WO2014160616A1 - Process for making urethane-isocyanurates - Google Patents
Process for making urethane-isocyanurates Download PDFInfo
- Publication number
- WO2014160616A1 WO2014160616A1 PCT/US2014/031520 US2014031520W WO2014160616A1 WO 2014160616 A1 WO2014160616 A1 WO 2014160616A1 US 2014031520 W US2014031520 W US 2014031520W WO 2014160616 A1 WO2014160616 A1 WO 2014160616A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyurethane
- polyisocyanurate
- isocyanurate polymer
- isocyanurate
- polymer
- Prior art date
Abstract
Description
Claims