AU625059B2 - Graft copolymers and blends thereof with polyolefins - Google Patents

Graft copolymers and blends thereof with polyolefins Download PDF

Info

Publication number
AU625059B2
AU625059B2 AU31716/89A AU3171689A AU625059B2 AU 625059 B2 AU625059 B2 AU 625059B2 AU 31716/89 A AU31716/89 A AU 31716/89A AU 3171689 A AU3171689 A AU 3171689A AU 625059 B2 AU625059 B2 AU 625059B2
Authority
AU
Australia
Prior art keywords
polymer
weight
blend
polyolefin
trunk
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
AU31716/89A
Other versions
AU3171689A (en
Inventor
Newman Bortnick
Roger Kenneth Graham
Casmir Stanislaus Ilenda
William James Work
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rohm and Haas Co
Original Assignee
Rohm and Haas Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US07/315,501 external-priority patent/US4957974A/en
Application filed by Rohm and Haas Co filed Critical Rohm and Haas Co
Publication of AU3171689A publication Critical patent/AU3171689A/en
Application granted granted Critical
Publication of AU625059B2 publication Critical patent/AU625059B2/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Description

625059 COMMONWEALTH OF AUSTRALIA PATENTS ACT 1952 COMPLEE SPECIFCATION NAME ADDRESS OF APPLICANT: Rohm and Haas Company Independence Mall West Philadelphia Pennsylvania 19105 United States of America S NAME(S) OF INVENTOR(S): Casmir Stanislaus ILENDA William James WORK Roger Kenneth GRAHAM Newman BORTNICK ADDRESS FOR SERVICE: DAVIES COLLISON Patent Attorneys 1 Little Collins Street, Melbourne, 3000.
COMPLETE SPECIFICATION FOR THE INVENTION ENTITLED: Graft copolymers and blends thereof with polyolefims The following statement is a full description of this invention, including the best method of performing it known to me/us:la- Field of the Invention This invention is concerned with novel graft copolymers and their production. The copolymers of the invention improve the tensile modulus resistance to sagging of polyolefins with which they are blended without unacceptably increasing melt viscosity.
The graft copolymers of the invention comprise polymerized olefin having grafted thereto, by covalent o* bonding, a polymeric methacrylate chain preferably of relatively high molecular weight. The methacrylate chain -frefrably has a weight average molecular weight (M of at least 20,000 and more advantageously about 30,000 to 150,000.
00 The graft copolymer can be made by introducing a non-polar polyolefin, preferably polypropylene or polyethylene, into an inert hydrocarbon solvent which dissolves (or swells) the polyolefin, by heating to a temperature at which the polyolefin is dissolved. While Sagitating the solution, methyl methacrylate (MMA) monomer, B together with an initiator which generates a constant, low radical flux concentration sufficient to initiate polymerization of the monomer at the temperature of the solution and the formation of the covalent bond, is gradually added. The polyolefin with a side-chain grafted thereto can thereafter be separated from the solvent by volatilizing the solvent, preferably in a devolatilizing
L
.:I
i: i 4 14 'a, 4,00 o 44 0 4 *4 4 4r 2 extruder. The graft polymer can then be blended with a suitable polyolefin such as polypropylene or polyethylene, and extruded into a desired shape.
BACKGROUND OF THE INVENTION Non-polar polyolefins, especially polypropylene and polyethylene and mixtures in various low-density, high-density, and linear low-density form, are major articles of commerce for a wide variety of uses.
Nevertheless, there exist specialty needs for which the marketplace has not provided a satisfactory answer. Among these are to overcome the difficulty of thermoforming and processing of the polyolefin, especially unfilled, in a molten or semi-molten form (substantially above its melting point); the polymer tends to sag readily under its own weight because it exhibits an undesirably low stiffness, and to form shapes of grossly non-uniform thicknesses upon thermoforming. Attempts to correct same by increasing the molecular weight lead to difficulties in processing the higher molecular weight polymer not encountered with the lower molecular weight grades.
For the isotactic polymer of butene-l, known also as polybutylene, the low melting point has made difficult crystallizing of the polymer after processing and obtaining the enhanced performance and handling properties crystallization imparts. Satisfactory nucleators have not appeared in the marketplace.
r
I
i: i i ;i 'i ,1 3- Means have also been sought to improve the toughness or impact strength of polypropylene, for instance. Use of copolymers or ethylene-propylene rubber modified polypropylene has improved toughness, but at the cost of even lower stiffness values, and lower values of heat distortion resistance. It would be desirable to combine impact performance of the copolymers with stiffness and heat distortion behavior of the homopolymer polypropylene resin.
Grafting of monomers capable of vinyl polymerization, such as styrene, methyl methacrylate, and the like, onto S polyolefins such as polyethylene, polypropylene, 4 ethylene-propylene copolymers, and ethylene-propylene-diene terpolymers has been studied almost since the discovery of 44 a, S° routes to practical preparation of such backbones. Grafting onto solid polymer by vapor-phase polymerization, by reaction in an extruder, by peroxidation of the olefinic backbone, and grafting onto pendant double bonds are all routes which have been attempted. There still exists a need for a route which allows for grafts of relatively high molecular weight, with relatively good grafting efficiency i lowered formation of unattached polymer molecules), freedom from gel, and a practical means for preparing and isolating the graft polymer in an efficient and lower-cost manner.
Blends of two or more polymers have often been made, for example in attempts to combine desirable properties of the individual polymers into the blend, to seek unique
Q
L i
I
I :r -i-ii-i~ i 4 0 0* trc 00 0 00O 0 o o 00 4 oa
Q
00 O i 1 it I properties in the blend, or to produce less costly polymer products by including less expensive or scrap polymers in the blend. Compatible polymers tend to form blends that contain small domains of the individual polymers; in the case of "miscible" polymers these occur at the molecular scale, resulting in properties usually considered characteristic of a single polymer. These may include occurrence of a single glass-transition temperature and optical clarity. Such blends are frequently termed "alloys." Compatible polymers that are not strictly miscible, as described above, nevertheless tend to form blends with properties that approach those of the miscible blends. Such properties as tensile strength, which rely upon adhesion of the domains to one another, tend not to be degraded when compatible polymers are blended.
Unfortunately many polymers are poorly compatible with one another. Poor compatibility cannot necessarily be predicted accurately for a given polymer combination, but in general it may be expected when non-polar polymers are blended with more polar polymers. Poor compatibility in a blend is apparent to those skilled in the art, and often evidences itself in poor tensile strength or other physical properties, especially when compared to the component polymers of the blend. Microscopic evidence of poor compatibility may also be present, in the form of large, poorly adhered domains of one or more polymer components in a matrix of another polymer component of the blend. More i t than one glass-transition temperature may be observed, and a blend of otherwise transparent polymers may be opaque because the domain sizes are large enough to scatter visible I light.
Much research has been directed toward finding ways to increase the compatibility of poorly compatible polymers when blended. Approaches that have been used include adding to the blend polymers which show compatibility with the other, mutually incompatible polymers; such added polymers act as a bridge or interface between the incompatible 4 'I
U
components, and often decrease domain size. Chlorinated polyethylene has been used as such an additive polymer, especially in blends of polyolefins with other, poorly S, o compatible polymers.
Graft polymers, as of incompatible polymers A onto B, S are known to aid in blending polymers A and B. Such graft polymers may also serve to aid in blending other incompatible polymers C and D, where A and C are compatible 41 and B and D are compatible.
What has also been difficult to predict in polymer science is the extent to which such a graft polymer will be effective in enhancing desirable properties of the blend over those of the incompatible blend alone. Consequently, those skilled in the art have had to treat each combination of graft polymer and other component polymers of a given blend as a special case, and determine experimentally whether an improvement in such properties as tensile i L ilh~~ 6 strength could be obtained by adding a specific graft polymer to a specific blend.
RELEVANT ART U.S.-A-4,094,927 describes copolymers of higher alkyl r methacrylates with (meth)acrylic acid as melt strength additives, foam stabilizers, and processing aids for polypropylene. Such polymers, however, are not fully compatible with polypropylene and the additive will tend to plate out and foul equipment during such operations as melt S calendering.
U.S.-A-4,409,345 describes polyolefin modified with a 4 0 0 polymerizable unsaturated carboxylic ester in affording improved processing of mixtures of polypropylene, high density polyethylene, and finely divided vegetable fibers.
The patent appears only to demonstrate reinforcement by the fibers which are bonded to the polyolefin by the graft copolymer. All examples are limited to "grafts" of maleic anhydride or acrylic acid, wherein the material grafted is of a molecular weight corresponding to a small number of Smonomer units.
South African Patent 826,440 describes "improved melt viscosity" (higher melt viscosity under low shear conditions while retaining the low melt viscosity at high shear rheology behavior of the unmodified polypropylene) and improved thermoforming characteristics for blends of i 7 polypropylene with certain salts af acid-modified propylene polymers.
U.S.-A-4,370,450 describes modification of polypropylene with polar vinyl monomers by polymerization in aqueous suspension containing a swelling agent at temperatures above 85*C with a radical chain initiator having a half-life of at least 2 hours in the temperature range 80-135"C. The patent does not describe direct solution grafting, stating such yields "only relatively low degrees of grafting". Hydrocarbons are listed as examples S of swelling agents.
U.S.-A-4,161,452 describes only grafts of unsaturated carboxylic acids or anhydrides and esters of (meth)acrylic acid onto ethylene/propylene copolymers in solution in the presence of a free-radical initiator capable of hydrogen abstraction at temperatures between 60 and 220 0 C. An oil o o soluble polymer is required.
o U.S.-A-4,595,726 describes graft copolymers of C2-C alkyl methacrylates onto polypropylene via a solvent-free vapor-phase polymerization wherein the molecular weight of the graft and the number of grafted chains are controlled to yield the desired (although undefined) length and number of chains for utility in adhesive applications between polypropylene and more polar substrates. The patent discloses that similar grafts can be made from methyl methacrylate, but do not exhibit the desired adhesive properties. The patent requires polymerization below the L 'i' -8softening point of polypropylene, which is not defined in their patent, which is known to be lowered by the presence of monomers, and for which no temperature higher than 140°C is exemplified, and in the absence of solvent. There is no indication or suggestion that a relatively high molecular weight chain is covalently grafted to the polyolefin.
Moreover-, the radical flux generated appears to be too high to form a high molecular weight, e.g. greater than 20,000, chain.
U.S.-A-4,692,992 describes grafting at temperatures between 60 and 160'C while maintaining the olefin polymer dissolved in a solvent which is a mixture of a hydrocarbon
III
and a ketonic solvent, the grafted polymer precipitating
A
upon cooling the reacted mixture below 40'C. Reaction conditions for achieving high molecular weight or the advantage in conducting the reaction in the presence only of a solvent of low chain transfer activity are not disclosed.
U.S.-A-3,862,265 only describes melting of polyolefins in an extruder, followed by grafting of unsaturated acids to achieve "improved rheology" as defined in S. Afr. 826440, supra.
U.S.-A-3,886,227 discloses (but does not exemplify for the esters) grafting of unsaturated acids and esters to form a material useful as a modifying agent for polypropylene.
The grafting is conducted in an extruder, and they also disclose that the molecular weight of the backbone polypropylene polymer be lowered by degradation during the 9grafting process, conducted at a temperature above 200"C.
It describes blending with polypropylene and the resulting modification found, such as nucleation, lack of warpage on molding, and the like. Although improvement in heat distortion temperature is noted, there is no disclosure of improved rheological performance at the temperatures required for thermoforming and the like.
Japanese Kokai 59-164347 describes grafts of unsaturated acids or their derivatives (including esters) at very low graft levels (10-5 to 10-8 g equivalents per gram S of polyolefin), blends of the grafts with polyolefins, and 4t00o their use in affecting surface tension in the molten state of the polyolefin while not affecting high-shear viscosity, making the blends useful in, e.g. blow molding of bottles.
Kallitis et al., Eur. Polymer 27, 117 (1987) 4:°o describes ethylene-propylene polymers as nucleating agents 6° 0 for polybutylene. They do not describe or suggest the utility of the polypropylene/methacrylic grafts of this invention.
Reike and Moore, in U.S.-A-2,987,501, disclose grafts of polymers of vinyl monomers onto polyethylene or polypropylene by oxidizing the polyolefin with fuming nitric acid or nitrogen tetroxide, followed by heating the activated polyolefin with the vinyl monomer. The reference exemplifies grafting methyl methacrylate onto polyethylene and polypropylene.
10 Japanese Kokai 223250/87 discloses compatibilizing a polyolefin and a polyamide using a reaction product of an unsaturated carboxylic acid or its derivative grafted onto a mixture of polyolefin and polyamide, that is, the reaction product is formed in the presence of a mixture of two or more polymers. The amount of acid or derivative reacted with the trunk polymers is less than 10%, and it is clear from the only examples present, which utilize unsaturated acids which do not homopolymerize, that what is attached or grafted are low-molecular-weight moieties,. They disclose S reaction conditions, including relatively low levels of a 0 .O unsaturated acid and relatively high levels of peroxide, which would lead one away from achieving the molecular a 0 0°.o weights of the grafted chains disclosed below as part of the present invention. A particular modifier disclosed by this reference, formed by reacting two non-polymerizable acids with a mixture of four trunk polymers, affects the compatibility of the polyamide and polyolefin. However, the comparative data suggest that a reaction of the acids onto polypropylene alone is not an effective compatibilizer for i i S" the two resins, and shows that graft polymers of low levels i of low molecular unsaturated acids or derivatives are not 1 effective in compatibilizing polyamide, with polyolefins.
Japanese Kokai 86040/87 directed to polymer adhesives, discloses an olefin polymer adhesive modified with a carboxylic or carboxylic anhydride group, further reacted 11 with a polyolefin having alcohol functionality, and still further reacted with an aromatic acid halide. bKK Boutevin et al., in Angewandte Makromolekular Chemie, Vol. 162, page 175 (1988), disclose the preparation of a graft polymer of poly(methyl methacrylate) onto a polyethylene trunk by ozonolysis of a low-density polyethylene followed by heating the activated polyethylene in the presence of methyl methacrylate. They disclose grafs of methyl methacrylate having a number-average molecular weight up to 21400, and the use of such grafts as polymeric emulsiliers or compatibilizers for mixtures of low-density .0 polyethylene and poly(vinyl chloride). They report that the compatibilized mixture has a distinct increase in the stress required to break it, and a decrease in the domain sizes in the blend. They also report appreciable degradation of the polyethylene molecular weight when it is ozonized prior to S grafting. This reference does not deal with higher S molecular weights, nor does it provide any indication that the graft polymer might be effective in reducing sag of a polyolefin matrix polymer or otherwise imparting desirable rheological effects to a polymer.
Thus, the art has described means for preparing grafts of methyl methacrylate homo- and copolymer upon polyolefin substrates, but has not produced a graft of the composition provided herein Neither has the art recognized the advantages of the polymerization process herein described for a rapid, efficient production of novel high molecular 12 weight grafts without gel and with ease of product isolation. The art teaches that certain grafts may be blended with polyolefins, but has not recognized the unexpected utility of the novel graft polymers of this invention as having positive effects on both low-shear melt and solid-state properties, especially with little or no effect on the high-shear performance. The art also has not recognized or identified that positive effects on sag resistance may be imparted by graft polymers of this invention.
It is thus an object of this invention to provide an improved process for the manufacture of novel graft polymers of methacrylic esters onto polyolefin substrates. Another object is to provide graft copolymers of at least one chain of methacrylate polymer of relatively high molecular weight, i.e. at least 20,000, onto a polyolefin homo- or copolymer substrate. Yet another object is to provide such graft copolymers which serve as compatibilizing agents for blends of polymers which are otherwise poorly compatible. It is a further object to provide blends of the graft copolymer with a polyolefin matrix which exhibit improved physical S performance in the melt, upon cooling, and in the solid state.
SUMMARY OF THE INVENTION The aforesaid objects and advantages may be accompl'shed by grafting onto a non-polar polyolefin trunk i.s -13in solution, at least one chain which is of a polymer, having a weight average molecular weight greater than about 20,000, present in a weight ratio with the polyolefin of from about 1:9 to 4:1. The graft polymer is derived from at least about 80% of methacrylic ester monomer of the formula CH2
C(CH
3 )COOR, where R may be alkyl (including cycloalkyl) or aryl, both of which may be substituted or unsubstituted, and optionally less than 20%, based on the total monomer weight, of styrenic or other acrylic monomer copolymerizable with the methacrylic ester. This may be accomplished by adding the methacrylate monomer to a solution of the polyolefin together with an initiator which generates a constant, low radical concentration, or radical "flux", at the solution temperature. These radicals initiate polymerization of the monomer and cause formation of a covalent bond with the trunk.
Therefore according to one embodiment of the present invention there is provided a graft copolymer suitable for improving the tensile modulus and sag resistance of a polyolefin when blended therewith, the copolymer comprising: a non-polar polyolefin trunk having a weight average molecular weight of 50,000 to 1,000,000 and comprising units of one or more of ethylene, propylene, butylene and 4-methylpentene, said trunk further S 20 optionally containing a minor amount of units of one or more of the following: 1-alkenes, vinyl esters, vinyl chloride, acrylic and methacrylic acids and esters thereof; and at least one poly(methacrylate) chain, grafted with a covalent bond to said trunk, said chain being present in a weight ratio to said trunk of from 1:9 to 4:1, said chain comprising at least 80% by weight Sunits of methacrylic ester of the formula CH 2
C(CH
3 )COOR, where R is alkyl, aryl, substituted alkyl, substituted aryl, or substituted alkaryl, and optionally up to 20% by weight of units of other monomer comprising styrenic, other acrylic or other monoethylenically unsaturated monomer copolymerizable with the methacrylic ester or, in an amount of up to maleic and/or itaconic acid of anhydride, said chain having a weight average molecular weight of from 20,000 to 920303,tgclet.021,31716-89.ee,1 3
LU
L6_ t T .1 14 200,000.
The resulting copolymer products, hereinafter referred to as "concentrate", may be blended with polyolefin either as a result of the manner by which it is made, or after it is made. It may be extruded into a desired shape either directly, or after pelletization. In either case, the resulting blended product exhibits an attractive combination of tensile modulus and sag resistance and melt viscosity characteristics, as compared with similar ungrafted polymers, viz: polyolefins without a hif'. molecular weight chain or chains covalently bonded thereto.
