AU2006203172A1 - Matrix for sustained, invariant and independent release of active compounds - Google Patents
Matrix for sustained, invariant and independent release of active compounds Download PDFInfo
- Publication number
- AU2006203172A1 AU2006203172A1 AU2006203172A AU2006203172A AU2006203172A1 AU 2006203172 A1 AU2006203172 A1 AU 2006203172A1 AU 2006203172 A AU2006203172 A AU 2006203172A AU 2006203172 A AU2006203172 A AU 2006203172A AU 2006203172 A1 AU2006203172 A1 AU 2006203172A1
- Authority
- AU
- Australia
- Prior art keywords
- naloxone
- release
- matrix
- oxycodone
- pharmaceutical formulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Description
S&FRef: 691751D1
AUSTRALIA
PATENTS ACT 1990 COMPLETE SPECIFICATION FOR A STANDARD PATENT Name and Address of Applicant: Actual Inventor(s): Address for Service: Invention Title: EURO-CELTIQUE of 122, Boulevard de la Petrusse, 2330, Luxembourg, Luxembourg Bianca Brogmann Silke Muhlau Christof Spitzley Spruson Ferguson St Martins Tower Level 31 Market Street Sydney NSW 2000 (CCN 3710000177) Matrix for sustained, invariant and independent release of active compounds The following statement is a full description of this invention, including the best method of performing it known to me/us:- 5845c CI Matrix for Sustained, Invariant and Independent Release of Active Compounds The invention concerns a storage stable pharmaceutical formulation comprising at least one pharmaceutically active compound in a substantially non-swellable diffusion matrix, wherein the compound is released from the matrix in a sustained and invariant, and where several compounds are present, an independent manner.
IND With respect to its essential release characteristics the matrix is formed by amounts of ethylcellulose and at least one fatty alcohol.
The invention also concerns a method for producing storage stable pharmaceutical formulations comprising at least one pharmaceutically active compound in a nonswellable diffusion matrix, wherein the at least one compound is released from the matrix in a sustained and invariant manner and, where several compounds are present, also an independent manner.
Sustained release formulations of pharmaceutical preparations take a central role in the development of improved therapies. It is the intent of all sustained release preparations to provide a longer period of pharmacological response after the administration of the drug than is ordinarily experienced after the administration of rapid release dosage forms. Sustained release pharmaceutical preparations comprising relatively large amounts of the pharmaceutically active compound and that release the compounds in a controlled, regulated manner over a longer period of time (typically 2-16 hours), ensure that the frequency with which the medicine has to be taken by the patient is reduced and that higher compliance by the patients is achieved.
The longer release duration and the concomitant prolonged effect of the active compounds, as is ensured by sustained release pharmaceutical preparations, provides moreover for many therapeutic benefits that are not achieved with corresponding short-acting, immediate release preparations. By using sustained release pharmaceutical preparations, therapy may be continued e.g. overnight without the necessity to interrupt the patient's sleep. This plays a role, for instance, in the -2treatment of epilepsy patients, where the occurrence of nocturnal attacks may thus be prevented. In the same way, patients suffering from chronic pain are allowed undisturbed sleep.
5 From the medical-pharmacological point of view, one advantage of sustained release Sformulations is the very uniform active compound concentration in the blood, C1 leading to a long-lasting effect and reduced side effects. The reduction of side effects plays a decisive role during, e.g. the use of opioids for pain therapy. Opioidinduced side-effects comprise among others the danger of an addiction developing.
As the addictive potential of an active compound is not defined by the compound itself, but rather by the way it is administered and the pharmaco-dynamic resulting therefrom by the rate at which the brain encounters an active compound), the sustained release of an opioid analgesic can reduce the addictive potential of these active compounds (Nolte, STK-Zeitschrift ftr angewandte Schmerztherapie, 2001, Vol. 2).
Since sustained release formulations allow for a uniformly high active compound concentration in the blood, the bio-availability of the active compound is increased.
A multitude of factors contribute to the bio-availability of an active compound. Such factors include the active compound concentration in the respective physiological fluid in the blood), the absorbability of the active compound across membranes for the re-absorption in the gastro-intestinal system) and the availability of the active compound at the desired tissue site.
In order to be absorbed, for instance by the intestinal system, an active compound must be in solution. The time required for a given proportion of an active compound present in a unit dosage of a pharmaceutical preparation in order to be dissolved in the respective physiological fluid, is designated as the dissolution time, also as the release time, or release rate. The dissolution time of an active compound is determined as the proportion of the active compound released from a unit dosage -3form over a specified time based on a test method conducted under standardized conditions. The physiological fluid in which the dissolution time of the active compound is determined may be, e.g. the fluid of the gastro-intestinal system. The O state of the art recognises may satisfactory test procedures for measuring dissolution 5 time for pharmaceutical compositions (and correspondingly, for the release rates of §the active compounds), and these test procedures are described in official compendia worldwide.
Among the various factors affecting dissolution time of pharmaceutical compositions, and thereby the release rates of active compounds, are the surface area of the pharmaceutical composition accessible to the dissolution solvent medium, the pH of the dissolution solvent medium, the solubility of the active compound in the dissolution solvent medium and the saturation concentration of dissolved materials in the dissolution solvent medium.
Despite the diverse factors that influence the dissolution of the active compound in the dissolution medium as well as the absorption of the active compound, a strong correlation has been established between the in vitro dissolution time determined for a pharmaceutical preparation and the in vivo bio-availability of the active compound.
This correlation is so well established that the dissolution time (release rate of the active compound) is considered to be a generally accepted criterion for the bioavailability of the active compound of a pharmaceutical preparation. In view of this correlation, it becomes clear that the release rate as determined for the active compound of a pharmaceutical formulation is one of the important fundamental characteristics that has to be considered when evaluating sustained release formulations.
Different approaches are known from the prior art that allow the formulation of sustained release pharmaceutical preparations. These approaches have in common that the active compound is combined with additives to shape bodies, such as tablets -4or dragdes, with the additives forming a release or dissolution barrier for the active compound. Depending on the nature of the release barriers, different sustained release methods can be distinguished. There are, e.g. osmotic systems, systems by which retardation is achieved through coatings, or systems in which the active compounds are embedded in waxes, polymethacrylates, gel-formers or silicic acids.
OThere are moreover the so-called matrix forms, which are of fundamental importance when formulating sustained release pharmaceutical preparations. Matrix means a shaped body comprising the active compound bound to additives which are as inert as possible. Depending on the type of matrix, one can differentiate between e.g.
swellable or non-swellable matrices. Moreover matrices differ depending on whether the active compound is released by pure diffusion or by erosion of the matrix SchOffling, Arzneiformenlehre, 1998, 3 rd edition, Deutscher Apotheker- Verlag, Stuttgart).
The additives used for the preparation of sustained release pharmaceutical preparations frequently lead to problems concerning the stability of the pharmaceutical preparation after prolonged storage times. For e.g. waxes, it has been shown that they are subject to changes, so that extensive precautionary steps have to be taken even at the time of production, in order to prevent changes during the storage time. If film coatings consisting of polymers produced from aqueous dispersions are used for retardation, these pharmaceutical preparations also frequently display problems with storage stability.
There are prior art sustained release pharmaceutical preparations having so-called controlled release of the pharmaceutically active compound, i.e. the release of the active compound is not only prolonged, but moreover can be adjusted to a predetermined release rate. Depending on which polymers (hydroxyalkylcelluloses, polymethacrylates or e.g. alkylcelluloses) are used for the production of e.g. matrixbased sustained release pharmaceutical preparations with controlled release, the release behaviour of the respective pharmaceutically active compounds may differ, the release behaviour of the active compound frequently being difficult to predict.
Generally, it should be ensured that pharmaceutical preparations of a given pharmaceutical formulation release the respective compound always with reproducible equal release rates or release profiles, even if the formulation comprises different absolute amounts of the active compounds. However, due to the stability problems, which are caused by the components responsible for the sustained release, this is not guaranteed.
There is a large number of sustained release pharmaceutical preparations for different therapeutic applications that frequently contain only one active compound. The medicament Oxygesic®, which is used in pain therapy, contains e.g. oxycodone as the only analgetically active compound. The medicament Kapanol®, which is also used in pain therapy, comprises morphine sulfate as analgetically active compound.
As the long term application opioid analgesics such as oxycodone may go along with the development of side effects such as breath depression and obstipation, cotreatment of patients with opioid antagonists that specifically counteract the opioidinduced side effects may be necessary. If patients seeking pain release are treated with preparations comprising an opioid analgesic, simultaneous treatment with preparations comprising antagonists such as naltrexone or naloxone may be desirable in order to counteract the aforementioned side effects. If the opioid-containing preparation is a sustained release preparation, the antagonist-preparation should also provide for a sustained release as otherwise development of side effects may not effectively be repressed. However, sustained release formulations of e.g. naloxone alone are not available on the market.
In the treatment of different symptoms it is therefore a common strategy to counteract the side-effects provoked by an active compound by simultaneous administration of another compound that selectively reduces these side-effects. If e.g. opioid analgesics are used in pain therapy, side-effects such as obstipation and C<1 breath depression may occur in addition to the danger of the development of dependency and addiction as already mentioned. Various attempts have therefore 0 71 5 been made to eliminate, or at least significantly reduce, the addictive and habit-
IND
0forming potential of opioid analgesics as well as their other side-effects, by the N"1 simultaneous administration of antagonists which counteract the opioid analgesic.
In view of the significant advantages that such combination preparations have and due to the aforementioned general advantages of sustained release pharmaceutical preparations, there is a great need for sustained release formulations of such combination preparations. Sustained release formulations of combination preparations should combine in an ideal manner the positive, synergistic effects of the different active compounds with the long-lasting release and the correspondingly increased period of effectiveness.
One example of such a combination preparation which releases several compounds in a sustained manner is Valoron® from Gidecke, which comprises tilidine as an analgetically active compound and naloxone as antagonist.
However, one problem that frequently occurs with combination preparations is that active compounds of different chemical structures and physical characteristics have to be combined in one matrix. Such a combination usually leads to different release profiles for both compounds. The release of both compounds with the same release profiles can, however, be highly desirable from a medical point of view. Moreover, it may be preferable that both compounds are released from the same matrix, since in this way e.g. tablets may be produced which can be split. Such tablets are suitable for individual dosing and the production process of the corresponding preparations can be significantly simplified. Another aspect is that with several compounds of different structures being present, the compounds may differ with respect to their -7stability in the matrix over a longer storage period. Additionally, the change of amount of one compound may change the release profile of other compounds in an unpredictable manner in such combination preparations, resulting in significant expenditure in the production of preparations having different amounts of the active compounds, since one cannot infer from the release behaviour of one preparation the release behaviour of another one.
Generally, medicaments have to be formulated in a such a way that the active compounds are stable as long as possible under standard storage conditions.
Medicaments also have to be formulation in such a way that the intended release profiles of the active compounds do not change during long-term storage.
It should also be ensured that the release profile of one active compound of a given sustained release formulation does not change depending on the amount of the active compound. This applies to the case where a single compound or also several compounds are present in the pharmaceutical preparation.
Additionally (also in the case of active compound combinations), the release profile of each single compound should be selectable as required. The measures to be taken in order to achieve this should not prevent, or even hamper the release profiles of additional active compounds, e.g. in the case of combinations of different active compounds, being chosen as required. Consequently, there should be no mutual dependency of the release profiles.
For a variety of therapeutic applications there is a great need for combination preparations. Particularly for pain therapy combination preparations are required that consist of opioid analgesics and corresponding antagonists, where the respective pharmaceutical preparations release both compounds in a sustained manner and also possess the aforementioned characteristics. Matrix formulations that ensure a sustained release of active compounds in general and of opioid analgesics and their -8antagonists in particular and that possess the aforementioned characteristics are not known from prior art.
c-I 0C German patent application DE 43 25 465 Al concerns the treatment of side-effects NC 5 during pain therapy by a preparation consisting of an opioid agonist and an Santagonist. The characterizing feature of this disclosure is that the antagonist must not be released in a sustained manner while the agonist should be released in a sustained manner.
