WO2015173110A1 - Catalysts for the synthesis of oxazolidinone compounds - Google Patents
Catalysts for the synthesis of oxazolidinone compounds Download PDFInfo
- Publication number
- WO2015173110A1 WO2015173110A1 PCT/EP2015/060060 EP2015060060W WO2015173110A1 WO 2015173110 A1 WO2015173110 A1 WO 2015173110A1 EP 2015060060 W EP2015060060 W EP 2015060060W WO 2015173110 A1 WO2015173110 A1 WO 2015173110A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- carbon atoms
- optionally substituted
- aliphatic
- cycloaliphatic
- aromatic
- Prior art date
Abstract
The present invention relates to a method for the production of oxazolidinone compounds with low colour intensity, comprising the step of reacting an isocyanate compound with an epoxide compound in the presence of a catalyst which is free of halide anions. The invention further relates to a method for the production of oligooxazolidinone and/or polyoxazolidinone compounds, comprising the step of reacting a polyisocyanate compound with a polyepoxide compound in the presence of said catalyst. The invention further relates to oligooxazolidinone and/or polyoxazolidinone compounds with low colour intensity, obtainable by a method according to the invention.
Description
Catalysts for the synthesis of oxazolidinone compounds
The present invention relates to a method for the production of oxazolidinone compounds with low colour intensity, comprising the step of reacting an isocyanate compound with an epoxide compound in the presence of a catalyst which is free of halide anions. The invention further relates to a method for the production of oligooxazolidinone and/or polyoxazolidinone compounds, comprising the step of reacting a polyisocyanate compound with a polyepoxide compound in the presence of said catalyst. The invention further relates to oligooxazolidinone and/or polyoxazolidinone compounds with low colour intensity, obtainable by a method according to the invention.
Oxazolidinones are widely used structural motifs in pharmaceutical applications, and the cycloaddition of epoxides and isocyanates seems to be a convenient one-pot synthetic route to produce them. Expensive catalysts, reactive polar solvents, long reaction times and low chemoselectivities are common in early reports for the synthesis of oxazolidinones (M. E. Dyen and D. Swern, Chem. Rev., 67, 197 (1967); X. Zhang and W. Chen, Chem. Lett., 39, 527 (2010); M.T. Barros and A.M.F. Phillips, Tetrahedron: Asymmetry, 21, 2746 (2010); H.-Y. Wu, J.-C. Ding and Y.-K. Liu, J. Indian Chem. Soc, 80, 36 (2003); C. Qian and D. Zhu, Synlett, 129 (1994)). Therefore, the development of new catalyst systems is desirable to achieve high chemoselectivities.
US 5 480 958 A describes the synthesis of polyepoxide resins incorporating epoxy terminated urethanes for the use as toughener. Herein the used epoxy terminated urethane prepolymer contains oxazolidinone structures. Said prepolymers are built up from polyisocyanates, carrying isocyanate end groups, and diepoxides and synthesised solvent free at a temperature of 160 °C catalysed by anhydrous potassium acetate. No other potential catalysts are given. The selectivity towards oxazolidinone formation is not described.
US 2014/121299 Al describes the synthesis of oxazolidinone containing thermosettable epoxysystems as tougheners. The method for the production of oxazolidinone is based on the combination of an isocyanate compound and a polyether glycol epoxy resin. The reaction is performed at 135°C to 180 °C with a catalyst. Possible catalysts for the reaction to oxazolidinone are uncharged strong, non-nucleophilic amine based bases such as DBU. The oxazolidinone is formed in selectivities of about 95% percent (compared to isocyanurate). US 2010/227090 Al discloses a method for producing an epoxy terminated polyoxazolidinone from a hydroxyl containing epoxide and an isocyanate can be cured to form high temperature stable thermosets. The reaction is performed at 160°C with a semi-batch addition. The catalyst used in the examples is 2-phenyl imidazole. Other possible catalysts named are tertiary amines and
phosphines, as well as ammonium and phosphonium salts. The only halogenide free salts disclosed are the corresponding acetates. There is no mentioning of thermoplastic behaviour.
Unpublished European Patent Application No. 12192611.7 relates to a method for the production of oxazolidinone compounds, comprising the step of reacting an isocyanate compound with an epoxide compound in the presence of a Lewis acid catalyst. All catalysts used in the examples (Sm , LiBr, PluSbBr PluPBr) contain a halide anion.
US 3687897 discloses a process for the preparation of oxazolidinone compounds by reacting an isocyanate with an epoxide in presence of a phosphonium catalyst such as tetrabutylphosphonium bromide. The examples disclose the use of a tetrabutylphosphonium bromide or iodide catalyst. The chemoselectivity as well as the use of catalysts free of halide anions have not been disclosed.
In all disclosures, the catalyst comprises a halide anion. The use of halide salts, in particular bromide and iodide salts, has the disadvantage that the resulting products tend to have a high colour intensity and may get further discoloured upon exposure to light. During the production of the oxazolidinone and/or polyoxazolidmone compounds, the presence of halides may cause corrosion and necessitates the use of special corrosion-resistant equipment. For the same reason, special corrosion-resistant equipment is required for processing of the resulting oxazolidinone and/or polyoxazolidmone compounds or the catalyst needs to be removed from the oxazolidinone and/or polyoxazolidmone products beforehand.
The object was therefore to identify catalysts for the production of oxazolidinone and/or polyoxazolidmone compounds by reacting isocyanate compounds with epoxide compounds, which lead to products having low colour intensity. It would further be desirable if such catalysts provide a high chemoselectivity to the oxazolidinone product. In the manufacture of polyoxazolidinones by reacting diisocyanates with diepoxides in the presence of the catalyst according to the invention, certain side reactions should be avoided to obtain polymers with useful properties. Such undesired side reactions include for example the trimerisation of isocyanate to isocyanurate groups, the formation of carbodiimides and homo-polymers of the epoxides. The specifications concerning a high chemoselectivity to the oxazolidinone compound are particularly stringent, if polyoxazolidmone compounds with an almost linear polymer backbone and thermoplastic properties are desired. In particular, the formation of isocyanurate groups should be supressed as this side reaction may result in crosslinking of the polymer chains.
Surprisingly, this was achieved by using catalysts free of halide anions, which comprise a conjugated trigonal-planar anionic moiety having a central atom selected from the elements C or N
and three further substituent atoms, independently selected from the elements C, N, O, S and/or P, and wherein the overall charge state of the anionic moiety is -1 or -2, in the reaction of isocyanate compounds with epoxide compounds. Therefore the subject matter of the present invention is a method for the production of oxazolidinone compounds, comprising the step of reacting an epoxide compound and an isocyanate compound in the presence of a catalyst, characterized in that the catalyst
is free of halide anions and
comprises a conjugated trigonal-planar anionic moiety having a central atom selected from the elements C or N and three further substituent atoms, independently of one another selected from the elements C, N, O, S and/or P, and
wherein the overall charge state of the conjugated trigonal-planar anionic moiety is -1 or -2.
The resulting products have a significantly reduced intensity in colour compared to oxazolidinone compounds obtained by the use of a catalyst known from the state of the art, in particular tetraphenylphosphonium bromide and tetraphenylphosphonium chloride. Furthermore, the catalysts according to the invention enable the production of the oxazolidinone compounds with high chemoselectivity. As used herein, the term "oxazolidinone compound" is meant to denote oxazolidinone compounds obtainable by the reaction of an isocyanate compound with an epoxide compound. The term "oxazolidinone compound" is meant to include polyoxazolidinone compounds with at least two oxazolidinone moieties in the molecule obtainable by the reaction of a polyisocyanate with a polyepoxide.
As used herein, the term "isocyanate compound" is meant to denote monoisocyanate compounds, polyisocyanate compounds (having two or more NCO groups), NCO-terminated biuretsisocyanurates, uretdiones, carbamates and NCO-terminated prepolymers. The term "monoisocyanate compound" is meant to denote isocyanate compounds having one isocyanate group. The term "polyisocyanate compound" is meant to denote isocyanate compounds having at least two isocyanate groups. The term "diisocyanate compound" is meant to denote polyisocyanate compounds having two isocyanate groups.
As used herein, the term "epoxide compound" is meant to denote monoepoxide compounds, polyepoxide compounds (having two or more epoxide groups) and epoxide-terminated prepolymers. The term "monoepoxide compound" is meant to denote epoxide compounds having one epoxy group. The term "polyepoxide compound" is meant to denote epoxide compounds
having at least two epoxy groups. The term "diepoxide compound" is meant to denote epoxide compounds having two epoxy groups.
Examples of suitable monoisocyanate compounds are methyl isocyanate, ethyl isocyanate, n-propyl isocyanate, isopropyl isocyanate, n-butyl isocyanate, isobutyl isocyanate, tert-butyl isocyanate, n- pentyl isocyanate, n-hexyl isocyanate, cyclohexyl isocyanate, ω-chlorohexamethylene isocyanate, n-heptyl isocyanate, n-octyl isocyanate, iso-octyl isocyanate, 2-ethyl hexyl isocyanate, 2-norbornyl methyl isocyanate, nonyl isocyanate, 2,3,4-trimethylcyclohexyl isocyanate, 3,3,5- trimethylcyclohexyl isocyanate, decyl isocyanate, undecyl isocyanate, dodecyl isocyanate, tridecyl isocyanate, tetradecyl isocyanate, pentadecyl isocyanate, hexadecyl isocyanate, octadecyl isocyanate, stearyl isocyanate, 3-butoxypropyl isocyanate, 3-(2-ethylhexyloxy)-propyl isocyanate, 6-chlorohexyl isocyanate benzyl isocyanate, phenyl isocyanate, ortho-, meta-, para-tolyl isocyanate, dimethylphenyl isocyanate (technical mixture and individual isomers), 4-pentylphenyl isocyanate, 4-cyclohexylphenyl isocyanate, 4-dodecylphenyl isocyanate, ortho-, meta-, para- methoxyphenyl isocyanate, chlorophenyl isocyanate (2,3,4-isomers), the different dichlorophenyl isocyanate isomers, 4-nitrophenyl isocyanate, 3-trifluoromethylphenyl isocyanate, 1-naphthyl isocyanate.
Preferred monoisocyanate compounds are benzyl isocyanate, phenyl isocyanate, ortho-, meta-, para-to\y\ isocyanate, dimethylphenyl isocyanate (technical mixture and individual isomers), 4- cyclohexylphenyl isocyanate and ortho-, meta-, /jara-methoxyphenyl isocyanate.