According to a further embodiment of the present invention there is provided a blend of polyolefin with graft copolymer, for improving the tensile modulus and sag resistance of said polyolefin in the blend, comprising: a non-polar polyolefin trunk comprising units of one or more of ethylene, propylene, butylene, and 4-methylpentene, said trunk further optionally containing a minor amount of units of one or more of the following: 1-alkenes, vinyl esters, vinyl chloride, acrylic and methacrylic acids and esters thereof, said trunk preferably having a weight average molecular weight of 50,000 to 1,000,000; and at least one poly(methacrylate) chain, grafted with a covalent i 20 bond to said trunk said chain being present in a weight ratio to said trunk of from 1:9 to 4:1, said chain comprising at least 80% by weight units of methacrylic ester of the formula CH 2
C(CH
3 )COOR, where R is alkyl, aryl, substituted alkyl, substituted aryl, or substituted alkaryl, and optionally up to 20% by weight of units of other monomer comprising styrenic, other acrylic or other monoethylenically unsaturated monomer copolymerizable with the methacrylic ester or, in an amount of up to maleic and/or itaconic acid of anhydride, said chain having a weight average molecular weight of from 20,000 to 200,000, preferably graft copolymer of any preceding claim; and, optionally, ungrafted methacrylate polymer having a monomer composition and weight-average molecular weight as defined in Claim 1(b).
920303,tgclet021,31716-89.ee,14 i T 14a The concentrate may also be blended with polymers other than polyolefins, and particularly with mixtures of two or more polymers which are poorly compatible with one another, and which may or may not include polyolefins, to improve the compatibility of the resulting mixture.
According to yet another embodiment of the invention there is provided a blend of one or more polar polymers with one or more non-polar polymers including, as a compatibiliser, graft copolymer comprising: a non-polar polyolefin trunk comprising units of one or more of ethylene, propylene, butylene, and 4-methylpentene, said trunk further optionally containing a minor amount of units of one or more of the following: 1-alkenes, vinyl esters, vinyl chloride, acrylic and methacrylic acids and esters thereof, said trunk preferably having a weight average molecular weight of 50,000 to 1,000,000; and at least one poly(methacrylate) chain, grafted with a covalent bond to said trunk said chain being present in a weight ratio to said trunk of from 1:9 to 4:1, said chain comprising at least 80% by weight units of methacrylic ester of the formula CH2 C(CH 3 )COOR, where "o R is alkyl, aryl, substituted alkyl, substituted aryl, or substituted alkaryl, and optionally up to 20% by weight of units of other monomer 20 comprising styrenic, other acrylic or other monoethylenically unsaturated monomer copolymerizable with the methacrylic ester or, in an amount of up to maleic and/or itaconic acid of anhydride, said 0 chain having a weight average molecular weight of from 20,000 to 200,000.
According to yet a further embodiment of the present invention there is provided a process for improving the mutual compatibility of polymers of different polar levels which comprises blending therewith 0.2 to 10% by weight, of the total polymer mixture, of graft polymer comprising: a non-polar polyolefin trunk comprising units of one or more of ethylene, propylene, butylene, and 4-methylpentene, said trunk further optionally containing a minor amount of units of one or more of the following: 1-alkenes, vinyl esters, vinyl chloride, acrylic and methacrylic 920303,tgclet021,31716-89.ee,15
IT-
0 ^iM 14b acids and esters thereof, said trunk preferably having a weight average molecular weight of 50,000 to 1,000,000; and At least one poly(methacrylate) chain, grafted with a covalent bond to said trunk said chain being present in a weight ratio to said trunk of from 1:9 to 4:1, said chain comprising at least 80% by weight units of methacrylic ester of the formula CH, C(CH 3 )COOR, where R is alkyl, aryl, substituted alkyl, substituted aryl, or substituted alkaryl, and optionally up to 20% by weight of units of other monomer comprising styrenic, other acrylic or other monoethylenically unsaturated monomer copolymerizable with the methacrylic ester or, in an amount of up to maleic and/or itaconic acid of anhydride, said chain having a weight average molecular weight of from 20,000 to 200,000.
The invention also is concerned with processes of making the graft polymers of the invention. Briefly, the process according to this invention involves dissolving or swelling the polyolefin in an inert hydrocarbon solvent, and heating to dissolve the polyolefin, i.e. at least to about 140 While agitating the solution, a monomer is introduced, together with an initiator which generates a constant, low radical flux at the temperature of the solution; 20 the radicals initiate polymerization of the monomer and formation of a covalent bond therewith on the polyolefin trunk. The reacted mixture may be allowed to solidify be removal of the solvent. The resultant product, the concentrate, consists of the polyolefin with the chain grafted thereto, unreacted polymer, i.e. polyolefin without the chain, and ungrafted methacrylic ester polymer. It may be pelletized, blended with another polyolefin and extruded into desired shape. Alternatively the reaction mixture may be extruded directly in a devolatilizing extruder to volatilize the solvent and residual monomer, and thereafter blended with a polyolefin and extruded to form article in such form as sheets, tubes and the like.
Therefore according to still another embodiment of the present invention there is provided a process for preparing a graft copolymer comprising the steps of: S 920303,tgclet021,31716-89.ee, 16 d c; 14c introducing inert solvent and non-polar polyolefin comprising units of one or more of propylene, ethylene, butylene,4-methylpentene and, optionally, minor amounts of units of one or more of the following: 1-alkenes, vinyl esters, vinyl chloride, acrylic and methacrylic acids and esters thereof, into a reaction vessel; heating the mixture so formed to a temperature at which the polyolefin dissolves; adding, with agitation, monomer capable of forming a chain as defined in Claim l(b); adding, to the mixture so formed, initiator which produces a low and constant radical flux for a time sufficient to produce methacrylate chain polymer of weight average molecular weight from 20,000 to 200,000 covalently bonded to the polyolefin; and removing the solvent.
,i 1( i 1 920303,gcet021,31716-89.ee,17 15 DETAILED DESCRIPTION In the following, LDPE is low-density polyethylene, usually branched, of density of about 0.91 to about 0.94 g/cc; HDPE is high-density polyethylene of a density above about 0.95 g/cc; LLPDE is linear low-density polyethylene of density about 0.91 to about 0.95 g/cc; EPDM includes rubber terpolymers of ethylene, propylene, and a non-conjugated diene monomer, such as 1,4-hexadiene or ethylidenenorbornene.
The term "polar substrate" or "non-polar" polymer, as used herein, is difficult to define in quantitative terms.
By "non-polar" is meant polymers which are predominantly formed from monomer units of mono- or di-olefins. "Polar", as generally understood in the polymer art, would refer to monomers or polymers which contain an oxygen, nitrogen, or sulfur-containing functionality. Thus, methyl methacrylate, acrylonitrile, and vinyl phenyl sulfone are "polar" monomers, whereas polypropylene is a "non-polar" polymer.
The polymers to be modified in the grafting process A include the non-polar olefin polymers and copolymers.
Included are polypropylene, polyethylene (HDPE, LDPE, and LLDPE), polybutylene, ethylene-propylene copolymers at all ratios of ethylene and propylene, EPDM terpolymers at all ratios of ethylene and propylene and with diene monomer contents up to 10%, poly(l-butene), polymethylpentene, ethylene-vinyl acetate copolymers with vinyl acetate -4.
16contents up to 25%, ethylene-methyl acrylate copolymers, ethylene-methyl methacrylate copolymers, and ethylene-ethyl acrylate copolymers. Also included are mixtures of these polymers in all ratios.
Useable graft copolymers typically include those with weight ratios of polyolefin:acrylic polymer or copolymer that vary from 20:80 to 80:20.
The weight ratio of polar polymers to non-polar polymers in the blend is preferably from 95:5 to 5:95, more preferably from 80:20 to 20:80.
The molecular weight of the olefin polymer which forms the trunk of the graft copolymer should be high enough to give a large amount of non-polar polymer when grafted, but low enough so that most of the graft copolymer has one acrylic polymer chain grafted to each polyolefin truck chain. The molecular weight of the polyolefin trunk is typically in the range of 50,000 to 1,000,000, a preferred range being 100,000 to 400,000. A polyolefin trunk having a molecular weight of about 200,000 800,000 M, is especially preferred, but polyolefins having a molecular weight of about 50,000 200,000 can be used with some beneficial effect. In general, a graft copolymer imparts greater melt-rheology improvement to a high molecular weight polyolefin.
This is especially true when the polyolefin trunk of the graft copolymer is of relatively low molecular weight.
Melt flow rate (mfr) is well known to correlate well with weight average 'molecular weight. The preferred range of mfr values for the polyolefin trunks used in preparing the graft polymers of the invention are from about 20 to i about 0.6 g/10 minutes as measured by ASTM Standard Method D-1238.
I 920303,tgclet021,31716-89.ee,16 17 The preferred monomer is methyl methacrylate. As much as 100% of this, or of other (C 2
-C
4 )-alkyl methacrylates, can be used. Up to 20% by weight of high alkyl, such as dodecyl and the like, aryl, such as phenyl and the like, alkaryl, such as benzyl and the like, and/or cycloalkyl, such as cyclohexyl and the like, methacrylates can be used.
Especially useful chain monomers fall into four categories:
(C
1
-C
4 )-alkyl methacrylates; i (C 5
-C
20 )-alkyl methacrylates; Sii 0- or S- substituted (C 2
-C
20 )-alkyl methacrylates lie iii (C 6
-C
10 )-aryl methacrylates optionally substituted with one or more (C 1
-C
9 )-alkyl groups; 11 ,iv (C 7
-C
12 )-aralkyl methacrylates optionally ring-substituted with one or more
(C
1
-C
9 )alkyl groups; v C 5
-C
8 cycloalkyl methacrylates methacrylic acid, methacrylamide, hydroxyethyl methacrylate, hydroxypropyl methacrylate, alkoxyalkyl acrylates, such as ethoxyethyl methacrylate and'the like, alkylthioalkyl acrylates, such as ethylethioethyl methacrylate and the like, methacrylamide, t-butylaminoethyl il i 18 18 methacrylate, dimethylaminoethyl methacrylate, dimethylaminopropyl methacrylamide, glycidyl methacrylate, methacryloxypropyltriethoxysilane, acrylate monomers (such as ethyl acrylate, butyl acrylate and the like), styrene, acrylonitrile, acrylamide, acrylic acid, acryloxypropionic acid, vinyl pyridine, and N-vinylpyrrolidone.
maleic acid or anhydride, itaconic acid or anhydride.
In its broadest preferred aspect the chain polymer in Sthe graft of the invention may comprise at least 80% by S weight of monomer from categories plus and less than 20% other acrylic or styrenic monomer such as monomer in category or more preferably the amount of category monomer does not exceed 20% of the total plus by weight. Especially preferred chain polymer however comprises at least 80% by weight of monomer from category and less than 20% by weight of monomer from category (b) plus plus Even more preferably, the maximum amount of category monomer is 10% by weight. Most preferably the chain polymer comprises units from category monomer, especially methyl methacrylate.
All the above options are subject to the proviso that the maximum amount of category monomer is 5% by weight of total monomer.
-19- It is important that the chain transfer of the polymerizing chains to its own polymer be minimal relative to transfer with the polyolefin chains for the efficient production of homogenous non-gelled graft polymer in good yield.
The molecular weight of the acrylic graft as measured by the weight average molecular weight of the ungrafted coprepared acrylic polymer may preefraby be about 20,000 to 200,000. The more preferred range is 30,000 to 150,000.
The process of graft polymerizing the monomer leads to the production of ungrafted and grafted material. The amount of grafted material is in the range of 5% to .the total acrylic polymer or copolymer produced. The graft copolymer is prepared in a process that polymerizes the monomer in the presence of the non-polar polyolefin. The process is conducted in a solvent which swells or dissolves the non-polar polymer. The solvent is also one that has no or low chain transfer ability. Examples include nonbranched tLit and branched aliphatic hydrocarbons, chlorobenzene, benzene, It t t-butylbenzene, anisole, cyclohexane, naphthas, and dibutyl ether. Preferably, the solvent is easy to remove by extrusion devolatilization, and therefore has a boiling Spoint below 200*C, preferably below about 150°C. To avoid excessive pressure, a boiling point above about 100°C is also preferred.
The final solids content (which includes polyolefin and acrylic polymer) depends on the viscosity and the ability to mix well. The practical limits are 20% to 70% but the r (I *I L l.
~~oti§1s ciontent can be as high as is consistent with good IIIl.dng for edonlomy. Preferably, the solids content falls in the rangje of about 35% to about gradual addition or multicharge addition of the monmerIs preferred. Optionally, the monomer charge need not be the same throughout, for example, the last 0-20% may contain all of the monomer used in minor amount to concentrate that monomer in one portion of the polymer.
The temperature during the polyrmerization can be in the range 110 to 200"C but the preferred range is 130 to 175*C.
2specially preferred is 145 to 160*C. The pressure can be atmxospheric to superatmospheric, or as high as 2100 kPa or vffiatever is necessiary to keep the reaction mixture in the l iquii phase at the polymerization temperature.
The unreacted monomer concentration should be kept low diinq the reaction. This is controlled by balancing the radical -elu)Z and the monomer feted conditions.
F'or polymerization,, oil-solu~ble thermal I free-radical ill liators, are~ Used. Those that' vork in this process Are -hose vith a one hour half life at anbout 60' to about 2001C.
Th ferdones have a one 'hour half 11ife iLn the range 0 to 170 C. Suitablea free raia ntaosInclude 'ceroxv Thlitiatcos sha's tJutv3. pazlaurvl -i 21 acid, 1-hydroxy-l-hydroperoxydicyclohexyl peroxide, 1,1bis(t-butylperoxy)-3,3,5-trimethylcyclohexane, t-butyl peroxycrotonate, 2,2-bis(t-butylperoxybutane), t-butylperoxy isopropyl carbonate, 2,5-dimethyl-2,5-bis(benzoylperoxy)-hexane, t-butyl peracetate, methyl ethyl ketone peroxide, di-t-butyl diperoxyphthalate, t-butyl perbenzoate, dicumyl peroxide, 2,5,dimethyl-2,5-di(t-butylperoxy)hexane, 2,4-pentanedione peroxide, di-t-butyl peroxide, 2,5,-dimethyl-2,5-di(tbutylperoxy)-hexyne-3, 1,1,3,3-tetramethylbutyl hydroperoxide, cumene hydroperoxide, S, 2,5-dimethyl-2,5-di(hydroperoxy)hexane, t-butyl hydroperoxide, t-butyl cumyl peroxide, p-menthane hydroperoxide and azo-bis-isobutyronitrile.
t'"I The initiator is introduced together with the monomer during the polymerization in a manner to maintain a fairly constant radical flux during most of the polymerization.
This is done to achieve the correct high molecular weight, a high graft efficiency, the desired molecular weight distribution, and freedom from gel.
Radical flux can be defined as the calculated rate of formation of free radicals, expressed in equivalent of radicals per liter per minute. While not being capable of being measured experimentally, this may be calculated from the known rate of decomposition of the free radical initiator present at any time, and its instantaneous concentration. Decomposition rates for initiators are iv 22 determined from published literature, and the concentration is either a known constant, as in continuous feed of initiator, or can be calculated (for a single charge of initiator) from the known decomposition rate constant and the time elapsed since feed.
Good results are achieved when a uniform radical flux is maintained and the radical flux is calculated to be in the range 0.00001 to 0.0005 equivalents of radicals per liter per minute. The preferred range is 0.00002 to 0.0002 equivalents of radicals per liter per minute. The radical flux is dependent on the specific initiator utilized, its ,concentration and rate of decomposition, and the reaction temperature chosen. The rate of decomposition can be found fi in tabulated data, such as in "The Polymer Handbook", 2nd Edition, ed. Brandrup and Iminergut, Wiley and Sons, New York (1975), or provided by the manufacturer. Even if the exact rate constant at the temperature of interest is not known, often activation energies are supplied from which the rate can be calculated. The radical flux is: Radical flux 2 (kd) where kd is that rate constant for decomposition of the particular initiator in units of inverse seconds, and I the S concentration of the initiator in mols/liter. In a batch reaction, I stead.ly decreases from Io, the initial charge, and the radical flux is not constant. When initiator is continuously fed, a calculation must be made to determine the instantaneous concentration of initiator, but the value ;l 23s I ~23 4 4 44
I
is much more constant than in a batch reaction, especially with careful control of initiator feed.
The process may be run in a semi-continuous or continuous manner. Monomer, solvent, and initiator may be added by means similar to those described above. Polymer may be separately dissolved in solvent and added at a rate essentially equivalent to that of product removal, or polymer may be melted and added as a solid to the reaction by means of an extruder.
After the polymerization, a hold time may be used.
Then the mixture is devolatilized to remove solvent and any unreacted monomer. Acceptable devolatilizing devices include a devolatilizing extruder, a rotary film evaporator, or any other convenient stripping device as known in the art. The polymerization reaction mixture may be conveyed to the devolatilization apparatus as a batch or continuously.
Prior to, during, or after the devolatilization step, appropriate additives may be admixed into the graft copolymer solution/suspension which are desired to be present in the isolated graft copolymer. If such additives do not affect the grafting reaction, they may be added prior to, during, or after the polymerization process. Such additives may also be added when the graft copolymer is blended with the matrix polymer. Such additives may include stabilizers against light or heat, such as benzotriazoles, hindered amines, alkyl polysulfides such as dialkyl disulfides, and the like, lubricants, or plasticizers; flame i t
B
B
I
j
I:
i 24 4 4o 4r 4 II 45 4455r St I S 54l retardants; and the like. Preferred is the addition of a disulfide, such as di-n-dodecyl disulfide or di-t-dodecyl disulfide and the like at levels between about 0.001% to about 0.05% by weight based on the weight of graft copolymer plus matrix polymer, to stabilize the acrylic portion of the graft copolymer against thermal degradation during melt processing while admixing into the matrix or blending and extruding.
A second class of stabilizer is the tris(polyalkylhydroxybenzyl)-s-triazinetriones. Preferred is tris-(4-t-butyl-3hydroxy-2,6-dimethylbenzyl)-s-triazine-(lH, 3H, at levels from about 0.001 to about 0.1% by weight, based on the total polymer weight.
Stability may also be imparted to the acrylic portion of the graft copolymer by including an alkylthioalkyl (meth)acrylate, preferably ethylthioethyl methacrylate, with the acrylic monomer or monomers during the graft polymerization.
The product is then isolated by stianding, cooling, chopping, drying, and bagging, or other known collection techniques.
