AU2004213383B2 - Starch-loaded polyvinyl alcohol copolymer film for packaging non-liquid product and method for making the same - Google Patents
Starch-loaded polyvinyl alcohol copolymer film for packaging non-liquid product and method for making the same Download PDFInfo
- Publication number
- AU2004213383B2 AU2004213383B2 AU2004213383A AU2004213383A AU2004213383B2 AU 2004213383 B2 AU2004213383 B2 AU 2004213383B2 AU 2004213383 A AU2004213383 A AU 2004213383A AU 2004213383 A AU2004213383 A AU 2004213383A AU 2004213383 B2 AU2004213383 B2 AU 2004213383B2
- Authority
- AU
- Australia
- Prior art keywords
- percent
- copolymer
- film
- weight
- range
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Description
WO 2004/074351 PCT/US2004/004048 STARCH-LOADED POLYVINYL ALCOHOL COPOLYMER FILM FOR PACKAGING NON-LIQUID PRODUCT AND METHOD FOR MAKING THE SAME TECHNICAL FIELD The present invention relates generally to water-soluble polyvinyl alcohol (PVOH) film. More specifically, the present invention relates to water-soluble PVOH film with particular applications for packaging of non-liquid products, such as cleansers, conditioners, disinfectants, and the like.
BACKGROUND
Polyvinyl alcohol (PVOH) is a synthetic resin generally prepared by the alcoholysis, usually termed hydrolysis or saponification, ofpolyvinyl acetate. Fully hydrolyzed PVOH, where virtually all the acetate groups have been converted to alcohol groups, is a strongly hydrogen-bonded, highly crystalline polymer which dissolves only in hot water-greater than about 1400 F (600 If a sufficient number of acetate groups are allowed to remain after the hydrolysis of polyvinyl acetate, the PVOH polymer then being known as partially hydrolyzed, it is more weakly hydrogenbonded and less crystalline and is soluble in cold water-less than about 50° F (100 C).
Both fully and partially hydrolyzed PVOH types are commonly referred to as PVOH homopolymers although the partially hydrolyzed type is technically a vinyl alcoholvinyl acetate copolymer.
The term PVOH copolymer is generally used to describe polymers that are derived by the hydrolysis of a copolymer of a vinyl ester, typically vinyl acetate, and another monomer. PVOH copolymers can be tailored to desired film characteristics by varying the kind and quantity of copolymerized monomers.
Examples of copolymerizations are those of vinyl acetate with a carboxylic acid or with an ester of a carboxylic acid. Again, if the hydrolysis of acetate groups in these copolymers is only partial, then the resulting polymer could be described as a PVOH terpolymer-having vinyl acetate, vinyl alcohol, and carboxylic acid groups-although it is commonly referred to as a copolymer.
WO 2004/074351 PCT/LS2004/004048 It is known in the art that many PVOH copolymers, because of their structure, can be much more rapidly soluble in cold water than the partially hydrolyzed type of PVOH homopolymers. Such copolymers have therefore found considerable utility in the fabrication of packaging films for the unit dose presentation of various liquid and powdered products including agrochemicals, household and industrial cleaning chemicals, laundry detergents, water treatment chemicals, and the like.
The manufacture of packaging films for liquid products poses a unique concern, as they must be free of bubbles and pin holes, and capable of resisting problems such as physical incompatibility exemplified by "weeping"-a condition whereby the package contents seep from the film over a prolonged storage periodcaused by certain components typically used in liquid detergent products. The increased level of quality required to manufacture a film and package such liquids adds significantly to the packaged product cost.
Conversely, powdered products are far more forgiving when it comes to packaging. Pin holes and micro bubbles in the film do not present problems for packaging powdered products. Physical compatibility is less problematic, due in part to the non-existence of migrating materials in powdered detergents. Weeping does not commonly occur with the packaging of powdered products. For these reasons the type and quality of PVOH film used to package powered products can be significantly varied from that for the liquid counterparts.
