WO2010034877A1 - Coating for wood board and wood board - Google Patents
Coating for wood board and wood board Download PDFInfo
- Publication number
- WO2010034877A1 WO2010034877A1 PCT/FI2009/050663 FI2009050663W WO2010034877A1 WO 2010034877 A1 WO2010034877 A1 WO 2010034877A1 FI 2009050663 W FI2009050663 W FI 2009050663W WO 2010034877 A1 WO2010034877 A1 WO 2010034877A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- film
- coupling agent
- cha
- coating
- Prior art date
Abstract
Description
Claims