A mixture of two or more of the aforementioned monoisocyanate compounds can also be used. Examples of polyisocyanate compounds are tetramethylene diisocyanate, hexamethylene diisocyanate (HDI), 2-methylpentamethylene diisocyanate, 2,2,4-trimethylhexamethylene diisocyanate (THDI), dodecamethylene diisocyanate, 1 ,4-diisocyanatocyclohexane, 3- isocyanatomethyl-3,3,5-trimethylcyclohexyl isocyanate (isophorone diisocyanate, IPDI), 4,4'- diisocyanatodicyclohexylmethane (H12-MDI), 4,4'-diisocyanato-3,3'-dimethyldicyclohexylmethane, 4,4'-diisocyanato-2,2-dicyclohexylpropane, poly(hexamethylene diisocyanate), octamethylene diisocyanate, tolylene-a,4-diisocyanate, poly(propylene glycol) tolylene-2,4-diisocyanate terminated, poly( ethylene adipate) tolylene-2,4-diisocyanate terminated, 2,4,6-trimethyl-l,3- phenylene diisocyanate, 4-chloro-6-methyl-l,3-phenylene diisocyanate, poly[l,4-phenylene diisocyanate-co-poly(l,4-butanediol)] diisocyanate, poly(tetrafluoroethylene oxide-co- difluoromethylene oxide) α,ω-diisocyanate, 1 ,4-diisocyanatobutane, 1,8-diisocyanatooctane, 1,3- bis(l -isocyanato-1 -methylethyl)benzene, 3,3 '-dimethyl-4,4'-biphenylene diisocyanate, naphthalene- 1,5-diisocyanate, 1,3-phenylene diisocyanate, 1 ,4-diisocyanatobenzene, 2,4- or 2,5- or
2,6-diisocyanatotoluene (TDI) or mixtures of these isomers, 4,4'-, 2,4'- or 2,2'- diisocyanatodiphenylmethane (MDI) or mixtures of these isomers, 4,4'-, 2,4'- or 2,2'-diisocyanato- 2,2-diphenylpropane-p-xylene diisocyanate and α,α,α',α'-tetramethyl- m- or -p-xylene diisocyanate (TMXDI), mixtures thereof or biurets, isocyanurates, carbamates or uretdiones of the aforementioned isocyanates.
Preferred polyisocyanates are hexamethylene diisocyanate (HDI), 3-isocyanatomethyl-3,3,5- trimethylcyclohexyl isocyanate (isophorone diisocyanate, IPDI), 4,4'- diisocyanatodicyclohexylmethane (H12-MDI), 2,4- or 2,5- or 2,6-diisocyanatotoluene (TDI) or mixtures of these isomers, 4,4'-, 2,4'- or 2,2'-diisocyanatodiphenylmethane (MDI) or mixtures of these isomers.
A mixture of two or more of the aforementioned polyisocyanates can also be used. Examples of monoepoxide compounds are ethylene oxide, propylene oxide, 1,2-butene oxide, 2,3- butene oxide, butadiene monoepoxide, 1,2-hexene oxide, cyclohexene oxide, vinylcyclohexene monoxide, limonene monoxide, oxides of C10 - C18 alpha-olefins, styrene oxide, the epoxides of unsaturated fatty acid CI - CI 8 alkyl esters, methyl glycidyl ether, ethyl glycidyl ether, propyl glycidyl ether, butyl glycidyl ether, pentyl glycidyl ether, hexyl glycidyl ether, cyclohexyl glycidyl ether, octyl glycidyl ether, 2-ethylhexyl glycidyl ether, CIO - CI 8 alkyl glycidyl ether, allyl glycidyl ether, benzyl glycidyl ether, phenyl glycidyl ether, 4-tert-butylphenyl glycidyl ether, 1- naphthyl glycidyl ether, 2-naphthyl glycidyl ether, 2-chlorophenyl glycidyl ether, 4-chlorophenyl glycidyl ether, 4-bromophenyl glycidyl ether, 2,4,6-trichlorophenyl glycidyl ether, 2,4,6- tribromophenyl glycidyl ether, pentafluorophenyl glycidyl ether, o-cresyl glycidyl ether, m-cresyl glycidyl ether, p-cresyl glycidyl ether, glycidyl acetate, glycidyl cyclohexylcarboxylate, glycidyl benzoate, and N-glycidyl phthalimide.
Preferred monoepoxide compounds are ethylene oxide, propylene oxide, 1,2-butene oxide, 2,3- butene oxide, styrene oxide, butyl glycidyl ether, benzyl glycidyl ether, phenyl glycidyl ether, p- tolyl glycidyl ether, 4-tert-butylphenyl glycidyl ether.
A mixture of the aforementioned monoepoxide compounds can also be used.
Diepoxide compounds are for example butadiene diepoxide, vinylcyclohexene diepoxide, limonene diepoxide, the diepoxides of double unsaturated fatty acid CI - CI 8 alkyl esters, ethylene glycol diglycidyl ether, di(ethylene glycol) diglycidyl ether, poly(ethylene glycol) diglycidyl ether, propylene glycol diglycidyl ether, di(propylene glycol) diglycidyl ether, poly(propylene glycol)
diglycidyl ether, neopentyl glycol diglycidyl ether, polybutadiene diglycidyl ether, 1,6-hexanediol diglycidyl ether, hydrogenated bisphenol-A diglycidyl ether, 1 ,2-dihydroxybenzene diglycidyl ether, resorcinol diglycidyl ether, 1 ,4-dihydroxybenzene diglycidyl ether, bisphenol-A diglycidyl ether, diglycidyl ethers of polybutadiene - bisphenol-A - block-copolymers, diglycidyl o-phthalate, diglycidyl isophthalate, diglycidyl terephthalate.
Preferred diepoxide compounds are butadiene diepoxide, the diepoxides of double unsaturated fatty acid CI - CI 8 alkyl esters, ethylene glycol diglycidyl ether, di( ethylene glycol) diglycidyl ether, poly(ethylene glycol) diglycidyl ether, propylene glycol diglycidyl ether, di(propylene glycol) diglycidyl ether, poly(propylene glycol) diglycidyl ether, neopentyl glycol diglycidyl ether, 1,6- hexanediol diglycidyl ether, hydrogenated bisphenol-A diglycidyl ether, 1 ,2-dihydroxybenzene diglycidyl ether, resorcinol diglycidyl ether, 1 ,4-dihydroxybenzene diglycidyl ether, bisphenol-A diglycidyl ether, diglycidyl o-phthalate, diglycidyl isophthalate, diglycidyl terephthalate. A mixture of two or more the aforementioned diepoxides can also be used.
Polyepoxide compounds are for example glycerol polyglycidyl ether, trimethylolpropane polyglycidyl ether, pentaerythritol polyglycidyl ether, diglycerol polyglycidyl ether, polyglycerol polyglycidyl ether, sorbitol polyglycidyl ether.
A mixture of one or more polyepoxide compounds and/or one or more of the aforementioned diepoxide compounds can also be used.
The catalyst according to the invention is a compound free of halide anions and comprising a conjugated trigonal-planar anionic moiety having a central atom selected from the elements C or N and three further substituent atoms, selected independently of one another from the elements C, N, O, S and/or P, wherein the overall charge state of the anionic moiety is -1 or -2. The term "trigonal- planar" in the context of this invention is used in accordance with the valence-shell electron pair repulsion model (VSEPR model) as described for example in Holleman, A. F.; Wiberg, E.; "Inorganic Chemistry"; Academic Press: San Diego, 2001. In this context, the term "trigonal- planar" describes a three dimensional geometrical arrangement, in which the three substituent atoms are arranged around the central atom in a triangular manner, and the central atom is located within the triangular plane. It is to be understood that within the scope of the invention, small deviations from the planar arrangement are accepted. Thus, the central atom may be slightly dislocated from the plane so that any bond between a substituent atom and the central atom forms an angle of no more than 30° with the triangular plane. The term "conjugated" as used herein is meant to denominate an arrangement, in which all four atoms are part of a common, conjugated π-
system. The condition "conjugated" is fulfilled if a mesomeric structure can be formulated in which one of the three substituent atoms is bound to the central atom by a double bond, and the remaining substituent atoms carry either a lone electron pair, or are bound to further substituents by a double bond, or are part of a further π-system, such as an aromatic system.
The anionic moiety contained in the catalyst according to the invention has an overall charge state of -1 or -2. The anionic moiety can be a mono- or double-charged anion without any covalent bonds to further binding partners, or be part of a larger molecular structure, to which it is connected by covalent bonds via one or two of the substituent atoms contained in the anionic moiety. One or two of the substituent atoms can also be connected to a larger molecular structure in such a way that they form, together with the central atom of the anionic moiety, a cyclic structure within the larger molecular framework.
The following examples are given to further elucidate the meaning of the term "conjugated trigonal-planar anionic moiety" in the context of the invention, it is however to be understood that the invention is not limited to these examples. Formulae (I) to (III) are examples for "conjugated trigonal-planar anionic moiety" structures whereas formula (IV) represents a "non-conjugated
(I) (Π) (III) (IV)
The structure shown in formula I (carbonate anion) features a double bond between one oxygen atom (substituent atom) and the central carbon atom, which is bound to two further oxygen atoms (substituent atoms), each of which carries a lone electron pair. The overall charge is -2. The carbonate is thus a conjugated trigonal-planar anionic moiety.
The structure shown in formula II (nitrate anion) features a double bond between one oxygen atom (substituent atom) and the central nitrogen atom, which is bound to two further oxygen atoms (substituent atoms), each of which carries a lone electron pair. The overall charge is -1. The nitrate is thus a conjugated trigonal-planar anionic moiety.
The structure shown in formula III (saccharinate anion) features a double bond between a nitrogen atom (substituent atom) and a central carbon atom, which is bound on one side to an oxygen atom (substituent atom) carrying a lone pair, and on the other side to a carbon atom (substituent atom) which is part of an aromatic π-system. The overall charge is -1. The N-C(0)-C-moiety is a conjugated trigonal-planar anionic moiety and has an overall charge of -1. The anionic moiety is part of a larger molecular framework. The saccharinate anion thus comprises a conjugated trigonal- planar anionic moiety.
The structure shown in formula IV (acetate anion) features a double bond between one oxygen atom (substituent atom) and the central carbon atom, which is bound to another oxygen atom (substituent atom) carrying a lone electron pair. The third substituent atom (carbon atom) does neither carry a lone electron pair, nor is it bound with a double bond to further binding partners or part of another π-system, such as an aromatic system. The acetate anion is therefore not a conjugated trigonal-planar anionic moiety.
