WO2010118841A1 - Bimolecular inverse emulsion polymer - Google Patents
Bimolecular inverse emulsion polymer Download PDFInfo
- Publication number
- WO2010118841A1 WO2010118841A1 PCT/EP2010/002218 EP2010002218W WO2010118841A1 WO 2010118841 A1 WO2010118841 A1 WO 2010118841A1 EP 2010002218 W EP2010002218 W EP 2010002218W WO 2010118841 A1 WO2010118841 A1 WO 2010118841A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- water
- cationic
- oil
- polymer
- monomers
- Prior art date
Abstract
Description
Claims