AU2005219450A1 - Paintable primer system - Google Patents
Paintable primer system Download PDFInfo
- Publication number
- AU2005219450A1 AU2005219450A1 AU2005219450A AU2005219450A AU2005219450A1 AU 2005219450 A1 AU2005219450 A1 AU 2005219450A1 AU 2005219450 A AU2005219450 A AU 2005219450A AU 2005219450 A AU2005219450 A AU 2005219450A AU 2005219450 A1 AU2005219450 A1 AU 2005219450A1
- Authority
- AU
- Australia
- Prior art keywords
- primer
- dispersion
- present
- ester
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
WO 2005/085341 PCT/AU2005/000300 1 TITLE PAINTABLE PRIMER SYSTEM FIELD OF THE INVENTION The present invention relates to a paintable primer system particularly for 5 use in the coating of surfaces, including but not limited to, thermoplastic polyolefin surfaces, metal surfaces and composite surfaces. The invention also relates to paintable primer systems suitable for applying to a polyethylene surface. BACKGROUND OF THE INVENTION Coating is typically used to improve an article's durability, corrosion 10 resistance, visibility and appearance. Examples of materials that require coating include thermoplastic polyolefins (TPOs), metals and composites, including but not limited to, those metals and composite materials used in the auto, marine and aviation industries. Some of the materials that require coating present challenges to coating, such as being difficult to coat, requiring multiple coats or requiring 15 pre-treatment of the material. TPO's such as polyethylene, polypropylene (PP), polystyrene (PS), thermoplastic elastomer (TPE) or ethylene-propylene rubbers have steadily grown in use as a material of construction for a large array of consumer goods. In particular, polyethylene (PE) is used in the manufacture of toys, containers, 20 packing films, household appliances, and in particular, the automotive industry as it exhibits the primary properties of being relatively inert, flexible, impermeable to water vapour, light weight, durable and is produced at a relatively low cost. However as PE is non-polar, it is reluctant to accept a coating of paint or decorative print coating. Most paints are polar, and thus require a surface with 25 some degree of surface polarity before they can adhere to it with any degree of desirable adherence. Conventional approaches to this problem have had limited success. One approach to enhancing the paintability of a TPO surface or substrate is to subject it to physical or chemical etching. For example, the outside surface of 30 PE water tanks are either lightly sanded or flame treated to remove the waxy, glossy surface prior to painting. Alternatively, the TPO surface or substrate may be irradiated with a plasma. A variation to this method is taught in WO 2005/085341 PCT/AU2005/000300 2 JP59114039A2, whereby a primer is applied to a non-vulcanised rubber substrate and dried prior to irradiation. While generally effective, these methods are complex in nature and are more difficult to control in terms of quality and consistency across the surface. In addition, these techniques are generally more 5 expensive than other alternatives. Another approach is to apply several primer coats to a TPO substrate. While such primers are generally recognized as effective over short durations, they are expensive and their application is an extra step in the finishing of the manufactured TPO article. In addition, primer systems require multiple coats and 10 still lack sufficient bonding strength to maintain adherence to the TPO substrate over time. Known primer compositions are unable to achieve satisfactory adhesion, resulting in peeling or chipping of the primer and/or covering paint over time. As conventional primers have had limited success, more recent techniques 15 have been to modify the physical and/or chemical properties of the TPO per se (e.g. as taught in WO 9325617). This can be achieved either by blending the thermoplastic polyolefin with other thermoplastic polymers, or by grafting functionalised groups to one or more polar groups along the polymeric backbone. While this approach has been successful, it is complex and can only be applied to 20 existing substrates at the time of manufacture. Metals and composite materials, including but not limited to metals and composites used in the auto, marine and aviation industries, also require coating. OBJECT OF THE INVENTION Accordingly, it is an object of the invention to provide a paintable primer 25 system suitable for applying to surfaces which overcomes or alleviates one or more of the problems of the prior art or provides a useful commercial alternative. SUMMARY OF THE INVENTION Until now, known primer compositions have achieved only partial and/or extremely short term paint adhesion to surfaces such as thermoplastic polyolefins, 30 metals and composite materials. The present invention is predicated upon a novel paintable primer system with adhesion suitable for use on various thermoplastic polyolefins, metals and composite materials.
WO 2005/085341 PCT/AU2005/000300 3 According to a first aspect of the invention there is provided a dispersion comprising: a thermoplastic polymer, a phthalate ester of a CI-C 6 alkylated aromatic alcohol, 5 a surfactant and further comprising one or more components selected from the group consisting of: a metal carbonate, a white metal oxide, an alkaline earth metal salt of a C 9
-C
20 aliphatic fatty acid, 10 a solvent, a rust inhibitor, and a lower alkyl methacrylate polymer. In a first embodiment of the first aspect the lower alkyl methacrylate polymer is an ethyl methacrylate polymer. 15 In a second embodiment of the first aspect the dispersion comprises a thermoplastic polymer, a phthalate ester of a C 1
-C
6 alkylated aromatic alcohol, a metal carbonate, a white metal oxide pigment, an alkaline earth metal salt of a C 9 C 20 aliphatic fatty acid, a lower alkyl methacrylate polymer, a surfactant and a solvent. 20 In a third embodiment of the first aspect the dispersion comprises a thermoplastic polymer, a phthalate ester of a CI-C 6 alkylated aromatic alcohol, a white metal oxide pigment, a surfactant, and a solvent. In a fourth embodiment of the first aspect the dispersion comprises a thermoplastic polymer, a phthalate ester of a CI 1
-C
6 alkylated aromatic alcohol, a 25 metal carbonate, a white metal oxide, an alkaline earth metal salt of a C 9
-C
20 aliphatic fatty acid, a lower alkyl methacrylate polymer, a surfactant, a solvent and a rust inhibitor. In a fifth embodiment of the first aspect the dispersion is in a solid form. In a sixth embodiment of the first aspect the dispersion is in a solid 30 granulated form. In a second aspect there is provided a primer comprising the dispersion of the fifth embodiment of the first aspect and a primer solvent.
WO 2005/085341 PCT/AU2005/000300 4 In a first embodiment of the second aspect the primer comprises a component selected from the group consisting of: a lower alkyl methacrylate polymer, a CI-C 6 ketone, a CI-C 6 ester, a phthalate ester of a CI-C 6 alkylated aromatic alcohol, a halogenated polyolefin, and a polymeric plasticizer. 5 In a second embodiment of the second aspect the primer further comprises a component selected from the group consisting of: an alcohol, a thermoplastic polymer, a polyhydroxy magnesium silicate derivate, and a silicon dioxide powder. In a third aspect there is provided a primer comprising a solvent, a lower 10 alkyl methacrylate polymer, a CI-C 6 ketone, a Ci-C 6 ester, a phthalate ester of a
CI
1
-C
6 alkylated aromatic alcohol, a polymeric plasticizer, a halogenated polyolefin, the dispersion of the second embodiment of the first aspect, and the dispersion of the third embodiment of the first aspect. In a fourth aspect there is provided a primer comprising a solvent, a lower 15 alkyl methacrylate polymer, a C 1
-C
6 ketone, a Ci-C 6 ester, a phthalate ester of a
C
1
-C
6 alkylated aromatic alcohol, a polymeric plasticizer, a halogenated polyolefin, the dispersion of the second embodiment of the first aspect, the dispersion of the third embodiment of the first aspect and the dispersion of the fourth embodiment of the first aspect. 20 In a fifth aspect there is provided a primer comprising a solvent, a lower alkyl methacrylate polymer, a C 1
-C
6 ketone, a C 1
-C
6 ester, a phthalate ester of a
C
1
-C
6 alkylated aromatic alcohol, an alcohol, a thermoplastic polymer, a polyhydroxy magnesium silicate derivate, a silicon dioxide powder, a polymeric plasticizer, a halogenated polyolefin, the dispersion of the second embodiment of 25 the first aspect, and the dispersion of the third embodiment of the first aspect. In a sixth aspect there is provided an adhesion promoter comprising an aromatic hydrocarbon, a co-polymer of a C 2
-C
6 alkene and a vinyl ester and a chlorinated polyolefin. In a seventh aspect there is provided a method of manufacturing a primer 30 including the steps of: mixing a first primer solution in a first vessel; WO 2005/085341 PCT/AU2005/000300 5 mixing a second primer solution comprising the solid dispersion of the fifth embodiment of the first aspect in a second vessel,; mixing the first primer solution and the second primer solution together to form the primer. 5 In an eighth aspect there is provided a method of manufacturing a primer comprising: mixing a first primer solution comprising a primer solvent and a lower alkyl methacrylate polymer; mixing a second primer solution comprising a CI-C 6 ketone, a CI-C 6 ester, 10 a phthalate ester of a C 1
-C
6 alkylated aromatic alcohol, and the dispersion of the first aspect; and mixing the first primer solution and the second primer solution together with a CI-C 6 ester, a CI-C 6 ketone, a primer solvent, a polymeric plasticizer, and a halogenated polyolefin to form the primer. 15 In a first embodiment of the eighth aspect the second primer solution comprises the dispersion of the second embodiment of the first aspect, and the dispersion of the third embodiment of the first aspect. In a second embodiment of the eighth aspect the second primer solution comprises the dispersion of the second embodiment of the first aspect, the 20 dispersion of the third embodiment of the first aspect and the dispersion of the fourth embodiment of the first aspect. In a ninth aspect of the invention there is provided a method for coating a surface of an article comprising: coating the surface with the adhesion promoter of the sixth aspect; and 25 coating the surface with the primer of the fifth embodiment of the first aspect. In a tenth aspect there is provided an article coated with the primer of the second aspect. Preferably, articles for coating with the dispersions, adhesion promoter, 30 and primers of the invention comprise thermoplastic polyolefins, metals, or composite materials.