The polyolefin and the graft copolymer concentrate may be blended by mixing the dry feed materials and extruding either directly to form a film, sheet or the like, or by collecting the blend and reprocessing it into the desired S $9 54 I S 4I 94 19 article, or by adding the polyolefin in the course of the devolatilization.
Polyolefins are often produced with one or more stabilizers to prevent degradation of the polymer appearance or physical properties during processing and/or end use.
Such stabilizers may include metal salts such as metal stearates, which act as acid acceptors, hindered phenols, which act as anti-oxidants, and sulfur-containing organic esters or derivatives, added as heat stabilizers. Examples of such additives, which are usually proprietary to the supplier, are metal stearates, 2,6-dimethylphenolic Scompounds, and thiodiesters of long-chain alcohols.
Polyolefins may also contain light stabilizers, such as 4 hindered amines, benzotriazoles, and the like. All of the polyolefins used in the present examples are thought to contain small amounts of these proprietary stabilizers.
One way to specify the preferred blend composition is that at least about 0.2% of the total formulation (polyolefin plus graft copolymer) should be graft polymer or copolymer of the invention. The preferred maximum amount is about 10% graft polymer, with up to about 5% graft polymer being more preferred for cost optimization and optimization of most properties of the blend.
Optionally, the blend of concentrate and polyolefin may be further modified by the introduction of fillers, both inorganic and organic, fibers, impact modifiers, colorants, stabilizers, flame retardants, and/or blowing agents.
-26- Blowing agents may be gases, such as nitrogen or carbon dioxide, admixed with the polymer melt in the extruder and allowed to expand upon extrusion. More often, blowing agents are solids which liberate gases, usually nitrogen, at a specific melt temperature, and which are mixed into the melt, or blended from a pre-compounded mixture dispersed in a polymeric matrix. The melt temperatures for the polyolefins are typically in the range of about 200 to about 230*C, although other temperatures may be used, depending on the specific blowing agent. Solid blowing agents include azo compounds such as azodicarbonamides, o azoisobutyronitriles, hydroazo compounds, or compounds Scontaining the nitroso group.
o The blend of the graft copolymer and polyolefin is useful in thermoforming, film making (especially blowing and extruding), blow molding, fiber spinning, acid and basic dyeing, foaming, extrusion (sheet, pipe, and profile), coextrusion (multilayer film, sheet, preforms, and parisons, 0 with or without the use of tie layers), hot melt adhesives, S .o calendering, and extrusion coating (for the preparation of polymer/fabric, carpet, foil, and other multilayer constructions). Such graft copolymers, especially with small amounts of copolymerized acid functionality, are useful when blended with polyolefins for improved printability. The grafts themselves may be used as tie layers between otherwise incompatible polymers.
L il 27 In extrusion, the graft copolymer is useful, especially with LLDPE, at reduction of melt fracture without an effect on the melt flow rate. Unlike the additives of U.S.-A-4,094,297, the present additives do not plate out p when the modified polyolefin is extruded for extended times.
When polypropylene is modified with the graft copolymers of the present invention, it may be employed in tne manufacture of many useful objects, such as extrusionor injection-blown bottles for packaging of foodstuffs, aqueous solutions such as intravenous feeds or hot-filled items such as ketchup, or extruded articles in profile form 1 such as clips, scrapers, window and door casings and the r 4r like. The foamed articles may be used as substitutes for wood in moldings, for packaging materials, for insulation or sound-deadening materials, for food containers, and other rigid-article applications. Films may be used in many protective or wrapping applications, such as for food packaging, blister packaging of consumer goods, and the like.
The graft copolymers of the present invention are useful in preparing polyolefin fibers, especially polypropylene fibers; they are especially useful when the graft copolymer is formed from a polypropylene trunk.
Polypropylene is relatively easy to process into fibers having high strength and toughness.
Polypropylene fibers show certain deficiencies which include difficulty in dyeing and poor long-term dimensional -28 stability. Grafts containing functional sites capable of accepting dye may be prepared by the present process by incorporating low levels of dye-accepting monomers, such as methacrylic acid, dimethylaminoethyl methacrylate, Nvinylpyridine, and the like. The improved sag resistance noted for the present graft polymers in a polypropylene matrix should correspond to improvements in creep resistance of the fiber.
The tensile modules and/or sag resistance of a polyolefin can be improved by blending a concentrate according to the invention therewith.
Typically the amounts of the ingredients used are such as to yield a product having a weight ratio of at least 80 parts of polyolefin to 20 parts of graft copolymer.
Polypropylene may be formed into fibers by slitting tape from extruded film to form large-denier, coarse fibers, by extruding monofilaments into largedenier fibers with a controlled cross-sectional size, or by extruding multifilaments through a spinnerette to produce bundles of small-denier fibers.
In all cases, the fibers may be draw-textured. As an example, small-denier polypropylene fiber bundles may be extruded from a 25.4-mm, single-screw extruder having a screw length-to-diameter ratio of 24:1, such as that supplied by Killion extruders of Cedar Grove, new Jersey and equipped with a static i 20 mixer, metering pump and spinnerette assembly with multiple orifices. Using such equipment the extruded polypropylene would be passed through a cooling bath and then over a series of godets (metal rolls with heating or coooling Scapability) to orient the polymer or quench existing orientation.
:Polypropylene fibers may be used for, among other things, strapping, netting (including fish nets), slit tape, rope, twine, bags, carpet backing foamed Sribbon, 2 i 1 i t 9 920303,tgclet021,31716-89.ee,28
I
-29upholstery, rugs, pond liners, awnings, swimming-pool covers, tarpaulins, lawn-furniture webbing, shades, bristles, sutures, cigarette filters, nonwoven fabrics, such as for tea bags, bed sheets, bandages, diaper liners and the like, and for doll hair, apparel and the like.
The graft copolymer of the present invention may also be used to improve the compatibility of polymers in blends where they would otherwise be poorly compatible. The graft copolymer is incorporated into such blends, preferably at levels of from about 0.2 to about 10%, preferably from about to about 5% and more preferably from about 0.8 to about to achieve the desired improvement in compatibility.
Higher levels of the graft copolymer may be used, but increases above the preferred level generally show only small improvements in compatibility.
As noted above, compatibility is not easily predicted.
As a general rule non-polar polymers are poorly compatible with more polar polymers, but poorly compatible blends may also be found experimentally among polar-polar or non-polar-non-polar blends. Examples of the non-polar polymers are olefinic polymers such as high- and low-density polyethylene and linear low-density polyethylene, polypropylene including atactic polypropylene, poly-l-butene, poly-iso-butylene, ethylene-propylene rubber, ethylene-acrylic acid copolymer, ethylene-propylene-diene terpolymer rubber, ethylene-vinyl acetate copolymer, poly (ethylene-propylene), polymethylpentenes, and ionomers such 30 as polymers of ethylene with metal-salt-neutralized acrylic acid.
Relatively more polar polymers, called polar polymers for the purposes of this disclosure, include acrylonitrile-butadiene-styrene polymer, acetal polymers, polyarylates, acrylic-styrene copolymers, acrylonitrile-styrene-acrylic polymers, acrylonitrile-styrene polymers modified with ethylene-propylene rubber, cellulosics, polyester-polyether block copolymers, polyesters such as polybutylene terephthalate and polyethylene terephthalate, and including liquid-crystal polyesters, polyetheramides, polyetheretherketones, polyetherimides, polyethersulfones, ethylene-vinyl alcohol copolymers, polyvinyl chloride, tit chlorinated polyvinyl chloride, polyvinylidene chloride and fluoride, styrene polymers such as polystyrene, high-impact polystyrene, styrene-acrylonitrile copolymers, styrene-butadiene copolymers, styrene-maleic anhydride copolymers, alkyl substituted styrene copolymer used with styrene alone or with the additional monomers listed for styrene, polyphenylene ether, polyphenylene sulfide, polysulfone, polyurethane, polyamides, nylons such as nylon 6, nylon 6.6, nylon 6.9, nylon 6.10, nylon 6.12, nylon 11, nylon 12, amorphous nylons, polyamideimide, polycaprolactone, polyglutarimide, polymethyl methacrylate other poly((C 1
-C
8 )-alkyl(meth)acrylates). The acrylic polymers referred to above of particular interest are 1' (1 4 4
L
i j jj i, 31 polymers containing at least 50 weight percent, and preferably at least 80 weight percent, of mers of acrylic acid and/or methacrylic acid (referred to collectively as (meth)acrylic acid) or their esters, preferably their alkyl esters and more preferably their alkyl esters in which the alkyl group contains from one to eight, preferably one to four, carbon atoms. The remaining mers are those from one or more monomers copolymerizable with the (meth)acrylic acid or ester by free-radical polymerization, preferably vinylaromatic monomers, vinyl esters or vinyl nitriles, and more preferably mers of styrene or acrylonitrile.
Polar/non-polar combinations which are of particular S interest in compatibilising using the graft polymers of the \invention include ethylene-vinylacetate polymer and I poly(vinyl chloride) and/or acrylic polymer; (b) ethylene-propylene-nonconjugated diene terpolymer and acrylic polymer and/or polyester, especially poly(ethylene terephthalate), and/or poly(vinyl chloride) and/or SI polycarbonate and/or polycarbonate/polyester blend; (c) high density polyethylene and ethylene/vinyl alcohol polymer and/or polyester, especially poly(ethylene terephthalate) and/or poly(vinyl chloride) aiid/or poly(vinylidene chloride).
In the Examples which 'follow, polymer concentrates and polymer blends were tested using standard procedures which are summarized below.
I 32
U
S 1 t a 0 40 o ooo 044, 0 4 *0 04 4, 4 0 4 44 Unreacted monomer in the reaction mixture prior to solvent removal or subsequent to extruder devolatilization was determined using a gas chromatographic technique.
The collected volatiles were analyzed by gas chromatography on a 25 meter CP wax 57 CB wall coated open tubular fused silica column at 40*C. A comparison of the major signals for the solvent with the MMA signal was used to determine the amount of residual monomer in the reactor and therefore give a measure of conversion immediately. A more accurate measure of conversion was obtained by a C,H,O analysis of the graft copolymer. The carbon content was used to calculate EPDM or polypropylene content by interpolating between the carbon content of EPDM (85.49%) or polypropylene (85.87%) and acrylic polymer The graft copolymers are analyzed by solvent extraction to remove the ungrafted (meth)acrylic portion, whose molecular weight is then determined by GPC techniques. A technique for separating the graft copolymer from ungrafted polyolefin is not available. For concentrates, 0.8-1.3 g of polymer was placed in a centrifuge tube with 17 cm 3 of xylene. The tube was shaken overnight. Then the tube was placed in an oil bath set at 138*C. The tubes were periodically taken from the bath and shaken until all polymer had dissolved. The fact that all dissolved indicates that no crosslinking occurred. The tubes were cooled during which time the polypropylene containing substances precipitate. Then the tubes were centrifuged at 51 -r i
C
I:
i ji ;i i 1-B~ -33- 15,000 rpm for 2 hours and the xylene solution was removed with care not to remove any floats. The molecular weight of the acrylic polymer extracted by the xylene was determined by gel permeation chromatography. The procedure was repeated on the resulting plug to extract additional (meth)acrylate. The value labelled graft is the portion of the (meth)acrylic polymer formed which remains with the polyolefin plug after repeated extraction. The composition is determined from the carbon analysis of this plug.
The polypropylene concentrate and any additives were blended in the melt on a 7.6 cm by 17.8 cm electric mill with a minimum gap of 3.8 mm set at 190°C. Once the S,,material had fluxed, it was mixed an additional 3 minutes.
no Higher temperatures were used for higher viscosity materials (for example, mfr=0.5-2 material was done at 195-210"C).
SWhile still hot, the material was either compression molded or cut into small chunks (about 1-2 cm in each dimension) for granulation (5 mm screen). It is of interest that the o additives of the present invention contribute to easy release from hot metal surfaces, such as mill rolls, Haake Rheocord bowls, etc.
Milling of polyethylene was done in a similar manner S. except that the HDPE blends were milled at 200"C and the LLDPE blends were milled at 170*C.
A 2.5 cm Killion extruder was used for extrusion blending. A two stage screw was used at 150 rpm, with all three zones set for 190*C. The one-strand die was also set if h 34 at the same temperature. A vacuum vent was used. The strand was cooled in water and pelletized. The extrusion rate was 4.5 kg per hour.
Melt blending in a Haake Rheocord (a batch melt mixer) was done on 50 g samples at 190°C or at 210°C and 100 rpm in air. Mixing was continued for three minutes after peak torque was reached. Sample size was 50 grams.
The polyolefin blends were compression molded in an electrically heated Carver press 15 x 15 cm or Farrel press 30.5 x 30.5 cm. The samples were molded between aluminum plates with an appropriate spacer to provide the required thickness 0.25-3.8 mm. In one method the hot melt was taken directly from the mill roll and placed between two aluminum sheets. This was then placed in the press set at 190'C and pressed at high pressure (68-91 metric tonnes for the Farrel press and 6820 kg for the Carver press). After three minutes the mold was placed in an unheated press at high pressure for three minutes. In the other procedure, granulated material or pellets produced from an extrusion, Haake, or milling operation were dried and then compression molded. The procedure used was the same as for molding a melt except that a 5 minute preheat was used while maintaining a slight pressure on the press. This was followed by the high pressure molding in the hot and cold presses. A hot press of 190'C was usually sufficient for mfr=4 polypropylenes, but higher viscosity polypropylenes
V
35 would split during sag testing unless higher molding temperatures were used (195-210°C).
Polyethylene was molded in a similar manner except that HDPE was molded at 170°C and LLDPE at 150°C.
Injection molding of polypropylene was performed on a Newbury injection molding machine in an ASTM family mold.
Material to be molded was dried for 16 hours at 60°C. The first barrel zone was set for 204°C, and the other two barrel zones and the nozzle were set for 218°C. The ram time was set for 3 seconds and the cycle of 15 seconds for injection and 45 seconds overall was used. The injection S0,* pressure was 2100 kPa and the back pressure was 690 kPa.
SThe screw speed was 100 rpm. Both mold platens were set for The sag tests are performed on a compression molded sheet 10 x 10 x 0.15 cm. This sheet was clamped in a frame with a 7.6-cm-square opening. There were metal rulers attached to the front and back of the frame for use in 1 .A measuring sag. The frame and sheet were placed in a hot, 4" forced air oven (typically at 190°C). The amount of sag of the center of the sheet was then recorded as a function of time. Typically, the sag was first recorded at 2.5 cm but i for slow sagging materials sags as low as 16 mm were
S
recorded. Data was recorded up to 10.2 cm of sag or for minutes, whichever occurred first.
The term "slope" refers to the slope of a plot of the natural logarithm of the sag in centimeters vs time, d -36 i p 44
I'
1(4444 4 4 4 4 .4 4 resulting in a straight line. A high slope indicates that the material sags quickly while a low slope indicates that it sags slowly. The advantage of comparing slopes in this manner is that it eliminates any differences in oven cooling when the sample is introduced (due to differences in the time the oven is open, room temperatures, etc.).
Crude thermoforming was done in the laboratory to illustrate this melt strength effect. A sheet of polypropylene or modified polypropylene was heated in a forced air oven at 190"C, removed from the oven, placed over a female mold, and subjected to vacuum.
The capillary flow data were measured on a Sieglaff McKelvey rheometer. The flows were recorded at ten shear rates (1 to 100-reciprocal seconds) at each temperature.
The data was fit to the power law, i.e., viscosity=k(temperature) (shear rate) y and the values at 1 and 1000 reciprocal seconds were calculated from this best fit equation. The parallel plate viscosity refers to measurements on the Rheometrics Dynamic Spectrometer, recorded at a strain of Differential scanning calorimeter (DSC) measurements of melting and nucleation were performed on a duPont instrument. A value of 59 cal/g was used for the heat of crystallization and per cent crystallinity was corrected for the presence of the melt additive. The nucleation temperature was measured in an experiment in which the polypropylene was melted at 200"C for 2 minutes and then 1 S- 7 cooled at 10C/min. The temperature at which peak crystallization occurred is called the nucleation temperature. The isothermal crystallization time was recorded by cooling the molten polypropylene quickly to 127"C and the exotherm rp -rded with time.
SThe physical properties of the polypropylene homopolymer and "medium impact" copolymer are determined on extruded and injection molded samples, although similar results have been observed in milled and compression molded samples. In certain Examples below are described specialized eqipment for preparing foamed sheet, rod or profile, extruded rod or tubing, fibers, cast film, monoaxially .oriented and biaxially oriented film, and injection blow-molded bottles or hollow containers.
The Examples illustrate the present invention in more detail but do not limit it. All percentages are by weight unless otherwise specified and all reagents are of good commercial quality unless otherwise specified.
Ii i f- -4 38 EXAMPLE 1 This example illustrates preparation of a Graft Copolymer (GCP) of Polypropylene Methyl Methacrylate (MMA) and Ethyl Acrylate (EA).
A polypropylene-acryiic graft copolymer is made by polymerizing a ethyl acrylate (EA) 95% methyl methacrylate (MMA) monomer mixture in the presence of polypropylene (weight ratio of polypropylene:monomer 0.67:1). Radicals are generated from ditertiary-butyl peroxide (DTBPO) at the rate of 0.00010 moles per liter per minute (radical flux). Monomer and initiator are fed over 60 minutes and the theoretical (100% conversion) solids at the end of the reaction is A 6.6 liter reactor equipped with a double helical agitator (115 rpm) was charged with 1780 g of an inert hydrocabon solvent mixture of 2-methylalkanes having 6-12 C-atoms and 880 g polypropylene (mfr=4) and heated to 175°C. After 2 hour,,, the temperature was decreased to 155°C and the batch was stirred for 1 additional hour. Over a two minute period two solutions were added. The first consisted of 1.04 g of di-tbutyl peroxide in 21 g of the hydrocarbon solvent. The second consisted of 0.06 g of di-t-butyl peroxide in 2.1 g of ethyl acrylate and 42 g of methyl methacrylate. For the next 58 minutes at the same feed rate a feed of 1.87 g of di-t-butyl peroxide and 62 g of ethyl acrylate in 1215 g of methyl methacrylate was added at the same feed rate as the second feed. This feed schedule results in a radical flux of 0.00010 during the feed time.
After the feed was complete the reaction was held at 1550C for an additional 15 minutes. Then it was devolatilized by passing through a mm Werner-Pfleiderer extruder with two vacuum vents at 200-2500C.
The concentrate product (concentrate) is a mixture wherein the elemental analysis showed that the composition is 56% (meth)acrylate. Extractive results showed 15.9% of the polymerized (meth)acrylic monomers were grafted, and the Mw of the (meth)acrylic polymer was 91,300. The 39 concentrate may be blended with other thermoplastic polymers such as polypropylene.