The catalyst according to the invention can also contain more than one anionic moiety within one molecule. It is preferred that all anionic moieties contained in the catalyst according to the invention have a conjugated trigonal-planar structure as specified above. The catalyst according to the invention is overall neutral in charge. It thus contains an appropriate number of positive charges to compensate for the negative charge or charges of the anionic moiety or moieties. The positive charges can be present in the form of one or more suitable separate counter cations, which are not bound via one or more covalent bonds to the anionic moiety. In this case, the catalyst according to the invention is a salt comprising separate cations and anions, whereby the anions comprise at least one conjugated trigonal-planar anionic moiety as specified above. The positive charges can also be present as cationic moieties in the same molecule as the anionic moieties, however, the charges are then strictly separated, i.e. the positive and the negative charge are not in conjugation to each other. In this case, the catalyst of the invention is a zwitterion. In one preferred embodiment of the invention the catalyst is a salt comprising separate cations and anions.
In one embodiment of the invention the anionic moiety in the catalyst has the general formula (V),
Y
X
(V)
wherein
n is an integer of 1 or 2,
A is C or N+,
X is O , OH, S\ SH, OR, SR, NRR', NHR, N(R)", N(S02R)" or PRR',
wherein R, R' independently of one another are linear or branched, saturated, mono- or polyunsaturated aliphatic, cycloaliphatic or aromatic groups comprising 1 to 20 carbon atoms, optionally substituted with one or more heteroatom containing groups, wherein the heteroatom is selected from N, O, S, P, Si, F and/or CI,
wherein R, R' can be connected within a (hetero) aliphatic or (hetero)aromatic mono- or polycyclic ring comprising 1 to 20 carbon atoms and/or heteroatoms selected from the group N, P, O and/or S optionally substituted with one or more heteroatom containing groups, wherein the heteroatom is selected from N, O, S, P, Si, F and/or CI, or with an alkyl group comprising 1 to 20 carbon atoms,
Y is O, S or N, wherein N can be substituted by a group R", wherein R" independently of R and
R' has the same meaning as specified for R, R',
Z is -0", S\ N(R"')~, N(S02R'")~, wherein R'" independently of R, R' and R" has the same meaning as specified for R, R', R", or a carbon atom which is part of an aromatic group comprising 1 to 20 carbon atoms,
wherein in case that Y is N, Y and X can be connected within a (hetero)aliphatic or (hetero)aromatic ring having 5 to 6 carbon atoms and/or heteroatoms selected from the group N, P, O and/or S and optionally comprising an annulated aromatic ring having 6 carbon atoms optionally substituted with one or more heteroatom containing groups, wherein the heteroatom is selected from N, O, S, P, Si, F and/or CI, or with an alkyl group comprising 1 to 20 carbon atoms.
Examples of compounds comprising an anionic moiety having the general formula (V) are CO3 ", RO-CO2-, RS-CO2-, RHN-CO2-, RR'N-C02-, CSO22-, RO-CSO", RHN-CSO", RR'N-CSO", RS- CSO", COS22-, RO-CS2-, RHN-CS2-, RR'NCS2-, RR'N-CSO", CS3 2", RS-CS2 _, RO-C(=NR")0", RO- C(=NR")S", RS-C(=NR")0", RS-C(=NR")S", R"N=C(NHR)0", R"N=C(NRR')0", R"N=C(NHR)S\ R"N=C(NRR')S\ RO-CO-N(R"')~, RS-CO-N(R"')~, RR'N-CO-N(R"')~, RO- CS-N(R"')~, RS-CS-N(R"')", RR'N-CS-N(R"')", RO-C(=NR")-N(R" ')", RS-C(=NR")-N(R"')", RR'N-C(=NR")-N(R"')", RO-CO-N(S02R'")", RS-CO-N(S02R'")", RR'N-CO-N(S02R'")", RO-
CS-N(S02R"')", RS-CS-N(S02R"')~, RR'N-CS-N(S02R"')~, RO-C(=NR")-N(S02R" ')~, RS-
C(=NR' ')-N(S02R' ' ')", RR'N-C(=NR' ')-N(S02R' ' ')",
wherein R, R', R", R' " independently of one another are linear or branched, saturated, mono- or polyunsaturated aliphatic, cycloaliphatic or aromatic groups comprising 1 to 20 carbon atoms, optionally substituted with one or more heteroatom containing groups, wherein the heteroatoms are selected from N, O, S, P, Si, F and/or CI,
wherein R and R' and/or R'", and/or R'and R" and/or R'" can be connected within a (hetero)aliphatic or (hetero)aromatic, mono- or polycyclic ring system comprising 1 to 20 carbon atoms and/or heteroatoms selected from the group N, P, O and/or S, optionally substituted with one or more heteroatom containing groups, wherein the heteroatom is selected from N, O, S, P, Si, F and/or CI, or with an alkyl group comprising 1 to 20 carbon atoms, 4,5-dihydro-oxazol-2-olate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, oxazol-2-olate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, benzoxazol-2-olate, wherein the benzene ring is optionally substituted with one to four aliphatic, cycloaliphatic or aromatic groups having 1 to 20 carbon atoms, 4,5-dihydro-thiazol- 2-olate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, thiazol-2-olate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, benzothiazol-2- olate, wherein the aromatic ring is optionally substituted with one to four aliphatic, cycloaliphatic or aromatic groups having 1 to 20 carbon atoms, 4,5-dihydro-l,3-diazol-2-olate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, l,3-diazol-2-olate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, benzo-l,3-diazol-2-olate, wherein the aromatic ring is optionally substituted with one to four aliphatic, cycloaliphatic or aromatic groups having 1 to 20 carbon atoms, 4,5-dihydro-oxazol-2-thiolate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, oxazol-2-thiolate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, benzoxazol-2-thiolate, wherein the aromatic moiety is optionally substituted with one to four aliphatic, cycloaliphatic or aromatic groups having 1 to 20 carbon atoms, 4,5-dihydro-thiazol-2-thiolate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, thiazol-2-thiolate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, benzothiazol-2-thiolate, wherein the aromatic moiety is optionally substituted with one to four aliphatic, cycloaliphatic or aromatic groups having 1 to 20 carbon atoms, 4,5-dihydro-l,3-diazol-2-thiolate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, l,3-diazol-2-thiolate,
optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, benzo-l,3-diazol-2-thiolate, wherein the aromatic moiety is optionally substituted with one to four aliphatic, cycloaliphatic or aromatic groups having 1 to 20 carbon atoms, pyrimidin-2-yl amide, optionally N-substitued, e.g. with aryl or alkylsulfonyl groups, 2-pyrimidin-2-olate, N-alkylsulfonyl or N-arylsulfonyl carbamimidoylamide, optionally with further JV- and/or N"-substituents, or NCb".
In another embodiment of the invention, the anionic moiety having the general formula (V) comprises CO32", CSO22", COS22", RO-CO2 , wherein R is methyl, ethyl, propyl, isopropyl, butyl or phenyl, RS-CO2", wherein R is methyl, ethyl, dodecyl or phenyl, R2N-CO2" , wherein R is methyl, ethyl or phenyl, R2N-CSO , wherein R is methyl, ethyl or phenyl, R2N-CS2", wherein R is methyl, ethyl, butyl or phenyl, RO-CS2", wherein R is methyl, ethyl, propyl, isopropyl, butyl or phenyl, 4,5- dihydro-oxazol-2-thiolate, oxazol-2-thiolate, benzoxazol-2-thiolate, 4,5-dihydro-thiazol-2-thiolate, thiazol-2-thiolate, benzothiazol-2-thiolate, 4,5-dihydro-l,3-diazol-2-thiolate, l,3-diazol-2-thiolate, benzo-l,3-diazol-2-thiolate or NC .
In a preferred embodiment of the invention, the anionic moiety of the catalyst having the general formula (V) is selected from the group comprising CO32", N03 ", CSO22", COS22", (CH3)2N-CS2", (C2H5)2N-CS2_, and benzothiazol-2-thiolate.
In another preferred embodiment of the invention, the anionic moiety of the catalyst having the general formula (V) is selected from the group comprising CO32", NO3", (CH3)2N-CS2~ or (C2H5)2N- CS2\ In another embodiment of the invention, the catalyst comprises two or more different anionic moieties of the general formula (V) as a mixture of separate compounds or combined in one common larger molecular framework.
In another embodiment of the invention, the conjugated trigonal-planar anionic moiety comprised in the catalyst is generated from an appropriate nucleophile and carbon dioxide CO2, carbonyl sulphide SCO or carbon disulfide CS2. Appropriate nucleophiles can be primary, secondary or tertiary alcohols, such as methanol, ethanol, n-propanol, isopropanol, n-butanol, isobutanol, tert- butanol, the different pentanol isomers, the different hexanol isomers and higher homologues, cyclopentanol, cyclohexanol, aromatic alcohols such as phenol or napththol, which may be further substituted, but preferably carry hydrogen atoms in 2-position to the hydroxyl group, primary, secondary or tertiary thiols, such as methane thiol, ethane thiol, n-propane thiol, isopropane thiol, n-butane thiol, isobutane thiol, tert-butane thiol, the different pentane thiol isomers, the different
hexane thiol isomers and higher homologues, cyclopentane thiol, cyclohexane thiol, aromatic thiols such as thiophenol or thionapththol, which may be further substituted, but preferably carry hydrogen atoms in 2-position to the thiol group, monoalkyl amines such as methyl amine, ethyl amine, ^-propyl amine, isopropyl amine, butyl amine and their higher homologues, cyclohexylamine, dialkylamines such as dimethylamine, diethylamine, di-n-propyl amine, diisopropyl amine, and their higher homologues, aromatic amines such as aniline, naphthyl amine and diphenyl amine, wherein the aromatic substituents may be further substituted, but preferably carry hydrogen atoms in 2-position to the amino group, N-alkyl-N-aryl amines such as N-methyl aniline, N-ethyl aniline and their higher homologues, ethanol amine or N-substituted ethanol amines. In the case of the above mentioned nucleophiles, especially alcohols and thiols, a non- nucleophilic base may be added during the generation of the anionic moiety. Further appropriate nucleophiles are primary, secondary or tertiary alcoholates or thiolates derived from the primary, secondary or tertiary alcohols or thiols listed above by deprotonation with an appropriate base such as metal hydrides, e.g. sodium hydride or potassium hydride, or alkaline metals such as sodium or potassium. Further appropriate nucleophiles are amides derived by deprotonation from any type of monoalkyl amine, dialkyl amine, aromatic amine or N-alkyl-N-aryl amine specified above, such as lithium diisopropylamide, hexamethyldisilazane. The generation of the anionic moiety from an appropriate nucleophile and carbon dioxide, carbonyl sulphide or carbon disulphide can be performed ex situ, i.e. in a separate reaction vessel, and then be injected into the reaction mixture, or in situ, meaning that the precursors (nucleophile and carbon dioxide or carbonyl sulphide or carbon disulphide) are added to the reaction vessel, either before or after addition of one or more of the substrates. Preferred nucleophiles are alcoholates such as sodium or potassium methylate, sodium or potassium ethylate, sodium or potassium n- or isopropylate, or higher linear or branched aliphatic or cycloaliphatic homologues, dialkylamines such as dimethylamine, diethylamine, di-«- propylamine, diisopropylamine and dialkylamines with larger linear or branched aliphatic or cycloaliphatic alkyl-substituents.