International patent application WO 99/32120 is also concerned with a preparation consisting of an opioid analgesic and an antagonist. According to this disclosure, both compounds should be released in a sustained manner. Storage stability and the mutual dependency of the release profiles of compounds is, however, not subject matter of this application.
The aforementioned pain-relief medicament Valoron is a tilidine/naloxonecombination. According to the manufacturer's data it is a formulation from which both active compounds are released in a sustained manner. The matrix used comprises a relevant part of water-swellable material (hydroxypropylmethylcellulose (HPMC)) and has therefore to be considered as a swellable (and possibly partially erosive) diffusion matrix. The disadvantage of this known formulation is that tilidine and naloxone, given identical mass ratios but different absolute amounts, display different release profiles, if the release is measured for certain pH values. The release rates of the agonist and the antagonist are not independent of each other, which is probably due to the sustained release formulation used. Accordingly, it is necessary for the physician to carry out extensive titration experiments for each individual patient if he wants to increase the dosage, even though he does not change the mass ratio of tilidine:naloxone, since he cannot assume that the release profiles of both components will remain constant. The range of therapeutically usable amounts of the analgesic available to the physician is therefore limited.
One objective of the present invention is to provide formulations for a pharmaceutical preparation that ensure that the active compounds of the preparations are released in a sustained manner, that are stable over a long storage period, and where the release of one compound does not change even when different amounts of the active compound are used. A further objective of the invention is to provide formulations for pharmaceutical preparations that display the above-mentioned characteristics and that show no mutual dependency of the release profiles of the active compounds.
Another objective of the present invention is to provide methods for producing pharmaceutical formulations comprising at least one pharmaceutically active compound and from which the compounds are released in a sustained, reproducibly invariant and, where several compounds are present, independent manner. Such formulations should remain stable even after longer storage periods.
A particular objective of the present invention is to provide formulations for pharmaceutical preparations that comprise the opioid antagonist naloxone, wherein the active compound is stable over a long storage time and is released from the preparation in a sustained and reproducibly invariant manner. Formulations that achieve this, are not known from prior art.
An additional objective of the present invention is to provide formulations for pharmaceutical preparations for pain therapy comprising at least one opioid analgesic and at least one antagonist counteracting the opioid analgesic, wherein the formulation is stable over a long storage period and wherein the active compounds are released from the preparation independently of each other in a sustained and reproducibly invariant manner.
The features of the independent claims serve to attain these and further objectives which can be noted from the following description of the invention. Preferred
C-I
embodiments of the invention are defined in the dependent claims.
0 C 5 According to the invention the objectives are solved by providing a pharmaceutical 0 formulation comprising at least one pharmaceutically active compound in a substantially non-swellable diffusion matrix, wherein the matrix is formed with respect to its essential release characteristics by ethylcellulose and at least one fatty alcohol.
It has surprisingly been found that only formulations having a (substantially) nonswellable diffusion matrix based on ethylcellulose and at least one fatty alcohol ensure a sustained, invariant and, if several active compounds are present, independent release of the active compounds.
The inventive matrix formulation which is stable over long storage periods permanently ensures that the active compounds are always released in predetermined percentages and that the release rates do not influence each other. For combination preparations that e.g. comprise opioid analgesics and the respective antagonists, abuse of the medicaments, which presupposes that the agonist can be selectively extracted from the formulation, is prevented.
The formulation according to the invention disables selective extraction of the agonist from the preparation without the corresponding amount of the antagonist,.
regardless of the absolute and relative amount of agonist and antagonist chosen.
Furthermore, such preparations reduce side-effects which usually occur during the application of opioids. Since the active compounds are released from the same matrix, a simplified and more efficient production process is made possible. This also applies for combination preparations comprising other compounds other than opioids analgesics or antagonists thereof.
11 Moreover, the inventive formulation of a medicament ensures that given identical Srelative amounts, the active compounds show the same release profiles regardless of the absolute amount present. Such independent release behaviour provides the N 5 physician with a wide range of usable absolute amounts of the active compounds, where the optimal compound ratio for opioid agonist/antagonist ratios) is known. It is thus possible to comfortably adjust the dosage for each individual patient, either by increasing the dosage gradually or, if necessary, by reducing the dosage gradually. This ability to adjust the dosage for the individual patient is extremely useful from a medical point of view, as is the increased compliance.
The inventive formulations also allow for the production of pharmaceutical preparations that release active compounds of different structures with the same release profiles.
Since the pre-determinable release of active compounds from the inventive formulation does not change regardless of the amount and the number of compounds and takes place from the same matrix, once a combination of active compounds has been established preparations with different amounts of active compound can be produced without significant technical effort and corresponding preparations for different therapeutically relevant areas may be provided.
The characterizing features of the present invention are the sustained, invariant, and if several active compounds are present, independent release of the active compounds from a non-swellable (at least not to an extent which is relevant for the release) diffusion matrix with the matrix being determined with respect to its essential release characteristics by ethylcellulose and at least one fatty alcohol and the active compounds remaining stable over long storage periods.
-12- 11 14According to the present invention "sustained" or "controlled sustained release" or N "retardation" means that pharmaceutically active substances are released from a medicament over a longer period of time than is the case with known formulations for immediate release. Preferably, the release takes place over a time period of two to twenty-four hours, of two to twenty hours, especially preferably over a time period of two to sixteen hours or two to twelve hours, with the specifications satisfying legal c-I requirements.
In the context of the present invention, "sustained release" does not mean that the active compounds are released from the formulation or the medicament in a pHdependent manner. According to the invention, the term "sustained release"! refers to the release of active compounds from a medicament over an extended period of time.
It does not imply the controlled release at a defined place; it therefore does not mean that the active compounds are either released only in the stomach, or only in the intestine. Correspondingly, the release of the active compounds from the inventive formulations occurs preferably pH-independently.
(Of course, a pH dependent release at a defined place could individually be achieved by, e.g. enteric coating of the medicament, although this presently seems not to be advantageous).
According to the invention, "independent release" means that, given the presence of at least two active compounds, a change of the absolute amount of one compound does not influence the release profiles of the other compounds so that the release profiles of the other compounds are not changed. For formulations according to the invention such an independent release behaviour is independent of the pH value, for which the release is measured, or of the production process. The pH independency particularly applies to the acidic range, i.e. for pH values 7. The release profile (or release behaviour) is defined as the change of the release of the active compound from the formulation with time, with the amount of each active compound released -13provided in percents of the total amount of the active compound. The release profile N,1 is determined by known tests.
Specifically, this means that for example the release profile of oxycodone, as it is ID 5 observed for an oxycodone/naloxone-combination with 12 milligrams oxycodone and 4 milligrams naloxone, does not change, if a corresponding preparation with the same formulation contains 12 milligrams oxycodone, but 6 milligrams naloxone.
The independent release feature preferably refers to the situation where preparations of substantially equal composition are compared for the release profile. Preparations of substantially equal composition have different amounts of the active compounds but are otherwise basically the same with respect the components of the composition which essentially influence the release behaviour.
If e.g. the above-mentioned preparations are compared (with the first preparation comprising 12 mg oxycodone and 4 mg naloxone and the second preparation comprising 12 mg oxycodone and 6 mg naloxone) both preparations, provided that they have the same total weight, will provide for the same release profile for oxycodone and naloxone if the difference in the naloxone amount is replaced by a component in the formulation that typically does not influence the release behaviour.
As shown in the Example section, the difference in the amount of naloxone may be replaced by a typical pharmaceutically inert filler such as lactose without changing the release profiles.
The person skilled in the art is well aware that if the amount of the active compound in which two preparations differ is replaced by a substance that is essential for the release behaviour of the formulation, such as ethylcellulose or a fatty alcohol, differences in the release behaviour may occur. Thus, the independent release feature preferably applies to formulations that have different amounts of the active compounds but are otherwise identical or at least highly similar with respect to the -14components that essentially influence the release behaviour (given that formulations N of the same total weight are compared).
According to the invention, "invariant release behaviour" or "invariant release profile" is defined so that the percentage of the absolute amount of each active compound released per time unit does not significantly change and remains sufficiently constant (and thus does not substantially change) if absolute amounts are changed. Sufficiently constant percentages mean that the percentage released per time unit deviates from a mean value by not more than 20%, preferably by not more than 15% and especially preferably by not more than 10%. The mean value is calculated from six measurements of the release profile. Of course, the amount released per time unit has to satisfy the legal and regulatory requirements.
Specifically, this means for example that given an oxycodone/naloxone combination of 12 mg oxycodone and 4 mg naloxone, during the first 4 hours 25% oxycodone and naloxone are released. If the oxycodone/naloxone combination instead contains 24 mg oxycodone and 8 mg naloxone, during the first 4 hours also 25% oxycodone and 20% naloxone will be released. In both cases the deviation will not be more than from the mean value (which in this case is 25% oxycodone and 20% naloxone).
As outlined for the independent release behaviour, the invariant release feature also preferably refers to a situation where preparations of substantially equal composition are compared. Such preparation differ with respect to the amount of the active compounds, but are of the same or at least highly similar composition with respect to the release-influencing components of the preparation. Typically, the difference in the amount of an active compound will be replaced by the amount of a pharmaceutical inert excipient which does not substantially influence the release behaviour of the preparation. Such a pharmaceutical excipient may be lactose, which is a typical filler in pharmaceutical preparations. The person skilled in the art is well aware that the invariant release feature may not apply to preparations where the difference in the amount of an active compound is replaced by substances that are N, known to essentially influence the release behaviour of the preparation, such as ethylcellulose or fatty alcohols.
ID 5 In the Example section it is set out that if one preparation comprises 20 mg oxycodone and 1 mg naloxone or 20 mg oxycodone and 10 mg naloxone, with the difference in naloxone being replaced by lactose, that the two preparations of identical weight provide for the same release profiles, so that they exhibit a sustained, invariant and independent release behaviour.
According to the invention "storage stable" or "storage stability" means that upon storage under standard conditions (at least two years at room temperature and usual humidity) the amounts of the active compounds of a medicament formulation do not deviate from the initial amounts by more than the values given in the specification or the guidelines of the common Pharmacopoeias. According to the invention, storage stability also means that a preparation produced according to the invention can be stored under standard conditions (60% relative humidity, 25 0 C) as it is required for admission to the market.
According to the invention, "storage stable" or "time stable" also means that after storage under standard conditions the active compounds show release profiles as they would upon immediate use without storage. According to the invention, the admissible fluctuations with respect to the release profile are characterized in that the amount released per time unit fluctuates by no more than 20%, preferably no more than 15% and especially preferably no more than 10 with respect to a mean value.
The mean value is calculated from six measurements of the release profile.
The term "storage stable" refers to the active compound as well as to the other components within the inventive formulation and therefore also to the formulation as a whole.
-16- Preferably, the release of the active compounds from a sustained release formulation is determined by the Basket Method according to USP at pH 1.2 or pH 6.5 with mC HPLC.
N SStorage stability is preferably determined by the Basket Method according to USP at N pH 1.2 with HPLC.
According to the invention, the term "formulation" refers to the preparation of a pharmaceutically active substance with additives (formulation aids) with the aim of enabling an optimal release, distribution and development of activity of the active compound for the respective applications.
According to the invention, a "non-swellable" or "substantially non-swellable" diffusion matrix is a matrix formulation for which the release of the active compounds is not influenced (or at least not to a relevant degree) by swelling of the matrix (particularly in the physiological fluids of the relevant target sites in the patient's body).