The following Table shows the efficiency of the above concentrate blended at different levels in-improving sag resistance of a polypropylene homopolymer having a melt flow rate (mfr=4) of four.
TABLE I Wt. of sag sample sag at concentrate siope, thickness 17 min time to in blend min-I (mm) (cm) sag 2.5 cm 0 0.18 1.75 22.- min 0.12 1.45 6.10 2.5 0.12 1.70 4.57 6.8 3.3 0.06 1.78 3.05 11.4 0.045 1.73 1.27 13.1 0.030 1.75 1.02 EXAMPLES 2 51 A polypropylene-acrylic graft copolymer is made by. polymerizing a ethyl acrylate (EA) 95% methyl methacrylate (MMA) monomer mixture in the presence of polypropylene (weight ratio of Spolypropylene:monomer 0.67:1). Radicals were generated from di-tertiary-butyl peroxide (DTBPO) at the rate of 0.00010 moles per liter per minute (radical flux). Monomer and initiator were fed over minutes and the theoretical (100% conversion) solids at the end of the reaction was 52.50%.
A 6.6 liter reactor equipped with a pitched-blade turbine agitator (375 rpm) was charged with 1880 g hydrocarbon solvent and 840 g KNT 0 I"v 40 polypropylene and heated to 155°C. The mixture was stirred for 3 hours. Over a two minute period two solutions were added. The first consisted of 1.06 g of di-t-butyl peroxide in 21 g of hydrocarbon solvent, as in Example 1. The second consisted of 0.06 g of di-t-butyl peroxide in 2.1 g of ethyl acrylate and 40 g of methyl methacrylate. For the next S58 minutes a feed of 1.87 g of di-t-butyl peroxide and 61 g of ethyl acrylate in 1157 g of methyl methacrylate was added at the same feed rate as the second feed. This feed schedule should produce a radical flux of 0.00010 during the feed time. After the feed was complete, the reaction was held at 170°C for an additional 15 minutes. Then it was devolatilized by passing through a 30-mm Werner-Pfleiderer extruder with vacuum vents at 200-250°C. The concentrate showed that the composition is 51% acrylate.
Additional polypropylene-acrylic graft copolymers (Examples 2- I f S51) were prepared by the procedure of this Example and evaluated as 3.5% blends in polypropylene (mfr=4) as melt strength additives. The following Table illustrates the polymerization conditions for the concentrate and the percent acrylic polymer present in the concentrate with the sag resistance of the blend with the polypropylene.
In the following Table II, DTBPO is di(t-butyl)peroxide, TBPB is tbutyl perbenzoate, and DDBH is 2,5-dimethyl-2,5-di(tbutylperoxy)hexane.
1 41 TABLE 1 sag slope Ex fL~nl 1 acrylic in cong in itfeed solids polymer time, temnQ2C min
%EA
in
MMA
IC
I 0 Gale
I
0
C
4~* I I I, If I S I I lIlt
'I
II
I I CI Con* 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 0.15-0.18 0.03-0.05 0.06 0.06 0.045 0.08 0.05 0.10 0.06 0.06 0.11 0.056 0.07 0.11 0.10 0.09 0.12 0.13 0.06 0.06 0.10 0.14 0.13 0.15 0.15 56 51 52 55 57 57 49 53 55 53 48 51 58 57 56 54 55 55 49 51 57 51.
55 56
DTBPO
DTBPO
DTBPO
DTBPO
DTBPO
DTBPO
DTBPO
DTBPO
DTBPO
DTBPO
DTBPO
DTBPO
DTBPO
TBPB
TBPB
TBPB
TB PB
DTBPO
TBPB
TBPB
TBPB
TBPB
TBPB
DDBH
55 52.5 55 55 55 57 55 55 55 55 55 50 55 55 55 55 55 55 55 55 56 55 55 55 155 155 155 150 145 150 150 150 150 150 155 1 50 145 145 150 150 150 150 150 150 150 150 150 150 60 60 60 60 60 60 60 60 60 60 60 60 120 120 120 120 120 120 60 120 120 60 120 120 0.00010 0.00010 0.00010 0.00010 0.00010 0.00010 0.00007 0.00015 0.00010 0.00010 0.00010 0.00010 0.00007 0.00007 0.00010 0.00007 0.00015 0.00007 0.00010 0.00010 0.00010 0.00010 0.00010 0.0001 r #1 0' I I
CC
CC 0 0 0 -42 TABLE 11 (continued)~ sag %feed rad- %EA slope acrylic init- solids polymer time, ical in Ex. n- in conc itg. r 2L ep min flux MMA 0.14 57 TBPB 55 150 120 0.00015 26 0.09 51 TBPB 55 150 60 0.00010 27 0.15 54 DDBH 55 150 120 0.00010 0 28 0.11 51 DDBH 55 155 120 0.00010 29 0.10 53 DTBPO 50 150 120 0.00007 30 14 s 0.10 54 DTBPO 50 150 120 0.00005 04., 31 0.15 53 DTBPO 50 150 120 0.00005 32 0.10 51 OTEPO 55 150 120 0.00007 33 0.12 55 TBPB 55 150 120 0.00007 34 0.18 55 DOSH 55 150 120 0.00007 0.07 53 DTBPO 55 150 120 0.00005 36 0.09 51 DTBPO 55 150 120 0.00010 37 0.14 51 TBPB 55 150 120 0.00005 38 0.10 37 DTBPO 55 155 60 0.00010 39 0.11 43 DTBPO 55 155 120 0.00007 0.08 48 DTBPO 55 155 120 0.00005 *41 0.10 47 DTBPO 55 155 120 0.00007 42 0.07 48 DTBPO 55 155 60 0.00010 43 0.10 43 DTBPO 55 155 120 0.00005 44 0.10 50 DTBPO 55 155 120, 0.00007 0.10 54 DTBPQ 55 150 120 0.00010 *46 0.10 54 DTBPO 55 150 120 0.00007 47 0.07 54 DTBPO 55 150 120 0.00005 48 0.08 56 DTBPO 55 150 120 0.00007 49 0.08 55 DTBPO 55 145 120 0.00007 TABLE 11 (continued) i L-43- 43 sag slope Ex min-1 acrylic initin conc Ltr feed solids polymer time, tem min radical flux
%EA
in
MMA
0.09 56 51 0.08 55 Control PP with no concentrate
DTBPO
DTBPO
120 0.00005 120 0.00010 The calculated percent of grafted acrylic polymer and the molecular weight (Mw) of ungrafted acrylic material are tabulated below in Table III on certain samples where the ungrafted acrylic polymer was separated from the concentrate by extraction.
I
4 *r 4 4044 4II riir I It 1.4r TABLE III Example Acrylic Polymer Grafted to PP 2 12.3 10.6 11 29.8 14.8 46 10.7 47 21.7 Note: (Mw weight average molecular weight) 107,000 119,000 71,800 43,000 62,600 87,300 f EXAMPLE 52 54 This example shows a larger scale preparation of a polypropyleneacrylic graft copolymer made by polymerizing a 5% ethyl acrylate (EA) methyl methacrylate (MMA) monomer mixture in the presence of polypropylene (weight ratio of polypropylene:monomer 0.67:1). Radicals were generated 44 from di-tertiary-butyl peroxide (DTBPO) at the rate of 0.000065 moles per liter per minute (radical flux). Monomer and initiator were fed over 122 minutes and the theoretical (100% conversion) solids at the end of the reaction was 47%.
A 380 liter reactor equipped with a back-slope turbine agitator was charged with 102.3 kg of the hydrocarbon solvent and 36.4 kg of mfr=4 polypropylene homopolymer and heated to 150 0 C over 4 hours. Two solutions were added over a twenty minute period. The first consisted of 82 g of di-tertiarybutyl peroxide in 826 g of the hydrocarbon solvent. The second consisted of 454 g of EA and 8.6 kg of MMA. Addition of the first solution was then continued at a lower rate to feed an additional 82 g of di-tertiary-butyl peroxide and 826 g of the hydrocarbon solvent over 90 minutes. At the same time the monomer addition of 2.3 kg of EA and 47.5 kg of MMA was continued over 102 minutes (ending 12 minutes after the initiator feed had finished). The reaction was held at 150 0 C for an additional 15 minutes. Then an additional 23 kg of hydrocarbon solvent was pumped in over 30 minutes.' The reaction mixture was then devolatilized by passing through a 20-mm Welding Engineers twin-screw extruder at 200 rpm and 200-250°C over 14 hours. This concentrate is Ex. 52.
Similar preparations labelled 53 and 54 were synthesized with changes in feed time and radical flux as indicated. The following Table IV shows the improvement in sag resistance when concentrates of Example 52, 53 and 54 are blended with polypropylene of mfr=4: *f *4 I I 45 TABLE !V Conc in Ex. BJlnd Con. none 52 2.5 53 3.5 54 3.5 Sag Slope min-1 0.19 0.11 0.10 0.11 0.10 0.15 0.09 Weight Fraction Acrylic in conc.
Initiafor Polymer Feed Rad.
Solids temo Time Flux DTBPO 47 DTBPO 45 DTBPO 49 122 0.000065 90 0.00007 78 0.00008 9r 9 19 91 9) 4 *949( 9 99 4 9 LI 9! t I 9* 9t 9 9 19 EXAMPLE This example and Table V demonstrate the unexpected advantage of the concentrate of Example 4 in the improvement of sag resistance for both high density polyethylene (HDPE) and linear low density polyethylene (LLDPE). Data for HDPE are for polymers of two different mfr values (4 and 8) and are obtained at 1500C, The LLDPE values are on a single resin having a density of 0.917 g/cc, but at two different temperatures. Comparison molded polyethylene samples prepared for this test had a significant increase in gloss over the unmodified control.
4
L
I.
46 :i 1 46 TABLE V Time to Sag, Minutes Temp °C 5-.?mm 7A.2 mm Polyethylene HDPE, mfr=8 HDPE, mfr=4 LLDPE, mfr=2 LLDPE, mfr=2 Wt-% Additive 8.7 10.2 15.8 31.4 8.0 10.5 26.0 5.3 17.7 4.6 9.3 11.9 30.0 12.0 21.4 5.2 10.0 44 4 t I 3 4 *4 3 4 43 43L EXAMPLE 56 A polyethylene-acrylic graft copolymer concentrate was synthesized in a manner similar to that previously described for polypropylene-acrylic graft copolymers. The polyethylene-acrylic graft copolymer concentrate was made by polymerizing a 100% methyl methacrylate (MMA) monomer mixture in the presence of polyethylene (weight ratio of polyethylene:monomer Radicals were generated from di-tertiary-butyl peroxide (DTBPO) at the rate of 0.00010 moles per liter per minute (radical. flux). Monomer and initiator were fed over 60 minutes ard the theoretical (100% conversion) solids at the end of the reaction was A 6.6 liter reactor equipped with a double helical agitator (115 rpm) was charged with 1760 g hydrocarbon solvent and 725 g ~aila a i~ 47 polyethylene (mfr=4, density=0.95) and heated to 150°C. The mixture was stirred for 3 hours. Over a two minute period two solutions were added. The first consisted of 1.63 g of di-t-butyl peroxide in 48 g of methyl methacrylate. For the next 58 minutes a feed of 1.73 g of di-tbutyl peroxide in 1401 g of methyl methacrylate was added at the same feed rate as the second feed. This feed schedule should produce a radical flux of 0.00010 during the feed time. After the feed was complete the reaction was held at 150°C for an additional 15 minutes.
Then it was devolatilized by passing through a 30-mm Werner- Pfleiderer extruder with vacuum vents at 200-2500C, The elemental analysis showed that the concentrate contained 64% (meth)acrylate.
o ara 4 a *4 4 4( 4 A.
a, £i 1 4 4; (4 4 a 44 EXAMPLE 57 This example shows that both polyethylene-acrylic graft polymer and polypropylene-acrylic graft polymer concentrate were effective at reducing the sag of HDPE. The blend of concentrate with HDPE mfr=4 and density=0.95 was milled at 220°C and the hot material from the mill was molded at 2100C. Sags were measured by the same procedure used for polypropylene sheet except that an oven temperature of 1500C was used.
TABLE VI
I
Concentrate of Example Sag Slope min-1 Control 56 56 4 none 5% 10% 5% 0.57 0.27 0.11 <0.015 25.4 mm Sag (min) 7.4 9.0 10.0 15.0 76.2 mm Sag (min) 9.4 13.0 19.8 30 min to 31.7 mm i 1 48 EXAMPLE 58 This example shows that the polyethylene and polypropylene graft copolymer concentrates are effective in improving sag resistance of HDPE while ungrafted acrylic polymer of similar Mw is not. Addition of as much as 5% of a comm.rcial acrylic molding powder poly(methyl methacrylate), Mw 105,000, designated showed no decrease in sag rate, while 3% poly(methyl methacrylate) present as the graft copolymer concentrate resulted in large reductions of sag rate.
The specific concentrate used in part of this study was synthesized in the following manner. The polypropylene-acrylic graft copolymer was made by polymerizing a 5% ethyl acrylate (EA) 95% methyl methacrylate (MMA) monomer mixture in the presence of polypropylene of mfr=0.4 (weight ratio of polypropylene:monomer 0.67:1). Radicals were generated from di-tertiary-butyl peroxide (DTBPO) at the rate of 0.00007 moles per liter per minute (radical flux). Monomer and initiator were fed over 120 minutes and the theoretical (100% conversion) solids at the end of the reaction was A 6.6 liter reactor equipped with a pitched-blade turbine agitator (375 rpm) was charged with 1780 g of the hydrocarbon solvent and 880 g polypropylene (mfr=0.4) and heated to 1600C. The mixture was stirred for 2 hours and then the temperature was decreased to 150°C for one hour. Over a two minute period two solutions were added. The first consisted of 1.22 g of di-t-butyl peroxide in 20 g of the hydrocarbon solvent. The second consisted of 0.0002 mg of monomethyl ether of hydroquinone (MEHQ) and 0.05g of di-t-butyl peroxide in 1.1 g of ethyl acrylate and 21 g of methyl methacrylate. For the next 118 minutes a feed of 13 mg MEHQ and 2.70 g of di-t-butyl peroxide in 66 g of ethyl acrylate and 1253 g of methyl methacrylate was added at the same feed L Jr 49 rate as the second feed. This feed schedule should produce a radical flux of 0.00007 during the feed time. After the feed was complete the reaction was held at 1500C for an additional 15 minutes. Then it was devolatilized by passing through a 30 mm Werner-Pfleiderer extruder with two vacuum vents at 200-2500C. The elemental analysis showed that the concentrate contained 53% (meth)acrylate.
The blends of HDPE (mfr=7, density=0.95) and graft copolymer concentrate was milled at 200°C and the hot materials were formed into sheets from the mill at 170°C. Sags were measured by the same procedure used for polypropylene sheet except that an oven temperature of 150°C was used.
TABLE V11 Concentrate Sag Slope 25.4 mm 50.8 mm Example Level min-1. sag (min sag (min) SControl none 0.59 7.4 8.7 A 3.0% 0.58 7.1 8.3 A 5.0% 0.54 7.6 56 5.0% 0.27 10.3 ,I 4 2.0% 0.28 8.2 10.2 4 3.5% 0.056 9.4 15.8 4 5.0% 0.038 10.4 31.4 58 3.5% 0.37 7.4 9.2 I58 5.0% 0.30 8.1 10.0 t S 50 EXAMPLE 59 The concentrate of Example 4 was blended with LLDPE and the results of evaluating the sag resistance improvements are shown below in Table VIII. The blend of modifier and LLDPE was milled at 1700C and the hot material from the mill was milled at 1500C. Sag resistance was measured by the same procedure used for polypropylene sheet at the temperature listed.
is an LLDPE having an mfr=2.3 and a density of 0.92, recommended for casting and extruding applications.
is an LLDPE having an mfr=1 and a density of 0.92, tg trecommended for blow molding and extrusion applications.
4 TABLE VIII Sag Sag Slope 25.4 mm 101.6 mm LLDPE Concentrate Temp. min-1 sac (min) sag (min) ,A none 1800C 0.58 3.4 5.6 A 5% Ex. 4 180°C 0.24 5.2 10.6 A none 1700C 0.54 .3.9 6.4 A 5% Ex. 4 1700C 0.096 9.5 23.0 B none 1500C 7.8 15.6 B 5% Ex. 4 15000 33.7 min at 19 mm EXAMPLE This example illustrates improved sag modification and increased nucleation temperature for polybutylene, when blended with the concentrate. Polybutylene, injection grade, mfr=4, with and without 2.44 wt. of the concentrate of Example 20 were milled at 1900C and
S!
51 pressed into plaques of about 1.7 mm thickness. Times were measured for various distances of sag at 1450C. DSC curves were used (heat/cool time 20 0 C/min). A higher crystallization temperature relates to increased speed of nucleation and solidification of the heated polymer.
TABLE IX Weight Percent Time to sag (min:sec) SC Temperature. °C Concentrate 25.4 mm 5Q. mm 101.6 mm Melt Crystallize Control 5:20 7:50 10:23 128 2.44 wt 7:24 15:53 >30 129 404990 00 "EXAMPLE 61 This example describes the preparation of a concentrate of polypropylene-acrylic graft copolymer made by polymerizing 5% ethyl acrylate (EA) -95% methyl methacrylate (MMA) monomer mixture in the presence of an oaual amount of polypropylene. Radicals were 0 "4 generated from di-tertiary-butyl peroxide (DTBPO) at the rate of 0.00017 moles per liter per minute (radical flux). Monomer and initiator were fed over 30 minutes and the theoretical (100% conversion) solids at the end of the reaction was A 6.6 liter reactor equipped with a double helical agitator (115 *0 ,rpm) was charged with 1980 g of the hydrocarbon solvent and heated to 1700C. 1000 g of polypropylene (mfr=5) was fed to the reactor via a melt extruder set at 200°C at a rate of about 10 g per minute. After minutes hold at 170°C the addition of monomer and initiator solutions was begun. Over a two minute period two solutions were added. ne first consisted of 0.44 g of di-t-butyl peroxide in 21 g of the hydrocarbon i 1 0 52 solvent. The second consisted of 0.11 g of di-t-butyl peroxide in 1.3 g of ethyl acrylate and 65 g of methyl methacrylate. For the next 28 minutes a feed of 1.59 g of di-t-butyl peroxide and 19 g of ethyl acrylate in 914 g of methyl methacrylate was added at the same feed rate as the second feed. This feed schedule should produce a radical flux of 0.00017 during the feed. After the feed was complete the reaction was held at 1700C for an additional 15 minutes. Then it was devolatilized by passing through a 30-mm Werner-Pfleiderer extruder with vacuum vents at 200-2500C. The elemental analysis (carbon content) showed that the concentrate contained 35% (meth)acrylate.
