Process for the production of a web from viscose solutions.

Info

Publication number
AT98833B
AT98833B AT98833DA AT98833B AT 98833 B AT98833 B AT 98833B AT 98833D A AT98833D A AT 98833DA AT 98833 B AT98833 B AT 98833B
Authority
AT
Austria
Prior art keywords
web
production
viscose solutions
alkali cellulose
treatment
Prior art date
Application number
Other languages
German (de)
Original Assignee
Glanzfaeden Actiengesellschaft
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Glanzfaeden Actiengesellschaft filed Critical Glanzfaeden Actiengesellschaft
Application granted granted Critical
Publication of AT98833B publication Critical patent/AT98833B/en

Description

  

   <Desc/Clms Page number 1> 
 



  Verfahren zur Herstellung eines Gespinstes ans   Viskoselösungell.   
 EMI1.1 
 

 <Desc/Clms Page number 2> 

 
 EMI2.1 
 

 <Desc/Clms Page number 3> 

 
 EMI3.1 
   Auflösung   mittels laugenhaltigem Wasser weniger vollkommen ausfällt : auf der anderen Seite wirken die schon während der   Behandlung mit Schwefelkohlenstoff   in   Gegenwart eines Überschusses   von Natronlauge unbeabsichtigt   gelosten Zellstoffteile, die unter   dem Einfluss der bei dieser Behandlung auftretenden und notwendigen Reaktionswärme schon eine weitgehende Zersetzung erfahren haben, nacheilig auf die Güte der   Viskoselösung und des daraus erzeugten Gespinstes   ein. 



   Die bei der Hydratisierung zu   beobachtenden Temperaturen   wurden schon oben im   allgemeinen   festgelegt. Auch hier sind engere Grenzen bestimmt worden, die zu einem noch   bessetCn Endergebnis   fuhren. 
 EMI3.2 
 lösung und die Güte des aus ihr gefertigten Gesinstes ungünstig beeinflusst. 



   Bei Einhaltung des vorgeschriebenen Laugegewichts der Alkalizellulose und der Temperaturen. welchen diese bis zu   ihrer Behandlung mit Schwefelkohlenstoff ausgesetzt   bleibt, erhält das   Gespinst   die ursprünglichen Eigenschaften des Zellstoffes in fast unvermindertem Masse. Es   ve@bindet mit einem   milden Wolleglanz eine   Reissfestigkeit,   die   50% höher ist als diejenige der hochglänzenden   Kunstseide 
 EMI3.3 
 reichlich 50% seiner Trockenfestigkeit, gegen etwa 30% bei Kunsteide. Die Nassfestigkeit zeigt also eine absolute Überlegenheit von mehr als 100% gegenber Kunstseide. 



   Die vorstehend behandelten Punkte sind im Rahmen des   neuen     Verfahrens von wesentlicher   Bedeutung. 



   PATENT-ANSPRÜCHE :
1.   Ve@fahren zur Herstellung eines Gespinstes aus iskoselösungen, dadurch gekenneichent,   
 EMI3.4 




   <Desc / Clms Page number 1>
 



  Process for the production of a web of viscose solution.
 EMI1.1
 

 <Desc / Clms Page number 2>

 
 EMI2.1
 

 <Desc / Clms Page number 3>

 
 EMI3.1
   Dissolution by means of water containing lye is less complete: on the other hand, the pulp parts that are inadvertently dissolved during the treatment with carbon disulfide in the presence of an excess of caustic soda, which have already undergone extensive decomposition under the influence of the heat of reaction that occurs during this treatment, have a disadvantage on the quality of the viscose solution and the web produced from it.



   The temperatures to be observed during hydration have already been generally specified above. Here, too, narrower limits have been set which lead to an even better end result.
 EMI3.2
 solution and the quality of the mind made from it unfavorably influenced.



   If the prescribed weight of alkali cellulose and the temperatures are observed. to which this remains exposed until it is treated with carbon disulfide, the web retains the original properties of the cellulose to an almost undiminished extent. With a mild wool sheen, Es ve @ has a tensile strength that is 50% higher than that of the high-gloss artificial silk
 EMI3.3
 50% of its dry strength, compared to about 30% for artificial silk. The wet strength shows an absolute superiority of more than 100% compared to rayon.



   The points discussed above are essential to the new process.



   PATENT CLAIMS:
1. Ve @ drive for the production of a web of iskose solutions, thereby identified,
 EMI3.4

Claims (1)

in Natronlauge getaucht wird und die weitere. sonst durch zeitliche Einwirkung der in ihr enthaltenen Restlauge hervorgerufene Hydratisierung ganz in Fortfall kommt. is immersed in caustic soda and the other. otherwise hydration caused by the temporal effect of the residual liquor contained in it is completely eliminated. 3. Verfahren nach Anspruch 1. dadurch gekennzeichnet, dass die Alkalizellulose nicht mehr als EMI3.5 der während der Behandlung der Alkalizellulose mit Schwefelkohlenstoff schon teilweise lösend auf erstere einwirken kann. EMI3.6 3. The method according to claim 1, characterized in that the alkali cellulose is not more than EMI3.5 which during the treatment of the alkali cellulose with carbon disulfide can already have a partially dissolving effect on the former. EMI3.6
AT98833D 1918-02-22 1918-09-05 Process for the production of a web from viscose solutions. AT98833B (en)