WO2012119947A1 - Method to produce a sawing bead - Google Patents
Method to produce a sawing bead Download PDFInfo
- Publication number
- WO2012119947A1 WO2012119947A1 PCT/EP2012/053643 EP2012053643W WO2012119947A1 WO 2012119947 A1 WO2012119947 A1 WO 2012119947A1 EP 2012053643 W EP2012053643 W EP 2012053643W WO 2012119947 A1 WO2012119947 A1 WO 2012119947A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- tube
- bead
- abrasive
- matrix material
- abrasive layer
- Prior art date
Abstract
Description
Claims