WO2017074810A1 - Rapid curing and high thixotropy epoxy adhesive compostions - Google Patents
Rapid curing and high thixotropy epoxy adhesive compostions Download PDFInfo
- Publication number
- WO2017074810A1 WO2017074810A1 PCT/US2016/058107 US2016058107W WO2017074810A1 WO 2017074810 A1 WO2017074810 A1 WO 2017074810A1 US 2016058107 W US2016058107 W US 2016058107W WO 2017074810 A1 WO2017074810 A1 WO 2017074810A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- precursor composition
- epoxy
- amine
- curing agent
- weight
- Prior art date
Abstract
Description
Claims