A sheet of polypropylene (mfr=4) with and without the concentrate of this example was heated in a forced air oven to 1900C, removed from the oven and immediately placed over a female mold and subjected to vacuum. The top and bottom corner measurements were the average of the 8 measurements in mm at the corner of each of the four side faces of the box. The top and bottom center measurements were the average of the 4 measurements in mm at the center of the edge of the 4 faces of the box. These measurements are summarized in Table X and demonstrate smaller wall thickness variations when the concentrate is present.
TABLE X WALL THICKNESS VARIATION IN THERMOFORMED PARTS Top Top Bottom Bottom Polypropylene Center Corner Cente Corner unmodified 1.14 mm 0.88 mm 0.75 mm 0.025 mm Ex. 61 0.97 mm 0.97 mm 0.35 mm 0.21 mm 53 EXAMPLE 62 This example demonstrated the unexpected higher nucleation temperature and shorter time for crystallization imparted by addition of the polymeric concentrate of Examples 1 and 52 to polypropylene of mfr=4. The nucleation temperature was measured while cooling at the melting temperature was measured while heating at 0 C/min and the crystallization time was measured isothermally at 127°C or 1300C. The extent of crystallization was reported for both cooling and melting measurements. Comparison was made with ungrafted PMMA of similar Mw.
4 TABLE XI S Temp. of crystallization 127 127 130 130 130 130 130 Percent Concentrate 0 5 0 1.1 2.2 3.9 7.8 Polymer Concentrate of Example 52 52 52 PMMA PMMA Crystallization Time, min. 16.3 3.6 24.5 3.7 3.0 8.1 10.6 Nucleation Temperature, "C 105 112 107 118 118 112 110 Crystallinity 39 40 41 46 42 42 41 Melting Temperature, °C 165 166 169 170 168 170 168 Crystallinity 41 44 44 44 46 46 44 EXAMPLE 63 This example demonstrated the lower equilibrium torque and improvement in time to flux for blends of the concentrate of Example 1 with polypropylene of mfr=4 using the Haake Rheocord. The test conditions are described above. Peak torque at flux was also reduced.
54 TABLE XII Wt.-% Concentrate in Polyoropylene 0 3 Time to flux (seconds) 109 50 50 Equilibrium Torque (meter-qrams at 215 695 690 670 ft ft i ft ft., *0 #4 ft.i ft f ft., ft I 4 44 ft .4 ft II 4 *i II 4 (4 EXAMPLE 64 This example shows that a propylene-acrylic graft copolymer concentrate may be used to improve the sag resistance of an acrylic sheet. About 20 parts of the graft polymer of Example 1 was milled with 100 parts of a commercial acrylic molding powder of Mw 105,000 and compression molded. Sag tests indicated that the sheet containing the concentrate may be heated to about 5-100C higher before flow equivalent to that of the unmodified sheet was observed.
EXAMPLES 65 66 Graft copolymer concentrates were prepared according to the process described in Examples 52-54, using the conditions shown in Table XIII.
I I i1i 55 TABLE XI11 Concentrate of Example
A
B
Acrylic In Cone.
55- 55 Init-
DTBPO
DTBPO
Monomer Feed Time Solids Temp. °C (min) Radical Flux 50% 50% 150 150 120 0.00010 120 0.00007 So a 0 a 4 a S 4 4 4 4 O 41 4 4 0 Concentrates A and B were blended together at a weight ratio of 2.8:1 to form concentrate C. As indicated in Table XIV, concentrate C was blended at the 4% level with polypropylene and the indicated amounts of di-t-dodecyl disulfide (DTDDS) and extruded. The sag results for these blends are given in Table XIV below.
TABLE XIV Examole 66 67 Concentrate 4 4 4 DTDDS Sag Slope in min-1 none 0.03% 0.3% 0.07 0.05 0.03 4 r 0 0r IIINIA
I
Stabilizing the concentrate during processing, as by using the DTDDS, is seen to produce even more significant improvement in melt strength.
EXAMPLE 67 This example further demonstrates that the graft copolymer has little effect on the high-shear viscosity but a pronounced effect on lowshear viscosity in polypropylene.
rsr 56 The graft copolymer of Example 1 was admixed at the five weight-percent level with an injection-molding grade of propylene homopolymer, mfr=4, as in Example 63. Capillary and parallel-plate viscosities were measured at various temperatures under conditions described above, under both low and high shear conditions. The results shown in Table XV below demonstrate the increase in low shear viscosity, especially at temperatures below about 210 °C with essentially no effect on viscosity at high shear rate.
.I 3(
I
.33 3,3
C
Conditions: Amount of Graft Polyme Test Capillary Viscosity (a) Capillary Viscosity (a) Capillary Viscosity (a) Parallel Plate Viscosity Parallel Plate Viscosity Parallel Plate Viscosity TABLE XV Low Shear 0% 5% TeIppeiratur High Shear 0% 180 OC 190 °C 210 °C 190 °C 210 °C 230 °C 94000 80000 57000 63000 54000 37000 133000 110000 75000 99000 58000 39000 1900 1900 1200 2100 1800 1500 2000 1600 1100 2100 1800 1400
:!B
i Shear Conditions: a: Low Shear=1.0 sec- 1 high shear= 1000 sec-1 S b: Low Shear=0.1 sec-1; high snear= 500 sec- 1 3( EXAMPLE 68 S I f This example shows improved stabilization to weight loss on heating by use of a disulfide or a substituted triazine stabilizer. A polypropylene-acrylic graft copolymer similar to that of Example 4 was blended with stabilizers on the mill roll. The graft copolymer (98 grams) !1 I Ilrt r
I
I
1(( :rrr f
I
57 was fluxed on the mill at 1950C. The stabilizer (2 grams) was added and blended in for 2 minutes. The material was removed from the mill, cut into chunks, and granulated. One or more of these stabilized versions were then let down in a similar manner in additional graft copolymer to produce graft copolymer stabilized at the 100-5000 ppm level. The results on the TGA of stabilization are shown in the table.
Weight loss is the temperature at which the particular percent weight loss is observed, utilizing a DuPont ThermoGravimetric Analyzer at a heating rate of 20°C in nitrogen. Although none of the stabilizers were deleterious to stability, only those designated 2 and 7 exhibited significant stability advantages.
The stabilizers studied were: 1. DLTDP (dilauryl thiodipropionate); 2. TNPP (trisnonylphenyl phosphite); 3. Irganox 1010 (tetrakis(methylene(3,5-di-t-butyl-4-hydroxyhydrocinnamate))methane); 4. DTDDS (di-t-dodecyldisulfide); Irgafos 168 (tris-(2,4-di-t-butylphenyl)phosphite); 6. Weston 618 (di-stearyl pentaerythritol diphosphite); 7. Cyanox 1790 (tris(4-t-butyl-3-hydroxy-2,6-dimethylbenzyl)-striazine-2,4,G-( 1 8. Irganox 1076 (octadecyl 3,5-di-t-butyl-4-hydroxyhydrocinnamate); 9. Topanol CA (3:1 condensate of 3-methyl-6-t-butylphenol with crotonaldehyde.
I:'
1' 3, 58 TABLE XVI STABILIZER (PPM) 1. 2 3 4 5 6 7 8 9 WEIGHT LOSS
TEMPERATURE
(DEGREES C) 600 2000 600 2000 2000 .300 1000 I *I I I I 141114
I
II
I I 11144
I
ala 600 2000 2000 2000 600 2000 2000 2000 2000 2000 600 2000 600 2000 600 2000 600 2000 2000 2000 2000 2000 2000 2000 2000 600 2000 -59- TABLE XVI (continued) STABILIZER (PPM) 1 2 3 4 5 6 7 8 9 WEIGHT LOSS
TEMPERATURE
(DEGREES C) 2000 2000 2000 2000 2000 2000 2000 600 2000 325 325 321 321 321 319 319 600 2000 1000 If 9 9 9 9999 999199 119 2000 4000 1000 1000 2000 2000 2000 2000 4000 4000 600 1000 1000 2000 285 291 285 289 289 292 282 288 291 291 278 2000 278 277 285 2000 280 2000 286 2000 2000 2000 1000 1000 60 EXAMPLE 69 This example illustrates the preparation of a larger amount of graft copolymer to be used in many of the following studies. The process and composition of Example 52 was followed with some variations. Several preparations were combined. In all but the last of these preparations, radicals are generated at the rate of 0.000070 moles per liter per minute (radical flux).
Monomer and initiator are fed over 120 minutes and the theoretical (100%) conversion) solids at the end of the reaction is A 380-liter reactor equipped with a pitched-blade turbine agitator was charged with 86.4 kg of the hydrocarbon solvent anD 34.5 kg of polypropylene homopolymer, mfr=4. After deoxygenating (applying vacuum to degas, followed by pressurizing with nitrogen to atmospheric pressure) through three cycles, it was pressurized to 103 kPa with nitrogen and heated to 150°C over 2 hours. A pressure of 241 kPa was maintained while the batch was held at 1500C for 3 hours. Two solutions were added over a fifteen minute period. The first consisted of 59 g of DTBPO in 841 g of the hydrocarbon solvent. The second consisted of 0.32 kg of ethyl acrylate and 6.14 kg of methyl methacrylate. Addition of the first solution was then continued at a lower rate to feed an additional 103 g of DTBPO and 1479 g of the hydrocarbon solvent over 105 minutes. At the same time the monomer addition of 2.26 kg of ethyl acrylate and 43.0 kg of methyl methacrylate was continued over 105 minutes.
Reaction exotherm increased the temperature to about 1600C. After the feed was complete, 5 kg of the hydrocarbon solvent was fed into the reaction mixture.
The reaction mixture was held in the reaction kettle for an additional minutes. It was then'transferred to a second kettle which was also under pressure at 150°C. During the transfer a solution of 80 g of di-tertiary dodecyl disulfide in 320 g of the hydrocarbon solvent was added to the second kettle.
Also during this transfer three 4.53 kg portions of the hydrocarbon solvent were I I 4 teatl tatt I i 61 fed into the reaction kettle. Material in this second kettle was fed to a 20.3-mm Welding Engineers twin-screw extruder where devolatilization occurred.
During the devolatilization the next batch was prepared in the reaction kettle. It was transferred to the extruder feed kettle while extrusion continued.
In this manner several batches were made in a "semi-batch" manner, that is, batchwise in the reactor with continuous feed to the extruder.
In the final preparation of the blend, radical flux was 0.000050 (42 g DTBPO 858 g of the hydrocarbon solvent in the first feed, 73 g DTBPO 1502 g of the hydrocarbon solvent in the second feed).
The final blend, designated Example 69, was prepared by blending pellets from 13 batches prepared as described and one batch of the final variant. All samples from individual batches gave acceptable sag resistance when tested in polypropylene.
EXAMPLE The following example illustrates that improved stability ca. be imparted to the graft copolymers of the present invention by copolymerization of an alkylthioalkyl monomer, specifically ethylthioethyl methacrylate.
The stability of graft copolymers prepared with alternate monomer compositions was also evaluated. All were prepared according to the procedure for Example 4, except that the monomer composition varied and the product was isolated by evaporating solvent instead of by devolatilizing in an extruder. The monomer compositions and the TGA results are summarized in the table below. The abbreviation EA indicates ethyl acrylate; MMA=methyl methacrylate; ETEMA= ethylthioethyl methacrylate and MA= methyl acrylate.
Weight loss is the temperature at which the particular percent weight loss is observed, utilizing a DuPont ThermoGravimetric Analyzer at a heating rate of 200C in nitrogen.
62 TABLE XVII
PI
Grafted Acrylic P olymer MMA, 5% EA MMA, 5% EA 0.05% ETEMA MMA, 5% EA 0.25% ETEMA MMA, 5% MA Temperature at Which Noted Percent Weight Los-s-'Occurs by TGA Analysis 1 2 5 1 221 260 281 254 274 289 305 290 307 314 335 317 333 346 360 325
'I
ftit ft
I
EXAMPLE 71 This example illustrates that an alternative method reported for the preparation of methacrylic ester//polyolefin graft copolymers does not proJuce a polymer useful in improving resistance to sagging of polypropylene. Example 2 of U.S. 2,987,501 was repeated, wherein linear low-density polyethylene homopolymer (mfr=2.3) was immersed in fuming nitric acid for 30 minutes at 70 0 C, removed, washed with water, and dried. The treated polyethylene was then suspended over refluxing methyl methacrylate for 4 hours. The polymer was extracted with methyl ethyl ketone, as taught in the reference, to remove ungrafted poly(methyl methacrylate). The.molecular weight of the ungrafted polymer was determined by gel permeation chromatography to be Mw=430,000, Mn 170,000.
I
L:l 63 TABLE XVIII Weight of Weight before Weight after Weight polyethylene, reaction (after reaction and of polymer nitration) extraction, a extracted.,.
3.397 3.48 5.964 4.40 Thus, the graft copolymer formed was 43% PMMA and 57% PE. The total sample prior to extraction was 67% PMMA, 33% PE, and the efficiency of grafting of the PMMA was 63.1%.
The resultant graft polymer, from which the ungrafted polymer had not been removed, was blended at the 4% level into the polypropylene resin of mfr=4 used as a standard for testing sag resistance. The graft copoly"- r of this example did not disperse well, and visible, large, undispersed fragments were S seen. The sag value (0.31) was worse than for the unmodified resin (0.18) or for resin modified with an equivalent amount of the graft copolymer of Example S69 (0.02).
The graft copolymer of this example was also milled into linear low-density polyethylene (mfr 2.3) in the manner taught in Example 59. Poor dispersion in polyethylene was also noted, with large chunks of the undispersed modifier visible. Sag resistance was determined at 150°C as in Example 59; sag for the unmodified control (by the sag slope test) was and for the graft copolymer of this example, 0.23. By comparison, sag when 4 1 using the graft copolymer of Example 4 would be expected to be well below 0.10.
4 1 S'i 1 64 EXAMPLES 72 77 This example illustrates preparation of blends of graft copolymer with polypropylene resins to form pellets useful for further processing into extruded or molded articles.
The graft copolymer of Example 69, not separated from any ungrafted polypropylene or acrylic polymer, was used as 3.2-mm-long pellets cut from an extruded strand.
The polypropylene resins used were Aristech T1-4020F (Aristech Chemical Corporation, Pittsburgh, PA), Himont 6523 (Himont Corporation, Wilmington, Delaware), and Rexene 14S4A (Rexene Corporation, Dallas, TX).
Characteristics are shown in Table Xlll; the term "copolymer" in th- table means a copolymer with ethylene.
The graft copolymer was blended at 5% with the polypropylene resins by tumbling. The blend was then extruded into strands through an Egan mm, twin-screw extruder equipped with screws of 32:1 length/diameter ratio; the strands were cooled and chopped into pellets. Variojs feed rates and screw speeds were utilized. Conditions for the unmc' Jified and modified resins used to obtain large-scale samples are summarized in Table XX. Sag tests as S' described in Example 1 were conducted on several other samples of modified resin processed under varying conditions, and the results were comparable to those reported below in Table XIX.
4 1t 4. Blends of Polynropviene With Methyl Methacrylate Graft Coolymer and Controls Example Ex. 6-- Graft, rohr Polypropylene Matrix Resin Name MF Comoosition V 0 a. 44 00 444
V
00040 00 40 4 0 V
V
S
44 a *4 00 03 0 4 O Ct 0 C 40 C
C
Aristech TI-402OF Himont 6523 Rexene 14S4A 2 copolymer 4 homopolymer 4 copolymer 0 .23 0 .02 0 .36 0.11* 0.35 0 .14 Sample tore on testing; other blends processed at slightly different conditions gave sags of 0.06 to 0.09.
66
TABLE.X
Pinesqnnrncjit* n s frr Vra-nlPnA nf Thl YTY Example: Modifier: 72 -73 74 5% 75 76 5% *a oa ao o a a 0 a *a ar a C a o aa Feed Rate, kg/hr (Set) Feed Rate (actual) Screw Speeds 200 Drive Amps Kg-m/si Head Pressure (kPa) Barrel Temps. 0
C)
Zone 1 Zones 2 8 Die Melt Temp. °C 90.7 90.2 101 103 1258 2137 163 204 204 213 181.4 185 200 121 3033 2758 163 204 204 222 90.7 89.8 100 97 1184 1448 163 204 204 208 181.4 181.4 200 111 2811 2068 163 204 204 216 181.4 178.7 200 112 2811 2275 163 204 204 217 181.4 182.3 112 2811 2206 163 204 204 217 1 Power applied to extruder screw.
EXAMPLES 78 83 This example illustrates preparations of blends of graft copolymer with other polypropylene resins on different compounding equipment to form pellets useful for further processing into film or profile. The Amoco 6214 is a film grade polypropylene resin containing a clarifier. The Eastman 4E11 is an impact-extrusion grade, propylene-ethylenecopolymer resin used in profile extrusion. In the present case, both 1% and 5% by weight of the graft copolymer described in Example 69 were used to form the blends.
ii 67 The two polymers were tumble blended, and the mixtures fed to an 83 mm Werner-Pfleiderer co-rotating, intermeshing, twin-screw extruder of 24/1 I/d ratio. The pellets were continuously fed to the extruder by means of an Acrison "loss-in-weight feeder", melted and mixed in the extruder, extruded through a 33-strand die, cooled in a water trough, dried, pelletized, and packaged. The machine conditions for the individual batches are as follows: TABLE XXI Compositions of Blends and Matrix Polymers Examle Modifier Matrix Polymer 78 Eastman 4E11 Copolymer 79 1 81 Amoco 6214 Homopolymer 82 1 83 i i it I 68 TABLE XXII Preparative Conditions for Various Blends of Ta~ble XXI Temnerature. 0
C
Ex.79 Zon set voint/actual Conditions z-1 z-2 z-3 Z-4 Z -5 Z-6 (DIE) Z-7 (DIE) 229 /229 235 /216 249 /227 213 /302 235 /221 227 /227 238 /241
RPM-
TORQUE FEED SET-
VACUUM-
MELT TEMP.-
RATE-
125 73-75% 380 mm Hg 227 0 C (STRANDS) 150 kg/hr 4.4.
