves into the metal and partially remains as solid; (iv) the gases transported into the metal layer and generated via devolatilisation produce significant buoyancy uplift of material from the metal layer which results in the abovedescribed upward movement of splashes, droplets and streams of material, and these splashes, droplets, and streams entrain further slag as they move through the slag \\me lbfiles\home$ \Ste1a\Keep\Speci\TRPL\TRPL.PP6471.doc 18/03/04 layer.

The material referred to in paragraph includes molten metal (which includes dissolved carbon) and molten slag that is drawn into the metal layer from above the metal layer as a consequence of solid/gas injection.

Another option, although by no means not the only other option, to generate the above-described upward movement of splashes, droplets, and streams of material is to inject solid carbonaceous material and carrier gas via one or more than one tuyere in the bottom of the vessel or in side walls of the vessel that contact the metal layer.

Preferably, the pre-reduction/melting means is positioned above the reduction means and communicates with the reduction means so that at least partially molten, partially reduced metalliferous feed material drains downwardly into the reduction means and, more particularly, 20 drains into the vigorously mixed central region of the slag layer in the molten bath. The applicant believes that this leads to more efficient smelting of the pre-reduced material.

e.oe oooo 25 As indicated above, the upward movement of splashes, droplets and streams of material from the metal layer promotes mixing of material from the metal layer in the slag layer and mixing of material in the slag layer in *"the metal layer. Preferably, the extent of mixing is 30 sufficient so that the slag layer is more or less homogeneous in terms of composition and temperature.

The mixing of material between the layers promotes reduction of metal oxides present in the molten bath by dissolved carbon in metal. In this connection the injection of solid carbonaceous material into the metal layer ensures that there are high levels of dissolved carbon (and possibly \\nelbfiles\home$\stella\Keep\Speci\TRPL\TRPL.PP6471.doc 18/03/04 6 solid carbon) in the metal layer and that, as a consequence, the metal layer is strongly reducing.

It is preferred that the level of dissolved carbon in metal be greater than 3.5 wt%.

Preferably the process includes the step of preheating the metalliferous feed material before supplying the metalliferous feed material into the prereduction/melting means.

Preferably the process includes discharging reaction gas from the pre-reduction/melting means as an offgas and preheating the metalliferous feed material with the off-gas, either hot or cold.

The term "post-combustion" means:

[CO

2

[H

2 0] 20 [C02] [H 2 0] [CO] [H 2 where: [C0 2 volume of CO 2 in the reaction gas; 25 [H 2 0] volume of H 2 0 in the reaction gas; *o*oo go ooo* \\melb_files\home$\stella\Keep\Speci\TRPL\TRPL.PP6471.doc 18/03/04 7 [CO] volume of CO in the reaction gas; and

[H

2 volume of H 2 in the reaction gas.

More particularly, the term "post-combustion" in the context of post-combustion in the vessel also means post-combustion in the absence of any addition of supplementary carbonaceous material for other purposes.

Preferably injection of oxygen-containing gas into the vessel in step is via one or more than one lance/tuyere that extend downwardly and inwardly into the vessel and are set back sufficiently to be clear of material flowing downwardly from the pre-reduction/melting means into the vessel.

The transition zone is important for three reasons.

Firstly, the ascending and thereafter descending splashes, droplets and streams of material are an effective 20 means of transferring to the molten bath the heat generated by post-combustion of reaction gas in the vessel.

Secondly, the material, and particularly the molten slag, in the transition zone is an effective means of S. 25 minimising heat loss by radiation via the side walls of the vessel.

Thirdly, dust containing carbon in the transition zone reduces heat loss by radiation to the side walls of the 30 vessel.

Preferably, the vessel includes: tap holes for discharging molten metal and slag from the vessel; and \\melbfiles\home$\stella\Keep\Speci\TRPL\TRPL.PP6471.doc 18/03/04 8 one or more than one outlet for transferring reaction gas to the pre-reducing/melting means.

It is preferred that the oxygen-containing gas be oxygen.

According to the present invention there is also provided an apparatus for carrying out the above-described process.

