WO2020221968A1 - Procede de traitement de residus d'enrichissement physique de bauxite - Google Patents
Procede de traitement de residus d'enrichissement physique de bauxite Download PDFInfo
- Publication number
- WO2020221968A1 WO2020221968A1 PCT/FR2020/000146 FR2020000146W WO2020221968A1 WO 2020221968 A1 WO2020221968 A1 WO 2020221968A1 FR 2020000146 W FR2020000146 W FR 2020000146W WO 2020221968 A1 WO2020221968 A1 WO 2020221968A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- residue
- bauxite
- pretreated
- alumina
- leaching
- Prior art date
Abstract
Description
Claims