AU607454B2 - Splicing optical fibre under inelastic stretching - Google Patents
Splicing optical fibre under inelastic stretching Download PDFInfo
- Publication number
- AU607454B2 AU607454B2 AU83244/87A AU8324487A AU607454B2 AU 607454 B2 AU607454 B2 AU 607454B2 AU 83244/87 A AU83244/87 A AU 83244/87A AU 8324487 A AU8324487 A AU 8324487A AU 607454 B2 AU607454 B2 AU 607454B2
- Authority
- AU
- Australia
- Prior art keywords
- segments
- fibre
- tension
- temperature
- fused
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Description
)AVIF;'& COLLISON, MELSOURNE andCANi3ERRA* r j S- AU-AI-832 4 4 /87 T WORLD INTELLECTUAL i PE OR l IZA'ON PCT lnternatipBuoa INTERNATIONAL APPLICATION PUBLISHED UNDER THE PATENT COOPERATION TREATY (PCT) (51) International Patent Classification 4 (11) International Publication Number: WO 88/ 03661 G02B 6/38 Al (43) International Publication Date: 19 May 1988 (19.05.88) (21) International Application Number: PCT/AU87/00380 (74) Agents: NOONAN, Gregory, J. et al; Davies Collison, 1 Little Collins Street, Melbourne, VIC 3000 (22) International Filing Date: 9 November 1987 (09.11.87) (AU).
(31) Priority Application Number: PH 8981 (81) Designated States: AT (European patent), AU, BE (European patent), CH (European patent), DE (Euro- (32) Priority Date: 14 November 1986 (14.11,86) pean patent), DK, FI, FR (European patent), GB (European patent), IT (European patent), JP, LU (33) Priority Country: AU (European patent), NL (European patent), NO, SE (European patent), US.
(71) Applicant (for all designated States except US): THE COMMONWEALTH OF AUSTRALIA [AU/AU]; Published Industry Research and Development Branch, Depart- With international search report.
ment of Industry, Technology and Commerce, Kings Avenue, Barton, ACT 2600 7 JUL 1988 8 J.P. -7 JUL 1988 (72) Inventors; and Inventors/Applicants (b'o US only} THORNCRAFT, David, Allen [AU/AU]; 9 Robnor Place, Isabella Plains, ACT 2905 KENNEDY, David, Robert I-4U [AU/AU]; 9 Tepper Circuit, Kambah, ACT 2902 AUSTRALIAN RASHLEIGH, Scott, Clarence [AU/AU]; 19 Harbison Crescent, Wanniassa, ACT 2903 1 JUN 1988 DABBS, Timothy, Peter [AU/AU]; 11l Abuklea Road, Eastwood, NSW 2122 PATENT OFFICE (54) Title: FABRICATION OF FIBRE OPTIC COMPONENTS (57) Abstract A method of fabricating a fused fibre optic coupler includes disposing two or more segments of optical fibre under longitudinal tension. The tensioned fibre segments are preheated to a temperature sufficient to soften the segments and thereby substantially relieve their tension by inelastic stretching of the segments, After the segments have cooled, the fibre segments are re-tensioned and then heated while in intimate side-by-side contact to a temperature sufficient to cause the fibre segments to fuse together, r -r r I .i i 1. L. 1 u r 1;; Ii i I-,Q WO 88/03661 PCT/AU87/00380 "FABRICATION OF FIBRE OPTIC COMPONENTS" FIELD OF THE INVENTION This invention relates to the fabrication of fused fibre optic couplers, especially biconical taper couplers, and is concerned in particular with improving the control and optimum management of the fabrication process.
BACKGROUND ART The usual technique for forming fused biconical taper fibre optic couplers entails disposing respective segments of two or more optical fibres in intimate side-by-side relationship and
S
5.55 0
OBSS
S
SSSB
S
SSSS
.5 5 S B
SB
0 SS 00 0 5 0
S
S.
S 0 S S 00 0050
S
OS..
0*O@ 0O 0s S 0
S
00SS05 S. 0
S.SB
1? 2 heating the segments to a temperature sufficient to cause the fibre segments to soften and fuse together. The heated fibres are then longitudinally drawn to cause each of the fused fibres to develop a biconical taper and to thereby form the coupler. A typical disclosure of these steps is to be found in U.S. patent 4,612,028 to Abebe.