An appropriate cation in the catalyst can be a Lewis acidic cation. In one embodiment of the invention, the catalyst according to the invention is a salt comprising a conjugated trigonal-planar anionic moiety, preferably an anionic moiety according to formula (V), and a cationic Lewis acid as counter cation. The cationic Lewis acid can be a metal cation or a cationic metal complex comprising a metal selected from the group comprising
Li(I), Rb(I), Cs(I), Ag(I), Au(I),
Mg(II), Ca(II), Sr(II), Ba(II), Dy(II), Yb(II), Cu(II), Zn(II), V(II), Mo(II), Mn(II), Fe(II), Co(II) Ni(II), Pd(II), Pt(II), Ge(II), Sn(II),
Sc(III), Y(III), La(III), Ce(III), Pr(III), Nd(III), Sm(III), Eu(III), Gd(III), Tb(III), Dy(III), Ho(III), Er(III), Tm(III), Yb(III), Lu(III), Hf(III), Nb(III), Ta(III), Cr(III), Ru(III), Os(III), Rh(III), Ir(III), Al(III), Ga(III), In(III), Tl(III), Ge(III),
Ce(IV), Ti(IV), Zr(IV), Hf(IV), Nb(IV), Mo(IV), W(IV), Ir(IV), Pt(IV), Sn(IV), Pb(IV),
Nb(V), Ta(V), P(V), Sb(V), Bi(V),
Mo(VI), W(VI).
In the cationic metal complex, an appropriately chosen ligand, such as phosphine, phosphite, arsenite, alkyl, acetylacetonate may be coordinated to the vacant coordination sites at the metal, whereby at least one coordination site remains available for binding of a Lewis base. The coordination site for binding of a Lewis base may also be created in the reaction mixture, e.g., by dissociation of a weakly coordinating ligand.
In one preferred embodiment of the invention, the cationic part of the catalyst is represented by formula (VI)
[M(R1)(R2)(R3)(R4)]+ (VI)
wherein
M is phosphorous or antimony,
(Rl), (R2), (R3), (R4) are independently of one another selected from the group comprising linear or branched alkyl groups containing 1 to 22 carbon atoms, optionally substituted with heteroatoms and/or heteroatom containing substituents, cycloaliphatic groups containing 3 to 22 carbon atoms, optionally substituted with heteroatoms and/or heteroatom containing substituents, CI to C3 alkyl- bridged cycloaliphatic groups containing 3 to 22 carbon atoms, optionally substituted with heteroatoms and/or heteroatom containing substituents and aryl groups containing 6 to 18 carbon atoms, optionally substituted with alkyl groups containing 1 to 10 carbon atoms and/or heteroatoms.
In another preferred embodiment of the invention, a catalyst as described above is used wherein the cationic part of the catalyst having formula (VI) is used, wherein
M is phosphorous or antimony,
(Rl), (R2), (R3), (R4) are independently of one another selected from the group comprising phenyl, n-butyl and cyclohexyl.
In one preferred embodiment of the invention the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises at least one anionic moiety of formula (V) and at least one cationic moiety of formula (VI) as described before.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises at least one anionic moiety selected from the group comprising CO32", NO3 , CSO22", COS22", (CH3)2N-CS2_, (C2Hs)2N-CS2~ and benzothiazol-2-thiolate and at least one cationic moiety of formula (VI), wherein M is phosphorous or antimony, (Rl), (R2), (R3), (R4) are independently of one another selected from the group comprising phenyl, n-butyl and cyclohexyl.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises at least one anionic moiety selected from the group comprising CO32", NO3 , CSO22", COS22", (CH3)2N-CS2_, (C2i¾)2N-CS2~ and benzothiazol-2-thiolate and at least one cationic moiety of formula (VI), wherein M is phosphorous or antimony, and (Rl), (R2), (R3), (R4) are equal and are selected from the group comprising phenyl, n-butyl and cyclohexyl. In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises at least one anionic moiety selected from the group comprising CO32", NO3 , CSO22", COS22", (CH3)2N-CS2_, (C2i¾)2N-CS2~ and benzothiazol-2-thiolate and at least one cationic moiety of formula (VI), wherein M is phosphorous, and (Rl), (R2), (R3), (R4) are equal and are selected from the group comprising phenyl, n-butyl and cyclohexyl.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises at least one anionic moiety selected from the group comprising CO32", NO3 , CSO22", COS22", (CH3)2N-CS2_, (C2i¾)2N-CS2~ and benzothiazol-2-thiolate and at least one cationic moiety of formula (VI), wherein M is phosphorous, and (Rl), (R2), (R3), (R4) are all phenyl.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises at least one anionic moiety selected from the group comprising CO32", NO3 , CSO22", COS22", (CH3)2N-CS2_, (C2i¾)2N-CS2~ and benzothiazol-2-thiolate and at least one cationic moiety of formula (VI), wherein M is phosphorous, and (Rl), (R2), (R3), (R4) are all n-butyl.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises at least one anionic moiety selected from the group comprising CO32", NO3 , CSO22", COS22", (CH3)2N-CS2_,
(C2]¾)2N-CS2~ and benzothiazol-2-thiolate and at least one cationic moiety of formula (VI), wherein M is phosphorous, and (Rl), (R2), (R3), (R4) are all cyclohexyl.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises at least one anionic moiety selected from the group comprising CO32", NO3", and at least one cationic moiety of formula (VI), wherein M is phosphorous, and (Rl), (R2), (R3), (R4) are equal and are selected from the group comprising phenyl, n-butyl and cyclohexyl. In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises at least one anionic moiety selected from the group comprising CO32" and NO3", and at least one cationic moiety of formula (VI), wherein M is phosphorous, and (Rl), (R2), (R3), (R4) are equal and phenyl.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises at least one anionic moiety selected from the group comprising CO32" and NO3", and at least one cationic moiety of formula (VI), wherein M is phosphorous, and (Rl), (R2), (R3), (R4) are equal and n- butyl.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises at least one anionic moiety selected from the group comprising C032"and NO3", and at least one cationic moiety of formula (VI), wherein M is phosphorous, and (Rl), (R2), (R3), (R4) are equal and cyclohexyl.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises CO32" and at least one cationic moiety of formula (VI), wherein M is phosphorous or antimony, (Rl), (R2), (R3), (R4) are independently of one another selected from the group comprising phenyl, « -butyl and cyclohexyl.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises CO32" and at least one cationic moiety of formula (VI), wherein M is phosphorous, (Rl), (R2), (R3), (R4) are independently of one another selected from the group comprising phenyl, n-butyl and cyclohexyl.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises CO32" and at least one cationic moiety of formula (VI), wherein M is phosphorous, (Rl), (R2), (R3), (R4) are equal and selected from the group comprising phenyl, n-butyl and cyclohexyl.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises CO32" and at least one cationic moiety of formula (VI), wherein M is phosphorous, (Rl), (R2), (R3), (R4) are equal and phenyl.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises CO32" and at least one cationic moiety of formula (VI), wherein M is phosphorous, (Rl), (R2), (R3), (R4) are equal and n-butyl.
In another preferred embodiment of the invention, the catalyst according to claim 1 for the reaction of isocyanates with epoxides or reaction of diisocyanates with diepoxides comprises CO32" and at least one cationic moiety of formula (VI), wherein M is phosphorous, (Rl), (R2), (R3), (R4) are equal and cyclohexyl.
In another embodiment of the invention in combination with one or more of the aforementioned embodiments the isocyanate compound is selected from benzyl isocyanate, phenyl isocyanate, ortho-, meta-, para-tolyl isocyanate, dimethylphenyl isocyanate (technical mixture and individual isomers), 4-cyclohexylphenyl isocyanate and/or ortho-, meta-, /jara-methoxyphenyl isocyanate and the epoxide compound is selected from ethylene oxide, propylene oxide, 1,2-butene oxide, 2,3- butene oxide, styrene oxide, butyl glycidyl ether, benzyl glycidyl ether, phenyl glycidyl ether, p- tolyl glycidyl ether and/or 4-tert-butylphenyl glycidyl ether.
In another embodiment of the invention in combination with one or more of the aforementioned embodiments the diisocyanate compound is selected from hexamethylene diisocyanate (HDI), 3- isocyanatomethyl-3,3,5-trimethylcyclohexyl isocyanate (isophorone diisocyanate, IPDI), 4,4'- diisocyanatodicyclohexylmethane (H12-MDI), 2,4- or 2,5- or 2,6-diisocyanatotoluene (TDI) or mixtures of these isomers and/or 4,4'-, 2,4'- or 2,2'-diisocyanatodiphenylmethane (MDI) or mixtures of these isomers and the diepoxide compound is selected from butadiene diepoxide, the diepoxides of double unsaturated fatty acid CI - CI 8 alkyl esters, ethylene glycol diglycidyl ether, di( ethylene glycol) diglycidyl ether, poly(ethylene glycol) diglycidyl ether, propylene glycol diglycidyl ether, di(propylene glycol) diglycidyl ether, poly(propylene glycol) diglycidyl ether,
neopentyl glycol diglycidyl ether, 1,6-hexanediol diglycidyl ether, hydrogenated bisphenol-A diglycidyl ether, 1 ,2-dihydroxybenzene diglycidyl ether, resorcinol diglycidyl ether, 1,4- dihydroxybenzene diglycidyl ether, bisphenol-A diglycidyl ether, diglycidyl o-phthalate, diglycidyl isophthalate and/or diglycidyl terephthalate.
In one embodiment the method according to the invention is performed in the presence of a solvent. Suitable solvents are high-boiling non-protic solvents such as N-methylpyrrolidone (NMP), N-ethylpyrrolidone, cyclic ethylene carbonate, cyclic propylene carbonate, sulfolane, chlorobenzene, the different isomers of dichlorobenzene, the different isomers of trichlorobenzene, decalin, hexamethylphosphoramide, dimethylformamide, Ν,Ν-dimethylacetamide (DMAc), dimethyl sulfoxide or mixtures of one or more of the aforementioned solvents among each other or with further non-protic solvents. Preferred solvents are NMP, sulfolane and/or DMAc.
In another embodiment of the method according to the invention, the reaction is conducted in the absence of a solvent. Preferably, the reaction mixture contains only the epoxide compound(s), the isocyanate compound(s) and the catalyst(s), as well as the oxazolidinone compound formed during the reaction.
