WO2011026925A1 - Procede de fabrication d'un module a zone creuse, de preference pour la circulation de fluide - Google Patents
Procede de fabrication d'un module a zone creuse, de preference pour la circulation de fluide Download PDFInfo
- Publication number
- WO2011026925A1 WO2011026925A1 PCT/EP2010/062921 EP2010062921W WO2011026925A1 WO 2011026925 A1 WO2011026925 A1 WO 2011026925A1 EP 2010062921 W EP2010062921 W EP 2010062921W WO 2011026925 A1 WO2011026925 A1 WO 2011026925A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- assembly
- plate
- recess
- defining
- plates
- Prior art date
Abstract
Description
Claims