According to the invention, the term "substantially non-swellable" diffusion matrix also refers to a matrix whose volume will increase by approximately 300%, preferably by approximately 200%, more preferably by approximately 100%, by approximately 75% or by approximately 50%, even more preferably by approximately 30% or by approximately 20% and most preferably by approximately 15%, by approximately 10%, by approximately 5% or by approximately 1% in aqueous solutions (and particularly in the physiological fluids of the relevant target sites in the patient's body).
It has now surprisingly been found that formulations for medicaments with a substantially non-swellable diffusion matrix allow for a sustained, invariant and, 17where several compounds are present, independent release of the active compounds, when the diffusion matrix comprises ethylcellulose as the matrix-scaffold-forming substance and is moreover determined with respect to its essential release characteristics by ethylcellulose and/or at least one fatty alcohol. Additionally, such N' 5 formulations are characterized by good storage stability. Given the present knowledge, mainly formulations with such a diffusion matrix allow to release the active compounds in the aforementioned inventive manner. Formulations with a (substantially) swellable diffusion matrix or an erosive matrix are currently not considered to be suitable for that.
Therefore, water-swellable substances and particularly water-soluble polymers may generally not be used as scaffold-forming substances for the production of matrices for formulations in accordance with the invention. Particularly, common matrixforming polymers such as polyvinylpyrridone, hydroxypropylcellulose, hydroxypropylmethylcellulose, hydroxyethylcellulose, hydroxymethylcellulose, poly(vinylalcohols), alginates, hydrated hydroxyalkylcellulose and hydroxypropylmethylcelluloseether are currently not considered to be suitable for the production of formulations in according with the invention.
Scaffold-forming substances that can form non-swellable diffusion matrices may be used for the production of formulations in accordance with the invention if they provide for a release behaviour of the active compound in accordance with the invention, i.e. for a sustained, invariant and, where several components are present, independent release, as well as for storage stability of the formulation. Waterinsoluble polymers, that are commonly used for the production of matrix-based sustained release pharmaceutical preparations may also not be used straightforwardly for the production of formulations in accordance with the invention. Common scaffold-forming substances such as acrylic acid and methacrylic acid copolymers, methylmethacrylate copolymers, ethoxyethylmethacrylate copolymers, cyanoethylmetha-crylate, aminoalkylmethacrylate copolymers, poly(acrylic acid), -18poly(methacrylic acid), polymethacrylates, poly(methylmethacrylate) copolymers, polyacrylamine or alginic acid are currently not considered to be suitable for the production of formulations in accordance with the invention.
N 5 Matrices which are based on polymethacrylates (as e.g. Eudragit® RS30D and 0Eudragit@ RL30D) or comprise relevant amounts of water-swellable material, ,1 particularly of hydroxyalkylcellulose such as HPMC will currently not be considered usable in accordance with the invention.
Currently, alkylcelluloses will generally also not be considered for the production of formulations in accordance with the invention. Propylcellulose e.g. is of too lipophilic character to produce matrices with release characteristics in accordance with the invention. Methylcellulose is also not suitable for the formulations in accordance with the invention.
In accordance with the invention, the matrix that ensures the sustained release of the active compound will be selected in such a way that the release of the active compounds takes place in a sustained, invariant and, if several compounds are present, independent manner, and that the formulation is storage stable. Preferably such matrices comprise polymers based on ethylcellulose, with ethylcellulose being an especially preferred polymer. Specifically preferred are matrices comprising polymers available on the market under the trademark Surelease®. Particularly preferred is the use of Surelease@ E-7-7050.
Other retardation methods, such as e.g. film coatings that ensure a sustained release, are currently not considered to be suitable for production of formulations that provide for a release behaviour of the active compounds which is in accordance with the invention. Furthermore, they are not considered to be suitable for production of formulations that ensure that the formulation is storage stable.
-19- For formulations in accordance with the invention which comprise a non-swellable diffusion matrix on an ethylcellulose basis, the amount of ethylcellulose (or Surelease® E-7-7050) in the matrix will vary between 1-15%, preferably between 3- 12%, particularly preferably between 5-9% and even more preferably between 6-8%.
IN 5 The percentages indicating the amount of ethylcellulose (or Surelease®) with respect to the total weight of the preparation.
Formulations in accordance with the preparation preferably comprise a fatty alcohol as the second component which has a sustained release effect besides ethylcellulose.
Fatty alcohols may comprise lauryl, myristyl, stearyl, cetylstearyl, ceryl and/or cetylalcohol. Preferably, stearyl and/or cetylalcohol will be used. The amount of fatty alcohol in the matrix will be between 5-30%, preferably between 10-25% and: particularly preferably between 15-20%. Particularly preferred is an amount of fatty alcohol of substantially 20% (if the matrix is produced by spray granulation) or of substantially 18% (if the matrix is produced by extrusion). All percentages indicating the amount of fatty alcohol refer to the total weight of the preparation.
Formulations with release behaviour according to the invention comprise in particular matrices comprising ethylcellulose and at least one fatty alcohol as the components that essentially influence the release characteristics of the matrix. The amount of ethylcellulose and the at least one fatty alcohol may vary significantly, so that preparations with different release profiles may be achieved. Even though the inventive preparations will usually comprise both of the aforementioned components, in some cases it may be preferred that the preparations comprise only ethylcellulose or the fatty alcohol(s) as the release determining components.
Formulations in accordance with the invention may comprise further components which have a sustained release effect if required. However, it has to be ensured that the release of the active compounds from the formulation and the storage stability of the formulation are in accordance with the invention and are not negatively
I
20 influenced. Such additional components with sustained release effect may comprise polyalkylene glycols and particularly preferably polyethylene glycols.
According to the invention, formulations that provide a release of the active N" 5 compounds in accordance with the invention may comprise, besides the matrix forming polymers, fillers and additional substances, such as granulating aids, C,1 lubricants, dyes, flowing agents and plasticizers.
Lactose, glucose or saccharose, starches and their hydrolysates, microcrystalline cellulose, cellactose, sugar alcohols such as sorbitol or mannitol, poorly soluble calcium salts like calciumhydrogenphosphate, dicalcium- or tricalciumphosphate may be used as fillers.
Povidone may be used as granulating aid.
Highly-disperse silica (Aerosil®), talcum, corn starch, magnesium oxide and magnesium- and/or calcium stearate may preferably be used as flowing agents or lubricants.
Magnesium stearate and/or calcium stearate can preferably be used as lubricants.
Fatty acids like stearic acid, or fats like hydrated castor oil can also preferably be used.
Polyethylene glycols and fatty alcohols like cetyl and/or stearyl alcohol and/ or cetostearyl alcohol can also be used as additional substances that influence retardation.
Other pharmaceutically acceptable excipients which are known in the art, such as surfactants, conserving agents, diluents, granulating aids, colorants, aromatic compounds, detergents, buffers and/or anti-sticking agents may also be comprised in -21the sustained release matrix, if the formulation still provides for a release behaviour in accordance with the invention, i.e. a sustained, invariant and, if several compounds are present, independent release. Such formulations also have to provide good storage stability of the active compounds within the matrix.
N If fillers and additional substances such as dyes and the mentioned lubricants, flowing agents and plasticizers are used, care has to be taken that according to the invention only such combinations together with the matrix forming substance and/or the matrix forming substances are used, which ensure release profiles of the active compounds in accordance with the invention.
All these additional components of the formulations will be chosen in such a way that the release matrix receives the character of a substantially non-water- or nonbuffer-swellable and non-erosive diffusion matrix.
According to the invention, a formulation is especially preferred that comprises ethylcellulose or Surelease® E-7-7050 as a matrix-building substance, stearyl alcohol as fatty alcohol, magnesium stearate as lubricant, lactose as filler and povidone as a granulating aid.
Matrices that are in accordance with the invention can be used to produce preparations that release active compounds in a sustained, independent and invariant manner and that release equal amounts of the active compounds per time unit.
Specifically, this means that in the case of a oxycodone/naloxone combination containing 12 mg oxycodone und 4 mg naloxone, 25% oxycodone and 25% naloxone are released within the first 4 hours. Correspondingly, in the case of a oxycodone/naloxone combination containing 24 mg oxycodone and 8 mg naloxone, oxycodone and 25% naloxone are released during the first 4 hours, with the deviation in both cases being no more than 20% of the mean value (which in this case is 25% oxycodone or naloxone).
22 Such an equal release behaviour for both active compounds may be desirable for medical aspects.
N 5 A preferred embodiment of the invention relates to preparations that release 1% to preferably 5% to 35%, more preferably between 10% and 30% and even more preferably between 15% and 25% of oxycodone and/or naloxone after 15 minutes.
In other preferred embodiments of the invention, 15% to 20%, 20% to approximately 15%, approximately 20% or approximately 25% of oxycodone and/or naloxone are released after 15 minutes.
Another preferred embodiment of the invention relates to preparations that release between 25% to 65%, preferably between 30% to- 60%, more preferably between to 55% and even more preferably between 40% to 50% of oxycodone and/or naloxone after one hour. Preferred embodiments of the invention also relate to preparations that release between 40% to 45%, 45% to 50%, approximately approximately 45% or approximately 50% of oxycodone and/or naloxone after one hour.
Yet another preferred embodiment of the invention relates to preparations that release between 40% to 85%, preferably between 45% to 80%, more preferably between 45% to 75% and even more preferably between 45% to 55%, 50% to to 65%, 65% to 75% or 75% to 85% of oxycodone and/or naloxone after 2 hours. Preferred embodiments also comprise preparations that release approximately 45%, approximately 50%, approximately 55%, approximately 60%, approximately approximately 70%, approximately 75%, approximately 80% or approximately of oxycodone and/or naloxone after 2 hours.
one preferred embodiment of the invention relates to preparations that release to 100%, preferably between 75% to 95%, more preferably between 80% to -23and even more preferably between 80% to 90% of oxycodone and/or naloxone after 4 hours. Preferred embodiments of the invention also relate to preparations that release between 80% to 85%, 85% to 90%, approximately 80%, approximately or approximately 90% of oxcodone and/or naloxone after 4 hours.
N One preferred embodiment of the invention also relates to preparations that release between 65% to 100%, preferably between 75% to 100%, more preferably between to 95% and even more preferably between 80% to 85%, between 85% to or between 90% to 95% of oxycodone and/or naloxone after 7 hours. Preferred embodiments of the invention also relate to preparations that release approximately approximately 85%, approximately 90% or approximately 95% of oxycodone and/or naloxone after 7 hours.
Yet another preferred embodiment of the invention relates to preparations that release between 85% to 100%, preferably between 90% to 100%, more preferably between 95% to 100% and even more preferably approximately 95% or 100% of oxycodone and/or naloxone after 12 hours.
Preparations in accordance with the invention can be produced as all common application forms which, on principle, are suitable for retardation formulations and which ensure that the active compounds are released in a manner in accordance with the invention. Especially suitable are tablets, multi-layer tablets and capsules.
Additional application forms like granules or powders can be used, with only those applications forms being admissible that provide a sufficient retardation and a release behaviour in accordance with the invention.
Pharmaceutical preparations may also comprise film coatings. However, it has to be ensured that the film coatings do not negatively influence the release properties of the active compounds from the matrix and the storage stability of the active compounds within the matrix. Such film coatings may be colored or may comprise a -24 initial dosage of the active compounds if required. The active compounds of this initial dosage will be immediately released so that the therapeutically effective blood plasma level is reached very quickly. It has to be ensured that, by coating the preparations in accordance with the invention, the release behaviour of the active N 5 compounds is not negatively influenced.
The active compounds that are comprised within the formulation in accordance with the invention and which are released in a sustained, invariant and, if several compounds are present, independent manner from the inventive matrix and which are also storage stable within the matrix, are not limited to a special class of compounds.