The isocyanate compound may be added to the epoxide compound in a continuous or step-wise manner with two or more individual addition steps in the step-wise addition wherein in each individual addition step the amount of isocyanate compound added is < 50 weight-% of the total amount of isocyanate compound to be added. This is to be understood in such a way that during the course of the reaction the isocyanate compound is added to the reaction mixture containing the epoxide compound continuously or in the aforementioned step-wise manner. Included is also the case that the isocyanate compound is added via a syringe pump, dripping funnel or other continuous or semi-continuous devices where the isocyanate is brought into the reaction mixture. Although some after-reaction time may be given to the reaction system, the reaction should be essentially complete shortly after the end of the addition of the isocyanate compound. By way of process criteria, one could establish a condition that 30 minutes, preferably 20 minutes and more preferred 10 minutes after the end of the isocyanate addition no more change in the NCO group content of the reaction mixture takes place (within the boundaries of experimental uncertainty). This may be observed, for example, by in-situ IR spectroscopy or analysis of samples of the reaction mixture concerning their NCO content, for example, by titration according to DIN ISO 10283.
In one embodiment of the method according to the invention, the isocyanate compound is added continuously to the reaction mixture. "Continuously" in the meaning of the invention means that the isocyanate compound is added to the reaction mixture over a defined period of time, while at the same time any isocyanate compound present in the reaction mixture is converted to the oxazolidinone compound. Preferably, the rate of isocyanate addition is smaller than or equal to the maximum rate, with which the isocyanate compound can be converted under these reaction conditions to the oxazolidinone compound in order to avoid accumulation of NCO groups in the reaction mixture. The actual concentration of NCO groups in the reaction mixture may be observed, for example, by in-situ IR spectroscopy. If the NCO group concentration is observed to increase above a set value, the rate of isocyanate addition is reduced. Preferably, the isocyanate compound is added to the reaction mixture (consisting of epoxide compound, isocyanate compound, onium salt and oxazolidinone compound, but not considering solvent, if present) with such an addition rate that the concentration of the isocyanate compound in the reaction mixture is < 40 weight-%, preferably < 20 weight-% and more preferred < 15 weight-%>.
In another embodiment of the method according to the invention, in each individual addition step the amount of isocyanate compound added is > 0.1 weight-%> to < 50 weight-%> of the total amount of isocyanate compound to be added. Preferably, the amount of isocyanate compound added per individual addition step is > 1.0 weight-%> to < 40 weight-%> of, more preferred > 5.0 weight-%> to < 35 weight-%) of the total amount of isocyanate compound to be added. Preferably, the time intervals between each individual addition of isocyanate compound to the reaction mixture (consisting of epoxide compound, isocyanate compound, onium salt and oxazolidinone compound, but not considering solvent, if present) is chosen in such a way that the concentration of the isocyanate compound in the reaction mixture at any given point in time is < 40 weight-%>, preferably < 20 weight-%> and more preferred < 15 weight-%>. The actual concentration of NCO groups in the reaction mixture may be observed, for example, by in-situ IR spectroscopy. If the NCO group concentration is observed to increase above a set value, the time interval between the addition steps is increased. In another embodiment of the method according to the invention, the isocyanate compound is a polyisocyanate compound with two or more NCO groups per molecule, preferably with two NCO groups per molecule and the epoxide compound is a polyepoxide compound with two or more epoxy groups per molecule, preferably with two epoxy groups per molecule. In another embodiment of the invention the catalyst is present in an amount of > 0.0001 mol-%> to < 4.0 mol-%), based on the initial amount of epoxide compound. Preferably, the catalyst is present in an amount of > 0.001 mol-%> to < 2.0 mol-%>, more preferred > 0.01 mol-%> to < 1.1 mol-%>.
The method according to the invention is performed for example at temperatures of > 130 °C to < 280 °C, preferably at a temperature of > 135 °C to < 240 °C, most preferred at a temperature of > 140 °C to < 210 °C.
In another embodiment of the method according to the invention, the oxazolidinone product is obtained with a chemoselectivity SOXA, given as the ratio of the molar amount of oxazolidinone moieties to the sum of the molar amount of oxazolidinone moieties and the molar amount of isocyanurate moieties, of > 93 %, preferably > 96 % and most preferably > 99 %. The determination of the chemoselectivity SOXA is described below in the methods.
The present invention is further directed towards an oligomeric or polymeric oxazolidinone compound, obtainable by a method according to the invention using an isocyanate compound with at least two NCO groups per molecule, preferably two NCO groups per molecule, and an epoxide compound with at least two epoxy groups per molecule, preferably two epoxy groups per molecule, comprising at least one unit derived from the isocyanate compound and at least two units derived from the epoxide compound or comprising at least one unit derived from the epoxide compound and at least two units derived from the isocyanate compound. The colour of these oligomeric or polymeric oxazolidinone compounds is < 21 CVI, preferably < 15 CVI and more preferably < 11 CVI in reference to the iodine colour scale (DIN6162). The determination of the colour is described in the methods.
The chain length for the prepolymers can be controlled by changing the ratio between the diepoxide and the diisocyanate compound. An epoxide terminated oligomer is obtained, when the diepoxide is employed in excess. An isocyanate terminated oligomer is obtained, when the diisocyanate is employed in excess. Linear polymer chains with high molecular weight are obtained, when equimolar amounts of diepoxide and diisocyanate are reacted with each other. The precise content of epoxy and isocyanate groups in the diepoxide and diisocyanate, respectively, are preferentially determined before the polymerisation reaction, e.g., by measuring the epoxide number according to German standard norm DIN EN 1877-1 and the isocyanate number according to German standard norm DIN EN ISO 11909.
The number average molecular weight Mn of the polyoxazolidinone compound may be, for example, in the range of > 320 g/mol to < 10Ό00Ό00 g/mol, preferably > 480 g/mol to < 600Ό00 g/mol and most preferably > 3Ό00 g/mol to < 200Ό00 g/mol. The number average molecular weight can be calculated by end-group analysis based on ¾ NMR spectroscopy or determined by gel permeation chromatography (GPC), as described in detail in the methods below.
Without being bound to a theory molecular weight is determined by the molar ratio of polyisocyanate compound to polyepoxide compound. An alternative method to control the molecular weight of the oligooxazolidinone or polyoxazolidinone product constitutes in adding a small amount of a monoepoxide or monoisocyanate to the mixture of polyepoxide and the polyisocyanate compound.
The polyoxazolidinone compounds obtained by a method according to the invention may have a glass transition temperature Tg of >155 °C, preferably >160 °C, most preferably >169 °C. The glass transition temperature Tg can be determined by differential scanning calorimetry (DSC) as described below in the methods.
Preferably this oligomeric or polymeric oxazolidinone compound comprises at at least one, preferably at least two and particularly preferred two terminal epoxide and/or isocyanate groups.
It is also possible that this oligomeric or polymeric oxazolidinone compound comprises at least one terminal group which is non-reactive towards epoxide and/or isocyanate groups. Examples include alkoxy groups or trialkylsiloxane groups. The invention is further directed to the use of a catalyst in the reaction of isocyanate compounds or polyisocyanate compounds with epoxide compounds or polyepoxide compounds, wherein the catalyst is free of halide anions, and comprises a conjugated trigonal-planar anionic moiety having a central atom selected from the elements C or N and three further substituent atoms, selected independently of one another from the elements C, N, O, S and/or P, and wherein the overall charge state of the conjugated trigonal-planar anionic moiety is -1 or -2.
The method according to the invention is suited for the synthesis of oxazolidinone compounds with interesting properties for use, for example, as pharmaceutics or antimicrobiotics. Polyoxazolidinones obtained by the method according to the invention are particularly suited as polymer building blocks in polyurethane chemistry. For example, epoxy-terminated oligomeric oxazolidinones (oligooxazolidinones) may be reacted with polyols or polyamines to form foams or thermosets. Such epoxy-terminated oligomeric oxazolidinones are also suited for the preparation of composite materials. Epoxy-terminated oligomeric oxazolidinones (oligooxazolidinones) may also be reacted with their NCO-terminated counterparts to form high molecular weight polyoxazolidinones, which are useful as transparent, high temperature-stable materials.
Polyoxazolidinones with high molecular weight obtained by the method according to the invention are particularly suited as transparent, high temperature-stable thermoplastic materials.
Examples
Epoxides
Monoepoxide 1 : R-(+)-Styrene oxide, purity 99 %>; stored under argon at -4 °C. Acros Organics, Belgium.
Diepoxide 1 : Bisphenol-A-diglycidylether (Epikote™ Resin 162), purity +99 %, stored at room temperature, Momentive, Germany.
Isocyanates
Monoisocyanate 1 : para-To\y\ isocyanate, purity 99 %; distilled in a partial vacuum (200 mbar, 80 °C) and stored under argon at -4 °C prior to use, Acros Organics, Belgium.
Monoisocyanate 2: /jara-Pentylphenyl isocyanate, purity > 99 %; obtained by reaction of para- pentylaniline with phosgene.
Diisocyanate 1 : 2,4-Toluenediisoyanate, >99 % 2,4-isomer, Bayer MaterialScience AG, Germany Solvents:
If not mentioned otherwise, solvents were purchased from Sigma- Aldrich, Germany, and used as received.
Sulfolane, purity 99%, was obtained from Sigma- Aldrich, Germany.
N-Methylpyrrolidinone (NMP), purity 99.5 %>, anhydrous, was obtained from Sigma-Aldrich, Germany.
Catalysts
Catalyst 1 : Bis-tetraphenylphosphonium carbonate
A mixture of silver carbonate (0.5 g, 1.81 mmol) and methanol (100 mL) was stirred under complete darkness for 1 h at 25 °C, whereupon a partial dissolution of the solid occurred. The clear, overstanding solution was then added dropwise to a solution of tetraphenylphosphonium bromide (1.52 g, 3.62 mmol) in methanol (4 mL) and the resulting mixture stirred in darkness at 25 °C for 3 h. After resting for 16 h, a yellow precipitate had formed, which was removed by filtration. The volatile components of the filtrated solution were then removed by evaporation under reduced pressure to give 1.45 g of a colourless solid.
Catalyst 2: Tetraphenylphosphonium nitrate
A solution of 0.81 g (4.76 mmol) silver nitrate in 33 mL ethanol was prepared at 50 °C and added dropwise to a solution of 1.0 g (2.38 mmol, 0.5 eq.) tetraphenylphosphonium bromide in 2 mL ethanol. The resulting yellow precipitate was removed by filtration. The volatile components of the filtrated solution were removed by evaporation under reduced pressure to give 0.39 g of a colourless solid.
