WO2010013006A2 - Blue-light emitting material - Google Patents
Blue-light emitting material Download PDFInfo
- Publication number
- WO2010013006A2 WO2010013006A2 PCT/GB2009/001874 GB2009001874W WO2010013006A2 WO 2010013006 A2 WO2010013006 A2 WO 2010013006A2 GB 2009001874 W GB2009001874 W GB 2009001874W WO 2010013006 A2 WO2010013006 A2 WO 2010013006A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- light
- perylene
- emitting material
- blue
- material according
- Prior art date
Abstract
Description
Claims