SUMMARY OF THE INVENTION It is an object of the invention to provide enhancements of the aforedescribed known technique for fabricating fibre optic couplers which will contribute to bettering existing commercial standards as to, for example, power loss and coupling factor tolerances.
Most generally, the invention provides in its first aspect a method of fabricating a fused fibre optic coupler, especially but not only a multi-mode biconical taper coupler, comprising: pretreating respective segments of optical fibre to relieve torsional stress therein for a predetermined time period; and heating for a second predetermined time period said pretreated segments while in intimate side'-by-side contact to a temperature sufficient to cause the fibre segments to fuse together, wherein said first predetermined time period precedes said second predetermined time period.
3 In preferred embodiments, the invention in its first aspect provides a method of fabricating a fused fibre optic coupler, especially but not only a multi-mode biconical taper coupler, comprising: disposing two or more segments of optical fibre under longitudinal tension, preferably substantially identical tension; preheating said tensioned fibre segments to a temperature sufficient to soften the segments and thereby substantially relieve said tension by inelastic stretching of the segments; and after the segments have cooled, S* re-tensioning the segments and heating them while in intimate side-by-side contact to a temperature sufficient to cause the fibre segments to fuse together.
It is believed that the initial heating step sees is useful in relieving torsional stress prior to the fusion heating. It is thought that pre-existing unrelieved torsional stress in the fibres contributes to unpredictable excessive power losses in the coupler and particularly to unpredictable excessive tolerances in its coupling factor.
Preferably, the longitudinal tension in the fibres is continuously or periodically monitored to detect when the tension falls substantially to zero during the preheating, whereupon the preheating is terminated and the fibre segments allowed to cool.
The degree of cooling will be dependent on circumstances but cooling is not necessarily to ambient temperature. Cooling is more generally to an intermediate temperature above ambient.
42; 1 0 000.
0 0000 0 6000
S
0000 00 0 00 0* 0 00 00 0
S
0 00 0 0 0 0 00 0000 0 0040 0000 00 00 0 0 0 606000 0 0 000000 O 0 a 00 0 0 *000 00 0 00 *0 Most preferably, the optical fibre segirents are brought into said intimate contact by being twisted about each other.
In a second aspect, the invention affords a method of fabricating a fused fibre optic coupler comprising: heating two or more initially tensioned segments of optical fibre while these segments are in intimate side-by-side contact; monitoring the longitudinal tension and temperature of each of said segments, directly or indirectly; and when the tension in the segments falls to a predetermined threshold value, thereafter continuing to raise the temperature of the segments a predetermined number of degrees above their temperature when their tension fell to said threshold value, to a temperature sufficient to cause the fibre segments to fuse together.
The method preferably further includes thereafter holding or reducing the temperature of the segments, for example, to that at the predetermined tension threshold, and then longitudinally drawing the heated fibres to cause each of the fused fibres to develop a biconical taper and thereby form a coupler of this kind.
The invention also provides apparatus for fabricating a fused fibre optic coupler, comprising:retaining means for disposing two or more segments of optical fibre under longitudinal tension; means for heating said tensioned fibre segments; and control means operably connected to said heating means and said retaining means and arranged to activate said heating means and said retaining means to preheat h.
WO 88/03661 PCT/AU87/00380 said tensioned fibre segments to a temperature sufficient to soften the segments and thereby substantially relieve said tension by inelastic stretching of the segments, and, after the segments have cooled, to re-tension the segments and heat them while in intimate side-by-side contact to a temperature sufficient to cause the fibre segments to fuse together.
Still further afforded by the invention is apparatus for fabricating a fused fibre optic coupler, comprising:means for disposing two or more segments of optical fibre under longitudinal tension; means for heating said tensioned fibre segments; means for monitoring the longitudinal tension and temperature of each of said segments, directly or indirectly; and control means responsive to said monitoring means and connected for controlling said heating means, which control means is arranged whereby, when the tension in the segments falls to a predetermined threshold value, the heating means continues to raise the temperature of the segments a predetermined number of degrees above their temperature when their tension fell to said threshold valne, to a temperature sufficient to cause the fibre segments to fuse together.
The control means in either of the arrangements just described is preferably a programmed computer control means.
