WO2014151647A1 - Methods for retreading tires employing tread composites made with dry-transfer cement composite - Google Patents
Methods for retreading tires employing tread composites made with dry-transfer cement composite Download PDFInfo
- Publication number
- WO2014151647A1 WO2014151647A1 PCT/US2014/026167 US2014026167W WO2014151647A1 WO 2014151647 A1 WO2014151647 A1 WO 2014151647A1 US 2014026167 W US2014026167 W US 2014026167W WO 2014151647 A1 WO2014151647 A1 WO 2014151647A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- tread
- cement
- composite
- release liner
- tire
- Prior art date
Abstract
Description
Claims