More particularly the present invention provides an apparatus for producing metals from a metalliferous feed material which includes: a pre-reduction/melting means which partially reduces and at least partially melts the metalliferous feed material and a reduction means which completely melts and reduces the at least partially molten and partially reduced feed material; which reduction means includes a vessel that contains a molten bath having a metal 20 layer and a slag layer on the metal layer; which prereduction/melting means is positioned directly above the vessel and communicates with the vessel whereby at least partially molten and partially reduced feed material flows downwardly into a central region of the vessel; and which 25 reduction means further includes: one or more than one lance/tuyere which inject solid carbonaceous material with a carrier gas into a metal rich region of the 30 molten bath; one or more than one lance/tuyere which inject oxygen-containing gas into the vessel that post-combusts reaction gas generated in the vessel, the one or more than one lance/tuyere extending downwardly and inwardly into the vessel and being \\melbfiles\homeS\stella\Keep\Speci\TRPL\TRPL.PP6471.doc 18/03/04 9 positioned so as to minimise contact with at least partially molten and partially reduced feed material flowing downwardly from the prereduction/melting means; and one or more than one lance/tuyere which inject oxygen-containing gas into the prereduction/melting means that post-combusts at least a part of the reaction gas from the vessel.

According to the present invention there is also provided a process for producing iron-containing metals from a metalliferous feed material which includes the steps of partially reducing and at least partially melting the metalliferous feed material in a pre-reduction/melting means and completely reducing the partially reduced feed material in a reduction means, which pre-reduction/melting means is 20 positioned directly above the reduction means and communicates with the reduction means so that at least partially molten, partially reduced feed material flows downwardly into a central region of the reduction means, which reduction means includes a vessel that contains a 25 molten bath having a metal layer and a slag layer on the metal layer, and which process further comprises: injecting solid carbonaceous material and *°carrier gas into a metal rich region of the °oooo 30 molten bath via one or more than one lance/tuyere that extend downwardly towards the metal layer, the injection of carbonaceous material and carrier gas causing upward movement of splashes, droplets, and streams of material from the metal layer which: 9a promotes mixing of material from the metal layer in the slag layer and mixing of material from the slag layer in the metal layer; and (ii) extends into a space above the molten bath to form a transition zone; injecting an oxygen-containing gas into the vessel and post-combusting part of a reaction gas generated in the molten bath via one or more than one lance/tuyere extending downwardly and inwardly into the vessel and being positioned so as to minimise contact with at least partially molten and partially reduced feed material flowing downwardly from the pre-reduction/melting means; allowing at least part of the reaction gas generated in the molten bath to flow upwardly from 20 the reduction means into the pre-reduction/melting means and partially reduce the metalliferous feed material in the pre-reduction/melting means; and injecting an oxygen-containing gas into 25 the pre-reduction/melting means and post-conbusting a part of the reaction gas and thereby generating heat which at least partially melts and partially reduces metalliferous feed material and generates the at least partially molten, partially reduced 30 feed material that flows downwardly into the reduction means; and whereby steps and post-combust the reaction gas generated in the molten bath to a post-combustion level of at least The present invention is described further by way 9b of example with reference to the accompanying drawings, of which: Figure 1 is a flowsheet, in largely schematic form, of one preferred embodiment of the process and the apparatus of the present invention; and Figure 2 is a flowsheet, in largely schematic form, of another preferred embodiment of the process and the apparatus of the present invention.

The following description is in the context of producing molten iron from iron ore and it is understood that the present invention is not limited to this application and is applicable to any suitable metalliferous material.

With reference to Figure 1, iron ore is transferred from a series of storage bins 3 into a pre-reduction/melting means that is in the form of a cyclone converter 5 and is 20 partially reduced (by way of example, up to FeO) and at least partially melted in the cyclone converter The cyclone converter 5 is positioned directly ego• *ooo *o oo* WO 00/22176 PCT/AU99/00884 10 above a reduction means that is in the form of: a metallurgical vessel 7 which contains a molten bath 15 having a metal layer and a slag layer and which has a suitable means (not shown) for tapping molten metal and slag and an outlet for reaction gas that opens directly into the cyclone converter and lances/tuyeres 11 for injecting solid carbonaceous material and optionally fluxes into the vessel 7 and lances/tuyeres 13 for injecting oxygen into the vessel 7, which lances/tuyeres 11, 13 extend downwardly and inwardly into the vessel through the side wall of the vessel.