Pharmaceutically active compounds according to the present invention thus comprise antipyretic, analgesic and anti-inflammatory agents such as indomethacin, aspirin, diclofenac, ibuprofren, antiulcer agents such as sulpiride, coronary vasodilaters such as nifedipine, peripheral vasodilators such as ifenprodil tartrate, antibiotics such as ampicillin, chloramphenicol or erythromycin, synthetic antimicrobial agents such as nalidixic acid, antispasmodic agents such as propantheline bromide, antitussive and antiasthmatic agents such as theophylline or aminophylline, bronchodilators such as diprophylline, diuretics such as furosemide, muscle relaxants such as chlorophenesin carbamate, cerebral metabolism improving agents such meclofenoxate hydrochloride, minor tranquilizers such as oxazolam, diazepam or clotiazepam, major tranquilizers such as sulpiride, beta-blockers such as pindolol, antiarrhythmic agents such as procainamide hydrochloride, anticoagulants such as ticlopidine hydrochloride, antiepileptics such as phenytoin, antihistaminics such as chlorpheniramine maleate, antiemetics such as difenidol hydrochloride, antihypertensive agents such dimethylaminoethyl reserpilinate hydrochloride, sympathomimetic agents such as dihydroergotamine mesilate, expectorants such as bromhexine hydrochloride, oral antidiabetic agents such as glibenclamide, cardiovascular system drugs such as ubidecarenone, iron preparations such as ferrous sulfate, non stearoidal anti-inflammatory drugs or vitamins. Particularly preferred are 25 analgesics comprising the group of opiates and opioids such as oxycodone, c-i morphine, dihydrocodeine, oxymorphine, buprenorphine or trarnadol. Also preferred are analgesic antagonists such as naltrexone or naloxone. Other opioid agonists and antagonists can be found, e.g. in WO 99/32119.
IND Particularly preferred are formulations in accordance with the invention that comprise opioid analgesics (opioid agonists) and/or opioid antagonists as pharmaceutically active compounds.
According to the invention, opioid analgesics or opioid agonists comprise all compounds that belong to class N02A of opioid analgesics according to the ATC Classification of the WHO, and that display an analgesic effect upon application in accordance with the invention. Preferably, an opioid agonist is selected from the.
group of morphine, oxycodone, hydromorphone, propoxyphene, nicomorphine, dihydrocodeine, diarnorphine, papaveretum, codeine, ethylmorphine, phenylpiperidine and derivates thereof, methadone, dextropropoxyphene, buprenorphine, pentazocine, tilidine, tramadol, hydrocodone. Further examples for useable analgesics according to the invention are meperidine, oxymorphone, aiphaprodine, anileridine, dextromoramide, metopone, levorphanol, phenazocine, etoheptazine, propiram, profadol, phenamprornide, thiamnbuten, pholcodeine, codeine, dihydrocodeinon, fentanyl, 3-trans-dimethylamino4-phenyl4-transcarbethoxy-A'-cyclohexen, 3-dimethylaxino-0-(4-methoxyphenyl-carbamnoyl)propiophenone oxime, (-)J3-2'-hydroxy-2, 9-dimethyl-5-phenyl-6, 7-benzomorphane, (-)2'-hydroxy-2-(3-methyl-2-butenyl)-9-methyl-5-phenyl- 6 7-benzomorphane, pirinitramide, (-)oL-5,9-diethyl-2' hydroxy-2-methyl-6, 7-benzomorpbane, ethyl 1 dimnethylaniinoethyl)4,5,6,7-tetrahydro-3-methyl-4-oxo-6-phenyl-indol- 2 carboxylate, I -benzoylmethyl-2, 3-dimethyl-3- (m-hydroxy-phenyl) -piperidine, Nallyl-7c~ (1 -R-hydroxy- 1 -methylbutyl)-6, 1 4endo-ethanotetrahydronororipavifle, )2'-hydroxy-2-methyl-6,7-benzomorpbane, noracylmethadol, phenoperidine, a-dl 26 methadol, a -1-methadol, p-dl-acetylmethadol, a-1-acetylmethadol and 3-1acetylmethadol. These lists are not to be understood as exclusive.
r-- Especially preferred analgesically effective opiod agonists are oxycodone, hydrocodone, hydromorphone, morphine, codeine, dihydrocodeine, methadone, oxymorphone, fentanyl and sufentanyl. Specifically, the opioid agonist is Cl oxycodone.
According to the invention, antagonists comprise such compounds that counteract opioid agonists (as defined earlier). Such compounds can also be found in the ATC Classification of the WHO. According to the invention, compounds are preferred that upon application in accordance with the invention decrease the side effects, the habituation effects and the addictive potential caused by the opioid agonists.
Antagonists can comprise among others, naltrexone, naloxone, nalmefene, nalorphine, nalbuphine, naloxoneazinen, methylnaltrexone, ketylcyclazocine, norbinaltorphimine, naltrindol, 6-B-naloxol and 6-B-naltrexol.
Especially preferred antagonists comprise naltrexone, nalmefene and naloxone.
Specifically preferred as an antagonist is naloxone.
According to the invention, formulations with a combination of oxycodone as agonist and naloxone as antagonist are particularly preferred. The agonist is preferably in excess compared to the antagonist. The excess of the agonist is defined based on the amount of the unit dosage of the antagonist present in the combination preparation. The extent of the excess of the opioid agonist is usually given in terms of the weight ratio of agonist to antagonist.
In the case of oxycodone and naloxone, preferred weight ratios of agonist to antagonist lie within a weight ratio range of 25:1 at maximum, especially preferred are the weight ratio ranges 15:1, 10:1, 5:1,4:1,3:1,2:1 and 1:1.
27 The absolute amounts of agonist and antagonist to be used depend on the choice of the active compounds. According to the invention, care has to be taken that agonist and antagonist are released from the pharmaceutical preparation that has been formulated for sustained release, only in an independent and invariant manner.
If oxycodone and naloxone are used for a combination preparation, preferably between 10 and 150 mg, especially preferably between 10 and 80 mg of oxycodone (typical amounts for use) and preferably between 1 and 50 mg naloxone per unit dosage are used.
In other preferred embodiments of the invention, the preparations may comprise between 5 and 50 mg of oxycodone, between 10 and 40 mg of oxycodone, between and 30 mg of oxycodone or approximately 20 mg of oxycodone. Preferred embodiments of the invention may also comprise preparations with between 1 and mg naloxone, 1 and 30 mg naloxone, 1 and 20 mg naloxone or between 1 and 10 mg naloxone per unit dosage.
According to the invention, the ratio between oxycodone and naloxone has to be chosen in such a way that release profiles for both active substances in accordance with the invention are guaranteed and that the agonist can display its analgesic effect while the amount of the antagonist is chosen in such a way that habituation- or addiction-promoting effects and side effects of the agonist are reduced or abolished, without (substantially) affecting the analgesic effect of the agonist. According to the invention, development of habituation and addiction as well as obstipation and breath depression are to be considered as side effects of analgesically effective opioid agonists.
Even though this might not be expressly stated, the term "agonist" or "antagonist" always comprises pharmaceutical acceptable and equally acting derivatives, salts and 28 the like. If, for example, oxycodone or naloxone is mentioned, this also comprises, N besides the free base, their hydrochloride, sulfate, bisulfate, tatrate, nitrate, citrate, bitratrate, phosphate, malate, maleate, hydrobromide, hydrojodide, fumarate, succinate and the like.
According to the invention, agonists and antagonists are formulated in a way that they are released from the resulting pharmaceutical preparation in a sustained, independent and invariant manner. This does not mean that the antagonist is in excess compared to the agonist. On the contrary, it is preferred that in formulations comprising an agonist/antagonist combination, that show a release profile in accordance with the invention, the agonist is in excess compared to the antagonist.
Preparations produced according to the invention can be applied orally, nasally, rectally and/or by inhalation for use in pain therapy. According to the invention, parenteral application is not envisaged. Especially preferred is a formulation for oral application.
Formulations in accordance with the invention may be produced by embedding the active compound into the matrix by e.g. melting, spray-freezing, spray-drying, granulating, direct tabletting and/or extrusion.
Pharmaceutical preparations or preliminary stages thereof which are in accordance with the invention can be produced by build-up or break-down granulation. A preferred embodiment is the production by spray granulation with subsequent drying of the granules. Another preferred embodiment is the production of granules by build-up granulation in a drum or on a granulating disk. The granules may then be pressed into e.g. tablets using appropriate additional substances and procedures.
The person skilled in the art is familiar with granulating technology as applied to pharmaceutical technology. The embodiment examples (see below) disclose specific -29 embodiments of the invention. However, it is well within the scope of the person 0C skilled in the art to adapt the parameters of the process in order to achieve specific purposes.
D 5 The pharmaceutical formulations in accordance with the invention or precursors Sthereof may be advantageously produced by extrusion (instead of granulation), since several working steps (such as the drying of the granulates during spray-granulation) may be omitted, so that formulations in accordance with the invention may be produced efficiently and with less cost.
As production of formulations in accordance with the invention by extrusion is a continuous process, several working steps can be omitted (in comparison to other production methods, such as spray-granulation), leading to more efficient production of the formulations in accordance with the invention.
For production of formulations in accordance with the invention by extrusion Surelease® E-7-7050, which comprises dibutylsebacat as plasticizer and additional other components may be omitted and ethylcellulose may be directly used, resulting in a cheaper and more efficient production process.
Production of pharmaceutical preparations or preliminary stages thereof, which are in accordance with the invention, by extrusion technology is especially advantageous.
In one preferred embodiment, pharmaceutical preparations or preliminary stages thereof are produced by melt extrusion with co- or counter-rotating extruders comprising two screws. Another preferred embodiment is the production by means of extrusion, with extruders comprising one or more screws. These extruders may also comprise kneading elements.
Extrusion is also a well-established production process in pharmaceutical technology and is well known to the person skilled in the art. The person skilled in the art is well aware that during the extrusion process, various parameters, such as the feeding rate, the screw speed, the heating temperature of the different extruder zones (if available), the water content, etc. may be varied in order to produce products of the desired characteristics. The Example section provides for numerous examples of preparations according to the invention that have been produced by extrusion.
The aforementioned parameters will depend on the specific type of extruder used.
For production of formulations in accordance with the invention, extrusion may be performed with one or multiple screw extruders which may be counter-rotating or co-rotating screws. The feeding rate of the components is dependent on the specific extruder type.
The aforementioned parameters will depend on the specific type of extruder used.
During extrusion the temperature of the heating zones, in which the components of the inventive formulation melt, may be between 40 to 120 preferably between to 100 more preferably between 50 to 90 even more preferably between 50 to 'C and most preferably between 50 to 650 C, particularly if counter-rotating twin screw extruders (such as a Leistritz Micro 18 GOL) are used. The person skilled in the art is well aware that not every heating zone has to be heated. Particularly behind the feeder where the components are mixed, cooling at around 25 *C may be necessary. The screw speed may vary between 100 to 500 revolutions per minute (rpm), preferably between 100 to 250 rpm, more preferably between 100 to 200 rpm and most preferably around 150 rpm, particularly if counter-rotating twin screw extruders (such as a Leistritz Micro 18 001,) are used. The geometry and the diameter of the nozzle may be selected as required. The diameter of the nozzle of commonly used extruders typically is between I to 10 mm, preferably between 2 to 8 mm and most preferably between 3 to 5 mm. The different extruders may differ with respect to their set up and comprise e.g. kneading elements. The ratio of length 31 versus diameter of the screw of extruders that may be used for production of inventive preparations is typically around 40: 1.
Typical screw profiles which may be used in the production of formulations N 5 according to the invention by extrusion are shown in Figures I A and IlB. Extrusion procedures for the production of pharmaceutical preparations which show a sustained release are well known to the person skilled in the art.
