WO2011113195A1 - 有机太阳能电池及其制备方法 - Google Patents
有机太阳能电池及其制备方法 Download PDFInfo
- Publication number
- WO2011113195A1 WO2011113195A1 PCT/CN2010/071056 CN2010071056W WO2011113195A1 WO 2011113195 A1 WO2011113195 A1 WO 2011113195A1 CN 2010071056 W CN2010071056 W CN 2010071056W WO 2011113195 A1 WO2011113195 A1 WO 2011113195A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- photosensitive layer
- solar cell
- conversion
- layer
- organic solar
- Prior art date
Description
Claims (14)
- 一种有机太阳能电池,其包括光反射性电极、位于所述光反射性电极上的光敏层、位于所述光敏层上的透明电极,其特征在于,还包括位于所述透明电极上的上转换结构,以及位于所述透明电极和上转换结构之间的透明绝缘层,所述上转换结构包括对光谱具有上转换功能的上转换材料,所述光敏层至少包括电子给体材料和电子受体材料相混合的混合异质结结构。
- 如权利要求1所述的有机太阳能电池,其特征在于,所述上转换材料包括单掺或双掺稀土离子的卤化物、氧化物、硫化物或者它们的组合物。
- 如权利要求1所述的有机太阳能电池,其特征在于,所述上转换材料包括单掺或双掺稀土离子的BaY2F8、KZnF3、NaYF4、NaYb(WO4)2、Ga2S3-La2O3、Y2O3、Gd2O3、ZrO2、ZnO、BaTiO3、ZrF2-SiO2或ZnO-SiO2。
- 如权利要求2或3所述的有机太阳能电池,其特征在于,所述单掺或双掺的稀土离子包括Er3+、Ho3+、Tm3+、Pr3+、Yb3+/Ho3+、Yb3+/Tm3+、Yb3+/Pr3+、Yb3+/Er3+或Tb3+/Er3+。
- 如权利要求1所述的有机太阳能电池,其特征在于,所述上转换结构为包含上转换材料的薄膜或者采用氧化物薄膜包覆上转换材料的复合结构。
- 如权利要求1所述的有机太阳能电池,其特征在于,所述光敏层还包括第一光敏层和第二光敏层,所述混合异质结结构为第三光敏层,并夹于所述第一光敏层和第二光敏层之间,所述第一光敏层包括所述混合异质结结构中的电子给体材料,所述第二光敏层包括所述混合异质结结构中的电子受体材料。
- 如权利要求1所述的有机太阳能电池,其特征在于,还包括位于所述光反射性电极与光敏层之间的第一缓冲层以及位于所述光敏层与透明电极之间的第二缓冲层,所述第一、第二缓冲层的材料选自聚乙烯二氧基噻吩:聚苯乙烯-磺酸复合材料、钛的氧化物、BCP、Alq3或LiF。
- 如权利要求1所述的有机太阳能电池,其特征在于,所述光敏层的电子给体材料选自聚对苯撑乙烯或其衍生物、聚噻吩材料、聚芴材料、聚咔唑材料、聚双噻吩环戊烷材料或含喹喔啉、噻吩并吡咯和噻吩并吡嗪单元的聚合物,所述光敏层的电子受体材料为聚北酰亚胺材料,所述各个缓冲层的材料为聚乙烯二氧基噻吩:聚苯乙烯-磺酸复合材料。
- 如权利要求1所述的有机太阳能电池,其特征在于,所述光敏层的电子给体材料选自酞菁染料、并五苯、卟啉化合物或菁染料,所述光敏层的电子受体材料选自四羧基北衍生物、C60、C70、二奈嵌苯或二奈嵌苯衍生物,所述各个缓冲层的材料选自钛的氧化物、BCP、Alq3或LiF。
- 一种有机太阳能电池制备方法,其包括如下步骤:提供一透明绝缘层,所述透明绝缘层具有相对的第一表面和第二表面;在所述透明绝缘层的第一表面上形成透明电极;在所述透明电极上形成光敏层,所述光敏层至少包括电子给体材料和电子受体材料相混合的混合异质结结构;在所述光敏层上形成光反射性电极;在所述透明绝缘层的第二表面上形成上转换结构,使得透明绝缘层位于所述透明电极和上转换结构之间,所述上转换结构包括对光谱具有上转换功能的上转换材料。
- 如权利要求10所述的有机太阳能电池制备方法,其特征在于,所述光敏层还包括第一光敏层和第二光敏层,所述混合异质结结构为第三光敏层,并夹于所述第一光敏层和第二光敏层之间,所述第一光敏层包括所述混合异质结结构中的电子给体材料,所述第二光敏层包括所述混合异质结结构中的电子受体材料。
- 如权利要求11所述的有机太阳能电池制备方法,其特征在于,所述三层光敏层都采用旋涂法或真空镀膜法中的一种方法形成。
- 如权利要求10所述的有机太阳能电池制备方法,其特征在于,所述上转换结构通过溶胶-凝胶法将所述上转换材料沉积于所述透明绝缘层的第二表面,或者采用化学共沉淀法将氧化物薄膜包覆上转换材料形成于所述透明绝缘层的第二表面。
- 如权利要求10所述的有机太阳能电池制备方法,其特征在于,所述光敏层采用旋涂法形成,并在旋涂之前,采用有机溶剂将电子给体材料和电子受体材料预先溶解,同时用磁力搅拌器充分搅拌,配成含电子给体材料和电子受体材料的溶液,然后,将电子给体材料溶液和电子受体材料溶液旋涂,以获得所述光敏层。