WO2011061166A1 - Sawing rope - Google Patents
Sawing rope Download PDFInfo
- Publication number
- WO2011061166A1 WO2011061166A1 PCT/EP2010/067527 EP2010067527W WO2011061166A1 WO 2011061166 A1 WO2011061166 A1 WO 2011061166A1 EP 2010067527 W EP2010067527 W EP 2010067527W WO 2011061166 A1 WO2011061166 A1 WO 2011061166A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- rope
- sawing
- sleeve
- abrasive
- wire rope
- Prior art date
Abstract
Description
Claims