However, those in the powdered product industry have been directed toward the use of either the higher quality, more expensive PVOH copolymer films designed for liquid product packaging or inferior films such as less diverse and more slowly soluble homopolyiner-based films including films produced by blown extrusion.
The present invention has solved this problem of film quality versus manufacturing cost as it relates to packaging of powdered product, as well as other problems faced by those in the industry. By making a less expensive PVOH copolymer film having good water-soluble qualities, those in the industry have an alternative source for packaging powdered products.
WO 2004/074351 PCT/US2004/004048
SUMMARY
A water-soluble film suitable for packaging a non-liquid product, including the method for preparing the film composition and packaging for the nonliquid product, is disclosed. In one particular embodiment of the invention, the film combination comprises a hydrolyzed copolymer of vinyl acetate and methyl acrylate in the range of from about 30 to about 95 percent by weight, modified starch in the range of from about 4 to about 30 percent by weight, plasticizer in the range of from about to about 30 percent by weight, lubricant/release agent in the range of from about 0.0 or about 0.01 to about 1.5 percent by weight, and surfactant in the range of from about 0.01 to about 1.5 percent by weight.
In a preferred embodiment of the invention, the film composition utilizes a bleaching agent to prevent color drift, such as browning, of a polymer solution used to cast the film. Oxidizing bleaching agents chlorine, chlorinated compounds, oxygen, and oxygenated compounds) and reducing bleaching agents hydrosulfites, borohydrides, and metabisulfites) are preferred. Examples include sodium percarbonate, sodium persulfate, peracetic acid, sodium hydrosulfite and sodium metabisulfite. Sodium percarbonate and sodium metabisulfite are preferred, and sodium metabisulfite is most preferred.
Preferably the agent comprises sodium metabisulflte in an amount in the range of from about 0.12 to about 1.0 percent by weight. Most preferably, the sodium metabisulfite is used in an amount in the range of from about 0.4 to about 0.7 percent by weight.
A preferred method for preparing a water-soluble copolymer film for packaging of a non-liquid product is also disclosed and claimed. The method comprises the steps of copolymerizing vinyl acetate and methyl acrylate to form a copolymer, hydrolyzing the vinyl acetate-methyl acrylate copolymer to form a vinyl alcohol-gamma lactone copolymer having a 4% solution viscosity in the range of from about 5 to about 50 cps at 200 C, slurrying the hydrolyzed polymer with water, adding modified starch to the copolymer-water slurry in an amount of from about 4.0 to about 25.0 percent by weight, heating the hydrolyzed copolymer and starch slurry to form a WO 2004/074351 PCTIUS2004004048 solution, treating the solution with caustic soda to create a solution of a copolymer having from about 1 to about 12 mol percent carboxylate groups, from about 0 to about 11 mol percent gamma lactone units, and from about 88 to about 99 mol percent vinyl alcohol units, and then casting the hot copolymer solution on a suitable surface to create a film having a thickness in the range of from about 0.1 to about 5.0 mils (about 0.0025 to about 0.127 mm).
A package for containing a non-liquid product is also disclosed. A preferred package comprises at least one compartment comprised of a water-soluble film comprising from about 30 to about 95 percent by weight of a hydrolyzed copolymer of vinyl acetate and methyl acrylate, from about 4 to about 30 percent by weight of modified starch filler, from about 5 to about 30 percent by weight of plasticizer, and from about 0.01 to about 1.5 percent by weight of a surfactant.
In one embodiment the package may be used to deliver a unit dose of a non-liquid agent. The preferred unit dose comprises a package comprising a watersoluble film comprising from about 40 to about 90 percent by weight of a hydrolyzed copolymer of vinyl acetate and methyl acrylate, from about 4 to about 30 percent by weight of a modified starch filler, from about 5 to about 30 percent by weight of a plasticizer, and from about 0.01 to about 1.0 percent by weight of a surfactant, and a non-liquid agent contained within the package. The non-liquid agent may be a cleanser, a disinfectant, a polish, a conditioner, or the like.
