WO2014029871A1 - Alternan polysaccharide that is functionalized with nitrogen groups that can be protonated, or with permanently positively charged nitrogen groups. - Google Patents
Alternan polysaccharide that is functionalized with nitrogen groups that can be protonated, or with permanently positively charged nitrogen groups. Download PDFInfo
- Publication number
- WO2014029871A1 WO2014029871A1 PCT/EP2013/067547 EP2013067547W WO2014029871A1 WO 2014029871 A1 WO2014029871 A1 WO 2014029871A1 EP 2013067547 W EP2013067547 W EP 2013067547W WO 2014029871 A1 WO2014029871 A1 WO 2014029871A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- alternan
- groups
- chr
- functionalized
- group
- Prior art date
Abstract
Description
Claims