WO 2005/085341 PCT/AU2005/000300 6 As used herein, "paint", "painting" and "painted" is meant a coat, covering or decoration using a liquid mixture, usually containing a solid pigment in a liquid vehicle and is used as a decorative or protective coating and that which forms a thin dry film when applied to a surface. 5 As used herein, "low molecular weight" is meant the sum of the atomic weights (International Atomic Weights) of the atoms in the molecule of up to 250 grams/mole. In this specification, the terms "comprises", "comprising" or similar terms are intended to mean a non-exclusive inclusion, such that a method, system or 10 apparatus that comprises a list of elements does not include those elements solely, but may well include other elements not listed. DETAILED DESCRIPTION The present invention resides in a novel paintable primer system which binds to surfaces with high bonding strength. Apart from cleaning, the primers of 15 the present invention do not require any pre-treatment of the surface to be coated. To further improve the high-bonding strength of the primers a manual mechanism, such as scouring, may be used. Advantageously, application of an adhesion promoter followed by a primer containing one or more dispersions is suitable for application to PE, PP and other plastic substrates and metals. The 20 primer may be applied to PP, other plastic substrates and metals without the need for the adhesion promoter whist still providing suitable adhesion. The invention provides one or more dispersions or solid dispersion "chips". It will be appreciated that in formulating either a first 180/9101, second 180/9020, or third 180/9103 chip, a number of substituted agents may be used. 25 It is understood that the dispersions are manufactured from components in liquid, solid and/or semi-solid (e.g. resin) form. The components can be mixed and processed into a solid "chip". The dispersion may be provided as a product in a solid "chip" form, other solid form, a semi-solid form or a liquid form. All examples provided below are non-limiting and provided for guidance. 30 It is appreciated that each of the components can be varied within 30% of the stated amount, more preferably within 25% of the stated amount, more preferably within 20% of the stated amount, more preferably within 15% of the stated WO 2005/085341 PCT/AU2005/000300 7 amount, more preferably within 10% of the stated amount and even more preferably within 5% of the stated amount. A person of skill in the art readily understand that when varying the percentage of one or more component the percentage of the other components 5 must be varied accordingly so that the sum of the components equals 100 %. General dispersion or 'chip 'formulation The general dispersion or chip formulation comprises a thermoplastic polymer, a phthalate ester of a C-C 6 alkylated aromatic alcohol and a surfactant. Thermoplastic polymer includes any thermoplastic cellulose polymer and 10 any thermoplastic polymer of a cellulose derivative. The thermoplastic polymer may be selected from cellulose acetate, cellulose propionate and cellulose acetate butyrate. Preferably the thermoplastic polymer is cellulose acetate butyrate. Preferably the cellulose acetate butyrate is provided in the form of the commercially available CAB 381-2 polymer available from and manufactured by 15 Eastman Chemical International Limited. The phthalate ester of a C 1
-C
6 alkylated aromatic alcohol is preferably butyl benzyl phthalate. A suitable commercially available butyl benzyl phthalate is Santicizer® 160, available from Monsanto. A variety of surfactants may be used. The surfactant may be cationic, 20 anionic or non-ionic. Preferably the surfactant is a cationic surfactant such as an amino derivative of a glycerol ester of a long chain fatty acid. Suitably, the surfactant is tallowpropane diamine dioleate. Supplementary Components for the Dispersion Formulation The dispersion formulation may also comprise additional components 25 such as a metal carbonate, a white metal oxide, an alkaline earth metal salt of a
C
9
-C
20 aliphatic fatty acid, a lower alkyl methacrylate polymer, a solvent and a rust inhibitor. The metal carbonate may be any metal carbonate, e.g. carbonates of lithium, sodium, potassium, magnesium, and calcium. Preferably the metal 30 carbonate is calcium carbonate. The calcium carbonate may be provided in the form of hakuenka cc manufactured by Shiraishi Kogyo Kaisha, Ltd., available in Australia from Chemiplas P/L.
WO 2005/085341 PCT/AU2005/000300 8 If a white metal oxide pigment is to be used in the dispersion it may take the form of any white metal oxide, e.g. oxides and dioxides of zinc, manganese and aluminium and white "d-block" metal dioxides. Suitable metal oxides include titanium dioxide such as the commercially available White RCL 575 available 5 from Tioxide P/L or Tiona RCL 575 available from Millennium Chemicals P/L. The alkaline earth metal salt of a C 9
-C
20 aliphatic fatty acid may be any stearate or other octadecanoic acid of an alkaline earth metal. Preferably, the stearate is a calcium salt. The lower alkyl methacrylate polymer may be a polymer of a lower 10 alkylmethacrylate or a polymer of a lower alkyl methacrylate derivative. By "lower alkyl" is meant C 1
-C
4 alkyl. Preferably, the lower alkyl methacrylate polymer is an ethyl methacrylate polymer. The lower alkyl methacrylate polymer can be a homopolymer, a copolymer or an acrylic polymer. Suitable acrylic polymers may be selected from the Paraloid@ and Plexigum@ family of resins 15 and the commercially available Paraloid® B72, Plexigum® N743 and Plexigum® N742 are suitable. Paraloid® B72, Plexigum® N743 and Plexigum® N742 are available from R6hm GmbH & Co., KG D-64275 Darmstadt Germany. Degalan LP65/12 is also a suitable polymer and is available from R6hm GmbH & Co., KG D-64275 Darmstadt Germany and also available from Degussa Australia P/L. 20 Solvents selected from solvents based on a glycol ester or a glycol derivative or low molecular weight (C1i-C 6 ) ketones based on propanones, butanones and pentanones may be used as the solvent. Suitably, the solvent is selected from one or more of methyl iso butyl ketone, methyl ethyl ketone, ethyl acetate, ethanol and isopropyl alcohol. Preferably, the solvent is methyl ethyl 25 ketone or ethyl acetate. The rust inhibitor may be any metal hydroxy phosphite selected from an alkaline earth metal hydroxy phosphite compound and metal tannates and metal derivatives of phosphoric acid. Preferably the rust inhibitor is a zinc hydroxy compound such as Nalzin 2. Nalzin 2 is available from Rheox Inc. Co and 30 distributed in Australia by ISM P/L. First Dispersion Formulation (180/9101) WO 2005/085341 PCT/AU2005/000300 9 The first dispersion comprises a metal carbonate, a white metal oxide pigment, an alkaline earth metal salt of a C 9
-C
20 aliphatic fatty acid, a thermoplastic polymer, a lower alkyl methacrylate polymer, a phthalate ester of a
CI-C
6 alkylated aromatic alcohol, a surfactant, and a solvent all as described 5 above. Preferably, the metal carbonate is calcium carbonate present between 19.175 and 10.325 parts by weight of the dispersion. More preferably, the metal carbonate is present between 17.7 and 11.8 parts by weight and more preferably, between 16.225 and 13.275 parts by weight of the dispersion. More preferably 10 still the metal carbonate is present at 14.75 parts by weight of the dispersion. Preferably, the white metal oxide is titanium dioxide such as the commercially available White RCL 575. Preferably, the white metal oxide is present between 8.229 and 4.431 parts by weight of the dispersion. More preferably, the white metal oxide is present between 7.596 and 5.064 parts by 15 weight and even more preferably between 6.963 and 5.697 parts by weight of the dispersion. More preferably the white metal oxide is present at 6.33 parts by weight of the dispersion. Preferably, the alkaline earth metal salt of a C 9
-C