In a preferred embodiment, a counter-rotating twin-screw extruder is used for the production of formulations in accordance with the invention. This may be e.g. an extruder of the type M icro 18 GGL (Leisfritz AG, N~irberg, Germany). For this preferred embodiment the extruder has no kneading elements (see also Figure IA).
The feeding rate of the components used for the production of the formulation in accordance with the invention is between 1-3 kg/h, preferably between 1-2 kg/h.
Particularly preferred is a feeding rate of 1.5 kg/h. The temperature of the heating zones is between 40*-120*C, 50 0 -100 0 C, preferably 50'-90*C, more preferably Particularly preferred are 50'-65"C. The extruder provides for 10 heating zones. In the first heating zone the components are generally cooled around The temperature in the other heating zones will then preferably be around 50*-65*C and may vary for every heating zone. The screw speed will be between 1-500 rpm, preferably between 1-250 rpm, more preferably between 120-200 rpm and even more preferably around 150 rpm. The diamneter of the nozzle will be between 1-10 mm, preferably between 2-8 mm, or between 3-5 mm. In a particularly preferred embodiment of the invention, the diameter of the nozzle is approximately 3 mm.
Generally, the temperatures of the heating zones have to be selected such that no temperatures develop that may destroy the pharmaceutically active compounds. The feeding rate und screw speed will be selected such that the pharmaceutically active compounds are released from the preparations produced by extrusion in a sustained, independent and invariant manner and are storage stable in the matrix. If e.g. the -32feeding rate is increased, the screw speed may have to be increased correspondingly to ensure the same retardation.
The person skilled in the art knows that all the aforementioned parameters depend on N 5 the specific production conditions (extruder type, screw geometry, number of components etc.) and may have to be adapted such that the preparations produced by extrusion provide for a sustained, independent and invariant release as well as for the afore-mentioned storage stability. The person skilled in the art knows how to properly adjust the aforementioned parameters The person skilled in the art can infer from the Examples (see below) that by changing the parameters during extrusion and by changing the composition with respect to the compounds.that are substantially responsible for the release behaviour of the preparations, preparations with different release profiles may be obtained.
Thus, the present invention allows to first produce a preparation with a desired release profile for oxycodone and naloxone or naloxone alone by e.g. varying the amount of fatty alcohols or the matrix-forming polymer ethylcellulose as well as production parameters such as temperature, screw speed (during extrusion) or pressure power during tablet production.
Once a preparation with the desired release profile has been obtained, the inventive preparations according to the invention allow the person skilled in the art to change the amounts of the preparations with respect to the active compounds as outlined above. Preparations comprising different amounts of the active compounds but of otherwise substantially equal composition, however, will then provide for the features of sustained, invariant and independent release.
The Example section therefore discloses numerous examples showing that preparations with different release profiles may be obtained by changing the amount of e.g. ethylcellulose. Other examples show that once a preparation has been -33established with desired release profiles, the change in the amount of naloxone will c,1 not influence the release behaviour of such preparations if the difference in the amount of the active compound is replaced by pharmaceutically inert excipients such as lactose.
N The production of formulations in accordance with the invention by extrusion is preferred with the formulations comprising opioid analgesics and opioid antagonists as active compounds. Particularly preferred is the production of formulations in accordance with the invention that comprise oxycodone and naloxone, wherein the preferred weight ratios of agonist to antagonist are within a weight ratio ranging from maximal 25:1, preferably of 20:1, 15:1, 10:1, 5:1, 2:1 and 1:1.
A preferred embodiment of the invention refers to a preparation that comprises the inventive matrix and naloxone as the pharmaceutically active compound. Such preparations may be advantageously used for a variety of different indications.
Preparations according to the invention comprising an opioid antagonist such as naloxone as the pharmaceutically active compound may e.g. be used for complete or partial treatment of opioid-induced side effects. Such side effects may comprise dizziness, breath depression, opioid-abuse, development of tolerance and addiction and particularly obstipation.
Preparations according to the invention which comprise naloxone as a pharmaceutically active compound preferably are used for the treatment of opioidinduced obstipation. Almost 90 of patients under opioid treatment show signs of obstipation which may be responsible for other additional ailments such as discomfort, tension and pain in the abdomen, nausea and emesis, anorexia, haemorrhoids, anal fissures, fecal incontinence, paradoxic diarrhoea, urine retention, intestinal pseudo obstruction, and decubitus of the colon which may lead to -34perforation (Neuenschander et. al. (2002), Palliativmedizin auf einen Blick, Schweizerische Krebsliga).
So far opioid-induced obstipation has been treated by the application of laxatives.
However, application of typical laxatives does not allow for the simultaneous treatment of other opioid-induced side effects The advantage of the use of inventive preparations comprising naloxone is that the inventive preparations allow for a sustained release of the antagonist naloxone. If e.g.
patients in pain are treated simultaneously with opioid analgesics, application of such preparations comprising naloxone will allow for a long term treatment of opioidinduced side effects including obstipation. Particularly, the application of naloxone as a sustained release formulation should allow for an efficient treatment of opioidinduced obstipation. At the same time it is ensured that there is no tolerance development towards opioid analgesics if applied simultaneously. Moreover, the use of naloxone does not lead to any disturbances in the water and electrolyte metabolism and does not induce colon irritation.
The provision of a sustained release formulation comprising naloxone as the only pharmaceutical active agent compound also has the advantage that patients that are treated with opioid analgesics may receive a dosis of naloxone which is sufficient to counteract the opioid-induced side effects without leading to a significant reduce of analgesia. With inventive preparations being available which comprise different amounts of naloxone, one has the possibility to specifically treat patients in need of pain treatment that receive different amounts of opioid agonists or are treated with different opioid agonists Yet another preferred embodiment of the invention relates to the use of inventive preparations comprising naloxone for treatment of opioid-induced pruritus. Opioidinduced puritus is one of the side effects that is experienced by the patients as N- extremely unpleasant.
In another embodiment of the invention, preparations comprising naloxone may also be used for treatment of idiopathic syndromes such as idiopathic pruritus or pruritus due to cholestasia and/or renal dysfunction. These preparations may also be used for the treatment of chronic idiopathic obstipation or irritable bowel syndrome. Thus, preparations in accordance with the invention comprising naloxone as a pharmaceutically active compound may be used for a multitude of therapeutic indications and purposes which may be either opioid-induced or not. As the inventive preparations provide for a sustained and reproducibly invariant release behaviour, they allow for an efficient treatment of the aforementioned syndromes.
In a preferred embodiment preparations in accordance with the invention comprising naloxone as the active compound release 30% to 60 preferably 35% to 55 more preferably 40% to 50 and even more preferably 40% to 45 or 45% to of naloxone after 90 minutes. In another preferred embodiment of the invention, preparations comprising nialoxone release approximately 40 approximately 45 or approximately 50 of the active compound after 90 minutes.
In another preferred embodiment preparations in accordance with the invention comprising naloxone release 30% to 70 preferably 35% to 65 and more preferably between 40% to 60 of naloxone after 120 minutes. In yet another embodiment of the invention, preparations comprising naloxone release preferably between 3 5% to 40%, 40% to 45 and 45% to 5 0 of naloxone after 120 minutes.
In another preferred embodiment of the invention the preparations comprising naloxone release approximately 35%, approximately 40%, approximately 45 approximately 50% or approximately 55% of naloxone after 120 minutes.
-36- In another preferred embodiment preparations in accordance with the invention comprising naloxone release 55% 90 preferably 60% to 80 more preferably to 75 and even more preferably 65% to 70 or 70% to 75 of naloxone after 420 minutes. In yet another preferred embodiment of the invention, preparations 5 comprising naloxone release approximately 65%, approximately 70% or 0approximately 75 of naloxone after 420 minutes.
In another preferred embodiment preparations in accordance with the invention comprising naloxone release 60% to 90 preferably 65% to 85 more preferably 70% to 80 and even more preferably 75% to 80 of naloxone after 600 minutes.
In yet another preferred embodiment of the invention, preparations comprising naloxone release approximately 75%, approximately 80% or approximately 85 of naloxone after 600 minutes.
Examples that display highly advantageous embodiments of the invention are set out below. Examples are also given showing that formulations which are in accordance with the invention differ mainly in their structure from formulations with a sustained release which has been produced by using commonly used scaffold-forming polymers. Only the formulations produced in accordance with the invention provide for a sustained, invariant and, if several compounds are present, independent release of the active compounds with the formulation being storage stable. The examples are not to be interpreted as limiting the possible embodiments of the invention.
37 Example 1 Production of tablets with different oxycodone/naloxone amounts in a non-swellable diffusion matrix by spray granulation: The following amounts of the listed components were used for the production of oxycodone/naloxone tablets according to the invention.
Preparation Oxy/Nal-0 Oxy/Nal-5 (designation) oxycodone HCI 20.0 mg 20.0 mg 20.0 mg naloxone HCI 5.0 mg 10.0 mg Lactose Flow Lac 100 59.25 mg 54.25 mg 49.25 mg Povidone 30 5.0 mg 5.0 mg 5.0 mg Surelease® 10.0 mg solid 10.0 mg solid 10.0 mg solid material material material Stearyl alcohol 25.0 mg 25.0 mg 25.0 mg Talcum 2.5 mg 2.5 mg 2.5 mg Mg-Stearate 1.25 mg 1.25 mg 1.25 mg The Surelease® E-7-7050 polymer mixture used had the following composition.
"Suree' Ethylcellulose 20 cps Dibutylsebacate Ammoniumhydroxide Oleic acid Siliciumdioxide Water For the production of tablets oxycodone HC1, naloxone HC1, Povidone 30 and Lactose Flow Lac 100 were mixed in a tumbling mixer (Bohle) and subsequently spray-granulated with Surelease® E-7-7050 in a fluidized bath granulating device (GPCG3). The material was sieved over a Comill 1.4 mm sieve. An additional granulation step was carried out with melted fatty alcohol in a high-shear mixer -38- (Collette). All tablet cores produced by this approach had a weight of 123 mg, based on dry substance.
O
C, 5 Example 2 Production of tablets with oxycodone and naloxone in a non-swellable 0 diffusion matrix by extrusion: The following amounts of the listed components were used for the production of the oxycodone/naloxone tablets according to the invention.
Preparation Oxy/Nal-Extr (designation) oxycodone HC1 20 mg naloxone HC1 10 mg Kollidon 30 6 mg Lactose Flow Lac 100 49.25 mg Ethylcellulose 45 epi 10 mg Stearyl alcohol 24 mg Talcum 2.5 mg Mg-Stearate 1,25 mg The listed amounts of oxycodone HC1, naloxone HC1, ethylcellulose 45 cpi, Povidone 30, stearyl alcohol and Lactose Flow Lac 100 were mixed in a tumbling mixer (Bohle). This mixture was subsequently extruded with a counter-rotating twin screw extruder of the type Micro 18 GGL (Leistritz AG, Nmrnberg, Germany). The temperature of heating zone 1 was 25 0 C, of heating zone 2, 50 0 C, of heating zones 3 to 5, 60 0 C, of heating zones 6 to 8, 55 0 C, of heating zone 9, 60 0 C and of heating zone 10, 65 0 C. The screw rotating speed was 150 revolutions per minute (rpm), the resulting melt temperature was 87 0 C, the feed rate was 1.5 kg/h and the diameter of the nozzle opening was 3 mm. The extruded material was sieved with a Frewitt 0.68 x 1.00 mm sieve. The grinded extrudate was then mixed with talcum and magnesium stearate that had been added over a 1 mm hand sieve and was subsequently pressed into tablets. The extruder has a screw geometry, as shown in Fig. 1A.
-39- In comparison to the oxycodone/naloxone tablets which also have the Sureleasebased non-swellable diffusion matrix produced by spray granulation (see Example extruded preparations comprise less components.
