WO2014062952A1 - 8-ring small pore molecular sieve with promoter to improve low temperature performance - Google Patents
8-ring small pore molecular sieve with promoter to improve low temperature performance Download PDFInfo
- Publication number
- WO2014062952A1 WO2014062952A1 PCT/US2013/065501 US2013065501W WO2014062952A1 WO 2014062952 A1 WO2014062952 A1 WO 2014062952A1 US 2013065501 W US2013065501 W US 2013065501W WO 2014062952 A1 WO2014062952 A1 WO 2014062952A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- molecular sieve
- catalyst
- small pore
- pore molecular
- ring small
- Prior art date
Abstract
Description
Claims