C,,
Kill! Ex. 80 Zon set ipoint/artual Condit ions z-1 z-2 z -3 Z-4 z-6 z-7 229 /229 235 /216 249 /235 213 /302 235 /232 241 /241 238 /238
RPM-
TORQUE-
FEED SET-
VACUUM-
MELT TEMP.- RATE 125 73-75 355-380 mm Hg 205-207 0
C
218 kg/hr Ex. 82 ZoQn~e set point/actual Ii Z-1 z -2 z -3 Z -4 z-6 z-7 288 296 299 252 293 266 268 /288 /304 /260 /316 /293 /232 /266 Conditions RPM- TORQUE- 50-53 FEED SET- VACUUM- 203 253 mm Hg MELT TEMP.- 223 0
C
RATE- 116 kg/hr :i
I
iii c.
1 69 Ex. 83 Zone set point/actual Conditions Z-1 Z-2 Z-3 Z-4 Z-6 Z-7 288 293 299 224 266 266 268 285 272 254 310 249 229 272
RPM-
TORQUE-
FEED SET-
VACUUM-
MELT TEMP.-
RATE-
50-56 304 329 mm Hg 226 0
C
122 kg/hr EXAMPLES 84 87 rrrr 1
I
I i i d
I~
1 This example illustrates the use of a graft copolymer of the present invention in the preparation of bottles from polypropylene materials.
The graft polymer of Example 69 was blended at various levels up to 5% by weight with either of two commercial polypropylenes used for blow molding of bottles. The matrix polymer of Example 84 was a propylene random copolymer believed to contain 2-4 ethylene, supplied by Fina Oil Chemical Co., Dallas, TX, as Fina 7231, mfr=2.
The matrix polymer of Example 86 was a propylene homopolymer, mfr=2, supplied by Quantum Chemical, USI Division, Rolling Meadows, IL as Norchem 7200GF. Blends were made by tumbling the resins.
Samples were injection blow molded on a Jomar machine, model (Jomar Corporation, Pleasantville, NJ). The resin blend, in melt form, was injected into a four-cavity mold (two cavities being blocked off) over a core pin with an air hole at the end to form an inflatable parison. The mold was heated and was designed to produce a pattern at the far end which will allow a cap to be attached after molding.
Temperatures of the mold were controlled at the bottle neck, bottle walls, and bottle bottom. The parisons were conveyed to a second i t i:i 70 station where they were inflated to form the bottle shape, and then to a third station where they were cooled and removed. Bottles, which were a 103.5 ml spice bottle, were judged versus non-modified controls for surface gloss, clarity, uniformity of thickness, wall strength, and the like, as well as to the ease of molding.
TABLE XXIII Molding Conditions for Bottles Temperatures. °C.
SExample Resin Graft.% Melt Bottom Wall Nck 00*408 84 84 243 77.7 104 48.9 85 84 Ex. 69, 5% 249 82.2 110 48.9 86 86 243 77.7 104 48.9 87 86 Ex. 69, 5% 249 82.2 110 48.9 When bottles from Example 85 were compared with their controls from Example 84, a slight improvement in gloss, notable increase in a 4 a, 4 a o. contact clarity, and noticeable improvement in stiffness were observed.
Similar advantages over the control were seen with at a 1% level of the agraft polymer with the matrix resin of Example 84. The clarity effect was not seen with bottles from Example 87 over control Example 86.
For reasons not fully understood, the same additive at 5% was I I deleterious to the formation of bottles from homopolymer or copolymer of higher melt flow rate, even with appropriate adjustments in processing temperatures; much of the problem was associated with poor dispersion of the modifier. Such poor dispersion has not been seen in other compoundi-g, processing or testing operations. Slightly stiffer bottle of improved gloss could be blown with the graft polymer additive at 0.5 weight percent, relative to a control with no additive A 4
I
71 A pre-blend (Example 73) of 5% graft copolymer with another mfr=2 high-impact copolymer yielded bottles with severe material non-uniformity. A dry blend of 0.5% graft copolymer with this same resin (the resin of Example 72) gave bottles with improved gloss and contact clarity.
EXAMPLES 88 94 These examples illustrate the utility of a graft polymer of the present invention in the preparation of polypropylene foam and foamed sheet. In the examples, a homopolymer of polypropylene (Example 72), mfr=2, a pre-blend (Example 73) of that polypropylene with a methacrylate//polypropylene graft copolymer, and a mixture of the Example73 pre-blend with 1% talc (designated Example 88) were employed; into all pellets were blended Ampacet 40104 to incorporate a blowing agent. Ampacet blowing agent is a 10%-active, proprietary S; chemical blowing agent dispersed in polyethylene. It is supplied by Ampacet Corporation, 250 South Terrace Avenue, Mt. Vernon, NY 10550. When 10 parts of Ampacet are blended, there is 1 part proprietary blowing agent in the formulation.
The polymer mixture was processed in a 25.4-mm, single-screw extruder produced by Killion Extruders Corporation, utilizing a 24:1 length/diameter screw of 4:1 compression ratio, and a 1-mm-diameter rod die. Extrusion conditions are summarized below. The unmodified polymer exhibited severe fluctuations in die pressure (6900 12,400 ,I kPa); the blend containing 5 parts of the graft copolymer could be extruded at a constant die pressure. In both cases good cell uniformity was observed. Uniform larger cells were noted in the graftpolymer-modified blend when the amount of active foaming ingredient
I
72 was increased to The presence of 1% talc in the modified polyolefin produced the best cell structure and fastest line speed.
Foam densities of the rods were measured according to ASTM Standard Method D-792, Method A-L. Although the unmodified matrix polymer produced the lowest-density foam, the modified polymer foams in general had a regular foam-cell structure.
The three materials were also processed on a similar line with a 202-mm cast film die and a heated collecting roll to yield foamed sheet; here no significant differences in processing were seen among the three resin blends. The individual sample preparations and results are shown in Table XXIV below.
itrr 1.41 TABLE XXIV Type: Rod Sample: Ex. 89 Polvymer of: Ex. 72 Talc, wt% Foaming agent,wt 1 Extruder rpm 80 Melt temp.,°C 214 Melt pressure, kg/cm 2 127 Puller speed, 13 meters/min Sample Density, 0.469 g/cm 3 Rod Ex. 90 Ex. 73 1 80 208 127 15 Rod Ex. 91 Ex. 88 1 1 80 209 140 23 Sheet Ex. 92 E. 21 1 75 227 56 Sheet Ex. 93 73 1 75 227 42 Sheet Ex. 94 73 1 227 42 0.664 0.733 i' 73- EXAMPLES 95 98 This example illustrates the utility of a graft copolymer of polypropylene//methyl methacrylate in the preparation of blown polypropylene film. Film was blown from the control polypropylene homopolymer of Example 74, the pre-blend of Example 75 which contained 5 weight percent of the graft copolymer of Example 69, and dry blends of the polypropylene of Example 74 with 1 and with 5 parts of the graft copolymer of example 69.
Blown film was produced on a Killion blown film line (Killion Extruders Co., Cedar Grove, NJ), which consists of a 25.4-mm, singlescrew extruder operating at a melt temperature of about 2160C., a mm spiral mandrel die, air input for producing a bubble, and a Killion vertical-blown -film tower. The blown-film tower contains two nip rolls for collapsing the bubble and a means for pulling the film through the nip rolls. The die and pull speeds are adjusted to produce film about 5.6 mm thick (two thicknesses) and either 108 or 165 mm wide, the blow-up ratios being 2.125 and 3.25 respectively, at respective top nip speeds of 7.65 and 5.94 meters/minute.
Table XXV Film of Materials Thickness Example Ex. 95 Ex. 74; no GCP 0.051 0.066 Ex. 96 Ex. 75;,5% GCP, Cmpd. 0.056 0.064 Ex. 97 Ex. 74; 5% GCP, Dry Blend 0.051 0.058 Ex. 98 Ex. 74; 1% GCP, Dry Blend 0.051 0.058 Ii F 74 Himont 6523, mfr=4, homopolymer polypropylene was blown into 0.025-mm-thick film (single layer) as Example 95 (control). The bubble was slightly lopsided, and the frostline (onset of crystallization) was at an angle to the die. A lopsided bubble results in less uniform film thicknesses.
With 5% of the graft copolymer of Ex. 69 present, the bubble of Example 96 was stabilized, the frostline levelled, and the frostline moved closer to the die. Both 108- and 165-mm, lay-flat films were produced. Although some fluctuation in die pressure was noted when forming the latter film, it had the most stable bubble.
This increase in bubble stability was also observed with the 1% and 5% dry blends of Examples 97 and 98. No significant differences in film appearance was observed between the 5% precompounded blends and the dry blends.
The modified films had decreased film see-through clarity.
Contact clarity remained unchanged. No difference in edge-roll color was observed between modified and unmodified film.
The "openability" of neat and modified film was tested. Although a very qualitative test (the collapsed film is snapped between the fingers and one feels how well it opens), no difference between the unmodified and modified resins was observed.
EXAMPLES 99 -104 The experiments illustrate the use of the graft polymer of the present invention in producing polypropylene cast film. A single-screw extruder, manufactured by Killion Co., was equipped with a 3.81-cm screw of 24/1 length/diameter ratio, a 20.3-cm x 0.635-mm cast film die, V i 11:
K
K"~i 75 a chill roll and a torque winder for the film, was utilized. The extruder melt temperature was 2260C. The melt was extruded through the die and onto the chill rolls, the take-up speed being adjusted to produce film of various thicknesses. Film thicknesses was measured, as was "neckin", an undesirable shrinkage of width. Film stiffness and edge roll color were measured qualitatively. Film thicknesses were adjusted increasing line speed of the torque winder and lowering the extruder output by reducing screw speed.
TABLE XXVI Film of Example Ex. 99 Ex. i00 Ex. 101 Ex. 102 Ex. 103 Ex. 104 Starting Material Ex. 74 Ex. 75 Ex. 74 and Ex. 69 Ex. 81 Ex. 82 Ex. 83 Form Unmodified Pre-blend; 5% GCP Dry blend; 5% GCP Unmodified Pre-blend; 1% GCP Pre-blend; 5% GCP
WJ
GCP graft copolymer of Example 69 Films of the composition of Example 99 were uniform and consistent at thicknesses of from 0.25 mm to below 2.5 mm. Example 100 produced acceptable film of improved edgr color and with less film neck-in. Example 101 also produced less neck-in, but did not improve edge color. Both modified versions yielded stiffer films at equivalent thickness vnrsus the control, allowing the film to be wound more easily.
The opacity of the film increased with the addition of the graft polymer.
76 With Examples 102 to 104, the neck-in differences were not noted when the graft copolymer additive was present. The films at both 1 and weight percent graft copolymer were stiffer than the unmodified control (Examples 103 and 104 versus Example 102).
SEXAMPLE 105 This example illustrates that biaxially oriented film can be prepared from a polypropylene resin containing 5% of the polypropylene/methyl methacrylate graft copolymer. Under the limited conditions tested, which were optimum for the unmodified resin, no distinct advantage could be seen for the additive. At identical extrusion and MDO (machine direction orientation) conditions, the modified resins could not achieve and maintain the line speeds possible with the unmodified resin during the TDO (transverse direction orientation).
The control resin was Example 81, mfr=2.2, high-clarity homopolymer marketed for film use. Pre-compounded resins were Examples 82 and 83, containing respectively 1% and 5% of the graft copolymer of Example 69 (under the extrusion conditions, a dry blend of 5 parts graft copolymer of Ex. 69 with the matrix resin of Example 81 gave very poor dispersion, leading to many gels and frequent film breaks). The blends were processed in a 50.8-mm, Davis-Standard single-screw extruder which conveyed the melt through a 0.48-meter die and onto a 1.02-meter casting roll. An air knife was used to blow the extrudate onto the casting roll. The casting roll rotated through a water bath to completely quench the sheet. The sheet then was conveyed into the MDO, supplied by Marshall and Williams Co., Providence, RI, and comprising a series of heated nip rolls, moving at speeds which cause monoaxial orientation.
i i 77 After the MDO, the film passed through a slitter to cut the film to the proper width and then onto a winder. These rolls were used to feed the film into the TDO, which is an oven with three heating zones, rolls for conveying the film forward, and clamps to grip and laterally expand the film.
The film from Example 81 (unmodified resin) was drawn both 4.75:1 and 5.0:1 in the MDO, and could be drawn 9:1 in the TDO. The unmodified 4.75:1 MDO resin could maintain a TDO line speed of 8.69 meters/minute; the unmodified 5.0:1 MDO resin could maintain a line speed of 6.85 meters/minute.
The film from Example 82 graft copolymer) could receive a MDO of 4.75:1 and TDO of 9:1 and maintain a 6.85-meters/minute TDO line speed. Frequent film breakage was encountered at higher MDO and higher line speeds. This biaxially oriented film appeared to be slightly more opaque than the biaxially oriented film from Example No difference between the edge roll colors of film from Examples 81 and 82 was observed for MDO film.
The films from Example 83 received MDO's of 4.75:1, 5.0:1, and 5.25:1 at a TDO of 9:1. The best film was obtained with a line speed of 6.85 meters/minute and with the lowest MDO; tearing would occur under more stressed conditions. Films from Example 83 were noticeably more opaque and the frost line appeared sooner than with the control film of Example 81.
EXAMPLE 106 This example illustrates a profile extrusion trial using polypropylene modified with a graft copolymer of the present invention.
A single-screw extruder was equipped with a die and appropriate cooling, pulling, and sizing equipment to form a profile in the shape of a :7.7 78 solid rod with horizontal flanges. The rod diameter was 4.83 cm., flanges 2.67 cm. (extended beyond rod), and flange thickness 1.52 cm.
With unmodified resin (Tenite 4E11 copolymer, Eastman Chemical, as described in Example 78), symmetry was difficult to maintain in the profile without sag or distortion. When blends of Example 79 and 80 (1 and 5% graft copolymer, respectively) were employed, the maintenance of shape was improved.
EXAMPLE 107 This example illustrates the use of a graft copolymer blend of the present invention in the modification of polypropylene to produce improved p!astic tubing. The polymers used were the unmodified resins and the resins compounded with 5% of the graft copolymer of Ex. 69, as described in Examples 72 to 77.
A 25.4-mm, single-screw Killion Extruder (Killion Extruders Co., Cedar Grove, NJ) was equipped with a screw of 24/1 length/diameter ratio, a tubing die with an outer die diameter of 11.4 mm. and a variable inner diameter, leading to a 0.25-meter-long water trough for cooling, an air wipe, and a puller and cutter. Conditions and observations are shown in Table xxviii below. Ovality is the ratio of smallest outer diameter to largest outer diameter, as measured by calipers; a value of 1 means the tube is uniformly round.
When tubing of good ovality was produced from the unmodified resin, the major effect of the additive was improvement in tubing stiffness.
S. With the resin of Example 72, where ovality was difficult to control at acceptable output rates, the modified resin (Example 73) improved ovality as well as stiffness.
S- 79- Table XXVII Tubing Prepared from Polyproyovene and Modified Polyvrooylene Polymer Ex. 72 Ex. 73 Ex. 74 Ex. 75 Ex. 76 Ex. 77 Melt Temperature,
°C
217 214 185 197 184 180 Melt Pressure, kPa(a) Inner Diameter mm (set 8270 6890 9650 6890 6890 8270 Ovality 0.75 0.88 (b) 0.97 0.77 0.92 0.90 (b,e) Extrusion rate equivalent for paired unmodified and modified resin.
Modified extrudate tube stiffer.
Higher melt temperature required to avoid "sharkskin" on tubing.
With this higher mfr resin, reduced melt temperature and higher puller speed led to tubing of lower outer diameter.
Modified tubing more opaque.
EXAMPLES 108- 109 This example illustrates the preparation of pre-compounded blends containing talc. The talc used is a white, soft, platy talc of particle size less than 40 p.m; known as Cantal MM-45-90 (Canada Talc Industries Limited, Madoc, Ontario). It was used at the 20% level. The polypropylene used was a homopolymer of mfr=4, known as Himont 6523. The graft copolymer was incorporated at the c P c i i 80 level and was the graft copoiymer of Example 69. The compounding/preparation of these samples was carried out on a Werner-Pfleiderer co-rotating, twin-screw extruder. The materials were tumble blended prior to the compounding.
TABLE XXVIII Blend Talc Modifier Example 108 (control) Example 109 20 Cantal 20 Cantal Matrix Polymer 80% Himont 6523 75% Himont 6523 5% Example The preparative conditions for the blends are given in Table XXIX.
The extruder was operated at 200 rpm, with no vacuum, at rates of 4.5 4.6 kg/hour, and 85-86% torque.
TABLE XXIX Zone Z-1 Z-2 Z-3 Z-4 Z-5 Z-6 Z-7 Z-8 (die) Melt Extruder Zone Settings. °C Example 108 set point/actual 125 148 220 218 230 228 230 242 240 239 240 239 .240 242 225 239 239 Examole 109 set point/actual 125 151 220 219 230 229 230 241 240 239 240 239 240 239 225 239 243 I -j .4 81 EXAMPLES 110-112 These examples teach the injection molding of polypropylene of various compositions and melt flow rates, the polypropylenes containing a graft copolymer of the present invention. In two examples, a 20% loading of platy talc is also present.
Polypropylene may be injection molded into useful objects by employing a reciprocating-screw, injection-molding machine such as that of Arburg Maschien Fabrik, Lossburg, Federal Republic of Germany, Model 221-51-250. In the preparation of test samples, the extruder is equipped with an ASTM mold which forms the various test pieces. The conditions chosen for molding were unchanged ,throughout the various matrix and modified matrix polymers, and no difficulties in molding were noted. Table XXX describes the blends which are molded; Table XXXI teaches the molding conditions; Table XXXII reports modulus values, Table XXXIII Dynatup impact data, and Table XXXIV heat distortion temperature values for the modified polymers and their controls.
In the following list of injection-molded polymers and blends, all samples contain 1 or 5 weight percent of the graft copolymer of Example 69. The polypropylene matrix resins are described in earlier examples; HP is homopolymer, CP is copolymer, the number is the mfr value. The blends with talc are described in Examples 108 and 109.
All materials were pre-blended in the melt, except where a dry blend ,from powder was directly molded. is an unmodified control; (CT) is a control with talc, but no graft copolymer All test methods were by ASTM standard methods: flexural modulus and stress are by ASTM Standard Method D 790, heat 82 distortion temperature under load is by ASTM Standard Method D 648 and Dynatup impact is by ASTM Standard Method D 3763.