Example 3 Release profile of the oxycodone/naloxone tablets from Example 1: The release of the active compounds was measured over a time period of 12 hours, applying the Basket Method according to USP at pH 1.2 using HPLC. Tablets Ox/Nal-0, Ox/Nal-5 and Ox/Nal-10 were tested.
One recognizes from Fig. 2 and the values listed in the Table that in the case of a non-swellable diffusion matrix based on Surelease®, the release rates of different oxycodone amounts, independent of the naloxone amount, remain equal (invariant).
Correspondingly, invariant release profiles are observed for naloxone at different oxycodone amounts.
Time Ox/Nal- Ox/Nal-5- Ox/Nal-5- Ox/Nal-10- (min) 0 0 N 0 N Oxy Oxy Nal Oxy Nal 0 0 0 0 0 0 26.1 24.9 23.5 22.8 24.1 120 62.1 63 61 57.5 60.2 420 91.7 94.5 91.9 89.4 93.5 720 98.1 99.6 96.6 95.7 100.6 The release values refer to oxycodone or naloxone (line 2) and are given as percentages. The mean value for the release of naloxone at e. g. 420 min is 92,7%.
The maximal deviation at 420 min is Oxy and Nal stand for oxycodone and naloxone and indicate the active compound which has been measured.
Example 4 Release profile of oxycodone/naloxone tablets from Example 2 at different pH-values: The release of active compounds from the tablets was measured over a time period of 12 hours at pH 1.2 or for 1 hour at 1.2 and subsequently for 11 hours at pH Release rates were determined by the basket method according to USP using HPLC.
The following release rates were measured for 12 hours at pH 1.2: Time Oxy/Nal-Extr-1,2-0 Oxy/Nal-Extr-1,2-N (min) Oxy Nal 0 0 0 24.1 24:0 120 62.9 63.5 420 92.9 93.9 720 96.9 98.1 The following release rates were measured for 1 hour at pH 1.2 and 11 hours at pH Time Oxy/Nal-Extr-6,5-0 (min) Oxy Nal 0 0 0 48.1 49.2 120 65.0 64.7 240 83.3 81.8 420 94.1 92.3 The release rates refer to oxycodone and naloxone (line 2) and are given as percentages. Oxy and Nal stand for oxycodone and naloxone and indicate the active compound measured.
-41 The comparison of the values given in the Tables of Example 4 and the Table of C Example 3 make clear that independent of the production process, active compounds are released in equal amounts from the preparations. For example, 89.4% of 0 oxycodone is released from spray-granulated tablets (Ox/Nal-10-tablets, see Example s0 5 3) at 420 minutes, while 92.9% is released from extruded tablets (Oxy/Nal-Extr-1.2- 0 0, Example 4) at 420 minutes. The release of oxycodone from extruded tablets thus deviates by 1.1% from the mean value of the release of oxycodone from spraygranulated tablets (91.9% at 420 minutes). 93.5% of naloxone is released from spray-granulated tablets (Ox/Nal-10-tablets, see Example 3) at 420 minutes, while 93.9% is released from extruded tablets (Oxy/Nal-Extr.-l.2-O, Example 4) at 420 minutes. The release of naloxone from extruded tablets thus deviates by 1.3% from the mean value of the release of naloxone from spray-granulated tablets (92.7% at 420 minutes).
Moreover, one can infer from a comparison of the values of the Tables of Example 4 and from Figures 3A and 3B that independent of the pH value at which the release rates have been measured the release of oxycodone and naloxone remain equal and invariant.
Example 5 Comparative example: release behaviour of Valoron® tablets: The release of the active substances from tablets was monitored over a time period of 7 hours. Valoron® tablets with 50 mg tilidine and 4 mg naloxone (Ti/Nal-50/4) or 100 mg tilidine and 8 mg naloxone (Ti/Nal-100/8) or 150 mg tilidine and 12 mg naloxone (Ti/Nal-150/12) were tested by the Basket Method according to USP for lh at pH 1.2 and then for additional 6h at pH 6.5 using HPLC One recognizes from Figures 4A and 4B and the values listed in the Table that in case of a swellable (and possibly erosive) diffusion matrix with relevant amounts of 42 HPMC, the release of different amounts of tilidine varies significantly and is not invariant for different amounts of naloxone. This applies in turn to naloxone. This means that for this pH the release of the active compounds is not independent of each other.
Time Ti/Nal- Ti/Nal- Ti/Nal- Ti/Nal- Ti/Nal- Ti/Nal- (min) 50/4-T 50/4-N 100/8-T 100/8-N 150/12-T 150/12-N Til Nal Til Nal Til Nal 0 0 0 0 0 0 0 37.2 27.6 33.9 27.3 29.9 23.3 120 47.6 31.7 46.5 33.4 41.5 28.5 180 54.7 37.4 55 41.2 48.2 240 59.7 44 68.2 59.5 54.5 40.1 300 65.2 50.6 82.6 72.9 60.5 47.5 360 70.3 58 85.7 82.7 67.2 56.4 420 74.2 60.8 93.1 90.9 84.9 78.9 The release values refer to tilidine or naloxone (line 2) and are given as percentages.
The mean value for the release of naloxone at e. g. 420 min is 78,87%. The maximal deviation at 420 min is 20,4%. Til und Nal stand for tilidine and naloxone and indicate the active compound tested.
Example 6 Structure comparison of tablets of Examples 1 and 2 with Valoron® N tablets by electron microscopy.
For electron microscopy tablets were used that comprised 20 mg oxycodone and mg naloxone and were produced either by spray granulation according to Example 1 or by extrusion according to Example 2 (Oxy/Nal-Extr). Additionally, a Valoron® N tablet with 100 mg Tilidin and 8 mg Naloxone was used. Figures and 5B show different magnifications of scanning electron microscopy pictures of a with a formulation according to the invention which was produced by spray granulation. Figures 6A and 6B show different magnifications of scanning 43 electron microscopy pictures of a Oxy/Nal-Extr-tablets with a formulation according to the invention, which was produced by extrusion. Figures 7A and 7B show scanning electron microscopy pictures of the Valoron® N-tablet.
From a comparison of the figures one can clearly see that tablets with a formulation according to the invention have a surface which is substantially finer and more homogeneously structured and which shows fewer cracks than the Valoron® tablet, regardless of whether the tablets have been produced by spray granulation or extrusion. The structural difference is possibly the reason for the different release behaviours of the different preparations.
Example 7 Production of tablets comprising.different amounts of naloxone: and different matrices by spray granulation.
The following amounts of the listed components were used for the production of naloxone tablets: Preparation Nal-5-Eud Nal-5-Sure (designation) naloxone HCI 5.0 mg 5.0 mg 10.0 mg Lactose Flow Lac 74.25 mg 74.25 mg 69.25 mg 100 Povidone 30 5.0 mg 5.0 mg 5.0 mg EUDRAGIT' RS 10 mg solid material Surelease 10 mg solid 10 mg solid material material Triacetin 2.0 mg Stearyl alcohol 25.0 mg 25.0 mg 25.0 mg Talcum 2.5 mg 2.5 mg 2.5 mg Mg-Stearate 1.25 mg 1.25 mg 1.25 mg EUDRAGIT®RS 30 D can be purchased from R6hm GmbH, Darmstadt. Surelease® can be purchased from Colorcon Ltd., Idstein.
-44- EUDRAGIT® RS 30 D or. Surelease®-Polymer mixtures of the following compositions were used: Ammoniomethacrylate copolymer B Ethylcellulose 20 cps Sorbic acid Dibutylsebacate Natriumhydroxide Ammoniumhydroxide Water Oleic acid Siliciumdioxide Water For the production of tablets, naloxone HCI, Povidone 30 and Lactose Flow Lac 100 were mixed in a tumbling mixer (Bohle) and subsequently spray-granulated with EUDRAGIT®RS 30 D or Surelease® in a fluidized bath granulating device (GPCG3). An additional granulation step was carried out with melted fat alcohol in a high-shear mixer (Collette). All tablet cores produced by this approach had a weight of 125 mg, referred to the dry substance.
Example 8 Production of tablets with naloxone in a non-swellable diffusion matrix by extrusion: The following amounts of the listed components were used for the production of naloxone tablets according to the invention.
Preparation Nal-Extr (designation) naloxone HC1 10 mg Lactose Flow Lac 100 70.25 mg Kollidone 30 5 mg Ethylcellulose 45 cpi 8 mg Stearyl alcohol 26.0 mg Talcum 2.5 mg Mg-Stearate 1.25 mg The listed amounts of naloxone HC1, ethylcellulose 45 cpi, Kollidone 30, stearyl alcohol and Lactose Flow Lac 100 were mixed in a tumbling mixer (Bohle). This mixture was subsequently extruded with a counter-rotating twin screw extruder of the type Micro 18 GGL (Leistritz AG, Niirnberg, Germany). The temperature of heating zone 1 was 25°C, of heating zone 2, 50°C, of heating zones 3 to 10, The screw rotating speed was 140 rpm, the resulting melt temperature was 65 the feed rate was 1.25 kg/h and the diameter of the nozzle opening was 3 mm. The extruded material was sieved with a Frewitt 0.68 x 1.00 mm sieve. The grinded extrudate was then mixed with talcum and magnesium stearate that had been added over a 1 mm hand sieve and was subsequently pressed into tablets. The extruder has a screw geometry, as shown in Fig. 1.
In comparison to the oxycodone/naloxone tablets which also have the Surelease®based non-swellable diffusion matrix produced by spray granulation (see Example extruded preparations comprise less components.
-46 Example 9 Release behaviour of naloxone tablets from Example 7 The release of the active compound was measured over a time period of 16 hours, applying the Basket Method according to USP at pH 1.2 using HPLC. Two tablets "1 5 (designated A and B) of Nal-5-Eud, Nal-5-Sure and Nal-10-Sure were tested.
6c One recognizes from Fig. 8A and 8B and the values listed in the Table that in the case of a non-swellable diffusion matrix based on Surelease, the release rates of naloxone independent of the absolute amount reproducibly do not change and remain substantially equal (invariant). This does not apply for the release of naloxone from matrix based on Eudragit®.
Time Nal-5- Nal-5- Nal-5- Nal-5- Nal-10- (min) Eud-A Eud-B Sure-A Sure-B Sure-A Sure-B 0 0 0 0 0 0 0 18.48 18.23 23.86 21.97 20.65 22.25 40.46 26.15 46.74 47.33 45.18 45.98 240 62.43 53.47 70.48 69.49 69.13 68.76 420 82.9 72.27 91.04 88.69 88.06 87.5 720 97.46 85.74 100.62 99.1 96.05 95.74 960 107.6 96.26 102.26 102.33 97.91 97.43 The release values refer to naloxone and are given as percentages. The mean value for the release of naloxone in the case of e.g. Nal-Sure tablets at 90 min is 46.3%.
The maximal deviation at 90 min is The mean value at this time point for Nal- Rud tablets is 33.3% and the deviation is 21.5%.
47 Example 10 Release behaviour of naloxone tablets from Example 8 The release of the active compound was measured for different tablets over a time period of 12 hours, applying the Basket Method according to USP at pH 1.2 using
HPLC.
One recognizes from Fig. 9 and the values listed in the Table that the release of naloxone independent of the production process reproducibly does not change when tablets have been produced by extrusion.
Zeit (min) Nal-Extr-A Nal-Extr-B Nal-Extr-C 0 0 0 0 15 15 14.3 120 40.7 41.9. 40.1 420 72 75.2 173.6 720 90.1 92.4 91.2 The release values refer to naloxone and are given as percentages. The mean value for the release of naloxone in the case of Nal-Extr tablets at 120 min is 40.9%. The maximal deviation at 120 min is 2.4%.
Example 11 Structure comparison of naloxone tablets of Examples 7 and 8.