Catalyst 3 (Comp.): Tetraphenylphosphonium chloride 98 % , Sigma-Aldrich, Germany.
Catalyst 4 (Comp.): Tetraphenylphosphonium bromide 97 %, Sigma-Aldrich, Germany. Reactor:
The 300 ml stainless steel autoclave used in the synthesis of polyoxazolidinones had a height (internal) of 10.16 cm and an internal diameter of 6.35 cm. The reactor was fitted with an electric heating jacket (510 watt maximum heating capacity). The counter cooling consisted of a U-shaped dip tube with an external diameter of 6 mm, which projected into the reactor to within 5 mm of the bottom and through which cooling water at approximately 10°C was passed. The water stream was switched on and off by means of a solenoid valve. The reactor was also fitted with an inlet tube and a temperature probe of 1.6 mm diameter, both of which projected into the reactor to within 3 mm of the bottom. The impeller agitator used in the examples was a pitched-blade turbine to which a total of two agitator stages, each with four agitator blades (45°) of 35 mm diameter and 10 mm height, were attached to the agitator shaft at a distance of 7 mm.
In the terminology used in the examples, the term "pulse addition", corresponding to the step-wise addition mode of the isocyanate, means that the isocyanate compound is added in individual steps, comprising a part of the total amount of the isocyanate compound, to the reaction mixture.
In-situ infrared (IR) spectroscopy:
The composition of the reaction mixture during the synthesis of oxazolidinone 1 was followed with a Matrix-MF spectrometer (Bruker Optic GmbH) equipped with a high-pressure attenuated total reflectance (ATR) IR fibre optical probe. The ATR IR fibre optical probe (3.17 mm outer diameter, 90° diamond prism with 1 x 2 mm basal area and 1 mm height as ATR element, 2 χ 45° reflection of the IR beam, IR beam coupled via fibre optics) was fitted into the reactor in such a way that the diamond at the end of the optical probe was immersed entirely into the reaction mixture. The IR spectra were recorded using the OPUS 6.5 software. Before starting the experiment, a background spectrum was taken against ambient air (scan velocity 40 kHz, average of 100 scans). During the experiment, Infrared spectra were recorded every 15 seconds (scan velocity 40 kHz, average of 20 scans). Complete conversion was indicated by the disappearance of the characteristic isocyanate band at 2250-2260 cm"1. The formation of oxazolidinone moieties was indicated by the appearance of the characteristic oxazolidinone band at 1743 cm"1. The formation of isocyanurate moieties was indicated by the appearance of the characteristic isocyanurate band at 1690 cm"1.
The spectra were analysed with the software PEAXACT 3.1 - Software for Quantitative Spectroscopy and Chromatography, S'PACT GmbH using the Integrated Hard Model (IHM)
method. The hard model for analysing the IR spectra of the reaction mixtures was created by linear combination of hard models for the single components monoisocyanate, oxazolidinone and isocyanurate. The hard model for the single components was created as follows: Monoisocyanate 1 :
A 10 mL glass flask containing 5 mL propylene carbonate was immersed into an oil bath preheated to 160 °C. A background IR spectrum (average of 100 scans) was measured against air. The IR probe was then inserted into the glass flask in such a way that the diamond at the end of the optical probe was immersed entirely into the reaction mixture. After flushing the glass flask with argon, the glass flask was capped with a rubber seal and another background IR spectrum was measured (average of 100 scans). Subsequently, monoisocyanate 1 (0.37 mL, 2.95 mmol, 5 mol% relative to propylene carbonate) was injected with a microliter syringe through the seal into the reaction mixture and several IR spectra were recorded of the resulting mixture. The relevant signals in the region 2150 to 2400 cm"1 were selected from a representative IR spectrum and the model refined to achieve an optimum fit between a superposition of the selected signals and the averaged IR spectra of the mixture.
Oxazolidinone 1 :
A 10 mL glass flask containing 0.5 mL propylene carbonate was immersed into an oil bath preheated to 160 °C. A background IR spectrum (average of 100 scans) was measured against air. The IR probe was then inserted into the glass flask in such a way that the diamond at the end of the optical probe was immersed entirely into the reaction mixture. After flushing the glass flask with argon, the glass flask was capped with a rubber seal and another background IR spectrum was measured (average of 100 scans). Subsequently, a solution of oxazolidinone 1 (0.471 g, 1.18 mmol, 10 mol% relative to propylene carbonate) in 0.5 mL propylene carbonate was injected with a microliter syringe through the seal into the reaction mixture and several IR spectra were recorded of the resulting mixture. The relevant signals in the region 1650 to 1800 cm"1 were selected from a representative IR spectrum and the model refined to achieve an optimum fit between a superposition of the selected signals and the averaged IR spectra of the mixture.
Isocyanurate 1 :
A 10 mL glass flask containing 0.5 mL propylene carbonate was immersed into an oil bath preheated to 160 °C. A background IR spectrum (average of 100 scans) was measured against air. The IR probe was then inserted into the schlenk flask in such a way that the diamond at the end of the optical probe was immersed entirely into the reaction mixture. After flushing the glass flask with argon, the Glass flask was capped with a rubber seal and another background IR spectrum was measured (average of 100 scans). Subsequently, a solution of isocyanurate 1 (0.471 g, 1.18 mmol,
10 mol% relative to propylene carbonate) in 0.5 mL propylene carbonate was injected with a microliter syringe through the seal into the reaction mixture and several IR spectra were recorded of the resulting mixture. The relevant signals in the region 1600 to 1750 cm"1 were selected from a representative IR spectrum and the model refined to achieve an optimum fit between a superposition of the selected signals and the averaged IR spectra of the mixture.
The IR spectra obtained in-situ during the catalyst tests were analysed by performing a hard modelling factor analysis (HMFA) as described in E. Kriesten, D. Mayer, F. Alsmeyer, C. B. Minnich, L. Greiner and W. Marquardt, Chemomet. Intell. Lab. Sys., 93(2), 108 (2008) using the hard models obtained by the method described above. The molar amount n of the respective component i was calculated.
The chemoselectivity SOXA towards oxazolidinone was calculated at the end point of the reaction based on the molar yield of oxazolidinone (OXA) and isocyanurate (ICT) according to eq. 1 ,
where nfmoxA is the molar amount of oxazolidinone at the end of the reaction and nfmicT is the molar amount of isocyanurate at the end of the reaction.
where ti 2 is half the time interval from injection of the second monoisocyanate pulse until no further decrease of the monoisocyanate concentration was observed, n co,to is the molar amount of monoisocyanate in the reaction mixture after injection of the second monoisocyanate pulse, nNco,ti/2 is the residual molar amount of monoisocyanate observed by in-situ IR spectroscopy at ti 2 after injection of the second monoisocyanate pulse, and ncat is the molar amount of catalyst in the reaction mixture after injection of the second isocyanate pulse.
Solid state infrared (IR) spectroscopy:
The solid state IR analysis was performed on a Bruker ALPHA-P IR spectrometer equipped with a diamond probe head. Before obtaining the IR spectrum of the sample, a background spectrum was recorded against ambient air. After that, a small sample (several milligrams) of the prepolymer sample was applied to diamond probe and the IR spectrum recorded on a computer connected with the spectrometer using OPUS 6.5 software averaging over 32 spectra obtained in the range of 4000 to 400 cm"1 with a resolution of 4 cm"1.
Colorimetry:
The colorimetric measurements were performed on a Hach Lange Lico 150 Colorimeter. For the measurement a solution of the sample in NN-dimethylacetamide (c = 5 mg/mL) was prepared. For reference pure NN-dimethylacetamide was used. For oxazolidinone 1, the listed values are given in Hazen units (HU) and refer to the Hazen (Pt/Co) scale (ISO 6271). In case of polyoxazolidinone 1, the listed values refer to the iodine color value (CVI, DIN 6162).
Gel permeation chromatography (GPC):
GPC measurements were performed at 40 °C in Ν,Ν-dimethylacetamide (DMAc, flow rate of 0.6 mL mm 1). The column set consisted of 4 consecutive columns (GRAM 3000, HEMA300, HEMA 40, HEMA 40). Samples (concentration 5-15 g L"1, injection volume 100 μΕ) were injected employing an HP1200 auto sampler. A UV-detector was used for following the concentration at the exit of the column. Raw data were processed using the PSS WinGPC Unity software package. Polystyrene of known molecular weight was used as reference to calculate the molecular weight distribution. The number average molecular weight measured by GPC is denominated as Mn(GPC) in the examples.
Thermogravimetric analysis (TGA):
The stability of the polyoxazolidinones was characterised by thermogravimetric analysis (TGA). The measurements were performed on a Mettler Toledo TGA/DSC 1. The sample (6 to 20 mg) was heated from 25 °C to 600 °C with a heat rate of 10 K/min and the relative weight loss followed in dependence of temperature. For data analysis the software STAR6 SW 11.00 was used. As decomposition temperature the inflection point of the sinuidal weight loss curve is stated. Differential scanning calorimetry (DSC):
The glass transition point Tg was recorded on a Mettler Toledo DSC 1. The sample (4 to 10 mg) was heated from 25 °C to 250 °C at a heating rate of 10 K/min then cooled down to 30 °C at a rate of 10 K/min. This heating cycle was repeated four times. For data analysis the software STAR6 SW 11.00 was used. For determination of the glass transition temperature a tangential analysis method was used. The midpoint of the intersection point between the tangent at low temperature and the tangent in the mid temperature range and the intersection point between the tangent in the mid temperature range and the tangent at high temperature is stated.The reported Tg was taken from the third heating cycle.
Polymerisation reactions
General procedure 1 : Synthesis of oxazolidinone 1 from monoepoxide 1 and monoisocyanate 1 A 10 mL glass flask containing catalyst, monoepoxide 1 (1 mL, 8.77 mmol), a cylindrical magnetic stirring bar (PTFE, length 10 mm, diameter 6 mm) and optionally 2 mL of solvent was immersed into a hot oil bath set to 160 °C and stirring started. A single IR background spectrum (average of 100 scans) was measured at air, then the IR probe was inserted into the glass flask in such a way that the diamond at the end of the optical probe was immersed entirely into the reaction mixture. After flushing the flask with argon, the glass flask was capped and another single IR background spectrum was measured (average of 100 scans). Then, IR measurement was started. IR spectra (average of 20 scans) were recorded throughout the entire experiment at 60 second time intervals. Subsequently, a pulse of monoisocyanate 1 (0.36 mL, 2.92 mmol, 0.33 equiv. with respect to monoepoxide 1) was injected with a microliter syringe through the seal into the reaction mixture. When the intensity of the monoisocyanate signal in the IR spectrum had decreased below 0.005 absorbance units, a second pulse of monoisocyanate 1 (0.36 mL, 2.92 mmol, 0.33 equiv. with respect to monoepoxide 1) was injected into the reaction mixture. When after injection of the second monoisocyanate pulse the intensity of the monoisocyanate signal in the IR spectrum had decreased below 0.005 absorbance units, a third pulse of monoisocyanate 1 (0.36 mL, 2.92 mmol, 0.33 equiv. with respect to monoepoxide 1) was injected into the reaction mixture. When after injection of the third monoisocyanate pulse monoisocyanate 1 had been completely consumed (indicated by the disappearance of the isocyanate signal at around 2270 cm"1 in the IR spectrum), the reaction was stopped by removing the oil bath and cooling the reaction mixture to 25 °C. The product was analysed without further purification.