2 0 aliphatic fatty acid is calcium stearate present between 0.455 and 0.245 parts by weight of the 20 dispersion, more preferably between 0.42 and 0.28 parts by weight, more preferably between 0.385 and 0.315 parts by weight and more suitably, is present at approximately 0.35 parts by weight of the dispersion. Preferably, the thermoplastic polymer, is cellulose acetate butyrate, present between 2.782 and 1.498 parts by weight of the dispersion and more 25 preferably, between 2.568 and 1.712 parts by weight. Still more preferably, the thermoplastic polymer is present between 2.354 and 1.916 parts by weight of the dispersion and preferably still, is present at 2.14 parts by weight of the dispersion. Preferably, the lower alkyl methacrylate polymer is Plexigum® N743 present between 2.782 and 1.498 parts by weight of the dispersion. Preferably, the 30 lower alkyl methacrylate polymer is present between 2.568 and 1.712 parts by weight and more preferably, between 2.354 and 1.916 parts by weight of the WO 2005/085341 PCT/AU2005/000300 10 dispersion. Preferably still, the lower alkyl methacrylate polymer is present at 2.14 parts by weight of the dispersion. The phthalate ester of a C 1
-C
6 alkylated aromatic alcohol is preferably butyl benzyl phthalate present between 1.17 and 0.63 parts by weight of the 5 dispersion. More preferably, the phthalate ester of a C 1
-C
6 alkylated aromatic alcohol is present between 1.08 and 0.72 parts by weight, more preferably between 0.99 and 0.81 parts by weight and even more preferably, is present at 0.9 parts by weight of the dispersion. Preferably the surfactant is tallowpropane diamine dioleate present 10 between 0.221 and 0.119 parts by weight of the dispersion. More preferably the surfactant is present between 0.204 and 0.136 parts by weight, more preferably is present between 0.187 and 0.153 parts by weight and still more preferably is present at 0.2 parts by weight of the dispersion. Preferably the solvent is methyl ethyl ketone present between 3.64 and 15 1.96 parts by weight of the dispersion. Preferably, the ketone is present between 3.36 and 2.24 parts by weight and even more preferably, between 3.08 and 2.52 parts by weight of the dispersion. Still more preferably, the ketone is present at 2.8 parts by weight of the dispersion. Second Dispersion Formulation (180/9020) 20 The second dispersion comprises a white metal oxide pigment, a thermoplastic polymer, a phthalate ester of a CI 1
-C
6 alkylated aromatic alcohol, a surfactant, and a solvent all as described above. Preferably the white metal oxide pigment is titanium dioxide present between 32.5 and 17.5 parts by weight of the dispersion. Preferably, the white 25 metal oxide pigment is present between 30 and 20 parts by weight and more preferably, between 27.5 and 22.5 parts by weight of the dispersion. Still preferably, the dioxide is present at 25 parts by weight of the dispersion. Preferably the thermoplastic polymer is cellulose acetate butyrate present between 8.45 and 4.55 parts by weight of the dispersion and more preferably, 30 between 7.8 and 5.2 parts by weight of the dispersion. Even more preferably, the thermoplastic polymer is present between 7.15 and 5.85 parts by weight and still preferably, is present at 6.5 parts by weight of the dispersion.
WO 2005/085341 PCT/AU2005/000300 11 Preferably the phthalate ester of a CI-C 6 alkylated aromatic alcohol is butyl benzyl phthalate present between 2.08 and 1.12 parts by weight of the dispersion and more preferably, between 1.92 and 1.28 parts by weight of the dispersion. Even more preferably, the phthalate ester of a C 1
-C
6 alkylated 5 aromatic alcohol is present between 1.76 and 1.44 parts by weight of the dispersion and still more preferably, is present at 1.6 parts by weight of the dispersion. Preferably the surfactant is tallowpropane diamine dioleate present between 0.325 and 0.175 parts by weight of the dispersion. More preferably, the 10 surfactant is present between 0.3 and 0.2 parts by weight, more preferably between 0.275 and 0.225 parts by weight and even more preferably the surfactant is present at 0.25 parts by weight of the dispersion. Preferably the solvent is present between 4.94 and 2.66 parts by weight of the dispersion. More suitably the solvent is present between 4.56 and 3.04 parts 15 by weight of the dispersion and even more suitably is present between 4.18 and 3.42 parts by weight of the dispersion. Still more suitably the solvent is present at 3.8 parts by weight of the dispersion. Preferably the solvent comprises methyl ethyl ketone, ethanol and isopropyl alcohol. Preferably the methyl ethyl ketone is present between 0.78 and 20 0.42 parts by weight of the dispersion. More suitably, the methyl ethyl ketone is present between 0.72 and 0.48 parts by weight of the dispersion and even more suitably, is present between 0.66 and 0.54 parts by weight of the dispersion. Still more suitably, the methyl ethyl ketone is present at 0.6 parts by weight of the dispersion. 25 Preferably the isopropyl alcohol is present between 1.56 and 0.84 parts by weight of the dispersion and more preferably, between 1.44 and 0.96 parts by weight of the dispersion. Even more preferably, the isopropyl alcohol is present between 1.32 and 1.08 parts by weight of the dispersion and still preferably, is present at 1.2 parts by weight of the dispersion. 30 Preferably the ethanol is present between 2.6 and 1.4 parts by weight of the dispersion. Still more preferably, ethanol is present between 2.4 and 1.6 parts by weight of the dispersion and even more preferably, between 2.2 and 1.8 parts WO 2005/085341 PCT/AU2005/000300 12 by weight of the dispersion. Preferably still, ethanol is present at 2 parts by weight of the dispersion. Third Dispersion Formulation (180/9103) The third dispersion formulation comprises a metal carbonate, and an 5 alkaline earth metal salt of a C 9
-C
2 0 aliphatic fatty acid of type and amount as described above for the first dispersion formulation (180/9101). The third dispersion formulation also contains a white metal oxide of the type described for the first dispersion formulation. In the third dispersion formulation the white metal oxide is preferably present between 5.2 and 2.8 parts 10 per weight of the dispersion, more preferably between 4.8 and 3.2 parts per weight of the dispersion, and still more preferably between 4.4 and 3.6 parts per weight of the dispersion. More preferably the white metal oxide is present at 4.0 parts by weight of the dispersion. The third dispersion formulation also contains a thermoplastic polymer of 15 the type described for the first dispersion formulation. In the third dispersion formulation the thermoplastic polymer is preferably present between 2.847 and 1.533 parts per weight of the dispersion, more preferably between 2.628 and 1.752 parts per weight of the dispersion, and still more preferably between 2.409 and 1.971 parts per weight of the dispersion, and even more preferably in an 20 amount of 2.19 parts per weight. The third formulation also contains a lower alkyl methacrylate polymer, preferably Degalan LP65/12 . In the third dispersion formulation the lower alkyl methacrylate polymer is preferably present between 2.847 and 1.533 parts per weight of the dispersion, more preferably between 2.628 and 1.752 parts by 25 weight of the dispersion, and still more preferably between 2.409 and 1.971 parts per weight of the dispersion, and even more preferably in an amount of 2.2 parts per weight of the dispersion. The third dispersion formulation also contains a phthalate ester of a C 1
-C
