WO2022204168A1 - Matériaux de verre métallique et leurs procédés de fabrication - Google Patents

Matériaux de verre métallique et leurs procédés de fabrication Download PDF

Info

Publication number
WO2022204168A1
WO2022204168A1 PCT/US2022/021372 US2022021372W WO2022204168A1 WO 2022204168 A1 WO2022204168 A1 WO 2022204168A1 US 2022021372 W US2022021372 W US 2022021372W WO 2022204168 A1 WO2022204168 A1 WO 2022204168A1
Authority
WO
WIPO (PCT)
Prior art keywords
substrate
homogeneous mixture
metals
heating
group
Prior art date
Application number
PCT/US2022/021372
Other languages
English (en)
Inventor
Liangbing Hu
Yonggang Yao
Qi DONG
Original Assignee
University Of Maryland, College Park
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University Of Maryland, College Park filed Critical University Of Maryland, College Park
Publication of WO2022204168A1 publication Critical patent/WO2022204168A1/fr

Abstract

La présente invention concerne des sels métalliques précurseurs d'au moins deux métaux différents pouvant être chargés sur un substrat. Le substrat peut être chauffé à une vitesse de chauffage à une première température, puis maintenu à la première température pendant un premier temps. La première température peut être dans une plage de 1000 à 3 000 K, et le premier temps peut être dans une plage de 1 µs à 10 s. Après le premier temps, le substrat peut être refroidi à partir de la première température à une vitesse de refroidissement, de telle sorte qu'un matériau de verre métallique est formé sur le substrat. Le matériau de verre métallique peut comprendre un mélange homogène des au moins deux métaux différents et former un solide amorphe unique.
PCT/US2022/021372 2021-03-22 2022-03-22 Matériaux de verre métallique et leurs procédés de fabrication WO2022204168A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US202163164425P 2021-03-22 2021-03-22
US63/164,425 2021-03-22

Publications (1)

Publication Number Publication Date
WO2022204168A1 true WO2022204168A1 (fr) 2022-09-29

Family

ID=83397886

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2022/021372 WO2022204168A1 (fr) 2021-03-22 2022-03-22 Matériaux de verre métallique et leurs procédés de fabrication

Country Status (1)

Country Link
WO (1) WO2022204168A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20080044488A1 (en) * 2004-05-29 2008-02-21 Jose Zimmer Nano Glass Powder and Use Thereof, in Particular Multicomponent Glass Powder with a Mean Particle Size of Less Than 1 µm
US20080248222A1 (en) * 2004-03-25 2008-10-09 Akihisa Inoue Metallic Glass Laminates, Production Methods and Applications Thereof
US9945785B2 (en) * 2011-05-27 2018-04-17 Drexel University Flexible SERS substrates with filtering capabilities
US20180369771A1 (en) * 2017-06-22 2018-12-27 University Of Maryland Nanoparticles and systems and methods for synthesizing nanoparticles through thermal shock

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20080248222A1 (en) * 2004-03-25 2008-10-09 Akihisa Inoue Metallic Glass Laminates, Production Methods and Applications Thereof
US20080044488A1 (en) * 2004-05-29 2008-02-21 Jose Zimmer Nano Glass Powder and Use Thereof, in Particular Multicomponent Glass Powder with a Mean Particle Size of Less Than 1 µm
US9945785B2 (en) * 2011-05-27 2018-04-17 Drexel University Flexible SERS substrates with filtering capabilities
US20180369771A1 (en) * 2017-06-22 2018-12-27 University Of Maryland Nanoparticles and systems and methods for synthesizing nanoparticles through thermal shock

Similar Documents

Publication Publication Date Title
Vadai et al. In-situ observation of plasmon-controlled photocatalytic dehydrogenation of individual palladium nanoparticles
Liang et al. High-yield uniform synthesis and microstructure-determination of rice-shaped silver nanocrystals
Sun et al. Ambient-stable tetragonal phase in silver nanostructures
Hu et al. Synthesis of uniform hexagonal prismatic ZnO whiskers
Van Der Veen et al. Single-nanoparticle phase transitions visualized by four-dimensional electron microscopy
Liu et al. Rapid synthesis of monodisperse Au nanospheres through a laser irradiation-induced shape conversion, self-assembly and their electromagnetic coupling SERS enhancement
Liang et al. Silver nanorice structures: oriented attachment-dominated growth, high environmental sensitivity, and real-space visualization of multipolar resonances
Chen et al. Properties of disorder-engineered black titanium dioxide nanoparticles through hydrogenation
Lao et al. Hierarchical ZnO nanostructures
Motl et al. Au− Cu alloy nanoparticles with tunable compositions and plasmonic properties: experimental determination of composition and correlation with theory
Iida et al. First-principles computational visualization of localized surface plasmon resonance in gold nanoclusters
Anumol et al. New insights into selective heterogeneous nucleation of metal nanoparticles on oxides by microwave-assisted reduction: rapid synthesis of high-activity supported catalysts
Rui et al. Ternary oxide nanocrystals: universal laser‐hydrothermal synthesis, optoelectronic and electrochemical applications
Wei et al. Rational strategy for shaped nanomaterial synthesis in reverse micelle reactors
Lin et al. Size and dimension dependent surface-enhanced Raman scattering properties of well-defined Ag nanocubes
Wu et al. Structural characterization of nickel oxide nanowires by X-ray absorption near-edge structure spectroscopy
Bian et al. Reproducible and recyclable SERS substrates: Flower-like Ag structures with concave surfaces formed by electrodeposition
Sun et al. Selective synthesis of gold cuboid and decahedral nanoparticles regulated and controlled by Cu2+ ions
Yu et al. Synthesis and multipole plasmon resonances of spherical aluminum nanoparticles
Huang et al. In-situ probing of crystal-phase-dependent photocatalytic activities of Au nanostructures by surface-enhanced Raman spectroscopy
Ye et al. Highly sensitive W18O49 mesocrystal Raman scattering substrate with large-area signal uniformity
Yang et al. Dependence of the localized surface plasmon resonance of noble metal quasispherical nanoparticles on their crystallinity-related morphologies
Tian et al. Quasi-metal for highly sensitive and stable surface-enhanced Raman scattering
Azevedo et al. Double-walled iron oxide nanotubes via selective chemical etching and Kirkendall process
Shi et al. In situ transmission electron microscopy study of nanocrystal formation for electrocatalysis

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22776490

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 18280625

Country of ref document: US

NENP Non-entry into the national phase

Ref country code: DE