Further aspects and advantages will be apparent to those of ordinary skill in the art from a review of the following detailed description, taken in conjunction with the drawings. While the film, package, and methods are susceptible of embodiments in various forms, the description hereafter includes specific embodiments with the understanding that the disclosure is illustrative, and is not intended to limit the invention to the specific embodiments described herein.
BRIEF DESCRIPTION OF THE DRAWINGS The embodiments described herein can be more readily understood with reference to the appended drawing figures where: WO 2004/074351 PCTIUS2004004048 FIGURE 1 is a perspective view of a test apparatus used to analyze the water disintegration and dissolution of film samples; FIGURE 2 is a perspective view of the test apparatus and test set-up illustrating the procedure for analyzing the water-solubility of film samples; and FIGURE 3 is a top view of the test set-up of FIGURE 2.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS While the invention is susceptible of embodiment in many different forms, this disclosure will describe in detail preferred embodiments of the invention with the understanding that the present disclosure is to be considered as an exemplification of the principles of the invention and is not intended to limit the broad aspect of the invention to the embodiments illustrated.
Film Composition: The present invention includes a water-soluble film for packaging a non-liquid product. The following is a list of terms used throughout the application: "Non-liquid" shall refer to any product that has as a component a form characteristic of a solid, including but not limited to powder, caked, shaving, solid, gel, slurry, paste, pelletized, and the like.
"Package" or "packaging" shall refer to any receptacle or method suitable for holding or enclosing, to a substantial degree, a quantity of non-liquid product, without regard to size, shape, or the number of parts used to form the container or carry out the method.
Further, all ranges set forth herein include all possible subsets of ranges and any combinations of such subset ranges. Ranges are inclusive of the stated endpoints.
The film is based on an amount of a hydrolyzed copolymer of vinyl acetate and methyl acrylate and is a vinyl alcohol-gamma lactone copolymer, in the range of fri-om about 30 to about 95 percent by weight. Preferably, the amount of copolymer is in the range of from about 50 to about 85 percent by weight. The WO 2004/074351 PCT/US2004/004048 copolymer may be prepared in any manner known by those skilled in the art. A particularly suitable copolymer is sold by E.I. duPont de Nemours under the tradename ELVANOL. The ELVANOL range of water-soluble synthetic polymers has excellent film-forming, emulsifying, and adhesive properties. Such polymers offer resistance to oil, grease and solvents, plus high tensile strength, flexibility, and high oxygen barrier.
Alternatively, and less preferably, a vinyl acetate-methyl acrylate copolymer must first undergo hydrolysis (also called alcoholysis) to form a vinyl alcohol-gamma lactone copolymer. The vinyl alcohol-gamma lactone copolymer preferably has a 4% solution viscosity in the range of from about 5 to about 50 cps (0.005 to 0.050 pascal seconds) at 20° C (680 More preferably the vinyl alcoholgamma lactone copolymer has a 4% solution viscosity in the range of from about 8 to about 35 cps (0.008 to 0.035 pascal seconds) and, most preferably, the vinyl alcoholgamma lactone copolymer has a 4% solution viscosity in the range of from about 15 to about 25 cps (0.015 to 0.025 pascal seconds).
The hydrolyzed copolymer initially comprises an amount of gamma lactone units preferably from about 2 to about 12 mol percent, more preferably from about 4 to about 6 mol percent. Modified starch is added to the hydrolyzed copolymer, which preferably is first slurried with water, in an amount in the range of from about 4 to about 30 percent by weight, preferably about 4 to about 12 percent by weight.
While other modified starches may be suitable, the preferred modified starch is hydroxyethyl modified starch in an amount of about 10 percent by weight. In another embodiment, the amount of starch is at least 5 percent by weight.