6 alkylated aromatic alcohol of the type described for the general dispersion or 30 'chip' formulation above. In the third dispersion formulation the phthalate ester of a CI-C 6 alkylated aromatic alcohol is preferably present between 1.209 and 0.651 parts by weight, more preferably between 1.116 and 0.744 parts by weight, WO 2005/085341 PCT/AU2005/000300 13 and more preferably between 1.023 and 0.837 parts by weight. Even more preferably the phthalate ester of a CI-C 6 alkylated aromatic alcohol is present in the third dispersion in an amount of 0.93 parts by weight. Additionally, the third formulation also contains a surfactant of the type 5 described for the general dispersion or 'chip' formulation above. In the third dispersion formulation the surfactant is preferably present between 0.195 and 0.105 parts by weight of the dispersion, more preferably present between 0.18 and 0.12 parts by weight of the dispersion and more preferably present between 0.165 and 0.135 parts by weight of the dispersion. More preferably still the surfactant is 10 present at 0.15 parts by weight of the dispersion. The third dispersion also contains a solvent, as described for the supplementary components for the dispersion formulation above. Preferably the solvent is ethyl acetate present between 2.6 and 1.4 parts by weight of the dispersion. Preferably, the solvent is present between 2.4 and 1.6 parts by weight 15 and even more preferably, between 2.2 and 1.8 parts by weight of the dispersion. Still more preferably, the solvent is present at 2.0 parts by weight of the dispersion. Additionally, the third dispersion formulation comprises a rust inhibitor as described in the supplementary components for the dispersion formulation above. 20 Preferably the rust inhibitor is zinc hydroxy phosphite present between 3.25 and 1.95 parts per weight of the dispersion, more preferably between 3.0 and 2.0 parts per weight of the dispersion, more preferably between 2.75 and 2.25 parts by weight and still more preferably at 2.5 parts by weight of the dispersion. Primers 25 One or more of the above dispersions may be incorporated into a primer for application to a surface. General primer The percentage amounts given for the preferred components of the primer formulation are the percentage amount in the final primer formulation. 30 The general primer may be used in the manufacture of specific primers, e.g. a white primer, a metal primer, and a plastic hi fill primer as discussed below. When the general primer is used to manufacture a specific primer it is understood WO 2005/085341 PCT/AU2005/000300 14 that the components of the general primer are mixed in the amounts specified for the general primer below. The primers are called "white primer", "metal primer' and "plastic hi fill primer" for ease of reference only, they are not restricted to these specific uses. 5 For example, the "metal primer" may be applied to plastic, ceramic, composite material or other non-metal materials. Similarly the "plastic hi fill primer" may be applied to metal, ceramic, composite material or other non-plastic materials. General primer composition In addition to one or more dispersion the general primer formulation 10 preferably comprises a primer solvent, a lower alkyl methacrylate polymer, a C 1 C 6 ketone, a CI-C 6 ester, a phthalate ester of a C 1
-C
6 alkylated aromatic alcohol, a polymeric plasticizer and a halogenated polyolefin. Preferably the primer comprises a primer solvent used as a suspending liquid or vehicle of the primer. A suitable primer solvent is an aromatic 15 hydrocarbon. Preferably the aromatic hydrocarbon is selected from xylol and toluol. Preferably the aromatic hydrocarbon comprises both toluol and xylol. Preferably the primer solvent is present between 39 and 21 % of the primer, more preferably between 36 and 24 % of the primer, more preferably between 33 and 27% of the primer and still more preferably at 30 % of the primer. 20 Preferably the toluol is between 27.95 and 15.05 % of the primer, more preferably between 25.8 and 17.2 % of the primer, more preferably between 23.65 and 19.35 % of the primer and even more preferably at 21.5 % of the primer. Preferably the xylol is present between 11.18 and 6.02 % of the primer, more preferably between 10.32 and 6.88 % of the primer, more preferably 25 between 9.46 and 7.74 and even more preferably at 8.6 % of the primer. Preferably the primer includes a lower alkyl methacrylate polymer as described for the general dispersion above. Preferably, the lower alkyl methacrylate polymer is present between 9.1 and 4.9 % of the primer, and more preferably, between 8.4 and 5.6 %. Preferably still, the lower alkyl methacrylate 30 polymer is present between 7.7 and 6.3 %, and even more preferably, the lower alkyl methacrylate polymer is present at 7 % of the primer.
WO 2005/085341 PCT/AU2005/000300 15 The primer preferably includes a C 1
-C
6 ketone selected from propanones, butanones and pentanones. Suitably, the C 1
-C
6 ketone is based on a butanone. Preferably the CI-C 6 ketone is present between 29.25 and 15.75 % of the primer, more preferably between 27 and 18 % of the primer, more preferably between 5 24.75 and 20.25 and even more preferably at 22.5 % of the primer. More suitably, the C 1
-C
6 ketone comprises both methyl iso butyl ketone and methyl ethyl ketone. Preferably methyl iso butyl ketone is present between 8.06 and 4.34 % of the primer, more preferably, between 7.44 and 4.96 % of the primer, and more preferably between 6.82 and 5.58 % of the primer. Still more 10 preferably, methyl iso butyl ketone is present at 6.2 % of the primer. Preferably, methyl ethyl ketone is present between 21.19 and 11.41 % of the primer, more preferably between 19.56 and 13.04 % of the primer, and more preferably between 17.93 and 14.67 % of the primer. Still more preferably the methyl ethyl ketone is present at 16.3 % of the primer. 15 The primer preferably includes a CI-C 6 ester based on methyl, ethyl, propyl and butyl chains. Also suitable are low molecular weight acetates such as diethylether and ethyl acetate. Suitably, the CI-C 6 ester ester is n-butyl acetate. Preferably, the C 1
-C
6 ester is present between 28.08 and 15.12 % in the primer. More preferably, the C 1
-C
6 ester is present between 25.92 and 17.28 % and even 20 more preferably, between 23.76 and 19.44 %. Preferably still, the C 1
-C
6 ester is present at 21.6 % of the primer. Preferably, a phthalate ester of a C 1
-C
6 alkylated aromatic alcohol as described for the general dispersion or 'chip' formulation is used in the general primer formulation. Preferably the phthalate ester of a CI-C 6 alkylated aromatic 25 alcohol is present between 0.182 and 0.098 % of the primer. More preferably, the phthalate ester of a C 1
-C
6 alkylated aromatic alcohol is present between 0.168 and 0.112 %, and more preferably between 0.154 and 0.126 % of the primer. Even more preferably the phthalate ester of a C 1
-C
6 alkylated aromatic alcohol is present at 0.14 % of the primer. 30 Preferably the primer includes a polymeric plasticizer selected from non migratory polymeric plasticizers. Suitably, the polymeric plasticizer is the WO 2005/085341 PCT/AU2005/000300 16 commercially available polymeric plasticizer Replas 150. Replas 150 is available from Townsend Chemicals, Melbourne, Victoria, Australia. Preferably, the polymeric plasticizer is present between 1.82 and 0.98 % of the primer, more preferably between 1.68 and 1.12 %, and more preferably 5 between 1.54 and 1.26 %. Preferably still, the chlorinated polyolefin is present at 1.4%. Preferably the primer comprises a halogenated polyolefin selected from polyolefins containing various percentages of xylene as solids. Suitable halogenated polyolefins include the chlorinated polyolefin 343-3 (50 % solids in 10 xylene) and chlorinated polyolefin 153-2 (25 % solids in xylene). Suitably, the chlorinated polyolefin is the commercially available chlorinated polyolefin CP 343-3. CP 343-3 and CP 153-2 are manufactured by and available from Eastman Chemical Limited. Preferably, the halogenated polyolefin is present between 1.3 and 0.7 % of 15 the primer, more preferably, between 1.2 and 0.8 % and more preferably between 1.1 and 0.9% of the primer. Preferably still, the halogenated polyolefin is present at 1%. White Primer The components of the general primer composition may be combined, in 20 the amounts within the ranges specified above, with other components to manufacture a white primer. In addition to the components of the general primer composition the white primer preferably comprises the first dispersion and the second dispersion. All percentage values given for components of the primers are percentages in the primer composition. 25 Preferably the first dispersion is present between 20.8 and 11.2 % of the white primer, more preferably between 19.2 and 12.8 % of the white primer, still more preferably between 17.6 and 14.4 % of the white primer, and even more preferably at 16 % of the metal primer. Preferably the second dispersion is present between 0.52 and 0.28 % of 30 the white primer, more preferably between 0.48 and 0.32 % of the white primer, still more preferably between 0.44 and 0.36 % of the white primer, and even more preferably at 0.4 % of the white primer.