For electron microscopy, Nal-Eud tablets according to Example 7 with 5 mg Eud) as well as a Nal-Extr tablets according to Example 8.
Figures 10A and 10B show different magnifications of scanning electron microscopy pictures of a Nal-5-Eud tablet. Figures 11A and 11B show different magnifications of scanning electron microscopy pictures of a Nal-Extr tablets with a formulation in accordance with the invention.
-48 From a comparison of the figures, one can clearly see that the formulation in Saccordance with the invention has a surface which is substantially finer and more homogeneously structured. Particularly, in Figures 10A and 10B naloxone blooms N 5 can be seen, but not in Figures 11A and 11 lB. This structural difference is possibly the reason for the different release behaviour of the different preparations.
Example 12 Structure comparison of naloxone granulates of Examples 7 and 8.
For electron microscopy, granulates as they were used for production of Nal-Sure tablets according to Example 7 witt 10 mg naloxone (Nal-10-Sure) and Nal-Extr tablets according to Example 8 were used.
Figures 12A and 12B show different magnifications of scanning electron microscopy pictures of Nal-10-Sure granulates. Figures 13A and 13B show different magnifications of scanning electron microscopy pictures of a Nal-Extr granulates with a formulation in accordance with the invention.
One can clearly see that independent of the production process granulates with a formulation in accordance have homogeneously structured surfaces without major cracks or blooms. Without wanting to be bound to a scientific theory it is assumed that the surface characteristics are responsible for the release behaviour of the formulations in accordance with the invention.
Example 13 Storage stability of naloxone tablets depending on the matrix used.
Multiple tablets comprising either EUDRAGIT(RS 30 D or Surelease® and 5 mg naloxone were produced as described in Example 1 .The tablets were stored at 250 C 49 and 60% relative humidity. At different time points, the release behaviour was tested as described in Example 4.
As can be recognized from Figures 4A and 4B and the Tables, the release profiles of naloxone tablets having been formulated with EUDRAGIT®RS 30 D differ already after a short time of storage. In contrast, the release profile of tablets which have been formulated with Surelease® are almost invariant, even after 15 months of storage.
Storage time 0 1 (Months) Preparation Nal-5- Nal-5- (designation) Eud-0 Eud-1 Time (min) 16.46 12.66 15.06 30.29 28.78 30.6 240 52.94 43.85 47.5 480 71.07 57.37 62.86 720 83.29 66.68 73.58 1020 91.61 73.03 80.97 Storage time 0 3 6 (Months) Preparation Nal-5- Nal-5- Nal-5- (designation) Sure-0 Sure-3 Sure-6 Time (min)__ 21.58 22.52 16.04 24.36 120 49.94 49.05 51.93 55.59 420 79.83 86.32 87.99 88.49 720 91.74 97.55 100.27 97.09 In the Table, the release rates are given in percentages. In each case, the release of naloxone was tested.
Example 14 Production of tablets with different oxycodone/naloxone amounts in a non-swellable diffusion matrix by extrusion: The following amounts of the listed components were used for the production of oxycodone/naloxone tablets according to the invention.
Preparation OxN2O 1 -Extr-A OxN2O/1 -Extr-B OxN20/1-Extr-C QxN2O/1 0-Extr-A (designation) Oxycodone 20 mg 20 mg 20 mg 20 mg HCl Naloxone HC1 1 mg 1 mg 1 mg 10 mg Lactose Flow 58.25 mg 58.25 mg 58.25 mg 49.25 mg Lac 100 6 mg 6 mg 6 mg 6 mg Ethyicellulose 10mg 10 mg 10 mg 10 mg Stearly alcohol 2mg24 mg 24 mg 24 mug Talcum 1.25 mg 1.25 mg 1.25 mg 1.25 mg Mg-Stearate 2.5 mg 2.5 mg 2.5 rug 2.5 mg Extrusion was performed as described above (Example 2) with the following parameters: OxN2O/1 -Extr-A: temperature: rpm (screw): feeding rate: temperature: rpm (screw): feeding rate: 55-63 0
C
150 rpm 1.5 kg/b 55-63 0
C
155 rpm 1.5 kg/h OxN2O/1 -Extr-B: -51 OxN20/1-Extr-C: OxN20/10-Extr-A: temperature: rpm (screw): feeding rate: temperature: rpm (screw): feeding rate: 55-63 °C 1505rpm 1.5 kg/h 55-63 °C 160 rpm 1.75 kg/h Tablet production was performed with a common tabletting device with the following parameters: OxN20/1-Extr-A: OxN20/1-Extr-B: OxN20/1-Extr-C: rpm: Pressure power: rpm: Pressure power: rpm: Pressure power: rpm: Pressure power: 40 rpm 9 kN 42 rpm 8.9 kN 36 rpm 9 kN 36 rpm 7.5 kN QxN2O/1 0-Extr-A: The release of the active compounds was measured over a time period of 12 hours, applying the Basket Method according to USP at pH 1.2 using HPLC. Tablets OxN20/1-Extr-A, OxN20/1-Extr-B, OxN20/1-Extr-C and OxN20/10-Extr-A were tested.
One recognizes from the values listed in the Table that in the case of a non-swellable diffusion matrix based on ethylcellulose, the release rates of different naloxone -52-
(N
1^ ^-i m 0
(N
^D
0 0
(N
amounts, independent of the oxycdone amount, remain substantially equal.
Correspondingly, the preparations provide for an independent and invariant release of the active compounds.
Time OxN20/1l- OxN20/l- OxN20/1- OxN20/10- (min) Extr-A Extr-B Extr-C Extr-A Oxy Nal Oxy Nal Oxy Nal Oxy Nal 0 0 0 0 0 0 0 0 0 21.2 25.8 21.7 21.1 19.7 19.3 23.3 24.3 120 56.6 53.8 58.8 57.3 57.7 56.2 64.5 66.9 420 87.2 84.5 94.2 92.6 93.7 91.5 92.7 96.3 720 99.7 96.8 100.1 98 100.6 97.5 93.6 97.4 The release values refer to oxycodone or naloxone (line 2) and are given as percentages. The mean value for the release of naloxone at e. g. 420 min is 92.3%.
The maximal deviation at 420 min is Oxy and Nal stand for oxycodone and naloxone and indicate the active compound which has been measured.
Thus, once a preparation with the desired release profile has been developed, one can change the amount of the active compounds without significantly changing the release profiles of the active compounds. The preparations comprising different amounts of the active compounds still provide for a sustained, independent an invariant release of the active compounds.
Example 15 Production of tablets with oxycodone/naloxone in a non-swellable diffusion matrix by extrusion: In the following example it is set out that using formulations according to the present invention, preparations comprising oxycodone and naloxone with particular release behaviours may be obtained.
53 The following amounts of the listed components were used for the production of oxycodone/naloxone tablets according to the invention.
Preparation OxN2O/l- OxN20/1- OxN20/10- OxN20/10- OxN2 '0/10- (designation) Extr-D Extr-E Extr-B Extr-C Extr-D Extr-E oxycodone HCI 20 mg 20 mg 20 mug 20 mg 20 mg 20 mg naloxoneflCl 1 m 1 mg 10 mg 10 mg 10 mg 10 mg Lactose Flow 56.25 rug 56.25 mg 54.25 mg 65.25 rug 60.25 rug 55.25 Lac 100 KollidonS 30 7 q m _g g 7.25 mg 7.5m 7.25 mug Ethylcellulose 11 mg 12 mg 10 mg 12 mg 12 g~ 12 mg Stearyl alcohol 24 mug 24 rug 24 rug 28.75 mug 28.75 mg 28.75 rug Talcum 1.25 mg 1.25 mg 1.25 mg 1.25 mg 1.2 m 1.25 mg Mg-Stearate 2.5 mg 2.5 mg 2.5 mg 2.5 mg 2.5 mg 2.5 mg Extrusion was performed as described above (Example 2) with the following parameters: OxN2O/1-Extr-D: QxN2O/1 -Extr-E: temperature: rpm (screw): feeding rate: temperature: rpm (screw): feeding rate: temperature: rpm (screw): feeding rate: temperature: rpm (screw): feeding rate: 55-63 0
C
150 rpm 1.5 kg/h 55-63 0
C
150 rpm 1.5 kg/h 55-63 0
C
160 rpm 1.75 kg/h 55-63 OC 160 rpm 1.75 kg/h OxN20/1 0-Extr-B: OxN2O/10-Extr-C: 54 OxN2O 1 0-Extr-D: OxN2O/1 0-Extr-E: temperature: rpm (screw): feeding rate: temperature: rpm (screw): feeding rate: 55-63 0
C
150 rpm 1.5 kg/h 55-63 0
C
150 rpm 1.5 kg/h Tablet production was performed with a common tabletting device with the following parameters: OxN2O 1 -Extr-D: OxN20/1 -Extr-E: OxN2O/1 0-Extr-B: rpm: Pressure power: rpm: Pressure power: rpm: Pressure power: rpm: Pressure power: rpm: Pressure power: rpm: Pressure power; 39 rpm 11 kN 39 rpm 10.5 kN 36 rpm 9.5 kN 36 rpm 7.8 kN 39 rpm 9 kN 39 rpm 7.5 kN OxN20/1 0-Extr-C: OxN20/10-Extr-D: 0-Extr-E: ,l The release of the active compounds was measured over a time period of 12 hours, applying the Basket Method according to USP at pH 1.2 using HPLC. Tablets O OxN20/1-Extr-D, OxN20/1-Extr-E, OxN20/10-Extr-B, OxN20/10-Extr-C, 0 5 OxN20/10-Extr-D and OxN20/10-Extr-E were tested.
Time OxN20/1- OxN20/l- OxN20/10- OxN20/10- OxN20/10- OxN20/10- (min) Extr-D Extr-E Extr-B Extr-C Extr-D Extr-E Oxy Nal Oxy Nal Oxy Nal Oxy Nal Oxy Nal Oxy Nal 0 0 0 0 0 0 0 0 0 0 0 0 0 16.6 16.2 17.4 17.2 26.1 26.8 21.8 21.9 18.5 18.2 18.4 18.2 120 47.6 46.9 49.6 49.7 71.1 73.0 61.2 61.8 52.8 52.8 53.3 53.3 420 82.7 84.5 84.6 85.7 94.3 96.6 93.2 94.7 86.3 86.3 87.2 88.2 720 95 97 95.2 95.8 94.9 97.9 96.4 97.9 94.8 94.8 95.7 96.5 The release values refer to oxycodone or naloxone (line 2) and are given as percentages. Oxy and Nal stand for oxycodone and naloxone and indicate the active compound which has been measured.
The example shows that preparations with particular release profiles may be produced if ethylcellulose and fatty alcohols are used as the matrix-components that essentially influence the release characteristics of the preparations. Once a preparation with desired release characteristics has been obtained the amount of the active compounds may be changed. The preparations will still provide for a sustained, independent and invariant release behaviour (see example 14).
Example 16 Production of tablets with naloxone in a non-swellable diffusion matrix by extrusion: The following amounts of the listed components were used for the production of naloxone tablets according to the invention.
