WO2017148682A1 - Food packaging film and manufacturing method for making the same - Google Patents
Food packaging film and manufacturing method for making the same Download PDFInfo
- Publication number
- WO2017148682A1 WO2017148682A1 PCT/EP2017/052919 EP2017052919W WO2017148682A1 WO 2017148682 A1 WO2017148682 A1 WO 2017148682A1 EP 2017052919 W EP2017052919 W EP 2017052919W WO 2017148682 A1 WO2017148682 A1 WO 2017148682A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- multilayer film
- range
- layer composite
- layers
- micrometers
- Prior art date
Abstract
Description
Claims