A suitable form of the vessel 7 and the lances/tuyeres 11, 13 and a suitable process for reducing metalliferous feed material in the vessel 7 is described in general terms in International applications PCT/AU99/00537 and PCT/AU99/00538 in the name of the applicant. The disclosure in the patent specifications lodged with these patent applications is incorporated by cross-reference.

The process flowsheet of Figure 1 includes injection of solid material and carrier gas into the metal layer 15 via the lances/tuyeres 11. A particular feature of the preferred process flowsheet is that the injected solid material is confined to solid carbonaceous material (typically coal) and optionally one or more than one slag forming agent (typically lime). The gases that are generated by and transported into the metal layer as a consequence of the injection of solid carbonaceous material and carrier gas into the metal layer produce significant buoyancy uplift of molten metal, solid carbon, and molten WO 00/22176 PCT/AU99/00884 11 slag (drawn into the metal layer as a consequence of solid/gas injection) from the metal layer which generates upward movement of splashes, droplets and streams of molten material and solid carbon, and these splashes, droplets and streams entrain slag as they move through the slag layer.

The buoyancy uplift of molten material and solid carbon causes substantial agitation in the metal layer and the slag layer, with the result that the slag layer expands in volume. The extent of agitation is such that there is strong mixing of material from the metal layer in the slag layer and strong mixing of material from the slag layer in the metal layer.

In addition, the upward movement of splashes, droplets and streams of material caused by the buoyancy uplift of molten metal, solid carbon, and molten slag extends into the gas space above the molten material in the vessel and form a transition zone.

The diameter of the cyclone converter 5 is relatively small compared to that of the vessel 7 and the cyclone converter 5 is positioned centrally above the vessel 7. Accordingly, the at least partially molten, partially-reduced iron ore produced in the cyclone converter 5 flows downwardly into the central region of the molten bath 15 and is completely reduced in the molten bath The mixing of material between the metal layer and the slag layer ensures that complete reduction is achieved effectively and efficiently.

The reactions that occur in the molten bath 15 in the vessel 7 generate reaction gas (such as CO and H 2 and the gas moves upwardly through the vessel 7. Oxygen produced in an oxygen plant 19 is injected into the gas space in the vessel 7 above the molten bath 15 via the lances/tuyeres 13 and post-combusts a part of the reaction WO 00/22176 PCT/AU99/00884 12 gas in the transition zone and other sections of the gas space. The heat is transferred to the ascending and thereafter descending splashes, droplets and streams of material and the heat is then transferred to the metal layer when the metal/slag returns to the metal layer. In order to avoid damage by contact with material flowing downwardly from the cyclone converter 5, the lances/tuyeres are set back to be clear of such downwardly flowing material.

The post-combusted reaction gas produced in the vessel 7 flows upwardly into the cyclone converter 5 and acts as a reducing gas which partially reduces the iron ore supplied to the cyclone converter In addition, oxygen produced in the oxygen plant 19 is injected into the cyclone converter 5 and postcombusts at least part of the reaction gas in the cyclone converter 5 and generates heat that melts the partiallyreduced iron ore.

The combined level of post-combustion in the vessel 7 and the cyclone converter 5 is at least An off-gas discharges from the cyclone converter via a duct 17. The duct 17 includes a water cooling assembly 9 which initially cools the off-gas by means of water panels and thereafter quenches the off-gas and thereby removes entrained solids from the off-gas and reduces the water vapour content of the off-gas.

The quenched off-gas is transferred via a line 27 and is used as a fuel gas or vented flue gas.

The process flowsheet shown in Figure 2 includes all of the components of the flowsheet shown in the figure.

