WO2013063238A1 - Glass compositions with improved chemical and mechanical durability - Google Patents
Glass compositions with improved chemical and mechanical durability Download PDFInfo
- Publication number
- WO2013063238A1 WO2013063238A1 PCT/US2012/061867 US2012061867W WO2013063238A1 WO 2013063238 A1 WO2013063238 A1 WO 2013063238A1 US 2012061867 W US2012061867 W US 2012061867W WO 2013063238 A1 WO2013063238 A1 WO 2013063238A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mol
- glass
- equal
- less
- glass composition
- Prior art date
Abstract
Description
Claims