Table XXX also includes the melt flow rates (mfr) for the unmodified and pre-compounded blends. In most cases, the melt flow rate is unchanged or slightly decreased in the presence of the graft copolymer, so that the melt viscosity under these intermediate-shear conditions is not extensively increased. The melt flow rate is by ASTM Standard Method D-1238, condition L (230°C., 298.2 kPa) and has units ol grams extruded/10 minutes.
t Example 74 (C) 110 108 (CT) 109 76 (C) 77 ill 72 (C) 73 112 78 (0) al79 8 1(0) 82 83 Matrix HP, 4 HP, 4 HP, 4 HP, 4 HP, 4
OP
1 4 OP, 4
OP
1 4
OP
1 2
OP
1 2
OP
1 2
OP
OP
OP
OP
OP
OP
83 TABLE XXX 5 5 0 v- Blend? mfr 4.40, 4.06 6.07
YES
YES
YES
4.47 3.75 2.37 2.02 2.92 2.04 2.12 2.33 3.81 2.16 at 1 84 TABLE XXXI Iniection Molding Conditions for Propylene Cylinder temperatures. °C (settina/measured) Feed -216/216 Metering -216/216 Compression -216/216 Nozzle 216/216 Mold Temperatures, °C Stationary -49/49 Cycle time, seconds Injection forward -14 Cure -14 Mold Closed -1.2 Moveable -49/49 Mold Open Total Cycle Machine readings: Screw speed (rpm) 400 Back pressure (kPa) -172 Injection (1st stage)(kPa) 861 The flexural modulus data from Table XXXII indicate the stiffening effect of the graft copolymer. Results are in megapascals (OiPa).
85 TABLE XXXII Example 74 (C) 110 108 (CT) 109
FLEXURAL
MODULUS
MPa 1470.6 1744.4 1783.1 2768.0 2867.0
STRESS
(at max) MPa 43.8 47.5 46.9 52.0 54.5
I
Table XXXIII summarizes Dynatup impact data (in Joules) at various temperatures for the blends and controls tested. The data indicate, in general, slightly improved impact for the pre-blended materials, a deterioration in impact strength on molding dry blends of graft copolymer and matrix polymer, and an increase in impact strength for the talc-modified blend also containing the graft copolymer.
t i.
86 TABLE XXXIII Example 74 (C) 110 108 (CT) 109 76 (C) 77 111 72 (C) 73 112 78 (C) 79 81* (C) 82 83 23 4.9±2.
5.7±3.
3.4±1.
3.0±0.
1.9+0.
Dynatup Impact (oules) at Test Temperature. °C 15 5 7 4.4±1.5 3.8±0.3 4 4.6±0.8 2.7±1.5 1 2.0±0.5 1.9±1.0 5 3.4±0.8 4.2±1.6 5 4.1+2.3 4.8±1.8 40.0±0.5 43.9±0.4 14.0±6.4 37.9±1.8 43.1±10.3 32.4±9.5 36.7±0.4 36.3±1.1 37.1±0.7 13.3±10.7 4.9±0.7 7.6±3.7 41 3.4±1.09 41 5.0±2.5 5.0±2. 2.7±0.2 3.0±0.8 3.5±1.1 3.3±0.8 3.0±1.4 3.3+0.8 The large standard deviation at room temperature is suspect.
Table XXXIV presents heat distortion and hardness values for one series. The modified polymer appears to exhibit a slightly higher heat distortion temperature and hardness, although there are inconsistencies noted. The Rockwell hardness values represent ls 1 87 separate determinations on two samples of the material from the indicated example.
TABLE XXXIV Heat Deflection Temperature Example at 2°C/Minute at 411 kPa 1645 kPa 74 110.9 61.0 113.8 63.3 110 117.3 68.7 108 (CT) 128.2 76.8 109 124.7 81.9 Rockwell Hardness Scale 58.4 60.7 57.9 57.3 65.4 56.5 59.3 46.9 64.7 63.7 EXAMPLE 113 This example illustrates the effect of the molecular weight of the polypropylene trunk component of the graft copolymer on the sag modification of polypropylenes of various molecular weights. Graft copolymers were prepared from polypropylene of various melt flow rates. All modifiers were prepared as in Example 58. The 35 mfr polypropylene (Himont PD-701) was run at 65% solids. The 12 mfr polypropylene (Himont Pro-fax 6323) was run at 60% solids. The 4 mfr polypropylene (Himont Pro-fax 6523) and the 0.8 mfr polypropylene (Himont Pro-fax 6723) were run at 55% solids. The molecular weights for the polypropylene base resins, where known, are given in Table XXXV, below.
These were evaluated as melt strength improvers at 4% by weight in several of these same polypropylenes. Standard mill and press conditions were used for all blends, except the 0.8 mfr/0.8 mfr 4 88 polypropylene blends which were milled at 2150°C and pressed at 215°C. Sag rates were measured by the standard procedures. The sag slope at 1900°C is reported in Table XXXVI below.
TABLE XXXV MW-MFR Data for Polvornovlene Base Pesin Molecular-Weight Source(a) (a) Weight-Average Molecular Weiaht 1Q01 12 mfr PD 4mfr PP 0.8 mfr PD 3 4.3 7.1 2.45 3.05 3.5,4.7 0.27* 0.45* I, 06 0 0 0000 0 000600 6 0 6 00* 000000 00 00 0 0 0 0 0600 0 0 0 04 0 0 0 0 00 Source of Molecular-Weight Value: a) Supplier's data. b) Sheehan et al, J. Appl. Polymer Sci., 8, 2359 (1964). c) Mays et al, ibid., 34, 2619 (1987).
These values are number-average molecular weight.
TABLE XXXVI Saa Slope at 190 0 °C for Olefin Blends min-q1 modifier none mfr PP based 12 mfr PP based 4 mfr PP based 0.8 mfr PP based a o6 polynropylene base resin (96%) 35 mfr PP 12 mfr P 0.8 nfr DP 1.6 0.52 0.25 0.099 1.8 0.52 0.23 0.074 1.2 0.41 0.034 0.02 1.0 0.16 0.022 0.02 0.64 0.16 0.031 0.02 In all cases except where a high-melt-flow base resin was modified with a graft polymer having a trunk of high-flow-rate (lowmolecular-weight) polypropylene, sag improvement was observed. The molecular weight for the resin of mfr=35 is not accurately known; it is
A.
I
<4 f $4 I t 1 4 89 believed to be made by thermal/oxidative processing of a higher molecular weight resin. Such a process would both lower the molecular weight and narrow the originally broad molecular-weight distribution.
EXAMPLE 114 This example illustrates the effectiveness of the graft copolymers of the present invention as compatibilizing agents for polymers that are otherwise poorly compatible. In this example a polyolefin, a polar polymer, and the graft copolymer of the present invention were compounded in an intermeshing, co-rotating, twin-screw extruder (Baker-Perkins MPC/ 30) with a screw length-to-diameter ratio of 10:1.
The compounder was run at 200 rpm and temperatures were adjusted to accommodate the polymers in the blend and achieve a good melt.
The melt temperature in the compounding zone is recorded in the second column of the table. The melt was fed directly to a 38-mm, single-screw, pelletizing extruder with a length-to-diameter ratio of 8:1.
The melt temperature in the transition zone between the compounding and the pelletizing extruder is shown in column 3 of Table XXXVIII, below. The melt was extruded into strands through a die, cooled in a water bath, and cut into pellets.
Table XXXVII below summarizes the polymers which were used in the blends of the present example, while Table XXXIX shows that the graft copolymer has little effect upon the tensile strength of the unblended polymers, that is, it does not act to a significant degree as a toughening agent. In the subsequent tables, Tables XL and XLI, improvement in tensiie strength of the blended polymers indicates an increase in compatibility of the blended polymers with one another in the presence of the graft copolymers of the present invention.
4 .1 14 p 90 Under the proper compounding conditions, an increase in compatibility may also produce a decrease in the size of polymer domains in the blend. Scanning electron microscopy confirms that in some of these examples, significant domain-size reductions occur when the graft copolymer is added. For example, the polypropylene domains average 2 micrometers in the 70 PMMA 30 PP blend of example 114.
The addition of 5 phr compatibilizer reduced the domain size to 0.5 p.m.
The addition of 15 phr compatibilizer reduced the domain size to 0.43 p.m. Although not all of the domain sizes were reduced, several others were reduced by 10-30% by the addition of 5 phr compatibilizer. This is a further suggestion that the compatibilizer is acting on the interface of the polymer domains rather than on the individual polymers.
Table XLI summarizes the compatibilizing effect of the graft copolymers upon the various polymer blends.
i -91 TABLE XXXVII Polymers Used in the Blend Examples Polymer and Designation Grade in Tables Produ~cer Designation Other Spec. Specifi- Gray. cations~
SA.N
Styrene-Acrylonitrile Polymer PA66 Nylon 6-6
PET
Polyethylene Terephthalate Monsanto Lustran SAN 33 DuPont Zytel 101 Eastman Kodapak PET Kodak 7352 EVAL Co. Eval EP-ElOS of America 1 .07 mfr=14 ASTM D 1238 Cond. (I) 1444*4 4 4.4 444 41411 4 41 14 4. 1 4.141 4 I I It I 14 4 4. 1 I 1% 4.1 11 4 1 4 1 1 1 1 c& I I I 4 1 11
EVOH
Ethylene Vinyl Alcohol Copolymer
PC
Polycarbonate
PVC
Polyvinyl Chloride P M1A Poly (Methyl Methacrylate)
EP
Ethylene Propylene Copolymer
HDPE
High-Density Polyethylene
PP
Polypropylene General Electric Plastics Lexan 121 Georgia Gulf Corp.
SP-7107 1.14 mp=255 0
C
(D2117) 1.4 mp=245'C
(DSC),
iv0O .74 1.14 44 mole% E, mp =164 C, mfr=5 (190 0
C,
2160 g) 1.20 mfr=16.5 ASTM D 1238 Cond. (0) 1.35 1.18 0.89 54 Mooney (D-164 6) 0.950 rnfr=4 0.903 mfr=4 0.933 12% VA mfr=8 Haas Co.
Exxon Plexiglas VM Vistalon 719 I wm&- Phillips Marlex 66 Co. HMN 5060 Himont Pro-fax 6523 Elvax 650 EVA DuPont Ethylene Vinyl Acetate
<A
L
92 TABLE XXXVI! (continued) Polymer and Designation Grade in Tables Prdue Designation
LLDPE
Linear Low-Density Polyethylene
PS
Polystyrene
PBT
Poly (butylene terephthalate) PA6 Nylon 6
ABS
Acrylonitrile- But adi en e-St yren e Resin
PC/PET
Polycarbonate! Poly(butylene terephthalate alloy Exxon Escorene LL- 62 02 Other Spec. Specifi- G ra v. cationsl~ 0.926 mfr=12 1.06 mfr=8 Huntsman PS-203 Chemical (crystal) General Electric Allied Signa1 Dow Chemical General Electric Valox 6120 Capron 8253 Magnum 341 Xenoy 1101 44 4 4 4 444449 4 444 444*41 4 4 44 (4 4 4 0 4 4 1.09 mp=2 1'C 1.05 mf 1.21 4,44 4 4 4 44 4 4 44 1 4 4 4 44 44 44 C 4 4 4 4 4 ~4 4.4 4 4 4.
CL
A
1.1: 93 TABLE XXLXII melt temperatures 0
C)
PMMA
SAN
EVOH
PA66
PET
PVC
PC
compounderZ 22 5-23 5 22 0-230 2 05-225 260-275 24 5-275 2 05-230 250-290 transition 210-220 2 10-220 200-215 25 5-2 24 5-2 190-2 24 0-2 The pellets were dried and injection molded on a reciprocatingscrew injection molding machine (New Britain Model 75) into test specimens.
-94- TABLE XXXIX Effect of om aiilizer On Polymer Tensile Strenorth Tensile Stre-ngrthsS~w nMaaacl
M
v comoatlbilizer concentration PlIY-mer T~ 5 phr .15 ohr PMMA 65.44 64.79 61.27 SAN 71.91 62.74 55.89 IEVOH 68.78 66.21 63.78 PA66 64.82 64.68 66.60 PET 58.26 59.33 59.72 PVC 45.25 44.97 45.22 PC 62.63 63.05 63.70 HDPE 22.59 22.66 24.14 PP 33.02 34.03 33.95 EP 4 .79 5.50 5.84 LLDPE 10.91 11.80 12.99 EVA 8.64 8.67 8.17
I
95 TABLE XL Tensile Strengths (MPa) of Blends of Polvolefins and Polar Polymers polar polymer 55% volar polymer 80% polar polymer polar z'olymer _0b.hr_ iphp.r/ DbL 5phr 15i&phr O.hr Sohr
HDPE
4 •4 I 4 4 1 4
PMMA
SAN
EVOH
PA66
PET
PVC
PC
25.26 25.77 26.57 26.94 25.97 20.89 25.66 27.00 28.09 26.80 28.85 28.61 22.92 28.80 30.26 30.57 27,74 29.72 30.98 24.86 30.93 31.42 34.71 33.18 38.34 37.70 19.91 31.11 38.30 41.5].
38 .00 38.11 37 .93 23. 67 35.20 39.54 38.33 39.58 38.33 40.09 27 .34 38 .53 50.78 51.88 49.24 61.22 50.23 26.18 55.61 53 .77 55 .08 51.32 65. 62 51.72 30 .72 50.41 55.55 51.23 50.79 69.23 50.91 34.87 51.92 P P 4£ I 4 44
PMMA
SAN
EVOH
PA66
PET
PVC
PC
34.02 33. 67 32.85 32.06 32.93 36.32 33.82 35.37 38.76 37.40 40.29 33.80 37 .68 36.68 37.81 41.05 38.56 40.38 35.15 39.35 39.09 40.23 37.67 35.01 42.72 39.47 35.28 36.69 43.45 47.65 44.65 52.17 43.81 37.87 40.13 45.84 46.08 45.60 51.10 43. 64 40.79 44.64 46.40 41.11 42.73 64 .71 37.67 30.88 42.38 53.70 54.12 53.38 67.84 53.12 40.00 46.24 56.6 51.81 52.57 66.15 54.04 42.56 51.64
PMMA
SAN
EVOH
PA66
PET
PVC
PC
8.20 8.10 12.19 13.04 7.94 6.17 10.31 10.87 12.53 12 .04 13 .04 8.40 9.05 12.05 12.51 14.11 11.69 12.36 11.13 12.88 13.66 19.99 22.14 24.92 27.62 20.22 12.93 23.10 24.17 28 .82 24. 66 27 .98 20.43 18.28 24 .34 27.81 28.15 23.17 26.33 22.27 19.22 25.60 42.47 45.92 41.29 40.87 33.72 25.50 40.18 44.59 50.68 42.39 48.77 37.00 28.41 41.79 46.93 44 .58 42.70 43.48 38.87 30.60 42.76 'p 96 TABLE XL (continued) Tensile Strenaths (MPa) of Blends of Polvolefins and Polar Polymers polar polymer 55% pLolr polymer 80% polar polymer polar polymer OQphr 5phr 15phr DSIr 5-phr 15phr Oohr 5phr LLDPE PMMA 15.23 18.63 20.90 24.88 30.68 32.84 48.95 55.36 54.14 SAN 15.78 21.08 22.57 26.50 35.76 36.71 47.52 56.92 48.84 EVOH 16.83 17.26 18.26 30.02 31.74 31.87 51.83 50.71 52.29 SPA66 17.93 17.99 19.98 29.67 28.49 25.23 64.65 67.55 67.26 PET 15.33 18.09 20.35 25.53 28.23 30.78 45.02 46.16 42.87 PVC 14.72 14.12 15.73 12.45 18.09 20.50 25.99 30.54 33.69 PC 13.64 19.20 18.48 19.22 27.83 30.46 38.45 40.59 38.86
I
9 EVA PMMA 10.57 11.28 14.38 23.06 21.10 28.31 45.99 47.02 50.87 SAN 12.40 13.62 15.22 27.97 27.29 29.35 48.94 52.01 46.14 EVOH 13.13 13.97 16.59 32.41 28.65 35.43 50.97 50.28 48.81 PA66 14.15 13.54 14.42 27.36 24.59 26.92 40.75 38.35 31.60 PET 14.55 14.35 12.31 21.22 23.90 26.45 43.20 43.91 48.44 PVC 7.69 8.28 10.25 13.40 14.29 18.17 19.22 23.76 28.12 g 1 PC 14.05 14.54 13.52 19.78 21.79 24.85 39.26 40.55 41.46 polar polymer levels are 20, 45,and 70% instead of 30, 55 and
I.
F 97 TABLE XL1 Effect of Compatibilizer on Tensile Strength of Blends of Polyolefins and Polar Polymers Inc -ease in Tensile Strengrth (MPa' from the Compatibilizer polar polymer 5.5% Dpolar oolvmer polar o hr 15 rohr 5 ph 15 3ohr 80% polar polymer 5 ohr 15 ohr H D P E i t?4 t ~t4 III II
C
I I*.