It is found that the control of fusion heating in response to monitod fibre tension results in improved reliability of the method in WO 88/03661 PCT/AU87/00380 6 terms of a closer uniformity of coupler parameters to standard or desired values. This is thought to occur because the tension in a fibre takes account of axial variations in the physical properties of the fibre, for example, viscosity, a dependency which is not achieveable by solely relying, for example, an observed furnace temperature, or even on fibre temperature. The optimum fusion temperature for given coupler characteristics indeed varies over a long length of fibre.
Monitoring of longitudinal tension in the fibres may be effected by means of any suitable stress or strain gauge. The gauge preferably interfaces to the abovementioned computer programmed to control the fibre heating means in response to a relevant tension signal fed back from the gauge.
The longitudinal tension of each fibre may be separately monitored and controlled.
Most preferably, the optical fibre segments are brought into said intimate contact by being twisted about each other.
BRIEF DESCRIPTION OF THE DRAWINGS The invention will now be further described, by way of example only, with reference to the accompanying drawings, in which: Figure I is a purely schematic plan view of apparatus in accordance with the invention: Figure 2 is a lateral cross-section on the line 2-2 in Figure 1, showing the heater assembly; Figure 3 is cross-section on th line 3-3 in Figure 2 and depicts the furnace in greater detail; Figure 4 is a plan view of the unit for WO 88/03661 PCT/AU87/00380 7 clamping, tensioning and drawing the optical fibres; Figure 5 is a side elevation of the unit of Figure 4; and Figure 6 is a block diagram of the computer control arrangement for the apparatus of Figure 1.
BEST MODES FOR CARRYING OUT THE INVENTION The illustrated apparatus 10 includes a heater assembly 11 with an elongate hollow tubular carbon furnace 12 (Figures 2 and respective translateable clamp units 14, 16 which are linearly moveable perpendicular to the axis of furnace 12 by lead screw drives 19,21 on respective transverse slideways 15, 17; respective stepper motors 18, operating the lead screw drives 19, 21; fibre drawing units,22, 24; devices 23 for measuring fibre tension; and a clamp rotater 26 associated with clamp unit 14.
Clamp units 14, 16, detailed further below, have respective platens 30, with grooves 31 which, in use of the apparatus, receive and locate a pair of optical fibres 8, 9, when they are extended between and securely held by the clamp units 14, 16, at an initial lateral spacing of 0.5 to 1.0 mm. The fibres are pressed and thereby clamped by hingeable padded plates 33. Clamp unit 14 is rotatable by drive 26 to subsequently twist the fibres about each other, for example, by one turn: clamps 14, 16 and drive 26 thereby constitute mean's to hold the fibres in intimate side-by-side contact. Drive 26 is designed to twist the fibres about each other without twisting the individual fibres, and is also detailed further below.
Drawing units 22, 24 are arranged to
-I*
WO 88/03661 PCT/AU87/00380 uniformly move clamp units 14, 16 oppositely away from each other parallel to the axis of furnace 12 and thereby serve to draw the fibres during the biconical formation step. They are employed to apply tension to the fibres during operation of the apparatus, in conjunction with tension monitoring devices 23 such as strain gauge bridges associated with clamp units 14, 16.
Heater assembly 11 is illustrated in greater detail in Figures 2 and 3. It includes a housing comprised of four principal parts: an annular heat insulating core 44, e.g. of graphite felt, a pair of larger annular electrodes 46, 47, and an outer mounting ring 48. Ring 48 extends about core 44, both being sandwiched between electrodes 46, 47, and is shaped to provide -&-stable pedestal 120 for the assembly (Figure This assembly is maintained by multiple screws 45 fastening the electrodes to ring 48, and the electrodes are wholly electrically insulated from each other, the core and the ring by suitable insulating shims and baffles 43, and by insulating sleeves 43a about screws Housing 40 defines at its centre a cavity 42 which receives furnace 12. The bores of electrodes 46, 47 are inwardly tapered to complement respective concical electrically conductive copper wedges 49 which firmly fix the furnace axially symmetrically in place. Wedges 49 are driven home and retained by end plates 49a held by screws 49b to the electrodes.
Wedges 49 allow for thermal expansion of the furnace during heating.
