WO2015156582A1 - 복합 금속 촉매 조성물과 이를 이용한 1,4-사이클로헥산디메탄올 제조방법 및 장치 - Google Patents
복합 금속 촉매 조성물과 이를 이용한 1,4-사이클로헥산디메탄올 제조방법 및 장치 Download PDFInfo
- Publication number
- WO2015156582A1 WO2015156582A1 PCT/KR2015/003476 KR2015003476W WO2015156582A1 WO 2015156582 A1 WO2015156582 A1 WO 2015156582A1 KR 2015003476 W KR2015003476 W KR 2015003476W WO 2015156582 A1 WO2015156582 A1 WO 2015156582A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- metal catalyst
- terephthalic acid
- compound
- reaction
- reduction
- Prior art date
Abstract
Description
Claims (20)
- 팔라듐(Pd) 화합물을 포함하는 제1금속 촉매; 및 루테늄(Ru) 화합물, 주석(Sn) 화합물 및 백금(Pt) 화합물을 포함하는 제2금속 촉매;를 포함하여 방향족 디카르복실산으로부터 지방족 고리의 디올 화합물로 전환시키는 복합 금속 촉매 조성물.
- 팔라듐(Pd) 화합물을 포함하는 제1금속 촉매; 및 루테늄(Ru) 화합물, 주석(Sn) 화합물 및 백금(Pt) 화합물을 포함하는 제2금속 촉매;를 포함하는 복합 금속 촉매 조성물의 존재 하에 테레프탈산을 환원시키는 단계를 포함하는 1,4-사이클로헥산디메탄올 제조방법.
- 제2항에 있어서,상기 테레프탈산을 환원시키는 단계는 상기 제1금속 촉매 존재 하에 수행되고, 상기 제2금속 촉매 존재 하에 상기 테레프탈산의 환원 결과물을 환원시키는 단계를 포함하는 것을 특징으로 하는 방법.
- 제3항에 있어서,상기 제2금속 촉매는 상기 루테늄(Ru) 화합물, 주석(Sn) 화합물 및 백금(Pt) 화합물을 1 : 0.8~1.2 : 0.2~0.6의 중량비로 포함하는 것을 특징으로 하는 방법.
- 제4항에 있어서,상기 테레프탈산을 환원시키는 단계 및 상기 테레프탈산의 환원 결과물을 환원시키는 단계는 연속적으로 수행되는 것을 특징으로 하는 방법.
- 제5항에 있어서,상기 테레프탈산을 환원시키는 단계 및 상기 테레프탈산의 환원 결과물을 환원시키는 단계는 하나의 반응기에서 수행되는 것을 특징으로 하는 방법.
- 제6항에 있어서,상기 반응기는 상기 제1금속 촉매와 상기 제2금속 촉매가 고정층에 분할되어 순차적으로 주입된 것을 특징으로 하는 방법.
- 제2항에 있어서,상기 제1금속 촉매와 상기 제2금속 촉매가 각각 담체에 고정된 것을 특징으로 하는 방법.
- 제8항에 있어서,상기 담체를 포함한 제1금속 촉매는 상기 테레프탈산 100중량부에 대하여 1~50중량부 사용되는 것을 특징으로 하는 방법.
- 제8항에 있어서,상기 담체를 포함한 제2금속 촉매는 상기 테레프탈산 100중량부에 대하여 1~50중량부 사용되는 것을 특징으로 하는 방법.
- 제8항에 있어서,상기 제2금속 촉매는 상기 루테늄(Ru) 화합물을 0.5~20중량% 포함하는 것을 특징으로 하는 방법.
- 제8항에 있어서,상기 담체는 200~900㎡/g의 비표면적을 갖는 다공성 무기물 담체인 것을 특징으로 하는 방법.
- 제8항에 있어서,상기 담체는 전체 세공 용적이 1.2㎤/g 이하이고, 10Å 이하의 반경을 갖는 세공의 용적이 0.1~0.8㎤/g인 것을 특징으로 하는 방법.
- 제8항에 있어서,상기 담체는 Y형 제올라이트인 것을 특징으로 하는 방법.
- 제3항에 있어서,상기 테레프탈산의 환원은 상기 테레프탈산 및 수소 기체를 접촉시켜 수행되고, 상기 테레프탈산의 환원 결과물의 환원은 상기 테레프탈산의 환원 결과물 및 수소 기체를 접촉시켜 수행되는 것을 특징으로 하는 방법.
- 제3항에 있어서,상기 테레프탈산의 환원 및 상기 테레프탈산의 환원 결과물의 환원은 각각 50~350℃의 온도에서 수행되는 것을 특징으로 하는 방법.
- 제3항에 있어서,상기 테레프탈산의 환원 및 상기 테레프탈산의 환원 결과물의 환원은 각각 30~150bar의 압력도에서 수행되는 것을 특징으로 하는 방법.
- 제3항에 있어서,상기 제2금속 촉매는 상기 루테늄(Ru) 화합물, 주석(Sn) 화합물 및 백금(Pt) 화합물을 1 : 0.9~1.1 : 0.3~0.55의 중량비로 포함하는 것을 특징으로 하는 방법.
- 제3항에 있어서,최종 생성된 상기 1,4-사이클로헥산디메탄올은 트랜스-1,4-사이클로헥산디메탄올 몰비율이 20% 이상인 것을 특징으로 하는 방법.
- 테레프탈산을 환원시켜 1,4-사이클로헥산디메탄올을 제조하는 장치에 있어서,테레프탈산이 이송되어 상단으로 유입되는 원료투입부, 상기 원료 투입부로 유입된 상기 테레프탈산의 환원 반응이 수행되는 반응부 및 하단에 형성되어 상기 반응부에서 생성된 생성물을 회수부로 이송되도록 하는 유출부를 포함하는 반응기;상기 테레프탈산과 이온교환수가 투입되어 질량유량계를 통한 불활성 기체에 의해 상기 반응기로 용해된 테레프탈산을 이동시키는 예열기; 및상기 반응부에서 생성된 생성물이 유출되는 상기 유출부로부터 상기 생성물을 회수하는 회수부;를 포함하되,상기 반응부는 팔라듐(Pd) 화합물을 포함하는 제1금속 촉매가 주입되어 원료 투입부로 유입된 상기 테레프탈산의 환원 반응이 수행되는 상부 반응부 및 루테늄(Ru) 화합물, 주석(Sn) 화합물 및 백금(Pt) 화합물을 포함하는 촉매로서 상기 제1금속 촉매와 계면을 형성하도록 제2금속 촉매가 주입되어, 상기 상부 반응부에서 환원된 결과물의 환원 반응이 수행되는 하부 반응부를 포함하는 것을 특징으로 하는 장치.