General procedure 2: Synthesis of polyoxazolidinone 1 from diepoxide 1 and diisocyanate 1 in solvent.
The reactions were performed in a 300 ml stainless steel autoclave as described above, using a motor with a stirring power of 90 W. The reactor was charged with diepoxide 1 (15.0 g, 44.1 mmol) and catalyst and subsequently flushed with argon. After addition of 40 ml of dry NMP, the reactor was sealed and the mixture was heated to 200 °C under rapid stirring (1000 rpm). After reaching 200 °C, a solution of diisocyanate 1 (7.3 g, 41.97 mmol) in 15 ml dry NMP was added with an HPLC pump (10 ml pump head) over 2.5 h. After an overall reaction time of 19.25 h (starting with addition of diisocyanate 1), the reaction mixture was cooled down to room temperature. The resulting reaction mixture was poured into 150 ml of methanol. The resulting precipitate was collected by filtration and washed with methanol and with diethylether. The obtained powder was dried at 5 χ 10"2 mbar for 3 hours.
Example 1 :
Synthesis of oxazolidinone 1 from monoepoxide 1 and monoisocyanate 1 in the presence of catalyst 1 (bis-tetraphenylphosphonium carbonate) at 160 °C in the absence of a solvent
The synthesis was performed following the general procedure 1 at 160 °C in the absence of a solvent, using 64.8 mg (0.0877 mmol, 1 mol% with respect to monoepoxide 1) of bis- tetraphenylphosphonium carbonate (catalyst 1). A pale yellow solid was obtained.
Colorimetry: 16 HU
The formation of side products like isocyanurates, carbodiimides and homo-polymers of the epoxides was not observed.
Example 2:
Synthesis of oxazolidinone 1 from monoepoxide 1 and monoisocyanate 1 in the presence of catalyst 2 (bis-tetraphenylphosphonium nitrate) at 160 °C in the absence of a solvent
The synthesis was performed following the general procedure 1 without a solvent, using 35.3mg
(0.0877 mmol, 1 mol% with respect to monoepoxide 1) of tetraphenylphosphonium nitrate
(catalyst 2). A pale yellow solid was obtained.
Colorimetry: 18 HU
The formation of other side products than isocyanurates, such as carbodiimides and homo- polymers of the epoxides was not observed.
Synthesis of oxazolidinone 1 from monoepoxide 1 and monoisocyanate 1 in the presence of reference catalyst 1 (tetraphenylphosphonium chloride) at 160 °C in the absence of a solvent
The synthesis was performed following the general procedure 1 without a solvent, using 33.1 mg (0.0877 mmol, 1 mol% with respect to monoepoxide 1) of tetraphenylphosphonium chloride (catalyst 3). A yellow solid was obtained.
Synthesis of oxazolidinone 1 from monoepoxide 1 and monoisocyanate 1 in the presence of reference catalyst 2 (tetraphenylphosphonium bromide) at 160 °C in the absence of a solvent
The synthesis was performed following the general procedure 1 without a solvent, using 36.8 mg (0.0877 mmol, 1 mol % with respect to monoepoxide 1) of tetraphenylphosphonium bromide (catalyst 4). A yellow solid was obtained.
Table 1 : Results of Examples 1 to 4
(comp.) = comparison
The resulting oxazolidinones prepared from monoepoxides and monoisocyanates in the presence of the inventive catalysts exhibit lower colour intensity (examples 1 and 2) than the ones prepared with the non-inventive catalysts (comparative examples 3 and 4). Furthermore, a higher chemoselectivity SOXA is obtained when the process is performed in the presence of the inventive catalysts (examples 1 and 2).
Example 1 (catalyst 1, according to the invention) compared to examples 3 and 4 (non- inventive catalysts) further demonstrates that a higher turnover frequency TOF1/2 is obtained.
Example 5:
Synthesis of oxazolidinone 1 from monoepoxide 1 and monoisocyanate 1 in the presence of catalyst 1 (bis-tetraphenylphosphonium carbonate) at 160 °C in the presence of a solvent
The synthesis was performed following the general procedure 1 in 2 mL sulfolane, using 32.4 mg (0.0439 mmol, 0.5 mol% with respect to monoepoxide 1) of catalyst 1. A pale yellow solution was obtained.
Example 5 demonstrates that oxazolidinones are obtained at high activity, when the reaction of monoepoxides and monoisocyanates is performed using a catalyst according to the invention in a solvent process.
Example 6:
Synthesis of oxazolidinone 1 from monoepoxide 1 and monoisocyanate 1 in the presence of a different amount of catalyst 1 (bis-tetraphenylphosphonium carbonate) at 160 °C in the absence of a solvent
The synthesis was performed following the general procedure 1 at 160 °C in the absence of a solvent, using 32.4 mg (0.0439 mmol, 0.5 mol% with respect to monoepoxide 1) of catalyst 1. A pale yellow solid was obtained.
Colorimetry: 18 HU
Table 2: Results of the reaction of monoisocyanate 1 and monoepoxide 1 in the presence of catalyst 1 at different catalyst concentrations.
Example 6 demonstrates that catalyst 1 (catalyst according to the invention) shows good activity (high TOF1/2) and affords oxazolidinones with a low colour intensity also at reduced catalyst concentration.
Examples 7 and 8:
Synthesis of oxazolidinone 1 from monoepoxide 1 and monoisocyanate 1 in the presence of catalyst 1 (bis-tetraphenylphosphonium carbonate) at different temperatures
Examples 7 and 8 were preformed following general procedure 1 in the absence of a solvent at different temperatures. The catalyst used in both examples was catalyst 1 (64.8 mg, 0.0877 mmol, 1 mol% with respect to monoepoxide 1). The results are presented in Table 3. Table 3: Reaction of monoisocyanate 1 and monoepoxide 1 in the presence of catalyst 1 under solvent-free conditions at different reaction temperatures.
Example Temperature TOF1/2
[°C] [h ]
7 140 83
1 160 278
8 180 327
The results of Table 3 are in accordance with the general teaching that the catalyst activity increases with the temperature. These examples demonstrate that the reaction may be also performed at higher temperatures than 160 °C. Example 9:
Synthesis of polyoxazolidinone 1 from diepoxide 1 and diisocyanate 1 in the presence of catalyst 1 (bis-tetraphenylphosphonium carbonate) at 200 °C in the presence of a solvent
The synthesis was performed following the general procedure 2 using 15.0 g (44.1 mmol) of diepoxide 1, 342 mg (0.46 mmol) of catalyst 1 (bis-tetraphenylphosphonium carbonate), 7.30 g (41.97 mol) of diisocyanate 1 in 60 mL of dry NMP. A pale brown powder (16.3 g) was obtained.
The presence of oxazolidinone moieties was confirmed by the characteristic IR-signal at v=1749 cm"1. The IR-spectra did not show the characteristic isocyanurate-band in the region of 1690-1710 cm"1, thus the chemoselectivity was > 96 %. The formation of other side products, such as carbodiimides and homo-polymers of the epoxides was not observed.
Colorimetry: 10.7 CVI
Mn(GPC): 3370 g/mol
TD: 402°C
Tg : 169°C
Example 10 (Comparison):
Synthesis of polyoxazolidinone 1 from diepoxide 1 and diisocyanate 1 in the presence of catalyst 4 (tetraphenylphosphonium bromide) at 200 °C in the presence of a solvent
The synthesis was performed following the general procedure 1 using 15.0 g (44.1 mmol) of diepoxide 1, 194 mg (0.46 mmol) of catalyst 4 (tetraphenylphosphonium bromide) and 7.30 g (41.97mol) of diisocyanate 1. A pale brown powder (14.6 g) was obtained.
The presence of oxazolidinone moieties was confirmed by the characteristic IR-signal at v=1746 cm"1. The IR-spectra did not show the characteristic isocyanurate-band in the region of 1690-1710 cm"1.
Colorimetry: 21.3 CVI
Mn(GPC): 3390 g/mol
TD: 409°C
Tg : 155°C
Table 4: Comparison of polyoxyzolidinone products obtained from reaction of diisocyanate 1 and diepoxide 1 by use of catalyst 1 and catalyst 4.
Example Catalyst Colorimetry Tg
[CVI] [°C]
9 Catalyst 1 10.7 169
10 (comp.) Catalyst 4 21.3 155
(comp.) = comparison
The comparison of example 9 (catalyst 1, according to the invention) with comparison example 10 (catalyst 4) demonstrates that under otherwise equal reaction conditions, polyoxazolidinones with lower colour intensity are obtained, when a catalyst according to the invention is employed.
Example 11 :
Synthesis of polyoxazolidinone 2 from diepoxide 1, diisocyanate 1 and monoisocyanate 2 in the presence of catalyst 1 (bis-tetraphenylphosphonium carbonate) at 200 °C in the presence of a solvent
The synthesis was performed following the general procedure 2 using 15.0 g (44.1 mmol) of diepoxide 1, 342 mg (0.46 mmol) of catalyst 1 (bis-tetraphenylphosphonium carbonate), 7.30 g (41.97 mmol) of diisocyanate 1 and 900 mg (4.76 mmol) of monoisocyanate 2 in 60 mL of a mixture of ort/zo-dichlorobenzene and NMP in a volume ratio of 1 :5. A pale brown powder was obtained.
The presence of oxazolidinone moieties was confirmed by the characteristic IR-signal at v=1749 cm"1.
Colorimetry: 4.3 CVI
Mn(GPC): 4821 g/mol
TD: 404°C
Tg: 153°C
Example 11 demonstrates that polyoxazolidinone compounds are obtained, when diepoxides, diisocyanates, and monoisocyanates are reacted in the presence of a catalyst according to the invention.
Claims
Claims:
A method for the production of oxazolidinone compounds, comprising the step of reacting an epoxide compound and an isocyanate compound in the presence of a catalyst,
characterized in that the catalyst
is free of halide anions, and
comprises a conjugated trigonal-planar anionic moiety having a central atom selected from the elements C or N and
three further substituent atoms, selected independently of one another from the elements C, N, O, S and/or P, and
wherein the overall charge state of the conjugated trigonal-planar anionic moiety is -1 or -2.