WO 2005/085341 PCT/AU2005/000300 17 Metal Primer The components of the general primer composition may be combined, in the amounts specified above, with other components to manufacture a metal primer. In addition to the components of the general primer composition the metal 5 primer preferably comprises the first dispersion, the second dispersion, and the third dispersion. Preferably the first dispersion is present between 17.94 and 9.66 % of the metal primer, more preferably between 16.56 and 11.04 % of the metal primer, still more preferably between 15.18 and 12.42 % of the metal primer, and even 10 more preferably at 13.8 % of the white primer. Preferably the second dispersion is present between 0.52 and 0.28 % of the metal primer, more preferably between 0.48 and 0.32 % of the metal primer, still more preferably between 0.44 and 0.36 % of the metal primer, and even more preferably at 0.4 % of the metal primer. 15 Preferably the third dispersion is present between 2.73 and 1.47 % of the metal primer, more preferably between 2.52 and 1.68 % of the metal primer, still more preferably between 2.31 and 1.89 % of the metal primer, and even more preferably at 2.1 % of the metal primer. Plastic Hi Fill Primer 20 The components of the general primer composition, in the amounts specified in the ranges above, may be combined with other components to manufacture a plastic hi fill primer. In addition to the components of the general primer composition the plastic hi fill primer preferably comprises the first dispersion, the second dispersion, an alcohol, a thermoplastic polymer, a 25 polyhydroxy magnesium silicate derivate, and a silicon dioxide powder. Preferably the first dispersion is present between 16.9 and 9.1 % of the plastic hi fill primer, more preferably between 15.6 and 10.4 % of the plastic hi fill primer, still more preferably between 14.3 and 11.7 % of the plastic hi fill primer, and even more preferably at 13 % of the plastic hi fill primer. 30 Preferably the second dispersion is present between 0.325 and 0.175 % of the plastic hi fill primer, more preferably between 0.3 and 0.2 % of the plastic hi WO 2005/085341 PCT/AU2005/000300 18 fill primer, still more preferably between 0.275 and 0.225 % of the plastic hi fill primer, and even more preferably at 0.25 % of the plastic hi fill primer. Preferably the alcohol in the primer (the primer alcohol or alcohol solvent) is a CI 1
-C
6 aliphatic primary alcohol. Preferably the alcohol is n-butanol. 5 Preferably the alcohol is present between 2.6 and 1.4 % of the plastic hi fill primer, more preferably between 2.4 and 1.6 % of the plastic hi fill primer, still more preferably between 2.2 and 1.8 % of the plastic hi fill primer, and even more preferably at 2% of the plastic hi fill primer. Preferably the thermoplastic polymer is a thermoplastic polymer as 10 defined for the general dispersion or 'chip' formulation above. Preferably the thermoplastic polymer is the commercially available CAB 381-2 polymer. Preferably the thermoplastic polymer is present between 0.195 and 0.105 % of the plastic hi fill primer, more preferably between 0.18 and 0.12 % of the plastic hi fill primer, still more preferably between 0.165 and 0.135 % of the 15 plastic hi fill primer, and even more preferably at 0.15 % of the plastic hi fill primer. Preferably the polyhydroxy magnesium silicate derivate is any polyhydroxy magnesium silicate derivate. More preferably the polyhydroxy magnesium silicate derivates is a talc such as CAS No. 14807-96-6 available from 20 Bronson and Jacobs Pty Ltd. Sydney, Australia. Preferably the polyhydroxy magnesium silicate derivate is present between 12.87 and 6.93 % of the plastic hi fill primer, more preferably between 11.88 and 7.92 % of the plastic hi fill primer, still more preferably between 10.89 and 8.91 % of the plastic hi fill primer, and even more preferably at 9.9 % of the 25 plastic hi fill primer. Preferably the silicon dioxide powder is any silicon dioxide powder. More preferably the silicon dioxide powder is an organically surface treated silicon dioxide power such as Acematt OK 412 available from Degussa. Preferably the silicon dioxide powder is present between 0.26 and 0.14 % 30 of the plastic hi fill primer, more preferably between 0.24 and 0.16 % of the plastic hi fill primer, still more preferably between 0.22 and 0.18 % of the plastic hi fill primer, and even more preferably at 0.2% of the plastic hi fill primer.
WO 2005/085341 PCT/AU2005/000300 19 Adhesion Promoter To promote adhesion of primers to difficult to coat surfaces, such as PE, the surface can be coated with an adhesion promoter, and then coated with the general primer or a specific primer. Preferably the adhesion promoter comprises 5 an aromatic hydrocarbon, a co-polymer of a C 2
-C
6 alkene and a vinyl ester and a chlorinated polyolefin. The aromatic hydrocarbon preferably comprises all aromatic hydrocarbons including alkylated aromatic hydrocarbons. Preferably the aromatic hydrocarbon is one or both of toluol and xylol. Preferably the aromatic hydrocarbon is present 10 between 95 and 57.75 %, more preferably between 90 and 66, more preferably between 85 and 74.25% and still more preferably 82.5 % of the adhesion promoter. More preferably the aromatic hydrocarbon comprises both toluol and xylol. Preferably the toluol is present between 90 and 50.75 and the xylol present 15 between 13 and 7 % of the adhesion promoter, more preferably the toluol is present between 87 and 58 % and the xylol is present between 12 and 8%, more preferably the toluol is present between 79.75 and 65.25% and the xylol is present between 11 and 9%, and still more preferably the toluol is present at 72.5 % and the xylol is present at 10% of the adhesion promoter composition. 20 Co-polymers of a C 2
-C
6 alkene with a vinyl ester such as ethylene vinyl acetate are used in the adhesion promoter formulation. Suitable co-polymers of
C
2
-C
6 alkene with vinyl esters include Elvax 260 available from DuPont E.I. DuPont-de Namours and Co. Inc. Preferably, the copolymer of a C 2
-C
6 alkene with a vinyl ester is present between 3.25 and 1.75 % of the adhesion promoter, 25 more preferably between 3 and 2 %, more preferably the copolymer is present between 2.75 and 2.25 % and even more preferably at 2.5 % of the adhesion promoter. Preferably the chlorinated polyolefin used is the commercially available chlorinated polyolefin 153-2 (25% in xylene). Preferably, the chlorinated 30 polyolefin is present between 19.5 and 10.5 % of the adhesion promoter, more preferably between 18 and 12 % and even more preferably between 16.5 and WO 2005/085341 PCT/AU2005/000300 20 13.5 % the adhesion promoter. Still preferably, the chlorinated polyolefin is present at 15 % of the adhesion promoter. Method ofManufacturing Primers Preferably the primers are made by mixing a first primer solution in a first 5 vessel and mixing a second primer solution in a second vessel and then mixing the first primer solution and the second primer solution together to make the primer. The second vessel may be the same vessel as the first vessel or a different vessel. Preferably other components are mixed together with the first primer solution and the second primer solution to make the primer. 10 It is understood two or more of the first primer solution, the second primer solution and the other components may comprise the same component, e.g. the same primer solvent. A person of skill in the art understands portioning the components in the first primer solution, the second primer solution and the other components must amount to the total amount required for the primer solution. 15 For example a portion of the component may be added to the first primer solution, a portion of the same component added to the second component and the remainder of the same component added to the other components. First primer solution Preferably the first primer solution comprises the primer solvent and a 20 lower alkyl methacrylate polymer. All % amounts are % in the first primer solution. Preferably, the primer solvent of the first primer solution is toluol. Preferably the primer solvent is present in an amount of 71.5 to 38.5 % of the first primer solution, more preferably the amount is 66 to 4 %, more preferably the 25 amount is 60.5 to 49.5%, and still more preferably the amount is 55 % of the first primer solution. Preferably, the lower alkyl methacrylate polymer is present in an amount of 58.55 to 31.5 % of the first primer solution, more preferably the amount is 54 to 36 %, more preferably the amount is 49.5-40.5 % and still more preferably the 30 amount is 45 % of the first primer solution. Preferably the first solution for mixing the white primer solution and the plastic hi fill primer comprises Plexigum® N743 as the lower alkyl methacrylate WO 2005/085341 PCT/AU2005/000300 21 polymer. Preferably the first solution for mixing the metal primer comprises Degalan LP65/12 as the lower alkyl methacrylate polymer. Second Primer Solution Preferably the second primer solution comprises the C 1