The composition also comprises plasticizer, such as in the range of from about 5 to about 30 percent by weight, preferably about 10 to about 20 percent by weight, or preferably in the range of from about 20 to about 30 percent by weight when sorbitol is present as a plasticizer.
The composition also preferably comprises lubricant/release agent in the range of from about 0.0 to about 1.5 percent by weight, and surfactant in the range of from about 0.01 to about 1.5 percent by weight. Other suitable components, such as
I
WO 2004/074351 PCT/LS2004/004048 additional plasticizers, lubricants, and release agents, fillers, extenders, antiblocking agents, detackifying agents, antifoams and other functional ingredients, may be added in proper amounts to achieve a desired effect to the extent such components do not inhibit other desired characteristics of the copolymer film.
The copolymer solution preferably is treated with caustic soda (sodium hydroxide), to yield a copolymer solution having from about 1 to about 12 mol percent, preferably from about 2 to about 6 mol percent, and most preferably from about 3 to about 4 mol percent carboxylate groups, from 0 to about 11 mol percent, preferably from 0 to about 5 mol percent, and most preferably from about 1 to about 2 mol percent gamma lactone units, and from about 88 to 99 mol percent, preferably from about 92 to about 98 mol percent, and most preferably from about 94 to about 96 mol percent vinyl alcohol units.
The copolymer solution is then cast to create a film having a thickness in the range of from about 0.5 mils to about 5.0 mils (about 0.013 to about 0.127 mm).
The film thickness can have a direct effect on the speed at which the final product will dissolve in water, with thin films less than 3.0 mil or 0.076 mm) completely dissolving in less time. Conversely, thinner films typically provide less structural protection than their thicker film counterparts. A balance must be struck between these and other factors. For many applications, a preferable film thickness is in the range of from about 0.5 to about 3.0 mils (about 0.013 to about 0.076 mm), and most preferably in the range of from about 1.0 to about 2.0 mils (about 0.025 to about 0.050 mm).
During preparation of the copolymer solution a browning effect can occur. It is desirable in most applications that the water-soluble film have a clear and colorless appearance. To combat this, and any other known color drift to which the copolymer solution may be susceptible, a suitable bleaching agent can be added to the copolymer solution. The use of sodium metabisulfite has been found to substantially maintain the solution clarity and colorlessness during preparation when used in an amount in the range of from about 0.12 to about 1.0 percent by weight, most preferably in an amount from about 0.4 to about 0.7 percent by weight.
WO 2004/074351 PCT/US2004/004048 Suitable plasticizers include, but are not limited to, glycerin, diglycerin, sorbitol, ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, propylene glycol, polyethylene glycols up to 400 MW, neopentyl glycol, trimethylolpropane, polyether polyols and ethanolamines. Preferred plasticizers are glycerin, triethyleneglycol, propylene glycol and trimethylolpropane.
Suitable surfactants may include the nonionic, cationic, anionic and zwitterionic classes. Preferably, the surfactants will be of the nonionic, cationic or zwitterionic classes or combinations of these. Suitable surfactants include, but are not limited to, polyoxyethylenated polyoxypropylene glycols, alcohol ethoxylates, alkylphenol ethoxylates, tertiary acetylenic glycols and alkanolamides (nonionics), polyoxyethylenated amines, quaternary ammonium salts and quaternized polyoxyethylenated amines (cationics), and amine oxides, N-alkylbetaines and sulfobetaines (zwitterionics). Preferred surfactants are alcohol ethoxylates, quaternary ammonium salts and amine oxides.
Suitable lubricants/release agents include, but are not limited to, fatty acids and their salts, fatty alcohols, fatty esters, fatty amines, fatty amine acetates and fatty amides. Preferred lubricants/release agents are fatty acids, fatty acid salts, and fatty amine acetates.