4' PMMThA
SAN
*EVOH
PA66
PET
PVC
PC
*P
SAN
*EVOH
PA66
PET
PVC
PC
1.74 2.32 0.23 1 .90 2 .65 2 .03 3.14 5.01 4 .80 1. 17 2 .77 5.01 3.97 5 .27 7.38 6.80 4.81 -0 .23 0.23 3.76 4 .10 8 .12 3.63 6.39 -0 .01 2.39 7.43 7.42 2.99 3.21 2 .08 4 .40 1.48 4 .54 -5 .20 4 .77 64 1.54 8 .00 0.68 8.69 -3.69 10.22 10.70 9.83 1.44 16.37 11. 68 9.26 P P 1.35 3.79 3.22 5.09 7.38 9.98 4.56 5.72 9. 64 8.23 8.32 9.45 0.86 2.22 4.34 1.36 3.03 2.59 2.86 5.27 3.43 5. 61 8.41 10.59 8.38 4 17 5.51 7. 94 7.29 13.02 10. 65 3 .13 15.44 9.11 3.85 I -J 11 I Ji 98 TABL E XLI (continued) Increase -in -Tenile1 Strengrth (MPg') from the Compatibilizer polar nol1YMer 55% p)olar polymer 80% polar poolymer polar polymer 5 h 15 phr LU1r 15 phr 5 .&hr 15 oh r EP ~t
I
J1'AI 14
I
454 4 1 41 44 I I 4 4 44 4 I 44 44 4 I 44 I S I 41 1% 44 4 I t
PMMA
SAN
EVOH-
PA66
PET
PVC
PC
P MNA
SAN
EVOH
PA66
PET
PVC
PC
P MMA
SAN
EVOH
PA6 6
PET
PVC
PC
2.66 4 .43 -0 .15 0.01 0.46 2.86 1.74 4.30 6.01 -0 .50 68 3.19 6.71 3.35 3.40 5.31 0.43 0.06 2.76 -0.59 5.56 5. 67 6.80 1. 43 2.05 5.01 1.01 4 .85 4 .18 6. 68 -0 .27 0.36 0.21 5.35 1.24
LLDPE
5.80 9.26 1 .72 -1.19 2.70 5. 64 8. 61 EVA 95 68 -3 .75 -2 .77 2.68 0.89 2.01 7 .82 6.01 -1.75 -1.29 2 .05 6.29 2 .50 2.12 4 .76 1.10 7 .90 3.29 2.91 1.61 7.96 10.21 1.85 -4 .44 5.25 8.05 11.24 6.42 9.40 -1.12 2 .90 1. 14 4 .56 2 .14 4 .46 -1 .34 1.41 2. 61 5.16 5.10 2.59 5.19 1.32 0. 2. 61 -2.14 7.70 0.41 4 .87 -2 -2 .16 -9.15 5.24 8.89 2 If 4 0.71 1.22 0.83 61 -0 .20 0.59 0.49 3.81 2.81 3.45 0.27 -2 .25 2.'5 6 -0 .53 5.25 1.38 3.02 -0.44 5.23 4.76 1 .03 3.07, 68 -2 .40 0.70 4 .54 1.30 55 and polar polymer levels are 20, 45 and 70% instead of 30, pi 99 TABLE XLII Compatibilization Effect HDPE EVA
PMMA
SAN
EVOH
PA66
PET
PVC
PC
C 4 *r 4 *44 9 4 6C 4 *I It 4I II 4 compatibilization at all three polyolefin-polar polymer ratios (not necessarily at all compatibilizer levels) compatibilization at two of the three polyolefin-polar polymer levels compatibilization at one of the two polyolefin-polar polymer levels 0 no compatibilization seen at any polyolefin-polar polymer ratio, at any compatibilizer level additional evidence for compatibilization in the reduction of domain size by 10-80% EXAMPLE 115 4 4r I I~ t The compatibilizing effect on selected, additional polymer pairs was evaluated in the following example. The blends were compounded, molded and tested for tensile strength as previously described. The results in Table XLIII again indicate that the compatibilizer has minimal or a negative effect on the polar polymers, but a positive effect on the polar/ nonpolar polymer blends. A large tensile strength improvement is seen for the ABS PP blend. Smaller but significant improvements are seen for the blends of PP with PA6 and with PC PBT. With the PS blends evaluated the effect was negligible.
~I
9:~R 100 TABLE XLIII tensile str polar polymer phr polar graft pEQjlyr1 fonolymer naths. (MP) encrths (MPa) polar nonpolar polymer polymer blend 1 15 phr graft blendi copolymer
PBT
PA6
PS
PS
ABS
PC/PBT
PP
PP
PP
HDPE
PP
PP
43.02 56.11 45.26 45.26 51.25 51.77 45.11 51.67 40.45 40.45 52.25 51.79 36.96 43.50 38.88 36.48 32.25 38.99 38.96 47.04 37.36 33.76 42.55 41.88 t t t IC C Ci 1 blend in all cases refers to 55 parts by weight polar polymer and 45 parts by weight nonpolar polymer.
The effect of the graft copolymer on multi-component blends such as those representative of commingled scrap polymers are shown in Table XLIV. In all cases a significant increase in tensile strength is observed when the compatibilizer is present.
J-
II) I
A
i; 1 liL; :lir~ 101 TABLE XLIV Compatibilization of Multicomponent Blends Polar Polymers Nonpolar Polymers HDPE LLDPE mP Compatibi li er Tensile Strength (MPa) 12 12 12 12 12 12 12 12 S 12 33.5 33.5 33.5 35 35 35 36 36 36 33.5 33.5 33.5 35 35 35 36 36 36 none 5 15 none 5 15 none 5 15 16.27 17.67 21.77 18.62 19.98 22.16 17.06 19.21 21.91 0 6 6 6 EXAMPLE 116 This example further illustrates compatibilization of polymer blends using graft copolymers of the present invention.
Blends of ethylene-vinyl alcohol copolymer (Kuraray EP-F101A), polypropylene (Himont 6523) and graft copolymer were milled on a 7.62-cm X 17.78-cm electric mill at 2040C to flux plus three minutes.
The stocks were pressed at 204°C and 103 MPa for three minutes (Carver Press, 12.7-cm X 12.7-cm X 3.175-mm mold)and at room temperature and 103 MPa for three minutes. Two graft copolymers were used in this example. The first (Graft Copolymer A) was a polypropylene acrylic graft copolymer prepared from mfr=4 polypropylene homopolymer (100 parts) and a 93:2:5 mixture of methyl
I
i, 102 methacrylate:ethyl acrylate:methacrylic acid (100 parts). Polymerization was done in Isopar E solvent at 1600C at 50% solids over one hour with a di-t-butyl peroxide radical flux of 0.00012. The product isolated contained 44% acrylate. The second graft copolymer (Graft Copolymer B) was a polypropylene acrylic graft copolymer prepared from mfr=4 propylene homopolymer (100 parts) and a 95:5 mixture of methyl methacrylate:ethyl acrylate (150 parts). Polymerization was done in Isopar E solvent at 1550C at 60% solids. The feed time was 60 minutes and the radical flux was 0.00010. The product contained 53% acrylate.
Addition of the graft copolymer results in an increase in tensile strength and modulus.
TABLE XLV a.
Comoatibilization of EVOH and Polypropylene notched graft Izod tensile tensile EVAL PP copolymer tensile strength modulus (grams) (rams) amLg s) (MPa) (MPa) 30 0 21 29.85 2570 25 51 21 48.06 3190 25 52 22 46.75 3270 90 0 18 21.37 1930 75 151 18 29.79 2140 75 152 13 30.41 2030 1 Graft Copolymer A (see text above).
2 Graft Copolymer B (see text above).
I 1 v

Claims (35)

1. A graft copolymer suitable for improving the tensile modulus and sag resistance of a polyolefin when blended therewith, the copolymer comprising: a non-polar rlyolefin trunk having a weight average molecular weight of 50,000 to 1,000,000 and comprising units of one or more of ethylene, propylene, butylene and 4-methylpentene, said trunk further optionally containing a minor amount of units of one or more of the following: 1-alkenes, vinyl esters, vinyl chloride, acrylic and methacrylic acids and esters thereof; and at least one poly(methacrylate) chain, grafted with a covalent bond to said trunk, said chain being present in a weight ratio to said trunk of from 1:9 to 4:1, said chain comprising at least 80% by weight units of methacrylic ester of the formula CH 2 C(CH 3 )COOR, where R is alkyl, oryl, substituted alkyl, substituted aryl, or substituted alkaryl, and optionally up to 20% by weight of units of other monomer comprising styrenic, other acrylic or other monoethylenically unsaturated monomer copolymerizable with the methacrylic ester or, in an amount of up to maleic and/or itaconic acid of anhydride, said 20 chain having a weight average molecular weight of from 20,000 to 200,000.
2. A copolymer as claimed in claim 1 wherein the methacrylate chain has a weight average molecular weight of 30,000 to 150,000.
3. A copolymer as cl!'med in claim 1 wherein the trunk has a weight average molecular weight of 100,000 to 400,000.
4. A copolymer as claimed in an;y preceding claim wherein the polyolefin trunk comprises polypropylene. A copolymer as claimed in any preceding claim wherein the S920303,tgclet021,31716-89.ee,103 L zl /YT -104 methacrylate chain comprises methyl methacrylate units.
6. A blend of polyolefin with graft copolymer, for improving the tensile modulus and sag resistance of said polyolefin in the blend, comprising: a non-polar polyolefin trunk comprising units of one or more of ethylene, propylene, butylene, and 4-methylpentene, said trunk further optionally containing a minor amount of units of one or more of the following: 1-alkenes, vinyl esters, vinyl chloride, acrylic a-'d methacrylic acids and esters thereof, said trunk preferably having a weight average molecular weight of 50,000 to 1,000,000; and at least one poly(methacrylate) chain, grafted with a covalent bond to said trunk said chain being present in a weight ratio to said trunk of from 1:9 to 4:1, said chain comprising at least 80% by weight units of methacrylic ester of the formula CH 2 C(CH 3 )COOR, where R is alkyl, aryl, substituted alkyl, substituted aryl, or substituted alkaryl, and optionally up to 29% by weight of units of other monomer comprising styrenic, other acrylic or other monoethylenically unsaturated monomer copolymerizable with the methacrylic ester or, in an amount of up to maleic and/or itaconic acid of anhydride, said I 20 chain having a weight average molecular weight of from 20,000 to 200,000, preferably graft copolymer of any preceding claim; and, optionally, ungrafted methacrylate polymer having a monomer composition and weight-average molecular weight as defined in 'V Claim l(b).
7. A polymer blend as claimed in claim 6 which is a concentrate containing from 5 to 50% of the graft copolymer, based on the weight of the blend or a composition containing at least 0.2% but less than 5% of said graft copolymer and, optionally, 0.001 to 0.05% alkyl polysulfide, or optionally, C.001 to 0.1% tris (polyalkylhydroxybenzyl)-s-trizinetrione and/or optionally a blowing agent the percentages being by weight based on the total polymer composition. 920303,tgclet021,31716-89.ee,104 KM. i -105
8. A blend as claimed in claim 6 wherein the polysulfide, if present, comprises di-t-dodecyl disulfide, the triazinetrione, if present, comprises tris-(4- t-butyl-3-hydroxy-2,6-dimethylbenzyl)-s-triazine-(lH,3H,5H)-trione, and the blowing agent, if present comprises one which liberates nitrogen at a temperature of 200 to 230 °C.
9. A blend as claimed in claim 8 wherein the blowing agent is present in an amount of 1 to 2% by weight based on the total polymer composition.
10. A polymer blend as claimed in any one of claims 6 to 9 wherein the polyolefin trunk comprises poly(propylene), poly(ethylene), poly(butylene) and/or a copolymer of at least 80% propylene with ethylene.
11. A polymer blend as claimed in any one of claims 6 to 10 comprising the ungrafted methacrylate polymer in an amount of at least 80% of the polymer blend. *14 S12. A process for preparing a graft copolymer comprising the steps of: introducing inert solvent and non-polar polyolefin comprising 20 units of one or more of propylene, ethylene, butylene,4-methylpentene and, optionally, minor amounts of units of one or more of the following: 1-alkenes, vinyl esters, vinyl chloride, acrylic and methacrylic acids and esters thereof, into a reaction vessel; heating the mixture so formed to a temperature at which the polyolefin dissolves; i adding, with agitation, monomer capable of forming a chain as defined in Claim l(b); adding, to the mixture so formed, initiator which produces a low and constant radical flux for a time sufficient to produce methacrylate chain polymer of weight average molecular weight from 20,000 to 200,000 covalently bonded to the polyolefin; and removing the solvent. S920303,tgclet021,31716-89.ee,105 r'^ 106
13. A process according to claim 12 as applied to the production of graft copolymer or blend according to any of claims 2 to 7.
14. A process according to claim 12 or claim 13 wherein the initiator comprises oil soluble, thermal free radical initiator which has a half life of one hour at a temperature of 60 °C to 200 °C. A process as claimed in claim 14 wherein the half life of one hour is at a temperature of 90 to 170 °C.
16. A process as claimed in any one of claims 12 to 15 wherein the constant radical flux at the temperature in the reaction vessel is from 0.00001 to 0.0005 equivalents of radicals per minute.
17. A process as claimed in any one of claims 12 to 16 wherein the solvent, is removed in a devolatilizing extruder.
18. A process as claimed in any one of claims 12 to 17 wherein the solvent is a hydrocarbon solvent.
19. A polymer blend as claimed in any one of claims 6 to 11 in the form of a shaped article. 4 4 4
20. A shaped article as claimed in claim 19 which comprises an extruded, calendered or moulded, optionally foamed, blend as claimed in any of claims Sto 8 or pellets of said blend.
21. An article as claimed in claim 20 comprising ungrafted polypropylene in an amount by weight of the total polymer content, of at least
22. A shaped article as claimed in claim 20 of claim 21 which is a fibre, sheet, film, other solid profile or a hollow tube, formed by extrusion, or a 920303,tgclet021,31716-89.ee,106 107 hollow container formed by moulding, preferably extrusion blow moulding or injection blow moulding.
23. A film or fibre as claimed in claim 22 of which the polymer is orientated.
24. A film or fibre as claimed in claim 23 in which the polymer is monoaxially orientated.
25. A film as claimed in claim 23 in which the polymer is biaxially orientated.
26. A process for improving the tensile modulus and/or sag resistance of polyolefin which comprises blending therewith a concentrate as claimed in any one of claims 7 to 11.
27. A process as claimed in claim 26 in which such amounts of the ingredients are used as to yield a product having a weight ratio of at least parts of polyolefin to 20 parts of graft copolymer.
28. A process as claimed in claim 26 or claim 27 wherein the blending is carried out at a temperature of at least 150 "C and alkyl polysulfide has Spreviously been incorporated into the mixture for blending.
29. A process as claimed in claim 28 in which the polysulfide comprises di- St-dodecyl disulfide in an amount of 0.001 to 0.05% by weight of the total mixture. 1 4 A process as claimed in any one of claims 26 to 29 wherein the polyolefin comprises polyethylene, polypropylene, polybutylene or a polyethylene/polypropylene or polypropylene/polybutylene mixture. 920303,tgclet021,31716-89.ee,107 L: i .I (JAI NT 108
31. A blend of one or more polar polymers with one or more non-polar polymers including, as a compatibiliser, graft copolymer comprising: a non-polar polyolefin trunk comprising units of one or more of ethylene, propylene, butylene, and 4-methylpentene, said trunk further optionally containing a minor amount of units of one or more of the following: 1-alkenes, vinyl esters, vinyl chloride, acrylic and methacrylic acids and esters thereof, said trunk preferably having a weight average molecular weight of 50,000 to 1,000,000; and at least one poly(methacrylate) chain, grafted with a covalent bond to said trunk said chain being present in a weight ratio to said trunk of from 1:9 to 4:1, said chain comprising at least 80% by weight units of methacrylic ester of the formula CH2 C(CH 3 )COOR, where R is alkyl, aryl, substituted alkyl, substituted aryl, or substituted alkaryl, and optionally up to 20% by weight of units of other monomer comprising styrenic, other acrylic or other monoethylenically unsaturated monomer copolymerizable with the methacrylic ester or, in an amount of up to maleic and/or itaconic acid of anhydride, said chain having a weight average molecular weight of from 20,000 to 200,000. 4 44t
32. A blend as claimed in claim 31 wherein the graft copolymer is a graft copolymer as claimed in any one of claims 1 to C 4a
33. A blend as claimed in claim 31 or claim 32 wherein the non-polar polymer comprises polyolefin and/or ethylenevinylacetate polymer, and/or ethylene/propylene/non-conjugated diene terpolymer and the polar polymer comprises one or more of the following: acrylic polymers, styrene-acrylonitrile polymers, ethylene-vinyl alcohol polymers, polyamides, polyesters especially poly(ethylene terephthalate), polycarbonates, poly(vinyl chloride), polyglutarimide, acrylonitrile-butadiene-styrene polymers, poly(vinylidene chloride), blends of polyester with polycarbonate and blends of poly(vinyl chloride) with polyester. 920303,tgclet021,31716-89.ee,108 -109-
34. A blend as claimed in claim 33 wherein the polyolefin comprises polypropylene and/or polyethylene. A blend as claimed in claim 34 wherein the polyolefin comprises high density polyethylene.
36. A blend as claimed in any one of claims 31 to 35 wherein the weight ratio of polar polymers to non-polar polymers is from 95:5 to 5:95.
37. A blend as claimed in claim 36 wherein the weight ratio is 80:20 to 20:80.
38. A blend as claimed in any one of claims 31 to 36 wherein the graft polymer is present in an amount of 0.2 to 10 parts by weight per 100 parts by weight of polar, non-polar and graft polymer.
39. A blend as claimed in claim 38 wherein the amount of graft polymer is 0.5 to 5 parts by weight per 100 parts by weight of polar, non-polar and graft polymer. A process for improving the mutual compatibility of polymers of different polar levels which comprises blending therewith 0.2 to 10% by weight, of the total polymer mixture, of graft polymer comprising: a non-polar polyolefin trunk comprising units of one or more of ethylene, propylene, butylene, and 4-methylpentene, said trunk further Soptionally containing a minor amount of units of one or more of the following: 1-alkenes, vinyl esters, vinyl chloride, acrylic and methacrylic acids and esters thereof, said trunk preferably having a weight average molecular weight of 50,000 to 1,000,000; and At least one poly(methacrylate) chain, grafted with a covalent bond to said trunk said chain being present in a weight ratio to said trunk of from 1:9 to 4:1, said chain comprising at least 80% by weight 920303,tgclet021,31716-89.ee,109
110- units of methacrylic ester of the formula CH 2 C(CH 3 )COOR, where R is alkyl, aryl, substituted alkyl, substituted aryl, or substituted alkaryl, and optionally up to 20% by weight of units of other monomer comprising styrenic, other acrylic or other monoethylenically unsaturated monomer copolymerizable with the methacrylic ester or, in an amount of up to maleic and/or itaconic acid of anhydride, said chain having a weight average molecular weight of from 20,000 to 200,000. 41. A process as claimed in claim 40 wherein the graft polymer is a graft copolymer as claimed in any one of claims 1 to 42. The product of a process of any one of the foregoing claims 12 to 18, 26 to 30, 41 or 42. #444 04 04* 41 4# 4 4* 43. A copolymer as claimed in claim 1, a polymer blend as claimed in claim 6 or 31, or a process as claimed in claim 12 or claim 40, substantially as hereinbefore described with reference to the Examples. DATED this 5th day of March, 1992. 25 ROHM AND HAAS COMPANY By their Patent Attorneys DAVIES COLLISON CAVE *4 0*~ 4 /VW 920305,tgcletO21,31716-89.ee,110 I--
AU31716/89A 1988-03-29 1989-03-28 Graft copolymers and blends thereof with polyolefins Ceased AU625059B2 (en)