-C
6 ketone, the C 1 5 C 6 ester, the phthalate ester of a Cl-C 6 alkylated aromatic alcohol, and one or more dispersion, all as described above. All % amounts are % amount in the second primer solution. Preferably, the C1-C 6 ketone comprises one or both of methyl isobutyl ketone and methyl ethyl ketone. Preferably the CI-C 6 ketone is present in an 10 amount of 35.49 and 19.11 % of the second primer solution, more preferably the amount is 32.76 and 21.84 %, more preferably the amount is 30.03 to 24.57% and still more preferably the amount is 27.3 % in the second primer solution. If as is preferable, methyl isobutyl ketone and methyl ethyl ketone comprise the C 1
-C
6 ketone, preferably the methyl isobutyl ketone is present in an 15 amount between 20.8 and 11.2 % of the second primer solution and the methyl ethyl ketone is present in an amount between 14.69 and 7.91 of the second primer solution, more preferably the amount is between 19.2 and 12.8 % methyl isobutyl ketone and between 13.56 and 9.04 % methyl ethyl ketone, more preferably the amount is between 17.6 and 14.4% methyl isobutyl ketone and between 12.43 and 20 10.17 % methyl ethyl ketone, and still more preferably the amount is 16 % methyl isobutyl ketone and 11.3 % methyl ethyl ketone in the second primer solution. Preferably the CI-C 6 ester is present in an amount between 39 and 21% of the second primer solution, more preferably the amount is between 36 and 24 %, more preferably the amount is between 33 and 24 %, and still more preferably the 25 amount is 30 % of the second primer solution. Preferably the phthalate ester of a CI-C 6 alkylated aromatic alcohol is present in an amount between 0.468 and 0.252 % of the second primer solution, more preferably the amount is between 0.432 and 0.288 %, more preferably the amount is between 0.396 and 0.324%, and still more preferably the amount is 30 0.36 % of the second primer solution. Preferably the dispersions are included in the second primer solution in amounts that will satisfy the preferable % amounts for the primer solution that is WO 2005/085341 PCT/AU2005/000300 22 being manufactured. A person of skill in the art is readily able to calculate the amounts based on the percentage values given for the dispersions in the primers above. Mixing First Primer Solution and Second Primer Solution 5 The components mixed with the first primer solution and the second primer solution to manufacture the primer solution preferably comprise the CI-C 6 ester, the CI-C 6 ketone, the primer solvent, the polymeric plasticizer, and the halogenated polyolefin, all of type described above. All % amounts are % amount of the components mixed with the first primer solution and the second 10 primer solution to manufacture the primer solution. Preferably the first primer solution in an amount between 20.15 and 10.85 % and the second primer solution in an amount between 50.31 and 27.09 % of the primer solution are mixed to manufacture the primer solution, more preferably the amounts are between 18.6 and 12.4 % first primer solution and between 46.44 and 15 30.96% second primer solution, more preferably the amounts are between 17.05 and 13.95% first primer solution and between 42.57 and 34.83% second primer solution. Still more preferably the first primer solution is present in the final primer in an amount of 15.5 % and the second primer solution is present in the final primer in an amount of 38.7 %. 20 Preferably the CI-C 6 ester is present in an amount between 13 and 7 %, more preferably in an amount between 12 and 8 %, more preferably in an amount between 11 and 9 %, and still more preferably in an amount of 10 %. Preferably the C 1
-C
6 ketone is present in an amount between 15.6 and 8.4%, more preferably the CI-C 6 ketone is present in an amount between 14.4 and 25 9.6%, more preferably the CI-C 6 ketone is present in an amount between 13.2 and 10.8%, and even more preferably the C 1
-C
6 ketone is present in an amount of 12%. Preferably the primer solvent is present in an amount between 27.95 and 15.05 %, more preferably the primer solvent is present in an amount between 25.8 30 and 17.2%, more preferably the amount is between 23.65 and 19.35%, and even more preferably in an amount of 21.5% of the primer solution.
WO 2005/085341 PCT/AU2005/000300 23 Preferably the polymeric plasticizer is present in an amount between 1.82 and 0.98 %, more preferably in an amount between 1.68 and 1.12%, more preferably the amount is between 1.54 and 1.26%, and even more preferably the polymeric plasticizer is present in an amount of 1.4 %. 5 Preferably the halogenated polyolefin is present in an amount between 1.3 and 0.7%, more preferably in an amount between 1.2 and 0.85%, more preferably in an amount between 1.1 and 0.9%, and even more preferably in an amount of 1.0%. So that the invention can be understood in more detail, the skilled person 10 is referred to the following non-limiting preferred embodiments. EXAMPLES The paintable primer system of the invention comprises a primer containing one or more dispersions or 'chips'. The paintable primer system may also comprise an adhesion promoter. 15 EXAMPLE 1 Dispersion Compositions First Dispersion ('180/9101 Chip') Constituents Trade Names parts by 'Range +/ weight Calcium Carbonate Hakuenka CC 14.8 15 % (Synthetic) Titanium Dioxide White RCL 575 6.3 25 % Calcium Stearate Calcium Stearate 0.4 20 % Cellulose Acetate Butyrate CAB 381-2 2.1 25 % Acrylic Polymer Plexigum® N743 2.1 25 % Butyl Benzyl Phthalate Santicizer® 160 0.9 25 % 2180/9101 Liquid 3.0 Tallow Diamine Dioleate 0.2 25 % Methyl ethyl ketone 2.8 30% WO 2005/085341 PCT/AU2005/000300 24 1 Range +/- : indicates a guide for the percentage range in which the amount of the component may be varied. 2 Liquid components of the dispersion. 5 Second Dispersion ('180/9020 Chip') Constituents Trade Names parts by 'Range+/ weight Titanium Dioxide Tiona RCL 575 25.00 15 % Cellulose Acetate Butyrate CAB 381-2 6.50 25 % Butyl Benzyl Phthalate Santicizer@ 160 1.60 25 % 2180/9020 Liquid 4.05 Tallow Diamine Dioleate 0.25 25 % Ethanol 2.0 30% Methyl ethyl ketone 0.6 30% Isopropyl alcohol 1.2 30% SRange +/-: indicates a guide for the percentage range in which the amount of the component may be varied. 2 Liquid components of the dispersion. 10 Third Dispersion ('180/9103 Chip') Constituents Trade Names parts by 'Range +/ weight Calcium Carbonate Hakuenka CC 15.0 15 % (Synthetic) Titanium Dioxide White RCL 575 4.0 25 % Calcium Stearate Calcium Stearate 0.35 20 % Cellulose Acetate Butyrate CAB 381-2 2.19 25 % Acrylic Polymer Degalan@ LP65/12 2.19 25 % Butyl Benzyl Phthalate Santicizer@ 160 0.93 25 % Rust inhibitor Nalzin 2 2.5 25 % WO 2005/085341 PCT/AU2005/000300 25 2180/9103 Liquid 2.15 Tallow Diamine Dioleate 0.15 25% Ethyl Acetate 2.00 30% Range +/- : indicates a guide for the percentage range in which the amount of the component may be varied. 2 Liquid components of the dispersion. 5 EXAMPLE 2 Dry grinding process of the dispersion The dispersion compositions of Example 1 are produced by the following method. Calcium carbonate, titanium dioxide and calcium stearate are blended into a first vessel. The mixture is wet down with the respective 'Liquid Mixes' or 10 solvents so as to coat the pigment particles prior to milling. In a second vessel, one or more powdered resin(s) and butyl benzyl phthalate are blended together. In formulating the first and third dispersions, the cellulose acetate butyrate and the acrylic polymer resins are used, whereas the cellulose acetate butyrate resin (only) is used in the second dispersion. 15 The above premixed compositions are put onto a mill for blending together. The resultant mix of both vessels forms a plasticine type material. This material is taken off the mill in sheet form and cut into small portions, e.g. 160 mm x 250 mm. The mill rolls are then completed closed or nipped tightly and the cut sheets are put into the mill. The pre-cut pieces form a thin sheet that is 20 continuously cut off and put back through the nip. The materials are continually ground until all the solvent is driven off, leaving a dry sheet to be taken off the mill. This sheet is then granulated to form a "chip" ready for use in manufacturing a primer. While using a white pigment, e.g. titanium dioxide in the first dispersion 25 agent is preferred, it is not essential as the second dispersion may also contain a white pigment. Specifically, the white pigment may be optionally and wholly present in a second dispersion to provide a white tinted opaque finish if desired.