Suitable fillers/extenders/antiblocking agents/detackifying agents include, but are not limited to, starches, modified starches, crosslinked polyvinylpyrrolidone, crosslinked cellulose, microcrystalline cellulose, silica, metallic oxides, calcium carbonate, talc and mica. Preferred materials are starches, modified starches and silica. If used, the preferred amount of such filler/extender/antiblocking agent/detackifying agent in the water-soluble film of the present invention is between 0.1% and 25% by weight, more preferably between 1% and 15% by weight, and preferably between 1% and 5% by weight if starch is absent.
Suitable antifoams include, but are not limited to, those based on polydimethylsiloxanes and hydrocarbon blends. If used, the preferred amount of antifoam in the water-soluble film of the present invention is between 0.001% and more preferably between 0.01% and 0.1% by weight.
WO 2004/074351 PCT/LS2004/004048 Film Formation: The preferred method for preparing the water-soluble copolymer film comprises the steps ofcopolymerizing vinyl acetate and methyl acrylate to form a copolymer. Alternatively, this vinyl acetate-methyl adrylate copolymer may be more readily purchased. In either case, the next steps include hydrolyzing the vinyl acetatemethyl acrylate copolymer to form a vinyl alcohol-gamma lactone copolymer having a 4% solution viscosity in the range of from about 5 to about 50 cps at 20 0 C, and slurrying the hydrolyzed polymer with water while adding modified starch to the copolymer-water slurry in an amount of from about 4.0 to about 25.0 percent by weight. Preferably the amount of modified starch is about 4 to about 12 percent by weight. The hydrolyzed copolymer and starch slurry is then heated to boiling point to form a solution.
The solution is then treated with caustic soda to create a solution of a copolymer having from about 1 to about 12 mol percent carboxylate groups, from about 0 to about 11 mol percent gamma lactone units, and from about 88 to about 99 mol percent vinyl alcohol units. More preferable ranges have been previously stated.
The next step is maintaining the solution at a temperature in the range of from about 160° F to about 200° F (about 71°C to about 93°C), and then casting the hot copolymer solution on a suitable surface to create a film having a thickness in the range of from about 0.1 to about 5.0 mils (about 0.0025 to about 0.127mm).
The treated solution can undergo browning while being held at high temperatures. This is undesirable for most applications, wherein a clear film is sought.
Therefore, the method can further comprise the step of adding a bleaching agent, such as sodium metabisulfite, in an amount greater than 0.12 percent by weight to substantially reduce or prevent browning of the heated solution. Most preferably, a bisulfite is added in the amount of from about 0.4 to about 0.7 percent by weight.
The resulting film can then be formed into a package for containing a non-liquid product, as previously described. Steps for forming a suitable package are known by those skilled in the art for similar handling films, or can be derived without undue experimentation. A preferred requirement of the film, and therefore the formed WO 2004/074351 PCT/US2004/004048 package, is that it be capable of complete dissolution in water in a relatively short period of time. A preferred film of the present invention, at a thickness of about mil (about 0.038 mm), dissolves in water at a temperature of about 20'C in less than seconds.
The following test procedure, referred to herein as MonoSol Test Method 205 (MSTM 205), is used to determine the time required for a water-soluble film to break apart (disintegrate) and its subsequent relative dissolution time when held stationary. The test procedure is disclosed with reference to drawing FIGURES 1-3.
MonoSol Test Method 205 (MSTM 205) APPARATUS AND MATERIALS.
600 mL Beaker 12 Magnetic Stirrer 14 (Labline Model No. 1250 or equivalent) Magnetic Stirring Rod 16 (5 cm) Thermometer (0 to 1000 C, 1o C) Template, Stainless Steel (3.8 cm x 3.2 cm) Timer, (0-300 seconds, accurate to the nearest second) Polaroid 35mm Slide Mount 20 (or equivalent) MonoSol 35mm Slide Mount Holder 25 (or equivalent, see FIGURE 1) Distilled Water TEST SPECIMEN: 1. Cut three test specimens from film sample using stainless steel template 3.8 cm x 3.2 cm specimen). If cut from a film web, specimens should be cut from areas of web evenly spaced along the transverse direction of the web.