Carbon furnace 12, a tube of solid and homogeneous graphite, is heated by an electrical current delivered from a suitable power supply 60 via WO 88/03661 PCT/AU87/00380 9 the sheaths of coolant supply conduits 62. The current passes via one electrode 46 through the associated wedge 49, the furnace 12, the other wedge 49 and electrode 47.
The axis of furnace 12 is advantageously horizontal, as illustrated, rather than vertical, to prevent a "chimney" effect and consequent undesirable deposition of particles and other contaminants on the fibres.
The hollow interior cavity 13 of furnace 12 is of axially symmetrical circular cross-section and is laterally open to the space between clamp units 14, 16 by registered co-planar longitudinal slots 51, 52 (Figure 2) respectively in the furnace, in insulating core 44, and in the outer mounting ring 48. Cavity 13 is furthermore open ended and registers with apertures in end plates 49a so that there is a clear axial line of sight through the heater assembly.
Furnace 12 has a temperaturo profile in its internal cavity 13 that is substantially both axially symmetrical and longitudinally symmetrical about a centre point. The preferred temperature profile of the hollow interior.exhibits a single peak, uniform temperature zone in the centre region of the furnace with steep downward gradients within a defined region greater than the centre region. Further detail is disclosed in applicant's co-pending international patent application PCT/AU87/003i7. The steepness of the gradients may be further enhanced by locating laterally slotted graphite plugs 65 in the bore of the furnace.
Assembly 11 has a transverse bore 66 to locate a pyrometer 110 (Figure 2) to monitor the WO 88/03661 PCT/AU87/00380 temperature of the fibres in furnace 12, as well as a duct 68 and port 69 for admitting a gas, for example an inert gas such as nitrogen, to cavity 42 and to the interior cavity 13 of the furnace during the heating and drawing steps. This gas is necessary for optimum operation of the graphite furnace, and may be periodically replaced as described above, by a gas such as methane for pyrolising the interior surface of the furnace. Electrodes 46, 47 are provided with internal coolant tubes, represented at 70, to which coolant is circulated via conduits 62.
Clamp unit 16 is depicted in greater detail in Figures 4 and 5. A pair of platens 30, 30' with fibre grooves 31a, 31b are secured to respective mounting blocks 32, 32' by pairs of stainless steel shims 34. Shims 34 are held by cover strips 35 and screws 35a. Shims 34 are in vertical planes and carry the aforementioned strain gauge devices 23.
Limits on the movement of platen 30 are provided by projecting detents 130, 131 on blocks 32, which engage an outstanding lug 132 on the platen, Three hingeable padded steel plates 33, 33' and 33" are provided on platens 30, 30'. The pads 33a are positioned on the undersides of plates 33, 33' and 33" so that they respectively clamp both fibres and the two fibres separately. Plates 33, 33' and 33" are retained against the fibres by magnets 37. Fibre grooves 31a, 31b are V-grooves dimensioned to leave about half the fibre cross-section above the surface of the platen.
Blocks 32, 32' are mounted on a common backplate 38 for sliding movement parallel to the fibre direction. These sliding motions are effected by rotation of finger knobs 39 and are used to WO 88/03661 PCT/AU87/00380 11 individually tension, or adjust the tension of, the respective fibres. The backplate 38 is part of a carriage 72 which is moveable uniformally on a lead screw 74 parallel to the fibres and on lead screw 21 perpendicular to the fibres. Lead screw 74 is driven by a motor 76 and these components thereby constitute drawing unit 24.
In use of the apparatus to fabricate a fused biconical taper fibre optic coupler, a pair of optical fibres 8, 9, for example multi-mode silica fibres of selected length with a germanium-doped core, are first stripped of their coating in respective segments to expose the cladding. The cladding is preferably etched by any suitable well know technique, e.g. immersion in a hydrofluoric acid bath, to reduce the cladding thickness in all or part of these segments. The fibres are then cleaned, for example, in a methanol bath or sponge, and securely held under prescribed substantially identical tension, e.g. 200kPa by clamp units 14, 16 in front of and in line with slot 52.
Stepper motors 18, 20 are then activated to rotate lead screws 19, 21 and thereby move clamps 14, 16 at equal speeds in slideways 15, 17, in the direction indicated by arrow 58, to move the fibres through slots 52, 51, 50 to the centre of furnace cavity 13. This position is shown by dot-dash lines in Figure 1: the centre of the fibre segments should desirably be at the centre of the longitudinal temperature profile of the furnace cavity.