WO 2005/085341 PCT/AU2005/000300 26 As an option to using both the first and second dispersion in a primer, the first dispersion may be used alone, provided an corresponding amount of the cellulose acetate butyrate resin component from the second dispersion is added to the first dispersion formulation. 5 Advantageously, this novel method of dry grinding to form the dispersion effectively disperses resins and other materials that are otherwise difficult to blend to a suitable fineness state and grinds all the ingredients to result in a solid form. This process provides a high quality lay and flow of the finished primer. To compare the effectiveness of the traditional bead mill method with that 10 of the dry mill process outlined above, the entire primer containing one or more ingredients was passed through both the traditional bead mill method and the dry mill process. Each primer was sprayed onto a bumper bar. The adhesion achieved by the primer using the traditional bead mill method was similar to that using the dry mill process. However, the primer using the bead mill method showed inferior 15 dispersion and the composition was highly textured and rough. The primer sandpaper finish was found unsuitable for the subsequent application of spray paint. In contrast, the primer produced by the dry mill method dispersed evenly and produced a glass-like finish that could be painted immediately. The above dry grinding process is contrasted to conventional liquid 20 dispersion 'mill grind' liquid dispersion methods used in other formulations. In this process, the components are dissolved in solvents and plasticisers and the mixture is then passed through a cylinder containing porcelain beads which continuously collide against each another and the material within the vessel. The frictional bead mill action acts to disperse the components within the mixture. 25 However, the degree of component dispersion in the conventional method is lower as compared to that of the present inventors' novel dry mill method. It may be appreciated by a skilled person that the dispersions may be alternatively produced by the conventional methods of liquid dispersion methods as described above, as well as by known extrusion techniques. 30 EXAMPLE 3 Polyethylene Adhesion Promoter Composition WO 2005/085341 PCT/AU2005/000300 27 Toluol (50.0%) is heated (65 -70 oC) in a water jacket under dry conditions. The solution is left to stand (10 to 15 min), to which is then added resin Elvax 260 (2.5 %) with continuous mixing. Once complete solubility is obtained, the mixture is readjusted (by weight) to make up any lost toluol. A 5 mixture of toluol (7.5 %) and xylol (25 %) is then added. To the cooled mixture is added chlorinated polyolefin CP 153-2 (25 % in xylene) (15.0 %) and stirred. EXAMPLE 4 Primer Composition White Primer 10 The weight amounts in brackets below are weight added, the percentage amounts below are % in the primer. The amounts provided for the components of the primers below are non limiting examples. The non-limiting examples are provided for guidance and it is appreciated that each of the components can be varied within 30% of the stated 15 amount, more preferably within 25% of the stated amount, more preferably within 20% of the stated amount, more preferably within 15% of the stated amount, more preferably within 10% of the stated amount and even more preferably within 5% of the stated amount. A person of skill in the art readily understand that when varying the 20 percentage of one or more component the percentage of the other components must be varied accordingly so that the some of the components equals 100 %. Plexigum N743 (44.83 kg, 6.9%) is slowly added to toluol (55.17 kg, 8.5%) and blended (2 min), and the mixture stirred, to form the first primer solution. 25 In a separate reaction vessel, each of the following is added to a continuously stirred mixture: methyl iso butyl ketone (11.2 kg, 4.3%) butyl acetate (21.0 kg, 8.1%) methyl ethyl ketone (8.0 kg, 3.06%) 30 butyl benzyl phthalate (Santicizer® 160) (0.36 kg, 0.14%) WO 2005/085341 PCT/AU2005/000300 28 To the above solution, both the first dispersion (180/9101 chip) (41.34 kg, 16%) and the second dispersion (180/9020 chip) (1.03 kg, 0.4%) as described above are slowly added to the above mixture and a thickened mixture is obtained. To the thickened mixture is added the following: 5 methyl iso butyl ketone (4.8 kg, 1.86%) n-butyl acetate (9.0 kg, 3.5%) methyl ethyl ketone (3.27 kg, 1.3%) The solution is then mixed to form the second primer solution. The first primer solution and the second primer solution are then 10 combined in a third reaction vessel. The first primer solution is added in an amount to constitute 15.40 % of the primer solution, and the second primer solution is added in an amount to constitute 38.70 % of the primer solution. The first and second primer solution are mixed while slowly adding: n-butyl acetate (10.0 kg, 10%) 15 methyl ethyl ketone (11.90 kg, 11.90 %) toluol (13.0 kg, 13.0 %) a polymeric plasticizer e.g. Replas 150 (1.4 kg, 1.4%) a halogenated polyolefin e.g. CP 343-3 (1.0 kg, 1.0%) xylol (8.6 kg, 8.6 %) 20 Metal Primer The Metal Primer is made as outlined for the White Primer with the components and component amounts adjusted as detailed for the Metal Primer above. As detailed above the Metal Primer contains the first (180/9101), second (180/9020) and third (180/9103) dispersions. 25 Plastic Hi Fill Primer The percentage amounts below are % in the plastic hi fill primer. Plexigum N743 (6.0%) is slowly added to toluol (15.95%) and blended (2 min), and the mixture stirred, to form the first primer solution. In a separate reaction vessel, each of the following is added to a 30 continuously stirred mixture: methyl iso butyl ketone (6.0%) butyl acetate (20.0%) WO 2005/085341 PCT/AU2005/000300 29 methyl ethyl ketone (15.0%) butyl benzyl phthalate (Santicizer® 160) (0.15%) n-butanol (2.0%) thermoplastic polymer (CAB 381-2) (0.15%) 5 a polymeric plasticizer (Replas 150) (1.0%) To the above solution, both the first dispersion (180/9101 chip) (13%) and the second dispersion (180/9020 chip) (0.25%) as described above are slowly added to the above mixture and a thickened mixture is obtained. When the components of the thickened mixture are completely dissolved 10 to the thickened mixture is added the following: polyhydroxy magnesium silicate derivate (9.9%) The solution is then mixed to form the second primer solution. The first primer solution and the second primer solution are then combined in a third reaction vessel. The first primer solution is added in an 15 amount to constitute 21.95 % of the primer solution to an amount of the second primer solution constituting 67.45 % of the primer solution. The first and second primer solution are mixed while slowly adding: silicon dioxide powder e.g. OK 412 (0.20%) halogenated polyolefin e.g. CP 343-3 (1.0%) 20 xylol (9.4 %). The present invention provides for a paintable primer system suitable for applying to various surfaces. For example, application of both the adhesion promoter followed by the primer is suitable for application to PE substrates. Alternatively, the primer may be applied (alone) to PP and other plastic 25 substrates and to metals and composite materials including metals and composite materials used in the auto, marine and aviation industries without the need for the adhesion promoter and still provide high adhesion to the substrate. Advantageously, the primer is flexible and is able to be tinted. In this way, the tinting assists the spray painter by permitting less topcoat paint required due to the 30 coverage of the primer. Inclusion of the third dispersion in a primer allows the primer to satisfactorily adhere to metals and composite materials, more specifically metals WO 2005/085341 PCT/AU2005/000300 30 and composite materials used in the auto, marine and aviation industries. Primers including the third dispersion will accommodate the aviation industry, the marine industry and the automotive industry. Primers including the third dispersion provide sufficient adherence to metal surfaces of new panels and already painted 5 panels. Before application of a primer comprising the third dispersion a panel surface should first be wiped down with a prepsol or cleaning solvent. EXAMPLE 5 Method of use The adhesion promoter is shaken and strained prior to application. The 10 surface to be coated, e.g. PE is wiped thoroughly with a cleaning solvent or thinners, e.g. acetone or acrylic thinners. The cleaning solvent or thinners are flashed off or removed with a clean cloth. Two medium wet coats of the adhesion promoter are applied, allowing 60 seconds flash off between each adhesion promoter coat. The polyolefin surface is heated, preferably by baking (e.g. 45 15 min, 450 C). Although this baking or 'curing' step is not essential, it is preferred as it accelerates a cross linking effect of the adhesive promoter to the polyolefin surface. The polyolefin surface is cooled to room temperature. The primer containing one or more solid dispersions or 'chips' is shaken (ca. 30 seconds), strained and 1 or 2 medium primer coats applied, allowing one 20 minute flash off time between each application. If desired, a longer period (e.g. 10 minutes) to dry before scuffing or sanding prior to painting to achieve a higher finish may be used. The polyolefin is now suitably prepared for painting with a top coat. Suitable top coats are selected from coloured tint or paint, antifouling paint agents or other top coats, e.g. acrylics, two-pack polyurethanes, polyesters 25 or cellulose based resins. The primers may also be used on surfaces without the use of the adhesion promoter. EXAMPLE 6 Adhesion performance evaluations 30 The crosshatch and tape peel test of ASTM D3359-87 was used to determine paint adhesion to a PE substrate. This test involves cutting the painted WO 2005/085341 PCT/AU2005/000300 31 substrate with a sharp bladed instrument (e.g. razor blade). Vertical (e.g. 10) and horizontal lines (e.g. 10) are cut, resulting in 100 - 2 mm squares or boxes, patterned by the cutting. Threaded adhesive tape is adhered to the cut portions and the blunt edge of the blade is rubbed over the tape insuring that the tape totally 5 adheres to all the formed boxes. The tape is removed with a quick motion. The number of boxes removed by the tape determines the level of adhesion. A 5% loss is acceptable and can be classified as total adhesion. Tests using the adhesion promoter and primer applied to PE substrates showed a 3% and 0 % loss after 24 and 48 hours respectively. Tests using the 10 metal primer applied to metal substrates (stainless steel, mild steel, aluminium, electroplated mild steel (automotive new panels)) showed a 0 % loss after 24 and 48 hours. Accelerated Weather Tests Accelerated Weather Tests were completed on a test PE substrate using 15 standard testing methodologies (Architectural & Industrial Coatings, Penrith, Australia). In the tests, 500 hours equated to 4 years of weathering to access deterioration in adhesion loss caused by weathering. The tests showed that the adhesion of the white primer to the PE had not been affected by the test weathering process. 20 The cross-hatch method was performed and showed zero loss of adhesion after 4 years of accelerated weathering. Field testing Experimental field testing was performed on PE truck bull bars travelling continuously across a hostile environment, i.e. the Nullabor Desert. These trucks 25 have sustained multiple impacts with wild fauna, e.g. kangaroos, road side posts and various airborne objects, e.g. stone chips. Analysis of the paint integrity showed no observable paint flaking on or around impacted areas. Advantageously, the paintable primer system of the present invention may be applied to existing PE substrates and need not be incorporated at the time of 30 article manufacturing, i.e. it may be applied to existing goods. Application of the present paintable primer system may be found in various fields.