WO 00/22176 PCT/AU99/00884 13 In addition, in the process flowsheet shown in Figure 2 the iron ore is preheated in a preheater assembly 29 prior to supplying the iron ore to the cyclone converter The preheater assembly 29 operates with a part of the fuel gas from the water cooling assembly 9 which is supplied via a line 31. The use of a preheater assembly 29 is an advantage in terms of productivity and operational costs, particularly in situations where the iron ore has high levels of loss of ignition (for example, crystalline water). Moreover, in situations where the iron ore has high levels of loss of ignition, the preheater assembly 29 has the advantage that it minimises thermal decrepitation of iron ore particles when the particles are exposed to high temperatures in the cyclone converter The Table set out below provides heat and mass balance calculations for the process flowsheets of Figures 1 and 2 under the stated operating conditions.

WO 00/22176 PCT/AU99/00884 14 Preeatr asebly(29 'Figure 1 flowsheet. Figure 2 flowsheet Pre-reduction/melting means Fines Feed 261 tph 2 66 tphL 9 25C LA 700C Oxygen I37.1 )Nm3Ih 29.S kXM3/h offgas 2S2k~m3/h 222 kNm3/h La 1800C cmuto Reduction means 11, 13, 15) Feed rate 221 tph 231 tph 9 1600C La 1600C 22% pre-reduction 22% Pre-reduction oxygen 71.1 ]Nm3/h 163.0 )Nm3/b coal 113.0 tph 105.0 tph Flux 7.1 tph -j7.9 tph Offgas 226 )c~m3/h 208 kNm3/h 9 31.S%& post combustion G2 34.9%~ post combustion metal 191 tph 189 tph 9 15O0C 9 iS00C 4.0% carbon 4.0% carbon slag 21 tph 21 tph Off gas from Prereduction/melting means Hood Cooling 132 MW 118. MW Gas ex Scrubber 211 )cNi3/h 88 )c~m3/h q 72% post combustion (9 71%~ post combustion The iron ore was sourced from North America and contained 68.2% iron, 0.6% SiO 2 and 0.95% A1 2 0 3 on a dry basis.

The coal had a heating value of 33.9MJ/kg, an ash content of 5.4% and a volatiles level of 14%. Other characteristics included 90.0% total carbon, 2.0% H 2 0, 1.39%

N

2 3.2% 02 and 4.0% H 2 Many modifications may be made to the preferred embodiments of the process and apparatus of the present invention as described above without departing from the spirit and scope of the present invention.

WO 00/22176 PCT/AU99/00884 15 By way of example, the present invention is not limited to the use of cyclone converters and extends to any suitable pre-reduction/melting means.

Furthermore, whilst the above described embodiments include injecting all of the solid carbonaceous material into the metal layers in the vessels 7, it can readily be appreciated that the present invention extends to embodiments in which part of the solid carbonaceous material is top-charged or otherwise supplied to the vessels 7.

Furthermore, whilst the above described embodiments are confined to injecting carrier gas and solid carbonaceous material and optionally slag forming agents into the metal layer via lances/tuyeres 11, it can readily be appreciated that the present invention extends to embodiments in which other solid materials, such as metalliferous feed material, are injected into the metal layers.

Claims (9)

1. A process for producing metals from a metalliferous feed material which includes the steps of partially reducing and at least partially melting the metalliferous feed material in a pre-reduction/melting means and completely reducing the partially reduced feed material in a reduction means, which pre-reduction/melting means is positioned directly above the reduction means and communicates with the reduction means so that at least partially molten, partially reduced feed material flows downwardly into a central region of the reduction means, which reduction means includes a vessel that contains a molten bath having a metal layer and a slag layer on the metal layer, and which process is characterised by: injecting solid carbonaceous material with a carrier gas into a metal rich region of the molten bath; causing upward movement of splashes, droplets, and streams of material from the metal layer which: promotes mixing of material from the metal layer in the slag layer and mixing of material from the slag layer in the metal layer; and (ii) extends into a space above the molten bath to form a transition zone; injecting an oxygen-containing gas into the vessel and post-combusting part of a reaction gas generated in the molten bath; allowing at least part of the reaction gas ,.,iLiED SHEET, IPEA/AU PCT/AU99/00884 Received 9 March 2000 17 generated in the molten bath to flow upwardly from the reduction means into the pre-reduction/melting means and partially reduce the metalliferous feed material in the pre-reduction/melting means; and injecting an oxygen-containing gas into the pre-reduction/melting means and post- combusting a part of the reaction gas and thereby generating heat which at least partially melts the partially-reduced metalliferous feed material, whereby steps and post-combust the reaction gas generated in the molten bath to a post- combustion level of at least