2. Lock each specimen in a separate 35 mm slide mount 3. Fill beaker 12 with 500 mL of distilled water. Measure water temperature with thermometer and, if necessary, heat or cool water to maintain temperature at 200 C (about 680 F).
4. Mark height of column of water. Place magnetic stirrer 14 on base 27 of holder 25. Place beaker 12 on magnetic stirrer 14, add magnetic stifling rod 16 to WO 2004/074351 PCTIUS2004004048 beaker 12, turn on stirrer 14, and adjust stir speed until a vortex develops which is approximately one-fifth the height of the water column. Mark depth of vortex.
Secure the 35 mm slide mount 20 in the alligator clamp 26 of the MonoSol 35mm slide mount holder 25 (FIGURE 1) such that the long end 21 of the slide mount 20 is parallel to the water surface, as illustrated in FIGURE 2. The depth adjuster 28 of the holder 25 should be set so that when dropped, the end of the clamp 26 will be 0.6 cm below the surface of the water. One of the short sides 23 of the slide mount 20 should be next to the side of the beaker 12 with the other positioned directly over the center of the stirring rod 16 such that the film surface is perpendicular to the flow of the water, as illustrated in FIGURE 3.
6. In one motion, drop the secured slide and clamp into the water and start the timer. Disintegration occurs when the film breaks apart. When all visible film is released from the slide mount, raise the slide out of the water while continuing to monitor the solution for undissolved film fragments. Dissolution occurs when all film fragments are no longer visible and the solution becomes clear.
DATA RECORDING: The results should include the following: complete sample identification; individual and average disintegration and dissolution times; and water temperature at which the samples were tested.
Standard quality control procedures may be followed for water-soluble PVOH film, with respect to bubble and pin-hole inspection, however, such quality checks are not absolutely necessary given the solid state of the contained product. A unit dose of a non-liquid agent contained within the formed package does not necessarily pose the same packaging problems as a liquid product. With respect to the use of such a unit dose, however, no procedural changes are required. That is, merely adding the unit dose package to the appropriate quantity of water and following the O necessary stirring or agitation times yields the desired cleaning, ('i conditioning, or disinfectant solution.
1 While specific embodiments have been illustrated and described, numerous modifications are possible without departing from the spirit of the invention.
Cc Throughout this specification and the claims which follow, unless the 00 00, context requires otherwise, the word "comprise", and variations such as "comprises" and ¢€3 "comprising", will be understood to imply the inclusion of a stated integer or step or ('i group of integers or steps but not the exclusion of any other integer or step or group of integers or steps.
The reference to any prior art in this specification is not, and should not be taken as, an acknowledgement or any form of suggestion that the prior art forms part of the common general knowledge in Australia.
Claims (22)
1. A unit dose of a non-liquid agent, comprising a package comprising at least one compartment comprised of a water-soluble film, the film comprising the CC following components with percentage weights calculated with respect to the weight of 00all components of the film: _a hydrolyzed copolymer of vinyl acetate and methyl acrylate in a range of from N about 30 to about 95 percent by weight; modified starch in a range of from about 4 to about 30 percent by weight; plasticizer in a range of from about 5 to about 30 percent by weight; lubricant/release agent in a range of from about 0.0 to about 1.5 percent by weight; and surfactant in a range of from about 0.01 to about 1.5 percent by weight; and a non-liquid agent contained within the compartment.
2. A package according to claim 1, wherein the non-liquid agent comprises a cleanser.
3. A package according to claim 1 or 2, wherein the non-liquid agent comprises a disinfectant.
4. A package according to any one of the preceding claims, wherein the modified starch comprises hydroxyethyl modified starch.
A package according to any one of the preceding claims, wherein the amount of modified starch is about 4 to about 12 percent by weight.