WO 2005/085341 PCT/AU2005/000300 32 The paintable primer system is suitable for application to PE substrates in the form of water buoys, boats, exterior shells of cars including concept cars and automotive parts such as bull bars, bumper bars, non-metallic 'smart bars' and any plastic components of semi-trailers, horse floats and similar vehicles, 5 inclusive of the side mirrors. Further application of the paintable primer system may also be found in other manufactured PE devices, such as marketing or exhibition displays suitable for commercial and retail markets. Currently, such displays have colour introduced when the substrate is rotormoulded, however, the colouring is inferior 10 by way of smoothness or finish. Hence it is contemplated that such PE displays and the like may be painted using the present paintable primer system and provide an 'automotive' quality finish, thus enabling the company a stronger visual marketing advantage over any other. Presently, the rapid growth of the algae requires continuous maintenance 15 by way of antifoul coating on objects such as vessels and water buoys which are continuously exposed to algae in marine environments. If this maintenance is not carried out, buoys become unbalanced, thereby reducing visibility and hence safety. Algal growth decreases the performance of speedboats and the like through surface drag. 20 Until now, PE water buoys and water vessels have been unable to be successfully coated with an antifouling agent due to poor adherence of either an antifoul coating or paint. Thus it may be readily apparent that the paintable primer system may be used to carry antifouling agents to objects such as boat hulls and buoys. Further advantageously, waterway buoys may be painted to give them a 25 brighter appearance than that obtained by conventional tint moulding to enhance safety. The paintable primer system is also suitable for application to metals and composite materials such as metals and composite materials used in the auto, marine and aviation industries. 30 It may be appreciated by the skilled person that the above composition may be varied to accommodate various formulation conditions such as temperature and humidity which may influence solubilities within the mixtures. It WO 2005/085341 PCT/AU2005/000300 33 may also be appreciated that the present paintable primer system may be used to coat non plastic substrates such as gyprock, concrete, metals, ceramics. It will be appreciated by the skilled person that the present invention is not limited to the embodiments described in detail herein, and that a variety of other 5 embodiments may be contemplated which are nevertheless consistent with the broad spirit and scope of the invention.
Claims (20)
1. A dispersion comprising a thermoplastic polymer, a phthalate ester of a CI-C 6 alkylated aromatic alcohol, a surfactant and further comprising one or more components selected from the group consisting of: 5 a metal carbonate a white metal oxide, an alkaline earth metal salt of a C 9 -C 20 aliphatic fatty acid, a solvent, a rust inhibitor, and 10 a lower alkyl methacrylate polymer.
2. The dispersion of claim I wherein the lower alkyl methacrylate polymer is an ethyl methacrylate polymer.
3. The dispersion of claim 1 comprising a thermoplastic polymer, a phthalate ester of a CI-C 6 alkylated aromatic alcohol, a metal carbonate, a white metal 15 oxide pigment, an alkaline earth metal salt of a C 9 -C 20 aliphatic fatty acid, a lower alkyl methacrylate polymer, a surfactant and a solvent.
4. The dispersion of claim 1 comprising a thermoplastic polymer, a phthalate ester of a CI-C 6 alkylated aromatic alcohol, a white metal oxide pigment, a surfactant, and a solvent. 20
5. The dispersion of claim 1 further comprising a thermoplastic polymer, a phthalate ester of a C 1 -C 6 alkylated aromatic alcohol, a metal carbonate, a white metal oxide, an alkaline earth metal salt of a C 9 -C 20 aliphatic fatty acid, a lower alkyl methacrylate polymer, a surfactant, a solvent and a rust inhibitor.
6. The dispersion of Claim 1 in a solid form. 25
7. The dispersion of Claim 6 in a granulated form.
8. A primer comprising the dispersion of claim 6 and a primer solvent.
9. The primer according to claim 8 further comprising a component selected from the group consisting of: a lower alkyl methacrylate polymer, a CI-C 6 ketone, a CI-C 6 ester, a phthalate ester of a C-C 6 alkylated aromatic alcohol, a 30 halogenated polyolefin, and a polymeric plasticizer. WO 2005/085341 PCT/AU2005/000300 35
10. The primer of claim 8 further comprising a component selected from the group consisting of: an alcohol, a thermoplastic polymer, a polyhydroxy magnesium silicate derivate, and a silicon dioxide powder.
11. A primer comprising a primer solvent, a lower alkyl methacrylate 5 polymer, a CI-C 6 ketone, a Cl-C 6 ester, a phthalate ester of a CI-C 6 alkylated aromatic alcohol, a polymeric plasticizer, a halogenated polyolefin, the dispersion of claim 3, and the dispersion of claim 4.
12. A primer comprising a primer solvent, a lower alkyl methacrylate polymer, a CI-C 6 ketone, a CI-C 6 ester, a phthalate ester of a CI-C 6 alkylated 10 aromatic alcohol, a polymeric plasticizer, a halogenated polyolefin, the dispersion of claim 3, the dispersion of claim 4, and the dispersion of claim 5.
13. A primer comprising a primer solvent, a lower alkyl methacrylate polymer, a C 1 -C 6 ketone, a C 1 -C 6 ester, a phthalate ester of a CI-C 6 alkylated aromatic alcohol, an alcohol, a thermoplastic polymer, a polyhydroxy magnesium 15 silicate derivate, a silicon dioxide powder, a polymeric plasticizer, a halogenated polyolefin, the dispersion of claim 3, and the dispersion of claim 4.
14. An adhesion promoter comprising an aromatic hydrocarbon, a co-polymer of a C 2 -C 6 alkene and a vinyl ester and a chlorinated polyolefin.
15. A method of manufacturing a primer including the steps of: 20 mixing a first primer solution in a first vessel; mixing a second primer solution comprising the dispersion of claim 6 in a second vessel,; mixing the first primer solution and the second primer solution together to form the primer. 25
16. A method of manufacturing a primer comprising: mixing a first primer solution comprising a primer solvent and a lower alkyl methacrylate polymer; mixing a second primer solution comprising a CI-C 6 ketone, a Ci-C 6 ester, a phthalate ester of a C 1 -C 6 alkylated aromatic alcohol, and the dispersion of 30 claim 1; and WO 2005/085341 PCT/AU2005/000300 36 mixing the first primer solution and the second primer solution together with a C 1 -C 6 ester, a C 1 -C 6 ketone, a primer solvent, a polymeric plasticizer, and a halogenated polyolefin to form the primer.
17. The method of manufacturing a primer of claim 16 wherein the second 5 primer solution comprises the dispersion of claim 3, and the dispersion of claim 4.
18. The method manufacturing the primer of claim 16 wherein the second primer solution comprises the dispersion of claim 3, the dispersion of claim 4 and the dispersion of claim 5.
19. A method for coating a surface of an article comprising: 10 coating the surface with the adhesion promoter of claim 14; and coating the surface with the primer of claim 6.
20. An article coated with the primer of claim 8.