The furnace is now activated and heat is applied to the etched segments to raise their temperature sufficiently to soften the segments and thereby substantially relieve the tension in the
I
disposing two or more segments of optical fibre under longitudinal tension; preheating said tensioned fibre segments to tension, continuously monitored by strain gauge devices 23, falls substantially to zero.
At zero fibre tension, the heater is disabled and the fibre segments allowed to cool to a predetermined lower temperature, monitored by WO 88/03661 PCT/AU87/00380 pysegments by inelastic stretching of the segments are The tensionmperatre is increased until the longitudinal tensioning, c ontinuously monitored by sting drain gaugenits 22,devices 23, falls substanti about eah other in intimate side-by-side contact by operating rotater 26.
The twisted contacted segments were then hea Ad t azero fibre tension, the hmperature sufficient to cdisabled and the fibre segments t o soften and fuseto cool to a togpredetermined lowaer temperature, monitored bya fusion Spyrometer of, e0. Thereafter th e segments arature re-tensioned to a value s imilar of 16 to the mfirst tensiong by temporarily activating drawby monitoring units 22, 24, and lightly twi sted about each other inexample 0.4, of it inimate side-by-sidal value the tact by operating rotater 26.gments is thereafter tised contacted segments wer e thene heated for a second timabove to a temperature suffiient tension fell to 0,4 of its initial value.
Drawing units 22, 24 are activated during to causion step to drawe the fibre segments to softe in oppand fuse directions at a relatively slow rate, for example 1 to mmgether in manner well known per se, over a fusion l ength of, about 1 cm. Thude temperatureical fibrequired is in excess of 1600suC. The maximumrnace cavity heating temperature is determined by monitoring fibre lf tension. When the tension falls to, for example 0.4, of its initial value, the temperature of the segments 13 thereafter raised by a fur ther number ofgauge degrees, 3 afor exmployed to ensurabove their temperature ibrwhen tension tension fell to 0.4 of its initial value Drawing unis p, ligh24 are activated duringably the fusion step to draw the fibres in opposite directions at a relatively slow rate, for example 1 to 4 mm per minute with a 1 cm fusion length, to i minimise sag sufficiently to preclude the optical p fibres from contacting the surface of furnace cavity 13 or other adjacent features. Strain gauge devices 23 are employed to ensure that adequate fibre tension is maintained.
During this process, light is preferably WO 88/03661 PCT/AU87/00380 13 being transmitted through one of the optical fibres from one end, and monitored at the other end of each fibre. It is then possible to continuously monitor the coupling factor and excess power loss. When the coupling factor is observed to reach, for example about fusion is deemed to be complete and the drawing rate is increased substantially, for example to 7 or 8 mm per minute: this is effective to cause the fused fibres to develop a biconical taper in the known fashion. Heating and drawing are stopped in a controlled fashion in order to achieve the desired coupling factor. Typically the waist of the coupler will be 30 microns wide for original etched fibres of diameter 80 to 90 microns each. During the faster draw, it may be desirable to lower the furnace temperature., The biconical taper coupler can now -bepackaged and/or encapsulated in accordance with techniques known per se to render it resistant to hostile environments, as well as robust and shock resistant.
Figure 6 is a block diagram of a computer-controilled arrangement for carrying out the above steps wholly automatically once the fibres are clamped in place. A particular task for the computer is to apply the different heating stages which are a notable preferred feature of the invention.
Claims (17)
1. A method of fabricating a fused fibre optic coupler, comprising: pretreating respective segments of optical fibre to relieve torsional stress therein for a predetermined time period; and heating for a second predetermined time period said pretreated segments while in intimate side-by-side contact to a temperature sufficient to cause the fibre segments to fuse together, wherein said first predetermined time period precedes said second predetermined time period.
2. A method of fabricating a fused fibre optic coupler, comprising: disposing two or more segments of optical fibre under longitudinal tension; preheating said tensioned fibre segments to a temperature sufficient to soften the segments and thereby substantially relieve said tension by inelastic stretching of the segments; and after the segments have cooled, re-tensioning the segments and heating them while in intimate side-by-side contact to a temperature sufficient to cause the fibre segments to fuse together.