6. A package according to any one of the preceding claims, wherein the hydrolyzed copolymer has a 4% solution viscosity in a range of about 15 to about cps (about 0.015 to about 0.025 pascal seconds) at 20 'C (about 68 F).
7. A package according to any one of the preceding claims, wherein the 0 copolymer film thickness is in a range of from about 1.0 to about 2.0 mils (about 0.025 C1 to about 0.050 mm). 00
8. A package according to any one of the preceding claims, wherein the amount of plasticizer is in a range of from about 20 to about 30 percent by weight. 00
9. A package according to any one of the preceding claims, wherein the film further comprises a bleaching agent for controlling color drift.
A package according to claim 9, wherein the bleaching agent is sodium metabisulfite.
11. A package according to claim 10, wherein the amount of sodium metabisulfite is in a range of from about 0.4 to about 0.7 percent by weight of all components of the film.
12. A package according to any one of the preceding claims, wherein the hydrolyzed copolymer initially comprises an amount of from about 4 to about 6 mol percent gamma lactone units, and wherein after treatment with a caustic soda the hydrolyzed copolymer comprises from about 3 to about 4 mol percent carboxylate groups and from about 1 to about 2 mol percent gamma lactone units.
13. A package according to any one of the preceding claims, wherein the film, at a thickness of about 1.5 mil (about 0.038mm), dissolves in less than 60 seconds in water at a temperature of about 20 °C (about 68 in accordance with MonoSol Test Method MSTM 205.
14. A method for preparing a unit dose of a non-liquid agent, the method comprising the steps of: providing a vinyl acetate-methyl acrylate copolymer; hydrolyzing the vinyl acetate-methyl acrylate copolymer to form a vinyl alcohol-gamma lactone copolymer having a 4% solution viscosity in a range of from about 5 to about 50 cps at 20 OC; 00 slurrying the hydrolyzed polymer with water; adding modified starch to the copolymer-water slurry in an amount of from .1 about 4.0 to about 25.0 percent by weight of all components of the film; Sheating the hydrolyzed copolymer and starch slurry to form a solution; 00 treating the solution with caustic soda to create a solution ofa copolymer having from about 1 to about 12 mol percent carboxylate groups, from about 0 to about 11 mol percent gamma lactone units, and from about 88 to about 99 mol percent vinyl alcohol 00 00) units; Scasting the hot copolymer solution on a suitable surface to create a film having a thickness in a range of from about 0.1 to about 5.0 mils (about 0.0025 to about 0.127 mm) disposing a unit does of a non-liquid agent in said film; and forming a compartment from said film.
A method, according to claim 14, wherein said step of providing a vinyl acetate-methyl acrylate copolymer comprises copolymerizing vinyl acetate and methyl acrylate to form a copolymer.
16. A method according to claim 14, further comprising the step of adding sodium metabisulfite to the copolymer-water slurry in an amount greater than 0.12 percent by weight of all components of the film to prevent browning of the heated solution.
17. A method according to claim 16, wherein the amount of sodium metabisulfite is in a range of from about 0.4 to about 0.7 percent by weight.
18. A method according to any one of claims 14-17, wherein the copolymer solution comprises from about 3 to about 4 mol percent carboxylate groups, from about 1 to about 2 mol percent gamma lactone units, and from about 94 to about 96 mol percent vinyl alcohol units.
19. A method according to any one of claims 14-18, wherein the amount of modified starch used is about 4 to about 12 percent by weight.
A method according to any one of claims 14-19, wherein the modified 00 0 starch comprises hydroxyethyl modified starch.
21. A method according to any one of claims 14-20, wherein the water- 00 soluble film at a thickness of about 1.5 mil (about 0.038 mm) dissolves in water at a temperature of about 20°C (about 68°F) in less than 60 seconds in accordance with c MonoSol test method MSTM 205. 00
22. A unit dose of a non-liquid agent, or a method for preparing a unit dose Sof a non-liquid agent, substantially as herein described with reference to the Drawings. 0',