2. A method according to claim 1, wherein the anionic moiety in the catalyst has the general formula (V),
(V)
wherein
n is an integer of 1 or 2,
A is C or N+,
X is 0", OH, S\ SH, OR, SR, NRR', NHR, N(R)", N(S02R)" or PRR',
wherein R, R' independently of one another are linear or branched, saturated, mono- or polyunsaturated aliphatic, cycloaliphatic or aromatic groups comprising 1 to 20 carbon atoms, optionally substituted with one or more heteroatom containing groups, wherein the heteroatom is selected from N, O, S, P, Si, F or CI,
wherein R, R' can be connected within a (hetero)aliphatic or (hetero)aromatic mono- or polycyclic ring comprising 1 to 20 carbon atoms and/or heteroatoms selected from the group N, P, O and/or S optionally substituted with one or more heteroatom containing groups, wherein the heteroatom is selected from N, O, S, P, Si, F and/or CI, or with an alkyl group comprising 1 to 20 carbon atoms,
Y is O, S or N, wherein N can be substituted by a group R", wherein R" independently of R and R' has the same meaning as specified for R, R',
Z is -0", S\ N(R"')-, N(S02R'")~, wherein R'" independently of R, R' and R" has the same meaning as specified for R, R', R", or a carbon atom which is part of an aromatic group comprising 1 to 20 carbon atoms,
wherein in case that Y is N, Y and X can be connected within a (hetero)aliphatic or (hetero)aromatic ring having 5 to 6 carbon atoms and/or heteroatoms selected from the group N, P, O and/or S and optionally comprising an annulated aromatic ring having 6 carbon atoms optionally substituted with one or more heteroatom containing groups, wherein the heteroatom is selected from N, O, S, P, Si, F and/or CI, or with an alkyl group comprising 1 to 20 carbon atoms.
A method according to claim 1 or 2, wherein the anionic moiety of the catalyst is selected from the group comprising
CO32-, RO-CO2-, RS-CO2-, RHN-CO2-, RRTNT-C02-, CSO22-, RO-CSCT, RHN-CSO", RRTM- CSCT, RS-CSCr, COS22-, RO-CS2-, RHN-CS2-, RRTSTCS2-, RR'N-CSO , CS3 2", RS-CS2 _, RO-C(=NR")0", RO-C(=NR")S", RS-C(=NR")0", RS-C(=NR")S", RN=C(NHR")0", R"N=C(NRR')0", R"N=C(NHR)S\ R"N=C(NRR')S\ RO-CO-N(R"')~, RS-CO-N(R"')~ , RR'N-CO-N(R"')~, RO-CS-N(R"')", RS-CS-N(R"')~, RR'N-CS-N(R"')~, RO-C(=NR")- N(R"')~, RS-C(=NR")-N(R"')~, RR'N-C(=NR")-N(R" ')~, RO-CO-N(S02R'")~, RS-CO- N(S02R'")~, RR'N-CO-N(S02R"')", RO-CS-N(S02R'")~, RS-CS-N(S02R'")~, RR'N-CS- N(S02R'")~, RO-C(=NR")-N(S02R"')", RS-C(=NR")-N(S02R'")~, RR'N-C(=NR")- N(S02R'")~,
wherein R, R', R", R'" independently of one another are linear or branched, saturated, mono- or polyunsaturated aliphatic, cycloaliphatic or aromatic groups comprising 1 to 20 carbon atoms, optionally substituted with one or more heteroatom containing groups, wherein the heteroatoms are selected from N, O, S, P, Si, F and/or CI,
wherein R and R' and/or R'", and/or R'and R" and/or R'" can be connected within a (hetero)aliphatic or (hetero)aromatic, mono- or polycyclic ring system comprising 1 to 20 carbon atoms and/or heteroatoms selected from the group N, P, O and/or S, optionally substituted with one or more heteroatom containing groups, wherein the heteroatom is selected from N, O, S, P, Si, F and/or CI, or with an alkyl group comprising 1 to 20 carbon atoms,
4,5-dihydro-oxazol-2-olate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, oxazol-2-olate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, benzoxazol-2-olate, wherein the benzene ring is optionally substituted with one to four aliphatic, cycloaliphatic or aromatic groups having 1 to 20 carbon atoms, 4,5-dihydro-thiazol-2-olate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, thiazol-2- olate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, benzothiazol-2-olate, wherein the aromatic
ring is optionally substituted with one to four aliphatic, cycloaliphatic or aromatic groups having 1 to 20 carbon atoms, 4,5-dihydro-l,3-diazol-2-olate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, l,3-diazol-2-olate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, benzo-l,3-diazol-2-olate, wherein the aromatic ring is optionally substituted with one to four aliphatic, cycloaliphatic or aromatic groups having 1 to 20 carbon atoms, 4,5-dihydro-oxazol-2-thiolate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, oxazol-2-thiolate, optionally substituted in 4- and/or 5- position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, benzoxazol-2-thiolate, wherein the aromatic moiety is optionally substituted with one to four aliphatic, cycloaliphatic or aromatic groups having 1 to 20 carbon atoms, 4,5-dihydro- thiazol-2-thiolate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, thiazol-2-thiolate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, benzothiazol-2-thiolate, wherein the aromatic moiety is optionally substituted with one to four aliphatic, cycloaliphatic or aromatic groups having 1 to 20 carbon atoms, 4,5-dihydro-l,3-diazol-2-thiolate, optionally substituted in 4- and/or 5- position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, l,3-diazol-2-thiolate, optionally substituted in 4- and/or 5-position with an aliphatic, cycloaliphatic or aromatic group having 1 to 20 carbon atoms, benzo-l,3-diazol-2-thiolate, wherein the aromatic moiety is optionally substituted with one to four aliphatic, cycloaliphatic or aromatic groups having 1 to 20 carbon atoms, pyrimidin-2-yl amide, optionally N-substitued, e.g. with aryl or alkylsulfonyl groups, 2-pyrimidin-2-olate, N- alkylsulfonyl or N-arylsulfonyl carbamimidoylamide, optionally with further N- and/or
N"-substituents, or NCb".
A method according to one of the claims 1 to 3, wherein the anionic moiety of the catalyst is selected from the group comprising CO32", CSO22", COS22", RO-CO2 , wherein R is methyl, ethyl, propyl, isopropyl, butyl or phenyl, RS-CO2", wherein R is methyl, ethyl or phenyl, R2N-CO2" , wherein R is methyl, ethyl or phenyl, R2N-CSO , wherein R is methyl, ethyl or phenyl, R2N-CS2", wherein R is methyl, ethyl or phenyl, RO-CS2", wherein R is methyl, ethyl or phenyl, 4,5-dihydro-oxazol-2-thiolate, oxazol-2-thiolate, benzoxazol-2- thiolate, 4,5-dihydro-thiazol-2-thiolate, thiazol-2-thiolate, benzothiazol-2-thiolate, 4,5- dihydro-l,3-diazol-2-thiolate, l,3-diazol-2-thiolate, benzo-l,3-diazol-2-thiolate or N03~.
5. A method according to one of the claims 1 to 4, wherein the anionic moiety of the catalyst is selected from the group comprising C03 2", N03 ", CS02 2", COS2 2", (CH3)2N-CS2~, (C2H5)2N-CS2_, and benzothiazol-2-thiolate. 6. A method according to one of the claims 1 to 5, wherein the anionic moiety of the catalyst is selected from the group comprising CO32", NO3 , (CH3)2N-CS2~ or (C2H5)2N-CS2~.
7. A method according to one of the claims 1 to 6, wherein the conjugated trigonal-planar anionic moiety comprised in the catalyst is generated from an appropriate nucleophile and C02, SCO or CS2.
8. A method according to one of the claims 1 to 7, wherein the cationic part of the catalyst is represented by formula (VI)
[M(R1)(R2)(R3)(R4)]+ (VI)
wherein
M is phosphorous or antimony,
(Rl), (R2), (R3), (R4) are independently of one another selected from the group comprising linear or branched alkyl groups containing 1 to 22 carbon atoms, optionally substituted with heteroatoms and/or heteroatom containing substituents, cycloaliphatic groups containing 3 to 22 carbon atoms, optionally substituted with heteroatoms and/or heteroatom containing substituents, CI to C3 alkyl-bridged cycloaliphatic groups containing 3 to 22 carbon atoms, optionally substituted with heteroatoms and/or heteroatom containing substituents and aryl groups containing 6 to 18 carbon atoms, optionally substituted with alkyl groups containing 1 to 10 carbon atoms and/or heteroatoms.
9. A method according to one of the claims 1 to 8, wherein the cationic part of the catalyst is represented by formula (VI)
[M(R1)(R2)(R3)(R4)]+ (VI)
wherein
M is phosphorous or antimony,
(Rl), (R2), (R3), (R4) are independently of one another selected from the group comprising phenyl, n-butyl and cyclohexyl.
10. Method according to one or more of claims 1 to 9 wherein the isocyanate compound is added to the epoxide compound in a continuous or step-wise manner with two or more individual addition steps in the step-wise addition,
wherein in each individual addition step the amount of isocyanate compound added is < 50 weight- % of the total amount of isocyanate compound to be added.
1 1. Method according to one or more of claims 1 to 10 wherein the reaction is conducted at a temperature of > 130 °C to < 280 °C.
12. An oxazolidinone compound, obtainable by a method according to one or more of claims 1 to 1 1 , with a chemoselectivity SOXA to the oxazolidinone product of > 93 %. 13. An oligomeric or polymeric oxazolidinone compound, obtainable by a method according to one or more of claims 1 to 1 1 using an isocyanate compound with two or more NCO groups per molecule and an epoxide compound with two or more epoxy groups per molecule, comprising at least one unit derived from the isocyanate compound and at least two units derived from the epoxide compound or comprising at least one unit derived from the epoxide compound and at least two units derived from the isocyanate compound, with a colour intensity of < 21 CVI in reference to the iodine colour scale (DIN 6162) .
The compound according to claim 12 or 13, comprising at least one terminal epoxide and/or isocyanate group or comprising at least one terminal group which is non-reactive towards epoxide and/or isocyanate groups.
The use of a catalyst in the reaction of isocyanate compounds or polyisocyanate compounds with epoxide compounds or polyepoxide compounds, wherein the catalyst is free of halide anions, and
comprises a conjugated trigonal-planar anionic moiety having a central atom selected from the elements C or N and
three further substituent atoms, selected independently of one another from the elements C, N, O, S and/or P, and
wherein the overall charge state of the conjugated trigonal-planar anionic moiety is -1 or -