3. A method according to claim 2 wherein the longitudinal tension in the fibres is continuously or periodically monitored to detect when the tension falls substantially to zero during the preheating, whereupon the preheating is terminated and the fibre segments allowed to cool.
4. A method according to claim 2 or 3 wherein the optical fibre segments are brought into said intimate contact by being twisted about each other.
L -v WO 88/03661 PCT/AU87/00380 A method according to claim 2, 3 or 4 for fabricating a fused biconical taper fibre optic coupler, further comprising longitudinally drawing the heated fibres during said heating step to cause each fused fibre to develop a biconical taper.
6. -A method according to any one of claims 1 to S further comprising; during said hea ting monitoring the longitudinal tension and temperature of each of said segments, directly or indirectly, and when the tension in the segments falls to a predetermined threshold value, thereafter continuing to raise the temperature of the segments a -predetermined number of degrees above their temperature when their tension fell to said threshold value, to a temperature sufficient to cause the fibre segments to fuse together.
7. A method according to claim 6 for fabricating a fused biconical taper fibre optic coupler, comprising: thereafter holding or reducing the temperature of the segments, for example to that at the predetermined tension threshold, and then longitudinally drawing~the heated fibres to cause each of the fused fibres to develop a biconical taper and thereby form the coupler.
8. A method of fabricating a fused fibre optic coupler, comprising: j heating two or more initially tensioned segments of optical fibre while these segments are in 4-4!-'\side-by-side contact; monitoring the longitudinal tension and -temperature of each of said segments, directly or indirectl~y, and 16 when the tension in the segments falls to a predetermined threshold value, thereafter continuing to raise the temperature of the segments a predetermined number of degrees above their temperature when their tension fell to said threshold value, to a temperature sufficient to cause the fibre segments to fuse together.
9. A method according to claim 8 for fabricating a fused biconical taper fibre optic coupler, comprising: thereafter holding or reducing the to.: temperature of the segments, for example to that at the predetermined tension threshold, and then longitudinally drawing the heated fibres to cause .i each of the fused fibres to develop a biconical taper and thereby form the coupler.
A method according to claim 8 or 9 wherein the optical fibre segments are brought into said intimate contact by being twisted about each other.
11. Apparatus for fabricating a fused fibre Roof optic coupler, comprising: retaining means for disposing two or more segments of optical fibre under longitudinal tension; means for heating said tensioned fibre segments; and control means operably connected to said heating B means and said retaining means and arranged to activate said B0. heating means and said retaining means to preheat said tensioned fibre segments to a temperature sufficient to soften the segments and thereby substantially relieve said tension by inelastic stretching of the segments, and, after the segments have cooled, to re-tension the segments and heat them while in intimate side-by-side contact to a temperature sufficient to cause the fibre segments to means and said retaining means and arranged to activate said heating means and said retaining means to preheat i WO 88/03661 PCT/AU87/00380 17 fuse together.
12. Apparatus according to claim 11 further comprising means for monitoring the longitudinal tension in the fibres, said control means being responsive to the detection of a fall in the tension substantially to zero during said preheating, to terminate said preheating and allow the fibre segments to cool.
13. Apparatus according to claim 11 or 12 further comprising: means for longitudinally drawing the heated fibres during said heating step to cause each fused fibre to develop a biconical taper.
14. Apparatus according to claims 11, 12 or 13 wherein said control means is a programmed computer control means.
Apparatus for fabricating a fused fibre optic coupler, comprising: means for disposing two or more segments of- optical fibre under longitudinal tension; means for heating said tensioned fibre segments; means for monitoring the longitudinal tension and temperature of each of said segments, directly or indirectly; and control means responsive to said monitoring means and controlling said heating means which control means is arranged whereby, when the tension in the segments falls to a predetermined threshold value, the heating means continues to raise the temperature of the segments a predetermined number of degrees above their temperature when their tension falls to said threshold value, to a temperature sufficient to cause the fibre segments to fuse results in improvea reiiaoDiity or tne metnoa in rl I I I* WO 88/03661 PCT/AU87/00380 18 together.
16. Apparatus according to claim 15 further comprising means for longitudinally drawing the heated fibres during said heating step to cause each fused fibre to develop a biconical taper.
17. Apparatus according to claims 15 or 16 wherein said control means is a programmed computer control means.