WO2013068502A2 - Härter für epoxidharz-beschichtungen - Google Patents
Härter für epoxidharz-beschichtungen Download PDFInfo
- Publication number
- WO2013068502A2 WO2013068502A2 PCT/EP2012/072193 EP2012072193W WO2013068502A2 WO 2013068502 A2 WO2013068502 A2 WO 2013068502A2 EP 2012072193 W EP2012072193 W EP 2012072193W WO 2013068502 A2 WO2013068502 A2 WO 2013068502A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- amine
- group
- formula
- bis
- groups
- Prior art date
Abstract
Description
Claims