WO2019191509A1 - Thiol-acrylate polymers, methods of synthesis thereof and use in additive manufacturing technologies - Google Patents
Thiol-acrylate polymers, methods of synthesis thereof and use in additive manufacturing technologies Download PDFInfo
- Publication number
- WO2019191509A1 WO2019191509A1 PCT/US2019/024704 US2019024704W WO2019191509A1 WO 2019191509 A1 WO2019191509 A1 WO 2019191509A1 US 2019024704 W US2019024704 W US 2019024704W WO 2019191509 A1 WO2019191509 A1 WO 2019191509A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- resin according
- resin
- photopolymerizable resin
- photopolymerizable
- cured material
- Prior art date
Abstract
Description
Claims