WO2018231583A1 - Curable composition for producing a dental composite crown and process of production - Google Patents
Curable composition for producing a dental composite crown and process of production Download PDFInfo
- Publication number
- WO2018231583A1 WO2018231583A1 PCT/US2018/036025 US2018036025W WO2018231583A1 WO 2018231583 A1 WO2018231583 A1 WO 2018231583A1 US 2018036025 W US2018036025 W US 2018036025W WO 2018231583 A1 WO2018231583 A1 WO 2018231583A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- amount
- curable composition
- meth
- composition
- acrylate
- Prior art date
Abstract
Description
Claims