-56- Preparation N IO-Extr- NIO-Extr- N1O-Extr- NIO-Extr- N1O-Extr- N1O-Extr- (designation) 1 2 3 4 5 6 NaloxoneNHCI 10 mg 10 mg 10 mg 10 mg 10 mg Lactose Flow 69.25 mg 69.25 mg 69.25 mg 69.25 mg 69.25 mg 69.25 mg Lac 100 Povidone 30 5.0 mg 5.0 mg 5.0 mg 5.0 mg; 5.0 mg 5. m Ethylcellulose 10 mg 10 mg 10 mg 10 mg 10 mg 10 M Stearyl alcohol 2mg 25 mg 25 mg 25 mg 25 mg 25 mg Talcum 11.25 mg 11.25 mg 1.25 mg 1.25 mg 1.25 mg Mg-Stearate 12.5 mg 12.5 mg 12.5 mg 12.5 mg 12.5 mg 12.5!m~g" Extrusion was performed as described above with the following parameters: N I 0-Extr- 1: N1 0-Extr-2: NI 0-Extr-3: temperature: rpm (screw): feeding rate: temperature: rpm (screw): feeding rate: temperature: rpm (screw): feeding rate: temperature: rpm (screw): feeding rate: temperature: rpm (screw): 55-63 OC 120 rpm 1.5 kg/h 55-63 0
C
140 rpm 1.5 kg/h 55-63 0
C
160 rpm 1.75 kg/h N1O-Extr-4: 55 0
OC
120 rpm 1.75 kg/h 55-55 oC 140 rpm N1O-Extr-5: feeding rate: 1.5 kg/h -57- NIO-Extr-6: temperature: rpm (screw): feeding rate: 55 OC 160 rpm 1.5 kg/h Tablet production was performed with a common tabletting device with the following parameters: NI 0-Extr- 1 NiO-Extr-2: NI 0-Extr-3: rpm: Pressure power: rpm: Pressure power: rpm: Pressure power: rpm: Pressure power: rpm: Pressure power: rpm: Pressure power: 39 rpm 11.6 kN 39 rpm 12.5 kN 39 rpm 11.6 kN 36 rpm 14.5 kN 36 rpm 15.0OkN 36 rpm 15.0OkN NI 0-Extr-4: NIO-Extr-5: Ni1 O-Extr-6: The release of the active compound was measured over a time period of 12 hours, applying the Basket Method according to USP at pH 1.2 using HPLC. Tablets Extr-A, Ni 0-Extr-B, NI O-Extr-C, Ni 0-Extr-D, Ni 0-Extr-E and NI O-Extr-F were tested.
-58- One recognizes the values listed in the Table that, in the case of a non-swellable diffusion matrix based on ethylcellulose and a fatty alcohol, the release rates of naloxone remain substantially equal (invariant).
Time N10- N10- N10- N10- N10- (min) Extr-1 Extr-2 Extr-3 Extr-4 Extr-5 Extr-6 0 0 0 0 0 0 0 13.0 12.9 13.0 13.2 13.3 13.5 120 37.4 37.6 37.9 37.6 37.9 38.7 420 67 67.3 67.9 67.5 67.4 69.5 600 78.1 78.5 78.7 78.4 78.3 80.5 The release values refer to naloxone and are given as percentages. The mean value for the release of naloxone at e. g. 420 min is 67.8%. The maximal deviation at 420 min is
Claims (30)
1. Storage stable pharmaceutical formulation comprising at least one pharmaceutically active compound in a diffusion matrix, IN 5 characterized in that the matrix is determined with respect to its essential release characteristics by ethylcellulose or an ethylcellulose-based polymer and at least one fatty alcohol and that the active compounds are released from the substantially non- swellable diffusion matrix in a sustained, invariant and, if several compounds are present, independent manner.
2. Pharmaceutical formulation according to claim 1, characterized in that the fatty alcohol comprises lauryl, myristyl, stearyl, cetylstearyl, ceryl and/or cetylalcohol, preferably stearyl alcohol.
3. Pharmaceutical formulation according to claim 1 or 2, characterized in that the formulation comprises ethylellulose.
4. Pharmaceutical formulation according to one of the preceding claims, characterized in that the formulation does not comprise relevant amounts of alkaline and/or water-swellable substances, particularly derivatives of acrylic acid and/or hydroxyalkylcelluloses. Pharmaceutical formulation according to one of the preceding claims, characterized in that the formulation comprises common pharmaceutical excipients, particularly fillers, lubricants, flowing agents and/or plasticizers.
6. Pharmaceutical formulation according to claim characterized in that the fillers are selected from the group comprising sugars, preferably lactose, glucose and/or saccharose, starches and hydrolysates thereof, preferably micro-crystalline cellulose and/or cellactose, sugar alcohols, preferably 60 sorbitol and/or mannitol, poorly soluble calcium salts, preferably calcium hydrogenphosphate, dicalciumphosphate or tricalciumphosphate and/or povidone.
7. Pharmaceutical formulation according to claim 1 5 characterized in that it comprises magnesium stearate, calcium stearate and/or O calcium laureate and/or fatty acids, preferably stearic acid as lubricant.
8. Pharmaceutical formulation according to claim characterized in that it comprises highly dispersed silica, preferably Aerosil®, talcum, corn starch, magnesium oxide, magnesium and/or calciumstearate as flowing agent.
9. Pharmaceutical formulation according to claim characterized in that it comprises dibutyl sebacate as plasticizer. Pharmaceutical preparation according to one of the preceding claims, characterized in that the formulation can be stored over a period of at least two years under standard conditions (60% relative humidity, 25 0 C) in accordance with admission guidelines.
11. Pharmaceutical preparation according to one of the preceding claims, characterized in that it comprises opioid analgesics as the pharmaceutically active compounds, preferably morphine, oxycodone, hydromorphone, propoxyphene, nicomorphine, dihydrocodeine, diamorphine, papaveretum, codeine, ethylmorphine, phenylpiperidine and/or derivatives thereof, methadone, dextropropoxyphene, buprenorphine, pentazocin, tilidine, tramadol and hydrocodone and/or opioid antagonists, preferably naltrexone, naloxone, nalmefene, nalorphine, nalbuphin, naloxonazinene, methylnaltrexone, ketyleyclazocine, norbinaltorphimine, naltrindol, 6-p-naloxol and/or 6- p-naltrexol. -61-
12. Pharmaceutical formulation according to claim 11, characterized in that the opioid analgesic and/or the antagonist are present in the form of their pharmaceutically acceptable and equally active derivatives, such as the free base, salts and the like, preferably as the hydrochloride, sulfate, bisulfate, tatrate, nitrate, citrate, bitatrate, phosphate, malate, maleate, hydrobromide, hydroiodide, fumarate or succinate.
13. Pharmaceutical formulation according to claim 11 or 12, characterized in that the formulation comprises at least two active compounds which are oxycodone and naloxone, and wherein oxycodone is present in an amount ranging from 10 to 150 mg, preferably from 10 to 80 mg and naloxone is present in an amount ranging from 1 to 50 mg per unit dosage.
14. Pharmaceutical formulation according to claim 13, characterized in that it comprises oxycodone and naloxone in a weight ratio ranging from maximal 25:1, preferably maximal 20:1, 15:1 and more preferably from 5:1, 4:1, 3:1, 2:1 and 1:1. Pharmaceutical formulation according to claim 11 or 12, characterized in that it contains oxycodone and naloxone with oxycodone being present in an amount ranging from 10 to 150 mg, preferably from 10 to 80 mg and naloxone being present in an amount ranging from 1 to 50 mg.
16. Pharmaceutical preparation according to one of the preceding claims, characterized in that the formulation is a tablet, preferably a multi-layered tablet, a capsule, a drag6e, a granulate and/or a powder.
17. Pharmaceutical formulation according to claim 16, characterized in that the pharmaceutical preparation is suitable or oral, nasal and/or rectal application. 62
18. Pharmaceutical formulation according to one of the preceding claims, characterized in that the formulation is produced by build-up and/or break-down granulation, preferably by spray granulation. ,1 0 19. Pharmaceutical formulation according to one of claims 1 to 17, 0, characterized in that the formulation is produced by extrusion. Storage stable pharmaceutical formulation comprising at least one active compound in a sustained release matrix, characterized in that the matrix is a substantially non-swellable diffusion matrix whose release characteristics are determined by amounts of ethylcellulose or an ethylcellulose-based polymer and at least one fatty alcohol as matrix components, and by extrusion or granulation of the matrix materials together with the amount of the active compounds for formation of an active compound-containing matrix.
21. Storage stable pharmaceutical formulation according to claim wherein the diffusion matrix is a substantially non-erosive matrix.
22. Storage stable pharmaceutical formulation according to claim 20 or 21, wherein the matrix material contains ethylcellulose.
23. Storage stable pharmaceutical formulation according to one of claims to 22, wherein the matrix is formed by extrusion, particularly by melt extrusion.
24. Storage stable pharmaceutical formulation having an effective amount of an opioid agonist and/or an opioid antagonist in a substantially non-swellable and non-erosive diffusion matrix, whose release characteristics are determined by amounts of ethylcellulose or an ethylcellulose-based polymer and at least one fatty alcohol. 63 Storage stable pharmaceutical formulation according to claim 24 having an effective amount of oxycodone and/or naloxone, with oxycodone being present mnan amount ranging from 10 to 150 mg, preferably from 10 to 80 mg and Ni 5 naloxone being present in an amount ranging from 1 to 50 mg per unit dosage. ci26. Storage stable pharmac~eutical formulation according to claim 24 or having an effective amount of oxycodone and/or naloxone, wherein oxycodone and naloxone are present in a weight ratio ranging from maximal 25: 1, preferably maximal 20:1, 15: 1, particularly preferably 5:1, 4:1, 3:1, 2:1 and 1: 1.
27. Method for producing a formulation according to one of claims I to *'26, characterized in that granulation, preferably build-up and/or break-down granulation, particularly preferably spray granulation is used.
28. Method of producing a formulation according to one of claims I to 26, being an extrusion method, wherein counter-rotating or co-rotating single or multiple screw extruders with/without kneading elements are used.
29. Method according to claim 28, being an extrusion method wherein counter-rotating twin-screw extruders, preferably without kneading elements, are used.
30. Method according to claim 28 or 29, characterized in that the temperature of the heating zones of the extruders is between 20'-120'C, preferably between 50'-100 0 C, more preferably between and even more preferably between 50'-70*C. -64- C
31. Method according to one of claims 28 to characterized in that the diameter of the nozzle on the extruder is between 1 to mm, preferably between 2 to 8 mm and particularly preferably between 3 to 5 mm. 0 1 5 32. Method according to one of claims 28 to 31, 0characterized in that the resulting temperature in the extruder does not influence C, the stability of the active compounds.
33. Method of producing a pharmaceutical dosage form for the treatment of opioid-induced side effects, characterized in that the pharmaceutical dosage form comprises a pharmaceutical formulation according to one of claims 1 to
34. Method according to claim 33, characterized in that the preparation is used for treatment of opioid-induced obstipation and preferably for treatment of opioid-induced pruritus. Method of producing a pharmaceutical dosage form for the treatment of idiopathic syndromes, characterized in that the pharmaceutical dosage form comprises a pharmaceutical formulation according to one of claims 1 to
36. Method according to claim 35, characterized in that the preparation is used for treatment irritable bowel syndrome, preferably for treatment of idiopathic pruritus or pruritus due to cholestasia and/or renal dysfunction.
37. Method according to one of claims 33 to 36, characterized in that the matrix is a substantially non-swellable diffusion matrix whose release characteristics are determined by amounts of ethylcellulose or an ethylcellulose- based polymer and of at least one fatty alcohol. S
38. Method according to one of claims 33 to 37, characterized in that the preparation comprises between approximately 1 to 50 mg naloxone, preferably between approximately 5 to 30 mg naloxone and even more preferably between approximately 5 to 20 mg naloxone.
39. Method according to one of claims 33 to 38, characterized in that naloxone is present in the form of its pharmaceutically acceptable and equally active derivatives, such as the free base, salts and the like, preferably as the hydrochlPride, sulfate, bisulfate, tatrate, nitrate, citrate, bitatrate, phosphate, malate, maleate, hydrobromide, hydroiodide, fumarate or succinate. Method according to one of claims 33 to 39, characterized in that the matrix is produced by extrusion. Dated 25 July, 2006 EURO-CELTIQUE S.A. Patent Attorneys for the Applicant/Nominated Person SPRUSON FERGUSON