WO2010069515A1 - Rubber-reinforced vinyl aromatic (co)polymer, having an optimum balance of physico-mechanical properties and a high gloss - Google Patents
Rubber-reinforced vinyl aromatic (co)polymer, having an optimum balance of physico-mechanical properties and a high gloss Download PDFInfo
- Publication number
- WO2010069515A1 WO2010069515A1 PCT/EP2009/008861 EP2009008861W WO2010069515A1 WO 2010069515 A1 WO2010069515 A1 WO 2010069515A1 EP 2009008861 W EP2009008861 W EP 2009008861W WO 2010069515 A1 WO2010069515 A1 WO 2010069515A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- rubber
- vinyl aromatic
- cps
- polymer
- weight
- Prior art date
Abstract
Description
Claims