2. The process defined in claim 1 wherein injection of solid carbonaceous material and carrier gas into the metal rich region of the molten bath in step causes upward movement of splashes, droplets, and streams of material from the metal layer in step

3. The process defined in claim 2 wherein injection of solid carbonaceous material and carrier gas is via one or more than one lance/tuyere that extend downwards towards the metal layer.

4. The process defined in claim 2 or claim 3 wherein injection of solid carbonaceous material and gas is via one or more than one tuyere in the bottom of the vessel or in side walls of the vessel that contact the metal layer.

The process defined in any one of the preceding claims includes the step of preheating the metalliferous feed material before supplying the metalliferous feed material into the pre-reduction/melting means. '~~MoED SHEET 'PEA/AU 18

6. The process defined in claim 5 includes discharging reaction gas from the pre-reduction/melting means as an off- gas and preheating the metalliferous feed material with the off-gas.

7. The process defined in any one of the preceding claims wherein injection of the oxygen-containing gas into the vessel is via one or more than one lance/tuyere that extend downwardly and inwardly into the vessel and are set- back sufficiently to be clear of material flowing downwardly from the pre-reduction/melting means into the vessel.

8. A process for producing iron-containing metals from a metalliferous feed material which includes the steps of 15 partially reducing and at least partially melting the metalliferous feed material in a pre-reduction/melting means and completely reducing the partially reduced feed material in a reduction means, which pre-reduction/melting means is positioned directly above the reduction means and communicates with the reduction means so that at least partially molten, partially reduced feed material flows downwardly into a central region of the reduction means, which reduction means includes a vessel that contains a molten bath having a metal layer and a slag layer on the 25 metal layer, and which process further comprises: injecting solid carbonaceous material and •carrier gas into a metal rich region of the molten bath via one or more than one lance/tuyere that extend downwardly towards the metal layer, the injection of carbonaceous material and carrier gas causing upward movement of splashes, droplets, and streams of material from the metal layer which: promotes mixing of material from the metal Z: \tella\Keep\speci\TRPL\TRPL.PP6471.doc 16/03/04 19 layer in the slag layer and mixing of material from the slag layer in the metal layer; and (ii) extends into a space above the molten bath to form a transition zone; injecting an oxygen-containing gas into the vessel and post-combusting part of a reaction gas generated in the molten bath via one or more than one lance/tuyere extending downwardly and inwardly into the vessel and being positioned so as to minimise contact with at least partially molten and partially reduced feed material flowing 15 downwardly from the pre-reduction/melting means; allowing at least part of the reaction gas generated in the molten bath to flow upwardly from the reduction means into the pre-reduction/melting means and partially reduce the metalliferous feed material in the pre-reduction/melting means; and injecting an oxygen-containing gas into the pre-reduction/melting means and post-conbusting 25 a part of the reaction gas and thereby generating heat which at least partially melts and partially reduces metalliferous feed material and generates i the at least partially molten, partially reduced feed material that flows downwardly into the reduction means; and whereby steps and post-combust the reaction gas generated in the molten bath to a post-combustion level of at least Z: \ete1Ia\Keep\Speci\ThPL\TRPL PP6471.doc 16/03/04 20

9. A process for producing metal from metalliferous feed material substantially as hereinbefore described with reference to the accompanying drawings. Dated this 18th day of March 2004 TECHNOLOGICAL RESOURCES PTY LTD By their Patent Attorneys GRIFFITH HACK Fellows Institute of Patent and Trade Mark Attorneys of Australia H: \stella\Keep\Speci\TRPL\TRPL.PP6471 .doc 18/03/04